CN110200146A - One kind licking brick quality improver and preparation method thereof - Google Patents
One kind licking brick quality improver and preparation method thereof Download PDFInfo
- Publication number
- CN110200146A CN110200146A CN201910602103.8A CN201910602103A CN110200146A CN 110200146 A CN110200146 A CN 110200146A CN 201910602103 A CN201910602103 A CN 201910602103A CN 110200146 A CN110200146 A CN 110200146A
- Authority
- CN
- China
- Prior art keywords
- attapulgite
- content
- concave
- quality improver
- stone powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of mixed feeds, are related to one kind and lick brick quality improver, have further related to a kind of preparation method for licking brick quality improver, and attapulgite enters agitating procedure after detection is qualified by sunning or the drying of hot-blast stove；Polyethylene glycol oxide 20, cellulose, lignosulfonates, sorbierite liver fatty acid ester are added in attapulgite after the drying, so that carrying out filters pressing after the standby acidification completely of attapulgite；Attapulgite after filters pressing crush to roller, and is stood in feed bin, for persistently reducing moisture, the attapulgite after standing is milled after the assay was approved；Attapulgite after milling is filtered；And review agent for fixing, agar are weighed simultaneously, it is pre-mixed with attapulgite, incorporation time is 0.5-2 hours, so that concave and convex rod stone powder is uniformly mixed with additive.Advantage is: having the characteristics that stronger caking property, is not easy the moisture absorption, facilitate the molding for licking brick, improves the resistance to dissolubility in water；Increase caking property, enhances hardness.
Description
Technical field
The present invention relates to a kind of feed improvers, are related to one kind and lick brick quality improver, have further related to one kind and have licked brick use
Quality improving agent and preparation method thereof.
Background technique
Licking brick with quality improver is the inorganic gel formed by carrier of modified attapulgite clay, mainly for ruminating
Animal.Concave-convex clay rod refers to a kind of clay mineral using attapulgite as main component.Attapulgite is a kind of crystalloid water
Alumina magnesia silicate is closed, there is unique layer chain structure feature, there is crystal lattice in its structure, helps to contain in crystal
Variable amount of Na+, Ca2+, Fe3+, Al3+, crystal is in needle-shaped, threadiness or fiber set shape.Attapulgite has unique point
Good colloidal nature and the higher adsorption bleaching abilities such as scattered, high temperature resistant, salt resistance alkali, and there is certain plasticity and bonding
Power is widely used in the fields such as petroleum, chemical industry, building materials, papermaking, medicine, agricultural.In agriculture field, attapulgite can be used as feeding
Material or feed addictive use, and can directly feed, can also process in feed, yellow bent due to existing in the raw material of feed
Mould toxin, zearalenone and vomitoxin, animal, which is critical, will appear problem, unhealthful.And the existing similar product in market
The shortcomings that there are the easy moisture absorptions.
Therefore, it is necessary to seek the new technology of one kind to solve the above problems.
Summary of the invention
The purpose of the present invention is: in view of the above deficiencies, one kind is provided and licks brick quality improver and preparation method thereof.
In order to achieve the above objectives, the technical solution adopted by the present invention is that:
One kind licking brick quality improver, this power helps element and includes following ingredient, and the mass parts of each ingredient are as follows: attapulgite
Content 80-90, the content 2-5 of polyethylene glycol oxide 20, agent for fixing content be content 1-4, the fibre of 2-6, lignosulfonates
Tie up the content 2-6 of the content 2-6 of element, the content 1-4 of agar, sorbierite liver fatty acid ester.
The agent for fixing is one or more of sodium alginate, alphalise starch, sodium carboxymethylcellulose, Sodium Polyacrylate.
The cellulose is one or more of sodium silicoaluminate, aluminum oxide, silica.
A kind of preparation method for licking brick quality improver, including following preparation step: step 1: attapulgite is by drying in the air
It shines or the drying of hot-blast stove, moisture is reduced to 12 hereinafter, entering agitating procedure after detection is qualified；
Step 2: polyethylene glycol oxide 20, cellulose, lignosulfonates, sorb are added in attapulgite after the drying
Alcohol liver fatty acid ester stirs 1-4 hour, so that carrying out filters pressing after the standby acidification completely of attapulgite；
Step 3: the attapulgite after filters pressing crush to roller, and is dried to moisture content at a high temperature of 85 DEG C again
For 10 hereinafter, and stood in feed bin, for persistently reducing moisture, the attapulgite after standing is ground after the assay was approved
Powder；
Step 4: the attapulgite after milling is filtered, so that concave and convex rod stone powder is by the quantity of 80 mesh screens
80% or more, verification semi-finished product step can be entered；
Step 5: carrying out weighing review for concave and convex rod stone powder, and weighs review agent for fixing, agar simultaneously, with concave convex rod
Stone is pre-mixed, and incorporation time is 0.5-2 hours, so that concave and convex rod stone powder is uniformly mixed with additive；
Step 6: moving to mixing machine for the material of premixing and mix, and incorporation time is 0.5-2 hours, guarantees concave-convex
Stick stone powder is uniformly mixed with additive；
Step 7: after verifying, concave and convex rod stone powder is finished product, carries out packing box storage to it.
Compared with prior art, the present invention feed achieved for having the technical effect that 1, this product can to aflatoxin,
Zearalenone and vomitoxin have suction-operated；2, this product has the characteristics that stronger caking property, is not easy the moisture absorption, has
Help lick the molding of brick, improves the resistance to dissolubility in water；3, increase caking property, enhance hardness.
Specific embodiment
One kind licking brick quality improver, this power helps element and includes following ingredient, and the mass parts of each ingredient are as follows: attapulgite
Content 80-90, specific in an embodiment of the present invention is 80,85,90；
The content 2-5 of polyethylene glycol oxide 20 is specifically 2,4,5 in the embodiment of the present invention couple；
Agent for fixing is one or more of sodium alginate, alphalise starch, sodium carboxymethylcellulose, Sodium Polyacrylate, in reality
Applying in example is specifically sodium alginate, alphalise starch, sodium carboxymethylcellulose, and content is 2-6, and corresponding content is 2,4,6；
The content 1-4 of lignosulfonates, specific in embodiment is 1,2,4；
Cellulose be one or more of sodium silicoaluminate, aluminum oxide, silica, in embodiment and specifically
For sodium silicoaluminate, aluminum oxide and silica, content 2-6, corresponding in embodiment is respectively 2,4,6；
The content 1-4 of agar, specific in embodiment is 1,2,4；
The content 2-6 of sorbierite liver fatty acid ester, specific in embodiment is 2,4,6.
A kind of preparation method for licking brick quality improver, including following preparation step: step 1: attapulgite is by drying in the air
It shines or the drying of hot-blast stove, moisture is reduced to 12 hereinafter, entering agitating procedure after detection is qualified；
Step 2: polyethylene glycol oxide 20, cellulose, lignosulfonates, sorb are added in attapulgite after the drying
Alcohol liver fatty acid ester stirs 1-4 hour, so that carrying out filters pressing after the standby acidification completely of attapulgite；
Step 3: the attapulgite after filters pressing crush to roller, and is dried to moisture content at a high temperature of 85 DEG C again
For 10 hereinafter, and stood in feed bin, for persistently reducing moisture, the attapulgite after standing is ground after the assay was approved
Powder；
Step 4: the attapulgite after milling is filtered, so that concave and convex rod stone powder is by the quantity of 80 mesh screens
80% or more, verification semi-finished product step can be entered；
Step 5: carrying out weighing review for concave and convex rod stone powder, and weighs review agent for fixing, agar simultaneously, with concave convex rod
Stone is pre-mixed, and incorporation time is 0.5-2 hours, so that concave and convex rod stone powder is uniformly mixed with additive；
Step 6: moving to mixing machine for the material of premixing and mix, and incorporation time is 0.5-2 hours, guarantees concave-convex
Stick stone powder is uniformly mixed with additive；
Step 7: after verifying, concave and convex rod stone powder is finished product, carries out packing box storage to it.
Compared with prior art, the present invention feed achieved for having the technical effect that 1, this product can to aflatoxin,
Zearalenone and vomitoxin have suction-operated；2, this product has the characteristics that stronger caking property, is not easy the moisture absorption, has
Help lick the molding of brick, improves the resistance to dissolubility in water；3, increase caking property, enhance hardness.
Below by specific embodiment the technical scheme of the present invention will be further described explanation, but the present invention is not limited to
Following embodiment:
Embodiment one:
A kind of preparation method for licking brick quality improver, including following preparation step: step 1: by the recessed of 80 mass parts
Moisture is reduced to 12 hereinafter, entering agitating procedure after detection is qualified by sunning or the drying of hot-blast stove by convex stick stone；
Step 2: the polyethylene glycol oxide 20 of 2 mass parts, the aluminosilicate of 2 mass parts are added in attapulgite after the drying
Sodium, the lignosulfonates of 1 mass parts, 2 mass parts sorbierite liver fatty acid ester, 2 hours are stirred, so that attapulgite is standby
Filters pressing is carried out after acidification completely；
Step 3: the attapulgite after filters pressing crush to roller, and is dried to moisture content at a high temperature of 85 DEG C again
For 10 hereinafter, and stood in feed bin, for persistently reducing moisture, the attapulgite after standing is ground after the assay was approved
Powder；
Step 4: the attapulgite after milling is filtered, so that concave and convex rod stone powder is by the quantity of 80 mesh screens
80% or more, verification semi-finished product step can be entered；
Step 5: carrying out weighing review for concave and convex rod stone powder, and weighs the sodium alginate of 2 mass parts of review, 1 matter simultaneously
The agar for measuring part, is pre-mixed with attapulgite, and incorporation time is 0.5 hour, so that concave and convex rod stone powder and additive are mixed
It closes uniform；
Step 6: moving to mixing machine for the material of premixing and mix, and incorporation time is 0.5 hour, guarantees concave convex rod
Stone powder is uniformly mixed with additive；
Step 7: after verifying, concave and convex rod stone powder is finished product, carries out packing box storage to it.
Embodiment two:
A kind of preparation method for licking brick quality improver, including following preparation step: step 1: by the recessed of 85 mass parts
Moisture is reduced to 12 hereinafter, entering agitating procedure after detection is qualified by sunning or the drying of hot-blast stove by convex stick stone；
Step 2: the polyethylene glycol oxide 20 of 4 mass parts, three oxidations of 4 mass parts are added in attapulgite after the drying
Two aluminium, the lignosulfonates of 2 mass parts, 4 mass parts sorbierite liver fatty acid ester, 3 hours are stirred, so that attapulgite
Filters pressing is carried out after standby acidification completely；
Step 3: the attapulgite after filters pressing crush to roller, and is dried to moisture content at a high temperature of 85 DEG C again
For 10 hereinafter, and stood in feed bin, for persistently reducing moisture, the attapulgite after standing is ground after the assay was approved
Powder；
Step 4: the attapulgite after milling is filtered, so that concave and convex rod stone powder is by the quantity of 80 mesh screens
80% or more, verification semi-finished product step can be entered；
Step 5: carrying out weighing review for concave and convex rod stone powder, and weighs the alphalise starch of 4 mass parts of review, 2 mass simultaneously
The agar of part, is pre-mixed with attapulgite, and incorporation time is 1 hour, so that concave and convex rod stone powder mixes with additive
It is even；
Step 6: moving to mixing machine for the material of premixing and mix, and incorporation time is 1 hour, guarantees attapulgite
Powder is uniformly mixed with additive；
Step 7: after verifying, concave and convex rod stone powder is finished product, carries out packing box storage to it.
Embodiment three:
A kind of preparation method for licking brick quality improver, including following preparation step: step 1: by the recessed of 90 mass parts
Moisture is reduced to 12 hereinafter, entering agitating procedure after detection is qualified by sunning or the drying of hot-blast stove by convex stick stone；
Step 2: the polyethylene glycol oxide 20 of 5 mass parts, the titanium dioxide of 6 mass parts are added in attapulgite after the drying
Silicon, the lignosulfonates of 4 mass parts, 6 mass parts sorbierite liver fatty acid ester, 4 hours are stirred, so that attapulgite is standby
Filters pressing is carried out after acidification completely；
Step 3: the attapulgite after filters pressing crush to roller, and is dried to moisture content at a high temperature of 85 DEG C again
For 10 hereinafter, and stood in feed bin, for persistently reducing moisture, the attapulgite after standing is ground after the assay was approved
Powder；
Step 4: the attapulgite after milling is filtered, so that concave and convex rod stone powder is by the quantity of 80 mesh screens
80% or more, verification semi-finished product step can be entered；
Step 5: carrying out weighing review for concave and convex rod stone powder, and weighs the carboxymethyl cellulose of 6 mass parts of review simultaneously
The agar of sodium, 4 mass parts, is pre-mixed with attapulgite, and incorporation time is 2 hours, so that concave and convex rod stone powder and addition
Agent is uniformly mixed；
Step 6: moving to mixing machine for the material of premixing and mix, and incorporation time is 2 hours, guarantees attapulgite
Powder is uniformly mixed with additive；
Step 7: after verifying, concave and convex rod stone powder is finished product, carries out packing box storage to it.
Example IV:
Gained is licked to the water-soluble experimental data, hardness test data and toxin adsorption rate test data such as table of brick feed
Shown in 1:
Table 1: water solubility, hardness and the toxin adsorption rate data of addition feed quality improver
According to table content, it is found that the water solubility for licking brick quality improver is shown in the table, needs at least 28 hours
Just start to dissolve；
And in experiment of hardness, with the recommendation of time, within 1-15 days, hardness guarantees 30 or more；
And in the experiment of toxin adsorption rate, over time, within 1-15 days, guarantee the adsorption rate of toxin 81 with
On.
In conclusion the feed of this product can have absorption to make aflatoxin, zearalenone and vomitoxin
With；This product has the characteristics that stronger caking property, is not easy the moisture absorption, facilitates the molding for licking brick, improves the resistance to dissolubility in water；Increase
Add caking property, enhances hardness.
The above embodiments merely illustrate the technical concept and features of the present invention, and its object is to allow person skilled in the art
Scholar cans understand the content of the present invention and implement it accordingly, and it is not intended to limit the scope of the present invention.It is all according to the present invention
Equivalent change or modification made by Spirit Essence, should be covered by the protection scope of the present invention.
Claims (4)
1. one kind licks brick quality improver, it is characterised in that: this power helps element and includes following ingredient, and the mass parts of each ingredient
Are as follows: the content 80-90 of attapulgite, the content 2-5 of polyethylene glycol oxide 20, agent for fixing content be 2-6, lignosulfonates
Content 1-4, the content 2-6 of cellulose, the content 1-4 of agar, sorbierite liver fatty acid ester content 2-6.
2. one kind according to claim 1 licks brick quality improver, it is characterised in that: the agent for fixing is alginic acid
One or more of sodium, alphalise starch, sodium carboxymethylcellulose, Sodium Polyacrylate.
3. one kind according to claim 1 licks brick quality improver, it is characterised in that: the cellulose is aluminosilicate
One or more of sodium, aluminum oxide, silica.
4. a kind of preparation method for licking brick quality improver, it is characterised in that: including following preparation step:
Step 1: moisture is reduced to 12 hereinafter, entering after detection is qualified by sunning or the drying of hot-blast stove by attapulgite
Agitating procedure；
Step 2: polyethylene glycol oxide 20, cellulose, lignosulfonates, sorbierite liver are added in attapulgite after the drying
Aliphatic ester stirs 1-4 hour, so that carrying out filters pressing after the standby acidification completely of attapulgite；
Step 3: the attapulgite after filters pressing crush to roller, and being dried to moisture content at a high temperature of 85 DEG C again is 10
Hereinafter, and stood in feed bin, for persistently reducing moisture, the attapulgite after standing is milled after the assay was approved；
Step 4: the attapulgite after milling is filtered, so that the quantity that concave and convex rod stone powder passes through 80 mesh screens is 80%
More than, verification semi-finished product step can be entered；
Step 5: carrying out weighing review for concave and convex rod stone powder, and simultaneously weigh review agent for fixing, agar, with attapulgite into
Row premixing, incorporation time is 0.5-2 hours, so that concave and convex rod stone powder is uniformly mixed with additive；
Step 6: moving to mixing machine for the material of premixing and mix, and incorporation time is 0.5-2 hours, guarantees attapulgite
Powder is uniformly mixed with additive；
Step 7: after verifying, concave and convex rod stone powder is finished product, carries out packing box storage to it.