WO2005063929A2 - Systems, methods, and catalysts for producing a crude product - Google Patents
Systems, methods, and catalysts for producing a crude product Download PDFInfo
- Publication number
- WO2005063929A2 WO2005063929A2 PCT/US2004/042399 US2004042399W WO2005063929A2 WO 2005063929 A2 WO2005063929 A2 WO 2005063929A2 US 2004042399 W US2004042399 W US 2004042399W WO 2005063929 A2 WO2005063929 A2 WO 2005063929A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- crude product
- crude
- grams
- crude feed
- catalyst
- Prior art date
Abstract
Description
Claims