CN1188786A - 改性多元接枝氯丁胶粘剂 - Google Patents
改性多元接枝氯丁胶粘剂 Download PDFInfo
- Publication number
- CN1188786A CN1188786A CN97105646A CN97105646A CN1188786A CN 1188786 A CN1188786 A CN 1188786A CN 97105646 A CN97105646 A CN 97105646A CN 97105646 A CN97105646 A CN 97105646A CN 1188786 A CN1188786 A CN 1188786A
- Authority
- CN
- China
- Prior art keywords
- multielement
- modified
- neoprene adhesive
- reaction
- rev
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种改性多元接枝氯丁胶粘剂。其主要成分及配比是甲苯60—70份、丁酮7—9份、乙酸乙酯6—9份、MMA7—9份、A—9011—14份、CPP1—3份。其制备过程是将上述成分按配比混合,在常温下溶解,加热至一定温度再加入引发剂使其反应,反应结束后再加入抗氧剂、阻聚剂等辅助成分,充分搅拌混合后即成。本发明适用于皮鞋、旅游鞋、运动鞋等有关皮革类鞋的粘合。
Description
本发明涉及鞋用接枝氯丁胶粘剂的改性，具体地说是一种改性多元接枝氯丁胶粘剂，适用于皮鞋、旅游鞋、运动鞋生产业方面的粘合。
目前在皮鞋、旅游鞋、运动鞋的生产中所使用的胶粘剂多为CR与MMA二元接枝共聚物，即目前应用的接枝氯丁胶。它较好地解决了具有高表面能PVC、PU材料的胶接，但具有质量不稳定，固体含量低、贮存时粘度变化大等缺点，不能适用于制鞋业发展的要求。近几年不少生产、科研单位也试制了CPE-CR-MMA、CR-MMA-AA等多种接枝品种，但仍不能解决上述问题。
本发明的目的是提供一种不仅对高表面能PVC、PU等极性材料具有较好的粘接强度，而且对低表面能TPR、EVA、PE等材料也具有较高的粘接强度，同时还具有颜色浅，初粘力显著提高，贮存稳定性大大延长等优点的多用途高档鞋用胶粘剂。
本发明是这样实现的：首先将甲苯、丁酮、乙酸乙酯、A-90、MMA、CPP混合溶解，再加入引发剂BPO使其反应，反应结束后，再加入抗氧剂264、紫外线吸收剂UV-531、阻聚剂对羟基苯甲醚、2402树脂混合而成。其主要成分具体配方是：甲苯60-70份、丁酮7-9份、乙酸乙脂6-9份、MMA7-9份、A-90 11-14份、CPP1-3份。其工艺分三个阶段，一是常温快速搅拌溶解：将上述物料在常温下加入反应釜，开动搅拌溶解，搅拌速度控制在100-140转/分。二是升温低速搅拌反应：将上述溶解好的溶液在反应釜内升温，搅拌速度控制在20-60转/分，料温升至60-80℃，加入少量引发剂BPO，反应开始，停止加热(反应为放热反应)，料温升至70-90℃时，保温2.5-3小时，料液粘度增加，当粘度达到1300-1400mPa.s时，可视为反应结束。三是快速搅拌降温：通冷却水，搅拌速度控制在100-140转/分，加入配好的抗氧剂264，料温降至30℃时，再加入紫外线吸收剂UV-531，阻聚剂对羟基苯甲醚和粉碎好的2402树脂。待树脂完全溶解，混合均匀，成为色浅、透明的均匀粘液，即可成为改性多元接枝氮丁胶粘剂。
本发明的优点是：由于在接技氯丁胶上又加接了CPP，因而形成的改性多元接枝氯丁胶粘剂比现有的接枝氯丁胶粘剂色浅，初粘性好、固体含量高、粘接强度高、不污染制鞋材料，性能稳定，使用范围广，可适用于高档制鞋业。
实施例1：取甲苯450g、丁酮60g、乙酸乙酯50g、A-90 90g、MMA57g、CPP13g，投入反应釜，开动搅拌溶解，搅拌速度100转/分，溶好后升温至60℃，加入BPO0.3g，进行接枝反应，搅拌速度20转/分，温度升至70℃保温2.5小时，粘度达到1300mPa.s反应完毕。通冷水降温，依次加入2642.4g、UV-531 0.33g、阻聚剂0.24g、2402树脂15g，待树脂溶解后，搅拌均匀即成。
实施例2：取甲苯450g、丁酮60g、乙酸乙酯50g、A-90、90g、MMA60g、CPP10g，投入反应釜，开动搅拌溶解，转速130转1分。溶好后升温至70℃，加入BPO0.3g，进行接枝反应，搅拌速度40转/分，料温升至80℃保温3小时，粘度达1350mPa.s反应结束。通冷却水降温，搅拌速度130转/分，依次加入264 2.4g、UV-531 0.33g、阻聚剂0.24g、2402树脂15g，待树脂溶好后，搅拌均匀即成。
实施例3：取甲苯450g、丁酮60g、乙酸乙酯50g、A-90 90g、MMA62g、CPP8g，投入反应釜，开动搅拌溶解，搅拌速度140转/分。溶好后升温至80℃加入BPO0.3g，进行接枝反应，搅拌速度60转/分，温度升到90℃时保温3小时，粘度达1400mPa.s反应完毕，通冷却水降温，搅拌速度140转/分。依次加入264 2.4g、UV-531 0.33g、阻聚剂0.24g、2402树脂15g，待树脂溶好后，搅拌均匀即成。
Claims (4)
1、一种改性多元接枝氯丁胶粘剂，主要用甲苯、丁酮、乙酸乙酯、A-90、MMA等成分混合反应而成。其特征在于首先将甲苯、丁硐、乙酸乙酯、A-90、MMA、CPP混合溶解，然后加入引发剂BPO使其反应，反应结束后再加入抗氧剂264、紫外线吸收剂UV-531、阻聚剂对羟基苯甲醚和粉碎好的2402树脂混合而成。
2、根据权利要求1所述的改性多元接枝氯丁胶粘剂，其特征在于其主要原料配比：甲苯60-70份、丁酮7-9份、乙酸乙酯6-9份、A-90 11-14份、MMA7-9份、CPP1-3份。
3、根据权利要求1所述的改性多元接枝氯丁胶粘剂，其特征在于常温下溶解、搅拌时搅拌速度100-140转/分，升温反应时搅拌速度20-60转/分，降温搅拌时转速100-140转/分。
4、根据权利要求1所述的改性多元接枝氯丁胶粘剂，其特征在于：加引发剂BPO时料温控制在60-80℃，反应时料温控制在70-90℃。