US20040130263A1 - High brightness led and method for producing the same - Google Patents
High brightness led and method for producing the same Download PDFInfo
- Publication number
- US20040130263A1 US20040130263A1 US10/336,568 US33656803A US2004130263A1 US 20040130263 A1 US20040130263 A1 US 20040130263A1 US 33656803 A US33656803 A US 33656803A US 2004130263 A1 US2004130263 A1 US 2004130263A1
- Authority
- US
- United States
- Prior art keywords
- led
- diffusion barrier
- epitaxial layers
- buffer layer
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The present invention discloses a high brightness LED (light emitting diode) and a method for producing the same. The LED of the present invention primarily includes a permanent substrate, LED epitaxial layers with a p-n or n-p junction structure, a layered structure formed between the permanent substrate and the LED epitaxial layers, a first electrode and a second electrode. The layered structure may include single layer, two layers or three layers. For the three layers structure, a reflective layer, a diffusion barrier and a buffer layer are usually included. These layers may be electrically conductive and formed by one or more thin films. Accordingly, the LED of the present invention can exhibit high brightness and excellent mechanical strength during manufacturing.
Description
- 1. Field of the Invention
- The present invention relates to an LED (light emitting diode) and a method for producing the same, and more particularly to a high brightness LED and a method for producing the same, in which excellent mechanical strength for manufacturing can be exhibited.
- 2. Related Prior Art
- Currently, how to promote the brightness or illuminence is a significant issue for developing LED (light emitting diode). Therefore, many studies and developments are being made by researchers and industries.
- As one of the most useful substrates for manufacturing LED, GaAs is still not satisfying enough in emitting efficiency, because partial wavelength will be absorbed. R.O.C. Pat. No. 385557, 391067 and 332344 mentioned solutions of this problem by forming epitaxial films with functions of conduction or reflection on the substrate. However, such design is still not satisfying for achieving high brightness.
- U.S. Pat. No. 5,376,580 mentioned another solution, in which the GaAs substrate is removed after a transparent GaP substrate is bonded to the LED epitaxial layers formed on the GaAs substrate. In this method, an epitaxial layer of 60-70 μm needs to be processed, and the alignment with crystal axes of the GaP substrates is difficult during the wafer bonding process. On the other hand, the thermal treatment for a long time may influence luminous effect of the LED with p-n or n-p junction.
- R.O.C. Pat. No. 415116 also provided a structure, in which a reflective layer and an adhesion layer are formed between the LED epitaxial layers and the conductive substrate. While such design facilitates brightness of the LED, the following problems exist:
- 1) The substrate tends to be damaged caused by thermal stress due to different heat transfer coefficients and different thermal expansion coefficients between the layers. For example, the heat transfer coefficient of silicon triples that of GaAs, but the thermal expansion coefficient of silicon is less than that of GaAs (Si: 2.6×10−6/K, GaAs: 5.7×10−6/K). Therefore, the Si substrate or GaAs or both may be broken during thermal process.
- 2) Reflectivity of the reflective layer or characteristic of the light emitting diode may regress because of mutual diffusion between the layers and the substrate.
- Therefore, it is desirable to provide an improved LED structure to mitigate and/or obviate the aforementioned problems.
- An object of the present invention is to provide a high brightness LED and a method for producing the same, so that mechanical strength of wafers can be improved and the productivity is thus promoted.
- The LED of the present invention primarily includes a permanent substrate, LED epitaxial layers with pn junction, a layered structure formed between the permanent substrate and the LED epitaxial layers, a first electrode and a second electrode; wherein the layered structure possesses properties of reflection, adhesion, diffusion barrier and buffer. The layered structure can include single layer, two layers or three layers, where in the three layers usually includes a reflective layer, a diffusion barrier layer and a buffer layer. These layers may be electrically conductive. The first electrode and the second electrode are respectively formed on proper position to supply enough energy for the LED epitaxial layers.
- The buffer layer, the reflective layer and the diffusion barrier aforementioned can be formed in an arbitrarily order, but the layer formed between the reflective layer and the LED epitaxial layers must be transparent.
- The diffusion barrier can be made by Pt, Ti or a nitride containing transition metals, for example, Ti, Ta, (Ti, Ta, W)—N, (Ti, Ta, W)—Si—N, (Ti, Ta, W)—B—N, and mixtures thereof with the function of diffusion barrier. The reflective layer can be made by material containing In, Sn, Al, Au, Pt, Pd, Zn, Ag, Ge, Ni, Au—Zn, Au—Be, Au—Ge, Au—Ge—Ni, etc., or mixtures thereof with the function of reflection. The buffer layer can be made by conductive metal oxides, for example, In2O3(Sn), SnO2(Sb), SnO2(F), Zn2O3(Al), ZnO(Al), ZnO(In), ZnO(Ga), RuO2, IrO2, NiO, Bi2O3, MoO3, Cd2SnO4, Cd2SnO3, super conductive oxides, and mixture thereof which have a function of buffering from stress. The aforementioned LED epitaxial layers can further include a using-for-epitaxy substrate thereon, for example, a GaAs substrate. The thermal expansion coefficient of the buffer layer should be larger than the maximum of the using-for-epitaxy substrate and the permanent substrate, or less than the minimum of the using-for-epitaxy substrate and the permanent substrate.
- The first electrode and the second electrode can be formed on positions referring to current LED structures.
- The method for producing the high brightness LED primarily includes step of: a) providing a temporary substrate for epitaxy; b) forming LED epitaxial layers on the temporary substrate, wherein the LED epitaxial layers with pn junction; c) providing a permanent substrate; d) forming a layered structure between the permanent substrate and the LED epitaxial layers, wherein the layered structure has properties of reflection, adhesion, diffusion barrier and buffer; and e) forming a first electrode and a second electrode on proper position to supply enough energy for the LED epitaxial layers.
- In the above step d), the layered structure can include a reflective layer, a diffusion barrier and a buffer layer, which can be formed on one or both of the LED epitaxial layers and the permanent substrate in an arbitrary order, and then the epitaxial layers and the permanent substrate are associated by wafer bonding. For example, (1) after the buffer layer and the reflective layer are formed on the LED epitaxial layers, and the diffusion barrier is formed on the permanent substrate, the two parts are associated by wafer bonding; (2) after the reflective layer is formed on the LED epitaxial layers, and the buffer layer and the diffusion barrier are sequentially formed on the permanent substrate, the two parts are associated by wafer bonding; (3) after the diffusion barrier, the buffer layer and the reflective layer are sequentially formed on the permanent substrate, the two parts are associated by wafer bonding.
- More detailed description about the present invention will be present in the following embodiments accompanying with drawings.
- FIG. 1 shows the epitaxial layer with multiple cladding layers;
- FIGS.2A-2D show the process in accordance with the first embodiment of the present invention;
- FIGS.3A-3D show the process in accordance with the second embodiment of the present invention;
- FIGS.4A-4C show the process in accordance with the third embodiment of the present invention;
- FIGS.5-7 show the other three structures of the LED in accordance with the present invention; and
- FIGS. 8A and 8B show different arrangements of the electrodes in accordance with the present invention.
- Referring to FIG. 1, epitaxial layers with multiple cladding layers formed on a GaAs
temporary substrate 10 used for epitaxy is provided. - The first layer is a GaInP
epitaxial layer 11, and the second layer is n+GaAsepitaxial layer 12. LEDepitaxial layers 13 are formed on the n+GaAsepitaxial layer 12. The LEDepitaxial layers 13 has a p-n or n-p structure, and can be II-IV or III-V metals with the direct-bandgap, for example, ZnSe, AlGaInP or GaN. - Next, a
buffer layer 21, areflective layer 22 and adiffusion barrier 23 are formed between the conductivepermanent substrate 20 and the LEDepitaxial layers 13. Thebuffer layer 21, thereflective layer 22 and thediffusion barrier 23 can be arranged in an arbitrary order, and individually including one or more films. Particularly, the film placed between thereflective layer 22 and the LEDepitaxial layers 13 must be transparent. These three layers can be preliminarily deposited on one or both of the LEDepitaxial layers 13 and thepermanent substrate 20, and finally be associated by wafer bonding. Three common embodiments are described as follows. - Referring to FIGS. 2A and 2B, the
buffer layer 21 and thereflective layer 22 are sequentially deposited and coated on the LED epitaxial layers 13 to form amulti-layer structure 021, and thediffusion barrier 23 is deposited on thepermanent substrate 20 to form anothermulti-layer structure 022. Then, themulti-layer structure 021 is flipped and bonded to anothermulti-layer structure 022, as shown in FIG. 2C. Next, thetemporary substrate 10 and the first layer (GaInP epitaxial layer) 11 are removed by etching, and stopping at the n+GaAs epitaxial layer 12 to obtain anLED 023 with the reflective layer and the conductive substrate as shown in FIG. 2D. In this embodiment, thebuffer layer 21, thereflective layer 22 and thediffusion barrier 23 can be formed by physical deposition, for example, sputtering, e-beam, and thermal deposition. - The
buffer layer 21, thereflective layer 22 and thediffusion barrier 23 of this embodiment are all electrically conductive, and the one adjacent to the LED epitaxial layers or the permanent substrate must have property of ohmic contact. Thebuffer layer 21 can be made from conductive metal oxides, for example, In2O3(Sn), SnO2(Sb), SnO2(F), Zn2O3(Al), ZnO(Al), ZnO(In), ZnO(Ga), RuO2, IrO2, NiO, Bi2O3, MoO3, Cd2SnO4, Cd2SnO3, super conductive oxides, and mixture thereof. It should be also noted that the thermal expansion coefficient of thebuffer layer 21 requires to be either larger than those of both the using-for-epitaxy temporary substrate and thepermanent substrate 20, or less than those of them both. In this embodiment, the using-for-epitaxytemporary substrate 10 is GaAs with a thermal expansion coefficient 5.7×10−6/K, and thepermanent substrate 20 is silicon with a thermal expansion coefficient 2.6×10−6. That is, thebuffer layer 21 has to have a thermal expansion coefficient larger than 5.7×10−6 or less than 2.6−10−6. - The
reflective layer 22 in this embodiment is made from Au and Au—Be. Other material such as In, Sn, Al, Pt, Pd, Zn, Ag, Ge, Ni, Au—Zn, Au—Ge, Au—Ge—Ni, etc., or mixtures thereof with the function of reflection can be used, too. - The
diffusion barrier 23 in this embodiment is made form Pt and Ti. Other material containing Ti, Ta, (Ti, Ta, W)—N, (Ti, Ta, W)—Si—N, (Ti, Ta, W)—B—N, and mixtures thereof with the function of diffusion barrier can be used, too. - FIGS. 3A, 3B,3C and 3D show the second embodiment in accordance with the present invention. The
reflective layer 22 is coated on the LED epitaxial layers 13 to form amulti-layer structure 031, and thebuffer layer 21 and thediffusion barrier 23 are sequentially deposited on thepermanent substrate 20 to form another multi-layer structure 032. Then themulti-layer structure 031 is flipped and bonded to another multi-layer structure 032, as shown in FIG. 3C. Next, thetemporary substrate 10 and the first layer (GaInP epitaxial layer) 11 are removed by etching, and stopping at the n+GaAs epitaxial layer 12 to obtain anLED 033 with the reflective layer and the conductive substrate as shown in FIG. 3D. - FIGS. 4A, 4B and4C show another embodiment, in which the
diffusion barrier 23, thebuffer layer 21 and thereflective layer 22 are sequentially deposited and coated on thepermanent substrate 20 to form a multi-layer structure 042. Then the multi-layer structure 041 including thetemporary substrate 10 and theepitaxial layers 11′ 12 and 13 is flipped, and bonded to the above multi-layer structure 042. Next, thetemporary substrate 10 and the first layer (GaInP epitaxial layer) 11 are removed by etching, and stopping at the n+GaAs epitaxial layer 12 as shown in FIG. 4C. - FIGS.5-7 show different arrangement of the
buffer layer 21, thereflective layer 22 and thediffusion barrier 23, wherein the technologies including physical deposition, wafer bonding, and etching are applied, too. - FIGS. 8A and 8B show two styles for forming electrodes. In FIG. 8A, a
transparent electrode 51 is formed on the n+GaAs epitaxial layer 12, and then afirst electrode 52 used for local wire bonding is formed on thetransparent electrode 51. Asecond electrode 53 is formed on backside of the conductivepermanent substrate 20. Certainly, thefirst electrode 52 can be directly formed on the n+GaAs epitaxial layer 12. The top surface of thefirst electrode 51 or the n+GaAs epitaxial layer 12 can be further shaped into a rough surface by dry etching so as to improve the refractive effect of the light source. - In FIG. 8B, most of the n+
GaAs epitaxial layer 12 are etched, and thefirst electrode 52 is formed on the remainedepitaxial layer 12. Next, the exposed LED epitaxial layers 13 are etched to expose partialreflective layer 22, on which thesecond electrode 53 is then formed. The second electrode can be also formed on backside of thepermanent substrate 20. - According to the above embodiments, the LED of the present invention possesses the following advantages:
- 1. No damage occurs on the epitaxial layers during wafer bonding, since the wafers are all thick enough, and therefore the yield of mass product can be increased.
- 2. The GaAs temporary epitaxial layer can be selectively removed, which promotes the emitting efficiency of the LED
- 3. The reflective layer facilitates light beams to emit from the front surface, which effectively increases brightness of the LED.
- 4. The buffer layer prevents the wafers from damage caused by different heat transfer coefficients and thermal expansion coefficients.
- 5. The diffusion barrier blocks the thermal diffusion of elements between layers during wafer bonding, so that characteristics and quality of the LED can be maintained.
- 6. The rough electrode surface may cause the light beams to be repeatedly refracted, and brightness of the LED can be enhanced.
- 7. The vertical LED (two electrodes are respectively arranged over the LED epitaxial layers and backside of the permanent substrate) may efficiently utilize the LED surfaces and increase productivity thereof.
Claims (20)
1. A high brightness LED (light emitting diode), comprising:
a permanent substrate;
LED epitaxial layers with p-n or n-p junction;
a layered structure formed between said permanent substrate and said LED epitaxial layers, and having properties of reflection, adhesion, diffusion barrier and buffer;
a first electrode and a second electrode formed on proper positions to provide enough energy for said LED epitaxial layers.
2. The high brightness LED as claimed in claim 1 , further comprising a using-for-epitaxy substrate on said LED epitaxial layers.
3. The high brightness LED as claimed in claim 1 , wherein said layered structure comprises single layer.
4. The high brightness LED as claimed in claim 1 , wherein said layered structure comprises two layers.
5. The high brightness LED as claimed in claim 1 , wherein said layered structure comprises a reflective layer, a buffer layer and a diffusion barrier.
6. The high brightness LED as claimed in claim 5 , wherein said diffusion barrier is adjacent to said permanent substrate, said buffer layer is adjacent to said LED epitaxial layers, said reflective layer is formed between said diffusion barrier and said reflective layer, and said buffer layer is transparent.
7. The high brightness LED as claimed in claim 5 , wherein said buffer layer is adjacent to said permanent substrate, said diffusion barrier is adjacent to said LED epitaxial layers, said reflective layer is formed between said buffer layer and said diffusion barrier, and said diffusion barrier is transparent.
8. The high brightness LED as claimed in claim 5 , wherein said buffer layer is adjacent to said permanent substrate, said reflective layer is adjacent to said LED epitaxial layers, and said diffusion barrier is formed between said buffer layer and said reflective layer.
9. The high brightness LED as claimed in claim 5 , wherein said reflective layer is adjacent to said permanent substrate, said buffer layer is adjacent to said LED epitaxial layers, said diffusion barrier is formed between said buffer layer and said reflective layer, and both said diffusion barrier and said buffer layer are transparent.
10. The high brightness LED as claimed in claim 5 , wherein said diffusion barrier is adjacent to said permanent substrate, said reflective layer is adjacent to said LED epitaxial layers, and said buffer layer is formed between said diffusion barrier and said reflective layer.
11. The high brightness LED as claimed in claim 5 , wherein said reflective layer is adjacent to said permanent substrate, said diffusion barrier is adjacent to said LED epitaxial layers, said buffer layer is formed between said buffer layer and said reflective layer, and both said diffusion barrier and said buffer layer are transparent.
12. The high brightness LED as claimed in claim 5 , wherein at least one of said diffusion barrier, said buffer layer and said reflective layer is electrically conductive.
13. The high brightness LED as claimed in claim 5 , wherein said buffer layer has a thermal expansion coefficient larger than both of said using-for-epitaxy substrate and said permanent substrate.
14. The high brightness LED as claimed in claim 5 , wherein said buffer layer has a thermal expansion coefficient less than both of said using-for-epitaxy substrate and said permanent substrate.
15. A method for producing a high brightness LED, comprising steps of:
a) providing a temporary substrate for epitaxy;
b) forming LED epitaxial layers on said temporary substrate, wherein said LED epitaxial layers with pn junction;
c) providing a permanent substrate;
d) forming a layered structure between said permanent substrate and said LED epitaxial layers, wherein said layered structure has properties of reflection, adhesion, diffusion barrier and buffer; and
e) forming a first electrode and a second electrode on proper position to supply enough energy for said LED epitaxial layers.
16. The method as claimed in claim 15 , wherein said layered structure comprises a buffer layer, a reflective layer and a diffusion barrier (in said step d).
17. The method as claimed in claim 16 , wherein said buffer layer, said reflective layer and said diffusion barrier are formed by deposition.
18. The method as claimed in claim 16 , wherein said buffer layer and said reflective layer are sequentially formed on said LED epitaxial layers, and said diffusion barrier is formed on said permanent substrate, and then said LED epitaxial layers and said permanent substrate are associated by wafer bonding technology.
19. The method as claimed in claim 16 , wherein said reflective layer is formed on said LED epitaxial layers, and said buffer layer and said diffusion barrier are sequentially formed on said permanent substrate, and then said LED epitaxial layers and said permanent substrate are associated by wafer bonding technology.
20. The method as claimed in claim 16 , wherein said diffusion barrier, said buffer layer and said reflective layer are sequentially formed on said permanent substrate, and then said LED epitaxial layers and said permanent substrate are associated by wafer bonding technology.