WO2019081003A1

WO2019081003A1 - Process for producing aqueous polyacrylamide solutions

Info

Publication number: WO2019081003A1
Application number: PCT/EP2017/077241
Authority: WO
Inventors: Hazel SPRAFKE; Markus OSTERMAYR; Tobias Zimmermann; Dennis Loesch; Dirk Meckelnburg; Faissal-Ali El-Toufaili
Original assignee: Basf Se
Priority date: 2017-10-25
Filing date: 2017-10-25
Publication date: 2019-05-02
Also published as: WO2019081319A1; AR113376A1

Abstract

Process for producing aqueous polyacrylamide solutions by polymerizing an aqueous solution comprising at least acrylamide thereby obtaining an aqueous polyacrylamide gel and dissolving said aqueous polyacrylamide gel in water, wherein the manufacturing steps are allocated to two different locations A and B and the process comprises the step of transporting an aqueous polyacrylamide gel hold in a transportable polymerization unit from a location A to a location B. The aqueous polyacrylamide gel furthermore comprises at least one stabilizer for prevention of polymer degradation.

Description

Process for producing aqueous polyacrylamide solutions

The invention relates to a process for producing aqueous polyacrylamide solutions by polymerizing an aqueous solution comprising at least acrylamide thereby obtaining an aqueous polyacrylamide gel and dissolving said aqueous polyacrylamide gel in water, wherein the manufacturing steps are allocated to two different locations A and B and the process comprises the step of transporting an aqueous polyacrylamide gel hold in a transportable polymerization unit from a location A to a location B. The transport time is from 6 hours to 14 days, preferably from 1 day to 14 days.

Water-soluble, high molecular weight homo- and copolymers of acrylamide may be used for various applications such as mining and oilfield applications, water treatment, sewage treatment, papermaking, and agriculture. Examples include its use in the exploration and production of mineral oil, in particular as thickeners in aqueous injection fluids for enhanced oil recovery or as rheology modifier for aqueous drilling fluids. Further examples include its use as flocculating agent for tailings and slurries in mining activities. A common polymerization technology for manufacturing such high molecular weight polyacrylamides is the so called "gel polymerization". In gel polymerization an aqueous monomer solution having a relatively high concentration of monomers, for example from 20 % by weight to 35 % by weight is polymerized by means of suitable

polymerization initiators under essentially adiabatic conditions in an unstirred reactor thereby forming a polymer gel. The polymer gels formed are converted to polymer powders by comminuting the gel into smaller pieces by one or more size reduction steps, drying such gel pieces for example in a fluid bed dryer followed by sieving, grinding and packaging. The obtained polyacrylamide powders are thereafter packaged and shipped to customers.

The aqueous polyacrylamide gel obtained from gel polymerization typically comprises from 65 % to 80 % of water. The residual amount of water in polyacrylamide powders typically is from about 4 to 12 % by weight. So, "drying" such polyacrylamide gels does not mean to remove only some residual moisture in course of drying but rather about 0.55 to 0.75 kg of water need to be removed per kg of polymer gel, or -with other words- per kg of polymer powder produced also 1 .5 to 2.5 kg of water are "produced".

It goes without saying that removing such a high amount of water from the aqueous polymer gels in course of drying is energy extensive and consequently the operational costs for drying are high. Furthermore, high-performance dryers are necessary as well as equipment for size reduction, sieving and grinding. Consequently, the capital expenditure for the entire post-processing equipment including size reduction, drying, sieving, grinding is significant in relation to the total capital expenditure for the entire plant.

High-molecular weight polyacrylamides are usually used as dilute aqueous solutions. Typical concentrations of polyacrylamides for oilfield and mining applications range from 0.05 wt. % to 0.5 wt. %. Consequently, the polyacrylamide powders manufactured as mentioned above need to be dissolved in aqueous fluids before use. Dissolving high molecular weight polymers in aqueous fluids is time consuming and it is difficult to do so without degrading the polymers and without forming lumps. Suitable equipment for dissolving polyacrylamide powders is necessary on-site.

For oilfield applications, such as enhanced oil recovery or for mining applications large amounts of polyacrylamides need to be available at one location, i.e. at an oilfield or at a mining area. By way of example, even for flooding only a medium size oilfield it may be necessary to inject some thousand m³ of polymer solution per day into the oil- bearing formation and usually the process of polymer flooding continues for months or even years. So, for a polymer concentration of only 0.2 wt. % and an injection rate of 5000 m³/day 10 t of polymer powder are needed per day and need to be dissolved in an aqueous fluid. It has been suggested not to dry the aqueous polyacrylamide gels after manufacture but directly dissolving said polyacrylamide gels in water thereby obtaining diluted aqueous solutions of polyacrylamides without drying and re-dissolving the dry powder. Working in such a manner saves capital expenditures and operational costs for drying and further post-processing. However, shipping dilute aqueous solutions of

polyacrylamides to customers is not an option because transport costs become extremely high as compared to transporting powders. It has therefore been suggested to manufacture aqueous polyacrylamide solutions on-site.

DE 2 059 241 discloses a process for preparing water-soluble polymers, including acrylamide containing polymers, in which an aqueous solution comprising water- soluble monomers and polymerization initiators is filled into transportable containers for polymerization. In the transportable containers, the aqueous solution polymerizes thereby forming polymer gel. The gel may be transported to the end users who can remove the polymer gels and dissolve them in water. The transportable containers may be -for instance- bags, cans, drums, or boxes having a volume from 2 I to 200 I.

US 4,248,304 discloses a process for recovering oil from subterranean formations wherein a water-in-oil-emulsion of an acrylamide polymer in the presence of an inverting agent is injected into the formation. The water-in-oil emulsion is manufactured in a small chemical plant located near the wells and the manufacturing procedure comprises the steps of forming a water-in-oil emulsion of acrylonitrile, converting a substantially portion of the acrylonitrile to acrylamide using a suitable catalyst, and polymerizing the water-in-oil emulsion of acrylamide in the presence of a free radical polymerization catalyst. The catalyst may be a copper catalyst.

ZA 8303812 discloses a process for preparing polyacrylamides comprising

polymerizing acrylamide and optionally suitable comonomers on-site and transferring the polymer formed to its desired place of use on site without drying or concentrating. The polymerization can be carried out as an emulsion polymerization, bead

polymerization, or as solution / dispersion polymerization. The polymer may be pumped from the polymerization reactor to the position on site where it is used.

WO 84/00967 A1 discloses an apparatus and method for the continuous production of aqueous polymer solutions, in particular partially hydrolyzed polyacrylamide. The apparatus comprises a polymerization reactor, a hydrolysis reactor and a diluter. The polymerization may be performed on-site and the solutions may be used in secondary or tertiary oil recovery.

US 4,605,689 discloses a method for on-site production of aqueous polyacrylamide solutions for enhanced oil recovery. In a first step an aqueous polyacrylamide gel is provided by polymerizing acrylamide and preferably acrylic acid as comonomer. The polyacrylamide gel obtained is conveyed together with a minor amount of aqueous solvent through at least one static cutting device thereby obtaining a slurry of small gel particles in water, the gel particles are dissolved in the aqueous solvent which forms a homogeneous solution concentrate which is then readily diluted with aqueous solvent thereby obtaining a diluted aqueous polyacrylamide solution.

US 4,845,192 discloses a method of rapidly dissolving particles of gels of water-soluble polymers comprising forming a suspension of such gel particles in water and subjecting said suspension to instantaneous and momentary conditions of high shearing effective to finely slice said particles.

Our older application PCT/EP2017/059392 relates to a process for producing an aqueous polymer solution comprising the steps of providing an aqueous

polyacrylamide gel comprising at least 10 % by weight of active polymer, cutting the aqueous polyacrylamide gel by means of an aqueous liquid at a pressure of at least 150 bar to reduce the size of the aqueous polyacrylamide gel, and dissolving the aqueous polyacrylamide gel in an aqueous liquid.

Our older application PCT/EP2017/059759 relates to a method of preparing an aqueous polyacrylamide solution, comprising hydrolyzing acrylonitrile in water in presence of a biocatalyst thereby obtaining an acrylamide solution, directly

polymerizing the acrylamide solution thereby obtaining a polyacrylamide gel, and directly dissolving the polyacrylamide gel by addition of water thereby obtaining an aqueous polyacrylamide solution. The method may be carried out on-site.

Our older application PCT/EP2017/059736 relates to a method of preparing an aqueous polyacrylamide solution, comprising hydrolyzing acrylonitrile in water in presence of a biocatalyst thereby obtaining an acrylamide solution, directly

polymerizing the acrylamide solution thereby obtaining a polyacrylamide gel, and directly dissolving the polyacrylamide gel by addition of water by means of a mixer comprising a rotatable impeller thereby obtaining an aqueous polyacrylamide solution. The method may be carried out on-site.

Our older application PCT/EP2017/059761 relates to a method of preparing an aqueous polyacrylamide solution, comprising hydrolyzing acrylonitrile in water in presence of a biocatalyst thereby obtaining an acrylamide solution, directly

polymerizing the acrylamide solution thereby obtaining a polyacrylamide gel, and directly dissolving the polyacrylamide gel by addition of water by means of water-jet cutting, thereby obtaining an aqueous polyacrylamide solution. The method may be carried out on-site. WO 2016/006556 A1 describes a method for producing a compound using a continuous tank reactor which is provided with two or more reaction tanks for producing the compound and with a reaction liquid feeding pipe that feeds a reaction liquid from an upstream reaction tank to a downstream reaction tank, said method being characterized in that the Reynold's number of the reaction liquid that flows in the reaction liquid feeding pipe is configured to be 1800-22000. The tank reactor may be mounted in a portable container. The compound may be acrylamide produced by conversion from acrylonitrile by means of a biocatalyst.

The production of polyacrylamide solution on-site saves equipment and operational costs for drying and re-dissolving of polyacrylamides on the one hand. On the other hand, for every point of consumption a separate plant is necessary which also requires a significant investment. Furthermore, raw materials for the production need to be shipped to a large plurality of sites which causes significant costs for transport and logistics.

It was an object of the present invention to provide an improved process for manufacturing aqueous solutions of polyacrylamides which avoids building a complete plant for every point of consumption. Accordingly, in one embodiment of the present invention, a process for producing an aqueous polyacrylamide solution by polymerizing an aqueous solution comprising at least acrylamide thereby obtaining an aqueous polyacrylamide gel and dissolving said aqueous polyacrylamide gel in water has been found, wherein the process comprises at least the following steps:

[1 ] Radically polymerizing an aqueous monomer in the presence of suitable

initiators for radical polymerization under adiabatic conditions at a location A, wherein

• the aqueous monomer solution comprises at least water and 5 % to 45 % by weight -relating to the total of all components of the aqueous monomer solution- of water-soluble, monoethylenically unsaturated monomers at a location A, wherein said water-soluble, monoethylenically unsaturated monomers comprise at least acrylamide, and wherein the temperature ΤΊ of the aqueous monomer solution does not exceed 30°C before onset of polymerization, and

• the polymerization is performed in a transportable polymerization unit

having a volume of 1 m³ to 40 m³,

thereby obtaining an aqueous polyacrylamide gel having a temperature T2 of 50°C to 90°C which is hold in the transportable polymerization unit,

[2] transporting the transportable polymerization unit filled with the aqueous

polyacrylamide gel from location A to a different location B, wherein the transport time is from 6 hours to 14 days,

[3] removing the aqueous polyacrylamide gel from the transportable

polymerization unit through the closable bottom opening at the location B, and

[4] dissolving the aqueous polyacrylamide gel in an aqueous liquid at the location B, thereby obtaining an aqueous polyacrylamide solution. In another embodiment of the invention additional measures have been found, in order to ensure transport of the aqueous polyacrylamide gel without gel damage, in particular at high temperatures T2 and/or long transport times.

List of figures:

Figure 1 Schematic representation of a storage unit for monomers with internal temperature control unit.

Figure 2 Schematic representation of a storage unit for monomers with external temperature control unit.

Figure 3 Schematic representation of a bio acrylamide reactor.

Figure 4 Schematic representation of a monomer make-up unit.

Figure 5 Schematic representation of a transportable polymerization unit P1 .

Figure 6 Schematic representation of the transport of a transportable polymerization unit.

Figure 7 Gel Cooling Curve (simulation).

Figure 8 Schematic representation of a transportable polymerization unit P1

connected with comminution unit.

Figure 9 Schematic representation of a water-jet cutting unit.

Figure 10 Schematic representation of another embodiment of a water-jet cutting unit.

Figure 1 1 Schematic representation of another embodiment of a water-jet cutting unit.

Figure 12 Schematic representation of another embodiment of a water-jet cutting unit.

Figure 13 Schematic representation of a water-jet cutting unit comprising additionally static cutting units.

Figure 14 Schematic representation of a water-jet cutting unit combined with a hole perforation plate (one nozzle). List of figures (cont):

With regard to the invention, the following can be stated specifically:

By means of the process according to the present invention, it is possible to prepare aqueous solutions of polyacrylamides.

Polyacrylamides

The term "polyacrylamides" as used herein means water-soluble homopolymers of acrylamide, or water-soluble copolymers comprising at least 10 %, preferably at least 20 %, and more preferably at least 30 % by weight of acrylamide and at least one additional water-soluble, monoethylenically unsaturated monomer different from acrylamide, wherein the amounts relate to the total amount of all monomers in the polymer. Copolymers are preferred.

The term "water-soluble monomers" in the context of this invention means that the monomers are to be soluble in the aqueous monomer solution to be used for polymerization in the desired use concentration. It is thus not absolutely necessary that the monomers to be used are miscible with water without any gap; instead, it is sufficient if they meet the minimum requirement mentioned. It is to be noted that the presence of acrylamide in the monomer solution might enhance the solubility of other monomers as compared to water only. In general, the solubility of the water-soluble monomers in water at room temperature should be at least 50 g/l, preferably at least 100 g/l.

Basically, the kind and amount of water-soluble, monoethylenically unsaturated comonomers to be used besides acrylamide is not limited and depends on the desired properties and the desired use of the aqueous solutions of polyacrylamides to be manufactured.

Neutral comonomers

In one embodiment of the invention, comonomers may be selected from uncharged water-soluble, monoethylenically unsaturated monomers. Examples comprise methacrylamide, N-methyl(meth)acrylamide, N,N'-dimethyl(meth)acrylamide, N- methylol(meth)acrylamide or N-vinylpyrrolidone. Further examples have been mentioned in WO 2015/158517 A1 page 7, lines 9 to 14.

Anionic comonomers

In a further embodiment of the invention, comonomers may be selected from water- soluble, monoethylenically unsaturated monomers comprising at least one acidic group, or salts thereof. The acidic groups are preferably selected from the group of - COOH, -SO3H and -PO3H2 or salts thereof. Preference is given to monomers comprising COOH groups and/or -SO3H groups or salts thereof. Suitable counterions include especially alkali metal ions such as Li⁺, Na⁺ or K⁺, and also ammonium ions such as NH4⁺ or ammonium ions having organic radicals. Examples of ammonium ions having organic radicals include [NH(CH₃)₃]⁺, [NH₂(CH₃)₂]⁺, [NH₃(CH₃)]⁺, [NH(C₂H₅ )₃]⁺, [NH2(C₂H₅ )₂]⁺, [NH₃(C₂H₅ )]⁺, [NH₃(CH₂CH₂OH)]⁺, [H₃N-CH₂CH₂-NH₃]²⁺ or [H(H₃C)₂N- CH₂CH₂CH₂NH₃]²⁺.

Examples of monomers comprising -COOH groups include acrylic acid, methacrylic acid, crotonic acid, itaconic acid, maleic acid or fumaric acid or salts thereof.

Preference is given to acrylic acid or salts thereof.

Examples of monomers comprising -SO3H groups or salts thereof include vinylsulfonic acid, allylsulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid (ATBS), 2- methacrylamido-2-methylpropanesulfonic acid, 2-acrylamidobutanesulfonic acid, 3- acrylamido-3-methylbutanesulfonic acid or 2-acrylamido-2,4,4-trimethylpentanesulfonic acid. Preference is given to 2-acrylamido-2-methylpropanesulfonic acid (ATBS) or salts thereof. Examples of monomers comprising -PO3H2 groups or salts thereof include

vinylphosphonic acid, allylphosphonic acid, N-(meth)acrylamidoalkylphosphonic acids or (meth)acryloyloxyalkylphosphonic acids, preferably vinylphosphonic acid. Preferred monomers comprising acidic groups comprise acrylic acid and/or ATBS or salts thereof.

Cationic comonomers In a further embodiment of the invention, comonomers may be selected from water- soluble, monoethylenically unsaturated monomers comprising cationic groups. Suitable cationic monomers include especially monomers having ammonium groups, especially ammonium derivatives of N-(co-aminoalkyl)(meth)acrylamides or co-aminoalkyl

(meth)acrylates such as 2-trimethylammonioethyl acrylate chloride H2C=CH-CO- CH2CH₂N⁺(CI-l3)3 Ch (DMA3Q). Further examples have been mentioned in WO

2015/158517 A1 page 8, lines 15 to 37. Preference is given to DMA3Q.

Associative comonomers In a further embodiment of the invention, comonomers may be selected from

associative monomers.

Associative monomers impart hydrophobically associating properties to

polyacrylamides. Associative monomers to be used in the context of this invention are water-soluble, monoethylenically unsaturated monomers having at least one hydrophilic group and at least one, preferably terminal, hydrophobic group. Examples of associative monomers have been described for example in WO 2010/133527, WO 2012/069478, WO 2015/086468 or WO 2015/158517. "Hydrophobically associating copolymers" are understood by a person skilled in the art to mean water-soluble copolymers which, as well as hydrophilic units (in a sufficient amount to assure water solubility), have hydrophobic groups in lateral or terminal positions. In aqueous solution, the hydrophobic groups can associate with one another. Because of this associative interaction, there is an increase in the viscosity of the aqueous polymer solution compared to a polymer of the same kind that merely does not have any associative groups.

Examples of suitable associative monomers comprise monomers having the general formula

(I) wherein R¹ is H or methyl, R² is a linking hydrophilic group and R³ is a terminal hydrophobic group. Further examples comprise having the general formula H₂C=C(R¹)-R²-R³-R⁴ (II) wherein R¹, R² and R³ are each as defined above, and R⁴ is a hydrophilic group. The linking hydrophilic R² group may be a group comprising ethylene oxide units, for example a group comprising 5 to 80 ethylene oxide units, which is joined to the H2C=C(R¹)- group in a suitable manner, for example by means of a single bond or of a suitable linking group. In another embodiment, the hydrophilic linking group R² may be a group comprising quaternary ammonium groups.

In one embodiment, the associative monomers are monomers of the general formula

wherein R¹ has the meaning defined above and k is a number from 10 to 80, for example, 20 to 40. R^3a is an aliphatic and/or aromatic, straight-chain or branched hydrocarbyl radical having 8 to 40 carbon atoms, preferably 12 to 32 carbon atoms. Examples of such groups include n-octyl, n-decyl, n-dodecyl, n-tetradecyl, n-hexadecyl or n-octadecyl groups. In a further embodiment, the groups are aromatic groups, especially substituted phenyl radicals, especially distyrylphenyl groups and/or tristyrylphenyl groups.

In another embodiment, the associative monomers are monomers of the general formula H2C=C(R¹)-0-(CH2)n-0-(CH2CH20)x-(CH2-CH(R⁵)0)y-(CH2CH₂0)zH (V), wherein R¹ is defined as above and the R⁵ radicals are each independently selected from hydrocarbyl radicals comprising at least 2 carbon atoms, preferably from ethyl or propyl groups. In formula (V) n is a natural number from 2 to 6, for example 4, x is a number from 10 to 50, preferably from 12 to 40, and for example, from 20 to 30 and y is a number from 5 to 30, preferably 8 to 25. In formula (V), z is a number from 0 to 5, for example 1 to 4, i.e. the terminal block of ethylene oxide units is thus merely optionally present. In an embodiment of the invention, it is possible to use at least two monomers (V), wherein the R¹ and R⁶ radicals and indices n, x and y are each the same, but in one of the monomers z = 0 while z > 0 in the other, preferably 1 to 4. In another embodiment, the associative monomers are cationic monomers. Examples of cationic associative monomers have been disclosed in WO 2015/158517 A1 , page 1 1 , line 20 to page 12, lines 14 to 42. In one embodiment, the cationic monomers having the general formula H₂C=C(R¹)-C(=0)0-(CH2)k-N⁺(CH3)(CH₃)(R⁶) X^" (VI) or H₂C=C(R¹)-C(=0)N(R )-(CH2)k-N⁺(CH3)(CH₃)(R⁶) X^" (VII) may be used, wherein R has the meaning as defined above, k is 2 or 3, R⁶ is a hydrocarbyl group, preferably an aliphatic hydrocarbyl group, having 8 to 18 carbon atoms, and X^" is a negatively charged counterion, preferably Ch and/or Br. Further comonomers

Besides water-soluble monoethylenically unsaturated monomers, also water-soluble, ethylenically unsaturated monomers having more than one ethylenic group may be used. Monomers of this kind can be used in special cases in order to achieve easy crosslinking of the acrylamide polymers. The amount thereof should generally not exceed 2% by weight, preferably 1 % by weight and especially 0.5% by weight, based on the sum total of all the monomers. More preferably, the monomers to be used in the present invention are only monoethylenically unsaturated monomers.

Composition of polyacrylamides

The specific composition of the polyacrylamides to be manufactured according the process of the present invention may be selected according to the desired use of the polyacrylamides.

Preferred polyacrylamides comprise, besides at least 10 % by weight of acrylamide, at least one water-soluble, monoethylenically unsaturated comonomer, preferably at least one comonomer selected from the group of acrylic acid or salts thereof, ATBS or salts thereof, associative monomers, in particular those of formula (V) or DMA3Q, more preferably at least one comonomer selected from acrylic acid or salts thereof, ATBS or salts thereof, associative monomers, in particular those of formula (V). In one embodiment, the polyacrylamides comprise 20 % to 90 % by weight of acrylamide and 10 % to 80 % by weight of acrylic acid and/or salts thereof, wherein the amounts of the monomers relate to the total of all monomers in the polymer.

In one embodiment, the polyacrylamides comprise 20 % to 40 % by weight of acrylamide and 60 % to 80 % by weight of acrylic acid and/or salts thereof.

In one embodiment, the polyacrylamides comprise 55 % to 75 % by weight of acrylamide and 25 % to 45 % by weight of acrylic acid and/or salts thereof. In one embodiment, the polyacrylamides comprise 45 % to 75 % by weight of acrylamide and 25 % to 55 % by weight of ATBS and/or salts thereof.

In one embodiment, the polyacrylamides comprise 30 % to 80 % by weight of acrylamide, 10 % to 40 % by weight of acrylic acid and/or salts thereof, and 10 % to 40 % by weight of ATBS and/or salts thereof. In one embodiment, the polyacrylamides comprise 45 % to 75 % by weight of acrylamide, 0.1 to 5 %, preferably 0.1 to 2 % by weight of at least one associative monomer of the general formulas (I) or (II) mentioned above and 10 to 54.9 % by weight of acrylic acid and/or ATBS and/or salts thereof. Preferably, the associative monomer(s) have the general formula (V) including the preferred embodiments mentioned above.

In one embodiment, the polyacrylamides comprise 60 % to 75 % by weight of acrylamide, 0.1 to 5 %, preferably 0.1 to 2 % by weight of at least one associative monomer of the general formula (V) mentioned above, including the preferred embodiments, and 20 to 39.9 % by weight of acrylic acid or salts thereof.

In one embodiment, the polyacrylamides comprise 45 % to 55 % by weight of acrylamide, 0.1 to 5 %, preferably 0.1 to 2 % by weight of at least one associative monomer of the general formula (V) mentioned above, including the preferred embodiments, and 40 to 54.9 % by weight of acrylic acid or salts thereof.

In one embodiment, the polyacrylamides comprise 60 % to 99 % by weight of acrylamide and 1 % to 40 % by weight of DMA3Q.

In one embodiment, the polyacrylamides comprise 10 % to 50 % by weight of acrylamide and 50 % to 90 % by weight of DMA3Q.

In one embodiment, the polyacrylamides comprise 90 to 99.5 % by weight of acrylamide, 0.5 to 2 % by weight of at least one associative monomer, and 0 % to 9.5 % by weight of and anionic monomer, for example ATBS or a cationic monomer, for example DM3AQ. Preferably, the associative monomer(s) have the general formula (V) including the preferred embodiments mentioned above. In all embodiments mentioned above, the amount of the monomers relates to the total of all monomers in the polyacrylamide. Further water-soluble, monoethylenically unsaturated monomers may be present besides those specifically mentioned, however, the embodiments each include also one embodiment in which besides the monomers specifically mentioned no further monomers are present, i.e. in these embodiments the total amount of the monomers specifically mentioned is 100 % by weight.

The weight average molecular weight M_w of the polyacrylamides to be manufactured usually ranges from 1 ^*10⁶ g/mol to 50^*10⁶ g/mol, preferably from 1.5^*10⁶ g/mol to 40^*10⁶ g/mol, more preferably from 2^*10⁶ g/mol to 30^*10⁶ g/mol, and for example from 5^*10⁶ g/mol to 25^*10⁶ g/mol. Locations A and B

The process for producing an aqueous polyacrylamide solution according to the present invention is carried out at two different locations A and B and includes transporting an aqueous polyacrylamide gel from location A to location B.

At location A, an aqueous monomer solution comprising acrylamide is polymerized in a transportable polymerization unit (step [1]) thereby obtaining an aqueous

polyacrylamide gel hold in the transportable polymerization unit. In a preferred embodiment of the invention, acrylamide is also manufactured at location A by hydrolysis of acrylonitrile by means of a biocatalyst (hereinafter referred to as step [0]).

In step [2], the transportable polymerization unit filled with the aqueous polyacrylamide gel is transported from location A to a different location B in a transportable

polymerization unit.

At location B, the aqueous polyacrylamide gel is removed from the transportable polymerization unit (step [3]) and dissolved in water thereby obtaining an aqueous polyacrylamide solution (step [4]).

Location B may be a location at which the polyacrylamide solutions are used or at least a location close to such a location of use. However, in other embodiments location B may be apart from such location of use and it is necessary to transport the aqueous polyacrylamide solutions from location B to the location of use. Such a transport may be performed by means of a pipeline although other means of transport are not excluded. In an embodiment, the aqueous polyacrylamide solution may be distributed from location B to a plurality of locations of use by means of pipelines.

Subterranean, oil-bearing reservoirs typically extend over a large area. Length and width of a subterranean, oil-bearing reservoir may be up to several hundred kilometers. For producing oil from such subterranean, oil-bearing reservoirs typically many oil wells, injection wells as well as production wells, are distributed over the subterranean reservoir. Similarly, regions comprising valuable minerals such as ores or oil sands may also extend over a large area and individual mines may be distributed in the mining area.

In one embodiment, location B may be at an oil and/or gas well to be treated with aqueous polyacrylamide solutions or close to such an oil and/or gas well. Examples comprise oil wells which into which aqueous polyacrylamide solutions are injected in course of enhanced oil operations, production wells whose productivity is enhanced by injection of fracturing fluids comprising polyacrylamides as friction reducers, or wells which are drilled and aqueous polyacrylamide solutions are used for making the drilling fluid. In another embodiment, location B may be in between a plurality of such oil and/or gas wells or at one of them and the aqueous polyacrylamide solution is distributed to all injection wells, for example by means of pipelines. In the field of mining, location B may be a location at or close to a tailings ponds in which mineral tailings are dewatered using aqueous polyacrylamide solutions. In one embodiment of the invention location B may be a location for the treatment of red mud, a by-product of the Bayer process for manufacturing aluminium. In other embodiments, location B may be at a paper production site, at sewage works, at seawater desalination plants or at sites for manufacturing agricultural formulations.

Location A is apart from location B. In one embodiment, location A may be a fixed chemical plant apart from location(s) B.

In a preferred embodiment of the invention, location A is a local hub which provides a plurality of different locations B with aqueous polyacrylamide gels. In an embodiment, the local hub is located at a central point having good transport connections in order to ensure easy and economic supply with raw materials.

In one embodiment, location A may at a central point over a subterranean, oil-bearing formation or a central point in between different subterranean, oil-bearing formations and from location A a plurality of oil wells to be treated is provided with aqueous polyacrylamide gels for further processing.

In another embodiment, location A is at a central point in a mining area and from location A a plurality of tailing ponds is provided with aqueous polyacrylamide gels for further processing.

The distance between location A and the location(s) B is not specifically limited.

However, in order to limit the costs of transporting the aqueous polymer gels, location A should be located close to the locations B or at least not too far apart from the locations B. Having said that, the abovementioned dimensions of mining areas or subterranean, oil-bearing formations should be kept in mind. So, even when location A is a local hub as outlined above, the local hub A and the locations B may be apart from each other up a few hundred kilometers.

By the way of example, the distance between location A and location(s) B may range from 1 to 3000 km, in particular from 10 km to 3000 km, for example from 10 to 1500 km or from 20 km to 500 km or from 30 to 300 km. Modular Plant

While it is possible to perform at least some steps of the process in fixed plants, it is preferred to perform the entire process of manufacturing aqueous polyacrylamide solutions according to the present invention in a modular manner using relocatable units.

Each relocatable unit bundles certain functions of the plant. Examples of such relocatable units comprise units for storing and optionally cooling the monomers and other raw materials, hydrolyzing acrylonitrile, mixing monomers, polymerization and gel dissolution. Details will be provided below. For performing the process according to the present invention individual units are connected with each other in a suitable manner thereby obtaining a production line. "Relocatable unit" means that the unit is transportable basically as a whole and that is it not necessary to disassemble the entire unit into individual parts for transport.

Transport may happen on trucks, railcars or ships.

In one embodiment, such modular, relocatable units are containerized units which may be transported in the same manner as closed intermodal containers for example on trucks, railcars or ships. Intermodal containers are large standardized (according to ISO 668) shipping containers, in particular designed and built for intermodal freight transport. Such containers are also known as ISO containers. Such ISO containers may have external dimensions of a height of ~ 2.59 m, a width of ~ 2.44 m and a length of ~ 6.05 m. Larger ISO containers have external dimensions of a height of ~ 2.59 m, a width of - 2.44 m and a length of -12.19 m.

In another embodiment, the relocatable units may be fixed on trucks or on trailers. With other words, for such relocatable units not a container or something similar is deployed at location A or location B, but the entire truck or the trailer including the unit in its loading spaces is deployed. The trucks or trailers advantageously also function as platform for the units on the ground. Also, two or more different units may be mounted together on a truck or trailer. The relocatable units are combined at the locations A and B, thereby obtaining modular production plants for performing the process according to the present invention.

Such a modular construction using relocatable units provides the advantage, that the plants at location A and at location B may be easily relocated if aqueous

polyacrylamide solutions are no longer needed at one location but at another location. By the way of example, in enhanced oil recovery aqueous polyacrylamide solutions are injected into a subterranean, oil-bearing formations through one or more than one injection wells sunk into the formation. Such an injection may continue for months or even years. For such an application, location B should be at or at least close to the injection wells and location B is provided with aqueous polyacrylamide gels from a location A. However, at some point in time no further oil production is possible. It may be possible to continue oil production by injecting into other injection wells located at other places over the subterranean, oil-bearing formation. The modular plant at location B may then easily be relocated to another location B at or close to the new wells for injection. Depending on the distance of the new location B, location A may also be relocated or location A may not be relocated but the new location B may be served from the same location A.

Provision of acrylamide

Acrylamide may be synthesized by partial hydrolysis of acrylonitrile using suitable catalysts. It is known in the art to use copper catalysts or other metal containing catalysts and it is also known to use biocatalysts capable of converting acrylonitrile to acrylamide. Pure acrylamide is a solid, however, typically acrylamide -whether made by bio catalysis or copper catalysis- is provided as aqueous solution, for example as aqueous solution comprising about 50 % by wt. of acrylamide.

Acrylamide obtained by means of biocatalysts (often referred to as "bio acrylamide") can be distinguished from acrylamide obtained by means of copper catalysts or other metal containing catalysts because the latter still comprises at least traces of copper or other metals. Acrylamide obtained by means of biocatalysts may still comprise traces of the biocatalyst. Such traces of metals or biocatalyst can be detected by analysis.

For the process according to the present invention, an aqueous acrylamide solution is used which has been obtained by hydrolyzing acrylonitrile in water in presence of a biocatalyst capable of converting acrylonitrile to acrylamide. As will be detailed below, using biocatalysts for hydrolyzing acrylonitrile has significant advantages for the present invention, in particular for transporting the aqueous polyacrylamide gel. In one embodiment of the invention, aqueous solutions of bio acrylamide for use in the process according to the present invention may be manufactured at another location, for example in a fixed chemical plant, and shipped to location A.

In a preferred embodiment of the present invention the manufacture of bio acrylamide is performed at location A (hereinafter designated as process step [0]). Manufacturing bio acrylamide at location A saves significant transport costs.

Acrylonitrile is a liquid and may be transported as pure compound to location A. The molecular weight of acrylamide is ~ 34 % higher than that of acrylonitrile and acrylamide is typically provided as ~ 50 % aqueous solution. So, for a 50 % aqueous solution of acrylamide the mass to be transported is about 2.5-fold as much as compared to transporting pure acrylonitrile. Transporting pure, solid acrylamide means transporting only ~ 34 % more mass as compared to transporting pure acrylonitrile, however, additional equipment for handling and dissolving the solid acrylamide is necessary at location A.

Step [0] - Hydrolysis of acrylonitrile

As already outlined above, step [0] is only optional for the process according to the present invention, however, in a preferred embodiment of the invention, the process according to the invention includes step [0]. In course of step [0] acrylonitrile is hydrolyzed in water in presence of a biocatalyst capable of converting acrylonitrile to acrylamide thereby obtaining an aqueous acrylamide solution. Step [0] is performed at location A. Provision of acrylonitrile

Acrylonitrile for step [0] may be stored in one or more than one relocatable storage units. The storage unit comprises a storage vessel. The volume of the storage vessel is not specifically limited and may range from 50 m³ to 150 m³, for example it may be about 100 m³. Preferably, the storage vessel should be double walled and should be horizontal. Such a construction avoids installing a pit for the collection of any leakage thereby ensuring an easier and quicker relocation of the storage unit. Double-walled vessels may be placed on every good bearing soil. The storage unit furthermore comprises means for charging and discharging the vessel, means for controlling the pressure in the vessel, for example a valve for settling low-pressure or overpressure, and means for controlling the temperature of the acrylonitrile which preferably should not exceed 25°C. It furthermore may comprise means for measurement and control to the extent necessary. Examples of relocatable storage units comprise relocatable cuboid, storage tanks, preferably double-walled tanks.

Other examples comprise tank containers having a cuboid frame, preferably a frame according to the ISO 668 norm mentioned above and one or more storage vessels mounted into the frame. Such normed tank containers may be stacked and transported on trucks, railcars or ships in the same manner closed intermodal containers. Basically, temperature control may be performed by any kind of temperature controlling unit. Temperature control may require -depending on the climatic conditions prevailing at location A- cooling or heating the contents of the storage units. Regarding the monomers, temperature control typically means cooling, because it should be avoided that the monomers become too hot. In one embodiment, an internal heat exchanger may be used for cooling or heating, i.e. a heat exchanger mounted inside of the storage vessel. The coolant is provided to the heat exchanger by a suitable cooling or heating unit mounted outside of the storage vessel. In another embodiment of the invention, for temperature control an external temperature control cycle, for example a cooling cycle is used, which comprises a pump which pumps the monomer from the storage vessel through a heat exchanger and back into the storage vessel. The temperature control cycle may be a separate, relocatable temperature control unit comprising pump and heat exchanger and which is connected with the storage vessel by pipes or flexible tubes.

In another embodiment, the temperature control cycle may be integrated into relocatable storage unit. It may -for example- be located at one end of the unit besides the storage vessel.

Figure 1 schematically represents one embodiment of a monomer storage unit comprising an integrated temperature control cycle. It comprises a frame (1 ). The frame may in particular be a cuboid frame preferably having standardized container dimensions which eases transport. The relocatable storage unit furthermore comprises a double-walled vessel mounted into the frame comprising an outer wall (2) and an inner wall (3). In other embodiments, there is no such frame (1 ) but the storage vessel is self-supporting. The storage vessel is filled with acrylonitrile. The storage unit furthermore comprises an external temperature control cycle comprising at least a pump and a temperature control unit. For cooling, acrylonitrile is circulated by means of a pump (4) from the storage vessel to the temperature control unit (5) and back into the storage vessel. The amount of acrylonitrile to be circulated in the temperature control cycle in order to control the temperature at an acceptable level, for example below 25°C depends in particular on the outside temperature and the internal temperature envisaged. In one embodiment, 10% to 100% of the volume of acrylonitrile in the vessel may be circulated per hour.

Figure 2 represents a schematically another embodiment of a monomer storage unit. It comprises a cuboic, preferably double-walled storage vessel (6). If necessary, the storage vessel (6) is connected with an external, relocatable temperature control unit (7). Acrylonitrile may be provided to location A by road tankers, ISOtanks or rail cars and pumped into the relocatable storage vessel(s). The acrylonitrile may be removed from the relocatable storage vessel through a bottom valve by means of gravity or it may be pumped, for example from the upper side using a suitable pump.

Biocatalysts

As biocatalyst for performing step [0], nitrile hydratase enzymes can be used, which are capable of catalyzing the hydrolysis of acrylonitrile to acrylamide. Typically, nitrile hydratase enzymes can be produced by a variety of microorganisms, for instance microorganisms of the genus Bacillus, Bacteridium, Micrococcus, Brevibacterium, Corynebacterium, Pseudomonas, Acinetobacter, Xanthobacter, Streptomyces,

Rhizobium, Klebsiella, Enterobacter, Erwinia, Aeromonas, Citrobacter, Achromobacter, Agrobacterium, Pseudonocardia and Rhodococcus. WO 2005/054456 discloses the synthesis of nitrile hydratase within microorganisms and therein it is described that various strains of Rhodococcus rhodochrous species have been found to very effectively produce nitrile hydratase enzymes, in particular Rhodococcus rhodochrous NCI MB 41 164. Such microorganisms, suitable as biocatalyst for the enzymatic conversion of acrylonitrile to acrylamide, which are known for a person skilled in the art, are able to be applied in a relocatable bioconversion conversion unit according to the present invention. Additionally, the specific methods of culturing (or cultivation, or fermentation) and/or storing the microorganism as well as the respective sequences of polynucleotides which are encoding the enzyme, particularly the nitrile hydratase, are known in the art, e.g. WO 2005/054456, WO 2016/050816, and are applicable in context of the present invention. Within the present invention nitrile hydratase and amidase producing microorganisms may be used for converting a nitrile compound into the corresponding amide compound as it is described for example in WO 2016/050816.

The terms "nitrile hydratase (NHase) producing microorganism" or "microorganism" or "biocatalysts" or the like, have the meaning to be able to produce (i.e. they encode and express) the enzyme nitrile hydratase (also referred to as, e.g., NHase) either per se (naturally) or they have been genetically modified respectively. Microorganisms which have been "genetically modified" means that these microorganisms have been manipulated such that they have acquired the capability to express the required enzyme NHase, e.g. by way of incorporation of a naturally and/or modified nitrile hydratase gene or gene cluster or the like. Produced products of the microorganisms that can be used in the context of the present invention are also contemplated, e.g. suspensions obtained by partial or complete cell disruption of the microorganisms. The terms "nitrile hydratase (NHase) producing microorganism" or "microorganism" or "biocatalysts" or the like, include the cells and/or the processed product thereof as such, and/or suspensions containing such microorganisms and/or processed products. It is also envisaged that the microorganisms and/or processed products thereof are further treated before they are employed in the embodiments of the present invention. "Further treated" thereby includes for example washing steps and/or steps to concentrate the microorganism etc. It is also envisaged that the microorganisms that are employed in the embodiments of the present invention have been pre-treated by a for example drying step. Also known methods for cultivating of the microorganisms and how to optimize the cultivation conditions via for example addition of urea or cobalt are described in WO 2005/054456 and are compassed by the embodiments of the present invention. Advantageously, the microorganism can be grown in a medium containing acetonitrile or acrylonitrile as an inducer of the nitrile hydratase. Preferably, the biocatalyst for converting acrylonitrile to acrylamide may be obtained from culturing the microorganism in a suitable growth medium. The growth medium, also called fermentation (culture) medium, fermentation broth, fermentation mixture, or the like, may comprise typical components like sugars, polysaccharides, which are for example described in WO 2005/054489 and which are suitable to be used for the culturing the microorganism of the present inventions to obtain the biocatalyst. For storage of the microorganism, the fermentation broth preferably is removed in order to prevent putrefaction, which could result in a reduction of nitrile hydratase activity. The methods of storage described in WO 2005/054489 may be applied according to the present invention ensuring sufficient biocatalyst stability during storage. Preferably, the storage does not influence biocatalytic activity or does not lead to a reduction in biocatalytic activity. The biocatalyst may be stored in presence of the fermentations broth components.

Biocatalyst make-up

The biocatalysts that are used according to the present invention in a relocatable plant can for example be cultured under any conditions suitable for the purpose in accordance with any of the known methods, for instance as described in the mentioned prior art of this specification. The biocatalyst may be used as a whole cell catalyst for the generation of amide from nitrile. The biocatalyst may be (partly) immobilized for instance entrapped in a gel or it may be used for example as a free cell suspension. For immobilization well known standard methods can be applied like for example entrapment cross linkage such as glutaraldehyde-polyethyleneimine (GA-PEI) crosslinking, cross linking to a matrix and/or carrier binding etc., including variations and/or combinations of the aforementioned methods. Alternatively, the nitrile hydratase enzyme may be extracted and for instance may be used directly in the process for preparing the amide. In a preferred embodiment, the microorganisms are whole cells. The whole cells may be pre-treated by a drying step. Suitable drying methods and/or drying conditions are disclosed e.g. in WO 2016/050816 and WO 2016/050861 and the know art can be applied in the context of the present invention for the use in a relocatable bioconversion unit.

The microorganisms that are employed in the context of the present invention are in a preferred embodiment used in an aqueous suspension and in a more preferred embodiment are free whole cells in an aqueous suspension. The term "aqueous suspension" thereby includes all kinds of liquids, such as buffers or culture medium that are suitable to keep microorganisms in suspension. Such liquids are well-known to the skilled person and include for example storage buffers at suitable pH such as storage buffers which are used to deposit microorganisms, TRIS-based buffers, saline based buffers, water in all quality grades such as distilled water, pure water, tap water, or sea water, culture medium, growing medium, nutrient solutions, or fermentation broths, for example the fermentation broth that was used to culture the

microorganisms. The biocatalyst may be provided as powder or as aqueous suspension to location A. If provided as powder it is frequently advisable to prepare an aqueous suspension before adding the catalyst into the bioconversion unit. In an embodiment, the biocatalyst suspension may be conducted by suspending the biocatalyst powder in water in a vessel comprising at least a mixing device, for example a stirrer, one or more inlets for water, the biocatalyst and optionally further additives and one outlet for the biocatalyst suspension. The volume of the vessel may be for example from 0.1 m³ to 1 m³. The concentration of the biocatalyst in the aqueous biocatalyst suspension may be for example from 1 % to 30% by wt., for example from 10 to 20% by wt. relating to the total of all components of the aqueous suspension.

A biocatalyst suspension may be added directly to the bioconversion unit. In another embodiment a concentrated suspension may be diluted before adding it to the bioconversion unit. Bioconversion

The hydrolysis of acrylonitrile to acrylamide by means of a biocatalyst is performed in a suitable bioconversion unit, preferably a relocatable bioconversion unit. Particularly, the bioconversion is performed by contacting a mixture comprising water and acrylonitrile with the biocatalyst. The term "contacting" is not specifically limited and includes for example bringing into contact with, admixing, stirring, shaking, pouring into, flowing into, or incorporating into. It is thus only decisive that the mentioned ingredients come into contact with each other no matter how that contact is achieved.

Therefore, in one embodiment of the present invention step [0] comprises the following steps:

(a) Adding the following components (i) to (iii) to a bioconversion unit to obtain a

composition for bioconversion:

(i) a biocatalyst capable of converting acrylonitrile to acrylamide;

(ii) acrylonitrile;

(iii) aqueous medium; and

(b) performing a bioconversion on the composition obtained in step (a).

The bioconversion can for example be conducted under any conditions suitable for the purpose in accordance with any of the known methods, for instance as described in the mentioned prior art of this specification like e.g. WO 2016/050817, WO 2016/050819, WO 2017/055518.

The conversion of acylonitrile to the acrylamide may be carried out by any of a batch process and a continuous process, and the conversion may be carried out by selecting its reaction system from reaction systems such as suspended bed, a fixed bed, a fluidized bed and the like or by combining different reaction systems according to the form of the catalyst. Particularly, the method of the present invention may be carried out using a semi-batch process. In particular, the term "semi-batch process" as used herein may comprise that an aqueous acrylamide solution is produced in a

discontinuous manner.

According to a non-limiting example for carrying out such a semi-batch process water, a certain amount of acrylonitrile and the biocatalyst are placed in the bioconversion unit. Further acrylonitrile is then added during the bioconversion until a desired content of acrylamide of the composition is reached. After such desired content of acrylamide is reached, the obtained composition is entirely recovered from the reactor, before new reactants are placed therein. In particular, in any one of the methods of the present invention the acrylonitrile may be fed such that the content of acrylonitrile during step (b) is maintained substantially constant at a predetermined value. In general, in any one of the methods of the present invention the acrylonitrile content and/or the acrylamide content during step (b) may be monitored. Methods of monitoring the acrylonitrile contents are not limited and include Fourier Transform Infrared

Spectroscopy (FTIR). In another embodiment, the heat-balance of the reaction may be used for monitoring the process.

Although the conversion of acrylonitrile to the acrylamide may preferably be carried out at atmospheric pressure, it may be carried out under pressure in order to increase solubility of acrylonitrile in the aqueous medium. Because biocatalysts are temperature sensitive and the hydrolysis is an exothermic reaction temperature control is important. The reaction temperature is not specifically restricted provided that it is not lower than the ice point of the aqueous medium. However, it is desirable to carry out the conversion at a temperature of usually 0 to 50°C, preferably 10 to 40°C, more preferably 15 to 30°C. Further suitable condition for the bioconversion according to the present invention are for example described in WO 2017/055518 and are preferably applicable for the method in a relocatable bioconversion unit.

Although the amount of biocatalyst may vary depending on the type of biocatalyst to be used, it is preferred that the activity of the biocatalyst, which is introduced to the reactor, preferably the relocatable bioconversion unit, is in the range of about 5 to 500 U per mg of dried cells of microorganism. Methods for determining the ability of a given biocatalyst (e.g. microorganism or enzyme) for catalyzing the conversion of acrylonitrile to acrylamide are known in the art. As an example, in context with the present invention, activity of a given biocatalyst to act as a nitrile hydratase in the sense of the present invention may be determined as follows: First reacting 100 μΙ of a cell suspension, cell lysate, dissolved enzyme powder or any other preparation containing the supposed nitrile hydratase with 875 μΙ of a 50 mM potassium phosphate buffer and 25 μΙ of acrylonitrile at 25°C on an Eppendorf tube shaker at 1 ,000 rpm for 10 minutes. After 10 minutes of reaction time, samples may be drawn and immediately quenched by adding the same volume of 1 .4% hydrochloric acid. After mixing of the sample, cells may be removed by centrifugation for 1 minute at 10,000 rpm and the amount of acrylamide formed is determined by analyzing the clear supernatant by HPLC. For affirmation of an enzyme to be a nitrile hydratase in context with the present invention, the concentration of acrylamide shall particularly be between 0.25 and 1.25 mmol/l - if necessary, the sample has to be diluted accordingly and the conversion has to be repeated. The enzyme activity may then be deduced from the concentration of acrylamide by dividing the acrylamide concentration derived from HPLC analysis by the reaction time, which has been 10 minutes and by multiplying this value with the dilution factor between HPLC sample and original sample. Activities >5 U/mg dry cell weight, preferably >25 U/mg dry cell weight, more preferably >50 U/mg dry cell weight, most preferably >100 U/mg dry cell weight indicate the presence of a functionally expressed nitrile hydratase and are considered as nitrile hydratase in context with the present invention.

It is preferred, that the concentration of acrylonitrile during the bioconversion should not exceed 6 % by wt. and may for example be in the range from 0.1 % by wt. to 6 % by wt., preferably from 0.2 % by wt. to 5 % by wt., more preferably from 0.3 % by wt. to 4 % by wt., even more preferably from 0.5 % by wt. to 3 % by wt., still more preferably from 0.8 % by wt. to 2 % by wt. and most preferably from 1 % by wt. to 1.5 % by wt., relating to the total of all components of the aqueous mixture. In order to obtain more concentrated solutions of acrylamide the total amount of acrylonitrile should not be added all at once but it should be added stepwise or even continuously keeping the abovementioned concentration limits in mind. The disclosure of WO 2016/050818 teaches a method of additional dosing of acrylonitrile, which is suitable to be used and applied in the present invention.

The concentration of acrylamide in the obtained solution is preferably in the range from 20% to 70%, more preferably in the range from 30% to 65%, even more preferably in the range from 40% to 60%, most preferably in the range from 45% to 55% by weight of acrylamide monomers. The reaction should be carried out in such a manner that the final concentration of acrylonitrile in the final acrylamide solution obtained does not exceed 0.1 % by weight relating to the total of all components of the aqueous solution. Typical reaction times may be from 2 to 20 h, in particular 4 h to 12 h, for example 6 h to 10 h. After completion of the addition of acrylonitrile, the reactor contents is allowed to further circulate for some time to complete the reaction, for example for 1 hour to 3 hours. The remaining contents of acrylonitrile should preferably be less than 100 ppm ACN. Suitable reactors for performing the bioconversion are known to the skilled artisan.

Examples comprise vessels of any shape, for example cylindrical or spherical vessels, or tube reactors. In one embodiment, the continuous tank reactor as disclosed in WO 2016/006556 A1 may be used for bioconversion. Further suitable reactors for the bioconversion according to the present invention are for example described in

US20040175809, EP2336346, EP2518154, JP2014176344, JP2015057968 and such reactors are preferably applicable for the process according to the present invention. Such reactors comprise particularly a pumping circuit, a heat-exchanger and/or an agitating element. In a preferred embodiment of the invention, the bioconversion unit is a relocatable bioconversion unit. In one embodiment, relocatable bioconversion unit is similar to the relocatable storage unit for acrylonitrile as described above. Using largely the same equipment for storing acrylonitrile or other monomers and the bioconversion step contributes to an economic process for manufacturing aqueous acrylamide solutions.

The bioconversion unit comprises a reaction vessel. The volume of the reaction vessel is not specifically limited and may range from 10 m³ to 150 m³, for example it may be about 20 m³ to 50 m³. Preferably, the reaction vessel should be double walled and should be horizontal. Such a construction avoids installing a pit for the collection of any leakage thereby ensuring an easier and quicker relocation of the reaction unit.

The bioconversion unit furthermore comprises means for mixing the reaction mixture and means for controlling the temperature of the contents of the vessel. The hydrolysis of acrylonitrile to acrylamide is an exothermal reaction and therefore heat generated in course of the reaction should be removed in order to maintain an optimum temperature for bioconversion. The bioconversion unit furthermore usually comprises means for measurement and control, for example means for controlling the temperature or for controlling the pressure in the vessel.

For temperature control, the preferred bioconversion unit comprises an external temperature control cycle comprising a pump which pumps the aqueous reactor contents from the storage vessel through a heat exchanger and back into the storage vessel, preferably via an injection nozzle.

In one embodiment, a separate, relocatable temperature control unit is used comprising pump and heat exchanger and which is connected with the bioconversion unit by pipes or flexible tubes. In a preferred embodiment, the temperature control cycle is integrated into the relocatable bioconversion unit. It may -for example- be located at one end of the unit besides the reaction vessel.

The reaction vessel may furthermore comprise means for mixing the aqueous reaction mixture, for example a stirrer.

Surprisingly, it has been found, that the external temperature control cycle described above may also be used as means for mixing. The stream of the aqueous reaction mixture which passes through the temperature control cycle and which is injected back into the reaction vessel causes a circulation of the aqueous reaction mixture within the reaction vessel which is sufficient to mix the aqueous reaction mixture.

Adding acrylonitrile to the contents of the bioconversion unit may be performed in various ways. It may be added into the reaction vessel or it may be added into the temperature control cycle, for example after the pump and before the heat exchanger or after the heat exchanger. Injecting acrylonitrile into the temperature control cycle ensures good mixing of the reaction mixture with freshly added acrylonitrile. Preferably, acrylonitrile is added between pump and heat exchanger. Figure 3 schematically represents an embodiment of the relocatable bioconversion unit with an integrated temperature control cycle. The bioconversion unit comprises a frame

(10) , a double-walled reaction vessel mounted into the frame comprising an outer wall

(1 1 ) and an inner wall (12). Preferred volumes of the reaction vessel have already been mentioned. In other embodiments, the reaction vessel is self-supporting and there is no frame (10). The reaction vessel is filled with the reaction mixture. The bioconversion unit furthermore comprises an external temperature control cycle comprising at least a pump (13) and a temperature control unit (14). The reaction mixture is circulated by means of a pump (13) from the reaction vessel to the temperature control unit (14) and is injected back into the storage vessel, preferably via an injection nozzle (16). In the depicted embodiment, acrylonitrile is injected into the temperature control cycle thereby ensuring good mixing (15). It may be added before or after the temperature control unit. Fig. 3 shows an embodiment in which acrylonitrile is added into the temperature control cycle between the pump and the heat exchanger. The stream of reaction mixture injected back into the reaction vessel causes a circulation of the reaction mixture in the reaction vessel which ensures sufficient mixing of the contents of the reaction mixture. The amount of reaction mixture cycled per hour through the temperature control cycle is chosen such that sufficient mixing to the contents of the reactor as well as sufficient temperature control is achieved. In one embodiment, the amount of reaction mixture cycled per hour through the temperature control cycle may be from 100 % to 1000 % of the total volume of the reaction mixture in the bioconversion unit, in particular from 200 % to 1000 % and for example from 500% to 800%.

Off-gases of the bioconversion unit may comprise acrylonitrile, acrylic acid and acrylamide. If necessary, according the applicable rules such off-gases may be treated in a manner known in the art. For example, it may be possible to combust the off- gases.

In one embodiment, all off-gases containing acrylonitrile, acrylic acid and acrylamide may be washed in a scrubber. The scrubber vessel may have a volume of 10 m³ to 100 m³. It may be for example an ISOtank or relocatable storage vessel, preferably a double walled vessel. The scrubber water may preferably be collected in a tank and it may be re-used next bio-conversion batch.

Biomass removal After bioconversion, the reaction vessel comprises an aqueous solution of acrylamide, which still comprises the biocatalyst suspended therein.

The biocatalyst preferably becomes removed completely, essentially completely, or partially before polymerization, however, removing the biocatalyst may not be absolutely necessary in every case. Whether it is necessary to remove the biocatalyst substantially depends on two factors, namely whether remaining biocatalyst negatively affects polymerization and/or the properties of the polyacrylamide obtained and/or the biocatalyst negatively affects the application of the obtained polyacrylamide solution. In one embodiment, at least 75 %, preferably at least 90 % by weight of the biomass - relating to the total of the biomass present- should be removed.

The method for removing the biocatalyst is not specifically limited. Separation of the biocatalyst may take place by for example filtration or centrifugation. In other embodiments, active carbon may be used for separation purpose.

Procedurally, for removing the biocatalyst there are several options.

In one embodiment, the aqueous acrylamide solution comprising the biocatalyst is removed from the bioconversion unit, passed through a unit for removing the biocatalyst, and thereafter the aqueous acrylamide solution is filled into a suitable storage unit for acrylamide, preferably a relocatable storage unit for acrylamide as described above.

In another embodiment, the aqueous acrylamide solution comprising the biocatalyst is removed from the bioconversion unit, passed through a unit for removing the biocatalyst and thereafter the aqueous acrylamide solution is filled directly into the monomer make-up unit, i.e. without intermediate storing in an acrylamide storage unit.

In another embodiment, the aqueous acrylamide solution comprising the biocatalyst is removed from the bioconversion unit and is filled directly, i.e. without removing the biocatalyst, into the monomer make-up unit. In said embodiment, the biocatalyst is still present in course of monomer make-up and is removed after preparing the aqueous monomer solution (step [1]) as described below.

In another embodiment, the aqueous acrylamide solution comprising the biocatalyst is removed from the bioconversion unit, passed through a unit for removing the biocatalyst and thereafter filled back into the bioconversion unit. In order to ensure complete discharge of the bioconversion unit before re-filling it with the acrylamide solution, the unit for removing the biocatalyst should comprise a buffer vessel having a volume sufficient for absorbing the contents of the bioconversion unit. Step [1 ] - Polymerization of an aqueous monomer solution

In course of step [1] an aqueous monomer solution comprising at least water, acrylamide and optionally further water-soluble, monoethylenically unsaturated monomers is polymerized in the presence of suitable initiators for radical

polymerization under adiabatic conditions thereby obtaining an aqueous

polyacrylamide gel. Step [1] is performed at location A.

Such a polymerization technique is also briefly denominated by the skilled artisan as "adiabatic gel polymerization". Reactors for adiabatic gel polymerization are unstirred. Due to the relatively high monomer concentration the aqueous monomer solution used solidifies in course of polymerization thereby yielding an aqueous polymer gel. The term "polymer gel" has been defined for instance by L. Z. Rogovina et al., Polymer Science, Ser. C, 2008, Vol. 50, No. 1 , pp. 85-92.

"Adiabatic" is understood by the person skilled in the art to mean that there is no exchange of heat with the environment. This ideal is naturally difficult to achieve in practical chemical engineering. In the context of this invention, "adiabatic" shall consequently be understood to mean "essentially adiabatic", meaning that the reactor is not supplied with any heat from the outside during the polymerization, i.e. is not heated, and the reactor is not cooled during the polymerization. However, it will be clear to the person skilled in the art that - according to the internal temperature of the reactor and the ambient temperature - certain amounts of heat can be released or absorbed via the reactor wall because of temperature gradients, but this effect naturally plays an ever lesser role with increasing reactor size.

The polymerization of the aqueous monomer solution generates polymerization heat. Due to the adiabatic reaction conditions the temperature of the polymerization mixture increases in course of polymerization.

Monomer storage

Basically, it is possible to run step [1 ] as just-in-time-process, i.e. providing the monomers to the location A when monomers are needed for polymerization and directly withdrawing the monomers from the transport vessels. However, in order to ensure an uninterrupted operation is preferred to hold available at least some storage capacity for the monomers at location A.

Depending on the chemical nature, the water-soluble, monoethylenically unsaturated monomers to be used may be provided as pure monomers or as aqueous solutions to location A.

Acrylamide and other water-soluble, monoethylenically unsaturated monomers such as acrylic acid, ATBS, or DM3AQ preferably may be stored in relocatable storage units. Details of such relocatable storage units for monomers have already been outlined above for acrylonitrile and we refer to the description above.

The monomers may be provided to location A by road tankers, ISOtanks, or rail cars and pumped into the relocatable storage unit(s).

In one embodiment, a relocatable storage unit with integrated temperature control cycle as depicted in Figure 1 as shown above may be used for storing the monomers. In another embodiment, a relocatable storage unit with a separate, external temperature control cycle as depicted in Figure 2 as shown above may be used for storing the monomers. As a rule, the temperature of the monoethylenically unsaturated monomers such as acrylamide, acrylic acid, ATBS or DM3AQ should not exceed 25°C to 30°C.

Pure associative monomers as described above may be waxy solids and may be stored at room temperature. They may be stored as aqueous solutions, for example as aqueous solutions comprising 25 % by weight of the associative monomer. Because the amounts of associative monomers are significantly smaller than the amounts of other monoethylenically unsaturated monomers smaller storage units than that described above may be used. Acidic monomers such as acrylic acid or ATBS are often partially or completely neutralized for polymerization using suitable bases.

Bases, such as aqueous solutions of NaOH may also be stored in storage vessels as described above. A cooling cycle is not necessary. To the contrary, depending on the climatic conditions, a heating such as a heating element in the vessel may be necessary because concentrated NaOH freezes at about +15°C.

Monomer Make-up The aqueous monomer solution for polymerization comprises water and 5 % to 45 % by weight of water-soluble, monoethylenically unsaturated monomers, relating to the total of all components of the aqueous monomer solution. The water-soluble, monoethylenically unsaturated monomers comprise at least acrylamide, preferably bio acrylamide which preferably is manufactured in step [0] also at location A.

For preparing the aqueous monomer solution, the water-soluble, monoethylenically unsaturated monomers to be used and the stabilizers to be used are mixed with each other. All monomers and optionally additives may be mixed with each other in a single step but it may also be possible to mix some monomers and add further monomers in a second step. Also, water for adjusting the concentration of the monomers may be added. Water eventually used for rinsing lines in course of transferring the monomer solution into the polymerization unit, needs to be taken into consideration when adjusting the concentration. Further additives and auxiliaries may be added to the aqueous monomer solution. Examples of such further additives and auxiliaries comprise bases or acids for adjusting the pH value. In certain embodiments of the invention, the pH-value of the aqueous solution is adjusted to values from pH 5 to pH 7, for example pH 6 to pH 7. Examples of further additives and auxiliaries comprise complexing agents, defoamers surfactants, or stabilizers.

In one embodiment, the aqueous monomer solution comprises at least one non- polymerizable surfactant. Adding such surfactants in particular is advisable when associative monomers are used. For such kind of polyacrylamides the surfactants lead to a distinct improvement of the product properties. Examples of suitable surfactants including preferred amounts have been disclosed in WO 2015/158517 A1 , page 19, line, 23 to page 20, line 27. If present, such non-polymerizable may be used in an amount of 0.1 to 5% by weight, for example 0.5 to 3 % by weight based on the amount of all the monomers used.

For preparing the aqueous monomer solution basically any kind of equipment suitable for mixing monomers may be used for example a stirred vessel. Preferably, the preparation of the aqueous monomer solution is performed in a relocatable monomer make-up unit.

In one embodiment, the relocatable monomer make-up unit is similar to the relocatable bioconversion unit as described above. Using largely the same equipment for storing acrylonitrile or other monomers, the bioconversion step and for monomer make-up contributes to an economic process for manufacturing aqueous acrylamide solutions.

The monomer make-up unit comprises a monomer make-up vessel in which the monomers, water and optionally further components are mixed.

The volume of the monomer make-up vessel is not specifically limited and may range from 10 m³ to 150 m³, for example it may be about 20 to 90 m³. Preferably, the monomer make-up vessel should be double walled and should be horizontal. Such a construction avoids installing a pit for the collection of any leakage thereby ensuring an easier and quicker relocation of the reaction unit.

The monomer make-up unit furthermore comprises means for controlling the temperature of the aqueous monomer solution. Usually, the temperature of the aqueous monomer solution should be not more than 5°C, for example from -15°C to +5°C. The monomer make-up unit furthermore comprises means for measurement and control. For temperature control, the monomer make-up unit comprises an external temperature control cycle comprising a pump which pumps the aqueous reactor contents from the storage vessel through a heat exchanger and back into the storage vessel, preferably via an injection nozzle.

The temperature control cycle may be a separate, relocatable temperature control unit comprising pump and heat exchanger and which is connected with the monomer make-up vessel by pipes or flexible tubes. In another embodiment, the temperature control cycle may be integrated into relocatable storage unit. It may -for example- be located at one end of the unit besides the monomer make-up vessel.

The monomer make-up vessel may be equipped with a stirrer for mixing the components of the aqueous monomer solution with each other. However, in the same manner as with the bioreactor, the external temperature control cycle may be used as means for mixing. The stream of the aqueous monomer mixture which passes through the temperature control cycle and which is injected back into the monomer make-up vessel causes a circulation of the aqueous reaction mixture within the reaction vessel which is sufficient to mix the aqueous reaction mixture.

Figure 4 represents a schematically one embodiment of the relocatable monomer make-up unit. The monomer make-up unit comprises a frame (20), a double-walled monomer make-up vessel mounted into the frame comprising an outer wall (21 ) and an inner wall (22). In another embodiment, the monomer make-up vessel is self- supporting and a frame is not necessary. The monomer make-up vessel is filled with the monomer mixture. The monomer make-up unit furthermore comprises an external temperature control cycle comprising at least a pump (23) and a temperature control unit (24). The monomer mixture is circulated by means of a pump (23) from the storage vessel to the temperature control unit (24) and is injected back into the storage vessel, preferably via an injection nozzle (25). The monomers may be added directly into the storage vessel or into the temperature control cycle (26) as indicated in Figure 4. The stream of monomer mixture injected back into the monomer make-up vessel causes a circulation of the monomer mixture in the storage vessel which ensures sufficient mixing of the contents of the monomer mixture.

In another embodiment, a separate temperature control cycle may be used.

The monomers to be mixed with each other and with water are preferably mixed in the monomer make-up vessel, however in another embodiment, it is possible to add the monomers into the temperature control cycle. It is frequently advisable, to first add water to the monomer make-up vessel and then one or more further monomers and/or acids or bases and/or further additives. If acidic monomers such as acrylic acid are used, they should be neutralized before adding acrylamide. For copolymers comprising acrylic acid and acrylamide at first the necessary amount of water may be added into the vessel, followed by NaOH, thereafter acrylic acid and thereafter acrylamide. Further additives which optionally might be present such as complexing agents, defoamers surfactants, or stabilizers as mentioned above may be dissolved in aqueous solvents, preferably water in suitable dissolution units and the solutions also added into the monomer make-up vessel. In another embodiment of the invention, the bioconversion unit may also be used for monomer make-up.

In a preferred embodiment, the aqueous acrylamide solution does no longer comprise the biocatalyst. However, in another embodiment the acyl amide solution still comprises the biomass. In said embodiment, the biocatalyst may be removed after preparing the aqueous monomer solution in the same manner as described above or it may not be removed. Criteria for deciding in which cases it may not be necessary to remove the biocatalyst have already been mentioned above. After mixing the aqueous monomer solution it is transferred from the monomer makeup vessel (or any other vessel serving as monomer make-up vessel such as the bioconversion unit) to the polymerization unit. Such connection for transferring the aqueous monomer solution hereinafter also is referred to as "monomer feed line". In one embodiment, associative monomers may also be added into the monomer make-up vessel. However, in a preferred embodiment, aqueous solutions of the associative monomers, in particular associative monomers having the formula (III), (IV), or (V) may be metered into the monomer feed line. In another embodiment of the invention, the polymerization unit itself may be used for monomer make-up. As will be detailed below, polymerization unit may be connected to a temperature control unit before polymerization, so that the monomer solution may also be cooled in the polymerization unit until directly before the start of polymerization. As will be detailed also below, the polymerization unit may comprise injection nozzles for nitrogen or other inert gases in order to inertize the contents of the polymerization unit and such injection of inert gases also efficiently mixes the contents of

polymerization unit. Also combinations are possible, for example providing a monomer concentrate in a separate monomer make-up unit and diluting the aqueous monomer solution in the polymerization unit with additional water. In another example, acids or bases -if necessary- may be added not into a separate monomer make-up unit but directly to the polymerization unit. Polymerization

The polymerization is performed in a transportable polymerization unit having a volume of 1 m³ to 40 m³, in particular 5 m³ to 40 m³, preferably from 5 m³ to 30 m³, more preferably from 20 m³ to 30 m³. The transportable polymerization unit may be transported for instance by trucks or railcars.

The transportable polymerization unit may be of cylindrical or conical shape.

Preferably, the polymerization unit is cylindrical having a conical taper at the bottom and a bottom opening for removing the aqueous poly acrylamide gel. The inner wall of the transportable polymerization unit may preferably be coated with an anti-adhesive coating. Basically, anti-adhesive coatings are known in the art. Examples comprise polypropylene, polyethylene, epoxy resins and fluorine containing polymers such as polytetrafluoroethylene or perfluoroalkoxy polymers.

One embodiment of a transportable polymerization unit for use in the present invention is schematically shown in Figure 5, hereinafter also denoted as polymerization unit P1 . The polymerization unit P1 comprises a cylindrical upper part (30) and a conical part (31 ) at its lower end. At the lower end, there is a bottom opening (32) which may be opened and closed. After polymerization, the polyacrylamide gel formed is removed through the opening (32). It furthermore comprises means (33) such as legs or similar elements allowing to deploy the transportable polymerization unit in a vertical manner.

The diameter (D) of the polymerization unit in the cylindrical section may in particular be from 1.5 to 2.5 m, preferably from 2 m to 2.5 m and the length (L) of the cylindrical section may be from 4 to 6 m, preferably 5 to 6 m. The conus angle a in the conical part (see also Figure 4) may be from 15° to 90°, preferably from 20° to 40°. Besides the opening (32) the transportable polymerization unit P1 comprises one or more feeds for the aqueous monomer solution, initiator solutions, gases such as nitrogen or other additives. The inner wall of the transportable polymerization unit P1 may be coated with an anti-adhesive coating. The diameter of the bottom opening (32) may for example be from 0.2 to 0.8 m, in particular from 0.4 to 0.7 m, preferably from 0.5 to 0.7 m.

For polymerization and removal of the polymer gel the transportable polymerization unit P1 is operated in a vertical position as depicted in Figure 5. The transportable polymerization unit P may be transported for instance by trucks or railcars.

For transport, it may preferably be tilted to a horizontal position. The transport in horizontal position on a truck is schematically shown in Figure 6. For polymerization, the aqueous monomer solution prepared is filled into the transportable polymerization unit, in particular into the polymerization unit P1. For that purpose, the monomer make-up vessel (or any other vessel serving as monomer make-up vessel such as the bioconversion unit) is connected with the transportable polymerization unit by a monomer feed line.

As already outlined above, in another embodiment the aqueous monomer solution may be prepared in the transportable polymerization unit itself. In such embodiment, the polymerization unit already is filled with an aqueous monomer solution.

The polymerization is performed in the presence of suitable initiators for radical polymerization. Suitable initiators for radical polymerization, in particular adiabatic gel polymerization are known to the skilled artisan.

In a preferred embodiment, redox initiators are used for initiating. Redox initiators can initiate a free-radical polymerization even at temperatures of less than +5°C. Examples of redox initiators are known to the skilled artisan and include systems based on Fe²⁺/Fe³⁺ - H2O2, Fe²⁺/Fe³⁺ - alkyl hydroperoxides, alkyl hydroperoxides - sulfite, for example t-butyl hydroperoxide - sodium sulfite, peroxides - thiosulfate or alkyl hydroperoxides - sulfinates, for example alkyl hydroperoxides/ hydroxymethane- sulfinates, for example t-butyl hydroperoxide - sodium hydroxymethanesulfinate. Furthermore, water-soluble azo initiators may be used. The azo initiators are preferably fully water-soluble, but it is sufficient that they are soluble in the monomer solution in the desired amount. Preferably, azo initiators having a 10 h ti/2 in water of 40°C to 70°C may be used. The 10-hour half-life temperature of azo initiators is a parameter known in the art. It describes the temperature at which, after 10 h in each case, half of the amount of initiator originally present has decomposed.

Examples of suitable azo initiators having a 10 h .1/2 temperature between 40 and 70°C include 2,2'-azobis[2-(2-imidazolin-2-yl)propane] dihydrochloride (10 h ti/2 (water): 44°C), 2,2'-azobis(2-methylpropionamidine) dihydrochloride (10 h ti ₂ (water): 56°C), 2,2'-azobis[N-(2-carboxyethyl)-2-methylpropionamidine hydrate (10 h ti/2 (water):

57°C), 2,2'-azobis{2-[1 -(2-hydroxyethyl)-2-imidazolin-2-yl]propane} dihydrochloride (10 h ti/2 (water): 60°C), 2,2'-azobis(1 -imino-1 -pyrrolidino-2-ethylpropane) dihydrochloride (10 h ti/₂ (water): 67°C) or azobis(isobutyronitrile) (10 h ti ₂ (toluene): 67°C). In one embodiment of the invention a combination of at least one redox initiator and at least one azo initiator is used. The redox initiator efficiently starts polymerization already at temperatures below +5°C. When the reaction mixture heats up, also the azo initiators decompose and also start polymerization. The initiators preferably are added as aqueous solutions to the aqueous monomer solution. The initiator raw material may be stored at location A in a cold storage container. Dissolving the initiators in water may be performed using suitable initiator make-up vessels. The initiator make-up vessel may comprise a temperature control cycle. Instead of an own temperature control cycle, cold water, for example water having a temperature of less than +5°C may be used for dissolving the initiators. The initiator make-up vessels furthermore may comprise means for mixing such as a stirrer. However, mixing may also be conducted by bubbling an inert gas through the aqueous mixture thereby simultaneously mixing and inerting the aqueous mixture. The solutions may be filtered before use.

Solutions of azo initiators may be added into the monomer feed line while the aqueous monomer solution is transferred from the monomer make-up vessel to the

polymerization unit. In another embodiment solutions of azo initiators may already been added to the monomer make-up vessel, provided the monomer solution has already been cooled to temperatures below ambient temperature, preferably to less than +5°C and the 10 h ti/2 temperature of the initiator is high enough so that the initiator doesn't decompose prematurely.

Solutions of redox initiators may be added into the monomer feed line or into the polymerization unit. Before polymerization oxygen from the reactor and the reaction mixture to be polymerized needs to be removed. Deoxygenation is also known as inertization.

In one embodiment, inertization is performed in the polymerization unit. For that purpose, inert gases such as nitrogen or argon are injected into the reactor filled with the monomer solution. Preferably, nozzles for injecting inert gases are located in the bottom of the polymerization unit. In the polymerization unit P1 they may for example be located in the conical taper. The bubbles of inert gases rising in the reactor remove oxygen and simultaneously mix the contents of the reactor very efficiently. Initiator solutions metered into the reactor are mixed with the aqueous solution by means of the inert gas injection.

In another embodiment, inertization may be performed in the monomer feed line. Inert gases such as nitrogen or argon may be injected into the feed line. In order to ensure effective mixing of the gas injected and the aqueous gases injected it is frequently desirable that the monomer feed line additionally comprises a static mixture. The gas injected into the monomer feed line may be removed before entering into the reactor by means of a suitable degassing unit such as the degassing units described in WO 2003/066190 A1 or in CN 202492486 U. In another embodiment, no separate degassing unit is used, but the solution is degassed after entering into the

polymerization unit. In one embodiment, the monomer solution enters into the reactor by means of a spray nozzle for the purpose of removing gas. Of course, it is possible to combine the two embodiments for degassing, i.e. to purging the polymerization unit with inert gases and degassing the monomer mixture.

The radical polymerization starts after adding the initiator solutions, preferably solutions of redox initiators, to the aqueous monomer solution thereby forming an aqueous polyacrylamide gel. Due to the polymerization heat generated in course of

polymerization and the adiabatic reaction conditions, the temperature in the

polymerization unit increases. In the following, the temperature of the aqueous monomer solution before the onset of polymerization shall be denominated as Ti and the temperature of the aqueous polymer gel directly after polymerization shall be denominated as T2. It goes without saying that T2 > Ti. Within the context of the present invention, the temperature Ti should not exceed

30°C, in particular Ti should not exceed 25°C. Preferably, Ti should not exceed 10°C, more preferably not +5°C. In one embodiment, Ti may be from -15°C to +30°C, for example from -15°C to +25°C, preferably from -15°C to +5°C, and more preferably from -5°C to +5°C. The temperature Ti of the monomer solution may be adjusted as already disclosed above, i.e. already the monomer solution in the monomer make-up vessel may be cooled appropriately. Of course, also the temperature control unit for adjusting Ti may be located in the monomer feed line, or the polymerization unit may be connected to a temperature control unit before polymerization, so that the monomer solution may still be cooled in the polymerization unit until directly before the start of polymerization.

As the polymerization is carried under adiabatic conditions, the temperature T2 reached in course of polymerization is not influenced by external heating or cooling but only depends on the polymerization parameters chosen. By suitable choice of the polymerization parameters, the skilled artisan can adjust T2. Because the reaction is adiabatic, the temperature increase in course of polymerization basically depends on the heat of polymerization generated in course of polymerization, the heat capacity of contents of the polymerization unit and the temperature Ti of the monomer solution, i.e. the temperature before the onset of polymerization. Due to high water contents of the mixture for polymerization the heat capacity of the mixture for polymerization is dominated by the heat capacity of water and it may of course be measured. The polymerization heat per mole (or per mass) for common monoethylenically unsaturated monomers is known in the art and may therefore be gathered from the scientific literature. Of course, it may also be measured. So, it is possible for the skilled artisan to calculate at least roughly the heat of polymerization for specific monomer compositions and specific monomer concentrations. The higher the concentration of the

monoethylenically unsaturated monomers in the aqueous solution the more heat of polymerization is generated. T2 may be roughly calculated from the parameter mentioned above by the formula T2 = ΤΊ + [(polymerization heat) / (heat capacity)]. According to the present invention the polymerization parameter are chosen such that the temperature T2 is from 50°C to 90°C. In one embodiment of the invention, T2 is limited to 50°C to 70°C.

Surprisingly, it has been found that limiting T2 to the range mentioned is advantageous for the transport of the polymer gel in course of step [3]. Details about properly choosing T2 will be provided below. Limiting T2 to may be achieved by the measures mentioned above. In particular, it is advisable to choose a concentration of monomers in the aqueous monomer solution of 5 % by weight to 24.9 % by weight relating to the total of all components of the aqueous solution, in particular 8 % by wt. to 24.9 % by weight and for example 20 % by weight to 24.9 % by weight. In addition, ΤΊ may be -15°C to + 5°C.

The time of polymerization may be from 2 to 24 h, for example from 3 to 6 h.

Step [3] Transport of the aqueous polyacrylamide gel

In course of step [3] the transportable polymerization unit filled with the aqueous polyacrylamide gel is transported from location A to location B.

The transport may be carried out by any transport means suitable for transporting the transportable polymerization unit, for example by trucks, railcars or ships. In one embodiment, the transport is carried out by trucks.

The cylindrical transportable polymerization unit P1 is operated in a vertical position for polymerization and removal of the polymer gel. For transport, it may preferably be tilted to a horizontal position. The transport in horizontal position on a truck is schematically shown in Figure 6.

In one embodiment, the truck comprises means for loading the polymerization unit P1 onto it in horizontal position and for unloading and deploying the polymerization unit in vertical position. When such kind of trucks are used, additional means, for example cranes, for loading at location A and unloading at location B are not necessary.

In another embodiment of the invention, means for loading and unloading the transportable polymerization unit may be provided at locations A and B. In such a case, the truck or any other transport device does not need means for loading and unloading.

Transporting the transportable polymerization unit filled with the aqueous polymer gel comprises several steps. For polymerization, the transportable polymerization unit is connected by pipes, flexible tubes and electrical connections with other units. For transport, all connections have to be removed and the transportable polymerization unit has to be loaded on the transport means, for example on a truck. Thereafter the transport from location A to location B follows. At location B the polymerization unit has to be unloaded and then it has to be connected with the equipment necessary for removing, comminuting and dissolving the aqueous polyacrylamide gel from the reactor (see steps [4] and [5]). According to the present invention, the time for transporting the transportable polymerization unit from location A to location B is from 6 h to 14 days, in particular from 1 day to 14 days. For example, the transport time may be from 3 days to 14 days, preferably from 3 days to 7 days. The term "transport time" shall mean the time period beginning with the end of polymerization at location A until the start of removing the aqueous polyacrylamide gel from the transportable polymerization unit at location B.

The polymerization in the polymerizable polymerization unit yields a polymerization unit filled with aqueous polyacrylamide gel, i.e. a block of an aqueous polyacrylamide gel. Depending on the volume of the transportable polymerization unit, also the volume of such a block may be from 1 m³ to 40 m³, and preferably from 20 m³ to 30 m³.

The temperature of the polyacrylamide gel directly after polymerization is 50°C to 90°C. The polyacrylamide gel block cools down only very slowly by releasing heat through the wall of the polymerization unit. Naturally, cooling down will be the slower the larger the volume of the polymerization unit. Furthermore, cooling will be the slower in the core of the polymerization unit than at the walls. Figure 7 shows a simulation of the temperature of an aqueous polyacrylamide gel in a cylindrical polymerization unit having a length of 6 m and a diameter of 2 m, i.e. having a volume of 18.8 m³. It shows the maximum temperature and the average temperature of the gel in the polymerization unit as a function of time. The detailed simulation parameters are provided in the experimental section.

In the simulation, the temperature of the aqueous polyacrylamide gel in the

polymerization unit after polymerization, i.e. T2, is 90°C. The simulation simulates the cooling of the gel. The simulation shows, that the temperature of the polymer gel only slowly decreases and it goes without saying the zones close to the walls of the polymerization unit cool down faster than zones in the center of the polymerization unit. After 5 days the average temperature within the reactor still is about 65°C and the maximum temperature still close to 90°C. After 10 days, the average temperature is about 45°C and the maximum temperature still about 80°C.

So, keeping the slow cooling rates and transporting times mentioned above in mind, the polyacrylamide gel hold in the transportable polymerization unit may be kept at a temperature well above room temperature for a significant time, i.e. for up to 14 days.

The inventors found out that the polyacrylamide gel may be damaged when keeping it in the polymerization unit at higher temperatures and for longer times, in particular when keeping it in the polymerization unit at higher temperatures for more than about a day.

"Damaged" shall mean that the properties of the polyacrylamides to be manufactured may degrade in course of time, for example insoluble portions may be formed, the filterability of aqueous solutions may decrease and/or the viscosity may decrease. It goes without saying that such damage also depends on the chemical composition of the polyacrylamide to be manufactured. Furthermore, it has to be kept in mind that a specific damage may still be acceptable for one application while it is no longer acceptable for another application. So, "damaged" does not necessarily mean that the polyacrylamide gel may not be used.

Measures for avoiding or diminishing gel damage

The inventors found several measures (a), (b), and (c) for avoiding or at least diminishing gel damage in course of transporting the aqueous polyacrylamide gel from location A to location B.

It is important to point out that the three measures (a), (b), and (c) are not compulsory for the process according to the present invention. Rather, a person skilled in the art may decide whether it is advisable to apply said measures or not. Applying the measures or not first of all depends on whether and to which extent gel damage is acceptable for a certain application or not.

Secondly, applying any of those measures or not in particular depends on the time of transport. If the gel remains in the polymerization unit only for a short time, for example for less than 24 h, for example less than 12 h then the measures might perhaps not be necessary. For longer times, for example if the gel remains for 7 to 14 days in the polymerization unit, it may be advisable to apply those measures.

Also, the shape and the size of the polymerization unit may be relevant for the decision whether to apply any of the measures (a), (b), and (c). The smaller the volume and the larger the surface of a polymerization unit the more rapidly the polymer gel cools down. In a smaller polymerization unit uncritical temperatures might be achieved already after a shorter time than in larger polymerization units. Measure (a) Measure (a) includes using an aqueous solution of acrylamide for step [1 ], wherein the acrylamide solution has been obtained by hydrolyzing acrylonitrile in water in the presence of a biocatalyst capable of converting acrylonitrile to acrylamide. Acrylamide manufactured in this manner is also denoted as "bio-acrylamide". Using bio-acrylamide in particular is helpful, if the temperature T2 increases to 60°C and more in course of polymerization. Comparative tests with Cu-catalyzed acrylamide for polymerization yielded polyacrylamides whose viscosity decreased upon holding the gels at higher temperatures for a longer time. Later, even some crosslinking was found so that the gels were no longer soluble in water. Using bio-acrylamide helped to avoid such viscosity decrease or at least to diminish such decrease.

Measure (b)

Measure (b) includes limiting the temperature T2, i.e. the temperature of the gel directly after polymerization to 50°C to 70°C, preferably to 50°C for 65°C. For example, T₂ may be from 55°C to 65°C.

Measures for adjusting T2 have already been mentioned above. In particular, it is advisable to limit the concentration of the monomers in the aqueous monomer solution to 5 % by weight to 24.9 % by weight relating to the total of all components of the aqueous solution, in particular 8 % by wt. to 24.9 % by weight and for example 20 % by weight to 24.9 % by weight.

In one embodiment of the invention, Ti is from -15°C to + 5°C and T2 is from 50°C to 70°C, preferably from 50°C for 65°C, and for example from 55°C to 65°C.

Measure (c)

Measure (c) includes adding at least one stabilizer for the prevention of polymer degradation to the aqueous monomer solution before polymerization.

The term "polymer degradation" includes all kind of deterioration of the properties of the polyacrylamides, including but not limited to reduction of the viscosity of aqueous solutions or the formation of insoluble portions. The stabilizers for the prevention of polymer degradation are what are called "free-radical scavengers", i.e. compounds which can react with free radicals (for example free radicals formed by heat, light, redox processes), such that said radicals can no longer attack and hence degrade the polymer.

Using such kind of stabilizers for the stabilization of aqueous solutions of

polyacrylamides basically is known in the art, as disclosed for example in WO

2015/158517 A1 , WO 2016/131940 A1 , or WO 2016/131941 A1 . However, in said publications the stabilizers serve to protect the polyacrylamides in course of using them, for example in course of enhanced oil recovery operations. As will be detailed below, adding such stabilizers for the prevention of polymer degradation surprisingly may also be advantageous for transporting the aqueous polyacrylamide gel in course of step [2] of the present process. Such an effect has not been known so far and may -depending on transport time and T2 significantly- contribute to the benefit of the present process.

The stabilizers are selected from the group of non-polymerizable stabilizers and polymerizable stabilizers. Polymerizable stabilizers comprise a monoethylenically unsaturated group and become incorporated into the polymer chain in course of polymerization. Non-polymerizable stabilizers don't comprise such monoethylenically unsaturated groups and don't become incorporated into the polymer chain. Non-polymerizable stabilizers are selected from the group of sulfur compounds, preferably organic sulfur compounds, sterically hindered amines, inorganic compounds comprising at least two nitrogen atoms, N-oxides, nitroso compounds, aromatic hydroxyl compounds or ketones. Organic sulfur compounds comprise at least one organic group and at least one functional group comprising sulfur, in particular functional groups selected from -SH (thiol groups) or salts thereof, in particular alkali metal salts, R^'-S-R' (thioether groups) -SCN (thiocyanate group), -NCS (isothiocyanate group), -NR'-C(=S)-NR'- (Thiourea group), -S-S-R' (disulfide groups), -NR'-C(=0)-S-R' (thiolurethane

groups), -NR'-C(=S)-0-R' (thionurethan group), -NR'-C(=S)-S-R' (dithiourethane groups), wherein R' stand for H or an organic hydrocarbon group respectively. Two R' groups may also be connected to a cycle. In particular, organic sulfur compounds may be selected from thiols, thiophenoles, thioethers, sulfur containing heterocyclic compounds, disulfides, thioureas, thiourethanes or thiocarbamates.

Examples of organic sulfur compounds include thiourea, substituted thioureas such as Ν,Ν'-dimethylthiourea, N,N'-diethylthiourea, Ν,Ν'-diphenylthiourea, thiocyanates, for example ammonium thiocyanate or potassium thiocyanate, tetramethylthiuram disulfide, and mercaptans such as 2-mercaptobenzothiazole or 2- mercaptobenzimidazole or salts thereof, for example the sodium salts, sodium dimethyldithiocarbamate, 2,2'-dithiobis(benzothiazole), 4,4'-thiobis(6-t-butyl-m-cresol). Examples of nitroso compounds include ammonium N-nitrosophenylhydroxylamine.

Examples of ketones include 2,5-di(t-amyl)-hydroquinone, 5-hydroxy-1 ,4- naphthoquinone, 2,5-di(t-amyl)hydroquinone and dimedone.

Examples of aromatic hydroxyl compounds include paramethoxyphenol, 2,6-di-t-butyl- 4-methylphenol, butylhydroxyanisole, propyl 3,4,5-trihydroxybenzoate and 8- hydroxyquinoline. Examples of N-oxides include 4-hydroxy-2 2 6 6-tetramethylpiperidine-1 -oxyl.

Examples of sterically hindered amines include 1 -substituted 2,2,6,6-tetramethyl-4- piperidinol compounds, such as 1 ,2,2,6, 6-pentamethyl-4-piperidinol, 1 -ethyl-2,2,6,6- tetramethyl-4-piperidinol, 1 -acetyl-2,2,6,6-tetramethyl-4-piperidinol, 1 -(2- hydroxypropyl)-2,2,6,6-tetramethyl-4-piperidinol, or 1 -(2-Hydroxybutyl)-2,2,6,6- tetramethyl-4-piperidinol. A further example includes N-(1 ,3-dimethylbutyl)-N'-phenyl-p- phenylenediamine.

Examples of inorganic compounds comprising at least two nitrogen atoms comprise dicyandiamide, guanidine, and cyanamide.

Preference is given to sterically hindered amines such as 1 ,2,2,6, 6-pentamethyl-4- piperidinol and sulfur compounds, preferably mercapto compounds, especially 2- mercaptobenzothiazole or 2-mercaptobenzimidazole or the respective salts thereof, for example the sodium salts, and particular preference is given to 2- mercaptobenzothiazole or salts thereof, for example the sodium salts.

Polymerizable stabilizers for the prevention of polymer degradation comprise at least one monoethylenically unsaturated group and a stabilizing moiety capable of preventing the polymer form thermal degradation.

Polymerizable stabilizers may be characterized by the general formula R⁷R⁸C=C(R⁹)S, wherein S is an organic stabilizing moiety and R⁷, R⁸, and R⁹ are selected from the group of H, C1-C4 alkyl, -COOH, and -CH2COOH wherein the carboxylate groups may also be present as salts, in particular alkali metal salts. In a preferred embodiment, R⁷ and R⁸ are H, and R⁹ is H or methyl. Polymerizable stabilizers are in particular derived from organic, non- polymerizable stabilizers by substituting such non polymerizable stabilizers with a monoethylenically unsaturated group.

Examples of polymerizable stabilizers comprising monoethylenically unsaturated groups comprise (meth)acrylic acid esters of 1 ,2,2,6-pentamethyl-4-piperidinol or other monoethylenically unsaturated groups comprising 1 ,2,2,6,6-pentamethyl-piperidin-4-yl groups. Examples of such polymerizable stabilizers comprise

wherein R¹⁰ is H, Ci to C₄ alkyl, and R¹¹ is selected from H or an alkali metal ion, in particular Na⁺.

In one preferred embodiment of the invention, the stabilizer is a (meth)acrylic acid ester of 1 ,2,2,6,6-pentamethyl-4-piperidinol (VIII)

wherein R¹² is H or methyl.

The aqueous monomer solution for polymerization comprises either at least one non- polymerizable stabilizer or at least one polymerizable stabilizer. Of course, also a combination of stabilizers of both types may be used. The amount of non-polymerizable stabilizers -if present- is from 0.1 % to 2.0 % by weight, relating to the total of all monomers in the aqueous monomer solution, preferably from 0.15 % to 1.0 % by weight and more preferably from 0.2 % to 0.75 % by weight.

The amount of polymerizable stabilizers -if present- is from 0.01 to 2% by weight, based on the sum total of all the monomers in the aqueous monomer solution, preferably from 0.02 % to 1 % by weight, more preferably from 0.05 % to 0.5 % by weight.

Stabilizers preferably are added to the aqueous monomer solution as solutions in water and/or water-miscible organic solvents. Examples of water-miscible organic solvents comprise alcohols such a methanol or ethanol. The concentration of stabilizers in the solvent may be selected by the skilled artisan. It may for example be from 5 % to 50 % by weight regarding to the total of all components of the solution.

Application of measures (a), (b) and (c)

In a preferred embodiment, at least one of the measures (a), (b), and (c) is taken.

In one embodiment of the invention, at least measure (a), i.e. using bio-acrylamide, is selected as measure. Bio-acrylamide for use in the present invention may preferably be manufactured in a separate process step [0] at location A. In another embodiment, it may be shipped to location A form another location. Using bio-acrylamide in particular is useful, when T2 exceeds 60°C and/or the transport time is 1 day or more. In one embodiment, measure (a) is taken, T2 is from 50°C and 70°C and the transport time is from 1 to 14 days, preferably from 3 to 14 days, for example from 3 to 7 days.

In another embodiment of the invention, at least measure (b), i.e. limiting T2 to 50 to 70°C, is selected as measure. Limiting T2 is in particular helpful, if the transport time is 3 days or more. In one embodiment, T2 is from 50°C and 70°C and the transport time is from 3 to 14 days, preferably from 3 to 7 days. Preferably, Ti is from -15°C to + 5°C, T2 is from 50°C to 70°C, preferably from 50°C for 65°C, more preferably from 55°C to 65°C, and the transport time is from 1 to 14 days, preferably from 3 to 14 days, for example from 3 to 7 days.

In another embodiment of the invention, at least measure (c), i.e. adding a stabilizer, is selected as measure. Suitable stabilizers, preferred examples and concentrations of stabilizers have already been mentioned above and we explicitly refer said disclosure. Adding at least one stabilizer in particular is helpful, if the transport time is more than 3 days and/or T2 is 60°C or more. In one embodiment, measure (c) is taken, T2 is from 50 to 90°C and the transport time is from 1 to 14 days, preferably from 3 to 14 days, for example from 3 to 7 days. Preferably, T2 is from 60 to 80°C and the transport time is from 1 to 14 days, preferably from 3 to 14 days, for example from 3 to 7 days.

In one embodiment, measure (c) is combined with measure (a), i.e. bio acrylamide and at least one stabilizer are used. In one embodiment, measures (a) and (c) is taken, T2 is from 50 to 90°C and the transport time is from 1 to 14 days, preferably from 3 to 14 days, for example from 3 to 7 days. Preferably, T2 is from 60 to 80°C and the transport time is from 1 to 14 days, preferably from 3 to 14 days, for example from 3 to 7 days.

In another embodiment, a combination of the three measures (a), (b), and (c) is selected, i.e. bio acrylamide and at least one stabilizer are used and T2 is limited to 50°C to 70°C. Such an embodiment in particular is useful for long transport times, in particular for transport times of more than 3 days. In one embodiment, a combination of the three measures (a), (b), and (c) is selected and the transport time is from 1 to 14 days, preferably from 3 to 14 days, more preferably from 4 to 10 days, and for example from 4 to 7 days.

Step [3] Removal of the aqueous polyacrylamide gel

Step [3] is performed at location B. In step [3], the aqueous polyacrylamide gel comprising stabilizers is removed from the transportable polymerization unit. After removal form the polymerization unit the aqueous polymer gel is further processed by comminuting and dissolving the gel in an aqueous fluid.

Basically, removing the aqueous polyacrylamide gel may be performed by any kind of technology. The details depend on the specific design of the transportable

polymerization unit and the connected downstream processing equipment.

The aqueous polyacrylamide gel may for example be removed by mechanical means from the polymerization unit. In other embodiments, the polymerization unit may be opened completely at the upper side, e.g. by removing a cover plate. By tipping the polymerization unit the gel block may be removed more or less as a whole from the reactor. Preferably, the aqueous polyacrylamide gel may be removed by applying pressure onto the gel and pressing it through an opening in the polymerization unit. By the way of example, pressure may be generated by mechanical means such as a piston, by means of gases such as compressed air, nitrogen, argon or by means of aqueous fluids, in particular water.

For removing the polyacrylamide gel from the preferred transportable polymerization unit P1 , the transportable polymerization unit P1 is operated in vertical position. The aqueous polyacrylamide gel is removed through the opening (26) at the bottom which is opened for the purpose of removing by applying pressure onto the gel from the top side of the reactor. Pressure may be applied using gases and/or water. Examples of gases comprise pressurized air, nitrogen or argon. Basically, any kind of gas may be used, provided it does not react with the polyacrylamide gel. In another embodiment, the transportable polymerization unit may comprise mechanical means, such as a piston for generating pressure. The pressure to be applied for removing the gel may be selected by the skilled artisan. Factors relevant for the selection of the pressure include the viscosity of the polyacrylamide gel, the width of the bottom opening (26), the geometry of the polymerization unit or -if present- the kind of anti-adhesive layer. For example, pressures may range from 1 10,000 Pa to 1 ,000,000 Pa, in particular 150,000 Pa to 750,000 Pa, for example 200,000 Pa to 500,000 Pa (absolute pressures). Should some polymer gel remain in the polymerization unit, the polymerization unit may be rinsed with water to remove the remaining amounts.

The bottom opening (26) of the polymerization unit P1 may be connected with a comminution unit -if present- or directly with a suitable dissolution unit, for instance with a stirred vessel. Said connection may simply be a pipe but it may also comprise means for transporting the gel such as for example screw conveyors or belt conveyors.

Step [4] Dissolution of the aqueous polyacrylamide gel

In course of step [4] the aqueous polyacrylamide gel is dissolved in an aqueous liquid, thereby obtaining an aqueous polyacrylamide solution.

The aqueous liquid used for dissolving the aqueous polyacrylamide gel comprises water. The term "water" includes any kind of water such as desalinated water, fresh water or water comprising salts, such as brines, sea water, formation water, or mixtures thereof. Besides water, the aqueous liquid may comprise organic solvents miscible with water, however the amount of water relating to the total of all solvent should be at least 70 % by weight, preferably at least 90 % by weight, more preferably at least 95 % by weight. In one preferred embodiment, the aqueous liquid comprises only water as solvent. Furthermore, the aqueous liquid may optionally also comprise additives such as for example surfactants, complexing agents, bases, acids of the like. Kind and amount of such additives may be selected according to the intended use of the aqueous polyacrylamide solution. Of course, additives may also be added at a later stage, for example after complete dissolution of the aqueous polyacrylamide gel. In a preferred embodiment, step [4] comprises at least the following two sub-steps, namely step [4-1] of comminuting the aqueous polyacrylamide gel thereby obtaining smaller pieces of polyacrylamide gel, and step [4-2] of dissolving the pieces of the polyacrylamide gel in the aqueous liquid.

Comminuting the aqueous polyacrylamide gel before dissolution in an aqueous liquid is helpful, because smaller gel particles dissolve more quickly in the aqueous liquid than larger gel particles. It should be kept in mind that already removing the aqueous polyacyrylamide gel from the polymerization unit (i.e. step [3]) may cause some disintegration of the gel into smaller gel pieces.

Steps [4-1 ] and [4-2] may be separate steps to be conducted consecutively or the steps may be combined with each other. In other embodiments, already some of the polyacrylamide gel may be dissolved in course of step [4-1 ] but dissolution mostly takes place in a consecutive step [4-2].

Step [4-1 ]

The particle size of the aqueous polyacrylamide gel pieces obtained in course of step [4-1 ] is not specifically limited. In an embodiment of the invention, particles of aqueous polyacrylamide gel should conveniently have a size such that at least two dimensions are no more than 1 cm, preferably no more than 0.5 cm. Preferably three dimensions of the aqueous polyacrylamide gel pieces should be no more than 1 cm, preferably no more than 0.5 cm. There is no lower limit necessary for the aqueous polyacrylamide gel pieces, since the smaller the pieces the easier it will be for the polymer to dissolve. Frequently, aqueous polyacrylamide gel pieces may have a size such that three dimensions are as low as 0.1 cm. Often the aqueous polyacrylamide gel pieces tend to have three dimensions each of from 0.1 cm to 0.5 cm.

Basically, any kind of comminution means may be used for disintegrating the aqueous polyacrylamide gel into smaller particles. Examples of suitable means for comminuting aqueous polyacrylamide gels include cutting devices such as knives or perforated plates, crushers, kneaders, static mixers or water-jets.

Suitable comminution units may be connected directly with the polymerization unit. In another embodiments, the comminution unit may not be directly connected with the polymerization unit but distant from it and the polyacrylamide gel is transported to the comminution unit, for example by screw conveyors or belt conveyors.

The comminution unit preferably also is a relocatable unit. When the preferred polymerization unit P1 is used, preferably, the bottom opening (32) is connected with the comminution unit although, in other embodiments, the

comminution unit may be distant from the polymerization unit. Preferably, the comminution unit is located directly under the bottom opening (32), so that the aqueous polyacrylamide gel which is pressed through the bottom opening (32) directly enters into the comminution unit. Figure 8 schematically shows such an embodiment. A comminution unit (34) is connected with the bottom opening (32). The aqueous polyacrylamide gel (35) enters into the comminution unit (34) through the bottom opening (32). The comminuted polyacrylamide gel (36) leaves the comminution unit preferably at its lower end.

Static cutting device

In one embodiment of the invention, the aqueous polyacrylamide gel is conveyed through a static cutting device, such as knives or metal grills thereby obtaining smaller gel particles. A static cutting device preferably is located directly under the bottom opening (32). Suitable static cutting devices comprise perforated plates or metal grills, such as disclosed, for instance, in US 4,605,689. In one embodiment, the aqueous gel is conveyed through the static cutting device together with an aqueous liquid as described above, preferably water, thereby yielding a mixture of particles of an aqueous polyacrylamide gel in an aqueous liquid. The aqueous liquid is metered into the connection between the bottom opening (32) and the static cutting device, i.e. before the gel enters into the static cutting device. Preferably, not the entire amount of the aqueous liquid necessary to dissolve the polyacrylamide gel completely and to achieve the desired concentration is added at this stage but only a portion of it.

Surprisingly, already 1 % of the total amount of aqueous liquid significantly improves conveying the aqueous polyacrylamide gel through the static cutting device. It goes without saying that already some portion of the polyacrylamide gel may dissolve in the aqueous liquid, thereby obtaining a mixture of an aqueous polyacrylamide gel in a diluted polyacrylamide solution. The mixture comprising aqueous polyacrylamide gel pieces in an aqueous liquid / a diluted acrylamide solution is conveyed to the dissolution unit, for example through a pipe.

Perforated plate In another embodiment of the invention, the aqueous polyacrylamide gel is conveyed through a perforated plate. An extruder or a screw conveyor may be used to generate the necessary pressure for passing the perforated plate. In course of passing through the perforated plates a number of separate cords of aqueous acrylamide gel are formed. They may be cut by a rotating knife or may be flushed away by means of a water jet and conveyed to the dissolution unit. Static mixer

In another embodiment of the invention, the aqueous polyacrylamide gel is conveyed together with an aqueous liquid through a static mixer thereby yielding a mixture of particles of an aqueous polyacrylamide gel in an aqueous liquid. Of course also a plurality of static mixers may be used. The aqueous liquid is metered into the connection between the bottom opening (26) and the static mixer, i.e. before the gel enters into the static mixer. In an embodiment, not the entire amount of aqueous liquid necessary to dissolve the polyacrylamide gel completely and to achieve the desired concentration is added at this stage but only a portion of it. It goes without saying that already some portion of the polyacrylamide gel may dissolve in the aqueous liquid, i.e. the mixture may be also a mixture of an aqueous polyacrylamide gel in a diluted polyacrylamide solution. The mixture comprising aqueous polyacrylamide gel pieces in an aqueous liquid / a diluted acrylamide solution is conveyed to the dissolution unit, for example through a pipe.

Water-jet cutting In a preferred embodiment of the invention, the aqueous polyacrylamide gel is cut into pieces on aqueous polyacrylamide gel by means of a water-jet cutting unit. The water- jet cutting unit cuts the aqueous polyacrylamide gel by means of at least one water jet at a pressure of at least 150^*10⁵ Pa thereby obtaining a mixture of particles of an aqueous polyacrylamide gel in an aqueous liquid. Of course, already some of the aqueous polyacrylamide gel may dissolve in the aqueous liquid in course of water-jet cutting.

Preferably, the surrounding wall section of the water jet cutting unit is a tubular section, a conical section or a combination of tubular and conical sections. The aqueous polyacrylamide gel may then enter into the water jet cutting unit from one end, pass through the cutting stage to reduce the size of the aqueous polyacrylamide gel and desirably the so formed aqueous polyacrylamide gel pieces should exit from the outlet. Aqueous liquid from the cutting stage, desirably should also exit from the outlet. Thus, a mixture of aqueous polyacrylamide gel pieces and water optionally comprising dissolved polymer gel may be formed in the cutting stage.

The surrounding wall section of the water jet cutting unit may be in any suitable orientation. Nevertheless, it is preferred that the surrounding wall section is

substantially upright, with the inlet at the upper end and the outlet at the lower end. The upper end may be preferably connected directly with the bottom opening (3) of the polymerization unit by suitable means. The passage of the aqueous polyacrylamide gel may be by gravity alone or may be fed into the water jet cutting unit under pressure, for instance, by pumping, mechanically feeding, by gas pressure or by the action of a vacuum. Preferably, the aqueous polyacrylamide gel is fed into the water jet cutting unit by means of gas or water pressure exerted on the contents of the polymerization unit P1 forming the aqueous polyacrylamide gel. Alternatively, or additionally, the aqueous polyacrylamide gel is fed into the water jet cutting unit by means of mechanical conveying devices, such as scrolls. The at least one water-jet has a pressure of at least 150^*10⁵ Pa. The pressure may be considerably higher than this, for instance, up to 10,000^*10⁵ Pa. However, it is not normally necessary for the pressure to be as high as this and lower pressures, for instance no higher than 7,500^*10⁵ Pa are usually adequate. In one embodiment of the invention, the pressure of the water jet in the cutting unit has a pressure of from 150^*10⁵ Pa to 5,000^*10⁵ Pa, preferably from 200^*10⁵ Pa to 2,000^*10⁵ Pa, more preferably from 250^*10⁵ Pa to 1000^*10⁵ Pa.

Typically, the water jet would flow from a nozzle having a nozzle orifice of suitable diameter. By the term nozzle we mean a device which is designed to control the direction or the characteristics of a fluid flow, including to increase the velocity, as it exits. In general, the nozzle orifice diameter should be from 0.1 mm to 3.00 mm, for instance, from 0.25 mm to 2.00, or from 0.25 mm to 1 .00 mm, suitably from 0.30 mm to 0.90 mm, desirably from 0.40 mm 0.80 mm. It may be desirable to employ a multiplicity of nozzles on a head in which each nozzle delivers a stream of aqueous liquid at the aforementioned pressures of at least 150Ί 0⁵ Pa. When a multiplicity of nozzles on a head is employed the number of nozzles may be at least 2, for instance, from 2 to 10 nozzles. The nozzles may be arranged in one plane or in different planes and angles. The nozzles may be arranged in such a way, for instance over a domed surface of the head, that the multiplicity of streams radiate out in different axises. Such a multiplicity of nozzles may be arranged such that the streams of aqueous liquid form an array each travelling in different directions.

The at least one nozzle may rotate or oscillate. In one embodiment, the at least one nozzle oscillates. Such oscillation of the nozzle may produce a fan shaped water stream sweep pattern. In this embodiment of the invention, it may be of particular value to employ a multiplicity of nozzles which can oscillate. Typically, the number of nozzles may be from 2 to 8, preferably from 2 to 6. It may also be desirable that a multiplicity of nozzles are arranged on at least one head, each head containing from 2 to 10 nozzles. It may be desirable for the multiplicity of heads, for instance, from 2 to 10 heads, each head containing the multiplicity of nozzles, to be employed. In this case each of the heads may separately oscillate. Such multiplicity of nozzles or multiplicity of heads each may be positioned

circumferentially with respect to the aqueous polyacrylamide gel, such that the water streams extend inwardly. The multiplicity of nozzles and/or multiplicity of heads may be positioned evenly such that the distance between all adjacent nozzles is equal.

Alternatively, they may not to be evenly spaced.

Thus, when the multiplicity of nozzles or multiplicity of heads are arranged

circumferentially the aqueous polyacrylamide gel would then pass within the circumferentially positioned nozzles and be cut by the multiplicity of aqueous liquid streams. The at least one oscillating nozzle or head may be moved by a suitable actuator mechanism.

Each oscillating nozzle may have a sweep of up to 180°. Typically, the sweep may be 30° to 180°, for instance from 35° to 75°. The exact range of the sweep will often depend on the exact number of nozzles employed. The oscillation frequency should for instance be up to 50 s^-1 (cycles per second), typically from 0.5 s^-1 to 50 s^_1.

When the at least one nozzle, for instance, multiplicity of nozzles, or at least one head, for instance multiplicity of heads, is/are arranged circumferentially with respect to the aqueous polyacrylamide gel, each of the at least one nozzles or at least one head may rotate circumferentially about the aqueous polyacrylamide gel. When the

circumferentially arranged at least one nozzle or at least one head rotates it may be desirable that each nozzle or each head may independently oscillate as given above. Alternatively, it may be desirable that when the circumferentially arranged at least one nozzle or at least one head rotates they may not oscillate. The rotation of the at least one nozzle or at least one head may be achieved by a suitable drive mechanism.

In another preferred embodiment of the invention, the at least one nozzle rotates and the stream of aqueous liquid generated forms a circular sweep pattern. The at least one nozzle may be a multiplicity of nozzles housed on at least one head. Such at least one rotating nozzle may be rotated by the action of a suitable motorized drive mechanism. It may be desirable to employ more than one rotating nozzle, for instance, a multiplicity of nozzles housed on at least one head. However, it is usually only necessary to employ one rotating nozzle or where more than one nozzle is employed the multiplicity of nozzles are arranged on one head. In one embodiment of the invention, the at least one rotating nozzle, or at least one head is mounted centrally and the aqueous liquid stream extends substantially perpendicular to the axis of the direction of the incoming aqueous polyacrylamide gel. In this embodiment, the aqueous liquid stream sweep pattern is disc shaped. In an adaptation of this preferred aspect the rotating nozzle or head, which is/are mounted centrally, may generate at least one stream of liquid which is not perpendicular to the direction of the incoming aqueous polyacrylamide gel, but instead is angled such that the at least one aqueous liquid stream sweep pattern is a cone shaped, for instance, an upright cone where the at least one aqueous liquid stream is angled downwards, or an inverted cone where the at least one aqueous liquid stream is angled upwards. Where the at least one aqueous liquid stream is angled either upwards or downwards it is preferred that the angle is no more than 50° up or down from the position which is perpendicular to the direction of the incoming aqueous polyacrylamide gel. Preferably this angle should be from 5° to 45°, more preferably from 10° to 35°, particularly from 15° to 25°.

In a further embodiment of the invention, the at least one rotating nozzle or rotating head is not mounted centrally but off center. For instance, where the cutting stage is contained in a surrounding wall section the rotating nozzle may be located at or close to the wall of the surrounding wall section. Typically, the nozzle or head would be orientated such that it generates at least one eccentric aqueous stream sweep pattern. The rotating nozzle or rotating head may rotate at a frequency of up to 3000 rpm

(revolutions per minute (i.e. 50 s^_1 cycles per second)). The rotational frequency may be selected by the skilled artisan. A higher rotational frequency, for example a rotational frequency from 500 rpm to 3000 rpm) may by trend tear the aqueous polyacrylamide gel into smaller parts while a smaller rotational frequency, for example from 10 rpm to less than 500 ppm, preferably 20 rpm to 200 rpm more properly cuts the aqueous polyacrylamide gel.

Desirably, the water-jet cutting unit will divide the aqueous polyacrylamide gel into numerous smaller sized pieces. The aqueous polyacrylamide gel pieces should conveniently have a size such that at least two dimensions are no more than 2 cm, preferably no more than 1 cm, more preferably no more than 0.5 cm. Preferably three dimensions of the aqueous polyacrylamide gel pieces should be no more than 2 cm, preferably no more than 1 cm, preferably no more than 0.5 cm. There is no lower limit necessary for the aqueous polyacrylamide gel pieces, since the smaller the pieces the easier it will be for the polymer to dissolve. In one embodiment, the aqueous polyacrylamide gel pieces have three dimensions each of from 0.1 to 0.5 cm.

The water-jet cutting unit may also comprise a sieve tray beneath the at least one stream of aqueous liquid. This is intended to prevent oversized aqueous

polyacrylamide gel lumps from passing into the next stage. The sieve tray should have openings of a size corresponding to the maximum size of aqueous polyacrylamide gel pieces which should be allowed to pass to the next stage. Suitably the sieve tray may be a mesh formed by a plurality of inter-meshing wires or bars. Alternatively, the sieve tray may be formed as a surface with a plurality of holes cut therein, for instance, analogous to a colander. Typically, the sieve tray should be a static device. It should extend to cover the whole area below where the aqueous polyacrylamide gel cutting is taking place. Preferably, the sieve tray may be affixed to the surrounding wall section. In embodiments of the present invention additional streams of aqueous liquid are directed at the surface of the sieve tray in order to facilitate the size reduction of the oversized aqueous polyacrylamide gel lumps captured by the tray. It may be desirable to employ one or more aqueous liquid streams of high-pressure, for instance, of at least 150^*10⁵ Pa in order to facilitate the cutting of the oversized aqueous

polyacrylamide gel lumps such that the aqueous polyacrylamide gel is cut into small enough pieces to pass through.

Desirably, a curtain of aqueous liquid is provided on the inside of the surrounding wall section. This curtain of aqueous liquid may help prevent aqueous polyacrylamide gel from sticking to the wall of the surrounding wall section and reduce friction of the moving polymer thereby reducing necessary static pressure or avoiding additional mechanical means to move the polymer towards the cutting area. Such curtain of aqueous liquid may be produced by providing a secondary aqueous liquid supply. Typically, the pressure of the aqueous liquid should be below 30^*10⁵ Pa, for instance, from 3^*10⁵ Pa to 20^*10⁵ Pa, desirably from 5^*10⁵ Pa to 10^*10⁵ Pa. The water may be fed to a ring main, in the form of an annulus, and mounted on the inside of the surrounding wall section. In order to be most effective, the ring main or annulus should be mounted at or close to the top of the surrounding wall section to provide the maximum protection by the curtain of water. Desirably the aqueous liquid flows from the ring main or annulus down the inner surface of the wall of the surrounding wall section as a curtain.

Figures 9 to 12 represent schematically several embodiments of a water-jet cutting unit for use in the present invention.

Figure 9 illustrates schematically a water-jet cutting unit for cutting the aqueous polyacrylamide gel. The device comprises a surrounding wall section (101 ), in this case a tubular wall, surrounding a centrally mounted nozzle (102) which rotates and is driven by a motor (103) or propelled by the flowing aqueous liquid, which forms the stream. The nozzle is supported on a fixed mounting (104). A high-pressure stream of aqueous liquid (105) is ejected perpendicular to the axis of the device and rotates as the nozzle rotates. The stream of aqueous liquid forms a circular disc pattern as the nozzle rotates. The nozzle is fed from a aqueous liquid feed line (106) supplied by a high pressure aqueous liquid source (107). A sieve tray (108) is located beneath the stream of water and prevents oversized polymer lumps from passing. A secondary aqueous liquid supply (109) of low pressure is fed into a ring main (1 10), in the form of an annulus, located at the upper end of the tubular wall. Aqueous liquid flows out of the annulus to form a water curtain (1 1 1 ), which prevents aqueous polyacrylamide gel from sticking to the tubular wall. Aqueous polyacrylamide gel (1 13) enters the tubular wall from above and passes down the device where it is cut by the high-pressure water stream to form cut hydrated polymer pieces which are small enough to pass through the sieve tray and then the cut aqueous polyacrylamide gel pieces (1 14) exit from the bottom of the device.

Figure 10 illustrates a device analogous to the device of Figure 8 except the nozzle (102) provides a high-pressure stream of water which is angled downwards (105A) to form a conical pattern as the nozzle rotates. The sieve tray is in the shape of an upright cone (108A). All other features are as in the case of Figure 8.

Figure 1 1 illustrates a device analogous to the device of Figure 8 except the nozzle (102) provides a high-pressure stream of water which is angled upwards (105B) to form a conical pattern as the nozzle rotates. The sieve tray is in the shape of an inverted cone (108B). All other features are as in the case of Figure 8.

Figure 12 illustrates a device analogous to the device of Figure 8 except the nozzle (102) is positioned off center to provide an eccentric high-pressure water stream (105) sweep pattern. All other features are as in the case of Figure 8.

Combinations The described methods of comminuting the aqueous polyacrylamide gel may also combined with each other.

In one embodiment of the invention, water-jet cutting is combined with cutting by means of a static cutting member. Preferably, such a static cutting member is integrated with the water-jet cutting unit and consequently, the water-jet cutting comprises at least one static cutting member. The at least one static cutting member may for instance be one or more knives, blades, cutting wires or any combination thereof. In one form the at least one cutting member may consist of a multiplicity of knives or blades mounted on the wall of the tubular section circumferentially with the knives or blades extending inwardly. In another form the at least one cutting member may be knives or blades mounted from a central position with the knives or blades extending out radially. In a further form the at least one cutting member may be a mesh of knives, blades or cutting wires. Typically, the static cutting member, where employed, should extend over the whole cross-section of the surrounding wall section. Suitably, the aqueous polyacrylamide gel may be cut by contacting the at least one static cutting member before contacting the at least one stream of aqueous liquid. Figure 13 illustrates schematically a water-jet cutting unit combined with static cutting means. The device comprises a surrounding wall section (101 ), in this case a tubular wall, into which the aqueous polyacrylamide gel (1 13) enters from the top. A mesh of cutting blades (1 12) initially cuts the hydrated polymer into strands as it descends. High-pressure water streams (105) are ejected from nozzles (102) that are positioned circumferentially. The nozzles each oscillate laterally to each generate a fan shaped water stream sweep pattern (1 15) which cut the polymer strands as they descend. The oscillation of the nozzles is driven by an actuator (not shown) in each case. The aqueous polyacrylamide pieces (1 14) exit through the bottom of the device.

In another embodiment, water-jet cutting may be combined with static mixing. For that purpose, the aqueous mixture comprising pieces of polyacrylamide gel leaving the water-jet cutting unit is conveyed through at least one static mixer. Additional aqueous liquid may be added to the mixture, before it enters into the at least one static mixer.

In another embodiment, water-jet cutting is combined with both, static cutting means and a static mixer. The combination with static cutting means has already been described above. Thereafter, the aqueous mixture comprising pieces of polyacrylamide gel leaving the comminution unit comprising a water-jet cutting step and a static cutting step is conveyed through at least one static mixer. Additional aqueous liquid may be added to the mixture, before it enters into the at least one static mixer.

In one embodiment, comminuting the aqueous polyacrylamide gel is carried out by at least one means selected from rotating water-jets, rotating knives or and a hole perforation plate. Preferably, a combination of at least one hole perforation plate and rotating water-jets or at least one hole perforation plate and rotating knives may be used.

In other embodiments, the comminution unit comprises a combination of water-jet cutting and a hole perforation plate. The hole perforation plate comprises holes. The shape of the holes is not specifically limited. Examples comprise circular holes, ellipsoidal holes, triangular holes, quadrangular holes such as quadratic, rectangular, or rhombic holes, pentagonal holes, hexagonal holes or star-like holes but also longitudinal holes such as slots. The holes may be cylindrical holes but they may also be conical.

The dimensions of the holes are not specifically limited. However, preferably at least one dimension of the holes should be from 0.5 to 5 mm. In one embodiment of the invention, the hole perforation plate comprises circular holes having a diameter from 0.5 to 5 mm, for example from 1 mm to 3 mm.

The aqueous polyacrylamide is conveyed from the polymerization unit through the hole perforation plate. One or more rotating nozzles for water-jets are mounted above or below the hole perforation plate.

One embodiment of such a combination is schematically shown in figure 14. Figure 14 schematically shows a polymerization unit having an upper cylindrical part (120), a lower conical part (121 ) and a bottom opening (125) which may be opened and closed. The polymerization unit is connected with a comminution unit comprising a hole perforation plate. One rotating nozzle for water-jets is mounted below the hole perforation plate. The aqueous polyacrylamide gel is removed from the polymerization unit by opening the bottom opening (125) and applying pressure onto the upper surface of the aqueous polyacrylamide gel. The gel is conveyed through the opened bottom opening and the hole perforation plate. The hole perforation plate generates strings of aqueous polyacrylamide gel ("spaghetti") which are cut into small pieces by the water- jets.

Figure 15 shows a similar embodiment except that not one two nozzles are mounted below the hole performation plate. Of course also more than two nozzles may be used, for example 4 nozzles. Figures 16 and 17 show similar embodiments in which the nozzle(s) for water-jets are mounted above and not below the hole perforation plate.

Figure 18 shows an alternative embodiment comprising a rotating knife mounted below the hole perforation plate for cutting. Its function is the same a detailed above (figures 14 and 15), except that a mechanical knife and not water-jets are used for cutting the strings of polyacrylamide gel. In this embodiment, water (127) is added into the cutting space below the hole perforation plate. The water may be added through one or more than one water inlets. The amount of water into the cutting space may already up to 50 % by weight of the entire amount of water needed for dissolving the aqueous polyacrylamide gel, for example from 5 % to 25 % by weight.

Step [4-2]

The dissolution of the aqueous polyacrylamide gel in an aqueous liquid basically may be performed in any kind of dissolution unit. Preferably, the dissolution of the aqueous polyacrylamide gel is conducted in a relocatable dissolution unit.

Examples of suitable dissolution units comprise stirred vessels. A dissolution unit may only comprise one vessel or it may comprise more than one vessel which may be operated in series or in parallel. Mixing may also be achieved by flowing the contents of the dissolution vessel out through a conduit and then recirculating back into the mixing vessel. Other examples comprise a combination of static mixers with unstirred vessels or in-line dispersing such as rotor-stator units.

In one embodiment of the invention, the aqueous polyacrylamide gel is dissolved in the aqueous liquid by passing the aqueous polyacrylamide gel pieces of step [5-1 ], preferably a mixture of aqueous polyacrylamide gel pieces in an aqueous liquid into a dissolution comprising at least a dissolution vessel and means for mixing the polyacrylamide gel with the aqueous liquid. Depending on the amount of aqueous liquid already added to the aqueous polyacrylamide gel in the preceding comminution step and the desired concentration of the final polyacrylamide solution additional aqueous liquid may be added to the dissolution vessel.

Examples of means for mixing comprise one or more impellers or stirrers which optionally may be combined with static mixing devices. Mixing may also be achieved by flowing the contents of the dissolution vessel out through a conduit and then recirculating back into the mixing tank. The dissolution unit may also comprise two or more than two dissolution vessels connected in series. The volume of the dissolution vessel is not specifically limited and may range from 10 m³ to 150 m³, for example from 20 m³ to 50 m³ per vessel. Figure 19 schematically represents one embodiment of a relocatable dissolution unit. The unit comprises a frame (40) and a dissolution vessel (41 ) filled with aqueous liquid and aqueous polyacrylamide gel pieces. For mixing the contents of the dissolution vessel (51 ), the dissolution unit comprises two stirrers (42) and (43). It goes without saying that also other numbers of stirrers and other constructions of stirrers than those depicted in figure 14 may be used. By the way of examples one agitator shaft may be equipped with two stirrers in different positions.

The aqueous polyacrylamide gel pieces, preferably a mixture of aqueous

polyacrylamide gel pieces and aqueous liquid / aqueous polyacrylamide solution is filled into the dissolution vessel through an opening (44) and the polyacrylamide solution may be removed through the line (45).

In another embodiment, two or more dissolution units may be connected in series. In embodiments of the invention 2 to 15, for example 5 to 12 dissolution units may be connected in series. The aqueous polyacrylamide gel pieces, preferably the mixture of aqueous polyacrylamide pieces are filled in the first dissolution vessel and mixed with aqueous liquid. The mixture is continuously transported into at least a second dissolution unit for further dissolution. It may transferred from there into a third dissolution unit. From the last dissolution unit aqueous polyacrylamide solution may be removed. It is also possible, that not separate relocatable dissolution units are used but that two or more dissolution vessels may be connected in series in just one frame.

In another embodiment, at least two the relocatable dissolution units, preferably at least three relocatable dissolution may be connected in a cyclical manner, i.e. they are connected in series and the last one is connected again with the first one.

Figure 20 schematically represents an embodiment in which two dissolution units are connected in series. The contents of the first dissolution unit (45) is added to the next dissolution unit the polyacrylamide solution may be removed through the line (46). Additional aqueous liquid may also be added to the second dissolution unit.

In another embodiment, a relocatable dissolution unit is a dissolution unit fixed on a truck.

The concentration of the aqueous polyacrylamide solution is selected by the skilled artisan according to the intended use of the solution. Typically, the concentration of the polyacrylamide solution may be up to 2% by weight, for instance, from 0.01 to 2%, suitably from 0.05 to 1.5%, often, 0.1 % to 1 %.

Basically, it is possible to transfer the aqueous polyacrylamide solution directly to the application where it is used. This may be by means of piping or other suitable conduit.

In one embodiment, the aqueous polyacrylamide solution is stored in a storage vessel or a series of storage vessels for use. Storing the solution in particular is advantageous to make the necessary analytics and the quality control.

Such storage vessels may be relocatable storage vessels. Also aqueous

polyacrylamide solutions obtained by dissolving polyacrylamide powders may be stored before using them. For that purpose, storage vessels for storing polyacrylamide solutions may already available at the site of use. It is of course possible to use such storage vessels -whether relocatable or not- for the purpose of storing aqueous polyacrylamide solutions obtained by dissolution of aqueous polyacrylamide gels. In another embodiment, the aqueous polyacrylamide solution may be further diluted for application after the dissolution unit.

Measurement and Control

In one embodiment, Locations A and B each comprise a central process measuring and control technology unit. In a preferred embodiment of the invention, the process measuring and control technology unit is a relocatable unit. Preferably, the process measuring and control technology unit at location A is connected with all units at location A and also preferably, the process measuring and control technology unit at location B is connected with all units at location B, thereby enabling a central process control similar to fixed plants. In one embodiment, all connections with measuring and control instruments of a certain unit, e.g. the dissolution unit, the monomer storage units or the polymerization units are bundled in one cable, for example BUS

technology, so that they may be easily plugged together. Of course, also other connecting technologies are possible, for example radio links. Use of the aqueous polyacrylamide solutions

The aqueous polyacrylamide solutions manufactured according to the present invention may be used for various purposes, for example for mining applications, oilfield applications, water treatment, waste water cleanup, paper making or agricultural applications.

For the application, the aqueous polyacrylamide solutions may be used as such or they may be formulated with further components. The specific composition of aqueous polyacrylamide solutions is selected by the skilled artisan according to the intended use of the polyacrylamide solution.

Oilfield applications

Examples of oilfield applications in which the aqueous polyacrylamide solutions manufactured according to the present invention may be used include enhanced oil recovery, oil well drilling or the use as friction reducers, for example friction reducers for fracturing fluids.

Enhanced oil recovery

In one embodiment of the invention, the aqueous polyacrylamide solutions

manufactured according to the present invention are used for enhanced oil recovery.

Accordingly, the present invention also relates a method for producing mineral oil from underground mineral oil deposits by injecting an aqueous fluid comprising at least an aqueous polyacrylamide solution into a mineral oil deposit through at least one injection well and withdrawing crude oil from the deposit through at least one production well, wherein the aqueous polyacrylamide solution is prepared by the process for producing an aqueous polyacrylamide solution as described above. Details of the process have already been disclosed above.

For the method of enhanced oil recovery, at least one production well and at least one injection well are sunk into the mineral oil deposit. In general, a deposit will be provided with a plurality of injection wells and with a plurality of production wells. An aqueous fluid is injected into the mineral oil deposit through the at least one injection well, and mineral oil is withdrawn from the deposit through at least one production well. By virtue of the pressure generated by the aqueous fluid injected, called the "polymer flood", the mineral oil flows in the direction of the production well and is produced through the production well. In this context, the term "mineral oil" does not of course just mean a single-phase oil; instead, the term also encompasses the customary crude oil-water emulsions.

The aqueous fluid for injection comprises the aqueous poly acrylamide solution prepared by process according to the present invention. Details of the process have been disclosed above. In one embodiment of the method of enhanced oil recovery according to the present invention, location B may be at an injection well to be treated with aqueous

polyacrylamide solutions or close to such an injection well. In another embodiment, location B may be in between a plurality of such injection wells or at one of them and the aqueous polyacrylamide solution is distributed form there to all injection wells, for example by means of pipelines.

Location A is apart from location B. Preferably, location A is a local hub which provides a plurality of different locations B with aqueous polyacrylamide gels. In one

embodiment, location A may at a central point over a subterranean, oil-bearing formation or a central point in between different subterranean, oil-bearing formations and from location A a plurality of oil wells to be treated is provided with aqueous polyacrylamide gels for further processing.

The aqueous acrylamide solution obtained may be used as such or it may be mixed with further components. Further components for enhanced oil recovery fluids may be selected by the skilled artisan according to his/her needs.

For enhanced oil recovery, a homopolymer of acrylamide may be used, however preferably water-soluble copolymers comprising at least 10 %, preferably at least 20 %, and more preferably at least 30 % by weight of acrylamide and at least one additional water-soluble, monoethylenically unsaturated monomer different from acrylamide are used. Suitable water-soluble comonomers have already been mentioned above and we refer to the disclosure above. In one embodiment, water-soluble comonomers may be selected from water-soluble, monoethylenically unsaturated monomers comprising at least one acid group, or salts thereof. The acidic groups are preferably selected from the group of -COOH, -SO3H and -PO3H2 or salts thereof. Preference is given to monomers comprising COOH groups and/or -SO3H groups or salts thereof. Suitable counterions have already been mentioned above. Examples of such comonomers comprise acrylic acid, methacrylic acid, crotonic acid, itaconic acid, maleic acid, fumaric acid, vinylsulfonic acid, allylsulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid (ATBS), 2- methacrylamido-2-methylpropane-sulfonic acid, 2-acrylamidobutanesulfonic acid, 3- acrylamido-3-methylbutane-sulfonic acid, 2-acrylamido-2,4,4-trimethylpentanesulfonic acid, vinylphosphonic acid, allylphosphonic acid, N-(meth)acrylamidoalkylphosphonic acids and (meth)acryloyloxyalkyl-phosphonic acids.

In a preferred embodiment, acrylic acid and/or ATBS or salts thereof may be used as comonomers.

In such copolymers, the amount of acrylamide usually is from 20 % by wt. to 90 % by wt. and the amount of acrylic acid and/or ATBS or salts thereof is from 10 % by wt. to 80 % by wt., relating to the amount of all monomers in the copolymer. Preferably, the amount of acrylamide is from 60 % by wt. to 80 % by wt. and the amount acrylic acid and/or ATBS or salts thereof is from 20 % by wt. to 40 % by wt. In another embodiment, the copolymers to be used for enhanced oil recovery comprise at least one water-soluble, monoethylenically unsaturated monomer comprising at least one acid group, or salts thereof, preferably acrylic acid and/or ATBS or salts thereof, and at least one associative monomer. Examples of associative monomers have already been disclosed above. In one embodiment, at least one associative monomer of the general formula (III), (IV), or (V) is used, preferably at least one associative monomer of the general formula (V). Preferred embodiments of the associative monomers (III), (IV), and (V) have already been disclosed above and it is explicitly referred to that description.

In such polyacrylamides, the amount of acrylamide usually is from 40 % by wt. to 89.9 % by wt., the amount of acrylic acid and/or ATBS or salts thereof is from 10 % by wt. to 59.9 %, and the amount of associative monomers is from 0.1 to 5 % by wt., relating to the amount of all monomers in the copolymer.

In one embodiment, the polyacrylamides for EOR comprise 45 % to 55 % by weight of acrylamide, 0.1 to 5 %, preferably 0.1 to 2 % by weight of at least one associative monomer of the general formula (V) mentioned above, including the preferred embodiments, and 40 to 54.9 % by weight of acrylic acid or salts thereof.

The aqueous fluid for injection can be made up in freshwater or else in water comprising salts, such as seawater or formation water. As already outlined above, water comprising salts may already be used for dissolving the aqueous polyacrylamide gel. Alternatively, the polyacrylamide gel may be dissolved in fresh water, and the solution obtained can be diluted to the desired use concentration with water comprising salts.

The aqueous injection fluid may of course optionally comprise further components. Examples of further components include biocides, stabilizers, free-radical scavengers, initiators, surfactants, cosolvents, bases and complexing agents.

The concentration of the copolymer in the injection fluid is fixed such that the aqueous formulation has the desired viscosity for the end use. The viscosity of the formulation should generally be at least 5 mPas (measured at 25°C and a shear rate of 7 s^-1), preferably at least 10 mPas.

In general, the concentration of the polyacrylamide in the injection fluid is 0.02 to 2% by weight based on the sum total of all the components in the aqueous formulation. The amount is preferably 0.05 to 0.5% by weight, more preferably 0.1 to 0.3% by weight and, for example, 0.1 to 0.2% by weight.

Friction reducers for hydraulic fracturing In another embodiment of the invention, the aqueous polyacrylamide solutions manufactured according to the present invention are used as friction reducers in hydraulic fracturing applications.

Hydraulic fracturing involves injecting fracturing fluid through a wellbore and into a formation under sufficiently high pressure to create fractures, thereby providing channels through which formation fluids such as oil, gas or water, can flow into the wellbore and thereafter be withdrawn. Fracturing fluids are designed to enable the initiation or extension of fractures and the simultaneous transport of suspended proppant (for example, naturally-occurring sand grains, resin-coated sand, sintered bauxite, glass beads, ultra-lightweight polymer beads and the like) into the fracture to keep the fracture open when the pressure is released.

In one embodiment of hydraulic fracturing, fracturing fluids having a high viscosity are used. Such a high viscosity may be achieved by crosslinked polymers, such as crosslinked guar. Such a high viscosity is necessary to ensure that the proppants remain distributed in the fracking fluid and don't sediment, for example already in the wellbore.

In another embodiment of hydraulic fracturing, also known as "slickwater fracturing", fluids having only a low viscosity are used. Such fluids mainly comprise water. In order to achieve proppant transport into the formation, the pumping rates and the pressures used are significantly higher than for high-viscosity fluids. The turbulent flow of the fracking fluid causes significant energy loss due to friction. In order to avoid or at least minimize such friction losses, high molecular weight

polyacrylamides may be used which change turbulent flow to laminar flow. Accordingly, in another embodiment the present invention relates to a method of fracturing subterranean formations by injecting an aqueous fracturing fluid

comprising at least water, proppants and a friction reducer through a wellbore into a subterranean formation at a pressure sufficient to flow into the formation and to initiate or extend fractures in the formation, wherein the friction reducer comprises an aqueous polyacrylamide solution prepared by the process for producing an aqueous polyacrylamide solution as described above. Details of the process have already been disclosed above. In that embodiment, location B is at a production well well to be treated with aqueous polyacrylamide solutions or close to such a

production well.

Mining applications

In one embodiment, the method for preparing an aqueous polyacrylamide solution according to the present invention is carried out in areas where mining, mineral processing and/or metallurgy activities takes place. Consequently, the aqueous polyacrylamide solution as product obtained by the method of the present invention is preferably used for applications in the field of mining, mineral processing and/or metallurgy and the method for preparing the aqueous polyacrylamide solution is preferably used at the plant of the respective industry.

Preferably, mining activities comprises extraction of valuable minerals or other geological materials from certain deposits. Such deposits can contain ores, for example metal containing ores, sulfidic ores and/or non-sulfidic ores. The ores may comprise metals, coal, gemstones, limestone or other mineral material. Mining is generally required to obtain any material in particular mineral material that cannot be grown through agricultural processes, or created artificially in a laboratory or factory. The aqueous polyacrylamide solution according to the present invention is preferably used to facilitate the recovery of mineral material, for beneficiation of ores and for further processing of ores to obtain the desired minerals or metals.

Typically, mining industries, mineral processing industries and/or metallurgy industries are active in the processing of ores and in the production of for example alumina, coal, iron, steel, base metals, precious metals, diamonds, non-metallic minerals and/or areas where aggregates play an important role. In such industries, the method of the present invention and the obtained homo- or copolymer of acrylamide can be used for example at plants for alumina production, where alumina is extracted from the mineral bauxite using the Bayer caustic leach process,

at plants where the coal washing process demands a closed water circuit and efficient tailings disposal to satisfy both economic and environmental demands, at plants for iron and steel production, where the agglomeration of fine iron concentrates to produce pellets of high quality is a major challenge for the iron ore industry,

at plants for base metal production, where flocculants find several uses in base metal production,

at plants for precious metals production, where reagents are used to enhance the tailings clarification process allowing the reuse of clean water,

at diamond plants, where efficient water recovery is paramount in the arid areas where diamonds are often found,

at plants for non-metallic mineral production where reagents enhance water recovery or aid the filtration processes to maximize process efficiency,

- at plants where aggregates have to be produced and flocculants and filter aids are needed to enhance solid/liquid separation.

Accordingly, the present invention relates to the use of an aqueous polyacrylamide solution for mining, mineral processing and/or metallurgy activities comprising the use for solid liquid separation, for tailings disposal, for polymer modified tailings deposition, for tailings management, as density and/or rheology modifier, as agglomeration aid, as binder and/or for material handling, wherein the aqueous polyacrylamide solution is prepared at the plant of the respective industry, comprising for example the following steps: hydrolyzing acrylonitrile in water in presence of a biocatalyst capable of converting acrylonitrile to acrylamide so as to obtain an acrylamide solution, polymerizing the acrylamide solution so as to obtain a polyacrylamide gel, and dissolving the polyacrylamide gel by addition of water so as to obtain an aqueous polyacrylamide solution.

For the mining, mineral processing and/or metallurgy activities a homopolymer of acrylamide for example can be used. Further preferred are also copolymers of acrylamide. Such copolymers of acrylamide can be anionic, cationic or non-ionic. Anionic copolymers are for example co-polymers of acrylamide with increasing proportions of acrylate groups, which give the polymers negative charges, and thus anionic active character, in aqueous solution. Anionic copolymers of acrylamide can in particular be used for waste water treatment in metallurgy like iron ore plants, steel plants, plants for electroplating, for coal washing or as flocculants. Non-ionic polymers and/or copolymers of acrylamide can be used for example as nonionic flocculants suitable as settlement aids in many different mineral processing applications and are particularly effective under very low pH conditions, as encountered for example in acidic leach operations. Cationic copolymers of acrylamide have in particular an increasing proportion of cationic monomers. The cationic groups, which are thus introduced into the polymer, have positive charges in aqueous solution. It is preferred, that the polymer obtained from the method of the present invention is used as flocculant in a process in which individual particles of a suspension form aggregates. The polymeric materials of the present invention forms for example bridges between individual particles in the way that segments of the polymer chain adsorb on different particles and help particles to aggregate. Consequently, the polymers of the present invention act as agglomeration aid, which may be a flocculant that carries active groups with a charge and which may counterbalance the charge of the individual particles of a suspension. The polymeric flocculant may also adsorb on particles and may cause destabilization either by bridging or by charge neutralization. In case the polymer is an anionic flocculant, it may react against a positively charged suspension (positive zeta potential) in presence of salts and metallic hydroxides as suspension particles, for example. In case the polymer of the present invention is for example a cationic flocculant, it may react against a negatively charged suspension (negative zeta potential) like in presence of for example silica or organic substances as suspension particles. For example, the polymer obtained from the method of the present invention may be an anionic flocculant that agglomerates clays which are electronegative.

Preferably, the method of the present invention and the obtained polymer and/or copolymer of acrylamide (polyacrylamide) is used for example in the Bayer process for alumina production. In particular, the polyacrylamide can be used as flocculant in the first step of the Bayer-Process, where the aluminum ore (bauxite) is washed with NaOH and soluble sodium aluminate as well as red mud is obtained. Advantageously, the flocculation of red mud is enhanced and a faster settling rate is achieved when acrylamide polymers and/or co-polymers are added. As red mud setting flocculants, polyacrylamide may be used for settling aluminum red mud slurries in alumina plants, provides high settling rates, offers better separation performance and reduces suspended solids significantly. Also the liquor filtration operations are improved and with that the processing is made economically more efficient. It is further preferred that the polyacrylamides are used in decanters, in washers, for hydrate thickening, for green liquor filtration, as crystal growth modifiers, as thickener and/or as rheology modifier.

It is further preferred that the method of the present invention and the polymers of acrylamide are used in processes for solid liquid separation as for example flocculant or dewatering aid, which facilitate thickening, clarifying, filtration and centrifugation in order to enhance settling rates, to improve clarities and to reduce underflow volumes. In particular, in filtration processes the polyacrylamide homo- or co-polymer of the present invention increase filtration rates and yields, as well as reducing cake moisture contents.

Further preferred is the use of the method and the obtained polyacrylamide of the present invention in particular for material handling and as binder. In the mining industry, the movement of large volumes of material is required for processing the rock and/or ores which have been extracted from the deposits. The typical rock and/or ore processing for example starts with ore extraction, followed by crushing and grinding the ore, subsequent mineral processing (processing or the desired/valuable mineral material), then for example metal production and finally the disposal of waste material or tailings. It was a surprise that with the method of the present invention and in particular the obtained polyacrylamide the handling of the mineral material can be enhanced by increasing efficiency and yield, by improving product quality and by minimizing operating costs. Particularly, the present invention can be used for a safer working environment at the mine site and for reduction of environmental discharges.

Preferably, the method and the obtained polyacrylamide of the present invention can for example be used as thickener, as density and/or rheology modifier, for tailings management. The obtained polyacrylamide polymer can modify the behavior of the tailings for example by rheological adjustment. The obtained polyacrylamide polymers are able to rigidify tailings at the point of disposal by initiating instantaneous water release from the treated slurry. This accelerates the drying time of the tailings, results in a smaller tailings footprint and allows the released water to be returned to the process faster. This treatment is effective in improving tailings properties in industries producing alumina, nickel, gold, iron ore, mineral sands, oil sands or copper for example. Further benefits of the polymers obtained according to the present invention are for example maximized life of disposal area, slurry placement control, no reworking of deposit required, co-disposal of coarse and fine material, faster trafficable surface, reduced evaporative losses, increased volume for recycling, removed fines contamination, reduced fresh water requirement, lower land management cost, less mobile equipment, lower rehabilitation costs, quicker rehabilitation time, lower energy consumption, accelerated and increased overall water release, improved rate of consolidation, reduced rate of rise, reduced amount of post depositional settlement. Preferably, the obtained product from the method of the present invention is used for agglomeration of fine particulate matter and for the suppression of dust. Particularly, polyacrylamide polymers or copolymers are used as organic binders to agglomerate a wide variety of mineral substrates. For example, the polyacrylamide polymers or copolymers are used for iron ore pelletization as a full or partial replacement for bentonite. The product from the method of the present invention can be used as binder, in particular as solid and liquid organic binders in briquetting, extrusion, pelletization, spheronization and/or granulation applications and gives for example excellent lubrication, molding and/or binding properties for processes such as coal-fines briquetting, carbon extrusion, graphite extrusion and/or nickel briquetting.

It is preferred that the method of the present invention and in particular the aqueous polyacrylamide solution obtained by the method is used for the beneficiation of ores which comprise for example coal, copper, alumina, gold, silver, lead, zinc, phosphate, potassium, nickel, iron, manganese, or other minerals.

Advantages of the process according to the invention

The process according to the present invention provides significant advantages as compared to known processes for the manufacture of polyacrylamide powders as well as compared to known processes for manufacturing polyacrylamide solutions at the site of use.

As already outlined above, drying aqueous polyacrylamide gel thereby obtaining polyacrylamide powders, transporting the powders to the site of use and redissolving the dry powders at the site of use is energy extensive and consequently the operational costs for drying are high. Furthermore, also the capital expenditure for the entire postprocessing equipment including size reduction, drying, sieving, grinding is significant in relation to the total capital expenditure for the entire plant.

As compared to the known processes of manufacturing aqueous polyacrylamide solutions on-site by polymerizing aqueous acrylamide solutions and dissolving the gels obtained the process according to the present invention has the advantage that it is not necessary to move the entire plant when polyacrylamide solutions are no longer needed at a location, i.e. at an oil well, but at another location, i.e. another oil well. The equipment for manufacturing the gels may remain at location A and only the equipment for comminuting and dissolving the aqueous gel needs to be moved. Furthermore, location A bundles everything being complicated (e.g. polymerization) and/or having a hazard potential (i.e. storage of potentially hazardous products) and therefore requires personnel experienced with chemical production. At location B only the less

complicated steps of comminuting and dissolving the aqueous polyacrylamide gel needed to be carried out (i.e. only physical processes).

Besides providing polyacrylamides as powders it is also known to manufacture inverse emulsions of polyacrylamides. Such inverse emulsions typically comprise about 30 % to 40 % by weight of polyacrylamides. The process according to the present invention also provides advantages as compared to using inverse emulsions. Keeping the concentration of polyacrylamides in the inverse emulsions in mind it is necessary to transport significant amounts of solvents to the site of use. Examples:

The invention is illustrated in detail by the examples which follow. I) Simulation of gel temperature in polymerization unit

In order to better to demonstrate that the polyacrylamide gel cools down in the polymerization unit only very slowly, a mathematical simulation was run. For the simulation, the following parameters were used:

temperature of the gel after polymerization, same starting temperature within entire reactor Figure 7 shows the results of the simulation.

As expected the average temperature decreases faster than the maximum temperature (the maximum temperature basically is observed in the center of the polymerization unit which is most apart from the walls). Basically, the temperature of the polymer gel only slowly decreases. Even after 5 days the average temperature still is about 65°C and the maximum temperature still close to 90°C. After 10 days the average temperature is about 45°C and the maximum temperature about 80°C. The simulation shows at least parts of the gel still have a temperature of 80°C even 10 days after polymerization. II) Gel Damage and strategies to avoid gel damage

Test Series 1

The first test series was performed with copolymers comprising 75 mole % acrylamide and 25 mole % sodium acrylate.

Copolymer 1 is an unstabilized copolymer for which a monomer concentration of 30 wt. % relating to the sum of all components of the monomer solution was used. The acrylamide used was made by Cu-catalysis. The temperature in course of

polymerization rose to 86 °C.

For copolymers 2, 3, and 4 the monomer concentration was reduced to 23 wt. % and the temperature in course of polymerization only rose to 60°C. Furthermore, bio acrylamide was used instead of Cu acrylamide.

Copolymer 2 also was unstabilized, copolymer 3 comprised the stabilizer NaMBT, and copolymer 4 the polymerizable stabilizer MA-HPMP (which is a monoethylenically unsaturated monomer which polymerizes with the other monomers).

Also for copolymer 5, the monomer concentration was 23 % by wt., acrylamide obtained by Cu-catalysis from acrylonitrile was used. No stabilizer was used.

Copolymer 1 :

Copolymer comprising 69.4 wt. % (75.0 mole %) of acrylamide and 30.6 wt. % (25 mole % ) of sodium acrylate A 5 I beaker with magnetic stirrer, pH meter and thermometer was initially charged with 918,0 g of a 35% aqueous solution of Na-acrylate, and then the following were added successively: 1020,4 g of distilled water, 1457,4 g of acrylamide (52 % by weight in water, Cu-catalysis), 26.3 g of 4,4'-azobis(4-cyanovaleric acid) solution (4 % by weight in 5 % sodium hydroxide solution) and 10.5 g of a 5% aqueous solution of

diethylenetriamine-pentaacetic acid, pentasodium salt.

After adjustment to pH 6.0 with a 50 % by weight solution of sulfuric acid and addition of the rest of the water to attain the desired monomer concentration of 30 % by weight (total amount of water 1069,6 g minus the amount of water already added, minus the amount of acid required), the monomer solution was adjusted to the initiation temperature of 0 °C. The solution was transferred to a Dewar vessel, the temperature sensor for the temperature recording was inserted, and the flask was purged with nitrogen for 45 minutes. The polymerization was initiated with 17.5 g of a 4% methanolic solution of the azo initiator azo-bis-(isobutyronitrile)dihydrochloride, 1 .68 g of a 1 % t-BHPO solution and 0.84 g of a 1 % sodium sulfite solution. With the onset of the polymerization, the temperature rose to 86 °C within about 50 min. A solid polymer gel was obtained.

After the polymerization, the gel was incubated for 2 hours at 80 °C and the gel block was comminuted with the aid of a meat grinder. The comminuted aqueous

polyacrylamide gel was kept for further testing without drying.

Copolymer 2:

Copolymer comprising 69.4 wt. % (75.0 mole %) of acrylamide and 30.6 wt. % (25 mole % ) of sodium acrylate

A 5 I beaker with magnetic stirrer, pH meter and thermometer was initially charged with 703.8 g of a 35% aqueous solution of Na-acrylate, and then the following were added successively: 1500 g of distilled water, 1074.4 g of acrylamide (52 % by weight in water, bio acrylamide), 10.5 g of a 5% aqueous solution of diethylenetriamine- pentaacetic acid, pentasodium salt, 2.8 g of a 1 wt. % aqueous solution of sodium hypophoshite hydrate.

After adjustment to pH 6.4 with a 20 % by weight solution of sulfuric acid and addition of the rest of the water to attain the desired monomer concentration of 23 % by weight (total amount of water 171 1 .3 g minus the amount of water already added, minus the amount of acid required), the monomer solution was adjusted to the initiation temperature of 0°C. The solution was transferred to Dewar vessel, the temperature sensor for the temperature recording was inserted, and the flask was purged with nitrogen for 45 minutes. The polymerization was initiated with 21 g of a 10% aqueous solution of the water-soluble azo initiator 2,2'-azobis(2-methylpropionamidine) dihydrochloride (Wako V-50; 10h 12 in water 56°C), 1 .75 g of a 1 % t-BHPO solution and 1.05 g of a 1 % sodium sulfite solution. With the onset of the polymerization, the temperature rose to 60°C within about 50 min. A solid polymer gel was obtained. After the polymerization, the gel was incubated for 4 hours at 60 °C and the gel block was comminuted with the aid of a meat grinder. The comminuted aqueous

polyacrylamide gel was kept for further testing without drying.

Copolymer 3:

Copolymer comprising 69.4 wt. % (75.0 mole %) of acrylamide and 30.6 wt. % (25 mole % ) of sodium acrylate, stabilized with 0.25 % wt. % NaMBT (relating to polymer) A 5 I beaker with magnetic stirrer, pH meter and thermometer was initially charged with 702.0 g of a 35% aqueous solution of Na-acrylate, and then the following were added successively: 1500 g of distilled water, 1071.7 g of acrylamide (52 % by weight in water, bio acrylamide) 10.5 g of a 5% aqueous solution of diethylenetriamine- pentaacetic acid, pentasodium salt, 2.8 g of a 1 wt. % aqueous solution of sodium hypophoshite hydrate, and 4 g of a 50 % aqueous solution of the stabilizer sodium 2- mercaptobenzothiazole (NaMBT). After adjustment to pH 6.4 with a 20 % by weight solution of sulfuric acid and addition of the rest of the water to attain the desired monomer concentration of 23 % by weight (total amount of water 1687.3 g minus the amount of water already added, minus the amount of acid required), the monomer solution was adjusted to the initiation temperature of 0°C. The solution was transferred to Dewar vessel, the temperature sensor for the temperature recording was inserted, and the flask was purged with nitrogen for 45 minutes. The polymerization was initiated with 21 g of a 10% aqueous solution of the water-soluble azo initiator 2,2'-azobis(2-methylpropionamidine) dihydrochloride (Wako V-50; 10h 12 in water 56°C), 1.75 g of a 1 % t-BHPO solution and 1.05 g of a 1 % sodium sulfite solution. With the onset of the polymerization, the temperature rose to 60°C within about 50 min. A solid polymer gel was obtained.

After the polymerization, the gel was incubated for 4 hours at 60 °C and the gel block was comminuted with the aid of a meat grinder. The comminuted aqueous

polyacrylamide gel was kept for further testing without drying.

Copolymer 4:

Copolymer comprising 69.4 wt. % (75.0 mole %) of acrylamide and 30.6 wt. % (25 mole % ) of sodium acrylate, stabilized with 0.05 wt. % MA-HPMP (relating to polymer)

1 ,2,2,6,6-pentamethyl-4-piperidinol methacrylate (MA-HPMP)

A 5 I beaker with magnetic stirrer, pH meter and thermometer was initially charged with 703.8 g of a 35% aqueous solution of Na-Acrylate, and then the following were added successively: 1500 g of distilled water, 1073.6 g of acrylamide (52 % by weight in water, bio acrylamide), 10.5 g of a 5% aqueous solution of diethylenetriamine- pentaacetic acid, pentasodium salt, 2.8 g of a 1 wt. % aqueous solution of sodium hypophoshite hydrate, and 4.0 g of a 10 % methanolic solution of the polymerizable stabilizer (MA-HPMP).

After adjustment to pH 6.4 with a 20 % by weight solution of sulfuric acid and addition of the rest of the water to attain the desired monomer concentration of 23 % by weight (total amount of water 1683.6 g minus the amount of water already added, minus the amount of acid required), the monomer solution was adjusted to the initiation temperature of 0°C. The solution was transferred to Dewar vessel, the temperature sensor for the temperature recording was inserted, and the flask was purged with nitrogen for 45 minutes. The polymerization was initiated with 21 g of a 10% aqueous solution of the water-soluble azo initiator 2,2'-azobis(2-methylpropionamidine) dihydrochloride (Wako V-50; 10h 12 in water 56°C), 1 .75 g of a 1 % t-BHPO solution and 1.05 g of a 1 % sodium sulfite solution. With the onset of the polymerization, the temperature rose to 60°C within about 50 min. A solid polymer gel was obtained.

polyacrylamide gel was kept for further testing without drying.

Copolymer 5:

Copolymer comprising 69.4 wt. % (75.0 mole %) of acrylamide and 30.6 wt. % (25 mole % ) of sodium acrylate A 5 I beaker with magnetic stirrer, pH meter and thermometer was initially charged with 703.8 g of a 35% aqueous solution of Na-Acrylate, and then the following were added successively: 1500 g of distilled water, 1 1 17.3 g of acrylamide (52 % by weight in water, Cu-catalysis), 10.5 g of a 5% aqueous solution of diethylenetriamine-pentaacetic acid, pentasodium salt and 7 g of a 0.1 wt. % aqueous solution of sodium hypophoshite hydrate.

After adjustment to pH 6.4 with a 20 % by weight solution of sulfuric acid and addition of the rest of the water to attain the desired monomer concentration of 23 % by weight (total amount of water 1668.4 g minus the amount of water already added, minus the amount of acid required), the monomer solution was adjusted to the initiation temperature of 0°C. The solution was transferred to Dewar vessel, the temperature sensor for the temperature recording was inserted, and the flask was purged with nitrogen for 45 minutes. The polymerization was initiated with 21 g of a 10% aqueous solution of the water-soluble azo initiator 2,2'-azobis(2-methylpropionamidine) dihydrochloride (Wako V-50; 10h 12 in water 56°C), 1 .75 g of a 1 % t-BHPO solution and 1.05 g of a 1 % sodium sulfite solution. With the onset of the polymerization, the temperature rose to 60°C within about 50 min. A solid polymer gel was obtained. After the polymerization, the gel was incubated for 3 hours at 60 °C and the gel block was comminuted with the aid of a meat grinder. The comminuted aqueous

polyacrylamide gel was kept for further testing without drying.

Storage of the polyacrylamide gels at various temperatures:

Test samples of the comminuted aqueous polyacrylamide gels to be tested were put into a vacuum bag, the vacuum bag purged with nitrogen for 15 min, the bags evacuated and heat-sealed. The bags filled with aqueous polyacrylamide gel were stored in a hot-air cabinet for up to 7 days at pre-defined temperatures.

With the stored gels, the following tests were performed: Viscosity in aqueous solution

Measurements were performed in "pH 7 buffer": For 10 I of pH 7 buffer fully dissolve 583.3 ± 0.1 g sodium chloride, 161 .3 ± 0.1 g disodium hydrogenphosphate · 12 H2O and 7.80 ± 0.01 g sodium dihydrogenphosphate · 2 H2O in 10 I dist. or deionized water. A 5000 ppm polymer solution was obtained by dissolving the appropriate amount of polymer gel in pH 7 buffer until being fully dissolved. Viscosity measurements were performed at a Brookfield RS rheometer with single gap geometry.

Filtration ratio

Determination of MPFR (Millipore Filtration Ratio)

The filterability of the polymer solutions was characterized using the MPFR value (Millipore filtration ratio). The MPFR value characterizes the deviation of a polymer solution from ideal filtration characteristics, i.e. when there is no reduction of the filtration rate with increasing filtration. Such a reduction of the filtration rate may result from the blockage of the filter in course of filtration.

To determine the MPFR values, about 200 g of the relevant polyacrylamide solution having a concentration of 1000 ppm were filtered through a polycarbonate filter have a pore size of 5 μηη at a pressure of 2 bar and the amount of filtrate was recorded as a function of time.

The MPFR value was calculated by the following formula

MPFR = (tl80 g - tl60 g) / (t.80 g " t.60 g).

T_X g is the time at which the amount solution specified passed the filter, i.e. tieo_g is the time at which 180 g of the polyacrylamide solution passed the filter. According to API RP 63 ("Recommended Practices for Evaluation of Polymers Used in Enhanced Oil Recovery Operations", American Petroleum Institute), values of less than 1 .3 are acceptable.

Gel fraction

A 5000 ppm polymer solution in pH 7 buffer is diluted to 1000 ppm with pH 7 buffer. The gel fraction is given as ml. of gel residue on the sieve when 250 g 1000 ppm polymer solution are filtered over 200 μηη sieve and consequently washed with 2 I of tab water.

The test results for copolymer 1 are summarized in table 1 , the results for copolymers 2 to 5 are summarized in table 2.

Table 1 : Results of gel storage tests. Viscosity measured at 5000 ppm in pH 7 buffer at RT, 50 s-1 . MPFR measured at 1000 ppm in pH 7 buffer, bar.

Table 2: Results of gel storage tests. Viscosity measured at 5000 ppm in pH 7 buffer at RT, 100 s-1 . MPFR measured at 1000 ppm in pH 7 buffer, 2 bar. (* in brackets: standard deviation for viscosity, mean value out of three independent samples, ** in brackets: standard deviation for viscosity mean value out of two independent samples)

Table 3: Results of gel storage tests. Viscosity measured at 5000 ppm in pH 7 buffer at RT, 100 s-1 . MPFR measured at 1000 ppm in pH 7 buffer, 2 bar. (* in brackets: standard deviation for viscosity, mean value out of three independent samples)

The tests with copolymer 1 demonstrate that it is possible to store an unstabilized aqueous polyacrylamide gel (acrylamide made by Cu catalysis) at 30°C for 14 days without significant deterioration of its properties. At 60°C one day storage is possible. After 3 days already some deterioration is observed. The 7 days and 14 days data indicate a very pronounced increase on insoluble fraction, indicating crosslinking. The 90°C data show that there is a pronounced deterioration already after 1 day.

Summarizing the results, the unstabilized aqueous polyacrylamide gel comprising copolymer 1 may be transported at 30°C without problems, at 60°C quick transports with transporting times of less than 3 days seems possible, while a transport at 90°C seems to be not possible.

The aqueous gel comprising copolymer 2 was synthesized with another recipe thereby limiting the temperature increase to temperature to 60°C. Furthermore, bio acrylamide was used. It also was unstabilized. The gel could be stored at 50°C and 60°C for 7 days without deterioration of its properties. At 70°C after 7 days a slight increase in the MPFR and a decrease in viscosity is observed. Copolymer 3 was synthesized in the same manner as copolymer 2, except that the stabilizer NaMBT was added. Adding the stabilizer yields an increased stability also at 70°C and the same holds true for MA-HPMP (Copolymer 4). In both cases the drop in viscosity after 7days as compared to copolymer 2 may be avoided. Finally, the tests with copolymer 5 demonstrate the advantages of using bio acrylamide as compared to acrylamide made by copper catalysis for the process according to the present invention. The tests at 50°C show that the viscosity decreases upon storing but the gel remains soluble and no gel fractions are formed. However, storing the gels at 60°C and at 70°C for 4 days yielded gel which no longer were soluble. So, the gels seemed to have been crosslinked.

Table 3 demonstrates that aqueous polyacrylamide gels stabilized with NaMBT may also be stored at 80°C for at least 7 days. The viscosity remained more or less the same (with the errors of measurement) for 21 days. Also, the MPFR remained stable for about 7 days and then began to increase slightly. However, even after 21 days it was slightly below the value of 1.3.

Test Series 2 Further tests were conducted with another type of polyacrylamide copolymer, namely a copolymer comprising about 33.3 wt. % of acrylamide and 66.7 wt. % of sodium acrylate. For copolymer 6, the monomer concentration was 35 % by weight and the temperature rose to 86°C in course of polymerization. No stabilizer was used.

For copolymer 7, the monomer concentration was 28 % by weight and the temperature rose to 73°C in course of polymerization. MA-HPMP was used as stabilizer.

Copolymer 6:

Copolymer comprising 33.3 wt. % (39.8 mole %) of acrylamide and 66.7 wt. % (60.2 mole % ) of sodium acrylate

A 1 I beaker with magnetic stirrer, pH meter and thermometer was initially charged with 266.8 g of a 35% aqueous solution of Na-Acrylate, and then the following were added successively: 35.1 g of distilled water, 89.7 g of acrylamide (52 % by weight in water, bio acrylamide), 2.04 g of 4,4'-Azobis(4-cyanovaleric acid) solution (4 % by weight in 5 % sodium hydroxide solution) and 1.2 g of a 5% aqueous solution of

diethylenetriamine-pentaacetic acid, pentasodium salt.

After adjustment to pH 6.7 with a 20 % by weight solution of sulfuric acid and addition of the rest of the water to attain the desired monomer concentration of 35 % by weight (total amount of water 40 g minus the amount of water already added, minus the amount of base required), the monomer solution was adjusted to the initiation temperature of 0°C. The solution was transferred to Dewar vessel, the temperature sensor for the temperature recording was inserted, and the flask was purged with nitrogen for 45 minutes. The polymerization was initiated 0.12 g of a 1 % t-BHPO solution and 0.24 g of a 1 % sodium sulfite solution. With the onset of the

polymerization, the temperature rose to 86°C within about 60 min. A solid polymer gel was obtained. After the polymerization, parts of the gel was comminuted with the aid of a meat grinder. The other part of the gel was incubated at 90 °C vacuum sealed under nitrogen for 24 hours and then comminuted with the aid of a meat grinder.

Copolymer 7:

Copolymer comprising 33.3 wt. % (39.8 mole %) of acrylamide and 66.7 wt. % (60.2 mole % ) of sodium acrylate, stabilized with 0.05 wt. % MA-HPMP (relating to polymer)

A 5 I beaker with magnetic stirrer, pH meter and thermometer was initially charged with 1867.6 g of a 35% aqueous solution of Na-Acrylate, and then the following were added successively: 900 g of distilled water, 626.6 g of acrylamide (52 % by weight in water, bio acrylamide) 4.9 g of a 10 % by weight methanolic MA-HPMP solution and 10.5 g of a 5% aqueous solution of diethylenetriamine-pentaacetic acid, pentasodium salt.

After adjustment to pH 6.9 with a 10 % by weight solution of sodium hydroxide and addition of the rest of the water to attain the desired monomer concentration of 28 % by weight (total amount of water 968.3 g minus the amount of water already added, minus the amount of base required), the monomer solution was adjusted to the initiation temperature of 0°C. The solution was transferred to Dewar vessel, the temperature sensor for the temperature recording was inserted, and the flask was purged with nitrogen for 45 minutes. The polymerization was initiated with 21 g of a 10% aqueous solution of the water-soluble azo initiator 2,2'-azobis[2-(2-imidazolin-2- yl)propane]dihydrochloride (Wako VA-044; 10h 12 in water 44°C), 1.05 g of a 1 % t- BHPO solution and 2.1 g of a 1 % sodium sulfite solution. With the onset of the polymerization, the temperature rose to 73°C within about 60 min. A solid polymer gel was obtained.

After the polymerization, the gel was comminuted with the aid of a meat grinder. A fraction of the gel granules obtained were dried in a fluidized bed drier at 55°C for two hours, another fraction was kept as aqueous polyacrylamide gel for further testing. Tests

The tests oft he polyacrylamide gels were performed in the same manner as described above. The data are summarized in table 4.

Table 4: Results of gel storage tests. Viscosity measured at 5000 ppm in 0.1 M NaOH at RT, 300 s-1 . Gel fraction: ml gel in 5000 ppm solution filtered over 190 pm sieve. (^* in brackets: standard deviation for viscosity, mean value out of three independent samples). Powder sample is generated from gel as described above for comparative purposes.

Storing the unstabilized copolymer 6 only 1 day at 90°C yields a significant decrease in viscosity and very pronounced amounts of gel are formed. Such a product were no longer suitable for oilfield uses and other uses. Copolymer 7 synthesized with an adapted recipe and stabilized with NaHPMP could be stored for 24 h without any decrease in viscosity and without any gel formation.

Claims

Claims:

Process for producing an aqueous polyacrylamide solution by polymerizing an aqueous solution comprising at least acrylamide thereby obtaining an aqueous polyacrylamide gel and dissolving said aqueous polyacrylamide gel in water, characterized in that the process comprises at least the following steps:

[1 ] Radically polymerizing an aqueous monomer in the presence of suitable

• the aqueous monomer solution comprises at least water and 5 % to 45 % by weight -relating to the total of all components of the aqueous monomer solution- of water-soluble, monoethylenically unsaturated monomers at a location A, wherein said water-soluble, monoethylenically unsaturated monomers comprise at least acrylamide, and the temperature ΤΊ of the aqueous monomer solution before onset of polymerization does not exceed 30°C, and

• the polymerization is performed in a transportable polymerization unit

having a volume of 1 m³ to 40 m³,

[2] transporting the transportable polymerization unit filled with the aqueous

[3] removing the aqueous polyacrylamide gel from the transportable

polymerization unit at the location B, and

[4] dissolving the aqueous polyacrylamide gel in an aqueous liquid at the location B, thereby obtaining an aqueous polyacrylamide solution.

Process according to claim 1 , wherein the transport time is from 1 day to 14 days.

Process according to claim 1 or claim 2, wherein the process comprises additionally at least one of the three measures (a), (b) and (c) in order to ensure transport of the aqueous polyacrylamide gel without gel damage, that is to say

(a) using an aqueous solution of acrylamide for step [1], wherein the acrylamide solution has been obtained by hydrolyzing acrylonitrile in water in the presence of a biocatalyst capable of converting acrylonitrile to acrylamide,

(b) limiting the temperature T₂ to 50°C to 70°C, and

(c) adding at least one stabilizer for the prevention of polymer degradation to the aqueous monomer solution, wherein the stabilizer is selected from the group of o non-polymerizable stabilizers selected from the group of sulfur compounds, sterically hindered amines, N-oxides, inorganic compounds comprising at least two nitrogen atoms, nitroso compounds, aromatic hydroxyl compounds and ketones, wherein the amount of such non-polymerizable stabilizers is from 0.1 % to 2.0 % by weight relating to the total of all monomers in the aqueous monomer solution, and

o polymerizable stabilizers comprising at least a monoethylenically

unsaturated group and a stabilizing moiety capable for the prevention of polymer degradation, wherein the amount of such polymerizable stabilizers is from 0.01 % to 2.0 % by weight, relating to the total of all monomers in the aqueous monomer solution.

4. Process according to claim 3, wherein at least measure (a) is selected.

5. Process according to claim 3, wherein at least measure (b) is selected.

6. Process according to claim 3, wherein at least measure (c) is selected.

7. Process according to claim 3, wherein at least measures (a) and (c) are selected. 8. Process according to claim 3, wherein measures (a), (b) and (c) are selected.

9. Process according to claims 7 and 8, wherein the transport time is from 3 days to 14 days. 10. Process according to claims 7 and 8, wherein the transport time is from 3 days to 7 days.

1 1 . Process according to any of claims 3 to 10, wherein the stabilizer is at least one non-polymerizable, sulfur containing stabilizer selected from the group of thiols, thiophenols, thioethers, sulfur containing heterocyclic compounds, disulfides, thioureas, thiourethanes or thiocarbamates.

Process according to any of claims 3 to 10, wherein the stabilizer is at least one non-polymerizable, sulfur containing stabilizer selected from the group Ν,Ν'- dimethylthiourea, N,N'-diethylthiourea, Ν,Ν'-diphenylthiourea, thiocyanates, tetramethylthiuram disulfide, 2-mercaptobenzothiazole or salts thereof, 2- mercaptobenzimidazole or salts thereof, sodium dimethyldithiocarbamate, 2,2'- dithiobis(benzothiazole), and 4,4'-thiobis(6-t-butyl-m-cresol).

Process according to any of claims 3 to 10, wherein the stabilizer is a non- polymerizable stabilizer which is 2-mercaptobenzothiazole or a salt thereof.

14. Process according to any of claims 3 to 13, wherein the amount of non- polymerizable stabilizers is from 0.15 % to 1.0 % by weight, relating to the sum of all monomers in the aqueous monomer solution. 15. Process according to any of claims 3 to 10, wherein the stabilizer is at least one polymerizable stabilizer comprising a monoethylenically unsaturated group and at least one 2,2,6,6-pentamethyl-piperidin-4-yl group.

16. Process according to any of claims 3 to 10, wherein the stabilizer is at least one polymerizable stabilizer selected from the group of

wherein R¹⁰ is H, Ci to C₄ alkyl, and R¹¹ is selected from H or an alkali metal ion.

17. Process according to any of claims 3 to 10, wherein the stabilizer is a

polymerizable stabilizer which is a (meth)acrylic acid ester of 1 ,2,2,6,6- pentamethyl-4-piperidinol (VIII)

wherein R¹² is H or methyl.

18. Process according to any of claims 3 to 10 and 15 to 17, wherein the amount of polymerizable stabilizers is from 0.02 % to 1.0 % by weight, relating to the sum of all monomers in the aqueous monomer solution.

19. Process according to any of claims 1 to 18, wherein location A is a local hub which provides a plurality of different locations B with aqueous polyacrylamide gels.

20. Process according to any of claims 1 to 18, wherein location A is over a

subterranean, oil-bearing formation or in between different, subterranean, oil- bearing formations and location(s) B are at oil wells. 21 . Process according to any of claims 1 to 18, wherein location A is located in a

mining area, and location(s) B are at tailings ponds.

22. Process according to any of claims 1 to 21 , wherein the distance between

locations A and B is from 1 km to 3000 km.

23. Process according any of claims 3 to 22, wherein measure (a) comprises

manufacturing an aqueous acrylamide solution by hydrolyzing acrylonitrile in water in the presence of a biocatalyst capable of converting acrylonitrile to acrylamide in an additional step [0] carried out at location A.

24. Process according to claim 23, wherein step [0] is performed in a relocatable

bioconversion unit.

25. Process according to claim 24, wherein the relocatable bioconversion unit

comprises a double-walled reaction vessel having a volume from 10 m³ to 150 m³, means for mixing the reaction mixture and means for controlling the temperature of the reaction mixture.

26. Process according to claim 25, wherein the relocatable bioconversion unit

comprises a frame, a double-walled reaction vessel mounted into the frame having a volume from 10 m³ to 150 m³, and an external temperature control cycle comprising at least a pump and a temperature control unit, wherein the reaction mixture is circulated by means of a pump from the reaction vessel into the temperature control unit and back into the reaction vessel, thereby simultaneously temperature control and mixing the reaction mixture.

27. Process according to claim 26, wherein the amount of reaction mixture cycled per hour through the temperature control cycle is from 100 % to 1000 % of the total volume of the reaction mixture in the bioconversion unit.

28. Process according to any of claims 1 to 27, wherein at least one redox initiator and at least one azo initiator is used for step [1 ].

29. Process according to any of claims 1 to 28, wherein the aqueous monomer

solution before the onset of polymerization has a temperature ΤΊ not exceeding 5°C.

30. Process according to any of claims 1 to 28, wherein the aqueous monomer

solution before the onset of polymerization has a temperature ΤΊ from -15°C to +

5°C and T₂ is from 50°C to 70°C.

Process according to claim 30, wherein the monomer concentration is from 8 to 24.9 % by wt.

Process according to any of claims 1 to 31 , wherein the transportable

polymerization unit is a transportable polymerization unit P1 comprising a cylindrical upper part (30) having a length of 4 m to 6 m and a diameter from 1 .5 m to 2.5 m, a conical part (31 ) at its lower end having a conus angle from 15° to 90°, feeds for the aqueous monomer solution, a bottom opening (32) having a diameter from 0.2 to 0.8 m for removing the polyacrylamide gel, and means (33) allowing to deploy the unit P1 in a vertical manner.

Process according to claim 25, wherein the volume of the transportable

polymerization unit P1 is from 20 m³ to 30 m³.

Process according to claim 32 or 33, wherein for transporting the transportable polymerization unit P1 in course of step [2], the polymerization unit P1 is tilted to a horizontal position and it is transported by truck.

Process according to claim 34, wherein the truck comprises means for loading the polymerization unit P1 onto the truck in horizontal position and for unloading and deploying the polymerization unit in vertical position and the transportable polymerization unit is loaded on the truck and unloaded from the truck by such means.

36. Process according to claim 34, wherein means for loading the polymerization unit P1 onto the truck in horizontal position and for unloading and deploying the polymerization unit in vertical position are provided for at locations A and B and the transportable polymerization unit P1 is loaded on the truck and unloaded from the truck by such means.

37. Process according to any of claims 32 to 36, wherein the aqueous polyacrylamide gel is removed from the transportable polymerization unit in course of step [3] by applying pressure onto the gel and pressing it through the bottom opening.

38. Process according to claim 37, wherein pressure onto the gel is applied by means of gases, selected from the group of air, nitrogen, or argon and/or by means of aqueous fluids.

Process according to any of claims 1 to 38, wherein step [4] comprises an additional step of comminuting the aqueous polyacrylamide gel before dissolution.

Process according to claim 39, wherein comminuting the aqueous polyacrylamide gel is carried out by conveying the aqueous polyacrylamide gel through at least one comminuting unit thereby yielding pieces of aqueous polyacrylamide gel.

Process according to claim 40, wherein the aqueous polyacrylamide gel is conveyed through the at least one comminuting unit together with an aqueous liquid thereby yielding a mixture of pieces of aqueous polyacrylamide gel in an aqueous polyacrylamide solution.

42. Process according to claims 40 or 41 , wherein the comminution unit comprises means for comminuting aqueous polymer gels selected from static cutting devices, moving cutting devices, perforated plates, static mixers, water-jet cutting devices or combinations thereof.

43. Process according to claims 40 or 41 , wherein at least one of the comminuting units is a water-jet cutting device. 44. Process according to any of claims 39 to 43, wherein the comminution unit is

connected with the bottom opening of the polymerization unit P1 and aqueous polyacrylamide gel is conveyed from the polymerization unit through the comminution unit.

Process according to any of claims 1 to 44, wherein dissolution in course of step [5] is performed in a dissolution unit comprising at least a dissolution vessel and means for mixing the aqueous polyacrylamide gel with the aqueous liquid. Process according to claim 45, wherein the dissolution unit is a relocatable dissolution unit.

Process according to claim 46, wherein the relocatable dissolution unit comprises at least a dissolution vessel, at least one stirrer, means for filling the dissolution unit with aqueous liquid and pieces of aqueous polyacrylamide gel and means for removing aqueous polyacrylamide solution.

Process according to claims 46 or 47, wherein at least two relocatable dissolution units are connected in series.

49. Process according to claim 46, wherein the dissolution unit is fixed on a truck or a trailer.

50. Process according to any of claims 1 to 49, wherein the polyacrylamide is a

copolymer comprising at least 20 % by weight of acrylamide and at least one further water-soluble, monoethylenically unsaturated comonomer. 51 . Process according to claim 50, wherein the at least one further water-soluble, monoethylenically unsaturated comonomer is selected from the group of acrylic acid or salts thereof, ATBS or salts thereof, associative monomers, or DMA3Q.

Use of aqueous polyacrylamide solutions for mining applications, oilfield applications, water treatment, waste water cleanup, paper making or agricultural applications, wherein the aqueous polyacrylamide solution is prepared according to the process according to any of claims 1 to 51 .

Use of aqueous polyacrylamide solutions for producing mineral oil from

underground mineral oil deposits by injecting an aqueous fluid comprising at least an aqueous polyacrylamide solution into a mineral oil deposit through at least one injection well and withdrawing crude oil from the deposit through at least one production well, wherein the aqueous polyacrylamide solution is prepared according to the process according to any of claims 1 to 51 .

Use of aqueous polyacrylamide solutions for fracturing subterranean formations by injecting an aqueous fracturing fluid comprising at least water, proppants and a friction reducer through a wellbore into a subterranean formation at a pressure sufficient to flow into the formation and to initiate or extend fractures in the formation, wherein the friction reducer comprises an aqueous polyacrylamide solution prepared by the process according to any of claims 1 to 51 .

55. Use of aqueous polyacrylamide solutions for mining, mineral processing and/or metallurgy comprising the use for solid liquid separation, for tailings disposal, for polymer modified tailings deposition, for tailings management, as density and/or rheology modifier, as agglomeration aid, as binder and/or for material handling, wherein the aqueous polyacrylamide solution is prepared according to the process according to any of claims 1 to 51.