KR100920123B1 - Non-sticker steel sheet and manufacturing method thereof - Google Patents
Non-sticker steel sheet and manufacturing method thereofInfo
- Publication number
- KR100920123B1 KR100920123B1 KR1020090047277A KR20090047277A KR100920123B1 KR 100920123 B1 KR100920123 B1 KR 100920123B1 KR 1020090047277 A KR1020090047277 A KR 1020090047277A KR 20090047277 A KR20090047277 A KR 20090047277A KR 100920123 B1 KR100920123 B1 KR 100920123B1
- Authority
- KR
- South Korea
- Prior art keywords
- metal plate
- printing
- coating
- sticker
- minutes
- Prior art date
Abstract
Description
본 발명은 스티커의 부착을 방지 할 수 있는 UV 실사 인쇄 금속판 및 그 제작 방법에 관한 것으로, 특히, 비교적 간단한 공정으로 이미지가 인쇄되는 매끄러운 금속판에 실리콘 코팅을 적용하여 금속판에 이미지를 보다 용이하고 견고하게 부착하고 보호하며 광고용 스티커 등 부착물의 부착을 방지할 수 있는 넌스티커 평판 인쇄 금속판 및 그 제작방법에 관한 것이다.The present invention relates to a UV live-print metal plate and a method of manufacturing the same, which can prevent the sticking of the sticker, and in particular, by applying a silicone coating to a smooth metal plate on which the image is printed in a relatively simple process to make the image on the metal plate more easily and firmly. The present invention relates to a non-sticky flat printed metal plate capable of attaching, protecting, and preventing the attachment of an adhesive such as an advertisement sticker, and a manufacturing method thereof.
일반적으로 금속 표면에 인쇄를 행하는 종래의 방법으로는 배면에 점착제 코팅층이 구비된 필름상에 인쇄를 한 후 인쇄된 필름의 배면을 금속 표면에 점착시키는 일명 데칼이라고 불리워지는 방식과, 피착체의 표면에 직접 실크 스크린 인쇄를 행하는 실크 스크린 인쇄 방식이 주로 사용되어 오고 있다.In general, a conventional method of printing on a metal surface is a method called a decal which prints on a film having a pressure-sensitive adhesive coating on the back and then sticks the back of the printed film to the metal surface, and the surface of the adherend Silk screen printing, which directly performs silk screen printing, has been mainly used.
이와 같은 상기의 종래 인쇄 방식 중 전자의 데칼 방식에서는 인쇄된 데칼 필름의 배면을 금속 표면에 점착시키는 과정에서 점착면과 금속 표면 사이의 공기를 완전히 제거하는 데 큰 어려움이 있고, 공기가 완전히 제거되지 않으면 피착체에 열이 가해지는 경우 공기의 팽창으로 인하여 필름이 부풀어올라서 인쇄필름이 피착체로부터 분리되어 버리는 치명적인 문제점이 있다. 또한, 데칼 방식의 경우 필름 제작과 부착 공정이 별도로 행해지므로 작업 속도와 비용에 불리한 점이 있다.The former decal method of the conventional printing method as described above has a great difficulty in completely removing the air between the adhesive surface and the metal surface in the process of sticking the back of the printed decal film to the metal surface, the air is not completely removed Otherwise, when heat is applied to the adherend, the film swells due to the expansion of air, which causes a fatal problem that the print film is separated from the adherend. In the case of the decal method, since the film production and the attaching process are performed separately, there is a disadvantage in the working speed and cost.
그리고, 후자의 실크 스크린 인쇄방식에서는 인쇄할 수 있는 색상이 4 ∼ 5가지 색상으로 제한되어 사실적인 색채의 구현에 어려움이 따르는 한편 대형의 피착체 표면에 인쇄를 행하는 경우에는 색상과 색상의 정확한 중첩이 매우 어렵기 때문에 인쇄품질이 떨어지는 단점이 있음으로 해서 실크 스크린 인쇄방식은 대체로 색상과 무늬가 단순한 패턴의 인쇄시에 국한하여 사용되고 있는 실정이다.In the latter silk screen printing method, the printable colors are limited to 4 to 5 colors, which makes it difficult to realize realistic colors, while accurate printing of colors and colors when printing on large adherend surfaces. Due to this very difficult, there is a disadvantage that the print quality is poor, the silk screen printing method is generally used only when printing a simple pattern of color and pattern.
한편, 기존 실사 출력은 전용지나 현수막과 같은 재질에만 출력이 가능하여 사용 가능한 매체에 제한이 있었으나 UV 평판 인쇄가 개발되어 재질에 관계없이 인쇄가 가능하게 되었으나 금속판과 같이 매끄러운 표면에 UV 평판 인쇄를 시행할 경우 잉크가 견고히 결합하지 못하고 판의 막 위에 떠있는 상태가 되어 작은 충격에도 쉽게 벗겨지는 단점이 있다.On the other hand, existing photorealistic output was limited to available media because it could be printed only on materials such as exclusive paper or banners, but UV flatbed printing was developed to enable printing regardless of materials, but UV flatbed printing was performed on smooth surfaces like metal plates. In this case, the ink is not firmly bonded and floats on the membrane of the plate, so that it is easily peeled off even with a small impact.
또한, 금속판을 건물 번호판이나 외장재 등으로 사용하는 경우 각종 광고물을 무단으로 부착하는 경우가 다발하여 외관이 손상되며 무단 부착된 광고물의 제거가 쉽지 않은 문제점이 있다.In addition, in the case of using the metal plate as a building license plate or exterior material, various advertisements are frequently attached to the building, and the appearance is damaged, and there is a problem in that the removal of the attached advertisement is not easy.
또한, 스티커 부착을 방지하기 위하여 일부 실리콘 코팅을 이용하였으나, 실리콘 코팅제의 특성상 피착물로부터 용이하게 박리되는 문제점이 있으며, 박리를 막기위하여 여러 단계의 공정이 필요하며, 표면 광택이 사라지는 문제점이 있다.In addition, although some silicone coatings are used to prevent sticking, there is a problem in that the silicone coating agent is easily peeled off from the adherend. In order to prevent peeling, several steps are required, and surface gloss disappears.
이에 본 발명은 상기와 같은 결점을 해소시키기 위하여 안출된 것으로 간단한 공정으로 UV 실사 인쇄된 금속판을 보호하며 광고물이 무단으로 부착되지 않도록 하는 넌스티커 평판 인쇄 금속판 및 그 제작 방법을 제공한다.Accordingly, the present invention provides a non-sticker plate printed metal plate and a method of manufacturing the same, which is designed to solve the above-mentioned drawbacks and protects the UV live-printed metal plate by a simple process and prevents the advertisements from being attached to the product without permission.
상기한 바의 문제점을 해결함과 아울러 상기 요구에 부응하기 위하여, 본 발명은 금속판, 상기 금속판에 아크릴실리콘수지 하도 코팅제를 도료와 경화제의 중량비가 9:1로 구성하여 도포한 후 열처리하여 형성되는 하도 코팅층, 상기 하도 코팅층 상에 평판 프린터를 이용하여 인쇄되는 UV 평판 인쇄층, 및 상기 UV 평판 인쇄층 상에 넌스티커 실리콘 조성물을 도료와 경화제의 중량비가 5:1로 구성하여 도포한 후 열처리하여 형성되는 실리콘 코팅층을 포함하는 것을 특징으로 한다.In order to solve the above problems and to meet the above requirements, the present invention is formed by applying a heat treatment after coating the weight ratio of the coating material and the curing agent to the metal plate, the acrylic plate resin coating agent to the metal plate of 9: 1 is formed by heat treatment A non-sticky silicone composition on the undercoat coating layer, a UV flatbed printing layer printed on the undercoat coating layer by using a flatbed printer, and a weight ratio of a coating material and a curing agent on the UV flatbed printing layer is 5: 1, and then coated and heat treated. It characterized in that it comprises a silicon coating layer formed.
본 발명의 다른 목적을 달성하기 위한 스티커 방지 금속판 제작 방법은, 평판 인쇄를 이용하는 금속판 인쇄 방법에 있어서, (a) 금속판을 가공 세척하는 인쇄 대상물 준비 단계; (b) 상기 (a)단계의 상기 대상물 표면에 아크릴실리콘수지 하도 코팅제를 도료와 경화제의 중량비가 9:1로 구성하여 도포한 후 열처리하는 하도 백색 코팅 단계; (c) 상기 (b)단계에서 형성되는 하도 백색 코팅층 위에 UV 평판 인쇄를 실행하는 UV 평판 인쇄 단계; 및 (d) 상기 (c)단계에서 생성되는 인쇄층 위에 넌스티커 실리콘 조성물을 도료와 경화제의 중량비가 5:1로 구성하여 도포한 후 열처리하는 실리콘 코팅 단계를 포함하는 것을 특징으로 한다.In order to achieve the another object of the present invention, a method for manufacturing a sticker-proof metal plate, the method for printing a metal plate using flat plate printing, comprising: (a) a printing object preparation step of processing and washing the metal plate; (b) an undercoat white coating step of applying an acrylic silicone resin undercoat coating agent on a surface of the object of step (a) by applying a weight ratio of paint and a curing agent of 9: 1 and then heat-treating; (c) a UV flatbed printing step of performing UV flatbed printing on the undercoat white coating layer formed in step (b); And (d) characterized in that it comprises a silicone coating step of applying a non-sticky silicone composition on the printed layer produced in the step (c) by applying a weight ratio of the coating material and the curing agent of 5: 1 and then heat treatment.
이하, 본 발명의 일 실시예를 첨부된 도면을 참조하여 상세히 설명하면 다음과 같다.Hereinafter, an embodiment of the present invention will be described in detail with reference to the accompanying drawings.
도 1 은 본 발명에 의한 넌스티커 평판 인쇄 금속판의 단면을 개략적으로 나타낸 확대 단면도이고, 도 2 는 본 발명에 의한 넌스티커 평판 인쇄 금속판의 제작 방법을 나타낸 흐름도이다.BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is an enlarged cross-sectional view schematically showing a cross section of a non-sticker flat plate printed metal plate according to the present invention, and Fig. 2 is a flowchart showing a method for producing a non-sticker flat plate printed metal plate according to the present invention.
본 발명에 의한 넌스티커 평판 인쇄 금속판은 도 1에 도시된 바와 같이 금속판(10)과, 상기 금속판(100) 상에 형성되는 하도 백색 코팅층(110), 상기 하도 백색 코팅층(110) 상에 형성되는 인쇄층(120), 상기 인쇄층(120) 상에 형성되는 실리콘 코팅층(130)으로 구성된다.The non-sticker flat plate printing metal plate according to the present invention is formed on the metal plate 10, the undercoat white coating layer 110 formed on the metal plate 100, the undercoat white coating layer 110 as shown in FIG. It is composed of a printed layer 120, the silicon coating layer 130 formed on the printed layer 120.
금속판(100)은 표면에 평판 인쇄 등을 필요로 하는 금속판으로 어느 금속이라도 제품에 적합한 금속을 선택할 수 있고, 알미늄, 철, 스테인레스 또는 그 합금이 바람직하다.The metal plate 100 is a metal plate requiring flat printing or the like on the surface, and any metal suitable for the product can be selected, and aluminum, iron, stainless steel, or an alloy thereof is preferable.
하도 코팅층(110)은 금속판(100)에 도료와 경화제를 9:1 중량비로 구성하고 용제는 20중량%로하여 도포한 후 경화시켜 형성된다. 스피타이트와 같은 아크릴실리콘수지 하도 코팅제를 이용하는 것이 바람직하고, 경화는 약 150℃에서 약 20분간 열처리하는 것이 바람직하다. 스피타이트와 같은 아크릴실리콘수지 하도 코팅제는 다른 프라이머 없이도 금속판(100)에 부착되며 후술하는 인쇄층(120)과 견고하게 결합하는 장점이 있다. 인쇄층(120)의 배경으로 사용될 수 있도록 백색을 사용하는 것이 인쇄할 이미지를 보다 선명하고 원 색감을 잘 나타낼 수 있도록 하므로 바람직하다.The undercoat coating layer 110 is formed of a 9: 1 weight ratio of a paint and a curing agent to the metal plate 100, and a solvent is formed by applying 20% by weight and then curing. It is preferable to use an acrylic silicone resin undercoat such as spite, and the curing is preferably heat-treated at about 150 ° C. for about 20 minutes. The acrylic silicone resin undercoat coating such as spitet is attached to the metal plate 100 without other primers, and has an advantage of being firmly bonded to the printing layer 120 described later. The use of white to be used as the background of the printed layer 120 is preferred because it makes the image to be printed clearer and better expresses the original color.
인쇄층(120)은 인쇄할 이미지가 입력된 컴퓨터와 연결되는 잉크젯 프린터(평판 프린터)를 이용하여 금속판(100) 표면에 선택된 이미지를 인쇄하여 형성된다.The print layer 120 is formed by printing a selected image on the surface of the metal plate 100 using an inkjet printer (flat panel printer) connected to a computer to which an image to be printed is input.
실리콘 코팅층(130)은 인쇄층(120)에 도료와 경화제를 5:1 중량비로 구성하고 용제는 20중량%로 하여 도포한 후 경화시켜 형성된다. 스피탄 넌스티커 ST와 같은 실리콘 코팅제를 이용하는 것이 바람직하고, 경화는 약 80℃에서 약 30분간 열처리하는 것이 바람직하다. 스피탄 넌스티커를 위와 같은 비율로 도포한 후 경화시키면 별도의 프라이머 없이도 인쇄층(120)에 견고히 결합하며 스티커 부착을 방지하고 다른 실리콘 코팅층과 달리 광택을 유지할 수 있어 미감을 증진시킬 수 있다.The silicone coating layer 130 is formed by coating and curing the coating agent and the curing agent in a 5: 1 weight ratio to the printing layer 120 and applying the solvent in an amount of 20% by weight. It is preferable to use a silicone coating agent such as spitan non-sticker ST, and the curing is preferably heat treated at about 80 ° C. for about 30 minutes. If applied after curing the spitan non-sticker in the same ratio as above, it can be firmly bonded to the print layer 120 without a separate primer to prevent the adhesion of the sticker and maintain the gloss unlike other silicone coating layer can enhance the aesthetics.
상술한 실시예에서는 금속판으로 한정하였으나, 표면이 매끄러워 평판 인쇄시 인쇄층이 견고하게 생성되지 않는 플라스틱 화합물, 금속을 포함한 다양한 재질에 응용이 가능하고 이는 본 발명의 범위에 포함됨을 알 수 있다.In the above-described embodiment, but limited to the metal plate, it is possible to apply to a variety of materials, including plastic compounds, metal that the surface is smooth and the print layer is not produced firmly when printing a flat plate, which is included in the scope of the present invention.
한편, 본 발명에 의한 스티커 방지 금속판 제작 방법은 도 2 에 도시된 바와 같이 금속판 준비 단계(S10), S10 단계의 금속판에 아크릴실리콘수지 하도 코팅제를 코팅하는 하도 백색 코팅 단계(S20), S20 단계의 하도 백색 코팅층 위에 UV 평판 인쇄를 실시하는 UV 평판 인쇄 단계(S30), 상기 S30 단계의 인쇄층에 넌스티커 실리콘 코팅액을 도포 경화시키는 실리콘 코팅 단계(S40)를 포함한다. 상기 공정을 보다 구체적으로 설명하면 다음과 같다.On the other hand, the anti-sticker metal plate manufacturing method according to the present invention, as shown in Figure 2 metal plate preparation step (S10), S10 of the undercoat white coating step (S20), S20 step of coating the acrylic silicone undercoat coating on the metal plate of step S10 UV flat plate printing step (S30) to perform a UV flat plate printing on the white coating layer, and the silicone coating step (S40) of applying a non-sticky silicone coating liquid to the printing layer of the step S30. The process is described in more detail as follows.
먼저 금속판 준비 단계(S10)에서 인쇄하고자 하는 금속판(100)을 선택 및 준비한다. 금속판(100)은 인쇄가 필요한 다양한 금속을 선택할 수 있고, 바람직하게, 알미늄, 알미늄 합금, 철, 철 합금, 또는 스테인레스 등이 사용될 수 있다.First, the metal plate 100 to be printed is selected and prepared in the metal plate preparation step (S10). The metal plate 100 may select various metals that require printing, and preferably, aluminum, aluminum alloy, iron, iron alloy, stainless steel, or the like may be used.
다음 하도 코팅 단계(S20)는 준비된 금속판(100) 표면에 도료와 경화제를 9:1 중량비로 구성하고 용제는 20 중량%로 하여 도포한 후 경화시켜 형성된다. 스피타이트와 같은 아크릴실리콘수지 하도 코팅제를 사용하는 것이 바람직하고, 경화는 약 150℃에서 약 20분간 처리하는 것이 바람직하다.Next coating step (S20) is formed by the coating and the curing agent in a 9: 1 weight ratio on the surface of the prepared metal plate 100, the solvent is applied to 20% by weight and then cured. It is preferable to use an acrylic silicone resin undercoat such as spitet, and curing is preferably performed at about 150 ° C. for about 20 minutes.
별도의 프라이머 없이도 금속판(100)에 부착되고 인쇄층(120)과 견고하게 결합하므로 별도의 프라이머 코팅 단계를 생략할 수 있다.Since it is attached to the metal plate 100 without a separate primer and firmly bonded to the printing layer 120, a separate primer coating step may be omitted.
S30 인쇄 단계에서는 평판 인쇄를 이용하는 것이 바람직하다. 먼저 인쇄할 이미지를 컴퓨터에 입력하여 이미지용 프로그램을 운용하여 이미지의 크기와 색상을 조절하고 모양 등을 결정하여 인쇄할 이미지를 선택하고, 컴퓨터와 연결되는 잉크젯 프린터(평판 프린터) 등을 이용하여 선택된 이미지를 프라이머 코팅 및 하도백색 코팅된 금속판(100) 위에 인쇄한다. 하도 백색 코팅된 금속판(100)에 인쇄하므로 매끄러운 금속판 상에서도 인쇄층이 겉돌지 않고 완전히 결합하여 작은 충격에도 손상되는 종래 기술과는 달리 어떠한 충격에도 벗겨지지 않는 견고함을 갖추게 된다.In the S30 printing step, it is preferable to use flatbed printing. First, input the image to be printed on the computer and operate the image program to adjust the size and color of the image, determine the shape, etc. to select the image to print, and select it using an inkjet printer (flatbed printer) connected to the computer. The image is printed onto the primer coating and the undercoat white coated metal plate 100. Since it is printed on the white-coated metal plate 100, the print layer is completely bonded even on a smooth metal plate, and thus is firmly attached to any impact unlike the prior art, in which the print layer is completely bonded and damaged even in a small impact.
평판 인쇄 수행 후 적외선 건조기나 히터 건조기 등을 이용하여 인쇄층(120)을 건조시킬 수 있다.After performing flat printing, the printed layer 120 may be dried using an infrared dryer or a heater dryer.
S40 실리콘 코팅 단계는 인쇄층(120) 상에 도료와 경화제를 5:1 중량비로 구성하고 용제는 20 중량%로 하여 도포한 후 경화시켜 형성된다. 경화는 약 80℃에서 약 30분간 열처리하는 것이 바람직하다. 별도의 프라이머 코팅 단계를 생략시킬 수 있고 완성 후 광택을 유지할 수 있도록 스피탄 넌스티커 ST와 같은 실리콘 코팅제를 사용하는 것이 바람직하다.S40 silicon coating step is formed by coating the paint and the curing agent in a 5: 1 weight ratio on the print layer 120 and the solvent is applied to 20% by weight and then cured. The curing is preferably heat treated at about 80 ° C. for about 30 minutes. It is preferable to use a silicone coating such as Spitan Nonsticker ST so that a separate primer coating step can be omitted and maintain gloss after completion.
본 발명에 의한 실리콘 코팅층(130)은 직사광선에 의한 변색도 방지하며 열로부터도 보호하며, 특히 스티커와 같은 광고물이 부착되지 않도록 하고 쉽게 제거되도록 하며, 광택을 유지하여 제품의 미감을 향상시킬 수 있다.The silicone coating layer 130 according to the present invention prevents discoloration due to direct sunlight and also protects from heat, and in particular, prevents advertisements such as stickers from being attached and easily removed, and maintains gloss to improve aesthetics of a product. have.
본 발명에 의한 넌스티커 평판 인쇄 금속판은 별도의 프라이머 코팅 없이 견고한 하도 백색 코팅과 실리콘 코팅을 가능하게 하므로 간단한 공정으로 견고한 컬러 인쇄 금속판을 형성할 수 있게 되며 인쇄된 금속판 상에 스티커 부착을 방지할 수 있게 된다.The non-sticker flat plate printing metal plate according to the present invention enables a solid undercoat white coating and a silicon coating without a separate primer coating, so that a simple process can form a solid color printing metal plate and can prevent sticking on the printed metal plate. Will be.
이상과 같은 본 발명에 의하면 금속과 같이 매끄러운 표면에도 견고하게 평판 인쇄가 가능해 지며, 인쇄층과 표면 사이에 블루밍(blooming) 현상에 의한 인쇄층 이탈로 인한 손상을 막을 수 있다. 또한 별도의 프라이머 코팅 없이 간단한 공정으로 평판 인쇄와 실리콘 코팅을 실시함으로써 작은 시간과 비용으로 이미지가 인쇄된 금속판을 제작할 수 있으며, 평판 인쇄된 금속판을 외부의 손상으로부터 보호하며, 스티커가 부착되지 않고 부착 후 제거를 용이하게 하며 광택을 유지하여 미감을 향상시킬 수 있다.According to the present invention as described above it is possible to firmly print a flat surface even on a smooth surface, such as metal, it is possible to prevent damage due to separation of the print layer due to the blooming (blooming) between the print layer and the surface. In addition, by performing flat printing and silicone coating in a simple process without a separate primer coating, it is possible to produce a metal plate printed images with a small time and cost, and to protect the flat plated metal plate from external damage, and to be attached without a sticker It is easy to remove afterwards and maintains gloss to improve aesthetics.
도 1 은 본 발명에 의한 넌스티커 평판 인쇄 금속판의 단면을 개략적으로 나타낸 확대 단면도, 및1 is an enlarged cross-sectional view schematically showing a cross section of a non-sticker flat plate printing metal plate according to the present invention; and
도 2 는 본 발명에 의한 넌스티커 평판 인쇄 금속판의 제작 방법을 나타낸 흐름도.Figure 2 is a flow chart showing a manufacturing method of a non-sticker flat plate printing metal plate according to the present invention.
Claims (2)