JPH09265059A - Lens for spectacles - Google Patents
Lens for spectaclesInfo
- Publication number
- JPH09265059A JPH09265059A JP8073977A JP7397796A JPH09265059A JP H09265059 A JPH09265059 A JP H09265059A JP 8073977 A JP8073977 A JP 8073977A JP 7397796 A JP7397796 A JP 7397796A JP H09265059 A JPH09265059 A JP H09265059A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- lens
- hard coat
- absorbents
- dioxide layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、紫外線遮断効果の
高い反射防止膜を有する眼鏡レンズに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a spectacle lens having an antireflection film having a high ultraviolet blocking effect.
【０００２】[0002]
【従来の技術】従来の眼鏡レンズは、３６０ｎｍまでの
紫外線をカットするように製造されていたが、最近では
４００ｎｍまでの紫外線をカットすることが要求される
ようになってきた。４００ｎｍまでの紫外線をカットす
るための紫外線吸収剤としてはベンゾフェノン系紫外線
吸収剤があり、基板中及び／又はハードコート中にベン
ゾフェノン系紫外線吸収剤を含有させていた。ところ
が、ベンゾフェノン系紫外線吸収剤は、紫外線によって
励起されて分解され、そのとき発生するガスが反射防止
膜に損傷を与え、反射防止膜にクラックが発生するとい
う問題があった。2. Description of the Related Art Conventional spectacle lenses have been manufactured to block ultraviolet rays up to 360 nm, but recently, it has been required to block ultraviolet rays up to 400 nm. There is a benzophenone-based ultraviolet absorber as an ultraviolet absorber for cutting ultraviolet rays up to 400 nm, and the benzophenone-based ultraviolet absorber was contained in the substrate and / or the hard coat. However, the benzophenone-based ultraviolet absorber has a problem in that it is excited by ultraviolet rays and decomposed, and the gas generated at that time damages the antireflection film, causing cracks in the antireflection film.
【０００３】[0003]
【発明が解決しようとする課題】本発明は、４００ｎｍ
までの紫外線をカットすることができ、長期間の屋外使
用による紫外線照射によっても反射防止膜にクラックが
発生しない眼鏡レンズを提供することを目的とする。DISCLOSURE OF THE INVENTION The present invention relates to 400 nm
It is an object of the present invention to provide a spectacle lens which can block ultraviolet rays up to and which does not cause cracks in the antireflection film even when exposed to ultraviolet rays for long-term outdoor use.
【０００４】[0004]
【課題を解決するための手段】本発明による眼鏡レンズ
は、レンズ基板及び／又はその上に形成されたハードコ
ート層中にベンゾフェノン系紫外線吸収剤、ベンゾトリ
アゾール系紫外線吸収剤、シアノアクリレート系紫外線
吸収剤及び立体障害アミン系紫外線吸収剤のうちから選
択された紫外線吸収剤１種又は２種以上を含み、該ハー
ドコート層上に所定の厚さ以上で形成された二酸化チタ
ン層を含む多層反射防止膜を有することを特徴とする。A spectacle lens according to the present invention comprises a benzophenone-based UV absorber, a benzotriazole-based UV absorber and a cyanoacrylate-based UV absorber in a lens substrate and / or a hard coat layer formed thereon. -Layer antireflection including a titanium dioxide layer formed on the hard coat layer in a predetermined thickness or more, containing one or more kinds of ultraviolet absorbers selected from the group of agents and sterically hindered amine ultraviolet absorbers. It is characterized by having a membrane.
【０００５】[0005]
【発明の実施の形態】本発明において、レンズ基板は、
ジエチレングリコールビスアリルカーボネート重合体、
ポリウレタン樹脂、アクリル樹脂、ポリカーボネート樹
脂、ポリスチレンなど、各種のプラスチックレンズ素材
から成るものであってよい。BEST MODE FOR CARRYING OUT THE INVENTION In the present invention, the lens substrate is
Diethylene glycol bisallyl carbonate polymer,
It may be made of various plastic lens materials such as polyurethane resin, acrylic resin, polycarbonate resin and polystyrene.
【０００６】眼鏡レンズにおいては、一般に、レンズ基
板及び／又はその上に形成されるハードコート層に紫外
線吸収剤が添加される。本発明においては、このような
レンズ基板又はハードコート層中に添加される紫外線吸
収剤として、４００ｎｍまでの紫外線をカットしうるベ
ンゾフェノン系紫外線吸収剤、ベンゾトリアゾール系紫
外線吸収剤、シアノアクリレート系紫外線吸収剤及び立
体障害アミン系紫外線吸収剤のうちから選択された紫外
線吸収剤１種又は２種以上を用いるか、あるいは通常の
紫外線カットレベルのレンズ用に製造されたレンズ基板
又はハードコート層付きレンズ基板を用い、そのレンズ
基板又はハードコート層付きレンズ基板をベンゾフェノ
ン系紫外線吸収剤、ベンゾトリアゾール系紫外線吸収
剤、シアノアクリレート系紫外線吸収剤及び立体障害ア
ミン系紫外線吸収剤のうちから選択された紫外線吸収剤
１種又は２種以上を界面活性剤や他の添加剤とともに水
中に溶解あるいは分散させた溶液中にレンズ基板又はハ
ードコート層付きレンズ基板を浸漬し、加熱した後、溶
液から取り出し、乾燥することによりレンズ基板及び／
又はハードコート層中にベンゾフェノン系紫外線吸収剤
を分散させることもできる。いずれの場合にも、４００
ｎｍまでの光線の透過率を０．１％以下に調節するのが
好ましい。In a spectacle lens, an ultraviolet absorber is generally added to the lens substrate and / or the hard coat layer formed thereon. In the present invention, as an ultraviolet absorber added to such a lens substrate or a hard coat layer, a benzophenone-based ultraviolet absorber capable of cutting ultraviolet rays up to 400 nm, a benzotriazole-based ultraviolet absorber, a cyanoacrylate-based ultraviolet absorber. Agent or a sterically hindered amine-based UV absorber selected from the group consisting of one or more UV absorbers, or a lens substrate or a lens substrate with a hard coat layer manufactured for a lens having an ordinary UV cut level Using a lens substrate or a lens substrate with a hard coat layer, a UV absorber selected from a benzophenone UV absorber, a benzotriazole UV absorber, a cyanoacrylate UV absorber and a sterically hindered amine UV absorber. One or more kinds of surfactants and other additives Both lens substrate or the lens substrate with a hard coat layer was immersed in a solution obtained by dissolving or dispersing in water, after heating, it is taken out from the solution, the lens substrate by drying and /
Alternatively, a benzophenone-based ultraviolet absorber can be dispersed in the hard coat layer. In each case, 400
It is preferable to adjust the light transmittance up to nm to 0.1% or less.
【０００７】使用しうるベンゾフェノン系紫外線吸収剤
としては、２−ヒドロキシベンゾフェノン、２，４−ジ
ヒドロキシベンゾフェノン、２−ヒドロキシ−４−メト
キシベンゾフェノン、２，２’，４−トリヒドロキシベ
ンゾフェノン、２，２’−ジヒドロキシ−４−メトキシ
ベンゾフェノン、２，２’，４，４’−テトラヒドロキ
シベンゾフェノンが挙げられ、ベンゾトリアゾール系紫
外線吸収剤としては２−（２−ヒドロキシ−５−テトラ
オクチルフェニル）ベンゾトリアゾールなどが挙げられ
る。また、本発明に用いるレンズ基板及び／又はハード
コート層に上記以外の紫外線吸収剤が含まれていてもよ
い。The benzophenone-based UV absorbers that can be used are 2-hydroxybenzophenone, 2,4-dihydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2,2 ', 4-trihydroxybenzophenone, 2,2'. -Dihydroxy-4-methoxybenzophenone and 2,2 ', 4,4'-tetrahydroxybenzophenone are mentioned, and 2- (2-hydroxy-5-tetraoctylphenyl) benzotriazole and the like are used as the benzotriazole-based UV absorber. Can be mentioned. Further, the lens substrate and / or the hard coat layer used in the present invention may contain an ultraviolet absorber other than the above.
【０００８】また、本発明の眼鏡レンズに用いられるハ
ードコート層の形成には、任意の公知ハードコート組成
物を用いることができ、例えば、金属酸化物微粒子、有
機珪素化合物及び硬化剤を含むハードコート組成物など
が用いられる。金属酸化物微粒子としては、シリカゾ
ル、チタニアゾル、酸化アンチモンゾル、酸化スズゾ
ル、酸化タングステンゾルなどが挙げられ、これらの１
種又は２種以上が用いられる。有機珪素化合物として
は、特に制限はなく、任意のものを用いることができ、
例えば、シラン化合物、有機ポリシロキサン、含フッ素
シリコーン化合物又はこれらの加水分解物、部分縮合物
などを用いることができる。Any known hard coat composition can be used for forming the hard coat layer used in the spectacle lens of the present invention. For example, a hard coat containing metal oxide fine particles, an organosilicon compound and a curing agent. A coat composition or the like is used. Examples of the metal oxide fine particles include silica sol, titania sol, antimony oxide sol, tin oxide sol, and tungsten oxide sol.
Species or two or more species are used. The organosilicon compound is not particularly limited, and any compound can be used,
For example, a silane compound, an organic polysiloxane, a fluorine-containing silicone compound or a hydrolyzate or partial condensate thereof can be used.
【０００９】上記のような各種の成分を、塗布作業性、
被膜の厚さの調節などの点からを考慮して、適切な溶剤
に溶解してハードコート液とするのが好ましい。溶剤と
しては、アルコール類、ケトン類、セロソルブ類、ホル
ムアミド類、水、フレオン類の各種の溶剤を用いること
ができる。通常、これらの溶剤を用いて１〜４０重量％
の固形分を含む溶液として用いるのが好適であるが、こ
の範囲に制限されるものではなく、その都度の状況によ
り適宜選定することができる。また、ハードコート液
に、さらに界面活性剤、酸化防止剤、チキソトロピー
剤、帯電防止剤などを添加することができる。ハードコ
ート液を塗布する方法としては、特に、制限はなく、浸
漬、スピン塗布など、各種の方法で行うことができる。
また、コーティング液をレンズ基板に塗布する場合、接
着強度の保持、硬度などの点から１〜１０μｍの塗膜と
なるように塗布するのが好ましく、２〜５μｍとするの
がさらに好ましい。膜厚が１０μｍを超えると、塗膜の
耐熱性が劣り、１μｍ未満では塗膜の密着性や耐擦傷性
が劣る。The above-mentioned various components are used for coating workability,
Taking into consideration the adjustment of the thickness of the coating film and the like, it is preferable to dissolve it in a suitable solvent to prepare a hard coat liquid. As the solvent, various solvents such as alcohols, ketones, cellosolves, formamides, water and freons can be used. Usually 1-40% by weight using these solvents
It is preferable to use it as a solution containing the solid content, but it is not limited to this range and can be appropriately selected depending on the situation in each case. Further, a surfactant, an antioxidant, a thixotropic agent, an antistatic agent and the like can be added to the hard coat liquid. The method for applying the hard coat liquid is not particularly limited, and various methods such as dipping and spin coating can be used.
Further, when the coating liquid is applied to the lens substrate, it is preferable that the coating liquid has a thickness of 1 to 10 μm, more preferably 2 to 5 μm, from the viewpoints of maintaining adhesive strength and hardness. When the film thickness exceeds 10 μm, the heat resistance of the coating film is poor, and when it is less than 1 μm, the adhesion and scratch resistance of the coating film are poor.
【００１０】本発明の眼鏡レンズにおいては、多層の反
射防止膜を有するが、多層反射防止膜のうち少なくとも
１層は所定の厚さ以上で形成された二酸化チタン層であ
る。二酸化チタンは、紫外線を遮断する効果が高いた
め、本発明により反射防止膜に二酸化チタン層を形成し
ておくことにより、その二酸化チタン層で紫外線を遮蔽
することができ、ベンゾフェノン系紫外線吸収剤などの
紫外線吸収剤の効果とともに完全な紫外線の遮蔽を達成
することができる。The spectacle lens of the present invention has a multilayer antireflection film, and at least one layer of the multilayer antireflection film is a titanium dioxide layer having a predetermined thickness or more. Since titanium dioxide has a high effect of blocking ultraviolet rays, it is possible to block ultraviolet rays with the titanium dioxide layer by forming a titanium dioxide layer on the antireflection film according to the present invention. Complete UV shielding can be achieved with the effect of the UV absorbers.
【００１１】反射防止膜を形成するには、高屈折率材料
と低屈折率材料との最低２種類の組合せが必要であり、
高屈折率材料としてはＡｌ2 Ｏ3 、Ｙ2 Ｏ3 、Ｈｆ
Ｏ2 、ＺｒＯ2 、ＴｉＯ2 及びＴａ2 Ｏ5 があり、低屈
折率材料としてはＳｉＯ2 及びＭｇＦ2 がある。本発明
においては、ＴｉＯ2 層を少なくとも１層有することが
必要であり、この層は二酸化チタンの実膜厚として（複
数層形成する場合は合計で）９０ｎｍ以上、好ましくは
９０〜４００ｎｍ、より好ましくは１００〜３５０ｎｍ
の層厚で形成される。この層厚が９０ｎｍより薄いと、
紫外線カット効果が充分でなく、ベンゾフェノン系紫外
線吸収剤を励起するおそれが残る。また、ＴｉＯ2 層の
厚さが４００ｎｍを超えると、膜にクラックが発生しや
すい。低屈折率材料としては、ＳｉＯ2 が好ましい。反
射防止膜は、真空蒸着法、スパッタリング法、イオンプ
レーティング法、イオンビームアシスト法など、任意の
方法で形成することができる。In order to form the antireflection film, a combination of at least two kinds of high refractive index material and low refractive index material is required,
High refractive index materials include Al 2 O 3 , Y 2 O 3 and Hf
O 2 , ZrO 2 , TiO 2 and Ta 2 O 5 are used, and low refractive index materials include SiO 2 and MgF 2 . In the present invention, it is necessary to have at least one TiO 2 layer, and this layer has a real film thickness of titanium dioxide of 90 nm or more (in the case of forming a plurality of layers), preferably 90 to 400 nm, more preferably Is 100 to 350 nm
Is formed. If this layer thickness is less than 90 nm,
The UV blocking effect is not sufficient, and there remains a risk of exciting the benzophenone-based UV absorber. If the thickness of the TiO 2 layer exceeds 400 nm, cracks are likely to occur in the film. As the low refractive index material, SiO 2 is preferable. The antireflection film can be formed by any method such as a vacuum vapor deposition method, a sputtering method, an ion plating method and an ion beam assist method.
【００１２】[0012]
【実施例】次に、実施例に基づいて本発明をさらに詳細
に説明するが、本発明はこれによって制限されるもので
はない。Next, the present invention will be described in more detail with reference to Examples, but the present invention is not limited thereto.
【００１３】実施例１ ジエチレングリコールビスアリルカーボネート樹脂から
なるレンズ基板上に、２−ヒドロキシベンゾフェノンを
０．１重量％含有するハードコート液（シリカゾル、シ
ランカップリング剤、メチルアルコール及び界面活性剤
の混合液）をスピンコート法により塗布し、１２０℃で
３時間加熱し、硬化させ、４００ｎｍ以下の光線透過率
が０．１％以下のハードコート層を形成した。その後、
真空蒸着法により基板側より第一層として実膜厚４０ｎ
ｍのＳｉＯ2 層、第二層として実膜厚２０ｎｍのＴｉＯ
2 層、第三層として実膜厚４０ｎｍのＳｉＯ2 層、第四
層として実膜厚３００ｎｍのＴｉＯ2 層及び第五層とし
て実膜厚９０ｎｍのＳｉＯ2 層を蒸着した。コート干渉
色は淡緑色であり、全体の透過率は９８％であった（４
００〜７００ｎｍ）。製品の評価結果を表１に示す。な
お、試験方法は下記のとおりである。Example 1 A hard coat liquid containing 0.1% by weight of 2-hydroxybenzophenone on a lens substrate made of diethylene glycol bisallyl carbonate resin (silica sol, silane coupling agent, methyl alcohol and surfactant mixed solution). Was applied by a spin coating method and heated at 120 ° C. for 3 hours to be cured to form a hard coat layer having a light transmittance of 400 nm or less and 0.1% or less. afterwards,
The actual film thickness is 40n as the first layer from the substrate side by the vacuum deposition method.
m SiO 2 layer, TiO 2 with an actual film thickness of 20 nm as the second layer
2-layer, SiO 2 layer of the actual film thickness 40nm as the third layer was deposited SiO 2 layer of the actual film thickness 90nm as a real film TiO 2 layer of thickness 300nm and fifth layer as a fourth layer. The coat interference color was light green, and the overall transmittance was 98% (4
00-700 nm). Table 1 shows the evaluation results of the products. The test method is as follows.
【００１４】 黄色度（ＹＩと略す） 黄色度（ＹＩと略す）は、中心厚２ｍｍの平板レンズを
ウェザーメーターで下記の条件で６０時間照射後のＹＩ
値を下記の計算式により、ＸＹＺ表色系における光原色
の三刺激値のＸＹＺを採用して求めた。 ＹＩ＝１００（１．２８Ｘ−１．６２Ｚ）／Ｙ ウェザーメータの条件 カーボンアーク灯で１２０分照射中、１８分間水噴霧を
１サイクルとした。 ブラックパネル温度５０〜６０℃Yellowness (abbreviated as YI) Yellowness (abbreviated as YI) is YI after irradiation of a flat lens having a central thickness of 2 mm with a weather meter under the following conditions for 60 hours.
The value was calculated by the following formula using the XYZ tristimulus values of the light primary colors in the XYZ color system. YI = 100 (1.28X-1.62Z) / Y condition of weather meter During irradiation for 120 minutes with a carbon arc lamp, water spray was set as one cycle for 18 minutes. Black panel temperature 50-60 ℃
【００１５】 コート膜の密着性 コート膜を設けた基板の表面にカッターを使用して約１
ｍｍ間隔で１１本の切込みを入れ、さらにこれと直交す
る方向にも同様の切込みを入れて１００個のマス目を作
る。切り込み面全面に市販のセロテープ（幅１８ｍｍ）
を貼りつけて密着させ、基板面に対して垂直方向に瞬間
的に剥がし、コート膜の剥がれ状況を目視で観察する。Adhesion of coat film About 1 is obtained by using a cutter on the surface of the substrate provided with the coat film.
Make 11 cuts at mm intervals, and make similar cuts in the direction orthogonal to the cuts to make 100 squares. Commercially available cellophane tape (width 18 mm) on the entire cut surface
Is adhered and adhered, and is peeled off instantaneously in the direction perpendicular to the substrate surface, and the peeled state of the coat film is visually observed.
【００１６】実施例２ 予め、２−（２−ヒドロキシ−５−テトラオクチルフェ
ニル）ベンゾトリアゾール５重量％、エチレングリコー
ル５重量％、クエン酸２重量％及び界面活性剤０．３重
量％及び水８７．７重量％から成る紫外線吸収剤溶液を
調製した。ジエチレングリコールビスアリルカーボネー
ト樹脂からなるレンズ基板を、上記紫外線吸収剤溶液中
に液温９０℃で約３０分浸漬してレンズの４００ｎｍ以
下の光線の透過率を０．１％以下にした後、紫外線吸収
剤を含まない以外は実施例１と同様のハードコート層及
び反射防止層を形成し、製品の試験結果を表１に示す。Example 2 In advance, 5% by weight of 2- (2-hydroxy-5-tetraoctylphenyl) benzotriazole, 5% by weight of ethylene glycol, 2% by weight of citric acid, 0.3% by weight of surfactant and 87% of water. A UV absorber solution consisting of 0.7% by weight was prepared. A lens substrate made of diethylene glycol bisallyl carbonate resin is immersed in the ultraviolet absorbent solution at a liquid temperature of 90 ° C. for about 30 minutes to make the transmittance of light rays of 400 nm or less of the lens 0.1% or less, and then the ultraviolet absorption. The same hard coat layer and antireflection layer as in Example 1 were formed except that the agent was not included, and the test results of the products are shown in Table 1.
【００１７】実施例３ キシリレンジイソシアネートとペンタエリトリットテト
ラキスメルカプトプロピオネートとを１：１のモル比で
重合させたウレタン樹脂（ｎ＝１．６０）上に２−（２
−ヒドロキシ−５−テトラオクチルフェニル）ベンゾト
リアゾールを０．１重量％含有するハードコート液（酸
化アンチモンゾル、シランカップリング剤、メタノー
ル、界面活性剤の混合液）をスピンコート法により塗布
し、１４０℃で３時間硬化させ、ｎ＝１．６０のハード
コート層（４００ｎｍ以下の光線透過率０．１％以下）
を形成した。洗浄後、真空蒸着法により実施例１と同様
な膜厚で反射防止膜を形成し、製品の評価結果を表１に
示す。Example 3 2- (2) on a urethane resin (n = 1.60) obtained by polymerizing xylylene diisocyanate and pentaerythritol tetrakismercaptopropionate in a molar ratio of 1: 1.
-Hydroxy-5-tetraoctylphenyl) benzotriazole was coated by a spin coating method with a hard coating solution containing 0.1% by weight (a mixed solution of antimony oxide sol, a silane coupling agent, methanol and a surfactant). Hard coat layer with n = 1.60 after curing at ℃ for 3 hours (light transmittance of 400 nm or less 0.1% or less)
Was formed. After cleaning, an antireflection film having the same film thickness as in Example 1 was formed by the vacuum deposition method, and the evaluation results of the products are shown in Table 1.
【００１８】実施例４ キシリレンジイソシアネートと４−メルカプト−３，６
−ジチア−１，８−オクタンジオールとを１：１のモル
比で重合させたウレタン樹脂（ｎ＝１．６６）上にハー
ドコート液（酸化スズと酸化タングステンの混合ゾル、
シランカップリング剤、メタノール、界面活性剤の混合
液）を浸漬によって塗布し、１３０℃で４時間硬化さ
せ、ｎ＝１．６５のハードコート膜を形成した。実施例
２で調製したのと同じ紫外線吸収剤溶液中に液温９０℃
で約３０分浸漬してレンズの４００ｎｍ以下の光線の透
過率を０．１％以下にした後、洗浄工程を経て、真空蒸
着法により実施例１と同様な膜厚で反射防止膜を形成
し、製品の評価結果を表１に示す。Example 4 Xylylene diisocyanate and 4-mercapto-3,6
-Dithia-1,8-octanediol was polymerized at a molar ratio of 1: 1 on a urethane resin (n = 1.66) to form a hard coating solution (a mixed sol of tin oxide and tungsten oxide,
A mixed solution of a silane coupling agent, methanol, and a surfactant was applied by dipping and cured at 130 ° C. for 4 hours to form a hard coat film with n = 1.65. Liquid temperature 90 ° C. in the same UV absorber solution as prepared in Example 2.
After soaking the lens for about 30 minutes to reduce the transmittance of light rays of 400 nm or less of the lens to 0.1% or less, a washing process is performed, and then an antireflection film having the same thickness as in Example 1 is formed by a vacuum deposition method. Table 1 shows the evaluation results of the products.
【００１９】比較例１ 実施例１で製造したのと同じハードコート層付きレンズ
基板を用い、そのハードコート層上に真空蒸着法により
基板側より第一層として実膜厚１５０ｎｍのＳｉＯ
2 層、第二層として実膜厚４０ｎｍのＺｉＯ2 層、第三
層として実膜厚３０ｎｍのＳｉＯ2 層、第四層として実
膜厚１００ｎｍのＴａ2 Ｏ5 層及び第五層として実膜厚
９０ｎｍのＳｉＯ2 層を蒸着し、製品の評価結果を表１
に示す。Comparative Example 1 The same lens substrate with a hard coat layer as that manufactured in Example 1 was used, and a SiO film having an actual film thickness of 150 nm was formed as a first layer on the hard coat layer from the substrate side by a vacuum deposition method.
Two layers, a ZiO 2 layer having an actual film thickness of 40 nm as the second layer, a SiO 2 layer having an actual film thickness of 30 nm as the third layer, a Ta 2 O 5 layer having an actual film thickness of 100 nm as the fourth layer, and an actual film as the fifth layer. A 90 nm thick SiO 2 layer is deposited and the evaluation results of the product are shown in Table 1.
Shown in
【００２０】比較例２ 比較例１と同じ反射防止膜を形成した以外は、実施例２
と同様にして、製品の評価結果を表１に示す。Comparative Example 2 Example 2 was repeated except that the same antireflection film as in Comparative Example 1 was formed.
Table 1 shows the evaluation results of the products similarly to the above.
【００２１】比較例３ 実施例３で製造したのと同じハードコート層付きレンズ
基板を用い、そのハードコート層上に真空蒸着法により
基板側より第一層として実膜厚１５０ｎｍのＳｉＯ
2 層、第二層として実膜厚４０ｎｍのＺｉＯ2 層、第三
層として実膜厚３０ｎｍのＳｉＯ2 層、第四層として実
膜厚８０ｎｍのＴｉＯ2 層及び第五層として実膜厚９０
ｎｍのＳｉＯ2 層を蒸着し、製品の評価結果を表１に示
す。Comparative Example 3 The same lens substrate with a hard coat layer as that manufactured in Example 3 was used, and a SiO film having an actual film thickness of 150 nm was formed as a first layer on the hard coat layer from the substrate side by a vacuum deposition method.
Two layers, a ZiO 2 layer having an actual film thickness of 40 nm as the second layer, a SiO 2 layer having an actual film thickness of 30 nm as the third layer, a TiO 2 layer having an actual film thickness of 80 nm as the fourth layer, and an actual film thickness of 90 as the fifth layer.
A SiO 2 layer having a thickness of 1 nm was deposited, and the evaluation results of the product are shown in Table 1.
【００２２】[0022]
【表１】 [Table 1]
【００２３】[0023]
【発明の効果】本発明による眼鏡レンズは、４００ｎｍ
までの紫外線をほぼ完全にカットすることができ、長期
間の屋外使用による多大の紫外線照射によっても反射防
止膜にクラックが発生せず、黄変も極めて少なく、膜の
密着性も良好であり、高い品質を有するものである。The spectacle lens according to the present invention is 400 nm.
It is possible to almost completely cut off the ultraviolet rays up to, no cracks occur in the antireflection film even when exposed to a large amount of ultraviolet rays due to long-term outdoor use, very little yellowing, and good film adhesion, It has high quality.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 加藤 元勝 東京都板橋区前野町２丁目36番９号 旭光 学工業株式会社内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Motokatsu Kato 2-36-9 Maenocho, Itabashi-ku, Tokyo Asahi Gaku Gakuin Kogyo Co., Ltd.
Claims (3)
たハードコート層中にベンゾフェノン系紫外線吸収剤、
ベンゾトリアゾール系紫外線吸収剤、シアノアクリレー
ト系紫外線吸収剤及び立体障害アミン系紫外線吸収剤の
うちから選択された紫外線吸収剤１種又は２種以上を含
み、該ハードコート層上に所定の厚さ以上で形成された
二酸化チタン層を含む多層反射防止膜を有することを特
徴とする眼鏡レンズ。1. A benzophenone-based ultraviolet absorber in a lens substrate and / or a hard coat layer formed thereon,
One or more UV absorbers selected from benzotriazole-based UV absorbers, cyanoacrylate-based UV absorbers and sterically hindered amine-based UV absorbers, and having a predetermined thickness or more on the hard coat layer. A spectacle lens having a multilayer antireflection film including the titanium dioxide layer formed in 1.
９０〜４００ｎｍである請求項１記載の眼鏡レンズ。2. The spectacle lens according to claim 1, wherein the total thickness of the titanium dioxide layer is 90 to 400 nm.
素層、二酸化チタン層、二酸化珪素層、二酸化チタン層
及び二酸化珪素層からなる請求項１記載の眼鏡レンズ。3. The spectacle lens according to claim 1, wherein the multilayer antireflection film comprises a silicon dioxide layer, a titanium dioxide layer, a silicon dioxide layer, a titanium dioxide layer and a silicon dioxide layer from the side of the substrate.