KR20180002240A - Dental cement composition comprising polyacrylic acid-based copolymer - Google Patents

Dental cement composition comprising polyacrylic acid-based copolymer Download PDF

Info

Publication number
KR20180002240A
KR20180002240A KR1020160081473A KR20160081473A KR20180002240A KR 20180002240 A KR20180002240 A KR 20180002240A KR 1020160081473 A KR1020160081473 A KR 1020160081473A KR 20160081473 A KR20160081473 A KR 20160081473A KR 20180002240 A KR20180002240 A KR 20180002240A
Authority
KR
South Korea
Prior art keywords
dental cement
acid
cement composition
dimethacrylate
polyacrylic acid
Prior art date
Application number
KR1020160081473A
Other languages
Korean (ko)
Other versions
KR101868873B1 (en
Inventor
김영주
오명환
김윤기
Original Assignee
(주) 베리콤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주) 베리콤 filed Critical (주) 베리콤
Priority to KR1020160081473A priority Critical patent/KR101868873B1/en
Publication of KR20180002240A publication Critical patent/KR20180002240A/en
Application granted granted Critical
Publication of KR101868873B1 publication Critical patent/KR101868873B1/en

Abstract

The present invention relates to a dental cement composition containing an inorganic filler and a polyacrylic acid-based copolymer which is produced by copolymerizing an itconic acid-based monomer and an acrylic acid-based monomer. The dental cement composition of the present invention ensures remarkably excellent mechanical properties after cured, by containing the molecular weight-adjusted polyacrylic acid-itconic acid copolymer.

Description

폴리아크릴산계 공중합체를 포함하는 치과용 시멘트 조성물{DENTAL CEMENT COMPOSITION COMPRISING POLYACRYLIC ACID-BASED COPOLYMER}TECHNICAL FIELD [0001] The present invention relates to a dental cement composition comprising a polyacrylic acid-based copolymer. [0002] DENTAL CEMENT COMPOSITION COMPRISING POLYACRYLIC ACID-BASED COPOLYMER [

본 발명은 폴리아크릴산계 공중합체를 포함하는 치과용 시멘트 조성물에 관한 것으로, 보다 상세하게는 분자량이 조절된 폴리아크릴산-이타콘산 공중합체를 포함하는 폴리아크릴산계 공중합체를 포함하는 치과용 시멘트 조성물에 관한 것이다.The present invention relates to a dental cement composition comprising a polyacrylic acid copolymer, and more particularly to a dental cement composition comprising a polyacrylic acid copolymer containing a polyacrylic acid-itaconic acid copolymer having a controlled molecular weight .

글라스 폴리알케노에이트(Glass polyalkenoate)라고도 알려져 있는, 글라스아이오노머 시멘트(Glass-ionomercement, GIC)는 치아수복재나 합착재로 광범위하게 이용되고 있다. 글라스아이오노머 시멘트는 이온용출성의 칼슘 플루오로-알루미노-실리케이트 시스템과 폴리(아크릴산) 수용액의 반응에 의한 경화산물이다. 상기 시멘트의 경화 반응이란, 아크릴산 용액이 분말의 표면을 녹이면서 용출된 이온들(예를 들어, Ca2 + 및 Al3 +)과 용액의 음이온과 가교결합을 하는 과정을 의미하며, 이를 통해 글라스아이오노머 시멘트는 자가-경화 과정(self-hardening process)을 겪는다고 알려져 있다.Glass ionomer cement (GIC), also known as glass polyalkenoate, is widely used as a dental restorative material or as a dental material. Glass ionomer cement is a cured product of the reaction of an ion-eluting calcium fluoro-alumino-silicate system with a poly (acrylic acid) aqueous solution. The curing reaction of the cement means a process in which an acrylic acid solution crosslinks with anions (for example, Ca 2 + and Al 3 + ) eluted while dissolving the surface of the powder and the anion of the solution, It is known that ionomer cement undergoes a self-hardening process.

치과용 글라스아이오노머 시멘트는 복잡한 구강 환경에서 용해에 높은 저항성, 기계적 결합이나 부착에 의한 강한 결합, 높은 인장, 전단 및 압축강도와 더불어 보철물과 치아 계면 사이에서의 응력에 저항하기 위한 우수한 파괴인성 등 다양한 물성을 만족해야 하는 고성능 다기능성의 치과 재료이다. Dental glass ionomer cements have high resistance to dissolution in complex oral environments, strong bonding due to mechanical bonding or adhesion, high tensile, shear and compressive strength as well as excellent fracture toughness to resist stresses between the prosthesis and tooth interface It is a high performance multifunctional dental material that must satisfy various physical properties.

특히, 치질에 대한 생체 적합성과 상아질과 법랑질 모두와 이온 교환 접착을 통해 세균에 대한 미세누출을 막을 수 있을 것을 요구한다. 이를 해결하기 위하여 다양한 실험이 진행되었으나 요구되는 강도와 경화 시간 등을 만족하지는 못하였다. In particular, biocompatibility with hemorrhoids and the need to prevent microleakage of bacteria through ion exchange bonding with both dentin and enamel. Various experiments have been conducted to solve this problem, but the required strength and curing time have not been satisfied.

글라스아이오노머 시멘트는 치의학에서 이용 분야가 확장되고 있으며, 나아가 정형외과 분야에서도 폴리메틸메타크릴레이트(PMMA) 뼈 시멘트의 대체물질로 관심을 모으고 있다. 이는 글라스아이오노머 시멘트의 낮은 발열경화반응과 뼈와의 접착성이 있는 물질이란 특성 때문이다.Glass ionomer cement has been expanding its use in dentistry and is also attracting attention as an alternative to polymethylmethacrylate (PMMA) bone cement in orthopedics. This is due to the property of low exothermic curing reaction of glass ionomer cement and adhesion to bone.

미국등록특허 제7,456,232호에는 치과용 재료로 가지가 달리지 않은 폴릭아크릴산을 이용하는 것에 대해 기재되어 있다. 그러나 농축된 수용액에서 폴릭아크릴산은 비가역적으로 겔화되는 경향이 있다. 겔화된 폴릭아크릴산 용액은 강도 등의 물성저하로 치과용 재료로 사용할 수 없는 문제가 있다. U.S. Patent No. 7,456,232 discloses the use of unbranched polyacrylic acid as a dental material. However, in concentrated aqueous solutions, polyacrylic acid tends to irreversibly gel. There is a problem that the gelled poly acrylic acid solution can not be used as a dental material due to a decrease in physical properties such as strength.

따라서, 종래의 폴리아크릴산을 이용한 글라스아이오노머 시멘트는 겔화로 인한 낮은 기계적 물성으로 인해 치과용 재료로 사용하는 데 문제점이 있었다.Therefore, the conventional glass ionomer cement using polyacrylic acid has a problem in that it is used as a dental material because of low mechanical properties due to gelation.

본 발명의 목적은 상기 문제점을 해결하기 위한 것으로, 분자량이 조절된 폴리아크릴산-이타콘산 공중합체를 포함함으로써 경화 후 기계적 물성이 우수한 페이스트형 치과용 시멘트 조성물을 제공하는 데 있다.An object of the present invention is to provide a paste-type dental cement composition having a polyacrylic acid-itaconic acid copolymer having a controlled molecular weight and having excellent mechanical properties after curing.

본 발명의 일 측면에 따르면, 이타콘산계 단량체 및 아크릴산계 단량체를 공중합하여 제조된 폴리아크릴산계 공중합체; 및 무기필러;를 포함하는 치과용 시멘트 조성물이 제공된다.According to one aspect of the present invention, there is provided a polyacrylic acid-based copolymer prepared by copolymerizing an itaconic acid monomer and an acrylic acid-based monomer; And an inorganic filler.

상기 폴리아크릴산계 공중합체의 중량평균분자량(Mw)이 1,000 내지 120,000일 수 있다. The polyacrylic acid-based copolymer may have a weight average molecular weight (Mw) of 1,000 to 120,000.

상기 폴리아크릴산계 공중합체의 중량평균분자량(Mw)이 25,000 내지 38,000일 수 있다. The polyacrylic acid-based copolymer may have a weight average molecular weight (Mw) of 25,000 to 38,000.

상기 폴리아크릴산계 공중합체의 중량평균분자량(Mw)이 26,000 내지 36,500일 수 있다. The polyacrylic acid-based copolymer may have a weight average molecular weight (Mw) of 26,000 to 36,500.

상기 무기필러가 비정질 합성 실리카, 결정성 천연 실리카, 카롤린, 탈크, 석영, 바륨 글라스, 바륨 글라스/실리카 혼합물, 석영/바륨 혼합물 글라스, 지르코니아/실리카 혼합물, 스트론튬 알루미노 실리케이트, 산 반응성 충진제, 나노 지르코니아 충진제, 플루오로알루미늄실리케이트, 리튬 알루미노 실리케이트 및 바륨 알루미노 실리케이트 중에서 선택된 1종 이상을 포함할 수 있다. Wherein the inorganic filler is selected from the group consisting of amorphous synthetic silica, crystalline natural silica, caroline, talc, quartz, barium glass, barium glass / silica mixture, quartz / barium mixture glass, zirconia / silica mixture, strontium aluminosilicate, acid reactive filler, A filler, a fluoroaluminum silicate, a lithium aluminosilicate, and a barium aluminosilicate.

상기 치과용 시멘트 조성물이 상기 폴리아크릴산계 공중합체 100 중량부에 대하여, 상기 무기필러 100 내지 500 중량부를 포함할 수 있다. The dental cement composition may include 100 to 500 parts by weight of the inorganic filler based on 100 parts by weight of the polyacrylic acid-based copolymer.

상기 치과용 시멘트 조성물이 라디칼 단량체를 추가로 포함할 수 있다. The dental cement composition may further comprise a radical monomer.

상기 라디칼 단량체가 트리에틸렌글리콜 디메타크릴레이트(TEGDMA), 메틸메타크릴레이트, 에틸렌글리콜 디메타크릴레이트(EGDMA), 디에틸렌글리콜 디메타크릴레이트(DEGDMA), 1,4-부탄디올 디메타크릴레이트, 1,6-헥산디올 디케타크릴레이트, 1-메틸-1,3-프로판디올 디메타크릴레이트, 폴리에틸렌 글라이콜 디메타크릴레이트(PEGDMA), 필로메리틱 디메타크릴레이트(PMDM), 2,2-비스-(4-(2-3-메타크릴로일옥시프로폭시)페닐)프로판(bis-GMA), 에콕실레이트 비스페놀 A 디메타크릴레이트(Bis-EMA), 우레탄 디메타크릴레이트(UDMA), 디펜타에릴트리톨 펜타아크릴레이트 모노페스페이트(dipentaerylthritol pentaacrylate monophosphate, PENTA), 2-하이드로에틸 메타크릴레이트(2-hydroethyl methacrylate, HEMA), 비페닐 디메타크릴레이트(biphenyl dimethacrylate, BPDM) 및 글리세롤 포스페이트 디메타크릴레이트(glycerol phosphate dimethacrylate, GPDM) 중에서 선택된 1종 이상을 포함할 수 있다. Wherein the radical monomer is selected from the group consisting of triethylene glycol dimethacrylate (TEGDMA), methyl methacrylate, ethylene glycol dimethacrylate (EGDMA), diethylene glycol dimethacrylate (DEGDMA), 1,4-butanediol dimethacrylate , 1-methyl-1,3-propanediol dimethacrylate, polyethylene glycol dimethacrylate (PEGDMA), phyllomeric dimethacrylate (PMDM), 1,6-hexanediol dimethacrylate, Bis-GMA), epoxylate bisphenol A dimethacrylate (Bis-EMA), urethane dimethacrylate (bis-ethyleneglycol bisacrylate) (UDMA), dipentaerythritol pentaacrylate monophosphate (PENTA), 2-hydroethyl methacrylate (HEMA), biphenyl dimethacrylate , BPDM) and glycerol phosphate dimethacrylate (glycerol phosphate dimethacrylate, GPDM).

상기 치과용 시멘트 조성물이 촉매를 추가로 포함할 수 있다. The dental cement composition may further comprise a catalyst.

상기 촉매가 타르타르산, p-톨루엔술핀산나트륨, 틴플루오라이드, 알루미늄옥살레이트, 틴포스페이트, 아이론옥살레이트, 틴옥사이드, 알루미늄클로라이드, 칼슘클로라이드, 소듐벤젠설피네이트, 소듐타이타늄플로오라이드, 트리에틸아민 및 페릭클로라이드 중에서 선택된 1종 이상을 포함할 수 있다. Wherein the catalyst is selected from the group consisting of tartaric acid, sodium p-toluenesulfinate, tin fluoride, aluminum oxalate, tin phosphate, iron oxalate, tin oxide, aluminum chloride, calcium chloride, sodium benzene sulfinate, sodium titanium fluoride, triethylamine And ferric chloride.

상기 치과용 시멘트 조성물이, 산과 화학반응을 하지 않는 무기필러를 포함하는 제1 페이스트;와 산과 화학반응을 하는 무기필러를 포함하는 제2 페이스트;의 조합으로 이루어질 수 있다. The dental cement composition may comprise a first paste containing an inorganic filler that does not chemically react with acid and a second paste including an inorganic filler that chemically reacts with acid.

상기 제2 페이스트가 비정질 합성 실리카 및 생체활성 바륨 글라스 중에서 선택된 1종 이상을 추가로 포함할 수 있다.The second paste may further include at least one selected from amorphous synthetic silica and bioactive barium glass.

상기 산과 화학반응을 할 수 있는 무기필러가 trivalent metla, oxygen, fluorine, alkaline earth metal, 및 silicon을 함유하는 무기필러이고, 바람직하게는 플루오르알루미늄실리케이트 글라스일 수 있다.The inorganic filler capable of chemically reacting with the acid is an inorganic filler containing trivalent meta, oxygen, fluorine, alkaline earth metal, and silicon, preferably a fluoroaluminum silicate glass.

상기 산과 화학반응을 하지 않는 무기필러가 비정질 합성 실리카, 결정성 천연실리카, 바륨 알루미늄 실리케이트 및 스트론튬 알루미늄 실리케이트 중에서 선택된 1종 이상일 수 있다. The inorganic filler which does not chemically react with the acid may be at least one selected from amorphous synthetic silica, crystalline natural silica, barium aluminum silicate and strontium aluminum silicate.

상기 제2 페이스트가 접착단량체를 추가로 포함할 수 있다. The second paste may further comprise an adhesive monomer.

상기 접착단량체가 2-히드록시에틸 메타크릴레이트, 4-메타크릴옥시에틸 트리메릴테이트 안히드라이드(4-Meta, 4-methacryloxyethyl trimellitate anhydride), 및 메타크릴옥시데실다이하이드로겐 포스페이트(10-MDP) 중에서 선택된 1종 이상일 수 있다. Wherein the adhesive monomer is selected from the group consisting of 2-hydroxyethyl methacrylate, 4-metha, 4-methacryloxyethyl trimellitate anhydride, and methacryloxydecyl dihydrogenphosphate (10-MDP ). ≪ / RTI >

본 발명의 다른 하나의 측면에 따르면, According to another aspect of the present invention,

상기 치과용 시멘트 조성물을 경화시켜 형성한 치과용 시멘트가 제공된다.There is provided a dental cement formed by curing the dental cement composition.

본 발명의 치과용 시멘트 조성물은 분자량이 조절된 폴리아크릴산-이타콘산 공중합체를 포함함으로써 경화 후 기계적 물성이 우수한 효과가 있다. The dental cement composition of the present invention contains a polyacrylic acid-itaconic acid copolymer having a controlled molecular weight, and thus has excellent mechanical properties after curing.

도 1은 제조예 5에 따라 제조된 폴리아크릴산-이타콘산 공중합체의 1H-NMR 원소 분석을 수행하여 그 결과를 나타낸 것이다.
도 2는 실시예 9 내지 16에 따라 제조된 치과용 시멘트의 접착강도를 나타낸 것이다.
도 3은 실시예 9 내지 16에 따라 제조된 치과용 시멘트의 압축강도를 나타낸 것이다.
1 shows the results of 1H-NMR elemental analysis of a polyacrylic acid-itaconic acid copolymer prepared according to Production Example 5.
Fig. 2 shows the adhesive strength of dental cements prepared according to Examples 9 to 16. Fig.
Fig. 3 shows the compressive strengths of the dental cements produced according to Examples 9 to 16. Fig.

이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 첨부된 도면을 참조하여 본 발명의 실시예를 상세히 설명하도록 한다. Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art can easily carry out the present invention.

그러나, 이하의 설명은 본 발명을 특정한 실시 형태에 대해 한정하려는 것이 아니며, 본 발명을 설명함에 있어서 관련된 공지 기술에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우 그 상세한 설명을 생략한다.However, the following description does not limit the present invention to specific embodiments. In the following description of the present invention, detailed description of related arts will be omitted if it is determined that the gist of the present invention may be blurred .

본원에서 사용한 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. The singular expressions include plural expressions unless the context clearly dictates otherwise. In the present application, the terms "comprises ", or" having ", and the like, specify that the presence of stated features, integers, steps, operations, elements, or combinations thereof, But do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, or combinations thereof.

이하, 본 발명의 치과용 시멘트 조성물에 대해 상세히 설명하도록 한다. Hereinafter, the dental cement composition of the present invention will be described in detail.

본 발명의 치과용 시멘트 조성물은 이타콘산계 단량체 및 아크릴산계 단량체를 공중합하여 제조된 폴리아크릴산계 공중합체; 및 무기필러;를 포함할 수 있다. The dental cement composition of the present invention comprises a polyacrylic acid-based copolymer prepared by copolymerizing an itaconic acid-based monomer and an acrylic acid-based monomer; And an inorganic filler.

상기 이타콘산계 단량체 및 아크릴산계 단량체의 중량비율을 조절하여 상기 폴리아크릴산계 공중합체의 중량평균분자량을 조절할 수 있으며, 이로 인해 상기 치과용 시멘트 조성물이 경화 후 기계적 물성이 향상될 수 있다. The weight average molecular weight of the polyacrylic acid copolymer can be controlled by controlling the weight ratio of the itaconic acid monomer and the acrylic acid monomer so that the mechanical properties of the dental cement composition after curing can be improved.

그러나, 상기 치과용 시멘트 조성물의 물성에 영향을 미치는 것은 상기 폴리아크릴산계 공중합체의 중량평균분자량이다.However, the weight-average molecular weight of the polyacrylic acid copolymer affects the physical properties of the dental cement composition.

상기 폴리아크릴산계 공중합체의 중량평균분자량(Mw)은 1,000 내지 120,000일 수 있고, 바람직하게는 25,000 내지 38,000, 더욱 바람직하게는 26,000 내지 36,500일 수 있다.The weight average molecular weight (Mw) of the polyacrylic acid-based copolymer may be 1,000 to 120,000, preferably 25,000 to 38,000, and more preferably 26,000 to 36,500.

상기 무기필러는 비정질 합성 실리카, 결정성 천연 실리카, 카롤린, 탈크, 석영, 바륨 글라스, 바륨 글라스/실리카 혼합물, 석영/바륨 혼합물 글라스, 지르코니아/실리카 혼합물, 스트론튬 알루미노 실리케이트, 산 반응성 충진제, 나노 지르코니아 충진제, 플루오로알루미늄실리케이트, 리튬 알루미노 실리케이트, 바륨 알루미노 실리케이트 등이 가능하나, 이들만으로 한정되는 것은 아니며, 경우에 따라서는, 이들의 혼합물의 형태로 사용될 수도 있다. The inorganic filler may be selected from the group consisting of amorphous synthetic silica, crystalline natural silica, caroline, talc, quartz, barium glass, barium glass / silica mixture, quartz / barium mixture glass, zirconia / silica mixture, strontium aluminosilicate, acid reactive filler, A filler, a fluoroaluminum silicate, a lithium aluminosilicate, a barium aluminosilicate, and the like, but the present invention is not limited thereto, and in some cases, it may be used in the form of a mixture thereof.

상기 치과용 시멘트 조성물은 상기 폴리아크릴산계 공중합체 100 중량부에 대하여, 상기 무기필러 100 내지 500 중량부를 포함할 수 있고, 바람직하게는 100 내지 400 중량부, 더욱 바람직하게는 120 내지 350 중량부를 포함할 수 있다.The dental cement composition may include 100 to 500 parts by weight, preferably 100 to 400 parts by weight, more preferably 120 to 350 parts by weight of the inorganic filler per 100 parts by weight of the polyacrylic acid copolymer can do.

상기 치과용 시멘트 조성물은 희석제로서 라디칼 단량체를 추가로 포함할 수 있으며, 상기 라디칼 단량체는 트리에틸렌글리콜 디메타크릴레이트(TEGDMA), 메틸메타크릴레이트, 에틸렌글리콜 디메타크릴레이트(EGDMA), 디에틸렌글리콜 디메타크릴레이트(DEGDMA), 1,4-부탄디올 디메타크릴레이트, 1,6-헥산디올 디케타크릴레이트, 1-메틸-1,3-프로판디올 디메타크릴레이트, 폴리에틸렌 글라이콜 디메타크릴레이트(PEGDMA), 필로메리틱 디메타크릴레이트(PMDM), 2,2-비스-(4-(2-3-메타크릴로일옥시프로폭시)페닐)프로판(bis-GMA), 에콕실레이트 비스페놀 A 디메타크릴레이트(Bis-EMA), 우레탄 디메타크릴레이트(UDMA), 디펜타에릴트리톨 펜타아크릴레이트 모노페스페이트(dipentaerylthritol pentaacrylate monophosphate, PENTA), 2-하이드로에틸 메타크릴레이트(2-hydroethyl methacrylate, HEMA), 비페닐 디메타크릴레이트(biphenyl dimethacrylate, BPDM), 글리세롤 포스페이트 디메타크릴레이트(glycerol phosphate dimethacrylate, GPDM) 등일 수 있다. The dental cement composition may further include a radical monomer as a diluent, wherein the radical monomer is selected from the group consisting of triethylene glycol dimethacrylate (TEGDMA), methyl methacrylate, ethylene glycol dimethacrylate (EGDMA), diethylene Glycol dimethacrylate (DEGDMA), 1,4-butanediol dimethacrylate, 1,6-hexanediol diketacrylate, 1-methyl-1,3-propanediol dimethacrylate, polyethylene glycol di Methacrylate (PEGDMA), phyllomeric dimethacrylate (PMDM), 2,2-bis- (4- (2-3-methacryloyloxypropoxy) phenyl) (UAE), dipentaerythritol pentaacrylate monophosphate (PENTA), 2-hydro-ethyl methacrylate (UAE), and the like. (2-hydroethyl methacrylate, HEMA), biphenyl Biphenyl dimethacrylate (BPDM), glycerol phosphate dimethacrylate (GPDM), and the like.

상기 치과용 시멘트 조성물이 촉매를 추가로 포함할 수 있고, 상기 촉매는 타르타르산, p-톨루엔술핀산나트륨, 틴플루오라이드, 알루미늄옥살레이트, 틴포스페이트, 아이론옥살레이트, 틴옥사이드, 알루미늄클로라이드, 칼슘클로라이드, 소듐벤젠설피네이트, 소듐타이타늄플로오라이드, 트리에틸아민, 페릭클로라이드 등일 수 있다. The dental cement composition may further comprise a catalyst, wherein the catalyst is selected from the group consisting of tartaric acid, sodium p-toluenesulfinate, tin fluoride, aluminum oxalate, tin phosphate, iron oxalate, tin oxide, aluminum chloride, calcium chloride , Sodium benzene sulfinate, sodium titanium fluoride, triethylamine, ferric chloride, and the like.

상기 촉매는 화학중합 촉매 또는 광중합 촉매 중 어느 하나일 수 있다. The catalyst may be either a chemical polymerization catalyst or a photopolymerization catalyst.

상기 치과용 시멘트 조성물은, 바람직하게는 산과 화학반응을 하지 않는 무기필러를 포함하는 제1 페이스트;와 산과 화학반응을 하는 무기필러를 포함하는 제2 페이스트;의 조합으로 이루어질 수 있다. The dental cement composition may be composed of a combination of a first paste including an inorganic filler that does not chemically react with acid, and a second paste including an inorganic filler that chemically reacts with acid.

상기 제2 페이스트는 비정질 합성 실리카 및 생체활성 바륨 글라스 중에서 선택된 1종 이상을 추가로 포함할 수 있다.The second paste may further include at least one selected from amorphous synthetic silica and bioactive barium glass.

상기 산과 화학반응을 하는 무기필러로서 trivalent metla, oxygen, fluorine, alkaline earth metal, 및 silicon을 함유하는 무기필러를 사용할 수 있고, 바람직하게는 플루오르알루미늄실리케이트 글라스를 사용할 수 있다.An inorganic filler containing trivalent meta, oxygen, fluorine, alkaline earth metal, and silicon may be used as an inorganic filler that chemically reacts with the acid, preferably a fluoroaluminum silicate glass.

상기 산과 화학반응을 하지 않는 무기필러로서 비정질 합성 실리카, 결정성 천연실리카, 바륨 알루미늄 실리케이트 또는 스트론튬 알루미늄 실리케이트를 사용할 수 있다.As the inorganic filler which does not chemically react with the acid, amorphous synthetic silica, crystalline natural silica, barium aluminum silicate or strontium aluminum silicate can be used.

상기 제2 페이스트는 접착단량체를 추가로 포함할 수 있고, 상기 접착단량체는 2-히드록시에틸 메타크릴레이트, 4-메타크릴옥시에틸 트리메릴테이트 안히드라이드(4-Meta, 4-methacryloxyethyl trimellitate anhydride), 메타크릴옥시데실다이하이드로겐 포스페이트(10-MDP) 등이 가능하다.The second paste may further comprise an adhesive monomer, wherein the adhesive monomer is selected from the group consisting of 2-hydroxyethyl methacrylate, 4-methacryloxyethyl trimellitate anhydride (4-methacryloxyethyl trimellitate anhydride ), Methacryloyldodecyl dihydrogenphosphate (10-MDP), and the like.

[실시예][Example]

이하, 본 발명의 바람직한 실시예를 들어 설명하도록 한다. 그러나 이는 예시를 위한 것으로서 이에 의하여 본 발명의 범위가 한정되는 것은 아니다.Hereinafter, preferred embodiments of the present invention will be described. However, this is for illustrative purposes only, and thus the scope of the present invention is not limited thereto.

제조예Manufacturing example 1:  One: 폴리아크릴산Polyacrylic acid -- 이타콘산Itaconic acid 공중합체의 제조 Preparation of Copolymer

아크릴산(7.34 wt%, Sigma Aldrich), 이타콘산(41.56 wt%, Sigma Aldrich), AIBN(3 wt%, azobisisobutyronitrile, Sigma Aldrich), THF(36.5 wt%, tetara hydrofuran, 대정화금) 및 2-프로판올(11.6 wt%, 대정화금)을 이중자켓 반응기에 넣고, 질소분위기 하에서 60℃까지 온도를 서서히 올려 중합시켰다. 다음으로, 디에틸에테르(diethyl ether, 대정화금)로 침전시킨 후 세척하는 과정을 반복하고, 40℃의 오븐에서 밤새 건조시켜 중량평균분자량(Mw)이 12,000인 폴리아크릴산-이타콘산 공중합체를 제조하였다.(3 wt%, azobisisobutyronitrile, Sigma Aldrich), THF (36.5 wt%, tetara hydrofuran, purified gold), and 2-propanol (3,3 wt%, Sigma Aldrich), itaconic acid (41.56 wt%, Sigma Aldrich) (11.6 wt%, purified water) was placed in a double-jacketed reactor, and the temperature was gradually raised to 60 ° C under a nitrogen atmosphere to polymerize. Next, the process of precipitating with diethyl ether and washing was repeated and dried in an oven at 40 ° C. overnight to obtain a polyacrylic acid-itaconic acid copolymer having a weight average molecular weight (M w ) of 12,000 .

제조예 2: 폴리아크릴산-이타콘산 공중합체의 제조Production Example 2: Production of polyacrylic acid-itaconic acid copolymer

아크릴산과 이타콘산의 함량비를 7.34:41.56 대신에 27.87:21.03으로 한 것을 제외하고는 제조예 1과 동일한 방법으로 중량평균분자량(Mw)이 24,000인 폴리아크릴산-이타콘산 공중합체를 제조하였다.A polyacrylic acid-itaconic acid copolymer having a weight average molecular weight (M w ) of 24,000 was prepared in the same manner as in Preparation Example 1, except that the content ratio of acrylic acid and itaconic acid was changed to 27.87: 21.03 instead of 7.34: 41.56.

제조예 3: 폴리아크릴산-이타콘산 공중합체의 제조Production Example 3: Production of polyacrylic acid-itaconic acid copolymer

아크릴산과 이타콘산의 함량비를 7.34:41.56 대신에 31.80:17.10으로 한 것을 제외하고는 제조예 1과 동일한 방법으로 중량평균분자량(Mw)이 26,000인 폴리아크릴산-이타콘산 공중합체를 제조하였다.A polyacrylic acid-itaconic acid copolymer having a weight average molecular weight (M w ) of 26,000 was prepared in the same manner as in Preparation Example 1, except that the content ratio of acrylic acid and itaconic acid was changed to 31.80: 17.10 instead of 7.34: 41.56.

제조예 4: 폴리아크릴산-이타콘산 공중합체의 제조Preparation Example 4: Preparation of polyacrylic acid-itaconic acid copolymer

아크릴산과 이타콘산의 함량비를 7.34:41.56 대신에 40.1:8.80으로 한 것을 제외하고는 제조예 1과 동일한 방법으로 중량평균분자량(Mw)이 28,500인 폴리아크릴산-이타콘산 공중합체를 제조하였다.A polyacrylic acid-itaconic acid copolymer having a weight average molecular weight (M w ) of 28,500 was prepared in the same manner as in Preparation Example 1, except that the content ratio of acrylic acid and itaconic acid was changed to 40.1: 8.80 instead of 7.34: 41.56.

제조예 5: 폴리아크릴산-이타콘산 공중합체의 제조Preparation Example 5: Preparation of polyacrylic acid-itaconic acid copolymer

아크릴산과 이타콘산의 함량비를 7.34:41.56 대신에 34.23:14.67로 한 것을 제외하고는 제조예 1과 동일한 방법으로 중량평균분자량(Mw)이 29,000인 폴리아크릴산-이타콘산 공중합체를 제조하였다.A polyacrylic acid-itaconic acid copolymer having a weight average molecular weight (M w ) of 29,000 was prepared in the same manner as in Preparation Example 1, except that the content ratio of acrylic acid and itaconic acid was changed to 34.23: 14.67 instead of 7.34: 41.56.

제조예 6: 폴리아크릴산-이타콘산 공중합체의 제조Production Example 6: Preparation of polyacrylic acid-itaconic acid copolymer

아크릴산과 이타콘산의 함량비를 7.34:41.56 대신에 33.25:15.65로 한 것을 제외하고는 제조예 1과 동일한 방법으로 중량평균분자량(Mw)이 36,500인 폴리아크릴산-이타콘산 공중합체를 제조하였다.A polyacrylic acid-itaconic acid copolymer having a weight average molecular weight (M w ) of 36,500 was prepared in the same manner as in Preparation Example 1, except that the content ratio of acrylic acid and itaconic acid was changed to 33.25: 15.65 instead of 7.34: 41.56.

제조예 7: 폴리아크릴산-이타콘산 공중합체의 제조Production Example 7: Preparation of polyacrylic acid-itaconic acid copolymer

아크릴산과 이타콘산의 함량비를 7.34:41.56 대신에 39.12:9.78로 한 것을 제외하고는 제조예 1과 동일한 방법으로 중량평균분자량(Mw)이 39,500인 폴리아크릴산-이타콘산 공중합체를 제조하였다.A polyacrylic acid-itaconic acid copolymer having a weight average molecular weight (M w ) of 39,500 was prepared in the same manner as in Preparation Example 1, except that the content ratio of acrylic acid and itaconic acid was changed to 39.12: 9.78 instead of 7.34: 41.56.

제조예 8: 폴리아크릴산-이타콘산 공중합체의 제조Production Example 8: Preparation of polyacrylic acid-itaconic acid copolymer

아크릴산과 이타콘산의 함량비를 7.34:41.56 대신에 44.01:4.89로 한 것을 제외하고는 제조예 1과 동일한 방법으로 중량평균분자량(Mw)이 46,000인 폴리아크릴산-이타콘산 공중합체를 제조하였다.The content ratio of acrylic acid and itaconic acid, 7.34: 44.01 instead of 41.56: and has a weight average molecular weight (M w) is 46,000 in the polyacrylic acid in the same manner as in Preparation Example 1 except that the 4.89 was prepared itaconic acid copolymer.

제조예 9: 폴리아크릴산-말레이산 공중합체의 제조Production Example 9: Preparation of polyacrylic acid-maleic acid copolymer

이타콘산 대신에 말레이산을 사용하고, 아크릴산과 말레이산의 함량비를 14.6:34.3으로 한 것을 제외하고는 제조예 1과 동일한 방법으로 중량평균분자량(Mw)이 18,000인 폴리아크릴산-말레이산 공중합체를 제조하였다.Maleic acid copolymer having a weight average molecular weight (M w ) of 18,000 was obtained in the same manner as in Production Example 1 except that maleic acid was used instead of itaconic acid and the content ratio of acrylic acid and maleic acid was changed to 14.6: Lt; / RTI >

하기 표 1에 제조예 1 내지 9에 따른 공중합체의 제조에 사용된 물질과 그의 사용량 및 공중합체의 분자량을 나타내었다. The materials used in the preparation of the copolymers according to Preparation Examples 1 to 9 and their amounts used and the molecular weights of the copolymers are shown in Table 1 below.

성분ingredient 역할role 함량(중량%)Content (% by weight) 제조예 1Production Example 1 제조예 2Production Example 2 제조예 3Production Example 3 제조예 4Production Example 4 제조예 5Production Example 5 제조예 6Production Example 6 제조예 7Production Example 7 제조예 8Production Example 8 제조예 9Production Example 9 아크릴산Acrylic acid 모노머Monomer 7.347.34 27.8727.87 31.8031.80 40.140.1 34.2334.23 33.2533.25 39.1239.12 44.0144.01 14.614.6 이타콘산Itaconic acid 모노머Monomer 41.5641.56 21.0321.03 17.1017.10 8.88.8 14.6714.67 15.6515.65 9.789.78 4.894.89 34.334.3 말레이산Malaysian 모노머Monomer 00 00 00 00 00 00 00 00 34.334.3 2-프로판올2-propanol 용매menstruum 11.611.6 11.611.6 11.611.6 11.611.6 11.611.6 11.611.6 11.611.6 11.611.6 11.611.6 THFTHF 용매menstruum 36.536.5 36.536.5 36.536.5 36.536.5 36.536.5 36.536.5 36.536.5 36.536.5 36.536.5 AIBNAIBN 개시제Initiator 33 33 33 33 33 33 33 33 33 합계Sum 100100 100100 100100 100100 100100 100100 100100 100100 100100 중량평균분자량Weight average molecular weight 12,00012,000 24,00024,000 26,00026,000 28,50028,500 29,00029,000 36,50036,500 39,50039,500 46,00046,000 18,00018,000 분자량 분포Molecular weight distribution 1.421.42 1.661.66 1.541.54 1.521.52 1.481.48 1.871.87 1.941.94 2.102.10 1.681.68

실시예Example 1: 치과용 시멘트 조성물의 제조 1: Preparation of dental cement composition

제조예 1에 따라 제조된 폴리아크릴산-이타콘산 공중합체, 용매인 증류수, 모노머인 폴리에틸렌글리콜 디메타크릴레이트(PEGDMA), 충전제인 바륨필러(입자 크기 3㎛), 타르타르산(tartaric acid), 촉매인 p-톨루엔술핀산나트륨(sodium p-toluenesulfinate), 촉매인 틴플루오라이드(tin fluoride), 지연제인 메톡시페놀(MEHQ) 및 산화방지제인 뷰틸레이트하이드록시톨루엔(BHT)을 혼합하여 제1 페이스트를 제조하였다.(Polyethylene glycol dimethacrylate (PEGDMA) as a monomer, barium filler as a filler (particle size: 3 탆), tartaric acid, a catalyst, and the like, which were prepared in accordance with Preparation Example 1, a polyacrylic acid-itaconic acid copolymer, distilled water as a solvent, A first paste was prepared by mixing sodium p -toluenesulfinate, a catalyst tin fluoride, a retarding agent methoxyphenol (MEHQ) and an antioxidant butylated hydroxytoluene (BHT) .

충전제인 글라스분말조성물(Specialty Glass Inc.), 접착단량체인 2-히드록시에틸 메타크릴레이트(2-hydroxyethyl methacrylate, HEMA), 희석제인 트리에틸렌글리콜 디메트릴레이트(TGEDMA), 모노머인 2,2-비스-(4-(3-메타크릴옥시-2-히드록시프로폭시)페닐프로판(Bis-GMA), 모노머인 우레탄 디메타크릴레이트(UDMA), 촉매인 알루미늄옥살레이트(aluminum oxalate), 충전제인 비정질 합성 실리카(TS530), 지연제인 메톡시페놀(MEHQ), 산화방지제인 뷰틸레이트하이드록시톨루엔(BHT) 및 조색제인 빨간 색소(산화철)와 노란 색소(산화철)를 혼합하여 제2 페이스트를 제조하였다. 2-hydroxyethyl methacrylate (HEMA) as a filler, triethylene glycol dimethacrylate (TGEDMA) as a diluent, 2,2-bis (2-hydroxyethyl methacrylate) (UDMA), which is a monomer, aluminum oxalate, a filler, and the like, which are used in the present invention, (II), amorphous synthetic silica (TS530), retarding agent methoxyphenol (MEHQ), antioxidant butylated hydroxytoluene (BHT), and red pigment (iron oxide) Respectively.

상기 글라스분말조성물은 칼슘 플루오르알루미노실리케이트 글라스를 의미하며 조성비(무게비)는 SiO2 30~40%, Al2O3 20~30%, AlF3 1~3%, CaF2 15~20%, NaF 3~10% 및 AlPO4 3~12%이다. The glass powder composition refers to calcium fluoroaluminosilicate glass. The composition ratio (weight ratio) is 30 to 40% of SiO 2 , 20 to 30% of Al 2 O 3 , 1 to 3% of AlF 3 , 15 to 20% of CaF 2 , 3 to 10% and AlPO 4 3 to 12%.

상기 제1 페이스트 및 제2 페이스트를 1:1.6의 함량 비율로 혼합하여 치과용 시멘트 조성물을 제조하였다.The first paste and the second paste were mixed at a ratio of 1: 1.6 to prepare a dental cement composition.

하기 표 2에 실시예 1에 따른 제1 페이스트의 제조에 사용된 물질 및 그의 사용량을, 표 3에 실시예 1에 따른 제2 페이스트의 제조에 사용된 물질 및 그의 사용량을 나타내었다. Table 2 shows the materials used in the preparation of the first paste according to Example 1 and the amounts used thereof, and Table 3 shows the materials used in the production of the second paste according to Example 1 and the amounts used thereof.

성분(제1 페이스트)Component (first paste) 함량(중량%)Content (% by weight) 폴리아크릴산-이타콘산 공중합체(제조예 1)Polyacrylic acid-itaconic acid copolymer (Production Example 1) 3535 증류수Distilled water 3535 폴리에틸렌글리콜 디메타크릴레이트(PEGDMA)Polyethylene glycol dimethacrylate (PEGDMA) 44 바륨필러Barium filler 1818 타르타르산(tartaric acid)Tartaric acid 55 p-톨루엔술핀산나트륨sodium p-toluenesulfinate 2.022.02 틴플루오라이드Tin fluoride 0.970.97 메톡시페놀Methoxyphenol 0.0040.004 뷰틸레이트하이드록시톨루엔Butylate Hydroxytoluene 0.0060.006 총 계sum 100100

성분(제2 페이스트)Component (second paste) 함량(중량%)Content (% by weight) 글라스분말조성물Glass powder composition 69.169.1 2-히드록시에틸 메타크릴레이트2-hydroxyethyl methacrylate 13.313.3 트리에틸렌글리콜 디메트릴레이트Triethylene glycol dimethacrylate 5.565.56 2,2-비스-(4-(3-메타크릴옥시-2-히드록시프로폭시)페닐프로판(Bis-GMA)(Bis-GMA), 2,2-bis- (4- (3-methacryloxy-2-hydroxypropoxy) 22 우레탄 디메타크릴레이트Urethane dimethacrylate 8.518.51 알루미늄옥살레이트Aluminum oxalate 0.30.3 비정질 합성 실리카(TS530)Amorphous synthetic silica (TS530) 1.21.2 메톡시페놀(MEHQ)Methoxyphenol (MEHQ) 0.0040.004 뷰틸레이트하이드록시톨루엔Butylate Hydroxytoluene 0.0060.006 조색제Colorant 0.020.02 총 계sum 100100

실시예Example 2: 치과용 시멘트 조성물의 제조 2: Preparation of dental cement composition

제조예 1에 따라 제조된 폴리아크릴산-이타콘산 공중합체 대신에 제조예 2에 따라 제조된 폴리아크릴산-이타콘산 공중합체를 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 치과용 시멘트 조성물을 제조하였다.A dental cement composition was prepared in the same manner as in Example 1, except that the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 2 was used instead of the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 1 .

실시예Example 3: 치과용 시멘트 조성물의 제조 3: Preparation of dental cement composition

제조예 1에 따라 제조된 폴리아크릴산-이타콘산 공중합체 대신에 제조예 3에 따라 제조된 폴리아크릴산-이타콘산 공중합체를 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 치과용 시멘트 조성물을 제조하였다.A dental cement composition was prepared in the same manner as in Example 1, except that the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 3 was used instead of the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 1 .

실시예Example 4: 치과용 시멘트 조성물의 제조 4: Preparation of dental cement composition

제조예 1에 따라 제조된 폴리아크릴산-이타콘산 공중합체 대신에 제조예 4에 따라 제조된 폴리아크릴산-이타콘산 공중합체를 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 치과용 시멘트 조성물을 제조하였다.A dental cement composition was prepared in the same manner as in Example 1, except that the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 4 was used instead of the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 1 .

실시예Example 5: 치과용 시멘트 조성물의 제조 5: Preparation of dental cement composition

제조예 1에 따라 제조된 폴리아크릴산-이타콘산 공중합체 대신에 제조예 5에 따라 제조된 폴리아크릴산-이타콘산 공중합체를 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 치과용 시멘트 조성물을 제조하였다.A dental cement composition was prepared in the same manner as in Example 1, except that the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 5 was used instead of the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 1 .

실시예Example 6: 치과용 시멘트 조성물의 제조 6: Preparation of dental cement composition

제조예 1에 따라 제조된 폴리아크릴산-이타콘산 공중합체 대신에 제조예 6에 따라 제조된 폴리아크릴산-이타콘산 공중합체를 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 치과용 시멘트 조성물을 제조하였다.A dental cement composition was prepared in the same manner as in Example 1, except that the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 6 was used instead of the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 1 .

실시예Example 7: 치과용 시멘트 조성물의 제조 7: Preparation of dental cement composition

제조예 1에 따라 제조된 폴리아크릴산-이타콘산 공중합체 대신에 제조예 7에 따라 제조된 폴리아크릴산-이타콘산 공중합체를 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 치과용 시멘트 조성물을 제조하였다.A dental cement composition was prepared in the same manner as in Example 1, except that the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 7 was used instead of the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 1 .

실시예Example 8: 치과용 시멘트 조성물의 제조 8: Preparation of dental cement composition

제조예 1에 따라 제조된 폴리아크릴산-이타콘산 공중합체 대신에 제조예 8에 따라 제조된 폴리아크릴산-이타콘산 공중합체를 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 치과용 시멘트 조성물을 제조하였다.A dental cement composition was prepared in the same manner as in Example 1, except that the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 8 was used instead of the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 1 .

실시예Example 9: 치과용 시멘트 조성물의 제조 9: Preparation of dental cement composition

실시예 1에 따라 제조된 치과용 시멘트 조성물을 경화시켜 치과용 시멘트를 제조하였다.The dental cement composition prepared according to Example 1 was cured to prepare a dental cement.

실시예Example 10: 치과용 시멘트의 제조 10: Manufacture of dental cement

실시예 2에 따라 제조된 치과용 시멘트 조성물을 경화시켜 치과용 시멘트를 제조하였다.The dental cement composition prepared according to Example 2 was cured to prepare a dental cement.

실시예Example 11: 치과용 시멘트의 제조 11: Manufacture of dental cement

실시예 3에 따라 제조된 치과용 시멘트 조성물을 경화시켜 치과용 시멘트를 제조하였다.The dental cement composition prepared according to Example 3 was cured to prepare a dental cement.

실시예Example 12: 치과용 시멘트의 제조 12: Manufacture of dental cement

실시예 4에 따라 제조된 치과용 시멘트 조성물을 경화시켜 치과용 시멘트를 제조하였다.The dental cement composition prepared according to Example 4 was cured to prepare a dental cement.

실시예Example 13: 치과용 시멘트의 제조 13: Manufacture of dental cement

실시예 5에 따라 제조된 치과용 시멘트 조성물을 경화시켜 치과용 시멘트를 제조하였다.The dental cement composition prepared according to Example 5 was cured to prepare a dental cement.

실시예Example 14: 치과용 시멘트의 제조 14: Manufacture of dental cement

실시예 6에 따라 제조된 치과용 시멘트 조성물을 경화시켜 치과용 시멘트를 제조하였다.The dental cement composition prepared according to Example 6 was cured to prepare a dental cement.

실시예Example 15: 치과용 시멘트의 제조 15: Manufacture of dental cement

실시예 7에 따라 제조된 치과용 시멘트 조성물을 경화시켜 치과용 시멘트를 제조하였다.The dental cement composition prepared according to Example 7 was cured to prepare a dental cement.

실시예Example 16: 치과용 시멘트의 제조 16: Manufacture of dental cement

실시예 8에 따라 제조된 치과용 시멘트 조성물을 경화시켜 치과용 시멘트를 제조하였다.The dental cement composition prepared according to Example 8 was cured to prepare a dental cement.

비교예Comparative Example 1: 치과용 시멘트 조성물의 제조 1: Preparation of dental cement composition

제조예 1에 따라 제조된 폴리아크릴산-이타콘산 공중합체 대신에 제조예 9에 따라 제조된 폴리아크릴-말레이산 공중합체를 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 치과용 시멘트 조성물을 제조하였다.A dental cement composition was prepared in the same manner as in Example 1, except that the polyacrylic-maleic acid copolymer prepared in Preparation Example 9 was used instead of the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 1 .

비교예Comparative Example 2: 치과용 시멘트 조성물의 제조 2: Preparation of dental cement composition

제조예 1에 따라 제조된 폴리아크릴산-이타콘산 공중합체 대신에 폴리아크릴산(Mw 5,000g/mol, Sigma Aldrich)을 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 치과용 시멘트 조성물을 제조하였다.A dental cement composition was prepared in the same manner as in Example 1, except that polyacrylic acid (Mw 5,000 g / mol, Sigma Aldrich) was used instead of the polyacrylic acid-itaconic acid copolymer prepared in Preparation Example 1.

비교예Comparative Example 3: 치과용 시멘트의 제조 3: Manufacture of dental cement

비교예 1에 따라 제조된 치과용 시멘트 조성물을 경화시켜 치과용 시멘트를 제조하였다.The dental cement composition prepared according to Comparative Example 1 was cured to prepare a dental cement.

비교예Comparative Example 4: 치과용 시멘트의 제조 4: Manufacture of dental cement

비교예 2에 따라 제조된 치과용 시멘트 조성물을 경화시켜 치과용 시멘트를 제조하였다.The dental cement composition prepared according to Comparative Example 2 was cured to prepare a dental cement.

[시험예][Test Example]

시험예Test Example 1:  One: 폴리아크릴산Polyacrylic acid -- 이타콘산Itaconic acid 공중합체 확인 Copolymer identification

도 1은 제조예 5에 따라 제조된 폴리아크릴산-이타콘산 공중합체의 1H-NMR 원소 분석을 수행하여 그 결과를 나타낸 것이다.FIG. 1 shows the results of 1H-NMR elemental analysis of the polyacrylic acid-itaconic acid copolymer prepared in Production Example 5.

1H NMR 데이터를 분석하여 폴리아크릴산-이타콘산 공중합체가 제조된 것을 확인하였고, 구체적인 하나의 예로서 도 1을 참조하면 제조예 5에 따라 폴리아크릴산-이타콘산 공중합체가 제조된 것을 확인할 수 있었다. 1 H NMR data were analyzed to confirm that the polyacrylic acid-itaconic acid copolymer was prepared. Referring to FIG. 1 as a specific example, it was confirmed that the polyacrylic acid-itaconic acid copolymer was prepared according to Production Example 5.

시험예Test Example 2: 치과용 시멘트 조성물 및 치과용 시멘트의 특성 분석 2: Characterization of dental cement composition and dental cement

도 2는 실시예 9 내지 16에 따라 제조된 치과용 시멘트의 접착강도를 나타낸 것이고, 도 3은 실시예 9 내지 16에 따라 제조된 치과용 시멘트의 압축강도를 나타낸 것이고, 표 4는 실시예 1 내지 8, 비교예 1 및 2에 따라 제조된 치과용 시멘트 조성물의 경화 시간, 실시예 9 내지 16, 비교예 3 및 4에 따라 제조된 치과용 시멘트의 압축 강도 및 접착 강도를 측정하여 그 결과를 나타낸 것이다. Fig. 2 shows the adhesive strength of the dental cements produced according to Examples 9 to 16, Fig. 3 shows the compressive strength of the dental cements produced according to Examples 9 to 16, The compression strength and the adhesive strength of the dental cement prepared according to Examples 9 to 16 and Comparative Examples 3 and 4 were measured, .

압축강도는 ISO 9917-1에 따라, 실시예 9 내지 16, 비교예 3 및 4에 따라 제조된 치과용 시멘트를 37℃의 생리식염수에 24시간 동안 침지한 후, 인스트론 시험기(Shimadzu 일본, Autograph AGS-X)에서 분당 1mm의 속도로 하중을 가하여 시편이 파괴될 때의 하중을 측정하고, 5번 측정한 평균값을 아래 표 4에 기재하였다.The dental cements prepared according to Examples 9 to 16 and Comparative Examples 3 and 4 were dipped in physiological saline at 37 占 폚 for 24 hours in accordance with ISO 9917-1 for compressive strength and then dipped in an Instron tester (Shimadzu Japan, Autograph AGS-X) at a rate of 1 mm per minute to measure the load when the specimen was broken, and the average value measured five times is shown in Table 4 below.

접착강도는 ISO 11405에 따라, 치아 시편을 교합면에 평행하게 일정한 두께로 자른 후, 실시예 1 내지 8, 비교예 1 및 2에 따라 제조된 치과용 시멘트 조성물을 혼합한 후, 경화시켜 얻어진 시편을 온도 37℃의 생리식염수에 24시간 동안 침지한 후 인스트론 시험기(Shimadzu 일본, Autograph AGS-X)에서 분당 0.75mm의 속도로 하중을 가하여 측정하고, 5번 측정한 평균값을 아래 표 4에 기재하였다.The adhesive strength was measured in accordance with ISO 11405 by cutting the tooth specimens to a predetermined thickness parallel to the occlusal surface, mixing the dental cement compositions prepared according to Examples 1 to 8 and Comparative Examples 1 and 2, Was immersed in physiological saline at 37 DEG C for 24 hours, and then subjected to a load at a rate of 0.75 mm per minute in an Instron tester (Shimadzu Japan, Autograph AGS-X). The average value measured five times was shown in Table 4 Respectively.

구분division 실시예 1Example 1 실시예 2Example 2 실시예 3Example 3 실시예 4Example 4 실시예 5Example 5 실시예 6Example 6 실시예 7Example 7 실시예 8Example 8 비교예 1Comparative Example 1 비교예 2Comparative Example 2 경화 시간Curing time 8'20"8'20 " 5'20"5'20 " 4'50"4'50 " 5'15"5'15 " 5'00"5'00 " 4'45"4'45 " 7'15"7'15 " 5'40"5'40 " 6'30"6'30 " 7'00"7'00 " 구분division 실시예 9Example 9 실시예 10Example 10 실시예 11Example 11 실시예 12Example 12 실시예 13Example 13 실시예 14Example 14 실시예 15Example 15 실시예 16Example 16 비교예 3Comparative Example 3 비교예 4Comparative Example 4 압축 강도
[MPa]
Compressive strength
[MPa]
51.351.3 57.957.9 117.5117.5 116.4116.4 120.6120.6 106.2106.2 72.372.3 45.645.6 37.937.9 56.256.2
접착 강도
[MPa]
Adhesive strength
[MPa]
0.560.56 1.781.78 3.293.29 3.453.45 3.513.51 2.642.64 0.790.79 0.460.46 0.550.55 0.460.46

도 2 및 도 3을 참조하면, 본 발명의 치과용 시멘트는 중량평균분자량이 26,000 내지 36,500일 때 약 2배 이상 접착강도가 높아 임계적 의의를 갖는 것을 알 수 있었다. 압축강도 또한 중량평균분자량이 26,000 내지 36,500인 실시예 11 내지 14에 따라 제조된 치과용 시멘트가 약 100MPa 이상의 2배 이상 높은 압축강도를 나타내었다. 이에 비하여, 치과용 시멘트에 포함된 폴리아크릴산-이타콘산 공중합체의 아크릴산 함량과 이타콘산 함량의 비율은 치과용 시멘트의 접착강도에 유의미한 영향을 미치지 않는 것으로 판단된다. Referring to FIGS. 2 and 3, it can be seen that the dental cement of the present invention has a critical significance because its adhesive strength is twice or more when the weight average molecular weight is 26,000 to 36,500. The dental cements produced according to Examples 11 to 14, which had a compressive strength and a weight average molecular weight of 26,000 to 36,500, exhibited a compressive strength of at least two times higher than about 100 MPa. In contrast, the ratio of acrylic acid and itaconic acid content of the polyacrylic acid-itaconic acid copolymer contained in the dental cement did not significantly affect the adhesive strength of the dental cement.

표 4를 참조하면, 실시예 11 내지 14에 따라 제조된 치과용 시멘트는 비교예 3 및 4에 따라 제조된 치과용 시멘트에 비해 접착강도는 5배이상 높은 것으로 나타났다. Referring to Table 4, the dental cements produced according to Examples 11 to 14 exhibited an adhesive strength five times higher than the dental cements prepared according to Comparative Examples 3 and 4.

따라서, 중량평균분자량이 26,000 내지 36,500인 실시예 11 내지 14에 따라 제조된 치과용 시멘트가 물성이 다른 중량평균분자량을 갖는 치과용 시멘트 보다 매우 우수한 것을 알 수 있었다. Thus, it can be seen that the dental cements prepared according to Examples 11 to 14 having a weight average molecular weight of 26,000 to 36,500 are far superior to dental cements having different weight average molecular weights.

본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위의 의미 및 범위 그리고 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.The scope of the present invention is defined by the appended claims rather than the detailed description and all changes or modifications derived from the meaning and scope of the claims and their equivalents are to be construed as being included within the scope of the present invention do.

Claims (18)

이타콘산계 단량체 및 아크릴산계 단량체를 공중합하여 제조된 폴리아크릴산계 공중합체; 및
무기필러;를
포함하는 치과용 시멘트 조성물.
A polyacrylic acid-based copolymer prepared by copolymerizing an itaconic acid-based monomer and an acrylic acid-based monomer; And
Inorganic filler;
≪ / RTI >
제1항에 있어서,
상기 폴리아크릴산계 공중합체의 중량평균분자량(Mw)이 1,000 내지 120,000인 것을 특징으로 하는 치과용 시멘트 조성물.
The method according to claim 1,
Wherein the polyacrylic acid-based copolymer has a weight average molecular weight (Mw) of 1,000 to 120,000.
제2항에 있어서,
상기 폴리아크릴산계 공중합체의 중량평균분자량(Mw)이 25,000 내지 38,000인 것을 특징으로 하는 치과용 시멘트 조성물.
3. The method of claim 2,
Wherein the polyacrylic acid-based copolymer has a weight average molecular weight (Mw) of 25,000 to 38,000.
제3항에 있어서,
상기 폴리아크릴산계 공중합체의 중량평균분자량(Mw)이 26,000 내지 36,500인 것을 특징으로 하는 치과용 시멘트 조성물.
The method of claim 3,
Wherein the polyacrylic acid-based copolymer has a weight average molecular weight (Mw) of 26,000 to 36,500.
제1항에 있어서,
상기 무기필러가 비정질 합성 실리카, 결정성 천연 실리카, 카롤린, 탈크, 석영, 바륨 글라스, 바륨 글라스/실리카 혼합물, 석영/바륨 혼합물 글라스, 지르코니아/실리카 혼합물, 스트론튬 알루미노 실리케이트, 산 반응성 충진제, 나노 지르코니아 충진제, 플루오로알루미늄실리케이트, 리튬 알루미노 실리케이트 및 바륨 알루미노 실리케이트 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는 치과용 시멘트 조성물.
The method according to claim 1,
Wherein the inorganic filler is selected from the group consisting of amorphous synthetic silica, crystalline natural silica, caroline, talc, quartz, barium glass, barium glass / silica mixture, quartz / barium mixture glass, zirconia / silica mixture, strontium aluminosilicate, acid reactive filler, A filler, a fluoroaluminum silicate, a lithium aluminosilicate, and a barium aluminosilicate.
제5항에 있어서,
상기 치과용 시멘트 조성물이 상기 폴리아크릴산계 공중합체 100 중량부에 대하여, 상기 무기필러 100 내지 500 중량부를 포함하는 것을 특징으로 하는 치과용 시멘트 조성물.
6. The method of claim 5,
Wherein the dental cement composition comprises 100 to 500 parts by weight of the inorganic filler based on 100 parts by weight of the polyacrylic acid copolymer.
제1항에 있어서,
상기 치과용 시멘트 조성물이 라디칼 단량체를 추가로 포함하는 것을 특징으로 하는 치과용 시멘트 조성물.
The method according to claim 1,
Wherein the dental cement composition further comprises a radical monomer.
제7항에 있어서,
상기 라디칼 단량체가 트리에틸렌글리콜 디메타크릴레이트(TEGDMA), 메틸메타크릴레이트, 에틸렌글리콜 디메타크릴레이트(EGDMA), 디에틸렌글리콜 디메타크릴레이트(DEGDMA), 1,4-부탄디올 디메타크릴레이트, 1,6-헥산디올 디케타크릴레이트, 1-메틸-1,3-프로판디올 디메타크릴레이트, 폴리에틸렌 글라이콜 디메타크릴레이트(PEGDMA), 필로메리틱 디메타크릴레이트(PMDM), 2,2-비스-(4-(2-3-메타크릴로일옥시프로폭시)페닐)프로판(bis-GMA), 에콕실레이트 비스페놀 A 디메타크릴레이트(Bis-EMA), 우레탄 디메타크릴레이트(UDMA), 디펜타에릴트리톨 펜타아크릴레이트 모노페스페이트(dipentaerylthritol pentaacrylate monophosphate, PENTA), 2-하이드로에틸 메타크릴레이트(2-hydroethyl methacrylate, HEMA), 비페닐 디메타크릴레이트(biphenyl dimethacrylate, BPDM) 및 글리세롤 포스페이트 디메타크릴레이트(glycerol phosphate dimethacrylate, GPDM) 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는 치과용 시멘트 조성물.
8. The method of claim 7,
Wherein the radical monomer is selected from the group consisting of triethylene glycol dimethacrylate (TEGDMA), methyl methacrylate, ethylene glycol dimethacrylate (EGDMA), diethylene glycol dimethacrylate (DEGDMA), 1,4-butanediol dimethacrylate , 1-methyl-1,3-propanediol dimethacrylate, polyethylene glycol dimethacrylate (PEGDMA), phyllomeric dimethacrylate (PMDM), 1,6-hexanediol dimethacrylate, Bis-GMA), epoxylate bisphenol A dimethacrylate (Bis-EMA), urethane dimethacrylate (bis-ethyleneglycol bisacrylate) (UDMA), dipentaerythritol pentaacrylate monophosphate (PENTA), 2-hydroethyl methacrylate (HEMA), biphenyl dimethacrylate , BPDM) and glycerol phosphate dimethacrylate and glycerol phosphate dimethacrylate (GPDM). The dental cement composition according to claim 1,
제1항에 있어서,
상기 치과용 시멘트 조성물이 촉매를 추가로 포함하는 것을 특징으로 하는 치과용 시멘트 조성물.
The method according to claim 1,
Wherein the dental cement composition further comprises a catalyst.
제9항에 있어서,
상기 촉매가 타르타르산, p-톨루엔술핀산나트륨, 틴플루오라이드, 알루미늄옥살레이트, 틴포스페이트, 아이론옥살레이트, 틴옥사이드, 알루미늄클로라이드, 칼슘클로라이드, 소듐벤젠설피네이트, 소듐타이타늄플로오라이드, 트리에틸아민 및 페릭클로라이드 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는 치과용 시멘트 조성물.
10. The method of claim 9,
Wherein the catalyst is selected from the group consisting of tartaric acid, sodium p-toluenesulfinate, tin fluoride, aluminum oxalate, tin phosphate, iron oxalate, tin oxide, aluminum chloride, calcium chloride, sodium benzene sulfinate, sodium titanium fluoride, triethylamine And ferric chloride. ≪ RTI ID = 0.0 > 11. < / RTI >
제1항에 있어서, 상기 치과용 시멘트 조성물이,
산과 화학반응을 하지 않는 무기필러를 포함하는 제1 페이스트;와 산과 화학반응을 하는 무기필러를 포함하는 제2 페이스트;의 조합으로 이루어진 것을 특징으로 하는 치과용 시멘트 조성물.
The dental cement composition according to claim 1,
A first paste including an inorganic filler which does not chemically react with an acid, and a second paste including an inorganic filler which chemically reacts with an acid.
제11항에 있어서,
상기 제2 페이스트가 비정질 합성 실리카 및 생체활성 바륨 글라스 중에서 선택된 1종 이상을 추가로 포함하는 것을 특징으로 하는 치과용 시멘트 조성물.
12. The method of claim 11,
Wherein the second paste further comprises at least one selected from amorphous synthetic silica and bioactive barium glass.
제11항에 있어서,
상기 산과 화학반응을 하는 무기필러가 trivalent metla, oxygen, fluorine, alkaline earth metal, 및 silicon 중에서 선택된 1종 이상을 함유하는 무기필러인 것을 특징으로 하는 치과용 시멘트 조성물.
12. The method of claim 11,
Wherein the inorganic filler chemically reacting with the acid is an inorganic filler containing at least one selected from trivalent meta, oxygen, fluorine, alkaline earth metal, and silicon.
제13항에 있어서,
상기 산과 화학반응을 하는 무기필러가 플루오르알루미늄실리케이트 글라스인 것을 특징으로 하는 치과용 시멘트 조성물.
14. The method of claim 13,
Wherein the inorganic filler chemically reacting with the acid is a fluoroaluminum silicate glass.
제11항에 있어서,
상기 산과 화학반응을 하지 않는 무기필러가 비정질 합성 실리카, 결정성 천연실리카, 바륨 알루미늄 실리케이트 및 스트론튬 알루미늄 실리케이트 중에서 선택된 1종 이상인 것을 특징으로 하는 치과용 시멘트 조성물.
12. The method of claim 11,
Wherein the inorganic filler which does not chemically react with the acid is at least one selected from amorphous synthetic silica, crystalline natural silica, barium aluminum silicate and strontium aluminum silicate.
제11항에 있어서,
상기 제2 페이스트가 접착단량체를 추가로 포함하는 것을 특징으로 하는 치과용 시멘트 조성물.
12. The method of claim 11,
Wherein the second paste further comprises an adhesive monomer.
제16항에 있어서,
상기 접착단량체가 2-히드록시에틸 메타크릴레이트, 4-메타크릴옥시에틸 트리메릴테이트 안히드라이드(4-Meta, 4-methacryloxyethyl trimellitate anhydride), 및 메타크릴옥시데실다이하이드로겐 포스페이트(10-MDP) 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는 치과용 시멘트 조성물.
17. The method of claim 16,
Wherein the adhesive monomer is selected from the group consisting of 2-hydroxyethyl methacrylate, 4-metha, 4-methacryloxyethyl trimellitate anhydride, and methacryloxydecyl dihydrogenphosphate (10-MDP ). ≪ RTI ID = 0.0 > 1. < / RTI >
제1항에 따른 치과용 시멘트 조성물을 경화시켜 형성한 치과용 시멘트.A dental cement formed by curing a dental cement composition according to claim 1.
KR1020160081473A 2016-06-29 2016-06-29 Dental cement composition comprising polyacrylic acid-based copolymer KR101868873B1 (en)