WO2024083881A1 - Lixiviation oxydative de précipités d'hydroxyde mixte contenant du carbone - Google Patents

Lixiviation oxydative de précipités d'hydroxyde mixte contenant du carbone Download PDF

Info

Publication number
WO2024083881A1
WO2024083881A1 PCT/EP2023/078919 EP2023078919W WO2024083881A1 WO 2024083881 A1 WO2024083881 A1 WO 2024083881A1 EP 2023078919 W EP2023078919 W EP 2023078919W WO 2024083881 A1 WO2024083881 A1 WO 2024083881A1
Authority
WO
WIPO (PCT)
Prior art keywords
mixed hydroxide
hydroxide precipitate
process according
nickel
carbon
Prior art date
Application number
PCT/EP2023/078919
Other languages
English (en)
Inventor
Bart KLAASEN
Original Assignee
Umicore
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Umicore filed Critical Umicore
Publication of WO2024083881A1 publication Critical patent/WO2024083881A1/fr

Abstract

La présente invention concerne un procédé de lixiviation sélective de nickel à partir d'un précipité d'hydroxyde mixte comprenant du nickel, du cobalt, du manganèse et du carbone, le carbone étant compris en tant que carbone et/ou graphite lié organiquement en une quantité de 0,10 à 10,00 % en poids par rapport au poids dudit précipité d'hydroxyde mixte, ledit procédé comprenant les étapes consistant à : i. fournir une suspension de précipité d'hydroxyde mixte, et lixivier au moins partiellement le nickel dans ledit précipité d'hydroxyde mixte par ajout d'acide sulfurique; ii. oxyder la suspension de précipité d'hydroxyde mixte au moins partiellement lixiviée provenant de l'étape i. avec de l'acide peroxymonosulfurique et/ou un sel de celui-ci dans un milieu aqueux acide à un pH d'au plus 4; iii. acidifier la suspension de précipité d'hydroxyde mixte oxydé obtenue à l'étape ii. en ajoutant de l'acide sulfurique pour dissoudre les quantités résiduelles de nickel dans la phase solide, ce qui permet d'obtenir une phase solide comprenant du cobalt et du manganèse et une phase aqueuse comprenant du sulfate de nickel; et iv. séparer ladite phase solide et ladite phase aqueuse.
PCT/EP2023/078919 2022-10-19 2023-10-18 Lixiviation oxydative de précipités d'hydroxyde mixte contenant du carbone WO2024083881A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP22202394 2022-10-19
EP22202394.7 2022-10-19

Publications (1)

Publication Number Publication Date
WO2024083881A1 true WO2024083881A1 (fr) 2024-04-25

Family

ID=83900124

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2023/078919 WO2024083881A1 (fr) 2022-10-19 2023-10-18 Lixiviation oxydative de précipités d'hydroxyde mixte contenant du carbone

Country Status (1)

Country Link
WO (1) WO2024083881A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA1180903A (fr) * 1980-12-05 1985-01-15 Diana M. Mounsey Separation du cobalt et du nickel
CA2396972A1 (fr) * 2001-08-10 2003-02-10 Cesar J. Ferron Traitement de solutions renfermant du nickel
CA2949580A1 (fr) 2015-12-09 2017-06-09 Bhp Billiton Nickel West Pty Ltd Procede de lessivage a l'acide selectif de nickel et de cobalt a partir d'un intermediaire d'hydroxyde melange

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA1180903A (fr) * 1980-12-05 1985-01-15 Diana M. Mounsey Separation du cobalt et du nickel
CA2396972A1 (fr) * 2001-08-10 2003-02-10 Cesar J. Ferron Traitement de solutions renfermant du nickel
CA2949580A1 (fr) 2015-12-09 2017-06-09 Bhp Billiton Nickel West Pty Ltd Procede de lessivage a l'acide selectif de nickel et de cobalt a partir d'un intermediaire d'hydroxyde melange

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
DELINA RUTH ESTHER ET AL: "Chromium occurrence in a nickel laterite profile and its implications to surrounding surface waters", CHEMICAL GEOLOGY, ELSEVIER SCIENCE PUBLISHER B.V., AMSTERDAM, NL, vol. 558, 12 September 2020 (2020-09-12), XP086386897, ISSN: 0009-2541, [retrieved on 20200912], DOI: 10.1016/J.CHEMGEO.2020.119863 *
DELINA RUTH ESTHER ET AL: "Supporting Information: Chromium occurrence in a nickel laterite profile and its implications to surrounding surface waters", CHEMICAL GEOLOGY., vol. 558, 1 December 2020 (2020-12-01), NL, pages 119863, XP093119142, ISSN: 0009-2541, DOI: 10.1016/j.chemgeo.2020.119863 *

Similar Documents

Publication Publication Date Title
AU2020259139B2 (en) Process for the recovery of metals from a Li-containing starting material
EP4160787A1 (fr) Procédé de récupération de métal précieux à partir d'un matériau de déchet d'électrode d'une batterie secondaire au lithium à l'aide de carbonate de lithium
EP2832700B1 (fr) Procédé de fabrication d'un sulfate de nickel de haute pureté
JP5686258B2 (ja) 高純度硫酸ニッケルを得るための溶媒抽出方法
CN112375910A (zh) 废动力电池粉的回收处理方法
KR20170061206A (ko) 폐 리튬 이온 전지를 이용한 전구체 원료의 회수 방법
CN112210679A (zh) 氢氧化镍钴制备硫酸镍的方法
KR20240049385A (ko) 블랙 매스로부터 금속을 회수하기 위한 방법 및 설비
CA3213841A1 (fr) Extraction de metaux a partir d'un materiau de batterie au lithium-ion
JP2004285368A (ja) コバルト水溶液の精製方法
CN103880630A (zh) 一种使用废铅膏制备高纯度乙酸铅和纳米铅粉的方法
WO2024083881A1 (fr) Lixiviation oxydative de précipités d'hydroxyde mixte contenant du carbone
US20240263273A1 (en) Precipitation of metals
CN114956189B (zh) 一种电池级硫酸锰制备方法
JP4259165B2 (ja) コバルトとカルシウムを含む硫酸ニッケル水溶液の精製方法
CN118369446A (zh) 氧化和还原浸出方法
CN115135782B (zh) 含铅废料的脱硫
KR20230136948A (ko) 리튬 이차전지 폐기물로부터 용매추출을 이용한 유가금속의 선택적 회수방법
KR20230054385A (ko) 폐 배터리 물질로부터 니켈을 재생하는 방법
CN113249593B (zh) 从含镍、钴、锰和锂的溶液中去除钙和镁的两段法工艺
WO2023286684A1 (fr) Procédé de production de sulfate de lithium et de sulfate de métal de transition
EA043878B1 (ru) Способ восстановления металлов из li-содержащего исходного материала
WO2024057307A1 (fr) Préparation de précurseur à partir de batteries rechargeables recyclées
CN117337339A (zh) 金属的沉淀
WO2023237716A1 (fr) Procédé de sulfuration de métaux

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23793724

Country of ref document: EP

Kind code of ref document: A1