JPH11346032A - Gallium nitride family compound semiconductor light-emitting device - Google Patents

Abstract

PROBLEM TO BE SOLVED: To perform light emission in blue and violet regions or an ultraviolet ray region with short wavelength, by composing a light emitting device of the n layer, active layer, and p layer of a gallium nitride family compound semiconductor consisting of a specific composition. SOLUTION: A sapphire substrate 1 is subjected to organic cleaning and then is installed at a crystal growth device. TMA and NH3 are supplied for forming an AIN layer 2 with a film thickness of approximately 50 nm. Then, TMA, TMG, and SiH4 are supplied for allowing an Si doped n-type (Alx1 Ga1-x1 )y1 In1-y1 N (in this case, 0<=X1<=1 and 0<=y1<=1) layer 3 (an n layer) to grow. The TMG is supplied for allowing an (Alx2 Ga1-x2 )y2 In1-y2 N (in this case, 0<=X2<=1 and 0<=y2<=1) layer 4 (an active layer) that has a thickness of 0.5 μm to grow. Furthermore, the TMA and Cp2 Mg are supplied for allowing a doped (Alx3 Ga1-x3 )y3 In1-y3 N (in this case, 0<=X3<=1 and 0<=y3<=1) layer 5 (a p layer) that has a thickness of 0.5 μm to grow.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a light-emitting device, for example, a semiconductor laser diode, which can emit light in a visible single wavelength, particularly in a blue region to a violet region, and in an ultraviolet region.

The light-emitting device of the present invention, for example, a semiconductor laser diode is obtained by an electron beam irradiation treatment first revealed by the present inventors ((Al _x Ga _{1 -x} ) _y In _{1 -y} N: 0 ≦ x ≤1,0
For the first time, ((Al _x Ga _1-x ) _y In _1-y N: 0 ≦ x ≦ 1,
0 ≦ y ≦ 1) A semiconductor laser diode can be manufactured.

[0003]

2. Description of the Related Art At present, current-injection type semiconductor laser diodes having the shortest wavelength that are practically used are manufactured using indium gallium aluminum phosphide (InGaAlP) -based crystals. Its oscillation wavelength belongs to the visible long wavelength region, that is, the 0.6 to 0.7 μm band which is the red region.

[0004]

However, further,
It is difficult to realize a semiconductor laser capable of emitting light in the blue, violet, or ultraviolet region, which is a short wavelength, due to the physical properties of this material. It is necessary to use a semiconductor material having a wider band gap. (Al _x Ga _1-x ) _y In _1-y N is one of the candidates.

[0005] (Al _x Ga _1-x ) _y In _1-y N, in particular, GaN has a room temperature (3
(00K) has been confirmed to be stimulated emission by photoexcitation
(H. Amano et al .; Japanese Journal of Applied Physics
Vol. 29, 1990, pp. L205-L206). For this reason, there is a possibility that a laser diode can be formed from the above semiconductor.

However, since it is difficult to produce a p-type single crystal thin film with the above-mentioned compound semiconductors, up to the present, semiconductors have been manufactured by current injection using (Al _x Ga _{1 -x} ) _y In _{1 -y} N. Laser diode is not realized.

SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned problems, and an object of the present invention is to obtain a light-emitting element, for example, a laser in a short wavelength blue, violet or ultraviolet region. That is.

[0008]

SUMMARY OF THE INVENTION The present invention provides an n-type conductivity.
The gallium nitride based compound semiconductor shown ((Al_x1Ga_1-x1)_y1In
_1-y1N: 0 ≦ x1 ≦ 1, 0 ≦ y1 ≦ 1) and gallium nitride
System compound semiconductor ((Al_{x Two}Ga_1-x2)_y2In_1-y2N: 0 ≦ x2 ≦ 1,0
≤ y2 ≤ 1) and gallium nitride exhibiting p-type conductivity
Based compound semiconductor ((Al_x33a_1-x3)_y3In_1-y3N: 0 ≦ x3 ≦ 1,0 ≦
a gallium nitride-based compound composed of a p-layer composed of y3 ≦ 1)
It is a conductor light emitting element.

In another aspect of the invention, the light emitting element is a laser diode. Another invention is characterized in that an insulating film having a strip-shaped window is provided on the p-layer, and a metal electrode for the p-layer is formed through the window. Further, another invention is characterized in that the electrode for the n-layer is formed on a surface exposed by etching a layer formed on the n-layer. Also, other inventions provide n
An electrode for a layer is formed on a surface exposed by forming a mask on an electrode forming portion on the n-layer, selectively growing the layer thereon, and then removing the mask. Another invention is characterized in that the active layer is n-type conductive. In another invention, an n layer, an active layer, and a p layer
It is characterized by being formed on a sapphire substrate.
In another invention, the n layer, the active layer, and the p layer are made of Si, 6H-
It is characterized in that it is formed on a substrate made of SiC or GaN. Another invention is directed to an n-layer, an active layer,
The layer is formed on a substrate made of Si, 6H-SiC or GaN, and an electrode for the n-layer is formed on the back surface of the substrate. Still another aspect of the invention is characterized in that the n-layer is a layer doped with a high concentration of donor impurities in the early stage of growth and not doped or lightly doped near the junction.

The following configuration is also possible. The n-layer and the p-layer may be made of a gallium nitride-based compound semiconductor having the same forbidden band width. The pn junction may be formed by joining a layer made of a gallium nitride-based compound semiconductor having a relatively large forbidden band width and a layer made of a gallium nitride-based compound semiconductor having a relatively small forbidden band width.

A layer having a relatively small band gap (active layer)
Are characterized by having a structure in which the forbidden band width and the mixed crystal composition are the same or different from each other, and are sandwiched between layers having relatively large forbidden band widths.

Further, a structure in which two or more layers having different forbidden band widths are laminated may be used.

A layer made of a gallium nitride-based compound semiconductor doped with an acceptor impurity is irradiated with an electron beam so that
It may have a shaped layer.

Further, the shape of the layer made of the p-type gallium nitride-based compound semiconductor and the contact portion between the layer and the electrode metal may be a strip shape.

The substrate may be sapphire, Si, 6H-SiC or Ga
N can be used.

[0016]

[Action and Effect] ((Al _x Ga _1-x ) _y In _1-y N: 0 ≦ x ≦ 1,0 ≦ y ≦
1) For semiconductors, the present inventors have made it possible for the first time to manufacture a layer exhibiting p-type conductivity. This has made it possible to manufacture and oscillate a carrier-injection type light-emitting element, such as a laser diode, composed of the gallium nitride-based compound semiconductor.

According to the present invention, (Al _x
By devising the p-type effect of Ga _1-x ) _y In _1-y N and devising the structure, a light emitting element having an oscillation wavelength in the blue to violet and ultraviolet regions, for example, a semiconductor laser diode has been realized.

[0018]

SUMMARY OF THE INVENTION In the above invention, sapphire, silicon (Si), 6H silicon carbide (6H-SiC) is used as the substrate for preparing aluminum gallium indium nitride (Al _x Ga _{1 -x} ) _y In _{1 -y} N single crystal. Alternatively, gallium nitride (GaN) can be used.

When sapphire is used as the substrate, it is preferable that at least a layer containing an AlN thin film deposited at a low temperature (for example, about 600 ° C.) be used as the buffer layer.

When Si is used as a substrate, at least 3C-SiC
It is desirable that the buffer layer be a thin film or a layer including two layers of a 3C-SiC thin film and an AlN thin film.

When 6H-SiC is used as a substrate, it is not directly or Ga
It is desirable that N be a buffer layer. When GaN is used as a substrate, a single crystal is directly produced. Si, 6H-SiC and GaN
Is used as a substrate, an n-type single crystal is used.

First, the case of manufacturing a pn junction structure using crystals of the same composition will be described. When sapphire is used as the substrate, the substrate temperature is set to a desired value (for example, 600 ° C.) immediately before (Al _x Ga _1-x ) _y In _1-y N is grown, and at least aluminum (Al) is introduced into the growth furnace. ) And a hydroxide of nitrogen are introduced to form an AlN thin film buffer layer on the sapphire substrate surface.

Thereafter, the introduction of the compound containing Al is stopped, and the substrate temperature is reset. Then, a compound containing Al, a compound containing gallium (Ga) and a compound containing indium (In) are introduced so as to have a desired mixed crystal composition, and n-type (Al _x Ga _1-x ) is introduced.
_y In _1-y N A single crystal is grown.

In this case, in order to lower the resistivity of the n-type single crystal, Si, oxygen (O), sulfur (S), selenium (Se), tellurium (Te)
For example, a compound containing an element serving as a donor impurity may be introduced at the same time.

In the case of doping with a donor impurity, the concentration may be uniform in the n-layer.
Further, in order to facilitate the formation of the n-layer ohmic electrode, the n-layer may be doped at a high concentration at the initial stage of growth and may not be doped near the pn junction or may be doped at a low concentration.

Next, the wafer is once taken out of the growth furnace, a part of the sample surface is covered with a material serving as a mask for selective growth, for example, silicon oxide (SiO ₂ ), and the wafer is returned to the growth furnace again. Alternatively, the growth is continued without taking out the wafer.

At least Al having a desired mixed crystal composition
, Compounds containing Ga, compounds containing In and compounds that become hydrides and acceptor impurities of nitrogen, such as beryllium (Be), magnesium (Mg), zinc (Zn), cadmium (cd), and carbon (C). Is introduced into a growth furnace to grow an (Al _x Ga _{1 -x} ) _y In _{1 -y} N single crystal (p layer) doped with acceptor impurities.

The growth thickness of the acceptor-doped layer is determined in consideration of the penetration depth of the electron beam when performing the electron beam irradiation treatment. Next, the wafer is taken out of the growth furnace, and the acceptor dope (Al _x
The Ga _{1- x} ) _y In _1-y N layer is subjected to electron beam irradiation.

The region to be irradiated with the electron beam is formed on the whole or a part of the sample surface, for example, in a strip shape. When the entire sample surface is irradiated with an electron beam, the acceptor-doped layer (p
An insulating layer is deposited on the layer, a strip-shaped window is opened in a part of the insulating layer, and a metal is contacted on the window to form an ohmic electrode for the p-layer. In the case where the electron beam irradiation treatment is performed in a strip shape, a metal is contacted so as to cover a part or the whole of the region irradiated with the electron beam, and an ohmic electrode for the p layer is formed.

Finally, the shape of the portion where the metal contacts the p layer is a strip. The electrode of the n-layer is formed after removing the selective growth mask, or by etching a part of the acceptor-doped layer (p-layer) from the surface side to form the n-layer electrode.
Open a window to the layer and contact the metal to form an ohmic electrode.

When n-type Si, 6H-SiC or GaN is used as a substrate, an element is manufactured by substantially the same means. However, the selective growth technique is not used, and the electrodes for the p layer and the n layer are formed on both the upper and lower sides of the device. That is, the n-layer electrode contacts the metal on the entire back surface of the substrate to form an ohmic electrode.

The above is a basic method for producing a light emitting device having a pn junction structure using crystals of the same composition, for example, a semiconductor laser diode. Also in the case of manufacturing a device using a junction of crystals of different mixed crystal compositions, that is, a so-called hetero junction, the formation of a pn junction is the same as the case of using the above-described junction of crystals of the same mixed crystal composition.

When a single heterojunction is formed, in addition to a pn junction formed of crystals having the same mixed crystal composition, an n-type crystal having a large forbidden band width is further joined to the n-layer side to form holes serving as minority carriers. A diffusion blocking layer.

Since the emission near the bandgap of the (Al _x Ga _{1 -x} ) _y In _{1 -y} N based single crystal is particularly strong in the n layer, it is necessary to use an n type crystal for the active layer. The band structure of the (Al _x Ga _1-x ) _y In _1-y N-based single crystal is (Al _x Ga _1-x ) _y In _1-y As-based single crystal or (Al _x Ga _1-x ) _y In _{1 -y}
Similar to a P-based single crystal, it is considered that the band discontinuity ratio is larger in the conduction band than in the valence band. However, (Al _x
In a Ga _1-x ) _y In _1-y N-based single crystal, since the effective mass of holes is relatively large, a heterojunction between n-types effectively acts as a hole diffusion inhibitor.

When two heterojunctions are formed, n-type and p-type crystals (n-layer and p-layer) having a large forbidden band width are provided on both sides of an n-type crystal (an active layer) having a relatively small forbidden band width, respectively. Are joined to sandwich an n-type crystal having a small forbidden band width.

When a large number of heterojunctions are formed, a plurality of thin film crystals of an n-type having a relatively large forbidden band width and a plurality of thin film crystals of a relatively small forbidden band width are joined to each other, and on both sides thereof, n and n have a further larger forbidden band width. Type and p-type crystals are joined to sandwich a number of heterojunctions.

Since the refractive index of light near the forbidden band width of the (Al _x Ga _1-x ) _y In _1-y N-based single crystal is larger as the forbidden band width is smaller, the other (Al _x Ga _1-x) ) as with _y in _1-y as-based single crystal or _{(Al x Ga 1-x)} y in 1-y P type semiconductor laser diode according to a single crystal heterostructure sandwiching a large crystal of the band gap in the confinement of light Is also effective.

In the case where a hetero junction is used, similarly to the case of a pn junction made of crystals having the same composition, the carrier concentration near the portion in contact with the electrode may be made high to facilitate the composition of the ohmic electrode.

The carrier concentration of the n-type crystal is controlled by the doping concentration of the donor impurity, and the carrier concentration of the p-type crystal is controlled by the doping concentration of the acceptor impurity and electron beam irradiation conditions. In addition, in order to facilitate the formation of an ohmic electrode, a crystal which can easily realize a high carrier concentration may be further bonded for contact with a metal.

[0040]

DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below with reference to specific embodiments. ((Al _x Ga _{1 -x} ) _y In _{1 -y} N: 0 ≦ x ≦ 1, 0 ≦ y ≦ 1) A horizontal organometallic compound vapor phase epitaxy apparatus was used for producing a single crystal for a semiconductor laser diode. Sapphire as a substrate,
The growth procedures for Si, 6H-SiC and GaN are shown below.

(1) Sapphire Substrate FIG. 1 is a cross-sectional view showing the structure of a semiconductor laser diode using a sapphire substrate. In FIG. 1, (0001)
After the organic cleaning of the sapphire substrate 1 having the surface as a crystal growth surface, the sapphire substrate 1 is set in a crystal growth section of a crystal growth apparatus. After evacuation of the growth furnace, hydrogen is supplied and the temperature is raised to about 1200 ° C. Thus, the hydrocarbon-based gas adhering to the surface of the sapphire substrate 1 is removed to some extent.

Next, the temperature of the sapphire substrate 1 is lowered to about 600 ° C., trimethylaluminum (TMA) and ammonia (NH ₃ ) are supplied, and the AlN layer 2 having a thickness of about 50 nm is formed on the sapphire substrate 1. To form Next, only the supply of TMA is stopped, the substrate temperature is raised to 1040 ° C., and TMA, trimethylgallium (TMG) and silane (SiH ₄ ) are supplied to grow the Si-doped n-type GaAlN layer 3 (n layer).

Once the wafer is taken out of the growth furnace, GaAl
After masking a part of the surface of the N layer 3 with SiO _2, it is returned to the growth furnace again, evacuated, supplied with hydrogen and NH ₃ , and heated to 1040 ° C. Next, TMG is supplied to grow a GaN layer 4 (active layer) having a thickness of 0.5 μm on a portion not masked with SiO ₂ . Next, TMA and biscyclopentadienyl magnesium (Cp ₂ Mg) are further supplied to grow the doped GaAlN layer 5 (p layer) to 0.5 μm.

Next, the SiO ₂ used as a mask is removed with a hydrofluoric acid-based etchant. Next, after depositing an SiO ₂ layer 7 on the doped GaAlN layer 5 (p layer), the length is 1 mm and the width is 50 μm.
The window 7A is opened in the shape of a strip of m, and the window 7A is moved to a vacuum chamber, and the doped GaAlN layer 5 (p layer) is subjected to an electron beam irradiation process. Tables show typical electron beam irradiation processing conditions.

[Table 1]

Next, metal electrodes are formed on the windows 8 of the doped GaAlN layer 5 (p layer) and on the Si-doped n-type GaAlN layer 3 (n layer). This is the end of the crystal growth.

(2) Case of Si Substrate FIG. 2 shows the structure of a laser diode formed on a Si substrate. After the low-resistance n-type Si (111) surface substrate 8 is organically cleaned, the surface oxide is removed by a hydrofluoric acid-based etchant and the substrate 8 is placed on the crystal growth portion. After evacuation of the growth furnace, hydrogen is introduced, the substrate is heated to 1000 ° C., the surface of the substrate 8 is cleaned, and propane (C ₃ H ₈ ) or acetylene (C ₂ H ₂ ) is supplied. Thereby, a 3C-SiC thin film 9 is formed on the surface.

Thereafter, the inside of the growth furnace is once evacuated to remove excess gas. Next, hydrogen is supplied to the growth furnace to set the substrate temperature to 600 ° C., and TMA and NH ₃ are supplied to remove the AlN thin film 10.
It is formed on the 3C-SiC thin film 9. Next, only the supply of TMA is stopped, the substrate temperature is set to 1040 ° C., and TMG, TMA and SiH ₄ are supplied to grow the n-type GaAlN layer 11 (n layer).

Next, the supply of only TMA and SiH ₄ was stopped and GaN
A layer 12 (active layer) is grown to a thickness of 0.5 μm, and again TMA and CP ₂
Mg is added, and a Mg-doped GaAlN layer 13 (p layer) is grown to a thickness of 0.5 μm. Next, after depositing an SiO ₂ layer 15 on the Mg-doped GaAlN layer 13 (p layer), the window 15 is formed into a rectangular shape having a length of 1 mm and a width of 50 μm.
Open A, move to vacuum chamber, and Mg-doped GaAlN layer 1
3 (p layer) is irradiated with an electron beam. The irradiation conditions of the electron beam are the same as in the previous embodiment. Thereafter, an electrode 14A for the Mg-doped GaAlN layer 13 (p layer) is formed from the SiO ₂ layer 15 side,
On the other hand, an electrode 14B for the n-type GaAlN layer 11 (n-layer) was formed on the back surface of the substrate 8.

(3) 6H-SiC Substrate FIG. 3 shows a laser diode formed on a 6H-SiC substrate. The (0001) plane substrate 16 of the low-resistance n-type 6H-SiC is organically cleaned, etched with an aqua regia etchant, and then placed in a crystal growth part. After evacuation of the growth furnace, hydrogen is supplied and the temperature is increased to 1200 ° C. Next, hydrogen is supplied to the growth furnace, the substrate temperature is set to 1040 ° C., and TMG, SiH ₄ and NH ₃ are supplied to grow the n-type GaN buffer layer 17 to about 0.5 to 1 μm. Next, TMA is added, and n-type GaAlN is placed on the n-type GaN buffer layer 17.
A layer 18 (n-layer) is grown.

Next, on the n-type GaAlN layer 18, the Si
The GaN layer 19 (active layer) and the Mg-doped GaAlN layer 20 (p layer) were formed in the same structure, using the same gas, and under the same growth conditions as the laser diode using the substrate under the same growth conditions.
It was formed to a thickness of 0.5 μm. Next, the Mg-doped GaAlN layer 2
After depositing the SiO ₂ layer 22 on the substrate 0, the window 22A was opened in a rectangular shape having a length of 1 mm and a width of 50 μm, moved to a vacuum chamber, and the Mg-doped GaAlN layer 20 (p layer) was irradiated with an electron beam. The irradiation conditions of the electron beam are the same as in the previous embodiment.

Thereafter, from the SiO ₂ layer 22 side, Mg-doped GaAlN
An electrode 21A for the layer 20 (p layer) was formed, while an electrode 21B for the n-type GaAlN layer 18 (n layer) was formed on the back surface of the substrate 16.

(4) GaN Substrate FIG. 4 shows a laser diode formed on a GaN substrate.
After the low-resistance n-type GaN (0001) plane substrate 23 is organically cleaned and etched with a phosphoric acid + sulfuric acid-based etchant, the substrate 23 is placed in a crystal growth part. Next, after evacuation of the growth furnace, hydrogen and NH ₃ were supplied, and the substrate temperature was set to 1040.
C. and leave for 5 minutes. Next, TMG and SiH ₄ were further added to form an n-type GaN buffer layer 24 having a thickness of 0.5 to 1 μm.

Next, TMA was added, and an n-type GaAlN layer 25 was grown. Next, on the n-type GaAN layer 25, the GaN layer 26 (active layer) was formed to a thickness of 0.5 μm under the same growth conditions and under the same growth conditions as those of the laser diode using the Si substrate. The Mg-doped GaAlN layer 27 (p layer) is
It was formed to a thickness of μm. Next, after depositing the SiO ₂ layer 29 on the Mg-doped GaAlN layer 27, a window 29A is opened in a rectangular shape having a length of 1 mm and a width of 50 μm, and is moved to a vacuum chamber.
The AlN layer 27 (p layer) was irradiated with an electron beam. The irradiation conditions of the electron beam are the same as in the previous embodiment.

Thereafter, from the SiO ₂ layer 29 side, Mg-doped GaAlN
An electrode 28A for the layer 27 (p layer) was formed, while an electrode 28B for the n-type GaAlN layer 25 (n layer) was formed on the back surface of the substrate 23.

The laser diodes having any of the above structures oscillated at room temperature.

[Brief description of the drawings]

FIG. 1 shows a specific example of the present invention fabricated on a sapphire substrate ((Al _x Ga _{1 -x} ) _y In _{1 -y} N: 0 ≦ x ≦ 1, 0 ≦ y ≦ 1)
Sectional drawing which showed the structure of the system semiconductor laser diode.

FIG. 2 shows a ((Al _x Ga _1-x ) _y In _1-y N: 0 ≦ x ≦ 1, 0 ≦ y ≦ 1) system according to a specific embodiment of the present invention fabricated on a Si substrate. FIG. 2 is a cross-sectional view illustrating a configuration of a semiconductor laser diode.

FIG. 3 shows ((Al _x Ga _1-x ) _y In _1-y N: 0 ≦ x ≦ 1, 0 ≦ y ≦ 1 according to one specific example of the present invention fabricated on a 6H-SiC substrate. FIG. 1 is a cross-sectional view illustrating a configuration of a semiconductor laser diode.

FIG. 4 shows ((Al _x Ga _1-x ) _y In _1-y N: 0 ≦ x ≦ 1, 0 ≦ y ≦ 1) according to a specific example of the present invention fabricated on a GaN substrate. FIG. 2 is a cross-sectional view illustrating a configuration of a semiconductor laser diode.

[Explanation of symbols]

DESCRIPTION OF SYMBOLS 1 ... (0001) plane substrate of sapphire 2, 9, 17 ... AlN buffer layer 3, 11, 18, 25 ... n-type AlGaN layer (n layer) 4, 12, 19, 26 ... GaN layer (active layer) 5, 13,20,27 ... Mg-doped AlGaN layer (p layer) 7,15,22,29 ... SiO ₂ layer 6A, 14A, 21A, 28A ... electrode (Mg-doped AlGaN
6B, 14B, 21B, 28B ... electrode (for n-type AlGaN layer (n layer))

 ──────────────────────────────────────────────────続 き Continuing on the front page (72) Nobuo Okazaki, Inventor No. 1 Nagahata Ochiai, Kasuga-cho, Nishi-Kasugai-gun, Aichi Prefecture Inside Toyoda Gosei Co., Ltd. Address: Toyoda Gosei Co., Ltd. (72) Inventor Isamu Akasaki 1-38-805, Joshin, Nishi-ku, Nagoya, Aichi Prefecture Building No.505

Claims (10)

[Claims] 1. An n-layer comprising a gallium nitride-based compound semiconductor exhibiting n-type conductivity ((Al _x1 Ga _{1-x 1} ) _y1 In _1-y1 N: 0 ≦ x1 ≦ 1,0 ≦ y1 ≦ 1) Gallium nitride based compound semiconductor ((Al _x2 Ga _1-x2 ) _y2 In _1-y2 N:
An active layer composed of 0 ≦ x2 ≦ 1,0 ≦ y2 ≦ 1) and a gallium nitride-based compound semiconductor exhibiting p-type conductivity ((Al _x33
a _1-x3 ) _y3 In _1-y3 N: 0 ≦ x3 ≦ 1, 0 ≦ y3 ≦ 1) p-layer and a gallium nitride based compound semiconductor light emitting device. 2. The gallium nitride based compound semiconductor light emitting device according to claim 1, wherein the light emitting device is a laser diode. 3. The semiconductor device according to claim 2, further comprising an insulating film having a rectangular window on the p-layer, and a metal electrode for the p-layer formed through the window. Gallium nitride based compound semiconductor light emitting device. 4. The electrode according to claim 1, wherein the electrode for the n-layer is formed on a surface exposed by etching a layer formed on the n-layer. 2. The gallium nitride-based compound semiconductor light emitting device according to item 1. 5. An electrode for the n-layer is formed on an exposed surface by forming a mask on an electrode forming portion on the n-layer, selectively growing a layer thereon, and then removing the mask. The gallium nitride-based compound semiconductor light-emitting device according to any one of claims 1 to 4, wherein: 6. The gallium nitride-based compound semiconductor light emitting device according to claim 1, wherein the active layer has n-type conductivity. 7. The gallium nitride-based compound according to claim 1, wherein the n-layer, the active layer, and the p-layer are formed on a sapphire substrate. Semiconductor light emitting device. 8. The n-layer, the active layer, and the p-layer are formed of S
The gallium nitride-based compound semiconductor light emitting device according to any one of claims 1 to 6, wherein the gallium nitride-based compound semiconductor light emitting device is formed on a substrate made of i, 6H-SiC, or GaN. 9. The n-layer, the active layer, and the p-layer are formed of S
4. An electrode formed on a substrate made of i, 6H-SiC, or GaN, and an electrode for the n-layer is formed on a back surface of the substrate.
The gallium nitride-based compound semiconductor light-emitting device according to claim 1. 10. The n-layer according to claim 1, wherein the n-layer is doped with a high concentration of donor impurities in the early stage of growth and is not doped or has a low concentration of doping near the junction. The gallium nitride-based compound semiconductor light-emitting device according to claim 1.