US20100058986A1 - System and method for plasma plating - Google Patents
System and method for plasma plating Download PDFInfo
- Publication number
- US20100058986A1 US20100058986A1 US11/759,606 US75960607A US2010058986A1 US 20100058986 A1 US20100058986 A1 US 20100058986A1 US 75960607 A US75960607 A US 75960607A US 2010058986 A1 US2010058986 A1 US 2010058986A1
- Authority
- US
- United States
- Prior art keywords
- vacuum chamber
- filament
- substrate
- radio frequency
- signal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This patent application is a divisional of U.S. patent application Ser. No. 09/427,775, filed Oct. 26, 1999, which is hereby incorporated by reference herein in its entirety.
- This invention relates in general to the field of deposition to technology for plating and coating materials and, more particularly, to a system and method for plasma plating.
- Various deposition technologies exist for plating and coating materials. These various technologies include, for example, vacuum deposition or physical vapor deposition (“PVD”), chemical vapor deposition (“CVD”), sputtering, and ion plating. All of these deposition technologies suffer from disadvantages such as poor deposition layer adhesion, high cost, generation of environmentally wasteful products that are expensive and cumbersome to dispose, damage to the substrate, elevated substrate temperatures, non-uniform deposition layers, inefficient use of expensive depositants, and inconsistent application of deposition layers are among some of the disadvantages suffered by one or more of the prior deposition technologies.
- From the foregoing it may be appreciated that a need has arisen for a system and method for plasma plating that generates a controllable and repeatable deposition layer on a substrate. In accordance with the present invention, a system and method for plasma plating are provided that substantially eliminate one or more of the disadvantages and problems outlined above.
- According to an aspect of the present invention, a method for plasma plating is provided to generate a deposition layer on a substrate. The method for plasma plating includes positioning a substrate within a vacuum chamber, positioning a depositant in a filament within the vacuum chamber, reducing the pressure in the vacuum chamber to a level at or below 4 milliTorr, and introducing a gas into the vacuum chamber at a rate to raise the pressure in the vacuum chamber to a level at or between 0.1 milliTorr and 4 milliTorr. In other embodiments, the gas is not required to be introduced. The method also includes applying a DC signal to the substrate at a voltage amplitude at or between 1 volt to 5000 volts, applying a radio frequency signal to the substrate at a power level at or between 1 watt and 50 watts, and heating the depositant to a temperature at or above the melting point of the depositant to generate a plasma in the vacuum chamber. The plasma will preferably include both positively charged gas and depositant ions that will be attracted to the substrate, which will, preferably, be provided at a negative potential if the DC signal is provided at a negative polarity.
- According to another aspect of the present invention, an system for plasma plating is provided that generates a deposition layer on a substrate. The system for plasma plating includes a vacuum chamber at a pressure that extends from 0.1 milliTorr to 4 milliTorr, a filament with an associated depositant located on or in the filament, a platform positioned within the vacuum chamber, a substrate positioned at or on the platform, a DC power supply generating a DC signal at a voltage in a range that extends from 1 volt to 5000 volts, a radio frequency transmitter generating a radio frequency signal at a power level defined by a range that extends from 1 watt to 50 watts, an electrically conductive path that electrically couples the DC signal and the radio frequency signal to the substrate, and a filament power control electrically coupled to the filament and generating a current through the filament at an amplitude to generate heat in the filament to melt the depositant.
- The present invention provides a profusion of technical advantages that include the capability to controllably, repeatably, and reliably plate a substrate using plasma plating to develop a deposition layer with a high adherence to the substrate.
- Another technical advantage of the present invention includes the capability to control the thickness of the deposition layer to around 500 Angstroms, while developing a more uniform deposition layer thickness that is repeatable from one application to the next.
- Another technical advantage of the present invention includes the capability to efficiently use depositants to minimize the consumption of depositants, which often are expensive precious metals such as gold and even platinum. These efficiencies are achieve through the proper placement of filaments and the use of proper operational parameters. This significantly reduces overall costs.
- Yet another technical advantage of the present invention includes the capability to perform plasma plating without heating up the substrate to extreme temperatures that often damage the substrate through molecular and/or metallurgical changes. This ensures that a deposition layer can be developed without the danger of possibly unknowingly damaging a substrate. This is especially significant when the failure of a substrate in its system or intended use results in a safety hazard. This also provides the significant advantage of allowing the substrate to be handled and used immediately after the plasma plating process.
- Still yet another technical advantage of the present invention includes the capability to perform plasma plating without bombarding the substrate with high energy ions, like ion plating, which could damage or alter the substrate through molecular, metallurgical, and possibly chemical changes. This is because plasma plating is believed to be achieved at medium energy levels, such as at a medium energy level on the average of between 10 eV and 90 eV, such that good adhesion is achieved but no metallurgical or chemical changes occur to the substrate due to the relatively shallow depth of embedment of the deposition layer.
- Still yet another technical advantage includes the capability plate a substrate with a deposition layer with a thickness that is small enough so as not to change the functional shape of the substrate, such as a bolt, a nut, a fastener, and other components with strict tolerances. The present invention will also work in the presence of an oxidation layer.
- Yet another technical advantage includes the capability to plate a substrate with a deposition layer without generating waste by products or any environmentally hazardous waste. This is significant.
- Other technical advantages are readily apparent to one skilled in the art from the following figures, description, and claims.
- For a more complete understanding of the present invention and the advantages thereof, reference is now made to the following brief description, taken in connection with the accompanying drawings and detailed description, wherein like reference numerals represent like parts, in which:
-
FIG. 1 is a schematic diagram that illustrates a system for plasma plating that can be used to plate materials, according to an embodiment of the present invention; -
FIG. 2 is a top view of a vacuum chamber of a system for plasma plating that illustrates one embodiment of a platform implemented as a turntable; -
FIG. 3 is a side view that illustrates the formation and dispersion of a plasma around a filament to plasma plate a substrate according to an embodiment of the present invention; -
FIG. 4 is a sectional view that illustrates a deposition layer that includes a base layer, a transition layer, and a working layer; -
FIG. 5 is a flowchart that illustrates a method for plasma plating according to an embodiment of the present invention; and -
FIG. 6 is a flowchart that illustrates a method for backsputtering using the system of the present invention, according to an embodiment of the present invention. - It should be understood at the outset that although an exemplary implementation of the present invention is illustrated below, the present invention may be implemented using any number of techniques, whether currently known or in existence. The present invention should in no way be limited to the exemplary implementations, drawings, and techniques illustrated below, including the exemplary design and implementation illustrated and described herein.
-
FIG. 1 is a schematic diagram that illustrates asystem 10 for plasma plating that can be used to plate any of a variety of materials, according to an embodiment of the present invention. Thesystem 10 includes various equipment used to support the plasma plating of asubstrate 12 within avacuum chamber 14. Once appropriate operating parameters and conditions are achieved, a depositant provided in afilament 16 and afilament 18 may be evaporated or vaporized to form a plasma. The plasma will contain, generally, positively charged ions from the depositant and will be attracted to thesubstrate 12 where they will form a deposition layer. The plasma may be thought of as a cloud of ions that surround or are located near thesubstrate 12. The plasma will generally develop a dark region, near the closest surface of thesubstrate 12 from thefilament 12 and thefilament 18, that provides acceleration of the positive ions into thesubstrate 12. - The
filament 12 and thefilament 14 reside within thevacuum chamber 14 along with aplatform 20, which supports thesubstrate 12. Adrive assembly 22 is shown coupled between adrive motor 24 and a main shaft of theplatform 20 within thevacuum chamber 14. In the embodiment shown inFIG. 1 , theplatform 20 is provided as a turntable that rotates within thevacuum chamber 14. Thedrive assembly 22 mechanically links the rotational motion of thedrive motor 24 with the main shaft of theplatform 20 to impart rotation to theplatform 20. The rotation of the main shaft of theplatform 20 is enhanced through various support bearings such as a base plate bearing 28 and a platform bearing 30. - As is illustrated, the
vacuum chamber 14 resides or is sealed on abase plate 32. Thevacuum chamber 14 may be provided using virtually any material that provides the appropriate mechanical characteristics to withstand an internal vacuum and an external pressure, such as atmospheric pressure. For example, thevacuum chamber 14 may be provided as a metal chamber or as a glass bell. In an alternative embodiment, thebase plate 32 serves as theplatform 20 to support thesubstrate 12. Thebase plate 32 may be thought of as part of thevacuum chamber 14. - The
base plate 32 also provides mechanical support for thesystem 10 while allowing various devices to feed through from its bottom surface to its top surface within thevacuum chamber 14. For example, thefilament 16 and thefilament 18 receive power from a filamentpower control module 34. It should be noted that although two filamentpower control modules 34 are shown inFIG. 1 , preferably, these two modules are implemented as one module. In order to provide power to thefilament 16 and thefilament 18, electrical leads must feed through thebase plate 32 as illustrated inFIG. 1 . Similarly, thedrive motor 24 must also penetrate or feed through thebase plate 32 to provide mechanical action to thedrive assembly 22 so that theplatform 20 may be rotated. The electrical feed through 26, described more fully below, also feeds through thebase plate 32 and provides an electrical conductive path between theplatform 20 and various signal generators, also described more fully below. In a preferred embodiment, the electrical feed through 26 is provided as a commutator that contacts the bottom surface of theplatform 20, in the embodiment where theplatform 20 is implemented as a turntable. The electrical feed through 26 may be implemented as a commutator and may be implemented as a metal brush which can contact the bottom surface of theplatform 20 and maintain an electrical contact even if theplatform 20 rotates. - The filament
power control module 34 provides an electric current to thefilament 16 and thefilament 18. In one embodiment, the filamentpower control module 34 can provide current to thefilament 16 for a particular duration, and then provide current to thefilament 18 during a second duration. Depending upon how the filaments are configured, the filamentpower control module 34 may provide current to both thefilament 16 and thefilament 18 at the same time or during separate intervals. This flexibility allows more than one particular depositant material to be plasma plated onto thesubstrate 12 at different times. The filamentpower control module 34 preferably provides alternating current to the filaments, but may provide a current using any known method of generating current. In a preferred embodiment, the filamentpower control module 34 provides current at an amplitude or magnitude that is sufficient to generate enough heat in thefilament 16 to evaporate or vaporize the depositant. - In order to ensure even heating of the depositant, which will be provided at or in the
filament 16 or thefilament 18, the current provided by thefilament control module 34 will preferably be provided using incremental staging so that a more even heat distribution will occur in the depositant that is being melted within thevacuum chamber 14. - In a preferred embodiment, the
platform 20 is implemented as a turntable and rotates using the mechanical linkage as described above. Aspeed control module 36, as shown inFIG. 1 , may be provided to control the speed of the rotation of theplatform 20. Preferably, the rotation of theplatform 20 occurs at a rate from five revolutions per minutes to 30 revolutions per minute. It is believed that an optimal rotational rate of theplatform 20 for plasma plating is provided at a rotational rate of 12 revolutions per minute to 15 revolutions per minute. The advantages of rotating theplatform 20 are that thesubstrate 12 can be more evenly plated or coated. This is especially true when multiple substrates are provided on the surface of theplatform 20. This allows each one of the multiple substrates to be similarly positioned, on average, within thevacuum chamber 14 during the plasma plating process. - In other embodiments, the
platform 20 may be provided at virtually any desired angle or inclination. For example, theplatform 20 may be provided as a flat surface, a horizontal surface, a vertical surface, an inclined surface, a curved surface, a curvilinear surface, a helical surface, or as part of the vacuum chamber such as a support structure provided within the vacuum chamber. As mentioned previously, theplatform 20 may be stationary or rotate. In an alternative embodiment, the platform includes rollers that may be used to rotate one or more substrates. - The
platform 20, in a preferred embodiment, provides or includes an electrically conductive path to provide a path between the electrical feed through 26 and thesubstrate 12. In one embodiment,platform 20 is provided as a metal or electrically conductive material such that an electrically conductive path is provided at any location on theplatform 20 between the electrical feed through 26 and thesubstrate 12. In such as a case, aninsulator 21, will be positioned between theplatform 20 and the shaft that rotates theplatform 20 to provide electrical isolation. - In another embodiment, the
platform 20 includes electrically conductive material at certain locations on its top surface that electrically coupled to certain locations on the bottom surface. In this manner, thesubstrate 12 can be placed at an appropriate location on the top side of theplatform 20 while the electrical feed through 26 may be positioned or placed at an appropriate location on the bottom side of theplatform 20. In this manner, thesubstrate 12 is electrically coupled to the electrical feed through 26. - The electrical feed through 26 provides a DC signal and a radio frequency signal to the
platform 20 and thesubstrate 12. The desired operational parameters associated with each of these signals are described more fully below. Preferably, the DC signal is generated by aDC power supply 66 at a negative voltage and the radio frequency signal is generated by anRF transmitter 64 at a desired power level. The two signals are then preferably mixed at a DC/RF mixer 68 and provided to the electrical feed through 26 through anRF balancing network 70, which provides signal balancing by minimizing the standing wave reflected power. TheRF balancing network 70 is preferably controlled through a manual control. - In an alternative embodiment, the
platform 20 is eliminated, including all of the supporting hardware, structures, and equipment, such as, for example, thedrive motor 24, and thedrive assembly 22. In such a case thesubstrate 12 is electrically coupled to the electrical feed through 26. - The remaining equipment and components of the
system 10 ofFIG. 1 are used to create, maintain, and control the desired vacuum condition within thevacuum chamber 14. This is achieved through the use of a vacuum system. The vacuum system includes aroughing pump 46 and aroughing valve 48 that is used to initially pull down the pressure in thevacuum chamber 14. The vacuum system also includes aforeline pump 40, aforeline valve 44, adiffusion pump 42, and amain valve 50. Theforeline valve 44 is opened so that theforeline pump 40 can began to function. After thediffusion pump 42 is warmed or heated to an appropriate level, themain valve 50 is opened, after theroughing pump 40 has been shut in by closing theroughing valve 44. This allows thediffusion pump 42 to further reduce the pressure in thevacuum chamber 14 below a desired level. - A
gas 60, such as argon, may then be introduced into thevacuum chamber 14 at a desired rate to raise the pressure in thevacuum chamber 14 to a desired pressure or to within a range of pressures. A gas control valve controls the rate of the flow of thegas 60 into thevacuum chamber 14 through thebase plate 32. - Once all of the operating parameters and conditions are established, as will be described more fully below in connection with
FIGS. 5 and 6 according to the teachings of the present invention, plasma plating occurs insystem 10. Thesubstrate 12 may be plasma plated with a deposited layer, which may include one or more layers such as a base layer, a transitional layer, and a working layer, through the formation of a plasma within thevacuum chamber 14. The plasma will preferably include positively charged depositant ions from the evaporated or vaporized depositant along with positively charged ions from thegas 60 that has been introduced within thevacuum chamber 14. It is believed, that the presence of the gas ions, such as argon ions, within the plasma and ultimately as part of the depositant layer, will not significantly or substantially degrade the properties of the depositant layer. The introduction of the gas into thevacuum chamber 14 is also useful in controlling the desired pressure within thevacuum chamber 14 so that a plasma may be generated according to the teachings of the present invention. In an alternative embodiment, the plasma plating process is achieved in a gasless environment such that the pressure within thevacuum chamber 14 is created and sufficiently maintained through a vacuum system. - The generation of the plasma within the
vacuum chamber 14 is believed to be the result of various contributing factors such as thermionic effect from the heating of the depositant within the filaments, such as thefilament 16 and thefilament 18, and the application of the DC signal and the radio frequency signal at desired voltage and power levels, respectively. - The vacuum system of the
system 10 may include any of a variety of vacuum systems such as a diffusion pump, a foreline pump, a roughing pump, a cryro pump, a turbo pump, and any other pump operable or capable of achieving pressures within thevacuum chamber 14 according to the teachings of the present invention. - As described above, the vacuum system includes the
roughing pump 46 and thediffusion pump 42, which is used with theforeline pump 40. The roughing pump 46 couples to thevacuum chamber 14 through the roughingvalve 48. When the roughingvalve 48 is open, theroughing pump 46 may be used to initially reduce the pressure within thevacuum chamber 14. Once a desired lower pressure is achieved within thevacuum chamber 14, the roughingvalve 48 is closed. The roughing pump 46 couples to thevacuum chamber 14 through a hole or opening through thebase plate 32. Theroughing pump 46 will preferably be provided as a mechanical pump. In a preferred embodiment of the vacuum system of thesystem 10 as shown inFIG. 1 . The vacuum system in this embodiment includes a foreline pump coupled to adiffusion pump 42 through aforeline valve 44. Theforeline pump 40 may be implemented as a mechanical pump that is used in combination with thediffusion pump 42 to reduce the pressure within thevacuum chamber 14 to a level even lower than that which was produced through the use of theroughing pump 46. - After the roughing pump has reduced the pressure within the
vacuum chamber 14, thediffusion pump 42, which uses heaters and may require the use of cooling water or some other substance to cool thediffusion pump 42, couples with thevacuum chamber 14 through amain valve 50 and through various holes or openings through thebase plate 32 as indicated inFIG. 1 by the dashed lines above themain valve 50 and below theplatform 20. Once thediffusion pump 42 has been heated up and made ready for operation, themain valve 50 may be opened so that the pressure within thevacuum chamber 14 may be further reduced through the action of thediffusion pump 42 in combination with theforeline pump 44. For example, the pressure within thevacuum chamber 14 may be brought below 4 milliTorr. During a backsputtering process, the pressure in thevacuum chamber 14 may be dropped to a level at or below 100 milliTorr on down to 20 milliTorr. Preferably, the pressure within thevacuum chamber 14 during a backsputtering process will be at a level at or below 50 milliTorr on down to 30 milliTorr. During normal operation of thesystem 10 during a plasma plating process, the pressure within thevacuum chamber 14 may be reduced by the vacuum system to a level at or below 4 milliTorr on down to a value of 0.1 milliTorr. Preferably, the vacuum system will be used during a plasma plating process to reduce the pressure within thevacuum chamber 14 to a level at or below 1.5 milliTorr on down to 0.5 milliTorr. -
FIG. 2 is a top view of a vacuum chamber of a system for plasma plating that illustrates one embodiment of a platform implemented as aturntable 20. Theturntable 20 is shown withsubstrates turntable 20. Theturntable 20 may rotate either clockwise or counterclockwise. Thesubstrates 12 a-12 d may be virtually any available material and are shown inFIG. 2 as round, cylindrical components such that the top view of each of the substrates presents a circular form. - The filament
power control module 34 is electrically coupled to a first set offilaments filaments FIG. 2 , it should be understood that the filamentpower control module 34 may supply current to the first set offilaments filaments filaments substrates 12 a-12 d using the depositants provided at the second set offilaments - The arrangement of the substrates in
FIG. 2 may be described as an array of substrates that include inwardly facing surfaces, which are closer to the center of theturntable 20, and outwardly facing surfaces, which are closer to the outer edge of theturntable 20. For example, the inwardly facing surfaces of the array ofsubstrates 12 a-d will be presented to thefilament 92 and thefilament 96, at different times of course, as they are rotated near the filaments. Similarly, the outwardly facing surfaces of thesubstrates 12 a-d will be presented to thefilaments - As mentioned previously, the filament
power control module 34 may provide a current in virtually any form, such as a direct current or an alternating current, but preferably provides current as an alternating current. - In operation,
turntable 20 rotates, for example, in a clockwise direction such that aftersubstrate 12 b passes near or through the filaments, the next substrate that will pass near or through the filaments issubstrate 12 c, and so on. In one example, the first set offilaments - After all of the operating parameters have been established within the vacuum chamber, as described throughout herein, the filament
power control module 34 may energize or provide alternating current to the first set offilaments substrates 12 a-d, which are at a negative potential. Generally, the closer the substrate is to the first set offilaments - After the first plasma has been plated onto the array of
substrates 12 a-d to form a base layer of the depositant layer on the substrates, the filamentpower control module 34 is energized so that a sufficient amount of current is provided to the second set offilaments - During the first shot when the base layer is being applied, the outwardly facing surfaces of
substrates 12 a-d are primarily coated through the nickel depositant located in thefilament 94. Similarly, the inwardly facing surfaces of the substrates are coated by the nickel depositant located in thefilament 96. The same relation holds true for the second shot where the silver\palladium is plasma plated onto the substrates to form the deposit layer. -
FIG. 3 is a side view that illustrates the formation and dispersion of a plasma around afilament 100 to plasma plate asubstrate 12 according to an embodiment of the present invention. Thefilament 100 is implemented as a wire basket, such as tungsten wire basket, and is shown with adepositant 102 located, and mechanically supported, within thefilament 100. As the filamentpower control module 34 provides sufficient current to thefilament 100, thedepositant 102 melts or vaporizes and aplasma 104 is formed. Of course, all of the operating parameters of the present invention must be present in order to achieve the plasma state so that plasma plating may takes place. - The
substrate 12, which is provided at a negative potential, attracts the positive ions of theplasma 104 to form a deposition layer. As is illustrated, the dispersion pattern of theplasma 104 results in most of the positive ions of theplasma 104 being attracted to the side adjacent or nearest to thefilament 100 and thedepositant 102. Some wrap around will occur such as that illustrated by theplasma 104 contacting the top surface of thesubstrate 12. Similarly, some of the positive ions of theplasma 104 may be attracted to the platform or turntable. As is illustrated, the present invention provides an efficient solution for the creation of a deposition layer by ensuring that most of the ions from the depositant are used in the formation of the deposition layer. -
FIG. 4 is a sectional view that illustrates a deposition layer of thesubstrate 12 that includes abase layer 110, atransition layer 112, and a workinglayer 114. It should be noted at the outset that the thickness of the various layers that form the deposition layer are grossly out of proportion with the size of thesubstrate 12; however, the relative thicknesses of the various sublayers or layers of the deposition layer are proportionate to one another, according to one embodiment of the present invention. - Generally, the thickness of the entire deposition layer on the substrate, according to the teachings of the present invention, are believed to generally range between 500 and 20,000 Angstroms. In a preferred embodiment, the entire thickness of the deposition layer is believed to range between 3,000 and 10,000 Angstroms. The present invention provides excellent repeatability and controllability of deposition layer thicknesses, including all of the sublayers such as the
base layer 110, thetransition layer 112, and the workinglayer 114. It is believed that the present invention can provide a controllable layer thickness at an accuracy of around 500 Angstroms. It should also be mentioned that the present invention may be used to form a deposition layer with one or any multiple of sublayers. - The thickness of the deposition layer is normally determined based on the nature of intended use of the plasma plated substrate. This may include such variables as the temperature, pressure, and humidity of the operating environment, among many other variables and factors. The selection of the desired metal or depositant type for each layer is also highly dependant upon the nature of the intended use of the plasma plated substrate.
- For example, the present invention prevents or substantially reduces galling or mating or interlocking components. Galling includes the seizure of mated components that often occur when two surfaces, such as threaded surfaces, are loaded together. Galling can cause components to fracture and break, which often results in severe damage. Plasma plating may be used to prevent or reduce galling by plating one or more contacting surfaces.
- Various depositants may be used to achieve this beneficial effect. It is believed, however, that galling is preferably reduced through a plasma plating process that deposits a base layer of nickel or titanium and a working layer of a silver/palladium metal alloy on one or more contacting surfaces. For high temperature applications, such as over 650 degrees Fahrenheit, it is believed that the galling is preferably reduced through a plasma plating process that deposits a nickel or titanium base layer and a working layer of gold.
- It has been found through experimentation that chromium does not work well to reduce galling, this includes when the chromium is deposited as either the base layer, the transition layer, or the working layer. It is believed that chromium may be a depositant that is more difficult to control during the plasma plating process.
- Plasma plating may also be used to plate valve parts, such as valve stems in non-nuclear applications, and are preferably plasma plated using a titanium base layer, a gold transition layer, and an indium working layer. In nuclear applications, such as nuclear power plant applications, indium is not a preferred plasma plating depositant because it is considered to be too much of a radioactive isotope absorber. Instead, valve stems in nuclear applications are preferably plasma plated using a nickel base layer and a silver/palladium metal alloy working layer.
- As is illustrated in
FIG. 4 , the workinglayer 14 is normally provided at a substantially larger thickness than thecorresponding transition layer 112 and thebase layer 110. It should also be noted that the coating of the top of thesubstrate 12 is shown to be thin at or near the center or middle of thesubstrate 12. This effect is due to how the filaments are positioned during the plasma plating process. For example, if the filaments are positioned similarly to that illustrated inFIGS. 2-3 , the middle or center portion of thesubstrate 12 will generally have a thinner overall profile than the side of the deposition layer. - Although various ranges of thicknesses have been discussed herein, it should be understood that the present invention is not limited to any maximum deposition layer thickness. The thickness of the deposition layer, especially the thickness of the working
layer 114, can be provided at virtually any desired thickness, normally depending upon the operating environment in which the plasma platedsubstrate 12 will be introduced. Thebase layer 110 and thetransition layer 112 and any other layers below the workinglayer 114 will preferably be provided at a substantially smaller thickness than the corresponding thickness of the workinglayer 114. For example, thebase layer 110 and thetransition layer 112 may be provided at a thickness ranging from 500 to 750 Angstroms while the workinglayer 114 may be provided at virtually any thickness such as for example 18,000 Angstroms. -
FIG. 5 is a flow chart of amethod 500 for plasma plating according to an embodiment of the present invention. Themethod 500 begins atblock 502 and proceeds to block 504. Atblock 504, the material or substrate that will be plasma plated is prepared for the process. This may include cleaning the substrate to remove any foreign materials, contaminants, and oils. Any of a variety of known cleaning processes may be used such as those defined by the Steel Structures Painting Council (SSPC). For example, the SSPC-5 standard may be employed to ensure that a substrate is cleaned to a white metal condition. Similarly, the SSPC-10 standard may be employed. Preferably, the substrate will undergo an abrasive blasting, such as for example, bead blasting to further ensure that any foreign materials or contaminants are removed. It should be noted that an oxidation layer may be present on the surface of the substrate. The present invention allows for a deposition layer to be plasma plated onto the substrate surface, even in the presence of an oxidation layer, with excellent adhesion and mechanical properties. - The
method 500 proceeds next to block 506 where the plasma plating system prerequisites are established. Depending upon the implementation of the system for plasma plating, this may involve any of a variety of items. In the situation where a diffusion pump is used as part of the vacuum system, items such as the availability of cooling water must be established. Similarly, the adequate availability of lube oil and air to operate the various equipment, valves, and machinery associated with the system for plasma plating must be established. An adequate supply of gas, such as argon gas, should also be verified and checked at this point before proceeding to block 510. - At
block 510, assuming that a diffusion pump is used as part of the vacuum system, the diffusion pump is prepared for operation. This may include opening a foreline valve and the starting of the foreline vacuum pump which is used in combination with the diffusion pump. Once a foreline vacuum has been drawn, the heaters of the diffusion pump may be energized. This places the diffusion pump in service. - The
method 500 proceeds next to block 512 where the vacuum chamber is set up. This includes any number of processes such as positioning the substrate within the vacuum chamber. This is normally achieved by positioning or placing the substrate at a specified location on a platform or turntable located within the vacuum chamber. Before accessing the internal volume of the vacuum chamber, the vacuum chamber seal must be broken and the bell jar or outer member is preferably lifted away from its base plate. Once the substrate is positioned on the platform, the filaments may be positioned relative to the placement of the substrate. - The positioning of the filaments may involve any number of techniques and includes such variables as the amount and type of depositant to be provided at the filament, and the distance, not only relative to the substrate, but relative to other filaments. Generally, the filament will be located a distance ranging from 0.1 inches to 6 inches from the substrate, as measured from the center line of the filament, or from the depositant, to the closest point of the substrate. Preferably, however, the distance between the filament or the depositant and the substrate will range anywhere from 2.75 inches to 3.25 inches when the depositant will serve as the base layer or transition layer of the deposition layer. Similarly, when the depositant will serve as the working layer of the deposition layer that will be deposited on the substrate, the distance between the filament or the depositant and the substrate is preferably provided at a distance between 2 inches and 2.5 inches.
- In the situation where multiple depositants or multiple shots will be performed in the plasma plating process, it is necessary to consider the placement of the filaments that will hold the first depositant relative to those that will hold the second depositant as well as each of the filament's position relative to each other and the substrate. Generally the distance of a second filament from a first filament, which will include a depositant that will serve as a base layer, transition layer, or a working layer of a deposition layer, should be anywhere between 0.1 inches and 6 inches.
- The spacing between filaments that include depositants that will serve as a base layer, is generally provided between 0.1 inches and 6 inches. Preferably, this distance shall be between 3 inches and 4 inches. The foregoing filament spacing information also applies when the depositant provided in the filaments will serve as the transition layer in the deposition layer. Similarly, the spacing between filaments, which include a depositant that will serve as the working layer of the deposition layer, should generally be between 0.1 inches and 6 inches, but, preferably, will be between 2.5 inches and 3 inches.
- The chamber setup of
block 512 may also need to take into account the arrangement of an array of substrates on the platform that are being plasma plated. For example, a filament that is positioned in the vacuum chamber so that it will provide a dispersion pattern to provide depositant coverage to inwardly facing surfaces of an array of substrates, it may require anywhere from 20 to 80 percent less mass or weight of depositant when compared with a filament positioned in the vacuum chamber to provide coverage for the array of outwardly facing surfaces. The reference to inwardly and outwardly are relative to the platform or turntable with inwardly referring to those surfaces closer to the center of the platform or turntable. This is because the efficiency of the plasma plating process is greater for the inwardly facing surfaces of an array of substrates than at the outwardly facing surfaces of the array of substrates because of the forces attracting the, generally, positive ions of the plasma. This also ensures that the thickness of the deposition layer on the inwardly facing surfaces and the outwardly facing surfaces are more uniform. In such a case, the weight or mass of the depositant will, preferably, need to vary between such filament positions. Generally, the variance in mass or weight between the two locations may be anywhere from 20 to 80 percent different. Preferably, the depositants in the filaments covering the inwardly facing surfaces will use 40 to 50 percent less mass or weight than the depositants of the filaments covering the outwardly facing surfaces. The amount of the depositant placed in the filaments corresponds to the desired thickness of the deposition layer, and any sublayers thereof. This was discussed more fully and is illustrated more fully in connection withFIG. 3 . - The type of filament affects the dispersion pattern achieved through the melting or evaporation of its depositant during the creation of the plasma. Any of a variety of filament types, shapes, and configurations may be used in the present invention. For example, the filament may be provided as a tungsten basket, a boat, a coil, a crucible, a ray gun, an electron beam gun, a heat gun, or as any other structure, such as a support structure provided within the vacuum chamber. The filaments are generally heated through the application of an electric current through the filament. However, any method or means of heating the depositant within the filament may be used in the present invention.
- The setup of the vacuum chamber also includes placing the depositants in the one or more filaments. The present invention contemplates the use of virtually any material that is capable of being evaporated under the conditions and parameters of the present invention so that a plasma will form. For example, the depositant may include virtually any metal, such as a metal alloy, gold, titanium, chromium, nickel, silver, tin, indium, lead, copper, palladium, silver/palladium and any of a variety of others. Similarly, the depositant may include any other materials such as carbon, nonmetals, ceramics, metal carbides, metal nitrates, and any of a variety of other materials. The depositants will generally be provided in a pellet, granule, particle, powder, wire, ribbon, or strip form. Once the filaments have been properly positioned and loaded, the vacuum chamber may be closed and sealed. This may include sealing the bell portion of the vacuum chamber with its base plate.
- The
method 500 proceeds next to block 514 where preparations are made to begin establishing a vacuum condition within the vacuum chamber. In one embodiment, such as thesystem 10 shown inFIG. 1 , a roughing pump is started to begin evacuating the vacuum chamber and to bring the pressure down within the vacuum chamber to a sufficient level so that additional pumps may take over to further reduce the pressure within the vacuum chamber. In one embodiment, the roughing vacuum pump is a mechanical pump that may be started, and a roughing valve may then be opened to provide access to the vacuum chamber. Once the roughing vacuum pump has achieved its desired function and has reduced the pressure in the vacuum chamber to its desired or designed level, the roughing valve is shut. At this point, themethod 500 transitions to block 516. - At
block 516, the pressure within the vacuum chamber is further reduced using another vacuum pump. For example, in one embodiment, a diffusion pump/foreline pump is utilized to further reduce the pressure within the vacuum chamber. In the embodiment of the present invention as illustrated inFIG. 1 , this is achieved by opening the main valve and allowing the diffusion pump, supported by the mechanical foreline pump, to further pull or reduce the pressure in the vacuum chamber. - Generally, the pressure in the vacuum chamber is reduced to a level that is at or below 4 milliTorr. Preferably, the pressure in the vacuum chamber is reduced to a level that is at or below 1.5 milliTorr. In the event that backsputtering, which is described below in connection with
block 518 of themethod 500, is to be performed, the pressure in the vacuum chamber is reduced to a level below 100 milliTorr and generally in a range between 20 milliTorr and 100 milliTorr. In a preferred embodiment when backsputtering is to be performed, the pressure is reduced in the vacuum chamber at a level below 50 milliTorr, and generally at a level between 20 milliTorr and 50 milliTorr. - Preceding next to block 518, a backsputtering process may be performed to further clean and prepare the substrate. It should be understood, however, that such a process is not mandatory. The backsputtering process is described in more detail below in connection with
FIG. 6 . The backsputtering process may include the rotation of the platform or turntable within the vacuum chamber. In such a case, the turntable will generally be rotated at a rate at or between 5 revolutions per minute and 30 revolutions per minute. Preferably, the turntable will be rotated at a rate between 12 revolutions per minute and 15 revolutions per minute. The operation of the turntable, which also will preferably be used as the deposition layer is being formed on the substrate according to the teachings of the present invention. -
Method 500 proceeds next to block 520 where an operating vacuum is established. Although a vacuum condition has already been established within the vacuum chamber, as previously discussed in connection withblock - At
block 522, various operating parameters and values of the system are established. This will generally include the rotation of a turntable, if desired, the application of a DC signal, and the application of a radio frequency signal. Assuming that the platform includes a turntable or some other rotating device, the turntable rotation will preferably be established at this point. This assumes, of course, that the rotation of the turntable was not previously started and thediscretionary backsputtering block 518. - Once the rotation of the turntable has been established, the DC signal and the RF signal may be applied to the substrate. The application of the DC signal to the substrate will generally be provided at a voltage amplitude that is at or between one volt and 5,000 volts. Note that the polarity of the voltage will preferably be negative; however, this is not always required. In a preferred embodiment, the application of the DC signal to the substrate will be provided at a voltage level at or between negative 500 volts and negative 750 volts.
- The application of the radio frequency signal to the substrate will generally be provided at a power level that is at or between 1 watt and 50 watts. Preferably, the power level of the radio frequency signal will be provided at 10 watts or between a range defined by 5 watts and 15 watts. The frequency of the radio frequency signal will generally be provided at an industrial specified frequency value in either the kilohertz range or the megahertz range. Preferably, the frequency signal will be provided at a frequency of 13.56 kilohertz. Although the term radio frequency has been used throughout to describe the generation and application of the radio frequency signal to the substrate, it should be understood that the term radio frequency should not be limited to its commonly understood definition of signals having frequencies roughly between 10 kilohertz and 100,000 megahertz. The term radio frequency shall also include any signal with a frequency component that is operable or capable of assisting with the creation or excitation of a plasma in a vacuum chamber.
-
Block 522 will also preferably include the mixing of the DC signal and the radio frequency signal, using mixer circuitry, to generate a mixed signal. This allows only one signal to be applied to the substrate. This is generally achieved using the electrical feed through that extends through the base plate of the vacuum chamber and contacts an electrically conductive portion of the platform, which in turn electrically couples to the substrate or substrates.Block 522 may also include the balancing of the mixed signal through the use of a radio frequency balancing network. Preferably, the mixed signal is balanced by minimizing the standing wave reflected power. This is preferably controlled through a manual control. - As the output or load characteristics of the antenna or output changes, as seen from the mixer circuitry, problems can arise when electrical signals or waves are reflected from the output load back to the mixer or source. These problems may include damage to the radio frequency transmitter and a reduction in the transfer of power to the substrate and vacuum chamber to ensure the formation of a sufficient plasma to achieve a successful plasma plating process.
- This problem can be reduced or solved by including the radio frequency balancing network that can adjust its impedance, including in one embodiment its resistance, inductance, and capacitance, to match or reduce the presence of reflected waves. The impedance and electrical characteristics of the output load or antenna are affected by such things as the presence and/or absence of a plasma and the shape and properties of the substrate or substrates on the platform. Because of such changes during the plasma plating process, the radio frequency balancing network may need to be adjusted during the process to minimize the standing wave reflected power or, stated differently, to prevent or reduce the standing wave ratio return to the radio frequency transmitter.
- Preferably, these adjustments are performed manually by an operator during the plasma plating process. In other embodiments, the radio frequency balancing network is automatically adjusted. Care must be taken, however, to ensure that the automatic adjustment does not over compensate or poorly track the changes in the output load.
- The
method 500 proceeds next to block 524 where the depositant or depositants are melted or evaporated so that a plasma will be generated. The generation of the plasma at the conditions provided by the present invention will result in a deposition layer being formed on the surface of the substrate through plasma plating. It is believed that the deposition layer is formed at a medium energy level on the average of between 10 eV and 90 eV. - The depositants are generally evaporated or vaporized by providing a current through the filament around the depositant. In a preferred embodiment, the depositants are slowly or incrementally heated to achieve a more even heat distribution in the depositant.
- This also improves the formation of the plasma. The current may be provided as an alternating current or as any other current that is sufficient to generate heat in the filament that will melt the depositant. In other embodiments, the depositant may be heated through the introduction of an agent that is in chemical contact with the depositant. In still other embodiments, the depositant may be heated through the use of electromagnetic or microwave energy.
- The conditions in the vacuum chamber will be correct for the formation of a plasma. The plasma will generally include gas ions, such as argon ions, and depositant ions, such as gold, nickel, or palladium ions. The gas ions and the depositant ions will generally be provided as positive ions due to the absence of one or more electrons. The creation of the plasma is believed to be assisted through the introduction of the radio frequency signal and because of thermionic phenomena due to the heating of the depositants. It is contemplated that in some situations, a plasma may be generated that includes negatively charged ions.
- The negative potential established at the substrate due to the DC signal will attract the positive ions of the plasma. Once again, this will primarily include depositant ions and may include gas ions, such as argon gas ions from the gas that was introduced earlier in
method 500. The inclusion of the gas ions, such as argon ions, are not believed to degrade the material or mechanical characteristics of the deposition layer. - It should be noted that some prior literature has suggested that the introduction of a magnet at or near the substrate is desirable to influence the path of the ions of the plasma as they are attracted to the substrate to form the deposition layer. Experimental evidence now suggests that the introduction of such a magnet is actually undesirable and produced unwanted effects. The presence of the magnet may lead to uneven deposition thicknesses, and prevent or significantly impede the controllability, repeatability, and reliability of the process.
- Whenever the deposition layer is designed to include multiple sublayers, multiple shots must be performed at
block 524. This means that once the base layer depositants have been melted through the heating of their filaments, the transition layer depositants (or the depositant of the next layer to be applied) are heated and melted by the introduction of heat at their filaments. In this manner, any number of sublayers may be added to the deposition layer. Before successive depositant sublayers are formed, the preceding layer shall have been fully or almost fully formed. Themethod 500 thus provides the significant advantage of allowing a deposition layer to be created through multiple sublayers without having to break vacuum and reestablish vacuum in the vacuum chamber. This can significantly cut overall plasma plating time and costs. - The
method 500 proceeds next to block 526 where the process or system is shut down. In the embodiment of the system shown inFIG. 1 , the main valve is closed and a vent valve to the vacuum chamber is opened to equalize pressure inside the vacuum chamber. The vacuum chamber may then be opened and the substrate items may be immediately removed. This is because themethod 500 does not generate excessive heat in the substrates during the plasma plating process. This provides significant advantages because the material or mechanical structure of the substrate and deposition layer are not adversely affected by excessive temperature. The plasma plated substrates may then be used as needed. Because the temperature of the substrates are generally at a temperature at or below 125 Fahrenheit, the substrates can generally be immediately handled without any thermal protection. - The
method 500 provides the additional benefit of not generating any waste byproducts and is environmentally safe. Further, themethod 500 is an efficient process that efficiently uses the depositants such that expensive or precious metals, such as gold and silver, are efficiently utilized and are not wasted. Further, due to the fact that the present invention does not use high energy deposition techniques, no adverse metallurgical or mechanical effects are done to the substrate. This is believed to be due to the fact that the deposition layer of the present invention is not deeply embedded within the substrate, but excellent adherence, mechanical, and material properties are still exhibited by the deposition layer. After the substrates have been removed atblock 528, themethod 500 ends atblock 530. -
FIG. 6 is a flow chart of amethod 600 for backsputtering using the system and method of the present invention, according to an embodiment of the present invention. As mentioned previously, backsputtering may be used to further clean the substrate before a deposition layer is formed on the substrate through plasma plating. - Backsputtering generally removes contaminants and foreign materials. This results in a cleaner substrate which results in a stronger and more uniform deposition layer. The
method 600 begins atblock 602 and proceeds to block 604 where a gas is introduced into the vacuum chamber at a rate that maintains or produces a desired pressure within the vacuum chamber. This is similar to what was previously described inblock 520 in connection withFIG. 5 . Generally, the pressure in the vacuum chamber should be at a level at or below 100 milliTorr, such as at a range between 20 milliTorr and 100 milliTorr. Preferably, the pressure is provided at a level at or between 30 milliTorr and 50 milliTorr. - The
method 600 proceeds next to block 606 where rotation of the platform or turntable is established, if applicable. As mentioned previously, the rotation of the turntable may be provided at a rate between 5 revolutions per minute and 30 revolutions per minute but is preferably provided at a rate between 12 revolutions per minute and 15 revolutions per minute. - Proceeding next to block 608, a DC signal is established and is applied to the substrate. The DC signal will generally be provided at an amplitude at or between one volt and 4,000 volts. Preferably, the DC signal will be provided at a voltage between negative 100 volts and negative 250 volts.
- Block 608 also involves the generation of a radio frequency signal that will be applied to the substrate. The radio frequency signal will generally be provided at a power level at or between 1 watt and 50 watts. Preferably, the radio frequency signal will be provided at a power level of 10 watts or at or between 5 and 15 watts. The DC signal and the radio frequency signal are preferably mixed, balanced, and applied to the substrate as a mixed signal. As a consequence, a plasma will form from the gas that was introduced at
block 604. This gas will generally be an inert gas or noble gas such as argon. The formation of the plasma includes positive ions from the gas. These positive ions of the plasma will be attracted and accelerated to the substrate, which will preferably be provided at a negative potential. This results in contaminants being scrubbed or removed from the substrate. Once the contaminants or foreign matter are removed from the substrate, they are sucked out of the vacuum chamber through the operation of the vacuum pump, such as the diffusion pump. - Proceeding next to block 610, the backsputtering process continues for a period of time that is generally between 30 seconds and one minute. Depending on the condition and cleanliness of the substrate, the backsputtering process may continue for more or less time. Generally, the backsputtering process is allowed to continue until the capacitance discharge, created by the backsputtering process is substantially complete or is significantly reduced. This may be visually monitored through the observation of sparks or light bursts that coincide with the capacitive discharge from the is contaminants from the substrate. This may be referred to as microarcing.
- During the backsputtering process, the DC signal must be controlled. This is normally achieved through manual adjustments of a DC power supply. Preferably, the voltage of the DC signal is provided at a level that allows the voltage to be maximized without overloading the DC power supply. As the backsputtering process continues, the current in the DC power supply will vary because of changes in the plasma that occur during the backsputtering process. This makes it necessary to adjust the voltage level of the DC signal during the backsputtering process.
- The
method 600 proceeds next to block 612 where the DC signal and the radio frequency signal are removed and the gas is shut off. Themethod 600 proceeds next to block 614 where the method ends. - Thus, it is apparent that there has been provided, in accordance with the present invention, a system and method for plasma plating that satisfies one or more of the advantages set forth above. Although the preferred embodiment has been described in detail, it should be understood that various changes, substitutions, and alterations can be made herein without departing from the scope of the present invention, even if all, one, or some of the advantages identified above are not present. For example, the DC signal and the radio frequency signal may be electrically coupled to the substrate using virtually any available electrically conductive path. The present invention may be implemented using any of a variety of materials and configurations. For example, any of a variety of vacuum pump systems, equipment, and technology could be used in the present invention. The present invention also does not require the presence of a gas, such as argon, to form a plasma, and the backsputtering process is not a mandatory process to practice the present invention. These are only a few of the examples of other arrangements or configurations of the system and method that is contemplated and covered by the present invention.
- The various components, equipment, substances, elements, and processes described and illustrated in the preferred embodiment as discrete or separate may be combined or integrated with other elements and processes without departing from the scope of the present invention. The present invention may be used to plasma plate virtually any material, object, or substrate using any of a variety of depositants. Other examples of changes, substitutions, and alterations are readily ascertainable by one skilled in the art and could be made without departing from the spirit and scope of the present invention.
Claims (17)