PL2738278T3 - Blacha stalowa cienka o dużej wytrzymałości i ocynkowana blacha stalowa cienka o dużej wytrzymałości oraz o doskonałej podatności na utrwalanie kształtu i sposób ich wytwarzania - Google Patents

Blacha stalowa cienka o dużej wytrzymałości i ocynkowana blacha stalowa cienka o dużej wytrzymałości oraz o doskonałej podatności na utrwalanie kształtu i sposób ich wytwarzania

Info

Publication number
PL2738278T3
PL2738278T3 PL12820033T PL12820033T PL2738278T3 PL 2738278 T3 PL2738278 T3 PL 2738278T3 PL 12820033 T PL12820033 T PL 12820033T PL 12820033 T PL12820033 T PL 12820033T PL 2738278 T3 PL2738278 T3 PL 2738278T3
Authority
PL
Poland
Prior art keywords
steel sheet
strength
manufacturing
shape fixability
galvanized steel
Prior art date
Application number
PL12820033T
Other languages
English (en)
Inventor
Akinobu MINAMI
Hiroyuki Kawata
Akinobu Murasato
Yuji Yamaguchi
Natsuko Sugiura
Takuya Kuwayama
Naoki Maruyama
Takamasa Suzuki
Original Assignee
Nippon Steel Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corporation filed Critical Nippon Steel Corporation
Publication of PL2738278T3 publication Critical patent/PL2738278T3/pl

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21B—ROLLING OF METAL
    • B21B3/00—Rolling materials of special alloys so far as the composition of the alloy requires or permits special rolling methods or sequences ; Rolling of aluminium, copper, zinc or other non-ferrous metals
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C21D1/19—Hardening; Quenching with or without subsequent tempering by interrupted quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/34—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
    • C25D5/34—Pretreatment of metallic surfaces to be electroplated
    • C25D5/36—Pretreatment of metallic surfaces to be electroplated of iron or steel
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D7/00—Electroplating characterised by the article coated
    • C25D7/06—Wires; Strips; Foils
    • C25D7/0614—Strips or foils
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D3/00—Electroplating: Baths therefor
    • C25D3/02—Electroplating: Baths therefor from solutions
    • C25D3/22—Electroplating: Baths therefor from solutions of zinc
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Mechanical Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Electrochemistry (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
PL12820033T 2011-07-29 2012-07-27 Blacha stalowa cienka o dużej wytrzymałości i ocynkowana blacha stalowa cienka o dużej wytrzymałości oraz o doskonałej podatności na utrwalanie kształtu i sposób ich wytwarzania PL2738278T3 (pl)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2011167689 2011-07-29
EP12820033.4A EP2738278B1 (en) 2011-07-29 2012-07-27 High-strength steel sheet and high-strength galvanized steel sheet excellent in shape fixability, and manufacturing method thereof
PCT/JP2012/069262 WO2013018741A1 (ja) 2011-07-29 2012-07-27 形状凍結性に優れた高強度鋼板、高強度亜鉛めっき鋼板およびそれらの製造方法

Publications (1)

Publication Number Publication Date
PL2738278T3 true PL2738278T3 (pl) 2020-05-18

Family

ID=47629264

Family Applications (1)

Application Number Title Priority Date Filing Date
PL12820033T PL2738278T3 (pl) 2011-07-29 2012-07-27 Blacha stalowa cienka o dużej wytrzymałości i ocynkowana blacha stalowa cienka o dużej wytrzymałości oraz o doskonałej podatności na utrwalanie kształtu i sposób ich wytwarzania

Country Status (13)

Country Link
US (1) US9988700B2 (pl)
EP (1) EP2738278B1 (pl)
JP (1) JP5299591B2 (pl)
KR (1) KR101598309B1 (pl)
CN (1) CN103703157B (pl)
BR (1) BR112014002026B1 (pl)
CA (1) CA2842800C (pl)
ES (1) ES2766756T3 (pl)
MX (1) MX366222B (pl)
PL (1) PL2738278T3 (pl)
TW (1) TWI488976B (pl)
WO (1) WO2013018741A1 (pl)
ZA (1) ZA201401402B (pl)

Families Citing this family (54)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2980227A4 (en) 2013-03-28 2016-12-21 Hyundai Steel Co STEEL SHEET AND PROCESS FOR PRODUCING SAME
CN105121672B (zh) 2013-03-28 2017-07-14 现代制铁株式会社 钢板及其制备方法
KR101597411B1 (ko) * 2013-08-30 2016-02-25 현대제철 주식회사 강판 및 그 제조 방법
KR101586893B1 (ko) * 2013-06-27 2016-01-20 현대제철 주식회사 강판 및 그 제조 방법
JP6264176B2 (ja) * 2013-04-23 2018-01-24 新日鐵住金株式会社 冷延鋼板およびその製造方法
JP6221424B2 (ja) * 2013-07-04 2017-11-01 新日鐵住金株式会社 冷延鋼板およびその製造方法
JP5728115B1 (ja) 2013-09-27 2015-06-03 株式会社神戸製鋼所 延性および低温靭性に優れた高強度鋼板、並びにその製造方法
JP5728108B2 (ja) 2013-09-27 2015-06-03 株式会社神戸製鋼所 加工性および低温靭性に優れた高強度鋼板、並びにその製造方法
CN103757562A (zh) * 2013-12-13 2014-04-30 芜湖金鹰机械科技开发有限公司 一种耐磨铸球材料及其制备方法
JP6306481B2 (ja) * 2014-03-17 2018-04-04 株式会社神戸製鋼所 延性及び曲げ性に優れた高強度冷延鋼板および高強度溶融亜鉛めっき鋼板、並びにそれらの製造方法
CN106574342B (zh) * 2014-08-07 2018-10-12 杰富意钢铁株式会社 高强度钢板及其制造方法、以及高强度镀锌钢板的制造方法
WO2016021197A1 (ja) * 2014-08-07 2016-02-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法、ならびに高強度亜鉛めっき鋼板の製造方法
JP5983896B2 (ja) * 2014-08-07 2016-09-06 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法、ならびに高強度亜鉛めっき鋼板の製造方法
JP5983895B2 (ja) * 2014-08-07 2016-09-06 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法、ならびに高強度亜鉛めっき鋼板の製造方法
CA2959096C (en) * 2014-08-25 2019-06-25 Tata Steel Ijmuiden B.V. Cold rolled high strength low alloy steel
KR101607011B1 (ko) * 2014-09-26 2016-03-28 현대제철 주식회사 강판 및 그 제조 방법
KR101620750B1 (ko) 2014-12-10 2016-05-13 주식회사 포스코 성형성이 우수한 복합조직강판 및 이의 제조방법
BR112017012803B1 (pt) 2014-12-16 2021-10-05 Greer Steel Company Composição de aço para cartuchos de munição de percussão anular e método de processamento da referida composição de aço para uso em um cartucho de percusão anular
CN104513927B (zh) * 2014-12-19 2017-04-05 宝山钢铁股份有限公司 一种抗拉强度800MPa级高强度高韧性钢板及其制造方法
RU2705741C2 (ru) 2015-02-25 2019-11-11 Арселормиттал Подвергнутый чистовому отжигу, высокопрочный стальной лист с покрытием, имеющий повышенный предел текучести и улучшенную степень раздачи отверстия
WO2016152870A1 (ja) * 2015-03-23 2016-09-29 新日鐵住金株式会社 熱延鋼板及びその製造方法、並びに冷延鋼板の製造方法
JP6434348B2 (ja) * 2015-03-23 2018-12-05 株式会社神戸製鋼所 加工性に優れた高強度鋼板
JP6472692B2 (ja) * 2015-03-23 2019-02-20 株式会社神戸製鋼所 成形性に優れた高強度鋼板
MX2017014816A (es) 2015-05-21 2018-05-11 Ak Steel Properties Inc Aceros avanzados de alta resistencia de tercera generacion de alto manganeso.
JP6460238B2 (ja) * 2015-07-13 2019-01-30 新日鐵住金株式会社 鋼板、溶融亜鉛めっき鋼板、及び合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
CN107849666B (zh) 2015-07-13 2020-05-12 日本制铁株式会社 钢板、热浸镀锌钢板和合金化热浸镀锌钢板、以及它们的制造方法
JP6172404B1 (ja) * 2015-09-04 2017-08-02 Ｊｆｅスチール株式会社 高強度薄鋼板およびその製造方法
JP6749818B2 (ja) * 2016-02-29 2020-09-02 株式会社神戸製鋼所 高強度鋼板およびその製造方法
WO2017150117A1 (ja) * 2016-02-29 2017-09-08 株式会社神戸製鋼所 高強度鋼板、及びその製造方法
KR102099769B1 (ko) 2016-03-25 2020-04-10 닛폰세이테츠 가부시키가이샤 고강도 강판 및 고강도 아연 도금 강판
CN105821349A (zh) * 2016-06-13 2016-08-03 苏州双金实业有限公司 一种具有价格低优点的钢
TWI618799B (zh) * 2016-09-21 2018-03-21 新日鐵住金股份有限公司 鋼板
MX2019004000A (es) * 2016-10-19 2019-08-14 Nippon Steel Corp Lamina de acero recubierta de metal, metodo de fabricacion de lamina de acero galvanizada por inmersion en caliente, y metodo de fabricacion de lamina de acero galvanizada-recocida aleada.
CN107142418A (zh) * 2017-04-14 2017-09-08 唐山钢铁集团有限责任公司 一种高铝高锰冷轧镀锌钢带和钢板及其生产方法
KR101998952B1 (ko) 2017-07-06 2019-07-11 주식회사 포스코 재질편차가 적고 표면품질이 우수한 초고강도 열연강판 및 그 제조방법
JP7320513B2 (ja) * 2017-09-20 2023-08-03 宝鋼湛江鋼鉄有限公司 インラインでＴｉ微量合金化熱間圧延高強度鋼の析出強化効果を向上させる生産方法
CN107653361B (zh) * 2017-10-14 2020-02-18 上海鑫昌众星实业有限公司 一种深加工汽车钢板的制备工艺
CN107641685B (zh) * 2017-10-14 2019-10-15 广西盛隆冶金有限公司 一种高强度钢板的热处理方法
KR102477508B1 (ko) 2018-03-30 2022-12-16 닛폰세이테츠 가부시키가이샤 용융 아연 도금 강판 및 합금화 용융 아연 도금 강판
TWI662139B (zh) * 2018-03-31 2019-06-11 日商新日鐵住金股份有限公司 Hot-dip galvanized steel sheet and alloyed hot-dip galvanized steel sheet
WO2020065372A1 (en) * 2018-09-25 2020-04-02 Arcelormittal High strength hot rolled steel having excellent scale adhesivness and a method of manufacturing the same
MX2021003246A (es) * 2018-10-04 2021-05-12 Nippon Steel Corp Lamina de acero galvanorrecocido.
KR102276740B1 (ko) * 2018-12-18 2021-07-13 주식회사 포스코 연성 및 가공성이 우수한 고강도 강판 및 그 제조방법
CN113597473B (zh) * 2019-04-11 2022-11-01 日本制铁株式会社 钢板及其制造方法
MX2022004926A (es) * 2019-10-31 2022-05-16 Jfe Steel Corp Lamina de acero, elemento y metodos para producir el mismo.
CN114829678B (zh) * 2019-12-20 2024-10-29 日本制铁株式会社 镀Ni钢板以及镀Ni钢板的制造方法
CN115362280B (zh) * 2020-04-03 2023-10-17 日本制铁株式会社 钢板及其制造方法
CN112375973B (zh) * 2020-10-26 2022-12-20 佛山科学技术学院 一种用于建筑幕墙工程的高强钢结构件及其热处理工艺
KR20230084534A (ko) 2020-11-11 2023-06-13 닛폰세이테츠 가부시키가이샤 강판 및 그 제조 방법
CN112501515B (zh) * 2020-11-30 2022-08-09 日照钢铁控股集团有限公司 一种1300MPa级高强高塑低成本热轧钢
CN112501516A (zh) * 2020-11-30 2021-03-16 日照钢铁控股集团有限公司 一种1080MPa级高强度高塑性热轧钢生产方法
KR102453006B1 (ko) * 2020-12-18 2022-10-12 주식회사 포스코 도금성이 우수한 고강도 용융아연도금강판 및 그 제조방법
JPWO2023135962A1 (pl) 2022-01-13 2023-07-20
CN115132301B (zh) * 2022-08-29 2022-12-16 中国航发北京航空材料研究院 钴基高温合金碳化物的检测方法、装置、存储介质及电子设备

Family Cites Families (32)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3248118B2 (ja) * 1994-01-12 2002-01-21 新日本製鐵株式会社 加工性と疲労特性に優れた引張強さ４５〜６５ｋｇｆ／ｍｍ２ の高強度複合組織熱延鋼板とその製造方法
JP3842897B2 (ja) * 1998-05-06 2006-11-08 新日本製鐵株式会社 形状凍結性に優れた良加工性熱延高張力鋼板の製造方法
JP3525812B2 (ja) * 1999-07-02 2004-05-10 住友金属工業株式会社 衝撃エネルギー吸収性に優れた高強度鋼板およびその製造方法
JP3872621B2 (ja) 1999-11-05 2007-01-24 新日本製鐵株式会社 自動車車体用亜鉛系メッキ鋼板
JP4465805B2 (ja) * 2000-05-02 2010-05-26 Ｊｆｅスチール株式会社 耐常温時効性と歪時効特性に優れる熱延鋼板およびその製造方法
JP2001355041A (ja) * 2000-06-13 2001-12-25 Kobe Steel Ltd 延性・めっき密着性に優れた変態誘起塑性めっき鋼板およびその製造方法
CN1208490C (zh) 2000-09-21 2005-06-29 新日本制铁株式会社 形状固定性优异的钢板及其生产方法
JP4188609B2 (ja) * 2001-02-28 2008-11-26 株式会社神戸製鋼所 加工性に優れた高強度鋼板およびその製造方法
JP3772686B2 (ja) * 2001-03-28 2006-05-10 住友金属工業株式会社 高張力鋼板およびその製造方法
JP2002317249A (ja) * 2001-04-18 2002-10-31 Nippon Steel Corp 延性の優れた低降伏比型高強度鋼板およびその製造方法
ATE383452T1 (de) 2001-10-04 2008-01-15 Nippon Steel Corp Ziehbares hochfestes dünnes stahlblech mit hervorragender formfixierungseigenschaft und herstellungsverfahren dafür
JP3921101B2 (ja) 2002-02-27 2007-05-30 新日本製鐵株式会社 形状凍結性に優れた高強度高延性溶融亜鉛めっき鋼板の製造方法
KR100451247B1 (ko) * 2002-11-06 2004-10-13 엘지전자 주식회사 전기밥솥
JP4119758B2 (ja) 2003-01-16 2008-07-16 株式会社神戸製鋼所 加工性および形状凍結性に優れた高強度鋼板、並びにその製法
JP4320198B2 (ja) 2003-03-28 2009-08-26 日新製鋼株式会社 衝撃特性と形状凍結性に優れた高強度冷延鋼板の製造方法
JP4325865B2 (ja) * 2003-08-29 2009-09-02 株式会社神戸製鋼所 加工性に優れた高張力鋼板およびその製法
JP4410741B2 (ja) * 2005-09-05 2010-02-03 新日本製鐵株式会社 成形性に優れた高強度薄鋼板およびその製造方法
JP4692259B2 (ja) 2005-12-07 2011-06-01 Ｊｆｅスチール株式会社 成形性および形状凍結性に優れる高強度鋼板
JP4732962B2 (ja) * 2006-06-09 2011-07-27 株式会社神戸製鋼所 合金化溶融亜鉛めっき鋼板の強度−延性バランスのバラツキ改善方法
JP4932363B2 (ja) 2006-07-20 2012-05-16 新日本製鐵株式会社 高強度合金化溶融亜鉛めっき鋼板及びその製造方法
JP5223360B2 (ja) 2007-03-22 2013-06-26 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5369663B2 (ja) 2008-01-31 2013-12-18 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
CA2718304C (en) * 2008-03-27 2012-03-06 Nippon Steel Corporation High-strength cold-rolled steel sheet, high-strength galvanized steel sheet, and high-strength alloyed hot-dip galvanized steel sheet having excellent formability and weldability,and methods for manufacturing the same
MX2010010989A (es) 2008-04-10 2010-12-21 Nippon Steel Corp Chapas de acero de alta resistencia que son excelentes en el equilibrio entre facilidad de trabajo en la desbastacion de metales y ductilidad, y excelentes en resistencia a la fatiga, chapas de acero recubiertas de zinc y procesos para la produccion
JP2010229514A (ja) * 2009-03-27 2010-10-14 Sumitomo Metal Ind Ltd 冷延鋼板およびその製造方法
JP5323563B2 (ja) * 2009-03-31 2013-10-23 株式会社神戸製鋼所 加工性および形状凍結性に優れた高強度冷延鋼板
KR101445813B1 (ko) * 2009-11-30 2014-10-01 신닛테츠스미킨 카부시키카이샤 내수소취화 특성이 우수한 인장 최대 강도가 900 ＭＰａ 이상인 고강도 강판 및 그 제조 방법
JP5651964B2 (ja) * 2010-02-16 2015-01-14 新日鐵住金株式会社 延性及び穴広げ性並びに耐食性に優れた合金化溶融亜鉛めっき鋼板及びその製造方法
FI122313B (fi) 2010-06-07 2011-11-30 Rautaruukki Oyj Menetelmä kuumavalssatun terästuotteen valmistamiseksi sekä kuumavalssattu teräs
PL2617849T3 (pl) 2010-09-16 2017-07-31 Nippon Steel & Sumitomo Metal Corporation Walcowana na zimno blacha stalowa o dużej wytrzymałości z doskonałą ciągliwością i podatnością na wywijanie kołnierza, ocynkowana blacha stalowa o dużej wytrzymałości, oraz sposób ich wytwarzania
JP5298114B2 (ja) * 2010-12-27 2013-09-25 株式会社神戸製鋼所 塗膜密着性と加工性に優れた高強度冷延鋼板、及びその製造方法
JP5533729B2 (ja) 2011-02-22 2014-06-25 新日鐵住金株式会社 局部変形能に優れ、成形性の方位依存性の少ない延性に優れた高強度熱延鋼板及びその製造方法

Also Published As

Publication number Publication date
KR20140043156A (ko) 2014-04-08
EP2738278B1 (en) 2019-11-13
JP5299591B2 (ja) 2013-09-25
CA2842800A1 (en) 2013-02-07
BR112014002026A2 (pt) 2017-02-21
CN103703157A (zh) 2014-04-02
TW201313913A (zh) 2013-04-01
MX366222B (es) 2019-07-03
KR101598309B1 (ko) 2016-02-26
ES2766756T3 (es) 2020-06-15
CA2842800C (en) 2016-09-06
ZA201401402B (en) 2015-04-29
EP2738278A4 (en) 2015-09-02
RU2014107494A (ru) 2015-09-10
WO2013018741A1 (ja) 2013-02-07
CN103703157B (zh) 2015-12-02
MX2014000956A (es) 2014-02-27
BR112014002026B1 (pt) 2019-03-26
EP2738278A1 (en) 2014-06-04
JPWO2013018741A1 (ja) 2015-03-05
US9988700B2 (en) 2018-06-05
TWI488976B (zh) 2015-06-21
US20140242414A1 (en) 2014-08-28

Similar Documents

Publication Publication Date Title
ZA201401402B (en) High-strength steel sheet and high-strength galvanized steel sheet excellent in shape fixability,and manufacturing method thereof
ZA201401401B (en) High-strength steel sheet excellent in impact resistance and manufacturing method thereof,and high-strength galvanized steel sheet and manufacturing method thereof
EP2881481A4 (en) HIGHLY RESISTANT STEEL PLATE WITH EXCELLENT FORMABILITY AND FORMING STRENGTH AND METHOD OF PRODUCTION THEREFOR
PL2698440T3 (pl) Blacha stalowa cienka walcowana na gorąco o dużej wytrzymałości mająca doskonałą miejscową podatność na odkształcenie oraz sposób jej wytwarzania
PL2738276T3 (pl) Blacha stalowa cienka ocynkowana o dużej wytrzymałości i blacha stalowa cienka o dużej wytrzymałości mająca doskonałą formowalność oraz sposób ich wytwarzania
EP2799578A4 (en) HOT ROLLED STEEL SHEET WITH HIGH STRENGTH AND METHOD FOR PRODUCING SAME
PL2698444T3 (pl) Blacha stalowa walcowana na gorąco i sposób jej wytwarzania
EP2765212A4 (en) HIGH-RESISTANCE STEEL PLATE AND MANUFACTURING METHOD THEREFOR
EP2684972A4 (en) STEEL PLATE FOR HOT IMPORTS, PRODUCTION METHOD THEREFOR, AND METHOD FOR PRODUCING HIGH-STRENGTH PARTS
ZA201402355B (en) High-strength hot-dip galvanized steel sheet and high-strength alloyed hot-dip galvanized steel sheet excellent in mechanical cutting property,and manufacturing method thereof
EP2799568A4 (en) FINE HIGH-STRENGTH STEEL SHEET AND MANUFACTURING METHOD THEREOF
ZA201402259B (en) Hot-dip galvanized steel sheet and manufacturing method thereof
PL2692895T3 (pl) Blacha stalowa cienka walcowana na zimno i sposób jej wytwarzania
ZA201402351B (en) High-strength hot-dip galvanized steel sheet having excellent delayed fracture resistance and manufacturing method thereof
ZA201401348B (en) High-strength cold-rolled steel sheet having excellent stretch flangeability and precision punchability,and manufacturing method thereof
ZA201307002B (en) Hot-rolled steel sheet and associated production method
EP2738275A4 (en) HIGH-FIXED GALVANIZED STEEL PLATE AND HIGH-RESISTANCE STEEL PLATE WITH EXCELLENT FORMABILITY AND METHOD FOR THE PRODUCTION THEREOF
PL2738280T3 (pl) Blacha stalowa cienka ocynkowana o dużej wytrzymałości mająca doskonałą zginalność oraz sposób jej wytwarzania
EP2902520A4 (en) HOT ROLLED STEEL SHEET AND PROCESS FOR PRODUCING THE SAME
EP2811047A4 (en) FIREPLATED STEEL PLATE AND METHOD OF MANUFACTURING THEREOF
EP2937433A4 (en) COLD LAMINATED STEEL SHEET, OF HIGH STRENGTH AND LOW ELASTICITY RATIO AND METHOD OF MANUFACTURING THE SAME
EP2829626A4 (en) METHOD FOR MANUFACTURING HIGH-STRENGTH HOT-DIP GALVANIZED STEEL SHEET AND HIGH-RESISTANCE HOT-DIP GALVANIZED STEEL SHEET
EP2695961A4 (en) HIGH STRENGTH STEEL PLATE WITH EXCELLENT WORKABILITY AND MANUFACTURING METHOD THEREFOR
ZA201207927B (en) High-strength cold-rolled steel sheet and method for manufacturing the same
EP2829627A4 (en) METHOD FOR THE PRODUCTION OF HIGH-TERM FIRED GALVANIZED STEEL PLATE AND HIGH-TERM FIRED-GEL STEEL PLATE