MX2019008642A - Material de acero y metodo para la produccion del material de acero. - Google Patents

Material de acero y metodo para la produccion del material de acero.

Info

Publication number
MX2019008642A
MX2019008642A MX2019008642A MX2019008642A MX2019008642A MX 2019008642 A MX2019008642 A MX 2019008642A MX 2019008642 A MX2019008642 A MX 2019008642A MX 2019008642 A MX2019008642 A MX 2019008642A MX 2019008642 A MX2019008642 A MX 2019008642A
Authority
MX
Mexico
Prior art keywords
steel material
equal
less
1069mpa
965mpa
Prior art date
Application number
MX2019008642A
Other languages
English (en)
Inventor
Soma Atsushi
Kamitani Hiroki
Arai Yuji
Yoshida Shinji
Original Assignee
Nippon Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp filed Critical Nippon Steel Corp
Publication of MX2019008642A publication Critical patent/MX2019008642A/es

Abstract

Se proporciona un material de acero que tiene un límite de elasticidad en un intervalo de 965 a 1069 MPa (grado 140 ksi) y también tiene una resistencia a SSC excelente. El material de acero de acuerdo con la presente descripción contiene una composición química que consiste, en % en masa, en C: más de 0.50 a 0.80%, Si: de 0.05 a 1.00%, Mn: de 0.05 a 1.00%, P: 0.025% o menos, S: 0.0100% o menos, Al: de 0.005 a 0.100%, Cr: de 0.20 a 1.50%, Mo: de 0.25 a 1.50%, Ti: de 0.002 a 0.050%, B: de 0.0001 a 0.0050%, N: de 0.002 a 0.010% y O: 0.0100% o menos, siendo el resto Fe e impurezas. El material de acero contiene una cantidad de C disuelto dentro de un intervalo de 0.010 a 0.060% en masa. El material de acero también tiene un límite de elasticidad dentro del intervalo de 965 a 1069 MPa y la relación de elasticidad del material de acero es de 90% o más.
MX2019008642A 2017-01-24 2018-01-22 Material de acero y metodo para la produccion del material de acero. MX2019008642A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017009977 2017-01-24
PCT/JP2018/001750 WO2018139400A1 (ja) 2017-01-24 2018-01-22 鋼材、及び、鋼材の製造方法

Publications (1)

Publication Number Publication Date
MX2019008642A true MX2019008642A (es) 2019-09-23

Family

ID=62978210

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2019008642A MX2019008642A (es) 2017-01-24 2018-01-22 Material de acero y metodo para la produccion del material de acero.

Country Status (10)

Country Link
US (1) US20190376167A1 (es)
EP (1) EP3575428A4 (es)
JP (1) JP6747524B2 (es)
CN (1) CN110234779A (es)
AU (1) AU2018213593A1 (es)
BR (1) BR112019014676A2 (es)
CA (1) CA3049859A1 (es)
MX (1) MX2019008642A (es)
RU (1) RU2725389C1 (es)
WO (1) WO2018139400A1 (es)

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105002425B (zh) * 2015-06-18 2017-12-22 宝山钢铁股份有限公司 超高强度超高韧性石油套管用钢、石油套管及其制造方法
JP6947012B2 (ja) * 2017-12-25 2021-10-13 日本製鉄株式会社 鋼材、油井用鋼管、及び、鋼材の製造方法
JP6950519B2 (ja) * 2017-12-25 2021-10-13 日本製鉄株式会社 鋼材、油井用鋼管、及び、鋼材の製造方法
AR114708A1 (es) * 2018-03-26 2020-10-07 Nippon Steel & Sumitomo Metal Corp Material de acero adecuado para uso en entorno agrio
US12024752B2 (en) 2019-04-11 2024-07-02 Nippon Steel Corporation Steel sheet and method for manufacturing same
CN111910055A (zh) * 2020-07-08 2020-11-10 东莞首嘉制管有限公司 一种内外精抽钢管及其加工工艺

Family Cites Families (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS59232220A (ja) 1983-06-14 1984-12-27 Sumitomo Metal Ind Ltd 耐硫化物腐食割れ性に優れた高強度鋼の製法
JPS60187664A (ja) * 1984-03-01 1985-09-25 Nippon Steel Corp 低硬度で降伏強度の高い電縫油井管及びその製造方法
JPH06104849B2 (ja) 1986-04-25 1994-12-21 新日本製鐵株式会社 硫化物応力割れ抵抗性に優れた低合金高張力油井用鋼の製造方法
JP3358135B2 (ja) 1993-02-26 2002-12-16 新日本製鐵株式会社 耐硫化物応力割れ抵抗性に優れた高強度鋼およびその製造方法
JP3332599B2 (ja) * 1994-09-07 2002-10-07 花王株式会社 漂白剤及び漂白洗浄剤組成物
JP3416857B2 (ja) * 1994-09-12 2003-06-16 住友金属工業株式会社 耐水素脆化特性に優れる鋼材とその製造方法
JP3755163B2 (ja) 1995-05-15 2006-03-15 住友金属工業株式会社 耐硫化物応力割れ性に優れた高強度継目無鋼管の製造方法
JPH1150148A (ja) * 1997-08-06 1999-02-23 Sumitomo Metal Ind Ltd 高強度高耐食継目無鋼管の製造方法
JP3493153B2 (ja) * 1999-01-12 2004-02-03 株式会社神戸製鋼所 冷間加工性に優れた線材または棒鋼および機械部品
JP2000256783A (ja) 1999-03-11 2000-09-19 Sumitomo Metal Ind Ltd 靭性と耐硫化物応力腐食割れ性に優れる高強度油井用鋼およびその製造方法
JP4058840B2 (ja) 1999-04-09 2008-03-12 住友金属工業株式会社 靭性と耐硫化物応力腐食割れ性に優れる油井用鋼およびその製造方法
JP4140556B2 (ja) * 2004-06-14 2008-08-27 住友金属工業株式会社 耐硫化物応力割れ性に優れた低合金油井管用鋼
JP4027956B2 (ja) * 2006-01-23 2007-12-26 株式会社神戸製鋼所 耐脆性破壊特性に優れた高強度ばね鋼およびその製造方法
JP4973663B2 (ja) * 2007-03-30 2012-07-11 住友金属工業株式会社 低合金油井管用鋼および継目無鋼管
FR2942808B1 (fr) * 2009-03-03 2011-02-18 Vallourec Mannesmann Oil & Gas Acier faiblement allie a limite d'elasticite elevee et haute resistance a la fissuration sous contrainte par les sulfures.
JP5728836B2 (ja) * 2009-06-24 2015-06-03 Ｊｆｅスチール株式会社 耐硫化物応力割れ性に優れた油井用高強度継目無鋼管の製造方法
JP5779984B2 (ja) * 2010-06-21 2015-09-16 Ｊｆｅスチール株式会社 耐硫化物応力割れ性に優れた油井用鋼管及びその製造方法
JP5662894B2 (ja) * 2011-07-27 2015-02-04 株式会社神戸製鋼所 耐食性に優れた原油タンカーのタンク上甲板用またはバラ積み船の船倉用鋼材
JP2013129879A (ja) * 2011-12-22 2013-07-04 Jfe Steel Corp 耐硫化物応力割れ性に優れた油井用高強度継目無鋼管およびその製造方法
JP5522322B1 (ja) * 2012-06-20 2014-06-18 新日鐵住金株式会社 油井管用鋼及びその製造方法
IN2015DN01476A (es) * 2012-09-26 2015-07-03 Nippon Steel & Sumitomo Metal Corp
CN104781440B (zh) * 2012-11-05 2018-04-17 新日铁住金株式会社 抗硫化物应力裂纹性优异的低合金油井管用钢及低合金油井管用钢的制造方法
US10240221B2 (en) * 2013-01-16 2019-03-26 Jfe Steel Corporation Stainless steel seamless pipe for oil well use and method for manufacturing the same
RU2673262C1 (ru) * 2014-12-12 2018-11-23 Ниппон Стил Энд Сумитомо Метал Корпорейшн Низколегированная сталь для трубы для нефтяной скважины и способ производства трубы для нефтяной скважины из низколегированной стали

Also Published As

Publication number Publication date
CA3049859A1 (en) 2018-08-02
JPWO2018139400A1 (ja) 2019-11-07
RU2725389C1 (ru) 2020-07-02
EP3575428A1 (en) 2019-12-04
JP6747524B2 (ja) 2020-08-26
US20190376167A1 (en) 2019-12-12
BR112019014676A2 (pt) 2020-05-26
EP3575428A4 (en) 2020-07-22
CN110234779A (zh) 2019-09-13
WO2018139400A1 (ja) 2018-08-02
AU2018213593A1 (en) 2019-08-01

Similar Documents

Publication Publication Date Title
MX2019008642A (es) Material de acero y metodo para la produccion del material de acero.
MX2016015580A (es) Meterial de acero tratado termicamente y metodo para producirlo.
AU2014243558B2 (en) High-performance, low-alloy, wear-resistant steel sheet and method of manufacturing the same
MX2017001374A (es) Procedimiento para la fabricacion de laminas de acero para el endurecimiento por presion y piezas obtenidas por este procedimiento.
NZ708752A (en) High-toughness low-alloy wear-resistant steel sheet and method of manufacturing the same
MX2018007185A (es) Cinta de acero galvanizada por inmersion en caliente de alta resistencia.
SG11201805206PA (en) Austenitic heat resistant alloy and method for producing the same
MX2016015400A (es) Material de acero tratado con calor y metodo para producir el mismo.
MX2019008377A (es) Tubo de acero inoxidable sin soldadura de alta resistencia y metodo de fabricacion del mismo.
MX2019011443A (es) Producto de acero inoxidable martensitico.
MX2018009402A (es) Chapa de acero inoxidable ferritico que contiene nb laminada en caliente y metodo para producir la misma, y chapa de acero inoxidable ferritico que contiene nb laminada en frio y metodo para producir la misma.
MX2017003993A (es) Lamina de acero laminado en frio de alta resistencia y alta formabilidad o banda de acero y metodo para fabricar la misma.
MX2016001050A (es) Material de acero de alta resistencia para pozo de petroleo y tuberias de pozo de petroleo.
MX2020002864A (es) Tubo sin costura de acero inoxidable martensitico para productos tubulares de region petrolifera, y metodo para la fabricacion del mismo.
MX2019003749A (es) Material de acero, tubo de acero para pozo de petróleo y método para producir el material de acero.
EP3216890A3 (en) Mold steel and mold
MX2017016905A (es) Acero resistente a la corrosion, metodo para producir dicho acero y uso del mismo.
MY192536A (en) High-mn steel and method for manufacturing same
MX2021000661A (es) Articulos de cuero biofabricado y metodos de estos.
UA103888C2 (ru) СПОСОБ ПОЛУЧЕНИЯ РАСПЛАВА СТАЛИ С содержанием марганца до 30 МАС. %
MX2019004216A (es) Lamina de acero para carburacion, y metodo para fabricar la lamina de acero para carburacion.
MX2019012451A (es) Lamina de acero de alta formabilidad para la fabricacion de partes estructurales ligeras y proceso de fabricacion.
MX2015016761A (es) Componente carburizado y metodo para manufacturar el mismo.
MX2020010540A (es) Material de acero adecuado para su uso en un ambiente acido.
MY173780A (en) Steel sheet for can and method for manufacturing the same