DD141428B1 - METHOD FOR PRODUCING A TWO-COMPONENT GAS RESIN - Google Patents
METHOD FOR PRODUCING A TWO-COMPONENT GAS RESINInfo
- Publication number
- DD141428B1 DD141428B1 DD141428B1 DD 141428 B1 DD141428 B1 DD 141428B1 DD 141428 B1 DD141428 B1 DD 141428B1
- Authority
- DD
- German Democratic Republic
- Prior art keywords
- resin
- epoxy resin
- producing
- graphite
- casting
- Prior art date
Description
Verfahren zum Herstellen eines ZweikomponentengießharzeeProcess for producing a two-component cast resin
Die Erfindung wird bei der Herstellung von kalthärtenden Zweikomponentengießharzen, insbesondere von Epoxidharzen, die Füllstoffe enthalten, wirksam, deren Anwendungsgebiet sowohl die Klebtechnik beim Verbinden von Teilen aus Metall oder anderen Werkstoffen miteinander, wie auch die Fertigung von insbesondere als Gleitlager oder Gleitführungen einsetzbaren Gießharzformkörpern sind, die entweder getrennt von oder im Verbund mit zugehörigen Bauteilen bzw. Maschinenelementen hergestellt werden können·The invention is effective in the production of cold-curing two-component casting resins, in particular epoxy resins containing fillers, whose field of application is both the bonding technique when joining parts made of metal or other materials with each other, as well as the production of cast resin molded articles which can be used in particular as slide bearings or sliding guides, which can be produced either separately from or in conjunction with associated components or machine elements
-2-210483-2-210483
Charakteristik der bekannten technischen Lösungen Es sind verschiedene Verfahren zum Herstellen von kalthärtenden Zweikomponentengießharzen auf der Basis von Epoxidharzen bekannt, denen Füllstoffe zugesetzt worden sind, um u.a. bestimmte technische Parameter bei dem ausgehärteten Gießharz werkst off oder Gießharzformkb'rper zu erzielen. Hierzu sind aus der Siebetechnik Beispiele bekannt, bei denen mittels Zugabe flüssiger Additiva zu Epoxidharz-Klebstoffen spezielle Eigenschaften der gefertigten Klebverbunde verbessert worden sind, Um die durch Siebung herzustellende Verbindung von Glas und keramischen Erzeugnissen zu verbessern, wird in der DJ)-PS 41 469 die Kombination von Epoxidharz mit , Sllanhaftmitteln angegeben. Weiterhin ist durch die DD-Ps 58 348 bekannt geworden, daß die Seewasserbeständigkeit von Epoxidharz-Metall-Verbindungen durch die Zugabe vom epoxidgruppen- bzw. aminogruppenhaltigen Silanhaftmitteln erhöht werden kann. Characteristic of known technical solutions Various methods are known for producing cold-curing two-component casting resins based on epoxy resins, to which fillers have been added in order, inter alia, to achieve certain technical parameters in the cured cast resin or casting resin moldings. For this purpose, examples of the sieving technique are known in which special properties of the finished adhesive composites have been improved by adding liquid additives to epoxy resin adhesives. In order to improve the connection of glass and ceramic products to be produced by screening, it is described in DJ) -PS 41 469 the combination of epoxy resin with silane coupling agents. Furthermore, it is known from DD-PS 58 348 that the seawater resistance of epoxy resin-metal compounds can be increased by the addition of epoxide groups or amino group-containing silane coupling agents.
Hach der DD-PS 123 672 ist es bekannt, daß die Empfindlichkeit der Epoxidharz-Klebstoffe gegenüber durch öle verschmutzten Klebflächen reduziert wird, wenn dem Klebstoff Polyaminoamid plus Silanhaftmittel zugesetzt werden. Ferner wird in der DD-PS 129 663 beschrieben, daß zur Verbesserung der Temperaturbeständigkeit von Klebverbindungen den hierzu verwendeten Epoxidharzklebstoffen Polyamlnoamid plus Aminaddukt plus Silanhaftmittel plus Benetzungsmittel zugemischt werden· Auf dem Gebiet der Herstellung von Lagerwerkstoffen ist es beispielsweise durch die DD-PS 50 390 bereits bekannt, für Lagerbuohsen Stoffzusammensetzungen zu verwenden, die aus kalt- oder heißhärtendem Epoxidharz, Kalt- bzw. Heißhärter, Molybdändlsolfid, Graphitpulver und Metallpulver in bestimmten anteiligen Verhältnissen bestehen.According to DD-PS 123 672, it is known that the sensitivity of the epoxy resin adhesives to oil-contaminated adhesive surfaces is reduced when polyaminoamide plus silane coupling agent is added to the adhesive. It is also described in DD-PS 129 663 that are mixed to improve the temperature resistance of adhesives used for this purpose Polyamlnoamid plus amine adduct plus silane coupling agent plus wetting agent · In the field of manufacturing bearing materials, it is for example by DD-PS 50 390 already Known to use for Lagerbuohsen composition compositions consisting of cold or hot curing epoxy resin, cold or hot hardener, Molybdändlsolfid, graphite powder and metal powder in certain proportionate proportions.
-3- 210483-3- 210483
Ein in der DD-PS 97 038 beschriebenes Verfahren sieht iA method described in DD-PS 97 038 sees i
dagegen vor, Epoxidharz, Härtungsmittel, Glaskugeln und !in contrast, epoxy resin, hardeners, glass beads and!
Gleitmittel, z.B. Graphit zu einer Mischung zu verarbeiten | und dann als Gleitschicht bei Gleitlagern, GleitbahnenLubricant, e.g. Graphite to process a mixture | and then as a sliding layer for plain bearings, slideways
und dgl. aufzubringen. Bei dem weiterhin bekannten, aus :and the like. In the still known, from:
der DD-PS 93. 612 entnehmbaren Verfahren, wird ein gieß- ' fähiger Pia st stoff zur Fertigung von Cleitbelägen ausDD-PS 93. 612 removable method, a pourable Pia is material for the production of Cleitbelägen
einem niedrigviskosen Epoxidharz hergestellt, das mit ja low viscosity epoxy resin prepared with j
Graphitpulver und Polyäthylenpulver modifiziert worden 'Graphite powder and polyethylene powder have been modified '
ist. ' !is. '!
Die Nachteile dieser bekannten Verfahren bestehen u.a. ! darin, daß die nach diesen hergestellten Zweikomponentengießharze im ausgehärteten Zustand Lunkerstellen in j Form von Lufteinschlüssen enthalten, welche beim Mischen j der zugehörigen Harzkomponenten and Füllstoffe bzw« ' Zusätze entstehen und lediglich durch einen z.B. im Vakuum [ durchzuführenden zusätzlichen Entgasungsprozeß verringert '< bzw. vermieden werden können. Derartige Lunker beein- ! trächtigen aber die Haltbarkeit der entsprechenden Kleb- ; stellen einerseits und die Funktionsfähigkeit der aus j diesen Zweikomponentengießharzen hergestellten Lager oder ] Gleitbeläge andererseits. Weiterhin besitzen die als j Klebstoffe vorgesehenen bekannten Zweikomponentengießharze ! zwar ein hohes Haftvermögen gegenüber metallischen Flächen, i auch wenn zuvor nicht vollständig von z.B. Ölresten diese 'The disadvantages of these known methods are, inter alia! that the Zweikomponentengießharze produced by these in the cured state include blowholes in j the form of air inclusions, which respectively during mixing j of the associated resin components and fillers "'additives are formed and reduced merely by an example in vacuum [carried out additional degassing'<or avoided can be. Such voids affect! but affect the durability of the corresponding adhesive; on the one hand and the functionality of the bearings made of j these two-component casting resins or] Gleitbeläge other hand. Furthermore, provided as j adhesives known Zweikomponentengießharze! Although a high adhesion to metallic surfaces, i even if not previously complete of eg oil residues this'
befreit worden sind. Sie sind aber nicht als Gleitbeläge ; have been liberated. But they are not as sliding coatings ;
von entsprechenden Lagerstellen oder Führungen einsetz- \ from appropriate bearings or guides use \
bar, weil ihnen die speziellen Funktionseigenschaften because of their special functional properties
eines Lagerwerkstoffes fehlen. Letztere sind dagegen zwar !of a bearing material missing. The latter are on the other hand!
bei den bisher als Lagerwerkstoffe eingesetzten, bekannten 'in the hitherto used as bearing materials, known '
Zweikomponentengießharzen, insbesondere kalthärtenden 'Two-component casting resins, in particular cold-curing '
Epoxidharzen vorhanden, es fehlt bei diesen dafür aber ; infolge ihres unzureichenden Haftvermögens an der Wider-Epoxy resins are present, but they are lacking; due to their insufficient ability to adhere to the
-4- 210483-4- 210483
Standsfähigkeit der Verbindungsstelle von Epoxidharz und Metallfläche gegenüber Scherkräften.Resilience of the junction of epoxy resin and metal surface to shear forces.
Die Erfindung hat die Herstellung eines kalthärtenden Zweikomponentengießharzes zum Ziel, aus dem mit möglichst geringem Fertigungsaufwand lunkerfreie Gießkörper gefertigt werden können, die auf Metallflächen ohne eine spezielle Vorbehandlung derselben durch einen Gießprozeß aufgebracht werden können, im ausgehärteten Zustand ohne zusätzliche Verbindungsmittel mit diesen Metallflächen < abscherfest verbunden sind und sowohl als Klebstoff beim Zusammenfügen von beispielsweise Metallteilen wie auch als Gleitbelag für Lagerstellen eingesetzt werden können·The invention has the production of a cold-curing Zweikomponentengießharzes the goal from which vandal-free casting bodies can be made with the lowest possible production costs, which can be applied to metal surfaces without a special pretreatment of the same by a casting process, connected in the cured state without additional connecting means with these metal surfaces <Shear and can be used both as an adhesive in the assembly of, for example, metal parts and as a sliding coating for bearings.
Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren zum Herstellen eines kalthärtenden Zweikomponentengießharzes, vorzugsweise eines Graphit als Füllstoff enthaltenden Epoxidharzes zu schaffen, das in seiner flüssigen Verarbeitungsphase eine geringe, ein Austreten von in dem Harz-Härter-Genri. sch enthaltenen Luftblasen zulassende Oberflächenspannung aufweist, mit metallischen Flächen ohne eine spezielle Vorbehandlung derselben eine Verbindung eingeht, die nach der Beendigung des Aushärteprozessee verhältnismäßig hohe Abscherkräfte aufnehmen kann und außerdem die Funktionseigenschaften eines Lagerwerkstoffes aufweist·The invention has for its object to provide a method for producing a cold-curing Zweikomponentengießharzes, preferably a graphite filler containing epoxy resin, which in its liquid processing phase a small, a leakage of resin in the Harri Genri. having air bubbles permitting surface tension, with metallic surfaces without a special pre-treatment of the same enters into a compound which can absorb relatively high shear forces after the completion of the curing process and also has the functional properties of a bearing material ·
Diese Aufgabe wurde durch die Entwicklung eines Verfahrens zum Herstellen eines Zweikomponentengisßharzes, insbesondereThis object has been achieved by the development of a process for producing a bicomponent molding resin, in particular
210483210483
kalthärtenden, Graphit, Molybdändisulfid oder andere Gleitwerkstoffe als Füllstoff enthaltenden Epoxidharzes gelöst, bei dem erfindungsgemäß der Harzkomponente außer den Füllstoffen ein epoxidgruppenhaltiges Silanhaftmittel und ein niedrigviskoses Silikonöl, beispielsweise Dimethyl-Silikonöl zugesetzt werden, wobei vorzugsweise ein Mischungsverhältnis von 63 % Epoxidharz, 10 % Verdünnungsmittel, 2 % Silanhaftmittel, 1 % Silikonöl und 24 % Graphit eingehalten wird, wonach die Härterkomponente zugesetzt wird.cold-hardening, graphite, molybdenum disulfide or other sliding materials containing epoxy resin as filler, are added to the resin component except the fillers, an epoxide silane coupling agent and a low viscosity silicone oil, for example dimethyl silicone oil, preferably a mixing ratio of 63 % epoxy resin, 10 % diluent, 2 % Silanhaftmittel, 1 % silicone oil and 24 % graphite is maintained, after which the hardener component is added.
Durch die nach dem erfindungsgemäßen Verfahren vorgesehene Kombination von einem Silikonöl mit einem Silanhaftmittel in einem Gießharz auf der Basis kalthärtender Epoxidharze ergeben sich Vorteile, die eich sowohl beim Einsatz derselben auf dem Gebiet der Klebtechnik wie auch auf dem der Lagerwerkstoffe auswirken. Diese Vorteile ergeben sich einerseits dadurch, daß das Silikonöl die Oberflächenspannung des flüssigen Gießharzgemischeθ derart herabsetzt, daß. in der Verarbeitungsphase des Gießens die Fließfähigkeit wesentlich verbessert wird und eingeschlossene Luftblasen nahezu ungehindert entweichen können» Hierdurch wird das Auftreten von Lunkerstellen in dem ausgehärteten Gießharzwerkstoff vermieden und ein vorrichtungsmäßig aufwendiger Entgasungsprozeß überflüssig. Andererseits wird durch den Gehalt an Silikonöl bei gleichzeitiger Anwesenheit von epoxidgruppenhaltigem Silanhaftmittel die Grundfestigkeit des Verbundes Epoxidharzwerkstoff/Metall bzw. Gleitbelag/Metall gegenüber Scherbeanspruchungen vergrößert und die Dauerbeständigkeit des Haftverbundes gegenüber Wasser um 50 % erhöht.The combination of a silicone oil with a silane coupling agent in a casting resin based on cold-curing epoxy resins provided by the process according to the invention affords advantages which have an effect both in the use of the same in the field of adhesive bonding and on the bearing materials. These advantages arise on the one hand in that the silicone oil reduces the surface tension of the liquid Gießharzgemischeθ such that. in the processing phase of the casting, the flowability is significantly improved and trapped air bubbles can escape almost unhindered »This avoids the occurrence of voids in the cured Gießharzwerkstoff and a device-consuming degassing process superfluous. On the other hand, by the content of silicone oil in the simultaneous presence of silane adhesive containing epoxide groups, the basic strength of the composite epoxy / metal or sliding / metal compared to shear stresses increased and increases the durability of the adhesive to water by 50 % .
210483210483
Die Erfindung wird nachstehend an einem Ausführungsbeispiel erläutert»The invention will be explained below using an exemplary embodiment »
Einer Harzkomponente, die zu 63 % aus Epoxidharz be-, steht, werden 10 % Verdünnungsmittel, beispielsweise Glycidäther, 2 % Silanhaftmittel, 1 % Silikonöl, z.B. DimethylaLlikonöl und 24 % Graphitpulver zugesetzt. Nachdem diese Stoffe miteinander zu einem Gemisch verarbeitet worden sind, wird eine Härterkomponente zugesetzt, die zu 100 % aus Amin-Addukt besteht. Hieraus wird durch einen weiteren Mischvorgang ein fließfähiges Gießharz, aus dem eingeschlossene Luftblasen sofort entweichen können und das entweder auf die Klebflächen von miteinander zu verbindenden Teilen aus Metall oder anderen Werkstoffen oder auf mit einem Gleitbelag zu versehende Gleitlager, Paßflächen oder Gleit- bzwTo a resin component consisting of 63 % epoxy resin is added 10 % diluent, for example, glycidyl ether, 2 % silane coupling agent, 1 % silicone oil, eg dimethylalcohol oil and 24 % graphite powder. After these substances have been processed together to form a mixture, a hardener component is added which consists of 100 % of amine adduct. From this, a flowable casting resin, from the trapped air bubbles can escape immediately and either on the adhesive surfaces of parts to be joined together made of metal or other materials or on a sliding surface to be provided with plain bearings, mating surfaces or sliding or
Führungsbannen im Gießvorgang aufgebracht wird. Nach Beendigung des nun folgenden Auehärtevorganges kann der fertige Gießharzwerkstoff die vorgesehenen Punktionen übernehmen. Führungsbannen is applied in the casting process. After completion of the now following Auehärtevorganges the finished resin material can take over the intended punctures.
Claims (1)
Family
ID=