KR100776233B1 - Toe insert - Google Patents

Abstract

The present invention relates to a toe insert that can prevent and treat foot disease, and more particularly, is formed of a cylindrical tube with both sides open to be selectively worn on the toe, the cylindrical tube is hemp, flax, PVC, The present invention relates to a toe insertion port characterized in that at least one selected from PET containing silver nano and cotton and elastic yarn is mixed.

Such a toe insertion port can be easily worn and can be worn without wearing a general sock without deteriorating the feeling of wearing, and also has excellent antibacterial and absorptive properties, which effectively prevents and treats foot diseases such as athlete's foot. There is an excellent advantage.

Toes, socks

Description

Toe Insertion {TOE INSERT}

1 is a perspective view schematically showing an toe insertion hole which is an embodiment of the present invention.

2 is a view schematically showing a state in which a toe insertion hole which is an embodiment of the present invention is worn on a toe.

*** Explanation of symbols for main parts of drawing ***

10: toe insert 110: cylindrical tube

120: overlock sewing 30: socks

The present invention relates to a toe insert that can prevent and treat foot disease, and more particularly, is formed of a cylindrical tube with both sides open to be selectively worn on the toe, the cylindrical tube is hemp, flax, PVC, It relates to a toe insert, characterized in that a mixture of at least one selected from silver nano-containing PET, cotton and stretch yarn.

In general, socks are widely worn on bare feet in order to absorb the sweat generated in cold weather or the foot and maintain the optimal condition of the foot.

On the other hand, users with a lot of sweat between the toes or foot disease such as athlete's foot is wearing a toe socks that can effectively block the skin contact between the toes and effectively remove the sweat and smell from the toes.

Such toe socks contribute to the prevention and treatment of foot disease to some extent, but when the toe socks are worn, the toe inserts are exposed as they are. Compared with others, there was a problem causing dissatisfaction.

In spite of this heterogeneity, there are many cases of avoiding wearing due to the heterogeneity felt compared to other people wearing general socks, despite the prevention and treatment effect of foot disease such as athlete's foot.

There is a need for socks or sock aids that can achieve the effect of such toe socks and may not feel heterogeneous with others wearing normal socks.

In order to meet the demands of the present invention, the present invention can be easily worn and can be worn as a general sock without degrading the fit in a worn state, and also has excellent antibacterial and absorbent properties to effectively prevent and prevent foot disease such as athlete's foot. The purpose is to provide a toe wearable which is treatable and has a good fit.

The present invention devised to achieve the above object is formed of a cylindrical tube with both sides open to be selectively worn on the toe, the cylindrical tube is selected from hemp, flax, PVC, silver-containing PET Provided is a toe insert, characterized in that the mixture is made of one or more, cotton and stretch yarn.

And it is preferable that the cylindrical tubular body contains 50 to 120 parts by weight of at least one selected from PET containing hemp, flax, PVC, and silver nano with respect to 100 parts by weight of cotton.

In particular, the cylindrical tubular body is made of a double knitted fabric, it is preferable that the end is sewn.

Hereinafter, the toe insertion hole of the present invention will be described in detail with reference to the accompanying drawings.

1 is a perspective view schematically showing an toe insertion hole as an example of the present invention.

Toe insertion hole 10 of the present invention consists of a cylindrical tubular body 110 formed so as to open both ends, as shown in Figure 1 is worn on one toe, the cylindrical tubular 110 is hemp, flax, PVC, containing silver nano At least one of the PET, cotton and stretch yarn is made of a mixture.

That is, the cylindrical tube 110 is formed of hemp, flax, PVC, silver nano-containing PET and one selected from cotton and stretch yarn by knitting, or selected from hemp, flax, PVC, silver nano-containing PET Two or more kinds and cotton and elastic yarn can be formed by the method of knitting.

In this case, hemp and flax are preferably used in combination with cotton in order to improve spinning and physical properties, ie hemp / cotton blend yarn, flax / cotton blend yarn, or hemp / flax / cotton blend yarn by the method of stretching yarn and knitting. It is preferable to form the tubular body 110.

As such, the cylindrical tube 110 is formed to contain at least one type of PET containing hemp, flax, PVC, and silver nano to prevent and treat foot diseases such as athlete's foot due to antibacterial activity against athlete's foot. In addition, the surface is mixed with the cylindrical tubular body 110, there is an advantage of excellent fit by not only absorb the sweat generated between the toes but also deodorizes sweat smell.

In particular, in order to form the cylindrical tubular body 110 having excellent antimicrobial properties and comfort, it is preferable to use 50 to 120 parts by weight of one or more of PET containing hemp, flax, PVC, and silver nano to 100 parts by weight of cotton. .

When mixed with less than 50 parts by weight of one or more PET containing hemp, flax, PVC and silver nano, the antimicrobial activity is lowered, effectively preventing and preventing foot diseases such as athlete's foot, and more than 120 parts by weight of hemp or flax If you use it, you will not be able to obtain the blended yarn with excellent physical properties as well as prevent the blended yarns from being manufactured.And if you use more than 120 parts by weight of PET containing PVC or silver nano, it will have excellent antibacterial effect. There is a problem that the poor wearability is poor.

And by mixing and using the elastic yarn in the cylindrical tubular body 110, the cylindrical tubular body 110 can be prevented from being pushed to one side or falling out of the toes after wearing the cylindrical tubular body 110, the poly The urethane filament yarn is mainly used as a yarn formed by being covered with nylon yarn, but is not particularly limited thereto.

The cylindrical tube 110, such as hemp, flax, PVC, silver nano-containing one or more selected from PET, and cotton and stretch yarn formed by knitting to prevent the end of the toe insertion hole of the present invention It is desirable to complete (10).

On the other hand, in the case of manufacturing the toe insert of the present invention using a single layer of knitted fabric, the end is sewn in order to prevent the end from being easily loosened according to wearing and handling. At this time, since the layer is made of a thin layer of knitted fabric, the overlock cannot be performed. Inevitably, hand sewing is performed, which requires a great deal of work time and manpower, thereby greatly reducing productivity.

In addition, when the cylindrical tubular body 110 is formed of a single layer of knitted fabric, a surface loop is formed on the surface of which hemp, flax, and the like are exposed on the surface, and a rear surface loop is formed on the back of the sheet.

When the toe insert of the present invention is formed such that the back side is located inward, effective antimicrobial and hygroscopicity can not be obtained, so that hemp, flax, and cotton are located on both the inside and the outside of the present invention using two-ply knitted fabrics as shown in FIG. 1. It is preferable to form the toe insertion hole 10 of.

In detail, it is preferable to complete the two-fold toe insertion hole 10 of the present invention by folding the end of the double-sided cylindrical knitted fabric as shown in FIG.

As such, when the end of the cylindrical tube 110 is made of two layers, the overlock sewing 120 is possible, thereby minimizing the working time and the work force, so that the productivity is greatly improved, and only one end is overlocked to have an excellent fit. There is this.

In addition, since both the outer and inner surfaces of the cylindrical tubular body 110 are hemp, flax and the like, the antibacterial activity against athlete's foot as well as the toes worn on the adjacent toes can be effectively prevented and treated as well as toes. There is an advantage to improve the fit by effectively absorbing the sweat generated between the toes and adjacent toes.

2 is a view schematically showing a state in which the socks 30 are worn after the toe insertion hole 10 of the present invention is worn on the toes.

In FIG. 2, when the toe insertion hole 10 of the present invention is worn only on the big toe (the first toe), the toe toe (the third toe) and the little toe (the fifth toe), the toe toe (the second toe) and the toe (the fourth toe) are also worn. Direct antibacterial, deodorant and sweat-absorbing effects can be seen, besides it can be worn only on toes with severe athlete's foot, and can also be worn only on tongs (second toe) and toes (fourth toe). .

Hereinafter, the toe insertion port of the present invention will be described in more detail with reference to Examples. The scope of the present invention is not limited to the following Examples, and the technical field of the present invention is not limited to the scope of the present invention. Of course, it can be variously modified by those skilled in the art.

[Examples 1-3]

30's cotton / hemp blended yarn mixed with 100 parts by weight of cotton and 50 parts by weight of hemp and nylon filament covered with polyurethane filament yarn were knitted and sewn into a small circular knitting machine to insert the two-toe insertion hole of Example 1 Completed. Unlike Example 1, 100 parts by weight of hemp and 120 parts by weight were mixed with 100 parts by weight of cotton, respectively, and the toe insertion holes of Examples 2 and 3 were completed using 30's cotton / hemp blend yarns.

EXAMPLES 4-6

Unlike Example 1, the toe inserts of Examples 4 to 6 were completed using 30's cotton / flax blend yarn spun by blending 100 parts by weight of cotton, perhaps 50 parts by weight, 100 parts by weight, and 120 parts by weight, respectively. Excellent fit was good.

EXAMPLES 7-9

Unlike Example 1, the toe inserts of Examples 7 to 9 were completed using 100 parts by weight of 30's cotton yarn and 50 parts by weight of 190 denier PVC yarn, 100 parts by weight, and 120 parts by weight, respectively.

[Examples 10-12]

Unlike Example 1, the toe insertion holes of Examples 10 to 12 were completed using 100 parts by weight of 30's cotton yarn and 50 parts by weight of 100 denier PET yarn containing silver nano, 100 parts by weight, and 120 parts by weight, respectively.

As a result of wearing the toe inserts of Examples 1 to 12 as described above, the sweat absorption was excellent, and the fit was good.

Comparative Example 1

Unlike Example 1, 25 parts by weight of hemp was blended with 100 parts by weight of cotton, and the toe insertion hole of Comparative Example 1 was completed using cotton / hemp blend yarn spun, and excellent sweat absorption resulted in excellent fit.

Comparative Example 2

Unlike Example 1, 120 parts by weight of hemp blended with 100 parts by weight of cotton / hemp blend yarn was attempted to prepare a toe insertion hole using a small circular knitting machine because of poor spinning and knitting.

Comparative Example 3

Unlike Example 4, the toe insertion hole of Comparative Example 4 was completed using cotton / flax blend yarn spun with 25 parts by weight of cotton, and 100 parts by weight of cotton, and excellent sweat absorption resulted in excellent fit.

[Comparative Example 4]

Unlike Example 4, the mixture was mixed with 100 parts by weight of 100 parts by weight to prepare a cotton / flax blend yarn. However, as in Comparative Example 2, the spunness and knitting were not good, and thus the toe insertion hole was not completed.

[Comparative Examples 5 and 6]

Unlike Example 7, the toe insertion holes of Comparative Examples 5 and 6 were completed using 100 parts by weight of 30's cotton yarn, 25 parts by weight of 190 denier PVC yarn, and 120 parts by weight, respectively. This was not good.

[Comparative Examples 7, 8]

Unlike Example 10, the toe insertion holes of Comparative Examples 7 and 8 were completed using 100 parts by weight of 30's cotton yarn and 25 parts by weight of 120 denier PET yarn containing silver nano, and 120 parts by weight, respectively. Sweat absorbency resulted in poor fit.

The antimicrobial and deodorant experiments of the toe inserts of Examples 1 to 12 and the toe inserts of Comparative Examples 1, 3 and 5 to 8 were completed as described in Table 1 below.

On the other hand, the antimicrobial test was tested by KS standard KS K 0693 (textile antimicrobial test method), and was used Staphylococcus aureus known as a type of athlete's foot fungus.

And the deodorizing experiment was tested by the KFIA-FI-1004 test method of the Korea Far Infrared Ray Evaluation Evaluation Institute, and the deodorization rate was calculated by exposing the specimen to a container containing ammonia gas and measuring the remaining amount after 2 hours.

Table 1 Antimicrobial and Deodorant Test Results of Examples and Comparative Examples

As confirmed in Table 1, the toe inserts of Examples 1 to 12 were all excellent in antimicrobial activity with a bacteriostatic reduction rate of 97.9% or more, and also excellent in ammonia deodorization rate of 70.5% or more.

On the other hand, in the toe insertion holes of Comparative Examples 1, 3, 5 and 7, the bactericidal reduction rate was less than 44.7%, and the antibacterial activity was not good, and in the toe insertion holes of Comparative Examples 6 and 8, the ammonia deodorization rate was not good as 58.1% or less.

As described above, the toe insertion hole of the present invention is made of hemp, flax, PVC, silver nano-containing PET and at least one selected from a cylindrical tubular body composed of a mixture of cotton and elastic yarn, such as athlete's foot In addition to effectively preventing and treating foot disease, sweat can be effectively absorbed between the toes, thereby improving the fit.

In addition, when wearing the general socks in the state of wearing the toe insertion hole of the present invention, the same or better fit and better athlete's foot prevention and treatment effect than the conventional toe socks as well as the toe insertion hole is located in the general socks by conventional toe socks As such, the toe insertion part is not exposed to the outside, so the heterogeneity with the wearer who wears only normal socks does not occur, thereby avoiding wearing.

And by containing at least 50 to 120 parts by weight selected from PET, hemp, flax, PVC, silver nano containing the cylindrical tubular body with respect to 100 parts by weight of cotton, not only antibacterial but also excellent fit to provide an insertion hole It works.

In particular, the cylindrical tubular body is made of a double knitted fabric folded in two so that the stretch yarn is located on the inside, and formed by sewing one end overlock, both the inner and outer surfaces of the cylindrical tubular body excellent in antibacterial and absorbent hemp, flax back and cotton By placing the exposed surface loops, the surface loops are in contact with both the toes and adjacent toes to be worn, thereby further improving foot disease and foot comfort, such as athlete's foot.

In addition, since one end portion is doubled, overlock sewing is possible, so that the worker does not need to sew by manual labor, thereby minimizing work time and work force, thereby greatly improving workability.

Claims (3)

It is formed of a cylindrical tube with both sides open to be selectively worn on the toe, the cylindrical tube is made of a mixture of hemp, flax, PVC, silver nano-containing PET, cotton and stretch yarn , The cylindrical tube is a toe insert, characterized in that 50 to 120 parts by weight of one or more selected from PET, hemp, flax, PVC, silver nano containing 100 parts by weight cotton. The toe insert of claim 1, wherein the cylindrical tubular body is made of a double knitted fabric, and the end is sewn. delete

Images