RU2014119361A - Литиево-силикатные стеклокерамика и стекло с оксидом одновалентного металла - Google Patents

Литиево-силикатные стеклокерамика и стекло с оксидом одновалентного металла Download PDF

Info

Publication number
RU2014119361A
RU2014119361A RU2014119361/03A RU2014119361A RU2014119361A RU 2014119361 A RU2014119361 A RU 2014119361A RU 2014119361/03 A RU2014119361/03 A RU 2014119361/03A RU 2014119361 A RU2014119361 A RU 2014119361A RU 2014119361 A RU2014119361 A RU 2014119361A
Authority
RU
Russia
Prior art keywords
glass
lithium
less
glass ceramic
glass ceramics
Prior art date
Application number
RU2014119361/03A
Other languages
English (en)
Other versions
RU2606999C2 (ru
Inventor
Кристиан РИТЦБЕРГЕР
Эльке АПЕЛЬ
Вольфрам ХЕЛАНД
Фолькер РАЙНБЕРГЕР
Original Assignee
Ивоклар Вивадент Аг
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ивоклар Вивадент Аг filed Critical Ивоклар Вивадент Аг
Publication of RU2014119361A publication Critical patent/RU2014119361A/ru
Application granted granted Critical
Publication of RU2606999C2 publication Critical patent/RU2606999C2/ru

Abstract

1. Литиево-силикатная стеклокерамика, включающая оксид одновалентного металла, выбранный из RbO, CsO и смесей таковых.2. Стеклокерамика по п. 1, за исключением литиево-дисиликатной стеклокерамики, которая включает, по меньшей мере, 6,1 масс.% ZrO.3. Стеклокерамика по п. 1 или 2, за исключением литиево-дисиликатной стеклокерамики, которая включает, по меньшей мере, 8,5 масс.% оксида переходного металла, выбранного из группы, состоящей из оксидов иттрия, оксидов переходных металлов, имеющих атомный номер 41-79 и смесей этих оксидов.4. Стеклокерамика по п. 1 или 2, которая включает менее 1,0, в частности, менее 0,5 масс.%, и, предпочтительно, менее 0,1 масс.% KO.5. Стеклокерамика по п. 1 или 2, которая включает менее 5,3, в частности, менее 5,1, предпочтительно, менее 4,0, особенно предпочтительно, менее 3,0 масс.% AlOи, наиболее предпочтительно, является, по существу, свободной от AlOили где мольное соотношение оксида одновалентного металла и AlOсоставляет, по меньшей мере, 0,5 и, предпочтительно, 0,5-1,5.6. Стеклокерамика по п. 1 или 2, которая включает менее 3,8, в частности, менее 3,6 и, предпочтительно, менее 2,5 масс.% ВаО.7. Стеклокерамика по п. 1 или 2, которая включает в себя оксид одновалентного металла или смесь таковых в количестве 0,1-17,0, в частности, 1,0-15,0, и, предпочтительно, 1,5-8,0 масс.%.8. Стеклокерамика по п. 1 или 2, которая содержит метасиликат лития в качестве основной кристаллической фазы и, в частности, содержит более 5 об.%, предпочтительно, более 10 об.% и, особенно предпочтительно, более 15 об.% кристаллов метасиликата лития.9. Стеклокерамика по п. 1 или 2, которая содержит дисиликат лития в качестве основной кристаллической фазы и, в частности, содержит более 10 об.%, предпоч�

Claims (24)

1. Литиево-силикатная стеклокерамика, включающая оксид одновалентного металла, выбранный из Rb2O, Cs2O и смесей таковых.
2. Стеклокерамика по п. 1, за исключением литиево-дисиликатной стеклокерамики, которая включает, по меньшей мере, 6,1 масс.% ZrO2.
3. Стеклокерамика по п. 1 или 2, за исключением литиево-дисиликатной стеклокерамики, которая включает, по меньшей мере, 8,5 масс.% оксида переходного металла, выбранного из группы, состоящей из оксидов иттрия, оксидов переходных металлов, имеющих атомный номер 41-79 и смесей этих оксидов.
4. Стеклокерамика по п. 1 или 2, которая включает менее 1,0, в частности, менее 0,5 масс.%, и, предпочтительно, менее 0,1 масс.% K2O.
5. Стеклокерамика по п. 1 или 2, которая включает менее 5,3, в частности, менее 5,1, предпочтительно, менее 4,0, особенно предпочтительно, менее 3,0 масс.% Al2O3 и, наиболее предпочтительно, является, по существу, свободной от Al2O3 или где мольное соотношение оксида одновалентного металла и Al2O3 составляет, по меньшей мере, 0,5 и, предпочтительно, 0,5-1,5.
6. Стеклокерамика по п. 1 или 2, которая включает менее 3,8, в частности, менее 3,6 и, предпочтительно, менее 2,5 масс.% ВаО.
7. Стеклокерамика по п. 1 или 2, которая включает в себя оксид одновалентного металла или смесь таковых в количестве 0,1-17,0, в частности, 1,0-15,0, и, предпочтительно, 1,5-8,0 масс.%.
8. Стеклокерамика по п. 1 или 2, которая содержит метасиликат лития в качестве основной кристаллической фазы и, в частности, содержит более 5 об.%, предпочтительно, более 10 об.% и, особенно предпочтительно, более 15 об.% кристаллов метасиликата лития.
9. Стеклокерамика по п. 1 или 2, которая содержит дисиликат лития в качестве основной кристаллической фазы и, в частности, содержит более 10 об.%, предпочтительно, более 20 об.% и, особенно предпочтительно, более 30 об.% кристаллов дисиликата лития.
10. Стеклокерамика по п. 1 или 2, которая включает в себя 55,0-85,0, в частности, 60,0-78,0 и, предпочтительно, 62,0-77,0 масс.% SiO2.
11. Стеклокерамика по п. 1 или 2, которая включает 9,0-20,0 и, в частности, 9,0-17,0, и, предпочтительно, 12,0-16,0 масс.% Li2O.
12. Стеклокерамика по п. 1 или 2, которая включает 0-12,0, в частности, 1,0-12,0, предпочтительно, 2,0-9,0, и, наиболее предпочтительно, 2,5-7,5 масс.% Р2О5.
13. Стеклокерамика по п. 1 или 2, которая включает K2O, Na2O и смеси таковых в количестве менее 1,0, в частности, менее 0,5 и, предпочтительно, менее 0,1 масс.%.
14. Стеклокерамика по п. 1 или 2, которая включает, по меньшей мере, один и, предпочтительно, все следующие компоненты:
Figure 00000001
Figure 00000002
15. Литиево-силикатная стеклокерамика по п. 1 или 2, которая включает дисиликат лития в качестве основной кристаллической фазы и обладает, в частности, вязкостью разрушения, измеренной как значение KIC, по меньшей мере, в 2,0 МПа·м0,5, и, в частности, по меньшей мере, примерно 2,3 МПа·м0,5.
16. Литиево-силикатная стеклокерамика по п. 1 или 2, в которой мольное соотношение между SiO2 и Li2O в находится между 2,2-2,6, в частности, 2,3-2,5 и, предпочтительно, примерно при 2,4.
17. Стеклокерамика по п. 1 или 2, при этом стеклокерамика присутствует в форме порошка, гранулята, заготовки или материала для реставрации зубов.
18. Исходное стекло, которое включает компоненты стеклокерамики по одному из пп. 1-7, 10-14 или 16.
19. Литиево-силикатное стекло с зародышами, которые являются пригодными для формирования кристаллов метасиликата лития и/или дисиликата лития, при этом стекло включает в себя компоненты стеклокерамики по одному из п.п. 1-7, 10-14 или 16.
20. Стекло по п. 18 или 19, при этом стеклокерамика присутствует в форме порошка, гранулята, заготовки или материала для реставрации зубов.
21. Способ изготовления стеклокерамики по одному из пп. 1-17, или стекла по п. 19 или 20, в котором исходное стекло по п. 18 или 20, стекло с зародышами по п. 19 или 20, или стеклокерамику с метасиликатом лития в качестве основной кристаллической фазы по пп. 8, 10-17, подвергают, по меньшей мере, одной термической обработке в диапазоне 450-950, в частности, 450-750, предпочтительно, 450-720 и, наиболее предпочтительно, 450-700°С.
22. Способ по п. 21, в котором
(a) исходное стекло подвергают термической обработке при температуре в 480-560°С для формирования стекла с зародышами, и
(b) стекло с зародышами подвергают термической обработке при температуре в 700-750°С для формирования стеклокерамики с дисиликатом лития в качестве основной кристаллической фазы.
23. Применение стеклокерамики по одному из пп. 1-17, или стекла по одному из п.п. 18-20 в качестве стоматологического материала и, в частности, для покрытия материалов для реставрации зубов и, предпочтительно, для изготовления материалов для реставрации зубов.
24. Применение для изготовления материалов для реставрации зубов по п. 23, в котором стеклокерамику или стекло формуют в желаемый материал для реставрации зубов, в частности, мост, вкладку, наружную вкладку, абатмент, винир, опорную коронку, коронку или гильзу.
RU2014119361A 2011-10-14 2012-10-11 Литиево-силикатные стеклокерамика и стекло с оксидом одновалентного металла RU2606999C2 (ru)