Earthquake Resistance of Pipeline With Local Metal Loss Subjected to Cyclic LoadingHashimoto et al., 2006
- Document ID
- 1483331254473509922
- Author
- Hashimoto Y
- Yatabe H
- Hagiwara N
- Oguchi N
- Publication year
- Publication venue
- International Conference on Offshore Mechanics and Arctic Engineering
External Links
Snippet
In this study, nine full-scale experiments were carried out to evaluate earthquake resistance of pipeline with local metal loss subjected to cyclic loading. The test pipes were API 5L X42 with a 762 mm diameter and 12.7 mm wall thickness. Each test pipe had an artificial local …
- 238000011068 load 0 title abstract description 103
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Netto et al. | On the effect of corrosion defects on the collapse pressure of pipelines | |
| Jayadevan et al. | Fracture response of pipelines subjected to large plastic deformation under tension | |
| Chegeni et al. | Effect of corrosion on thin-walled pipes under combined internal pressure and bending | |
| Netto | On the effect of narrow and long corrosion defects on the collapse pressure of pipelines | |
| Østby et al. | Fracture Control–Offshore Pipelines JIP Results from large scale testing of the effect of biaxial loading on the strain capacity of pipes with defects | |
| Zhao et al. | Standards and methods for dent assessment and failure prediction of pipelines: A critical review | |
| Wham et al. | Large axial deformation performance of steel pipeline designed for fault crossings | |
| Konosu et al. | Plastic collapse load for vessel with external flaw simultaneously subjected to internal pressure and external bending moment: Experimental and FEA results | |
| YOSHIZAKI et al. | Large deformation behavior of buried pipelines with low-angle elbows subjected to permanent ground deformation | |
| Hashimoto et al. | Earthquake Resistance of Pipeline With Local Metal Loss Subjected to Cyclic Loading | |
| Benjamin et al. | Burst tests on pipeline with nonuniform depth corrosion defects | |
| Gao et al. | Bending capacity of corroded pipeline subjected to internal pressure and axial loadings | |
| Yatabe et al. | Effects of mechanical properties on the deformability of high grade linepipe | |
| Igi et al. | Strain Capacity of 48" OD X80 Pipeline in Pressurized Full-scale Bending Test | |
| Shitamoto et al. | Effect of full scale pipe bending test method on deformability results of SAW pipes | |
| Ndubuaku et al. | Expression of a Generic Full-Range True Stress-True Strain Model for Pipeline Steels Using the Product-Log (Omega) Function | |
| Ramezani et al. | Strain based evaluation of dents in pressurized pipes | |
| Ahmed et al. | Strengthening of misaligned welded pipes with outer circumferentially crack using FRP bandage finite element analysis | |
| Suzuki et al. | Seismic integrity of high-strength pipelines | |
| Yoshizaki et al. | Large deformation behavior of low-angle pipeline elbows subjected to in-plane bending | |
| Gioielli et al. | Characterization of the stable tearing during pipeline strain capacity tests | |
| Mantovano et al. | Modeling of the Collapse and Propagation Behavior of UOE SAW Pipes Under External Pressure: Influence of Thermal Treatments for Typical Coating Applications | |
| Shim et al. | Bulging factor for axial surface cracks in pipes | |
| CN113378424B (en) | Method and system for evaluating axial deformation bearing capacity of pipeline girth welding joint | |
| Kubo et al. | Application of WES2808 to brittle fracture assessment for gas pipelines |