KR101588556B1 - Gold glaze ash composition and Manufacturing method for goldenware using it - Google Patents

Gold glaze ash composition and Manufacturing method for goldenware using it Download PDF

Info

Publication number
KR101588556B1
KR101588556B1 KR1020150111505A KR20150111505A KR101588556B1 KR 101588556 B1 KR101588556 B1 KR 101588556B1 KR 1020150111505 A KR1020150111505 A KR 1020150111505A KR 20150111505 A KR20150111505 A KR 20150111505A KR 101588556 B1 KR101588556 B1 KR 101588556B1
Authority
KR
South Korea
Prior art keywords
glaze
weight
golden
water
soil
Prior art date
Application number
KR1020150111505A
Other languages
Korean (ko)
Inventor
양웅모
Original Assignee
양웅모
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 양웅모 filed Critical 양웅모
Priority to KR1020150111505A priority Critical patent/KR101588556B1/en
Application granted granted Critical
Publication of KR101588556B1 publication Critical patent/KR101588556B1/en

Abstract

The present invention relates to: a golden ash glaze which allows an elegance gold color on an outer surface of pottery, is easy to obtain materials because of mostly using ash readily available, and is eco-friendly; and a manufacturing method of pottery using the same. The golden ash glaze comprises: 35 wt% of tree ash; 25 wt% of feldspar; 17 wt% of soil in a rice paddy; 15 wt% of gairome, 5 wt% of quartzite, and 3 wt% of zinc oxide.

Description

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a gold glaze and a method for manufacturing the same,

The present invention relates to a golden glaze and a method of manufacturing a ceramics using the glaze. More particularly, the present invention relates to a golden glaze and a method of manufacturing a ceramics using the glaze to make a golden color appear on the surface of the ceramics using the glaze.

It was used to form the rough surface of the earthenware. When it was used during the process of burning, it was observed that the ash melted down and the surface was smooth. It has been untouched for over a thousand years and has been undeveloped.

Such reclaimed glaze is not smooth and gaudy as compared with general glaze, and is manufactured by low-temperature calcination, so that it is weak in durability and has a disadvantage that artistic beauty is reduced in color and pattern.

Recently, a technology utilizing ashes in glaze has been introduced as disclosed in Korean Patent Registration No. 10-1466965 (Oct. 10, 2014), but ceramics produced by such techniques are merely excellent in terms of practical use , There is a problem in that it is not enough to satisfy the demand of consumers who desire various aesthetics.

In addition, although a method of manufacturing ceramics using gold glaze has been disclosed in Korean Patent Publication No. 10-0328464 (issued on March 16, 2002), since the amount of metal used is too high, There is no problem.

Korean Registered Patent Publication No. 10-1466965 (issued October 10, 2014) Korean Registered Patent Publication No. 10-0328464 (published on March 16, 2002)

It is an object of the present invention to provide a golden glaze and a method for manufacturing ceramics using the glaze so that the golden color is expressed on the surface of the ceramics.

It is another object of the present invention to provide a golden ash glaze which is easy to obtain a material by using mainly easily available materials, and which is environmentally friendly, and a method for manufacturing ceramics using the same.

It is another object of the present invention to provide a golden glaze and a method for manufacturing ceramics using the glaze so as to improve productivity by suggesting a method of obtaining a beautiful golden color ceramics using the glaze.

As a means for solving the above problems, the golden glaze of the present invention is a glaze comprising 35% by weight of wood, 25% by weight of feldspar, 17% by weight of soil, 15% by weight of wood, 5% by weight of zirconium and 3% .

The present invention also relates to a method for manufacturing ceramics using a golden ash glaze,

The soil is crushed, the impurities are sifted through the sieve, the sediment is settled in the water, and only the sediments are collected,

A molding step of kneading and molding the dried soil,

A shaping step of shearing the formed soil and making it smooth,

A decorative step to put the shape into the outer shape,

A drying step for drying the material,

A baking step to raise the temperature of the dried material to 750 ~ 850 ℃

Painting and calligraphy steps to add paintings and text to unglazed objects,

The golden re-glaze applying step and /

And a roasting step of raising the temperature to 1250 ~ 1300 < 0 > C,

At the time of temperature increase in the above-mentioned chrysanthemum roasting step

It was fired in an oxidation state to 900 ° C,

It is fired in a reducing furnace state up to 1100 ° C,

The mixture is fired at 1250 ° C with the amount of air supplied increased by 30%

And thereafter fired in a reduced-fire state.

The golden glaze and the method for manufacturing ceramics using the glaze according to the present invention are characterized in that the golden color is expressed on the surface of the ceramics to enhance the artwork and the strength and the durability are enhanced. And it is advantageous in that it is easy to obtain materials by using mainly easily available materials and is environmentally friendly, and productivity can be improved by suggesting a method of obtaining a beautiful golden color ceramics by using re-glazing.

1 is a block diagram illustrating a method of manufacturing a pottery using a golden ash glaze according to the present invention.
FIGS. 2 and 3 show a pottery manufactured through a golden glaze and a method of manufacturing a pottery using the same according to the present invention.

The golden glaze according to the present invention and the method for manufacturing ceramics using the same will now be described in detail.

FIG. 1 is a block diagram illustrating a method of manufacturing a pottery using a golden ash glaze according to the present invention, and FIGS. 2 and 3 illustrate a pottery manufactured through a golden glaze and a method of manufacturing a pottery using the same according to the present invention .

Prior to the description, there is a disadvantage in that the number of experiments is large and the material cost is considerably high because the result is completely different even if the glaze material composition ratio is different by 1%, and when the temperature is 900 to 1280 ° C., There is a difficulty.

For example, you can not put a piece of pottery into a large pottery kiln, so you have to work every few months to fill the kiln, and every time you burn a pottery kiln a few times a year, you need to experiment. do.

The golden glaze according to the present invention comprises 35% by weight of wood, 25% by weight of feldspar, 17% by weight of soil, 15% by weight of wood, 5% by weight of silica, By weight and 3% by weight of zinc.

Hereinafter, a method of manufacturing a pottery using a golden ash glaze according to the present invention will be described.

1. Earth defense step

In this step, the soil is crushed, the impurities are sifted through a sieve, the sediment is precipitated in water, and only fine sediment is collected and dried in the shade for a certain period.

2. Forming step

This step is a process of molding the shape by applying water to the dried soil, kneading it, removing air from the kneaded soil, pinching, coiling, turning the mill.

3. Orthography step

This is the process of smoothing the bottom soil after the molding before the soil is completely dry.

4. Decoration stage

This step is the process of putting a shape through a sculpture on the appearance of a basic figure made of ceramics to enhance the beauty or functionality.

5. Drying stage

This step is the process of completely drying the material that has been made, since it is necessary to completely dry the material to be baked.

There is a natural artificial drying method in which drying is carried out in a well-ventilated shade with a natural drying method and a drying chamber, which is heated in the drying chamber, and the humidity is raised or removed promptly.

6. Unglazed stage

In this step, it is preferable to increase the strength and hardness of the dried product by raising the temperature of the dried product, and to raise the temperature to 750 to 850 ° C so that the glaze can be adsorbed well.

7. Coloring and calligraphic steps

This step is the process of adding pictures and letters to unglazed pottery.

8. References

This step is performed by adding water to a golden ash glaze prepared by mixing 35% by weight of wood materials, 25% by weight of feldspar, 17% by weight of clay, 15% by weight of wood, 5% by weight of zirconium and 3% It is the process of applying the glaze to the surface.

First, in this step, a glaze material mixing step for mixing the above-mentioned materials is provided. In the glaze material mixing step, the feldspar, the wood, the quartz and the zincification are mixed, water is added and the mixture is filtered through a 120- A second step of mixing the wood material with water and filtering the mixture with aluminum mesh of primary 80th, secondary 100th and tertiary 120th woods, and a second step of mixing the soil with primary 100 Neck, second 120 mesh, and aluminum mesh, and a fourth step of mixing all the materials, adding water, stirring with a stirrer, and filtering the mixture with 120 mesh aluminum mesh.

By separating feldspar, wood, quartz, and zinc, and wood and earth from each other, it is possible to prevent the lowering of the material utilization rate caused by the difference in characteristics and size of each particle and reduce the work time for sieving There is a problem that it is possible to easily solve the mixing ratio adjustment problem such that the specific material is excessively loosened.

After the glaze material mixing step, a specific gravity adjusting step of adjusting the specific gravity while adding or removing water is provided. In this process, the concentration of the glaze is adjusted by using a gravity meter and adjusted to be 1.41 to 1.49. This is because the color does not come out sufficiently at 1.40 or less and becomes too light color, and at 1.50 or more, the glaze layer thickens and flows to the bottom. It is preferably adjusted to 1.45.

9. The chaebol's grilling stage

This step is the process of baking the object by raising the temperature to 1250 ~ 1300 ℃.

In the present invention, in order to obtain a beautiful golden color, at this stage, the temperature is increased to 900 ° C in the oxidation state, the product is calcined in a reduced state to 1100 ° C, The air is increased by 30%, and then the air is fired in a reduced-fire state.

Through the above-described construction, the golden glaze and the method for manufacturing ceramics using the glaze according to the present invention can produce a beautiful golden color on the surface of the ceramics, thereby enhancing artistic workability, and having high strength and durability, And it is advantageous in that it is easy to obtain materials by using mainly easily available materials and is eco-friendly, and productivity can be improved by suggesting a method of obtaining beautiful golden ceramics using re-glaze.

Claims (2)

The soil is crushed, the impurities are sifted through the sieve, the sediment is settled in the water, and only the sediments are collected,
A molding step of kneading and molding the dried soil,
A shaping step of shearing the formed soil and making it smooth,
A decorative step to put the shape into the outer shape,
A drying step for drying the material,
A baking step to raise the temperature of the dried material to 750 ~ 850 ℃
Painting and calligraphy steps to add paintings and text to unglazed pottery,
A step of applying water to a golden glaze comprising 35% by weight of wood material, 25% by weight of feldspar, 17% by weight of clay, 15% by weight of wood, 5% by weight of zirconium and 3%
And a roasting step of raising the temperature to 1250 ~ 1300 < 0 > C,
At the time of temperature increase in the above-mentioned chrysanthemum roasting step
It was fired in an oxidation state to 900 ° C,
It is fired in a reducing furnace state up to 1100 ° C,
Up to 1250 deg. C, the amount of air to be supplied is increased by 30%
Thereafter, it is calcined in a reducing furnace state,
Wherein the glaze material mixing step and the specific gravity adjusting step for mixing the golden glaze materials are provided in the refining step,
The glaze material mixing step comprises mixing a feldspar, a wood, a silicate, and a zincification, adding water, filtering the mixture with a 120 mesh aluminum mesh, holding the water for 20 hours or longer, and mixing the wood material with water The second stage is to filter out the first 80 trees, the second 100 trees, the third 120 trees and the aluminum mesh. The third step is to filter out the soil from the first 100 trees and the second 120 trees. Adding water, stirring with an agitator, and filtering with 120 mesh of aluminum mesh,
Wherein the specific gravity adjusting step is performed by adjusting the specific gravity while adding or removing water after the glaze material mixing step and adjusting the specific gravity to be 1.41 to 1.49
How to make pottery using golden ash
delete
KR1020150111505A 2015-08-07 2015-08-07 Gold glaze ash composition and Manufacturing method for goldenware using it KR101588556B1 (en)