CN109881084A - Strip cast-rolled 550 MPa-grade weathering steel and production method thereof - Google Patents
Strip cast-rolled 550 MPa-grade weathering steel and production method thereof Download PDFInfo
- Publication number
- CN109881084A CN109881084A CN201810587494.6A CN201810587494A CN109881084A CN 109881084 A CN109881084 A CN 109881084A CN 201810587494 A CN201810587494 A CN 201810587494A CN 109881084 A CN109881084 A CN 109881084A
- Authority
- CN
- China
- Prior art keywords
- strip
- continuous casting
- production method
- percent
- steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A550 MPa-level weathering steel for strip continuous casting and a production method thereof are disclosed, the production method comprises the following steps: 1) smelting, wherein the molten steel comprises the following chemical components: 0.03 percent of C, 0.20 to 0.80 percent of Si, 1.0 percent of Mn, 0.03 to 1.50 percent of P, less than or equal to 0.008 percent of S, less than or equal to 0.008 percent of N, 0.40 to 1.50 percent of Cu, 0.50 to 1.50 percent of Cr, 0.10 percent of Ni, 0.05 to 0.20 percent of Nb, and the balance of Fe and inevitable impurities; 2) continuously casting thin strips, namely continuously casting the qualified smelted molten steel into casting strips with the thickness of 1.4-2.5mm by a pair of copper casting rolls rotating in opposite directions, wherein the superheat degree of the molten steel is controlled below 80 ℃; 3) carrying out online hot rolling on the cast strip, wherein the hot rolling reduction is 15-65%, and the temperature of the rolled strip steel is 950-; 4) cooling and coiling, wherein the hot rolled strip steel is cooled to 450-600 ℃ through gas spray to obtain uniform and fine ferrite and a small amount of pearlite structures. The 550 MPa-grade weathering steel has the characteristics of short production flow, low production cost, good strip steel plate shape and easiness in welding.
Description
Technical field
The invention belongs to Hi-Stren steel manufacturing field, more particularly to a kind of low cost, short route, easily welding,
High durable, high-intensitive weathering steel strip and its production method.
Background technique
Weathering steel has characteristics and the significant advantages such as green, environmental protection, longevity, is applicable not only to a variety of weathers and environment, and
And had both the performances such as high intensity, high tenacity, solderable, fire resisting, wear-resisting, be widely used in making case tank, vehicle, building,
The all trades and professions such as bridge, pipeline, machinery.
Currently, the 550MPa grade weathering steel produced both at home and abroad, mostly uses Nb, V, Ti, Mo combined microalloying technology, lead to
Refined crystalline strengthening and precipitation strength are crossed to improve the comprehensive mechanical property of weathering steel.
Patent document CN20021011858.6 discloses a kind of weathering steel of the yield strength greater than 550MPa, passes through addition
The intensity of the elements such as Mn, Ti, Nb, V, Mo raising weathering steel.Patent document CN200910301054.0 discloses a kind of 550MPa
The manufacturing method of grade weathering steel strengthens the power of weathering steel by adding the alloying elements such as the Ni of high-content, and addition Nb, V, Ti
Learn performance.Above two production method is all made of traditional hot continuous rolling process production, the finger gauge of usual weathering steel produced
Lattice produce 2mm high-strength weather-proof steel product below and there is very big difficulty in 2mm or more.It is produced in traditional hot continuous rolling
In high-strength weathering steel, be frequently present of following problems: process flow is long, energy consumption is high, unit equipment is more, capital construction is at high cost, production
Overall cost is high；During slab CC machine, it is be easy to cause the segregation of the elements such as P, Cu, leads to each of slab and hot-strip
Anisotropy and macroscopic cracking etc., so that lumber recovery is low；In heating of plate blank and course of hot rolling, it be easy to cause Cu element in slab
Surface, which is in a liquid state, to be distributed and penetrates into crystal boundary, is formed hot-short crackle during the rolling process, is seriously affected the surface matter of hot-strip
Amount and cold-bending property etc.；Overall reduction is big in the hot rolling for high-strength weathering steel, and hot-rolling draught pressure is big, traditional hot continuous rolling
Machine produces high-intensitive thin gauge weathering steel, and there are bigger difficulty, and in addition the plate shape of thin gauge weathering steel is also difficult to control.
A kind of production method of 550MPa grades of weathering steels according to the present invention, using sheet-band continuous casting and rolling technique, significantly
Production procedure is shortened, production cost is reduced, reduces element segregation, avoids hot-short defect, ensure that the resistance to of weathering steel
Performance is waited, and improves the welding performance of weathering steel by the design of low C ingredient, in addition, being mentioned by Nb element solid solution strengthening mechanism
The high intensity of weathering steel, also avoids the conventional problem added V, Mo element and cause welding performance low.
Summary of the invention
The center segregation of casting blank that is easy to appear for existing 550MPa grades of weathering steel, surface quality be poor, thin gauge production
Long flow path, high production cost, production efficiency is low, the control of thin slab product plate shape difficulty, the problems such as welding performance is poor, the present invention provides
A kind of novel weathering steel and its production method, it is therefore an objective to shorten the production procedure of weathering steel, reduce production cost, improve thin rule
The production efficiency of lattice weathering steel, improves weathering steel welding performance at the plate shape for improving thin gauge strip.
To achieve the goals above, on the one hand, the invention discloses a kind of productions of thin strap continuous casting 550MPa grades of weathering steels
Method follows the steps below:
1) it smelts
Ladle chemistry are as follows: C < 0.03%, Si:0.20-0.80%, Mn < 1.0%, P:0.03-1.50%, S≤
0.008%, N≤0.008%, Cu:0.40-1.50%, Cr:0.50-1.50%, Ni < 0.10%, Nb:0.05-0.20%,
Remaining is Fe and inevitable impurity；
2) thin strap continuous casting
Qualified molten steel will be smelted and be casting continuously to form Cast Strip by the casting in bronze roller of a pair of of opposite direction rotating；
3) the online hot rolling in Cast Strip
By 1 passage hot rolling at Thin Strip Steel, it is 950-1050 DEG C that strip, which rolls rear temperature, for Cast Strip；
4) it cools down and batches
Hot-strip is cooled to 450-600 DEG C by aerosol, and batches coiled.
A kind of production method of thin strap continuous casting 550MPa grades of weathering steels according to the present invention, it is preferable that in the step 2),
Cast Strip is with a thickness of 1.4-2.5mm.
A kind of production method of thin strap continuous casting 550MPa grades of weathering steels according to the present invention, it is preferable that in the step 2),
Degree of superheat when molten steel continuous casting is controlled at 80 DEG C or less.
A kind of production method of thin strap continuous casting 550MPa grades of weathering steels according to the present invention, it is preferable that in the step 3),
Drafts of the Cast Strip Jing Guo hot-rolling mill hot rolling is 15-65%.
A kind of production method of thin strap continuous casting 550MPa grades of weathering steels according to the present invention, it is preferable that in the step 3),
Cast Strip is by hot rolling formation hot rolling thin strip with a thickness of 0.6-1.9mm.
A kind of production method of thin strap continuous casting 550MPa grades of weathering steels according to the present invention, it is preferable that in the step 3),
The width of hot-strip is 600-1500mm.
A kind of production method of thin strap continuous casting 550MPa grades of weathering steels according to the present invention, it is preferable that in the step 4),
The yield strength of Thin Strip Steel is in 550MPa or more, and tensile strength is in 650MPa or more, and elongation percentage is 22% or more.
A kind of production method of thin strap continuous casting 550MPa grades of weathering steels according to the present invention, it is preferable that in the step 4),
The microstructure of strip is uniformly tiny ferrite and a small amount of pearlite.
To achieve the goals above, on the other hand, the invention also discloses a kind of thin strap continuous casting 550MPa grades of weathering steels,
It is produced using a kind of production method of thin strap continuous casting 550MPa grades of weathering steels above-mentioned.
A kind of thin strap continuous casting 550MPa grades of weathering steel strips according to the present invention, it is preferable that the yield strength of Thin Strip Steel exists
550MPa or more, tensile strength is in 650MPa or more, and for elongation percentage 22% or more, the microstructure of strip is uniformly tiny iron
Ferritic and a small amount of pearlite.
Beneficial technical effect
Compared with prior art, the features of the present invention and beneficial effect include at least:
(1) C content in weathering steel is reduced, ensure that the surface quality of Cast Strip and hot rolling thin strip, ensure that resistance to
Wait the bending property of steel；
(2) C, Ni content in weathering steel are reduced, the welding performance of weathering steel is improved；
(3) the Si content in weathering steel is improved, improves the strong of weathering steel while promoting weathering steel weather resistance
Degree；
(4) strengthened by addition Nb element solid solution, improve the intensity and welding performance of weathering steel；
(5) molten steel overheat when thin strap continuous casting is reduced, Cast Strip austenite grain is refined, so that weathering steel hot rolled thin strip shape
At uniform small grains, the forming property of weathering steel is improved while improving weather-proof hardness of steel；
(6) drafts for improving strip tandem rolling, ensure that the convexity and plate shape of strip；
(7) hot rolling pass for reducing traditional hot rolling and thin slab continuous casting and rolling shortens production procedure and process, drop
Low production cost.
Detailed description of the invention
In order to illustrate more clearly of the technical solution of the embodiment of the present invention, the attached drawing of embodiment will be made simply below
It introduces.It should be evident that the accompanying drawings in the following description merely relates to some embodiments of the present invention, rather than to limit of the invention
System.
Fig. 1 is the metallographic structure of 550MPa grades of weathering steel according to the present invention.
Specific embodiment
It in order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below will be to the embodiment of the present invention
Technical solution is clearly and completely described.Obviously, described embodiment is a part of the embodiments of the present invention, rather than
Whole embodiments.Based on described the embodiment of the present invention, those of ordinary skill in the art are without creative work
Under the premise of every other embodiment obtained, shall fall within the protection scope of the present invention.
Unless otherwise defined, technical term or scientific term used in the disclosure are should be in fields of the present invention
The ordinary meaning that personage with general technical ability is understood.
Embodiment 1
The present embodiment follows the steps below:
1) it smelts
Ladle chemistry are as follows: C:0.25%, Si:0.40%, Mn:0.55%, P:0.06%, S:0.002%, N:
0.003%, Cu:0.70%, Cr:0.60%, Ni:0.04%, Nb:0.15%, remaining is Fe and inevitable impurity；
2) thin strap continuous casting
Qualified molten steel will be smelted and be casting continuously to form the Cast Strip with a thickness of 1.9mm, molten steel by the casting in bronze roller of a pair of of opposite direction rotating
The degree of superheat is 52 DEG C；
3) the online hot rolling in Cast Strip
Hot rolling drafts is 53%, and it is 1020 DEG C that strip, which rolls rear temperature,；
4) it cools down and batches
Hot-strip is cooled to 580 DEG C by aerosol, and batches coiled.
It is 0.9mm by the obtained weathering steel strip thickness of above step, Mechanics Performance Testing, surrender is carried out to strip
Intensity is 572MPa, tensile strength 687MPa, elongation percentage 28%.
Embodiment 2
The present embodiment follows the steps below:
1) it smelts
Ladle chemistry are as follows: C:0.15%, Si:0.38%, Mn:0.40%, P:0.04%, S:0.002%, N:
0.002%, Cu:1.20%, Cr:0.80%, Ni:0.07%, Nb:0.08%, remaining is Fe and inevitable impurity；
2) thin strap continuous casting
Qualified molten steel will be smelted and be casting continuously to form the Cast Strip with a thickness of 2.4mm, molten steel by the casting in bronze roller of a pair of of opposite direction rotating
The degree of superheat is 45 DEG C；
3) the online hot rolling in Cast Strip
Hot rolling drafts is 46%, and it is 1030 DEG C that strip, which rolls rear temperature,；
4) it cools down and batches
Hot-strip is cooled to 520 DEG C by aerosol, and batches coiled.
It is 1.3mm by the obtained weathering steel strip thickness of above step, Mechanics Performance Testing, surrender is carried out to strip
Intensity is 586MPa, tensile strength 698MPa, elongation percentage 26%.
Embodiment 3
The present embodiment follows the steps below:
1) it smelts
Ladle chemistry are as follows: C:0.20%, Si:0.78%, Mn:0.85%, P:0.05%, S:0.003%, N:
0.002%, Cu:0.90%, Cr:1.20%, Ni:0.05%, Nb:0.05%, remaining is Fe and inevitable impurity；
2) thin strap continuous casting
Qualified molten steel will be smelted and be casting continuously to form the Cast Strip with a thickness of 2.2mm, molten steel by the casting in bronze roller of a pair of of opposite direction rotating
The degree of superheat is 38 DEG C；
3) the online hot rolling in Cast Strip
Hot rolling drafts is 50%, and it is 970 DEG C that strip, which rolls rear temperature,；
4) it cools down and batches
Hot-strip is cooled to 470 DEG C by aerosol, and batches coiled.
It is 1.1mm by the obtained weathering steel strip thickness of above step, Mechanics Performance Testing, surrender is carried out to strip
Intensity is 598MPa, tensile strength 730MPa, elongation percentage 25%.
The above is only exemplary embodiment of the invention, protection scope and is not intended to limit the present invention, this hair
Bright protection scope is determined by the attached claims.
Claims (10)
1. a kind of production method of thin strap continuous casting 550MPa grades of weathering steels, includes the following steps:
1) it smelts
Ladle chemistry are as follows: C < 0.03%, Si:0.20-0.80%, Mn < 1.0%%, P:0.03-1.50%, S≤
0.008%, N≤0.008%, Cu:0.40-1.50%, Cr:0.50-1.50%, Ni < 0.10%, Nb:0.05-0.20%,
Remaining is Fe and inevitable impurity；
2) thin strap continuous casting
Qualified molten steel will be smelted and be casting continuously to form Cast Strip by the casting in bronze roller of a pair of of opposite direction rotating；
3) the online hot rolling in Cast Strip
By 1 passage hot rolling at Thin Strip Steel, it is 950-1050 DEG C that strip, which rolls rear temperature, for Cast Strip；
4) it cools down and batches
Hot-strip is cooled to 450-600 DEG C by aerosol, and batches coiled.
2. the production method of thin strap continuous casting 550MPa grades of weathering steels as described in claim 1, which is characterized in that the step 2)
In, Cast Strip is with a thickness of 1.4-2.5mm.
3. the production method of thin strap continuous casting 550MPa grades of weathering steels as described in claim 1, which is characterized in that the step 2)
In, degree of superheat when molten steel continuous casting is controlled at 80 DEG C or less.
4. the production method of thin strap continuous casting 550MPa grades of weathering steels as described in claim 1, which is characterized in that the step 3)
In, drafts of the Cast Strip Jing Guo hot-rolling mill hot rolling is 15-65%.
5. the production method of thin strap continuous casting 550MPa grades of weathering steels as described in claim 1, which is characterized in that the step 3)
In, Cast Strip is by hot rolling formation hot rolling thin strip with a thickness of 0.6-1.9mm.
6. the production method of thin strap continuous casting 550MPa grades of weathering steels as described in claim 1, which is characterized in that the step 3)
In, the width of hot-strip is 600-1500mm.
7. the production method of thin strap continuous casting 550MPa grades of weathering steels as described in claim 1, which is characterized in that the step 4)
In, the yield strength of Thin Strip Steel is in 550MPa or more, and tensile strength is in 650MPa or more, and elongation percentage is 22% or more.
8. the production method of thin strap continuous casting 550MPa grades of weathering steels as described in claim 1, which is characterized in that the step 4)
In, the microstructure of strip is uniformly tiny ferrite and a small amount of pearlite.
9. a kind of thin strap continuous casting 550MPa grades of weathering steels, which is characterized in that using as described in any one in claim 1-8
Production method produced.
10. thin strap continuous casting 550MPa grades of weathering steels as claimed in claim 9, which is characterized in that the yield strength of Thin Strip Steel exists
550MPa or more, tensile strength is in 650MPa or more, and for elongation percentage 22% or more, the microstructure of strip is uniformly tiny iron
Ferritic and a small amount of pearlite.