CN107673695A - A kind of castoff regenerative brick and tile and preparation method thereof - Google Patents
A kind of castoff regenerative brick and tile and preparation method thereof Download PDFInfo
- Publication number
- CN107673695A CN107673695A CN201710982920.1A CN201710982920A CN107673695A CN 107673695 A CN107673695 A CN 107673695A CN 201710982920 A CN201710982920 A CN 201710982920A CN 107673695 A CN107673695 A CN 107673695A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- tile
- castoff regenerative
- regenerative brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of castoff regenerative brick and tile and preparation method thereof, belong to building material technical field.It is made up of the raw material of following parts by weight：5 15 parts of 10 30 parts of construction refuse regenerated aggregate, 5 15 parts of reinforcing agent, 10 20 parts of water reducer, 5 15 parts of curing agent, 10 30 parts of hydroxymethyl-propyl cellulose, 5 15 parts of portland cement, 20 40 parts of water, 10 20 parts of discarded concrete particle and polyamide.The castoff regenerative brick and tile intensity of the present invention is high, steady quality, and service life length, cost is low, can turn waste into wealth, environmental protection and energy saving, has good economic benefit and extensive social benefit.
Description
Technical field
The present invention relates to a kind of castoff regenerative brick and tile and preparation method thereof, belong to building material technical field.
Background technology
Building waste is the chief component of municipal refuse.Currently building waste is treated with traditional air storage, depth
Based on excavation and filling buries, although this mode treating capacity is big, convenient and simple, processing cost is low, really land resource is occupied.
If building waste can not recycle in time, environment is not only polluted, also creates the wasting of resources.
The content of the invention
An object of the present invention, it is to provide a kind of castoff regenerative brick and tile.The castoff regenerative brick and tile intensity of the present invention
Height, steady quality, service life length, cost is low, can turn waste into wealth, environmental protection and energy saving, with good economic benefit and extensively
Social benefit
The technical scheme that the present invention solves above-mentioned technical problem is as follows：A kind of castoff regenerative brick and tile, by following parts by weight
Several raw materials are made：Construction refuse regenerated aggregate 10-30 parts, reinforcing agent 5-15 parts, water reducer 10-20 parts, curing agent 5-15
Part, hydroxymethyl-propyl cellulose 10-30 parts, portland cement 5-15 parts, water 20-40 parts, discarded concrete particle 10-20 parts
With polyamide 5-15 parts.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, it is made up of the raw material of following parts by weight：20 parts of construction refuse regenerated aggregate, 10 parts of reinforcing agent, diminishing
15 parts of agent, 10 parts of curing agent, 20 parts of hydroxymethyl-propyl cellulose, 10 parts of portland cement, 30 parts of water, discarded concrete particle
15 parts and 10 parts of polyamide.
Further, the construction refuse regenerated aggregate refers to that the particle diameter through crushing, sieve, being obtained after impurities removing is
2-10mm building waste.
Further, the reinforcing agent is wollastonite powder and redispersable latex powder in mass ratio 1:5 mixture.
Further, the water reducer is high-efficiency water-reducing agent of poly-carboxylic acid.
Further, the curing agent by mass percentage by 10% calcium sulfate, 10% sodium chloride, 10% calcium chloride,
10% ammonium hydrogen carbonate, 10% potassium carbonate and 50% water are mixed with and formed.
The second object of the present invention, it is to put on the preparation method for stating castoff regenerative brick and tile.The preparation method letter of the present invention
It is single, wide market, it is adapted to large-scale production.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：A kind of preparation method of castoff regenerative brick and tile, bag
Include following steps：
(1) raw material of following parts by weight is taken：Construction refuse regenerated aggregate 10-30 parts, reinforcing agent 5-15 parts, water reducer
It is 10-20 parts, curing agent 5-15 parts, hydroxymethyl-propyl cellulose 10-30 parts, portland cement 5-15 parts, water 20-40 parts, discarded
Concrete particle 10-20 parts and polyamide 5-15 parts；
(2) by construction refuse regenerated aggregate, reinforcing agent, hydroxymethyl-propyl cellulose, portland cement, discarded concrete
Particle, polyamide are poured into mixer, spray curing agent while stirring, after stirring 3min, add water and water reducer, are stirred
5min, produce the castoff regenerative brick and tile.
The beneficial effects of the invention are as follows：
(1) castoff regenerative brick and tile intensity of the invention is high, steady quality, and service life length, cost is low, can become useless
For treasured, environmental protection and energy saving, there is good economic benefit and extensive social benefit.
(2) castoff regenerative brick and tile of the invention have preferable split tensile strength, shock resistance, good toughness, slump
Spend for 60-100mm, on the premise of proof strength is up to standard, there is good mobility.
(3) each low raw-material cost of the invention, preparation method is simple, wide market, is adapted to large-scale production.
Embodiment
The principle and feature of the present invention are described below in conjunction with specific embodiment, example is served only for explaining this
Invention, is not intended to limit the scope of the present invention.
Embodiment 1：
The castoff regenerative brick and tile of the present embodiment, are made up of the raw material of following weight：Construction refuse regenerated aggregate 10kg,
Reinforcing agent 15kg, water reducer 10kg, curing agent 15kg, hydroxymethyl-propyl cellulose 10kg, portland cement 15kg, water 20kg,
Discarded concrete particle 20kg and polyamide 5kg, wherein, the construction refuse regenerated aggregate refers to through crushing, sieving, rejecting
The particle diameter obtained after debris is 2-10mm building waste, and the reinforcing agent is that wollastonite powder and redispersable latex powder press quality
Than 1:5 mixture, the water reducer are high-efficiency water-reducing agent of poly-carboxylic acid, and the curing agent is by mass percentage by 10% sulfuric acid
Calcium, 10% sodium chloride, 10% calcium chloride, 10% ammonium hydrogen carbonate, 10% potassium carbonate and 50% water are mixed with and formed.
The preparation method of above-mentioned castoff regenerative brick and tile, comprises the following steps：
(1) raw material of following weight is taken：Construction refuse regenerated aggregate 10kg, reinforcing agent 15kg, water reducer 10kg, solidification
Agent 15kg, hydroxymethyl-propyl cellulose 10kg, portland cement 15kg, water 20kg, discarded concrete particle 20kg and polyamide
5kg；
(2) by construction refuse regenerated aggregate, reinforcing agent, hydroxymethyl-propyl cellulose, portland cement, discarded concrete
Particle, polyamide are poured into mixer, spray curing agent while stirring, after stirring 3min, add water and water reducer, are stirred
5min, produce the castoff regenerative brick and tile.
Embodiment 2：
The castoff regenerative brick and tile of the present embodiment, are made up of the raw material of following weight：Construction refuse regenerated aggregate 20kg,
Reinforcing agent 10kg, water reducer 15kg, curing agent 10kg, hydroxymethyl-propyl cellulose 20kg, portland cement 10kg, water 30kg,
Discarded concrete particle 15kg and polyamide 10kg, wherein, the construction refuse regenerated aggregate refers to through crushing, sieving, rejecting
The particle diameter obtained after debris is 2-10mm building waste, and the reinforcing agent is that wollastonite powder and redispersable latex powder press quality
Than 1:5 mixture, the water reducer are high-efficiency water-reducing agent of poly-carboxylic acid, and the curing agent is by mass percentage by 10% sulfuric acid
Calcium, 10% sodium chloride, 10% calcium chloride, 10% ammonium hydrogen carbonate, 10% potassium carbonate and 50% water are mixed with and formed.
The preparation method of above-mentioned castoff regenerative brick and tile, comprises the following steps：
(1) raw material of following weight is taken：Construction refuse regenerated aggregate 20kg, reinforcing agent 10kg, water reducer 15kg, solidification
Agent 10kg, hydroxymethyl-propyl cellulose 20kg, portland cement 10kg, water 30kg, discarded concrete particle 15kg and polyamide
10kg；
(2) by construction refuse regenerated aggregate, reinforcing agent, hydroxymethyl-propyl cellulose, portland cement, discarded concrete
Particle, polyamide are poured into mixer, spray curing agent while stirring, after stirring 3min, add water and water reducer, are stirred
5min, produce the castoff regenerative brick and tile.
Embodiment 3：
The castoff regenerative brick and tile of the present embodiment, are made up of the raw material of following weight:Construction refuse regenerated aggregate 30kg,
It is reinforcing agent 5kg, water reducer 20kg, curing agent 5kg, hydroxymethyl-propyl cellulose 30kg, portland cement 5kg, water 40kg, useless
Abandon concrete particle 10kg and polyamide 15kg, wherein, the construction refuse regenerated aggregate refer to through crush, sieve, reject it is miscellaneous
The particle diameter obtained after thing is 2-10mm building waste, the reinforcing agent be wollastonite powder and redispersable latex powder in mass ratio
1:5 mixture, the water reducer are high-efficiency water-reducing agent of poly-carboxylic acid, the curing agent by mass percentage by 10% calcium sulfate,
10% sodium chloride, 10% calcium chloride, 10% ammonium hydrogen carbonate, 10% potassium carbonate and 50% water are mixed with and formed.
The preparation method of above-mentioned castoff regenerative brick and tile, comprises the following steps：
(1) raw material of following weight is taken：Construction refuse regenerated aggregate 30kg, reinforcing agent 5kg, water reducer 20kg, curing agent
5kg, hydroxymethyl-propyl cellulose 30kg, portland cement 5kg, water 40kg, discarded concrete particle 10kg and polyamide
15kg；
(2) by construction refuse regenerated aggregate, reinforcing agent, hydroxymethyl-propyl cellulose, portland cement, discarded concrete
Particle, polyamide are poured into mixer, spray curing agent while stirring, after stirring 3min, add water and water reducer, are stirred
5min, produce the castoff regenerative brick and tile.
The performance of castoff regenerative brick and tile obtained by embodiment 1-3 is detected, it is specific as shown in table 1.
The performance detection of castoff regenerative brick and tile obtained by the embodiment 1-3 of table 1
As can be seen here, castoff regenerative brick and tile of the invention have preferable split tensile strength, shock resistance, toughness
It is good, on the premise of proof strength is up to standard, there is good mobility, there is good economic benefit and extensive society to imitate
Benefit.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (7)
1. a kind of castoff regenerative brick and tile, it is characterised in that be made up of the raw material of following parts by weight：Construction refuse regenerated aggregate
10-30 parts, reinforcing agent 5-15 parts, water reducer 10-20 parts, curing agent 5-15 parts, hydroxymethyl-propyl cellulose 10-30 parts, silicic acid
Salt cement 5-15 parts, water 20-40 parts, discarded concrete particle 10-20 parts and polyamide 5-15 parts.
2. a kind of castoff regenerative brick and tile according to claim 1, it is characterised in that by the raw material system of following parts by weight
Into：20 parts of construction refuse regenerated aggregate, 10 parts of reinforcing agent, 15 parts of water reducer, 10 parts of curing agent, hydroxymethyl-propyl cellulose 20
Part, 10 parts of portland cement, 30 parts of water, 15 parts of discarded concrete particle and 10 parts of polyamide.
A kind of 3. castoff regenerative brick and tile according to claim 1 or 2, it is characterised in that the construction refuse regenerated bone
Material refers to the building waste that the particle diameter through crushing, sieve, being obtained after impurities removing is 2-10mm.
4. a kind of castoff regenerative brick and tile according to claim 1 or 2, it is characterised in that the reinforcing agent is wollastonite powder
With redispersable latex powder in mass ratio 1:5 mixture.
5. a kind of castoff regenerative brick and tile according to claim 1 or 2, it is characterised in that the water reducer is polycarboxylic acids
High efficiency water reducing agent.
6. a kind of castoff regenerative brick and tile according to claim 1 or 2, it is characterised in that the curing agent presses quality hundred
Divide and made than being mixed by 10% calcium sulfate, 10% sodium chloride, 10% calcium chloride, 10% ammonium hydrogen carbonate, 10% potassium carbonate and 50% water
It is standby to form.
7. a kind of preparation method of castoff regenerative brick and tile, it is characterised in that comprise the following steps：
(1) raw material of following parts by weight is taken：Construction refuse regenerated aggregate 10-30 parts, reinforcing agent 5-15 parts, water reducer 10-20
Part, curing agent 5-15 parts, hydroxymethyl-propyl cellulose 10-30 parts, portland cement 5-15 parts, water 20-40 parts, discarded concrete
Particle 10-20 parts and polyamide 5-15 parts；
(2) by construction refuse regenerated aggregate, reinforcing agent, hydroxymethyl-propyl cellulose, portland cement, discarded concrete particle,
Polyamide is poured into mixer, sprays curing agent while stirring, after stirring 3min, is added water and water reducer, is stirred 5min, i.e.,
Obtain the castoff regenerative brick and tile.