ZA201707321B - Flat steel product and method for the production thereof - Google Patents

Flat steel product and method for the production thereof

Info

Publication number
ZA201707321B
ZA201707321B ZA2017/07321A ZA201707321A ZA201707321B ZA 201707321 B ZA201707321 B ZA 201707321B ZA 2017/07321 A ZA2017/07321 A ZA 2017/07321A ZA 201707321 A ZA201707321 A ZA 201707321A ZA 201707321 B ZA201707321 B ZA 201707321B
Authority
ZA
South Africa
Prior art keywords
production
flat steel
steel product
flat
product
Prior art date
Application number
ZA2017/07321A
Inventor
Richard G Thiessen
6 Duisburg 47229 Germany Robert-Koch-Strasse
Karsten Machalitza
Roland Sebald
Original Assignee
Kaiser Wilhelm Strasse 100 Duisburg 47166 Germany
Thyssenkrupp Ag
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kaiser Wilhelm Strasse 100 Duisburg 47166 Germany, Thyssenkrupp Ag filed Critical Kaiser Wilhelm Strasse 100 Duisburg 47166 Germany
Publication of ZA201707321B publication Critical patent/ZA201707321B/en

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C21D1/19—Hardening; Quenching with or without subsequent tempering by interrupted quenching
    • C21D1/22—Martempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
    • C23F17/00—Multi-step processes for surface treatment of metallic material involving at least one process provided for in class C23 and at least one process covered by subclass C21D or C22F or class C25
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Steel (AREA)
ZA2017/07321A 2015-05-06 2017-10-27 Flat steel product and method for the production thereof ZA201707321B (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/EP2015/059968 WO2016177420A1 (en) 2015-05-06 2015-05-06 Flat steel product and method for the production thereof
PCT/EP2016/059960 WO2016177763A1 (en) 2015-05-06 2016-05-04 Flat steel product and method for the production thereof

Publications (1)

Publication Number Publication Date
ZA201707321B true ZA201707321B (en) 2022-11-30

Family

ID=53267305

Family Applications (1)

Application Number Title Priority Date Filing Date
ZA2017/07321A ZA201707321B (en) 2015-05-06 2017-10-27 Flat steel product and method for the production thereof

Country Status (9)

Country Link
US (1) US20190119774A1 (en)
EP (1) EP3292228B1 (en)
JP (1) JP6788612B2 (en)
KR (1) KR102594922B1 (en)
CN (1) CN107580634A (en)
ES (1) ES2820348T3 (en)
MX (1) MX2017014090A (en)
WO (2) WO2016177420A1 (en)
ZA (1) ZA201707321B (en)

Families Citing this family (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018108653A1 (en) * 2016-12-14 2018-06-21 Thyssenkrupp Steel Europe Ag Hot-rolled flat steel product and method for the production thereof
KR101917472B1 (en) * 2016-12-23 2018-11-09 주식회사 포스코 Tempered martensitic steel having low yield ratio and excellent uniform elongation property, and method for manufacturing the same
MX2019004535A (en) * 2017-01-31 2019-06-12 Nippon Steel & Sumitomo Metal Corp Steel sheet.
CN110651377A (en) * 2017-05-18 2020-01-03 蒂森克虏伯钢铁欧洲股份公司 Battery case
EP3688203B1 (en) * 2017-09-28 2022-04-27 ThyssenKrupp Steel Europe AG Flat steel product and production method thereof
CN108359895A (en) * 2018-03-14 2018-08-03 河钢股份有限公司 A kind of the hot forming steel and its hot rolling technology of tensile strength 950MPa ranks
CN112585284A (en) * 2018-05-22 2021-03-30 蒂森克虏伯钢铁欧洲股份公司 Sheet metal formed part made of steel and having high tensile strength, and method for producing same
WO2019238741A1 (en) * 2018-06-12 2019-12-19 Thyssenkrupp Steel Europe Ag Flat steel product and method for the production thereof
CN109266956B (en) * 2018-09-14 2019-08-06 东北大学 A kind of automobile B-pillar reinforcement plate steel and preparation method thereof
CN112789358B (en) * 2018-09-26 2022-03-25 蒂森克虏伯钢铁欧洲股份公司 Method for producing a coated flat steel product and coated flat steel product
JP7410936B2 (en) 2018-09-28 2024-01-10 ポスコ カンパニー リミテッド High-strength cold-rolled steel sheet with high hole expandability, high-strength hot-dip galvanized steel sheet, and manufacturing method thereof
KR102276741B1 (en) * 2018-09-28 2021-07-13 주식회사 포스코 High strength cold-rolled steel sheet and galvanized steel sheet having high hole expansion ratio and manufacturing method thereof
PT3754037T (en) * 2019-06-17 2022-04-19 Tata Steel Ijmuiden Bv Method of heat treating a high strength cold rolled steel strip
EP4095272A4 (en) * 2020-01-22 2023-07-26 Nippon Steel Corporation Steel sheet and method for producing same
EP3872206B1 (en) * 2020-02-28 2023-06-21 ThyssenKrupp Steel Europe AG Post-treated cold rolled steel sheet product and method of manufacturing a post-treated cold rolled steel sheet product
WO2021176249A1 (en) * 2020-03-02 2021-09-10 Arcelormittal High strength cold rolled and galvannealed steel sheet and manufacturing process thereof
CN114107794B (en) * 2020-08-31 2023-08-11 宝山钢铁股份有限公司 980 MPa-grade ultra-low carbon martensite and residual austenite ultra-high hole-enlarging steel and manufacturing method thereof

Family Cites Families (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0826401B2 (en) * 1990-12-29 1996-03-13 日本鋼管株式会社 Manufacturing method of ultra high strength cold rolled steel sheet with excellent workability and impact characteristics
JPH06108152A (en) * 1992-09-30 1994-04-19 Kobe Steel Ltd Production of high strength hot-dipping galvanized steel sheet excellent in bending workability
JP2826058B2 (en) * 1993-12-29 1998-11-18 株式会社神戸製鋼所 Ultra-high strength thin steel sheet without hydrogen embrittlement and manufacturing method
JP3849625B2 (en) * 1995-06-09 2006-11-22 Ｊｆｅスチール株式会社 Manufacturing method of ultra-high strength ERW steel pipe
JP3374659B2 (en) * 1995-06-09 2003-02-10 日本鋼管株式会社 Ultra-high tensile ERW steel pipe and method of manufacturing the same
JP5365216B2 (en) * 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 High-strength steel sheet and its manufacturing method
JP5402007B2 (en) * 2008-02-08 2014-01-29 Ｊｆｅスチール株式会社 High-strength hot-dip galvanized steel sheet excellent in workability and manufacturing method thereof
JP5418047B2 (en) 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 High strength steel plate and manufacturing method thereof
KR20100034118A (en) * 2008-09-23 2010-04-01 포항공과대학교 산학협력단 Hot-dip galvanized steel sheet having a martensitic structure with ultimate high strength and method for manufacturing the same
JP5315956B2 (en) * 2008-11-28 2013-10-16 Ｊｆｅスチール株式会社 High-strength hot-dip galvanized steel sheet with excellent formability and method for producing the same
JP5342912B2 (en) * 2009-03-31 2013-11-13 株式会社神戸製鋼所 High strength cold-rolled steel sheet with excellent bending workability
EP2524970A1 (en) * 2011-05-18 2012-11-21 ThyssenKrupp Steel Europe AG Extremely stable steel flat product and method for its production
JP6047037B2 (en) * 2012-03-29 2016-12-21 株式会社神戸製鋼所 Manufacturing method of high-strength cold-rolled steel sheet with excellent steel plate shape
JP5906154B2 (en) * 2012-07-20 2016-04-20 株式会社神戸製鋼所 High strength steel plate with excellent delayed fracture resistance and method for producing the same

Also Published As

Publication number Publication date
ES2820348T3 (en) 2021-04-20
CN107580634A (en) 2018-01-12
WO2016177420A1 (en) 2016-11-10
US20190119774A1 (en) 2019-04-25
JP6788612B2 (en) 2020-11-25
JP2018518593A (en) 2018-07-12
EP3292228A1 (en) 2018-03-14
KR102594922B1 (en) 2023-10-27
WO2016177763A1 (en) 2016-11-10
KR20180003581A (en) 2018-01-09
MX2017014090A (en) 2018-03-01
EP3292228B1 (en) 2020-08-12

Similar Documents

Publication Publication Date Title
ZA201707321B (en) Flat steel product and method for the production thereof
ZA201703011B (en) Method for manufacturing a high strength steel product and steel product thereby obtained
GB201622340D0 (en) Product and Method
PL3150737T3 (en) Heat-treated steel material and method for producing same
ZA201701938B (en) Cold-rolled and recrystallisation annealed flat steel product, and method for the production thereof
PL3150736T3 (en) Heat-treated steel material and method for producing same
IL301514A (en) Cannabis products and industrial methods for production thereof
PL2924140T3 (en) Method for manufacturing a high strength flat steel product
PL3140430T3 (en) Process for the production of grain non- oriented electric steel strip, with a high degree of cold reduction
EP3138936A4 (en) High-strength steel sheet and production method therefor
PL3170912T3 (en) Steel product and manufacturing method of the same
PL3688203T3 (en) Flat steel product and production method thereof
EP3287514A4 (en) Production device and production method for cultured-cell product
HUE043819T2 (en) Method for the further processing of a prefabricated product, and associated prefabricated product
SG11202001418YA (en) High-mn steel and production method therefor
EP3093358A4 (en) Steel material and process for producing same
PL3150733T3 (en) Hot-rolled steel sheet and production method therefor
GB201501603D0 (en) Method and product
PT3354669T (en) Solid surface product and process for manufacturing thereof
GB201515411D0 (en) Substituted materials, process for the production and uses thereof
GB201503420D0 (en) Composite product and method
ZA201701012B (en) Steel-strip production method, and steel strip
EP3366884A4 (en) Blisk production method and blisk intermediate product
TWI560280B (en) Steel sheet for drawn-can and producing method thereof
EP3272435A4 (en) H-shaped steel production method and h-shaped steel product