WO2008035672A1 - Procédé de fabrication d'un film durci transparent en utilisant une couche de résine photosensible positive pendant une demie exposition - Google Patents

Procédé de fabrication d'un film durci transparent en utilisant une couche de résine photosensible positive pendant une demie exposition Download PDF

Info

Publication number
WO2008035672A1
WO2008035672A1 PCT/JP2007/068083 JP2007068083W WO2008035672A1 WO 2008035672 A1 WO2008035672 A1 WO 2008035672A1 JP 2007068083 W JP2007068083 W JP 2007068083W WO 2008035672 A1 WO2008035672 A1 WO 2008035672A1
Authority
WO
WIPO (PCT)
Prior art keywords
component
photosensitive resin
sensitivity
positive photosensitive
cured film
Prior art date
Application number
PCT/JP2007/068083
Other languages
English (en)
Japanese (ja)
Inventor
Tadashi Hatanaka
Original Assignee
Nissan Chemical Industries, Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nissan Chemical Industries, Ltd. filed Critical Nissan Chemical Industries, Ltd.
Priority to JP2008535354A priority Critical patent/JP5083566B2/ja
Priority to KR1020097006060A priority patent/KR101334753B1/ko
Priority to CN2007800346563A priority patent/CN101517492B/zh
Publication of WO2008035672A1 publication Critical patent/WO2008035672A1/fr

Abstract

L'objet de l'invention est un procédé de fabrication d'un film durci transparent qui présente une importante marge d'exposition tout en maintenant un haut niveau de sensibilité, en particulier un procédé de fabrication d'un film durci transparent qui peut être appliqué à la fabrication d'un film aplatissant les TFT dans un élément d'affichage à cristaux liquides du type à semi-transmission et qui est notamment utilisé pour former simultanément des trous de contact et des surfaces concavo-convexes de réflexion par une demie exposition. Le procédé de fabrication d'un film durci transparent est caractérisé par l'empilement de deux couches de résine photosensible positive différentes l'une de l'autre à une sensibilité d'exposition sur un matériau de base de telle sorte que la couche de résine photosensible positive ayant une sensibilité moindre est située entre le matériau de base et la couche de résine photosensible positive ayant une sensibilité plus forte, l'exposition des couches de résine positive à la lumière, le chauffage des couches de résine positive exposées, le développement de l'ensemble et la cuisson ultérieure de l'ensemble. Un élément d'affichage comprenant un film durci transparent produit par le procédé présenté ci-dessus.
PCT/JP2007/068083 2006-09-20 2007-09-18 Procédé de fabrication d'un film durci transparent en utilisant une couche de résine photosensible positive pendant une demie exposition WO2008035672A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
JP2008535354A JP5083566B2 (ja) 2006-09-20 2007-09-18 ハーフ露光用ポジ型感光性樹脂層を用いる透明性硬化膜の製造方法
KR1020097006060A KR101334753B1 (ko) 2006-09-20 2007-09-18 하프노광용 포지티브형 감광성 수지층을 이용하는 투명성 경화막의 제조방법
CN2007800346563A CN101517492B (zh) 2006-09-20 2007-09-18 使用半曝光用正型感光性树脂层的透明性固化膜的制造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2006-254755 2006-09-20
JP2006254755 2006-09-20

Publications (1)

Publication Number Publication Date
WO2008035672A1 true WO2008035672A1 (fr) 2008-03-27

Family

ID=39200497

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2007/068083 WO2008035672A1 (fr) 2006-09-20 2007-09-18 Procédé de fabrication d'un film durci transparent en utilisant une couche de résine photosensible positive pendant une demie exposition

Country Status (5)

Country Link
JP (1) JP5083566B2 (fr)
KR (1) KR101334753B1 (fr)
CN (1) CN101517492B (fr)
TW (1) TWI431425B (fr)
WO (1) WO2008035672A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009282312A (ja) * 2008-05-22 2009-12-03 Nissan Chem Ind Ltd 感光性樹脂組成物
US8168371B2 (en) 2007-01-22 2012-05-01 Nissan Chemical Industries, Ltd. Positive photosensitive resin composition
US8828651B2 (en) 2005-07-25 2014-09-09 Nissan Chemical Industries, Ltd. Positive-type photosensitive resin composition and cured film manufactured therefrom

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101807553B (zh) * 2010-03-18 2013-05-01 信利半导体有限公司 一种具有感光性树脂薄膜材料的tft阵列板的制备方法
JP6743693B2 (ja) * 2015-03-11 2020-08-19 東レ株式会社 有機ｅｌ表示装置、およびその製造方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004020667A (ja) * 2002-06-13 2004-01-22 Kyocera Chemical Corp 感光性樹脂組成物およびポジ型パターン形成方法
JP2004144905A (ja) * 2002-10-23 2004-05-20 Tokyo Ohka Kogyo Co Ltd Ｌｃｄ製造用ポジ型ホトレジスト組成物およびレジストパターンの形成方法
JP2005316117A (ja) * 2004-04-28 2005-11-10 Kansai Paint Co Ltd 感光性樹脂組成物
JP2006030971A (ja) * 2004-06-15 2006-02-02 Techno Network Shikoku Co Ltd フォトリソグラフィー方法

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4173413B2 (ja) * 2003-08-28 2008-10-29 東京応化工業株式会社 リフトオフ用レジストパターンの形成方法
JP4131864B2 (ja) * 2003-11-25 2008-08-13 東京応化工業株式会社 化学増幅型ポジ型感光性熱硬化性樹脂組成物、硬化物の形成方法、及び機能素子の製造方法

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004020667A (ja) * 2002-06-13 2004-01-22 Kyocera Chemical Corp 感光性樹脂組成物およびポジ型パターン形成方法
JP2004144905A (ja) * 2002-10-23 2004-05-20 Tokyo Ohka Kogyo Co Ltd Ｌｃｄ製造用ポジ型ホトレジスト組成物およびレジストパターンの形成方法
JP2005316117A (ja) * 2004-04-28 2005-11-10 Kansai Paint Co Ltd 感光性樹脂組成物
JP2006030971A (ja) * 2004-06-15 2006-02-02 Techno Network Shikoku Co Ltd フォトリソグラフィー方法

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8828651B2 (en) 2005-07-25 2014-09-09 Nissan Chemical Industries, Ltd. Positive-type photosensitive resin composition and cured film manufactured therefrom
US8168371B2 (en) 2007-01-22 2012-05-01 Nissan Chemical Industries, Ltd. Positive photosensitive resin composition
JP2009282312A (ja) * 2008-05-22 2009-12-03 Nissan Chem Ind Ltd 感光性樹脂組成物

Also Published As

Publication number Publication date
JPWO2008035672A1 (ja) 2010-01-28
TWI431425B (zh) 2014-03-21
CN101517492A (zh) 2009-08-26
CN101517492B (zh) 2012-04-18
TW200819918A (en) 2008-05-01
JP5083566B2 (ja) 2012-11-28
KR20090058530A (ko) 2009-06-09
KR101334753B1 (ko) 2013-12-02

Similar Documents

Publication Publication Date Title
JP5163899B2 (ja) 環構造を持つ高分子化合物を含有するポジ型感光性樹脂組成物
US8828651B2 (en) Positive-type photosensitive resin composition and cured film manufactured therefrom
JP5019055B2 (ja) ポジ型感光性樹脂組成物及びそれから得られる硬化膜
JP4753040B2 (ja) 重合性基を有する化合物を含有するネガ型感光性樹脂組成物
TW201007362A (en) Positive type resist composition and method for producing microlens
JP5077526B2 (ja) 末端に不飽和基を有する化合物を含有するポジ型感光性樹脂組成物
JP7239895B2 (ja) 感光性樹脂組成物
JP5083566B2 (ja) ハーフ露光用ポジ型感光性樹脂層を用いる透明性硬化膜の製造方法
JP4753036B2 (ja) ポジ型感光性樹脂組成物及びそれから得られる硬化膜
TWI400570B (zh) 正型感光性樹脂組成物及由其所得之硬化膜
JP2024038456A (ja) バンクパターンの形成方法
JP2009192760A (ja) ポジ型感光性樹脂組成物
TWI424270B (zh) 正型感光性樹脂組成物及所得層間絕緣膜以及微透鏡
JP7045001B2 (ja) 感光性樹脂組成物
JP2008256974A (ja) ポジ型感光性樹脂組成物
JP5585796B2 (ja) 末端に不飽和基を有する化合物を含有するポジ型感光性樹脂組成物
JP7041402B2 (ja) 感光性樹脂組成物

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 200780034656.3

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07807483

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2008535354

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 1020097006060

Country of ref document: KR

122 Ep: pct application non-entry in european phase

Ref document number: 07807483

Country of ref document: EP

Kind code of ref document: A1