Jiang et al., 1994 - Google Patents

Approach of selective nucleation and epitaxy of diamond films on Si (100)

Jiang et al., 1994

Document ID
12172543176661129799
Author
Jiang X
Boettger E
Paul M
Klages C
Publication year
Publication venue
Applied physics letters

External Links

Snippet

Heteroepitaxial diamond fiIms were selectively nucleated and grown on mirror-polished single crystalline (100) silicon by microwave plasma assisted chemical vapor deposition (MWCVD). The silicon substrates were coated by 0.5, um thick SiO, films patterned by a …
Continue reading at pubs.aip.org (other versions)

Classifications

    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/04—Manufacture or treatment of semiconductor devices or of parts thereof the devices having at least one potential-jump barrier or surface barrier, e.g. PN junction, depletion layer, carrier concentration layer
    • H01L21/18—Manufacture or treatment of semiconductor devices or of parts thereof the devices having at least one potential-jump barrier or surface barrier, e.g. PN junction, depletion layer, carrier concentration layer the devices having semiconductor bodies comprising elements of Group IV of the Periodic System or AIIIBV compounds with or without impurities, e.g. doping materials
    • H01L21/30—Treatment of semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/26
    • H01L21/302—Treatment of semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/26 to change their surface-physical characteristics or shape, e.g. etching, polishing, cutting
    • H01L21/306—Chemical or electrical treatment, e.g. electrolytic etching
    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02518—Deposited layers
    • H01L21/02521—Materials
    • H01L21/02524—Group 14 semiconducting materials
    • H01L21/02529—Silicon carbide
    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02612—Formation types
    • H01L21/02617—Deposition types
    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02367—Substrates
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL-GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B25/00—Single-crystal growth by chemical reaction of reactive gases, e.g. chemical vapour-deposition growth
    • C30B25/02—Epitaxial-layer growth
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL-GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B23/00—Single-crystal growth by condensing evaporated or sublimed material
    • C30B23/02—Epitaxial-layer growth
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/22—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the deposition of inorganic material, other than metallic material
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL-GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B29/00—Single crystals or homogeneous polycrystalline material with defined structure characterised by the material or by their shape
    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H01L29/00—Semiconductor devices adapted for rectifying, amplifying, oscillating or switching, or capacitors or resistors with at least one potential-jump barrier or surface barrier, e.g. PN junction depletion layer or carrier concentration layer; Details of semiconductor bodies or of electrodes thereof; Multistep manufacturing processes therefor
    • H01L29/02—Semiconductor bodies; Multistep manufacturing processes therefor
    • H01L29/12—Semiconductor bodies; Multistep manufacturing processes therefor characterised by the materials of which they are formed
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL-GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B33/00—After-treatment of single crystals or homogeneous polycrystalline material with defined structure

Similar Documents

Publication Publication Date Title
CA1329167C (en) Dry etching of silicon carbide
US5632812A (en) Diamond electronic device and process for producing the same
EP0573943B1 (en) Method for the manufacture of large single crystals
Jiang et al. Atomic‐force‐microscopic study of heteroepitaxial diamond nucleation on (100) silicon
Jiang et al. Approach of selective nucleation and epitaxy of diamond films on Si (100)
CA2034361A1 (en) Polycrystalline cvd diamond substrate for single crystal epitaxial growth of semiconductors
Koizumi et al. Initial growth process of epitaxial diamond thin films on cBN single crystals
GB2615867A (en) A method of forming a graphene layer structure and a graphene substrate
Tischler et al. Growth and characterization of compound semiconductors by atomic layer epitaxy
Zhou et al. Heteroepitaxial nucleation of diamond on Si (100) via double bias-assisted hot filament chemical vapor deposition
JP3742877B2 (en) Method for producing SiC single crystal thin film
Hörmann et al. Epitaxial Ir layers on SrTiO3 as substrates for diamond nucleation: deposition of the films and modification in the CVD environment
Gillis et al. Highly anisotropic, ultra-smooth patterning of GaN/SiC by low energy electron enhanced etching in DC plasma
Hu et al. High-rate growth of single-crystal diamond with an atomically flat surface by microwave plasma chemical vapor deposition
US7989260B2 (en) Method of selectively forming atomically flat plane on diamond surface, diamond substrate produced by the method, and semiconductor device using the same
Sun et al. Crystal morphology and phase purity of diamond crystallites during bias enhanced nucleation and initial growth stages
Jiang et al. High quality heteroepitaxial diamond films on silicon: recent progresses
JP2005015325A (en) Method for manufacturing extremely flat microcrystalline diamond thin film by laser ablation method
JP2022171727A (en) diamond substrate
GB2607410A (en) A method of forming a graphene layer structure and a graphene substrate
Yang et al. The epitaxial growth of (1 1 1) oriented monocrystalline Si film based on a 4: 5 Si-to-SiC atomic lattice matching interface
Barrat et al. Synthesis of highly oriented CVD diamond films by ultra short bias enhanced nucleation step
Chang et al. Transmission electron microscopy study of diamond nucleation on 6H‐SiC single crystal with possibility of epitaxy
Kotaki et al. Deposition of diamond from a plasma jet with dichlorobenzene as carbon source
Jiang et al. Epitaxy of diamond on Si (100) and surface-roughening-induced crystal misorientation