JP5551330B2 - Lubricating oil composition - Google Patents
Lubricating oil composition Download PDFInfo
- Publication number
- JP5551330B2 JP5551330B2 JP2007046308A JP2007046308A JP5551330B2 JP 5551330 B2 JP5551330 B2 JP 5551330B2 JP 2007046308 A JP2007046308 A JP 2007046308A JP 2007046308 A JP2007046308 A JP 2007046308A JP 5551330 B2 JP5551330 B2 JP 5551330B2
- Authority
- JP
- Japan
- Prior art keywords
- lubricating oil
- oil composition
- viscosity
- kinematic viscosity
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、潤滑油組成物に関する。詳しくは、低粘度かつ疲労寿命に優れ、特に自動車の変速機用潤滑油として好適な潤滑油組成物に関する。 The present invention relates to a lubricating oil composition. Specifically, the present invention relates to a lubricating oil composition that has a low viscosity and excellent fatigue life, and is particularly suitable as a lubricating oil for automobile transmissions.
近年、地球規模の二酸化炭素排出量問題と世界的なエネルギー需要の増大を背景とし、自動車の省燃費化に対する要求はますます高くなっている。その中で、変速機にも従来に増して動力伝達効率の向上が求められており、その重要な構成要素である潤滑油にも高トルク容量化が求められている。
例えば、変速機の省燃費化手段の一つとして、潤滑油の低粘度化が挙げられる。変速機の中でも自動車用の自動変速機や無段変速機はトルクコンバータ、湿式クラッチ、歯車軸受機構、オイルポンプ、油圧制御機構などを有しており、これらに使用される潤滑油をより低粘度化することにより、攪拌抵抗および摩擦抵抗が低減され、動力の伝達効率が向上することで自動車の燃費の向上が可能となる。
In recent years, against the background of the global carbon dioxide emission problem and the increase in global energy demand, there has been an increasing demand for fuel saving in automobiles. Among them, the transmission is also required to improve the power transmission efficiency as compared with the prior art, and the lubricating oil which is an important component of the transmission is also required to have a high torque capacity.
For example, one of the means for reducing the fuel consumption of the transmission is to reduce the viscosity of the lubricating oil. Among automatic transmissions, automatic transmissions and continuously variable transmissions for automobiles have a torque converter, a wet clutch, a gear bearing mechanism, an oil pump, a hydraulic control mechanism, and the like. As a result, the stirring resistance and the frictional resistance are reduced, and the power transmission efficiency is improved, thereby improving the fuel efficiency of the automobile.
しかしながら、低粘度化された潤滑油は、金属間の接触を生じさせ易く，その結果，軸受や歯車等の機械要素部品の疲労寿命が大幅に低下し、焼付きなどが生じて変速機などに、不具合が生じることがある。
そこで、低粘度でありながらも疲労寿命が長い変速機用潤滑油組成物が特許文献１〜４に提案されている。
However, low-viscosity lubricants tend to cause metal-to-metal contact. As a result, the fatigue life of machine element parts such as bearings and gears is greatly reduced, resulting in seizures and other problems. , Malfunctions may occur.
Therefore, Patent Documents 1 to 4 propose a lubricating oil composition for a transmission that has a low fatigue life and a long fatigue life.
しかしながら、特許文献１〜４に開示された潤滑油組成物は、いずれも粘度指数向上剤としてポリメタアクリレート（ＰＭＡ）を使用しているため、粘度指数は向上するものの、油膜維持性に劣るという問題があった。特に、弾性流体潤滑(ＥＨＬ：Elasto Hydrodynamic Lubrication)の条件の下では、油膜の厚さを維持することは困難である。ＥＨＬとは、高い接触圧力のために潤滑面が変形するなどの影響が現れる流体潤滑領域のことであり、ベアリングやギヤなどの極めて狭い接触面積に高い荷重が負荷されるような高接触圧力領域で生じる潤滑状態である。このようなＥＨＬ条件下では、油膜の厚さを維持することが難しいので、金属同士の摩耗が起きやすく、結果として疲労寿命が短くなってしまうのである。 However, since the lubricating oil compositions disclosed in Patent Documents 1 to 4 all use polymethacrylate (PMA) as a viscosity index improver, the viscosity index is improved, but the oil film maintainability is inferior. There was a problem. In particular, it is difficult to maintain the thickness of the oil film under the condition of elastohydrodynamic lubrication (EHL). EHL is a fluid lubrication region where the lubrication surface deforms due to a high contact pressure, and a high contact pressure region where a high load is applied to a very narrow contact area such as a bearing or gear. This is a lubrication state that occurs in Under such EHL conditions, it is difficult to maintain the thickness of the oil film, so metal wear tends to occur, resulting in a short fatigue life.
そこで、本発明の目的は、低粘度かつ粘度の温度依存性が少なく、油膜維持性に優れ、さらに疲労寿命の長い潤滑油組成物を提供することである。 Accordingly, an object of the present invention is to provide a lubricating oil composition having a low viscosity, a low temperature dependence of viscosity, excellent oil film maintenance, and a long fatigue life.
前記課題を解決すべく、本発明は、以下のような潤滑油組成物を提供するものである。（１）基油が、１００℃における動粘度が１〜４．５ｍｍ２／ｓの鉱油からなる潤滑油基油のみと、１００℃における動粘度が２０００〜３０００ｍｍ２／ｓであるエチレン−プロピレン共重合体を組成物全量基準で２．５質量％以上と、を含有し、１００℃における動粘度が５．７９ｍｍ２／ｓ以下、かつ、粘度指数が１７０以上である潤滑油組成物であって、自動車の変速機用潤滑油として用いられることを特徴とした潤滑油組成物。 In order to solve the above problems, the present invention provides the following lubricating oil composition. (1) base oil, the only lubricating base oil kinematic viscosity of the mineral oil 1~4.5mm 2 / s at 100 ° C., a kinematic viscosity at 100 ° C. is 2000 ~3000mm 2 / s ethylene - propylene copolymer A lubricating oil composition containing 2.5% by mass or more of the polymer based on the total amount of the composition, having a kinematic viscosity at 100 ° C. of 5.79 mm 2 / s or less and a viscosity index of 170 or more. A lubricating oil composition characterized by being used as a lubricating oil for automobile transmissions .
本発明によれば、低粘度で、粘度の温度依存性が小さく、さらに、油膜維持性に優れ、疲労寿命の長い潤滑油組成物を提供することができる。特に、ＥＨＬ条件下で使用される変速機用潤滑油組成物として有効に使用することができる。 According to the present invention, it is possible to provide a lubricating oil composition having low viscosity, low viscosity temperature dependency, excellent oil film maintenance, and long fatigue life. In particular, it can be effectively used as a lubricating oil composition for transmissions used under EHL conditions.
本発明の潤滑油組成物に含まれる潤滑油基油は、１００℃における動粘度が１〜５ｍｍ２／ｓの範囲であるものを使用する。１００℃における動粘度が５ｍｍ２／ｓを超えると、潤滑油組成物の粘度指数が良好な値を示さない。また、粘性抵抗による動力損失が大きくなり、燃費改善効果が得られない。一方、１００℃における動粘度が１ｍｍ２／ｓ未満だと、油膜が十分に形成されず、摩擦抵抗が増大してしまう。また、蒸発損失も大きくなってしまう。潤滑油基油の１００℃における動粘度のより好ましい範囲は、２〜４．５ｍｍ２／ｓである。
なお、１００℃における動粘度は、ＪＩＳ Ｋ ２２８３に準拠して測定した値である。
The lubricating base oil contained in the lubricating oil composition of the present invention has a kinematic viscosity at 100 ° C. in the range of 1 to 5 mm 2 / s. When the kinematic viscosity at 100 ° C. exceeds 5 mm 2 / s, the viscosity index of the lubricating oil composition does not show a good value. In addition, power loss due to viscous resistance increases, and the fuel efficiency improvement effect cannot be obtained. On the other hand, when the kinematic viscosity at 100 ° C. is less than 1 mm 2 / s, the oil film is not sufficiently formed, and the frictional resistance increases. Moreover, evaporation loss also becomes large. A more preferable range of the kinematic viscosity at 100 ° C. of the lubricating base oil is 2 to 4.5 mm 2 / s.
The kinematic viscosity at 100 ° C. is a value measured according to JIS K 2283.
ここで、潤滑油基油は、特に限定されるものではなく、通常潤滑油の基油として使用されているものであれば鉱油および合成油を問わず使用できる。
鉱油としては、例えば、原油を常圧蒸留および減圧蒸留して得られた潤滑油留分を、溶剤脱れき、溶剤抽出、水素化分解、溶剤脱ろう、接触脱ろう、水素化精製、硫酸洗浄、あるいは白土処理等の精製処埋を適宜組み合わせて精製したパラフィン系、ナフテン系などの基油が好適に使用できる。
Here, the lubricating base oil is not particularly limited, and any mineral oil or synthetic oil can be used as long as it is normally used as a base oil for lubricating oil.
As mineral oils, for example, lubricating oil fractions obtained by subjecting crude oil to atmospheric distillation and vacuum distillation can be used for solvent removal, solvent extraction, hydrocracking, solvent dewaxing, catalytic dewaxing, hydrorefining, sulfuric acid washing Alternatively, base oils such as paraffinic and naphthenic oils, which are refined by appropriately combining refining treatment such as white clay treatment, can be suitably used.
また、合成油としては、例えば、ポリブテン、ポリオールエステル、二塩基酸エステル、リン酸エステル、ポリフェニルエーテル、アルキルベンゼン、アルキルナフタレン、ポリオキシアルキレングリコール、ネオペンチルグリコール、シリコーンオイル、トリメチロールプロパン、ペンタエリスリトール、さらにはヒンダードエステルなどを用いることができる。 Synthetic oils include, for example, polybutene, polyol ester, dibasic acid ester, phosphate ester, polyphenyl ether, alkylbenzene, alkylnaphthalene, polyoxyalkylene glycol, neopentyl glycol, silicone oil, trimethylolpropane, pentaerythritol. Furthermore, a hindered ester or the like can be used.
これらの鉱油や合成油で、１００℃における動粘度が１〜５ｍｍ２／ｓの範囲内のものを単独で使用しても良く、またこれらの中から選ばれる２種以上の基油を任意の割合で混合して使用してもよい。 Of these mineral oils and synthetic oils, those having a kinematic viscosity at 100 ° C. in the range of 1 to 5 mm 2 / s may be used alone, or two or more base oils selected from these may be used arbitrarily. You may mix and use it in a ratio.
また、本発明の潤滑油組成物には、１００℃における動粘度が４００〜４０００ｍｍ２／ｓのオレフィンコポリマー（ＯＣＰ）が組成物全量基準で２．５質量％以上含まれている。
ＯＣＰの１００℃における動粘度が４００ｍｍ２／ｓ未満であると、潤滑油組成物の油膜の粘性抵抗が小さくなってしまう。特にＥＨＬ条件下で使用した場合、荷重がかかると油膜の厚さを維持できない。すなわち、油膜が薄くなるので金属同士の摩耗が起きやすく、結果として疲労寿命が短くなってしまう。また、１００℃における動粘度が４０００ｍｍ２／ｓを超えると、油膜の形成能が著しく低下する。
ＯＣＰの１００℃における動粘度のより好ましい範囲は、６００ｍｍ２／ｓ〜３０００ｍｍ２／ｓである。
The lubricating oil composition of the present invention contains 2.5% by mass or more of an olefin copolymer (OCP) having a kinematic viscosity at 100 ° C. of 400 to 4000 mm 2 / s based on the total amount of the composition.
When the kinematic viscosity at 100 ° C. of OCP is less than 400 mm 2 / s, the viscosity resistance of the oil film of the lubricating oil composition becomes small. In particular, when used under EHL conditions, the thickness of the oil film cannot be maintained when a load is applied. That is, since the oil film becomes thin, metal wears easily, resulting in a short fatigue life. On the other hand, when the kinematic viscosity at 100 ° C. exceeds 4000 mm 2 / s, the ability to form an oil film is significantly reduced.
A more preferable range of the kinematic viscosity at 100 ° C. of OCP is 600mm 2 / s~3000mm 2 / s.
また、潤滑油組成物は、上記範囲の１００℃における動粘度であるＯＣＰが２．５質量％未満であると、高い粘度指数が得られず、温度の変化による粘度の変化が大きくなってしまう。なお、ＯＣＰの添加量は、ＯＣＰの１００℃における動粘度が大きいほど少ないほうがよい。
ＯＣＰとして、例えば、エチレン−プロピレン共重合体などを用いることができる。
In addition, when the OCP, which is the kinematic viscosity at 100 ° C. in the above range, is less than 2.5% by mass, a high viscosity index cannot be obtained, and the change in viscosity due to a change in temperature becomes large. . The amount of OCP added is preferably as small as the kinematic viscosity of OCP at 100 ° C. is large.
As the OCP, for example, an ethylene-propylene copolymer can be used.
さらに、本発明の潤滑油組成物には、各種添加剤を含むことができる。添加剤は、所望の特性を発揮する各種添加剤を使用する。例えば、酸化防止剤、他の極圧剤、耐摩耗剤、油性剤、清浄分散剤および流動点降下剤などが挙げられる。
酸化防止剤としては、アミン系酸化防止剤、フェノール系酸化防止剤および硫黄系酸化防止剤などが挙げられる。
Furthermore, the lubricating oil composition of the present invention can contain various additives. As the additive, various additives exhibiting desired characteristics are used. For example, antioxidants, other extreme pressure agents, antiwear agents, oiliness agents, cleaning dispersants, pour point depressants and the like can be mentioned.
Examples of the antioxidant include amine-based antioxidants, phenol-based antioxidants, and sulfur-based antioxidants.
アミン系酸化防止剤としては、例えば、モノオクチルジフェニルアミン、モノノニルジフェニルアミンなどのモノアルキルジフェニルアミン系、４，４’−ジブチルジフェニルアミン、４，４’−ジペンチルジフェニルアミン、４，４’−ジヘキシルジフェニルアミン、４，４’−ジヘプチルジフェニルアミン、４，４’−ジオクチルジフェニルアミン、４，４’−ジノニルジフェニルアミンなどのジアルキルジフェニルアミン系、テトラブチルジフェニルアミン、テトラヘキシルジフェニルアミン、テトラオクチルジフェニルアミン、テトラノニルジフェニルアミンなどのポリアルキルジフェニルアミン系、α−ナフチルアミン、フェニル−α−ナフチルアミン、ブチルフェニル−α−ナフチルアミン、ペンチルフェニル−α−ナフチルアミン、ヘキシルフェニル−α−ナフチルアミン、ヘプチルフェニル−α−ナフチルアミン、オクチルフェニル−α−ナフチルアミン、ノニルフェニル−α−ナフチルアミンなどのナフチルアミン系を挙げることができ、中でもジアルキルジフェニルアミン系のものが好ましい。 Examples of amine-based antioxidants include monoalkyl diphenylamines such as monooctyldiphenylamine and monononyldiphenylamine, 4,4′-dibutyldiphenylamine, 4,4′-dipentyldiphenylamine, 4,4′-dihexyldiphenylamine, 4, Polyalkyldiphenylamines such as 4'-diheptyldiphenylamine, 4,4'-dioctyldiphenylamine, dialkyldiphenylamines such as 4,4'-dinonyldiphenylamine, tetrabutyldiphenylamine, tetrahexyldiphenylamine, tetraoctyldiphenylamine, tetranonyldiphenylamine , Α-naphthylamine, phenyl-α-naphthylamine, butylphenyl-α-naphthylamine, pentylphenyl-α-naphthylamine , Hexylphenyl -α- naphthylamine, heptylphenyl -α- naphthylamine, octylphenyl -α- naphthylamine, there may be mentioned naphthylamine such as nonylphenyl -α- naphthylamine, among others those of the dialkyl diphenylamine is preferred.
フェノール系酸化防止剤としては、例えば、２，６−ジ−ｔｅｒｔ−ブチル−４−メチルフェノール、２，６−ジ−ｔｅｒｔ−ブチル−４−エチルフェノールなどのモノフェノール系、４，４’−メチレンビス（２，６−ジ−ｔｅｒｔ−ブチルフェノール）、２，２’−メチレンビス（４−エチル−６−ｔｅｒｔ−ブチルフェノール）などのジフェノール系を挙げることができる。
硫黄系酸化防止剤としては、例えばフェノチアジン、ペンタエリスリトール−テトラキス−（３−ラウリルチオプロピオネート）、ビス（３，５−ｔｅｒｔ−ブチル−４−ヒドロキシベンジル）スルフィド、チオジエチレンビス（３−（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシフェニル））プロピオネート、２，６−ジ−ｔｅｒｔ−ブチル−４−（４，６−ビス（オクチルチオ）−１，３，５−トリアジン−２−メチルアミノ）フェノールなどが挙げられる。
Examples of the phenolic antioxidant include monophenols such as 2,6-di-tert-butyl-4-methylphenol and 2,6-di-tert-butyl-4-ethylphenol, 4,4′- Examples include diphenols such as methylene bis (2,6-di-tert-butylphenol) and 2,2′-methylene bis (4-ethyl-6-tert-butylphenol).
Examples of the sulfur-based antioxidant include phenothiazine, pentaerythritol-tetrakis- (3-laurylthiopropionate), bis (3,5-tert-butyl-4-hydroxybenzyl) sulfide, thiodiethylenebis (3- ( 3,5-di-tert-butyl-4-hydroxyphenyl)) propionate, 2,6-di-tert-butyl-4- (4,6-bis (octylthio) -1,3,5-triazine-2- And methylamino) phenol.
これらの酸化防止剤は、一種を単独で用いてもよく、二種以上を組み合わせて用いてもよい。また、その配合量は、潤滑油組成物全量基準で、通常０．０１〜１０質量％、好ま
しくは０．０３〜５質量％の範囲で選定される。
These antioxidants may be used individually by 1 type, and may be used in combination of 2 or more type. Moreover, the compounding quantity is 0.01-10 mass% normally on the basis of lubricating oil composition whole quantity, Preferably it selects in the range of 0.03-5 mass%.
他の極圧剤、耐摩耗剤、油性剤としては、例えばジチオリン酸亜鉛（ＺｎＤＴＰ）、ジチオカルバミン酸亜鉛（ＺｎＤＴＣ）、硫化オキシモリブデンオルガノホスホロジチオエート（ＭｏＤＴＰ）、硫化オキシモリブデンジチオカルバメート（ＭｏＤＴＣ）などの有機金属系化合物が挙げられる。これらの配合量は、潤滑油組成物全量基準で、通常０．０５〜５質量％、好ましくは０．１〜３質量％である。 Examples of other extreme pressure agents, antiwear agents, and oil-based agents include zinc dithiophosphate (ZnDTP), zinc dithiocarbamate (ZnDTC), sulfurized oxymolybdenum organophosphorodithioate (MoDTP), and sulfurized oxymolybdenum dithiocarbamate (MoDTC). And organometallic compounds such as These compounding quantities are 0.05-5 mass% normally on the basis of lubricating oil composition whole quantity, Preferably it is 0.1-3 mass%.
また、ステアリン酸、オレイン酸などの脂肪族飽和及び不飽和モノカルボン酸、ダイマー酸、水添ダイマー酸などの重合脂肪酸、リシノレイン酸、１２−ヒドロキシステアリン酸などのヒドロキシ脂肪酸、ラウリルアルコール、オレイルアルコールなどの脂肪族飽和及び不飽和モノアルコール、ステアリルアミン、オレイルアミンなどの脂肪族飽和及び不飽和モノアミン、ラウリン酸アミド、オレイン酸アミドなどの脂肪族飽和及び不飽和モノカルボン酸アミドなどの油性剤が挙げられる。
これらの油性剤の好ましい配合量は、潤滑油組成物全量基準で０．０１〜１０質量％の範囲であり、０．１〜５質量％の範囲が特に好ましい。
In addition, aliphatic saturated and unsaturated monocarboxylic acids such as stearic acid and oleic acid, polymerized fatty acids such as dimer acid and hydrogenated dimer acid, hydroxy fatty acids such as ricinoleic acid and 12-hydroxystearic acid, lauryl alcohol, oleyl alcohol, etc. Oily agents such as aliphatic saturated and unsaturated monoalcohols, aliphatic saturated and unsaturated monoamines such as stearylamine and oleylamine, aliphatic saturated and unsaturated monocarboxylic amides such as lauric acid amide and oleic acid amide .
The preferable compounding amount of these oil-based agents is in the range of 0.01 to 10% by mass, particularly preferably in the range of 0.1 to 5% by mass, based on the total amount of the lubricating oil composition.
清浄分散剤としては、例えばコハク酸イミド類、ホウ素含有コハク酸イミド類、ベンジルアミン類、ホウ素含有ベンジルアミン類、コハク酸エステル類、脂肪酸あるいはコハク酸で代表される一価又は二価カルボン酸アミド類などの無灰系分散剤、中性金属スルホネート、中性金属フェネート、中性金属サリチレート、中性金属ホスホネート、塩基性スルホネート、塩基性フェネート、塩基性サリチレート、過塩基性スルホネート、過塩基性サリチレート、過塩基性ホスホネートなどの金属系清浄剤が挙げられる。これらの配合量は、潤滑油組成物全量基準で、通常０．１〜２０質量％、好ましくは０．５〜１０質量％である。
流動点降下剤としては、重量平均分子量が５万〜１５万程度のポリメタクリレートなどを用いることができる。
Examples of the detergent / dispersant include succinimides, boron-containing succinimides, benzylamines, boron-containing benzylamines, succinic acid esters, monovalent or divalent carboxylic acid amides represented by fatty acids or succinic acid. Ashless dispersants, neutral metal sulfonates, neutral metal phenates, neutral metal salicylates, neutral metal phosphonates, basic sulfonates, basic phenates, basic salicylates, overbased sulfonates, overbased salicylates And metal detergents such as overbased phosphonates. These compounding quantities are 0.1-20 mass% normally on the basis of lubricating oil composition whole quantity, Preferably it is 0.5-10 mass%.
As the pour point depressant, polymethacrylate having a weight average molecular weight of about 50,000 to 150,000 can be used.
本発明の潤滑油組成物には、所望により、前記以外の添加剤、例えば防錆剤、金属不活性化剤、消泡剤、界面活性剤などを含有させることができる。
防錆剤としては、例えば、アルケニルコハク酸やその部分エステルなどが、金属腐食防止剤としては、例えば、ベンゾトリアゾール系、ベンズイミダゾール系、ベンゾチアゾール系、チアジアゾール系などが、金属不活性化剤としては、例えば、ベンゾトリアゾール、ベンゾトリアゾール誘導体、ベンゾチアゾール、ベンゾチアゾール誘導体、トリアゾール、トリアゾール誘導体、ジチオカルバメート、ジチオカルバメート誘導体、イミダゾール、イミダゾール誘導体などが用いられる。消泡剤としては、例えば、ジメチルポリシロキサン、ポリアクリレートなどが、界面活性剤としては、例えば、ポリオキシエチレンアルキルフェニルエーテルなどが用いられる。
If desired, the lubricating oil composition of the present invention may contain additives other than those described above, such as a rust inhibitor, a metal deactivator, an antifoaming agent, and a surfactant.
Examples of rust inhibitors include alkenyl succinic acid and partial esters thereof, and examples of metal corrosion inhibitors include benzotriazole, benzimidazole, benzothiazole, thiadiazole, and the like as metal deactivators. For example, benzotriazole, benzotriazole derivative, benzothiazole, benzothiazole derivative, triazole, triazole derivative, dithiocarbamate, dithiocarbamate derivative, imidazole, imidazole derivative and the like are used. Examples of the antifoaming agent include dimethylpolysiloxane and polyacrylate, and examples of the surfactant include polyoxyethylene alkylphenyl ether.
なお、これら各種添加剤を合わせた配合量は、潤滑油組成物全量基準で、通常０．１〜２０質量％、好ましくは５〜１５質量％となるように調整する。 In addition, the compounding quantity which match | combined these various additives is 0.1-20 mass% normally based on lubricating oil composition whole quantity basis, Preferably it adjusts so that it may become 5-15 mass%.
以上の配合で調整された潤滑油組成物は、１００℃における動粘度が６．５ｍｍ２／ｓ以下である。１００℃における動粘度が６．５ｍｍ２／ｓを超えると、粘度が高いために摩擦抵抗が大きくなり、動力の伝達効率が低下する。
また、潤滑油組成物の粘度指数は１６０以上、より好ましくは１７０以上である。粘度指数が１６０未満であると、温度の変化による粘度変化が大きくなる恐れがあり好ましくない。
The lubricating oil composition prepared by the above blending has a kinematic viscosity at 100 ° C. of 6.5 mm 2 / s or less. When the kinematic viscosity at 100 ° C. exceeds 6.5 mm 2 / s, since the viscosity is high, the frictional resistance increases, and the power transmission efficiency decreases.
Further, the viscosity index of the lubricating oil composition is 160 or more, more preferably 170 or more. If the viscosity index is less than 160, the viscosity change due to temperature change may increase, which is not preferable.
以上より、１００℃における動粘度が１〜５ｍｍ２／ｓである潤滑油基油と、１００℃における動粘度が４００〜４０００ｍｍ２／ｓのＯＣＰを少なくとも２．５質量％以上と、添加剤とを含有する潤滑油組成物の１００℃における動粘度が６．５ｍｍ２／ｓ以下、かつ、粘度指数が１６０以上であるように潤滑油基油とＯＣＰの添加量を調整するものである。そして、このようにして調整した潤滑油組成物は、油膜維持性に優れており、金属同士の摩耗が起きにくく、疲労寿命が長い。
したがって、低粘度かつ粘度の温度依存性が少なく、油膜維持性に優れた疲労寿命の長い潤滑油組成物を提供することができる。
From the above, at least 2.5 mass% or more of the lubricating base oil having a kinematic viscosity at 100 ° C. of 1 to 5 mm 2 / s, the OCP having a kinematic viscosity at 100 ° C. of 400 to 4000 mm 2 / s, The lubricating oil base oil and the OCP are adjusted so that the kinematic viscosity at 100 ° C. of the lubricating oil composition containing no more than 6.5 mm 2 / s and the viscosity index is 160 or more. And the lubricating oil composition adjusted in this way is excellent in oil film maintenance property, wear of metals does not occur easily, and fatigue life is long.
Therefore, it is possible to provide a lubricating oil composition having a low fatigue viscosity and a low temperature dependency of the viscosity and having an excellent oil film maintenance property and a long fatigue life.
このような特性を備えた潤滑油組成物は、特にＥＨＬ条件下でその特性を発揮できるので、自動車などの変速機用潤滑油として好適に用いられる。 Since the lubricating oil composition having such characteristics can exhibit the characteristics particularly under EHL conditions, it is suitably used as a lubricating oil for transmissions of automobiles and the like.
次に、実施例を挙げて本発明をさらに詳しく説明するが、本発明はこれらの実施例の記載内容に何ら制約されるものではない。 EXAMPLES Next, although an Example is given and this invention is demonstrated in more detail, this invention is not restrict | limited at all to the content of description of these Examples.
[実施例１〜５、比較例１〜８]
表１に示す組成で潤滑油組成物を調整し、調整した組成物の１００℃における動粘度、粘度指数および摩擦係数立ち上がり時間を以下に示す方法で測定した。
[Examples 1-5, Comparative Examples 1-8]
A lubricating oil composition was prepared with the composition shown in Table 1, and the kinematic viscosity, viscosity index, and friction coefficient rise time at 100 ° C. of the prepared composition were measured by the following methods.
[１００℃における動粘度]
ＪＩＳ Ｋ ２２８３に準拠して測定した。
[Kinematic viscosity at 100 ° C]
The measurement was performed according to JIS K 2283.
[粘度指数（ＶＩ：Viscosity Index）]
ＪＩＳ Ｋ ２２８３に準拠して測定した。
[Viscosity Index (VI)]
The measurement was performed according to JIS K 2283.
[摩擦係数立ち上がり時間]
摩擦係数立ち上がり時間とは、金属と金属との間に摩擦が発生した場合その摩擦係数は時間とともに増大するが、ある摩擦係数に到達するまでの時間をｍsecで表したものである。なお、摩擦係数立ち上がり時間と，４球試験による転がり疲労寿命には相関係数０．９７の相関が確認されている。
測定にはブロックオンリング試験機を用い，１ｍ／ｓの状態で無負荷から，５０ｋｇｆの荷重をかけた時における摩擦係数の変化を測定した。本実施例では、摩擦係数μ＝０．０２となる時間を測定し、摩擦係数立ち上がり時間とした。摩擦係数立ち上がり時間は、２７５ｍsec以上であることが好ましい。
上記の方法により測定した実施例の結果を表１に、比較例の結果を表２に示す。
[Friction coefficient rise time]
The friction coefficient rise time is the time taken to reach a certain friction coefficient in msec, although the friction coefficient increases with time when friction occurs between metals. Note that a correlation coefficient of 0.97 has been confirmed between the friction coefficient rise time and the rolling fatigue life of the four-ball test.
A block-on-ring tester was used for the measurement, and the change in the coefficient of friction when a load of 50 kgf was applied from no load at 1 m / s was measured. In this example, the time when the friction coefficient μ = 0.02 was measured and used as the friction coefficient rise time. The friction coefficient rise time is preferably 275 msec or more.
The results of Examples measured by the above method are shown in Table 1, and the results of Comparative Examples are shown in Table 2.
実施例および比較例では、基油として、ＡＰＩ（American Petroleum Institute、米国石油協会）が規定しているGroup IIの基油を用い、添加剤には、インフィニアム社製、商品名「Ｉｎｆｉｎｅｕｍ Ｔ４２６１」を用いた。 In Examples and Comparative Examples, Group II base oil defined by API (American Petroleum Institute, American Petroleum Institute) is used as the base oil, and the additive “Infineum T4261” manufactured by Infinium is used as the additive. Was used.
表１が示すように、本発明の潤滑油組成物である実施例１〜５はいずれも、摩擦係数立ち上がり時間が２７５ｍsec以上で、摩擦係数μ＝０．０２になるまでの時間が長い。すなわち、油膜が維持される時間が長いということである。したがって、油膜維持性に優れており、さらに、１００℃における動粘度が６．５ｍｍ２／ｓ以下と低粘度で、粘度指数も１６０以上で良好である。 As shown in Table 1, in all of Examples 1 to 5 which are the lubricating oil composition of the present invention, the friction coefficient rise time is 275 msec or more, and the time until the friction coefficient μ = 0.02 is long. That is, the time for which the oil film is maintained is long. Therefore, it is excellent in oil film maintenance, and has a kinematic viscosity at 100 ° C. of 6.5 mm 2 / s or less and a viscosity index of 160 or more.
表２が示すように、比較例１〜８は、潤滑油組成物の１００℃における動粘度、粘度指数、摩擦係数立ち上がり時間のうち少なくとも一つ以上が良好な範囲から外れているため、低粘度、粘度指数および油膜維持性に優れるという３つの特性を同時に発揮することができない。 As Table 2 shows, Comparative Examples 1 to 8 have low viscosity because at least one of the kinematic viscosity, viscosity index, and friction coefficient rise time at 100 ° C. of the lubricating oil composition is out of the good range. The three properties of excellent viscosity index and oil film maintenance cannot be exhibited at the same time.
本発明は、例えば、自動車の変速機用潤滑油、パワーステアリング油、ショックアブソーバ油、エンジン油及び自動車・産業用ギヤー油、油圧油、軸受油などに好適に用いられるが、特に、EHL条件下で使用される自動車の自動変速機、手動変速機、無段変速機などの変速機用潤滑油として好適に利用することができる。 The present invention is suitably used for, for example, lubricating oil for automobile transmissions, power steering oil, shock absorber oil, engine oil and automobile / industrial gear oil, hydraulic oil, bearing oil, etc. Can be suitably used as lubricating oil for transmissions of automatic transmissions, manual transmissions, continuously variable transmissions and the like of automobiles used in the above.
Claims (1)
１００℃における動粘度が２０００〜３０００ｍｍ２／ｓであるエチレン−プロピレン共重合体を組成物全量基準で２．５質量％以上と、を含有し、
１００℃における動粘度が５．７９ｍｍ２／ｓ以下、かつ、
粘度指数が１７０以上である潤滑油組成物であって、
自動車の変速機用潤滑油として用いられることを特徴とした潤滑油組成物。 The base oil is only a lubricating base oil composed of a mineral oil having a kinematic viscosity at 100 ° C. of 1 to 4.5 mm 2 / s,
An ethylene-propylene copolymer having a kinematic viscosity at 100 ° C. of 2000 to 3000 mm 2 / s and 2.5% by mass or more based on the total amount of the composition,
The kinematic viscosity at 100 ° C. is 5.79 mm 2 / s or less, and
A lubricating oil composition having a viscosity index of 170 or more,
A lubricating oil composition characterized by being used as a lubricating oil for an automobile transmission .