JP5302756B2 - Polyester film - Google Patents

Polyester film Download PDF

Info

Publication number
JP5302756B2
JP5302756B2 JP2009107195A JP2009107195A JP5302756B2 JP 5302756 B2 JP5302756 B2 JP 5302756B2 JP 2009107195 A JP2009107195 A JP 2009107195A JP 2009107195 A JP2009107195 A JP 2009107195A JP 5302756 B2 JP5302756 B2 JP 5302756B2
Authority
JP
Japan
Prior art keywords
film
polyester film
polyester
layer
present
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2009107195A
Other languages
Japanese (ja)
Other versions
JP2010254826A (en
Inventor
智久 齋藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsubishi Plastics Inc
Original Assignee
Mitsubishi Plastics Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Plastics Inc filed Critical Mitsubishi Plastics Inc
Priority to JP2009107195A priority Critical patent/JP5302756B2/en
Publication of JP2010254826A publication Critical patent/JP2010254826A/en
Application granted granted Critical
Publication of JP5302756B2 publication Critical patent/JP5302756B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、紫外線(以下、UVと略記することがある)照射で着色(カラ−チェンジ)する有機フォトクロミック化合物を含むポリエステルフィルムであり、UV照射後に可視範囲でカラーチェンジの機能を有するポリエステルフィルムに関するものである。   The present invention relates to a polyester film containing an organic photochromic compound that is colored (color-changed) by irradiation with ultraviolet rays (hereinafter sometimes abbreviated as UV), and has a color-changing function in the visible range after UV irradiation. Is.

近年、太陽電池や電子機器、さらには建材などの生活装飾品関連に至るまで多方面で機能性ポリエステルフィルムが使われている。これらの用途では安価で、環境に優しく、高機能性のポリエステルフィルムが望まれている。   In recent years, functional polyester films have been used in a variety of fields ranging from solar cells, electronic equipment, and other home decorations such as building materials. In these applications, low-cost, environmentally friendly and highly functional polyester films are desired.

既存のポリエステルフィルムでは、生活用品装飾における建材用途として、主流のインクジェット法によるプリントが施されたポリエステルフィルムが知られている。インクジェット法の問題点としては、様々なポリマーや顔料を多量に使用することから環境への負荷が大きい、また、汚染などのメンテナンスや設備投資費の大きさ、ランニングコスト、さらには、乾燥工程や、フィルム厚みの変化などの技術的な難点が挙げられる。   As an existing polyester film, a polyester film that has been printed by a mainstream inkjet method is known as a building material application for household goods decoration. The problems with the inkjet method are that a large amount of various polymers and pigments are used, so the burden on the environment is large, the size of maintenance such as contamination, capital investment costs, running costs, and the drying process and And technical difficulties such as changes in film thickness.

従来のインクジェット法ではなく、例えば、UV感光型のカラーチェンジ性能を有するポリエステルフィルムは、光触媒をコーティングした窓ガラスに貼ることで、紫外線強度測定の目安になること、また、同様の用途として、太陽電池における紫外線強度測定の目安になることなどから、その活用が期待されている。   For example, a polyester film having UV-sensitive color change performance is not a conventional ink jet method, but can be used as a measure of ultraviolet intensity by sticking it to a window glass coated with a photocatalyst. It is expected to be used because it can be used as a standard for measuring the UV intensity of batteries.

さらなる例としては、電子部品におけるUV感光マーカーや光センサー技術としての用途可能性があるばかりではなく、UV感光着色技術を用いた美しい生活用品への応用の可能性もある。   As a further example, there is not only the possibility of use as a UV photosensitive marker or photosensor technology in electronic components, but also the possibility of application to beautiful daily goods using UV photosensitive coloring technology.

そこで、ポリエステルフィルムに、ある種のUV感光着色機能を付与できたならば、インクジェット法に代わる新しい新規なポリエステルフィルムを提供することができる。   Therefore, if a certain UV photosensitive coloring function can be imparted to the polyester film, a new novel polyester film that can replace the ink jet method can be provided.

特開2007−146014号公報JP 2007-146014 A

本発明は、上記実情に鑑みなされたものであって、その解決課題は、インクジェット法による環境負荷、コストなどの問題を解決し、安価で簡便な紫外線照射によってカラーチェンジすることが可能であり、屋外向けの建材など様々な用途で紫外線強度測定に利用でき、また、電子部品におけるUV感光マーカーや光センサー技術としての用途への適用もできるポリエステルフィルムを提供することにある。   The present invention has been made in view of the above circumstances, and its solution is to solve problems such as environmental impact and cost due to the inkjet method, and it is possible to change the color by cheap and simple ultraviolet irradiation, An object of the present invention is to provide a polyester film that can be used for ultraviolet intensity measurement in various uses such as outdoor building materials, and can also be applied to uses as UV photosensitive markers and optical sensor technology in electronic parts.

本発明者は、上記実情に鑑み鋭意検討した結果、特定の構成を有するポリエステルフィルムによれば、上記課題を容易に解決できることを見いだし、本発明を完成するに至った。   As a result of intensive studies in view of the above circumstances, the present inventor has found that the above problem can be easily solved by a polyester film having a specific configuration, and has completed the present invention.

すなわち、本発明の要旨は、表面粗さ(Ra)が0.1〜1,0μmの範囲のフィルム表面を構成するポリエステル層が平均粒径3〜10μmの粒子を3〜30重量%含有する、三層以上の構成の積層ポリエステルフィルであって、当該積層フィルムの表層中に紫外線照射で着色する有機フォトクロミック化合物を含有し、当該有機フォトクロミック化合物のポリエステルフィルム中の含有量が0.05〜1.0重量%であることを特徴とするポリエステルフィルムに存する。 That is, the gist of the present invention is that the polyester layer constituting the film surface having a surface roughness (Ra) in the range of 0.1 to 1.0 μm contains 3 to 30% by weight of particles having an average particle size of 3 to 10 μm. It is a laminated polyester film having a structure of three or more layers, and an organic photochromic compound that is colored by ultraviolet irradiation is contained in the surface layer of the laminated film, and the content of the organic photochromic compound in the polyester film is 0.05 to 1. 0 resides in a polyester film, wherein the percentages by weight.

本発明のポリエステルフィルムによれば、有機フォトクロミック化合物を適量範囲内で練り込むことで、カラーチェンジ性能を持つ有機フォトクロミック化合物含有ポリエステルフィルムを提供することができる。また、本発明のポリエステルフィルムは、太陽電池をはじめとして、屋外向けの建材など様々な用途で紫外線強度測定に利用できるばかりでなく、インクジェットなどの方法に代わる、生産ラインの何らかの目印になること、また、電子部品におけるUV感光マーカーや光センサー技術としての用途可能性があるばかりではなく、UV感光発光技術を用いた美しい生活用品への応用が期待できるため、その工業的価値は高い。   According to the polyester film of the present invention, an organic photochromic compound-containing polyester film having color change performance can be provided by kneading the organic photochromic compound within an appropriate amount range. In addition, the polyester film of the present invention can be used for measuring UV intensity in various applications such as outdoor building materials including solar cells, and can be used as a mark for production lines in place of ink jet methods. In addition to its potential use as a UV photosensitive marker and optical sensor technology in electronic parts, it can be expected to be applied to beautiful daily necessities using the UV photosensitive light emitting technology, so its industrial value is high.

以下、本発明をさらに詳細に説明する。本発明の着色性能を持つマット調ポリエステルフィルムの詳細について説明する。本発明における着色性能を持つポリエステルフィルムを構成する、ポリエステルフィルムは、機能性や価格の面を考慮した時に、多層構成が望ましく、2層、3層構成以外にも本発明の要旨を越えない限り、4層またはそれ以上の多層であってもよく、特に限定されるものではない。   Hereinafter, the present invention will be described in more detail. The details of the matte polyester film having the coloring performance of the present invention will be described. The polyester film constituting the polyester film having coloring performance in the present invention preferably has a multilayer structure in consideration of functionality and price, as long as it does not exceed the gist of the present invention other than the two-layer or three-layer structure. There may be four or more layers, and there is no particular limitation.

本発明のポリエステルフィルムを構成するポリエステルとしては、代表的には、例えば、構成単位の80モル%以上がエチレンテレフタレートであるポリエチレンテレフタレート、構成単位の80モル%以上がエチレン−2,6−ナフタレートであるポリエチレン−2,6−ナフタレート、構成単位の80モル%以上が1,4−シクロヘキサンジメチレンテレフタレートであるポリ−1,4−シクロヘキサンジメチレンテレフタレート等が挙げられる。それらの他にも、ポリエチレンイソフタレート、ポリブチレンテレフタレート等も挙げることができる。   As the polyester constituting the polyester film of the present invention, typically, for example, polyethylene terephthalate in which 80 mol% or more of the structural unit is ethylene terephthalate, and 80 mol% or more of the structural unit is ethylene-2,6-naphthalate. Specific polyethylene-2,6-naphthalate and poly-1,4-cyclohexanedimethylene terephthalate in which 80 mol% or more of the structural unit is 1,4-cyclohexanedimethylene terephthalate. In addition to these, polyethylene isophthalate, polybutylene terephthalate, and the like can also be mentioned.

本発明のポリエステルフィルムでは、表面外観を保つために、特定範囲のRa(算術平均粗さ)、すなわち高度の表面凹凸を付与することが必須となる。   In the polyester film of the present invention, in order to maintain the surface appearance, it is essential to provide a specific range of Ra (arithmetic mean roughness), that is, a high degree of surface unevenness.

以下に、本発明のポリエステルフィルムに高度の表面凹凸を付与させる方法について説明する。フィルム表面に凹凸を付与するに当たっては、当該表面を構成するポリエステル層に、不活性な無機粒子もしくは有機粒子を配合する方法が採用できる。   Hereinafter, a method for imparting a high degree of surface irregularities to the polyester film of the present invention will be described. In providing unevenness on the film surface, a method of blending inactive inorganic particles or organic particles into the polyester layer constituting the surface can be employed.

上記の不活性粒子としては、主に酸化ケイ素(シリカ)、酸化チタン、炭酸カルシウム、硫酸バリウム、酸化アルミニウム、カオリン、クレー、カーボンブラック等の公知の無機粒子、およびアクリル樹脂、ポリスチレン、有機シリコーン樹脂、アクリル−スチレン共重合体等の有機粒子が挙げられ、いずれか1種以上を配合すればよい。中でも酸化ケイ素(シリカ)が粒径分布、製膜性の点で好ましい。また、酸化ケイ素粒子に加えて他の粒子、例えば酸化チタンを配合することも好ましい態様の一つである。   The inert particles include mainly known inorganic particles such as silicon oxide (silica), titanium oxide, calcium carbonate, barium sulfate, aluminum oxide, kaolin, clay, carbon black, acrylic resin, polystyrene, and organic silicone resin. And organic particles such as an acrylic-styrene copolymer, and any one or more of them may be blended. Among these, silicon oxide (silica) is preferable from the viewpoints of particle size distribution and film formability. In addition to the silicon oxide particles, it is also one of preferred embodiments that other particles such as titanium oxide are blended.

本発明のフィルムにおいて、表面粗度(Ra)が0.10〜1.0μmの範囲のフィルム表面を構成するポリエステル層中の不活性粒子の平均粒径は、3〜10μmであり、好ましくは3.5〜9μm、さらに好ましくは4〜8μmの範囲である。平均粒径が3μm未満の場合、フィルム表面に十分な凹凸が形成されず、所望のRa、すなわち、いわゆるマットフィルム特有の外観が表現できない。一方、平均粒径が10μmを超えると、フィルム表面の凹凸の高低が大きくなりすぎて、粒子の脱落、製膜連続性の低下等の問題が生じる。   In the film of the present invention, the average particle diameter of the inert particles in the polyester layer constituting the film surface having a surface roughness (Ra) in the range of 0.10 to 1.0 μm is 3 to 10 μm, preferably 3 It is in the range of 5-9 μm, more preferably 4-8 μm. When the average particle size is less than 3 μm, sufficient unevenness is not formed on the film surface, and a desired Ra, that is, an appearance peculiar to a so-called mat film cannot be expressed. On the other hand, if the average particle diameter exceeds 10 μm, the unevenness of the film surface becomes too high, causing problems such as dropout of particles and deterioration of film forming continuity.

本発明において、表面粗度(Ra)が0.1〜1.0μmの範囲のフィルム表面を構成するポリエステル層中の不活性粒子の含有量は、3〜30重量%であり、好ましくは4〜20重量%、さらに好ましくは5〜15重量%である。不活性粒子の含有量が3重量%未満の場合は、フィルム表面に十分な凹凸が形成されず、所望のRa、すなわちマットフィルム特有の外観が表現できない。一方、含有量が30重量%を超える場合には、フィルム表面の凹凸が大きくなりすぎて、粒子の脱落や製膜連続性の低下等の問題が生じる。   In the present invention, the content of the inert particles in the polyester layer constituting the film surface having a surface roughness (Ra) in the range of 0.1 to 1.0 μm is 3 to 30% by weight, preferably 4 to 20% by weight, more preferably 5 to 15% by weight. When the content of the inert particles is less than 3% by weight, sufficient unevenness is not formed on the film surface, and desired Ra, that is, an appearance peculiar to the mat film cannot be expressed. On the other hand, when the content exceeds 30% by weight, the unevenness of the film surface becomes too large, causing problems such as dropout of particles and deterioration of film forming continuity.

本発明のポリエステルフィルムの固有粘度は、好ましくは0.60dl/g以上、さらに好ましくは0.65dl/g以上である。極限粘度が0.60dl/g未満の場合、十分な機械的強度を有するフィルムが得られないことがある。   The intrinsic viscosity of the polyester film of the present invention is preferably 0.60 dl / g or more, more preferably 0.65 dl / g or more. When the intrinsic viscosity is less than 0.60 dl / g, a film having sufficient mechanical strength may not be obtained.

本発明のポリエステルフィルムの少なくとも一方の表面の算術平均粗さ(Ra)は0.1〜1.0μmであることが必要であり、好ましくは0.4〜0.9μm、さらに好ましくは0.5〜0.8μmの範囲である。Raが0.1μm未満では、マットフィルム特有の外観が表現できない。一方、Raが1.0μmを超える場合には、フィルム製膜時に破断などを起こしやすくなり、生産性の面で問題になる。   The arithmetic average roughness (Ra) of at least one surface of the polyester film of the present invention needs to be 0.1 to 1.0 μm, preferably 0.4 to 0.9 μm, more preferably 0.5. It is in the range of ~ 0.8 μm. When Ra is less than 0.1 μm, the appearance unique to the mat film cannot be expressed. On the other hand, when Ra exceeds 1.0 μm, breakage or the like is likely to occur during film formation, which causes a problem in terms of productivity.

本発明のポリエステルフィルムの少なくとも一方の表面の十点平均粗さ(Rz)は、1.0〜5.0μmであることが好ましく、より好ましくは1.3〜4.0μm、さらに好ましくは1.0〜3.0μmの範囲内である。Rzが1.0μmに満たない場合、フィルム表面に十分な凹凸が形成されず、マットフィルム特有の外観が表現できない傾向にある。一方、Rzが5.0μmを超える場合、フィルム表面の凹凸が大きくなり過ぎる傾向にあり、その大きすぎる粒子のためにフィルム製膜時に破断などを起こしやすくなり、生産性の面で問題になることがある。   The ten-point average roughness (Rz) of at least one surface of the polyester film of the present invention is preferably 1.0 to 5.0 μm, more preferably 1.3 to 4.0 μm, still more preferably 1. It is in the range of 0 to 3.0 μm. When Rz is less than 1.0 μm, sufficient unevenness is not formed on the film surface, and there is a tendency that the appearance specific to the mat film cannot be expressed. On the other hand, when Rz exceeds 5.0 μm, the unevenness of the film surface tends to be too large, and because of the excessively large particles, breakage or the like tends to occur during film formation, which causes a problem in terms of productivity. There is.

本発明のポリエステルフィルムの総厚みは特に限定されないが、電子機器や車の内装などの装飾品として汎用に使われる可能性があるので、生産性やコストの面などを考慮して、ベースフィルム厚みは、適度の腰強さ、シワの発生回避の観点から通常20〜100μm、好ましくは25〜75μm、さらに好ましくは30〜50μmの範囲である。   Although the total thickness of the polyester film of the present invention is not particularly limited, it may be used for general purposes as a decorative item such as an electronic device or a car interior. Therefore, considering the productivity and cost, the thickness of the base film Is usually in the range of 20 to 100 μm, preferably 25 to 75 μm, and more preferably 30 to 50 μm from the viewpoint of moderate waist strength and avoiding the occurrence of wrinkles.

本発明のポリエステルフィルムは、2層以上からなることが好ましいが、上記条件を満足するのであれば、単層構造のフィルムであってもよい。   The polyester film of the present invention is preferably composed of two or more layers, but may be a single-layer film as long as the above conditions are satisfied.

少なくとも一方の最表面は高度の凹凸(マット調)を保持する必要から、特定の粒径(3〜10μm)の無機粒子もしくは有機粒子を相当量(3〜30重量%)含有する必要があり、そのような組成からなるフィルムは、しばしば単層構成では二軸延伸に耐えうる強度を保てなくなるおそれがあり、製膜連続性を保てないこともある。したがって、この表面層とは異なる少なくとも一つの粒子低減層(フィルム強度の維持に貢献するための層)を有する構成のものが好ましい。なお、本発明の要旨を越えない限り、この粒子低減層が2層以上の複数層から構成されても差し支えはない。   Since at least one outermost surface needs to maintain a high degree of unevenness (matte tone), it is necessary to contain a considerable amount (3 to 30% by weight) of inorganic particles or organic particles having a specific particle size (3 to 10 μm), A film having such a composition often has a risk of not being able to maintain the strength to withstand biaxial stretching in a single-layer structure, and may not be able to maintain film forming continuity. Therefore, a structure having at least one particle reducing layer (a layer for contributing to maintaining the film strength) different from the surface layer is preferable. As long as the gist of the present invention is not exceeded, the particle reduction layer may be composed of two or more layers.

少なくとも一方の最表面を構成する粒子多量層の厚さは、通常3μm以上であり、好ましくは5μm以上、さらに好ましくは7μm以上である。最表面層の厚さが3μm未満の場合、フィルム表面に十分な凹凸が形成されず、目的とするマットフィルム特有の外観が表現できない傾向にある。   The thickness of the particle multi-layer constituting at least one outermost surface is usually 3 μm or more, preferably 5 μm or more, more preferably 7 μm or more. When the thickness of the outermost surface layer is less than 3 μm, sufficient unevenness is not formed on the film surface, and the appearance peculiar to the target mat film tends not to be expressed.

この粒子多量層の厚さの上限については、フィルムの全厚さにより制限されるが、粒子低減層の比が低減することによる強度低下、コストアップの問題などを考慮すると、好ましくは全厚さの1/3以下、より好ましくは1/4以下である。   The upper limit of the thickness of the particle multi-layer is limited by the total thickness of the film. However, in consideration of the problem of strength reduction and cost increase due to the reduction of the ratio of the particle reduction layer, the total thickness is preferable. 1/3 or less, more preferably 1/4 or less.

本発明のポリエステルフィルムには、帯電防止性、滑り性、剥離性の向上のために表面塗布層を設けてもよい。塗布面はポリエステルフィルムの片面、両面を問わず、また両面の場合、同一の塗布層、異なる塗布層のどちらでもよい。   The polyester film of the present invention may be provided with a surface coating layer in order to improve antistatic properties, slip properties, and peelability. The coated surface is not limited to one side or both sides of the polyester film, and in the case of both sides, either the same coating layer or different coating layers may be used.

次に本発明のフィルムの製造方法について具体的に説明するが、以下の製造例に何ら限定されるものではない。すなわち、先に述べたポリエステル原料を使用し、ダイから押し出された溶融シートを冷却ロールで冷却固化して未延伸シートを得る方法が好ましい。この場合、シートの平面性を向上させるためシートと回転冷却ドラムとの密着性を高めることが好ましく、静電印加密着法および/または液体塗布密着法が好ましく採用される。次に得られた未延伸シートは二軸方向に延伸される。その場合、まず、前記の未延伸シートを一方向にロールまたはテンター方式の延伸機により延伸する。延伸温度は、通常70〜120℃、好ましくは80〜110℃であり、延伸倍率は通常2.5〜7.0倍、好ましくは3.0〜6.0倍である。次いで、一段目の延伸方向と直交する方向に延伸するが、その場合、延伸温度は通常70〜170℃であり、延伸倍率は通常3.0〜7.0倍、好ましくは3.5〜6.0倍である。そして、引き続き180〜270℃の温度で緊張下または30%以内の弛緩下で熱処理を行い、二軸配向フィルムを得る。上記の延伸においては、一方向の延伸を2段階以上で行う方法を採用することもできる。その場合、最終的に二方向の延伸倍率がそれぞれ上記範囲となるように行うのが好ましい。   Next, although the manufacturing method of the film of this invention is demonstrated concretely, it is not limited to the following manufacture examples at all. That is, a method of using the polyester raw material described above and cooling and solidifying a molten sheet extruded from a die with a cooling roll to obtain an unstretched sheet is preferable. In this case, in order to improve the flatness of the sheet, it is preferable to improve the adhesion between the sheet and the rotary cooling drum, and an electrostatic application adhesion method and / or a liquid application adhesion method is preferably employed. Next, the obtained unstretched sheet is stretched in the biaxial direction. In that case, first, the unstretched sheet is stretched in one direction by a roll or a tenter type stretching machine. The stretching temperature is usually 70 to 120 ° C., preferably 80 to 110 ° C., and the stretching ratio is usually 2.5 to 7.0 times, preferably 3.0 to 6.0 times. Next, the film is stretched in the direction perpendicular to the first stretching direction. In that case, the stretching temperature is usually 70 to 170 ° C., and the stretching ratio is usually 3.0 to 7.0 times, preferably 3.5 to 6 times. .0 times. Subsequently, heat treatment is performed at a temperature of 180 to 270 ° C. under tension or under relaxation within 30% to obtain a biaxially oriented film. In the above-described stretching, a method in which stretching in one direction is performed in two or more stages can be employed. In that case, it is preferable to carry out so that the draw ratios in the two directions finally fall within the above ranges.

また、本発明において有機フォトクロミック化合物含有ポリエステルフィルムを構成するポリエステルフィルム製造に関しては同時二軸延伸法を採用することもできる。同時二軸延伸法は、前記の未延伸シートを通常70〜120℃、好ましくは80〜110℃で温度コントロールされた状態で機械方向および幅方向に同時に延伸し配向させる方法であり、延伸倍率としては、面積倍率で4〜50倍、好ましくは7〜35倍、さらに好ましくは10〜25倍である。そして、引き続き、170〜250℃の温度で緊張下または30%以内の弛緩下で熱処理を行い、延伸配向フィルムを得る。上述の延伸方式を採用する同時二軸延伸装置に関しては、スクリュー方式、パンタグラフ方式、リニアー駆動方式等、従来公知の延伸方式を採用することができる。   In the present invention, a simultaneous biaxial stretching method may be employed for producing a polyester film constituting the organic photochromic compound-containing polyester film. The simultaneous biaxial stretching method is a method in which the above-mentioned unstretched sheet is usually stretched and oriented in the machine direction and the width direction at a temperature controlled normally at 70 to 120 ° C., preferably 80 to 110 ° C. Is 4 to 50 times, preferably 7 to 35 times, and more preferably 10 to 25 times in terms of area magnification. Subsequently, heat treatment is performed at a temperature of 170 to 250 ° C. under tension or under relaxation within 30% to obtain a stretched oriented film. With respect to the simultaneous biaxial stretching apparatus that employs the above-described stretching method, a conventionally known stretching method such as a screw method, a pantograph method, or a linear driving method can be employed.

本発明において使用することのできる有機フォトクロミック化合物として、ナフトピラン系化合物、スピロオキサジン系化合物、1,4−2H−オキサジン、ベンゾピラン系化合物などの有機フォトクロミック物質が挙げられるが、これらの中でもスピロオキサジン系化合物およびベンゾピラン系化合物が好ましい。   Examples of organic photochromic compounds that can be used in the present invention include organic photochromic substances such as naphthopyran compounds, spirooxazine compounds, 1,4-2H-oxazine, and benzopyran compounds. Among these, spirooxazine compounds And benzopyran compounds are preferred.

有機フォトクロミック化合物の具体例としては、1,3,3−トリメチルスピロ[インドリン−2,3’−(3H)−ナフト−(2,1−b)(1,4)−オキサジン]、6’−インドリノ−1,3,3−トリメチルスピロ[インドリン−2,3’−(3H)−ナフト−(2,1−b)(1,4)−オキサジン]、5−クロル−1,3,3−トリメチルスピロ[インドリン−2,3’−(3H)−ナフト−(2,1−b)(1,4)−オキサジン]、6’−ピペリジノ−1,3,3−トリメチルスピロ[インドリン−2,3’−(3H)−ナフト−(2,1−b)(1,4)−オキサジン]、1−ベンジル−3,3−ジメチルスピロ[インドリン−2,3’−(3H)−ナフト−(2,1−b)(1,4)−オキサジン]、1,3,5,6−テトラメチル−3−エチルスピロ[インドリン−2,3’−(3H)−ナフト−(2,1−b)(1,4)−オキサジン]、1,3,3,5,6−ペンタメチルスピロ[インドリン−2,3’−(3H)−ナフト−(2,1−b)(1,4)−オキサジン]、1,3,5,6−テトラメチル−3−エチルスピロ[インドリン−2,3’−(3H)−ピリド−(3,2−f)(1,4)−ベンゾオキサジン]、1,3’,3′−トリメチルスピロ(2H−1−ベンゾピラン−2,2’−インドリン)、スピロ[2H−クロメン−2,2’−トリシクロ[3.3.1.13.7]デカン]、5,7−ジメチル−スピロ[2H−クロメン−2,2’−トリシクロ[3.3.1.13.7]デカン]、等が挙げられる。   Specific examples of the organic photochromic compound include 1,3,3-trimethylspiro [indoline-2,3 ′-(3H) -naphtho- (2,1-b) (1,4) -oxazine], 6′- Indolino-1,3,3-trimethylspiro [indoline-2,3 ′-(3H) -naphtho- (2,1-b) (1,4) -oxazine], 5-chloro-1,3,3- Trimethylspiro [indoline-2,3 ′-(3H) -naphtho- (2,1-b) (1,4) -oxazine], 6′-piperidino-1,3,3-trimethylspiro [indoline-2, 3 ′-(3H) -naphtho- (2,1-b) (1,4) -oxazine], 1-benzyl-3,3-dimethylspiro [indoline-2,3 ′-(3H) -naphtho- ( 2,1-b) (1,4) -oxazine], 1,3,5,6- Tramethyl-3-ethylspiro [indoline-2,3 ′-(3H) -naphtho- (2,1-b) (1,4) -oxazine], 1,3,3,5,6-pentamethylspiro [indoline] -2,3 '-(3H) -naphtho- (2,1-b) (1,4) -oxazine], 1,3,5,6-tetramethyl-3-ethylspiro [indoline-2,3'- (3H) -pyrido- (3,2-f) (1,4) -benzoxazine], 1,3 ′, 3′-trimethylspiro (2H-1-benzopyran-2,2′-indoline), spiro [ 2H-chromene-2,2′-tricyclo [3.3.1.13.7] decane], 5,7-dimethyl-spiro [2H-chromene-2,2′-tricyclo [3.3.1.13]. .7] decane], and the like.

有機フォトクロミック化合物は、単独で使用することも可能であるが、変色機能を向上させることや耐光性を向上させることを目的として、高沸点タイプの溶媒、可塑剤、合成樹脂、ヒンダードアミン系化合物、ヒンダードフェノール系化合物などの助剤を併用することが好ましい。これらの化合物は、有機フォトクロミック化合物と併用する材料として公知のものであり、芳香族ジカルボン酸としては、テレフタル酸、2,6−ナフタレンジカルボン酸などが挙げられ、脂肪族グリコールとしては、エチレングリコール、ジエチレングリコール、1,4−シクロヘキサンジメタノール等が挙げられる。代表的なポリエステルとしては、ポリエチレンテレフタレート等が例示される。一方、共重合ポリエステルのジカルボン酸成分としては、イソフタル酸、フタル酸、テレフタル酸、2,6−ナフタレンジカルボン酸、アジピン酸、セバシン酸、オキシカルボン酸(例えば、p-オキシ安息香酸など)等の一種または二種以上が挙げられ、グリコール成分として、エチレングリコール、ジエチレングリコール、プロピレングリコール、ブタンジオール、1,4−シクロヘキサンジメタノール、ネオペンチルグリコール等の一種または二種以上が挙げられる。   Organic photochromic compounds can be used alone, but they have high boiling point solvents, plasticizers, synthetic resins, hindered amine compounds, hinders for the purpose of improving the discoloring function and improving light resistance. It is preferable to use an auxiliary such as a dophenol compound. These compounds are known as materials used in combination with organic photochromic compounds. Examples of aromatic dicarboxylic acids include terephthalic acid and 2,6-naphthalenedicarboxylic acid. Examples of aliphatic glycols include ethylene glycol, Examples include diethylene glycol and 1,4-cyclohexanedimethanol. Typical polyester includes polyethylene terephthalate and the like. On the other hand, the dicarboxylic acid component of the copolyester includes isophthalic acid, phthalic acid, terephthalic acid, 2,6-naphthalenedicarboxylic acid, adipic acid, sebacic acid, oxycarboxylic acid (for example, p-oxybenzoic acid, etc.), etc. 1 type or 2 types or more are mentioned, As a glycol component, 1 type or 2 types or more, such as ethylene glycol, diethylene glycol, propylene glycol, butanediol, 1, 4- cyclohexane dimethanol, neopentyl glycol, is mentioned.

有機フォトクロミック化合物のフィルム中の含有量は、0.05〜1.0重量%の範囲である。含有量が0.05重量%未満では、フィルムの変色効果が劣る。一方、1.0重量%を超えて含有する場合、フィルム中での劣化物により、不具合が生じる。   The content of the organic photochromic compound in the film is in the range of 0.05 to 1.0% by weight. When the content is less than 0.05% by weight, the discoloration effect of the film is inferior. On the other hand, when it contains exceeding 1.0 weight%, a malfunction arises with the degraded material in a film.

次に本発明におけるUV照射でカラ−チェンジを引き起こす有機フォトクロミック化合物のポリエステルへの練り込みについて説明する。それらの化合物はポリエステルレジンに練り込んだマスターバッチとして用いる方が好ましいが、ポリエステルレジンへのそれらの化合物の直接添加でもよい。   Next, the kneading of polyester with an organic photochromic compound that causes color change by UV irradiation in the present invention will be described. These compounds are preferably used as a masterbatch kneaded into a polyester resin, but may be directly added to the polyester resin.

さらに本発明におけるUVによりカラーチェンジ性能を有するポリエステルフィルムについて、有機フォトクロミック化合物の練り込みの層構成について説明する。有機フォトクロミック化合物はポリエステルフィルムの表層、もしくは中間層どちらへの練り込みでも構わない。フィルム全体として、上記の含有量となるように表層あるいは中間層の含有量を調整すればよい。   Furthermore, the layer structure of the kneading of the organic photochromic compound will be described for the polyester film having color change performance by UV in the present invention. The organic photochromic compound may be kneaded into either the surface layer or the intermediate layer of the polyester film. What is necessary is just to adjust content of a surface layer or an intermediate | middle layer so that it may become said content as the whole film.

本発明のマット調ポリエステルフィルムにおける、カラ−チェンジ(着色)とは、ポリエステルフィルム外観における色の変化である。詳しくは、輝度測定におけるコントラスト比で表現することができ、具体的には、UV照射部分と未照射部分の比から求められる相対輝度が101〜104程度の値、好ましくは104以上である。また、L*a*b*色差評価から求められるΔEによっても、着色を表現することができ、ΔE値が5.0〜20.0程度の値が好ましく、さらに好ましくは、20.0以上である。   The color change (coloring) in the matte polyester film of the present invention is a color change in the appearance of the polyester film. Specifically, it can be expressed by a contrast ratio in the luminance measurement. Specifically, the relative luminance obtained from the ratio of the UV irradiated portion to the unirradiated portion is a value of about 101 to 104, preferably 104 or more. Further, coloring can also be expressed by ΔE obtained from L * a * b * color difference evaluation, and the ΔE value is preferably about 5.0 to 20.0, more preferably 20.0 or more. is there.

以下、本発明を実施例によりさらに詳細に説明するが、本発明はその要旨を越えない限り、以下の実施例に限定されるものではない。また、本発明で用いた測定法および評価方法は次のとおりである。なお、本発明における各種の物性およびその測定方法、定義は下記のとおりである。また、以下において「部」および「%」とあるのは、それぞれ「重量部」および「重量%」を意味する。   EXAMPLES Hereinafter, although an Example demonstrates this invention further in detail, this invention is not limited to a following example, unless the summary is exceeded. The measurement method and evaluation method used in the present invention are as follows. In addition, the various physical property in this invention, its measuring method, and a definition are as follows. In the following, “parts” and “%” mean “parts by weight” and “% by weight”, respectively.

マット調ポリエステルフィルムの実施例、比較例について説明する。 Examples and comparative examples of the matte polyester film will be described.

(1)添加物の平均粒径(μm)
株式会社 島津製作所製遠心沈降式粒度分布測定装置SA−CP3型を用いてストークスの抵抗則に基づく沈降法によって粒子の大きさを測定した。測定により得られた粒子の等価球形分布における積算(体積基準)50%の値を用いて平均粒径とした。
(1) Average particle size of additive (μm)
The size of the particles was measured by a sedimentation method based on Stokes' resistance law using a centrifugal sedimentation type particle size distribution analyzer SA-CP3 manufactured by Shimadzu Corporation. The average particle diameter was determined by using a value of 50% of integration (volume basis) in the equivalent spherical distribution of particles obtained by measurement.

(2)ポリエステルの固有粘度(dl/g)
ポリエステル1gに対し、フェノール/テトラクロロエタン:50/50(重量比)の混合溶媒を100mlの比で加えて溶解させ、30℃で測定した。
(2) Intrinsic viscosity of polyester (dl / g)
A mixed solvent of phenol / tetrachloroethane: 50/50 (weight ratio) was added to 1 g of polyester at a ratio of 100 ml, and the mixture was measured at 30 ° C.

(3)算術平均粗さ(Ra)および十点平均粗さ(Rz)
小坂研究所製のサーフコーダSE3500を用いて、RaおよびRzを測定した。下記の条件でサンプルの片面(キャスト面)につき12回測定し、最大最小の2点を除いた十点の平均値をとった。
触針先端径:5μm
測定力:30mgf
測定長:2.5mm
カットオフ値:0.08mm
本発明の実施例、比較例において、得られたポリエステルフィルムについて、Raによる判断を行った。次のような基準で判断する。
○:0.10〜1.0以上
×:0.10より低いもしくは1.0より大きい
(3) Arithmetic average roughness (Ra) and ten-point average roughness (Rz)
Ra and Rz were measured using a surf coder SE3500 manufactured by Kosaka Laboratory. Measurement was performed 12 times on one side (cast surface) of the sample under the following conditions, and an average value of ten points excluding the maximum and minimum two points was taken.
Stylus tip diameter: 5μm
Measuring power: 30mgf
Measurement length: 2.5mm
Cut-off value: 0.08mm
In the examples and comparative examples of the present invention, the obtained polyester films were judged by Ra. Judgment is based on the following criteria.
○: 0.10 to 1.0 or more ×: lower than 0.10 or larger than 1.0

(4)有機フォトクロミック化合物含有ポリエステルフィルムの外観の目視評価
UVによる可逆的なカラーチェンジ(着色)性能を有するポリエステルフィルムにおいて、本発明は将来的には工業的生産を目的としていて、目視綺麗なポリエステルフィルムである事が第一条件となるため、得られたポリエステルフィルムについて、目視による外観の判断を行った。次のような基準で判断する。
○:外観良し
△:外観悪くはない
×:外観悪し
(4) Visual Evaluation of Appearance of Organic Photochromic Compound-Containing Polyester Film In the polyester film having reversible color change (coloring) performance by UV, the present invention is aimed at industrial production in the future. Since the first condition is that the film is a film, the appearance of the obtained polyester film was visually determined. Judgment is based on the following criteria.
○: Appearance is good △: Appearance is not bad ×: Appearance is bad

(5)ポリエステルフィルムのUV照射後の着色強度のコントラスト評価
輝度計を用いて、UV照射前のフィルムの非着色部分とUV照射後の着色部分のコントラスト比の評価を行った。具体的には、電通産業製フラットイルミネーター:HF−SL−A48LCFにサンプルを置き、さらに、コニカミノルタセンシング社製:CS−200を用い、測定視野角1°、サンプルと輝度計との距離を500mmとし、輝度値(cd/m)を測定した。なお、相対輝度(%)を下記式より求めた。
(5) Contrast evaluation of coloring strength after UV irradiation of polyester film Using a luminance meter, the contrast ratio between the non-colored portion of the film before UV irradiation and the colored portion after UV irradiation was evaluated. Specifically, a sample is placed on a flat illuminator manufactured by Dentsu Sangyo Co., Ltd .: HF-SL-A48LCF, and further, using Konica Minolta Sensing Co., Ltd. CS-200, the measurement viewing angle is 1 °, and the distance between the sample and the luminance meter is measured. The luminance value (cd / m 2 ) was measured at 500 mm. The relative luminance (%) was obtained from the following formula.

相対輝度=(UV未照射部分の測定値)÷(UV照射部分の測定値)×100
得られた相対輝度の値から下記基準で評価した。
Relative luminance = (measured value of UV non-irradiated part) ÷ (measured value of UV irradiated part) × 100
The relative luminance was evaluated according to the following criteria from the obtained relative luminance value.

◎:104を超える(強い着色)
○:102〜104(着色している)
△:101〜102(薄い着色)
×:101未満(ほとんど着色していない)
A: More than 104 (strong coloring)
○: 102 to 104 (colored)
Δ: 101-102 (lightly colored)
X: Less than 101 (almost not colored)

(6)ポリエステルフィルムのUV照射後の着色強度のΔE評価
得られたUV照射後のポリエステルフィルムについて、色差計を用いて、UV照射前のフィルムの非着色部分とUV照射後の着色部分のL*a*b*色差の評価を行った。具体的には、JIS Z 8729に従い、コニカミノルタ製色彩色差計CR−410(サンプル径50mm)を用いて、UV照射部分と非照射部分のL*a*b*色差値を測定した。このとき、光源はC/D65で、背面を白色とし、反射法にて測定を行った。測定回数は3回行い、平均値を採用した。その後、ΔL*(照射部分のL*値−非照射部分L*値)、Δa*(照射部分のa*値−非照射部分a*値)、Δb*(照射部分のb*値−非照射部分b*値)をそれぞれ求め、ΔE値を算出し、評価した。
なお、ΔE値を下記式より求めた。
(6) ΔE Evaluation of Coloring Strength after UV Irradiation of Polyester Film About the obtained polyester film after UV irradiation, using a color difference meter, L of the uncolored part of the film before UV irradiation and the colored part after UV irradiation * A * b * Color difference was evaluated. Specifically, according to JIS Z 8729, the L * a * b * color difference values of the UV irradiated portion and the non-irradiated portion were measured using a color difference meter CR-410 (sample diameter 50 mm) manufactured by Konica Minolta. At this time, the light source was C / D65, the back surface was white, and measurement was performed by a reflection method. The measurement was performed three times, and an average value was adopted. ΔL * (irradiated portion L * value−non-irradiated portion L * value), Δa * (irradiated portion a * value−non-irradiated portion a * value), Δb * (irradiated portion b * value−non-irradiated portion) (Part b * value) was calculated, and ΔE value was calculated and evaluated.
The ΔE value was determined from the following formula.

ΔE={(ΔL*)+(Δa*)+(Δb*)1/2
得られたΔEの値から下記基準で評価した。
◎:10.0を超える(強い着色)
○:5.0〜10.0(着色している)
△:2.5〜5.0(薄い着色)
×:2.5未満(ほとんど着色していない)
ΔE = {(ΔL *) 2 + (Δa *) 2 + (Δb *) 2 } 1/2
Evaluation was performed based on the following criteria from the obtained ΔE value.
A: Over 10.0 (strong coloring)
○: 5.0 to 10.0 (colored)
Δ: 2.5 to 5.0 (light color)
X: Less than 2.5 (almost not colored)

(7)ポリエステルフィルムのUV照射後の着色強度の目視評価
UVによる可逆的なカラーチェンジ(着色)性能を有するポリエステルフィルムにおいて、本発明は将来的には工業的生産を目的としていて、目視で変化が見て取れる事が第一条件となるため、得られたUV照射後のポリエステルフィルムについて、目視による強度の判断を行った。次のような基準で判断する。
◎:強い着色
○:着色している
△:薄い着色
×:着色していない
(7) Visual Evaluation of Coloring Strength after UV Irradiation of Polyester Film In the polyester film having reversible color change (coloring) performance by UV, the present invention aims at industrial production in the future and changes visually. Since the first condition is that it can be seen, the obtained polyester film after UV irradiation was visually evaluated for strength. Judgment is based on the following criteria.
◎: Strong coloring ○: Colored △: Light color ×: Not colored

実施例 1:
平均粒径4.5μmの無定型シリカ粒子を9.0%含有する、固有粘度0.71のポリエチレンテレフタレートチップと有機フォトクロミック化合物であるスピロオキサジン系化合物、1,3,3−トリメチルスピロ[インドリン−2,3’−(3H)−ナフト−(2,1−b)(1,4)−オキサジン]をそれぞれ99.72:0.28の割合で混合した混合原料を表層原料とし、平均粒径2.5μmの無定型シリカ粒子を600ppm含有する、固有粘度0.71のポリエチレンテレフタレートチップを中間層原料として、表層の混合原料と中間層のポリエステルを1:4の割合で2台の押出機に各々を供給し、各々290℃で溶融した後、40℃に設定した冷却ロール上に、2種3層(表層/中間層/表層)の層構成で共押出し冷却固化させて未延伸シートを得た。次いで、ロール周速差を利用してフィルム温度85℃で縦方向に3.4倍延伸した後、テンターに導き、横方向に120℃で4.0倍延伸し、225℃で熱処理を行った後、横方向に2%弛緩し、厚さ50μm(表層5μm、中間層40μm)のポリエステルフィルムを得た。得られたポリエステルフィルムは、白色のポリエステルフィルムであった。そのポリエステルフィルムについて、高圧水銀灯によるUV(ウシオ電気株式会社:UVC−402/1HN:302/1MN:JC01)光照射(181mW/cm,10m/分,d=100mm)を行い、カラーチェンジ性能を評価したところ、黄色着色状態への変化は良好なものであった。得られたフィルムの相対輝度は105%、ΔEは8.4(L*=87.01,a*=−0.97,b*=9.76)であった。
Example 1:
A polyethylene terephthalate chip having an intrinsic viscosity of 0.71 containing 9.0% of amorphous silica particles having an average particle diameter of 4.5 μm and a spirooxazine compound as an organic photochromic compound, 1,3,3-trimethylspiro [indoline- 2,3 ′-(3H) -naphtho- (2,1-b) (1,4) -oxazine] in a ratio of 99.72: 0.28, respectively, was used as a surface layer material, and the average particle size A polyethylene terephthalate chip having an intrinsic viscosity of 0.71 containing 2.5 μm of amorphous silica particles and having an intrinsic viscosity of 0.71 is used as an intermediate layer raw material. Each is supplied, melted at 290 ° C, and then coextruded in a layer configuration of two types and three layers (surface layer / intermediate layer / surface layer) on a cooling roll set to 40 ° C and solidified by cooling. Not to obtain an unstretched sheet. Next, the film was stretched 3.4 times in the machine direction at a film temperature of 85 ° C. using the roll peripheral speed difference, then led to a tenter, stretched 4.0 times at 120 ° C. in the transverse direction, and heat-treated at 225 ° C. Thereafter, the polyester film was relaxed by 2% in the lateral direction to obtain a polyester film having a thickness of 50 μm (surface layer: 5 μm, intermediate layer: 40 μm). The obtained polyester film was a white polyester film. The polyester film is irradiated with UV light (181 mW / cm 2 , 10 m / min, d = 100 mm) using a high-pressure mercury lamp (Ushio Electric Co., Ltd .: UVC-402 / 1HN: 302 / 1MN: JC01) to provide color change performance. As a result of evaluation, the change to the yellow colored state was satisfactory. The relative luminance of the obtained film was 105%, and ΔE was 8.4 (L * = 87.01, a * = − 0.97, b * = 9.76).

実施例2:
実施例1の原料と1,3,3−トリメチルスピロ[インドリン−2,3’−(3H)−ナフト−(2,1−b)(1,4)−オキサジン]の比をそれぞれ95.2:4.8の割合で混合した混合原料を表層の原料として用いて、ポリエステルフィルムを得るということ以外は同様の方法でフィルムを得た。得られたポリエステルフィルムは、白色のポリエステルフィルムであった。そのポリエステルフィルムについて、実施例1と同様の方法でUV照射行い、カラーチェンジ(着色)性能を評価したところ、黄色着色状態への変化は良好なものであった。得られたフィルムの相対輝度は105%、ΔEは24.2(L*=85.15,a*=−2.18,b*22.54)であった。
Example 2:
The ratio of the raw material of Example 1 to 1,3,3-trimethylspiro [indoline-2,3 ′-(3H) -naphtho- (2,1-b) (1,4) -oxazine] was 95.2 respectively. A film was obtained in the same manner except that a polyester film was obtained using the mixed raw material mixed at a ratio of 4.8 as a raw material for the surface layer. The obtained polyester film was a white polyester film. The polyester film was subjected to UV irradiation in the same manner as in Example 1 and the color change (coloring) performance was evaluated. As a result, the change to a yellow colored state was satisfactory. The relative luminance of the obtained film was 105%, and ΔE was 24.2 (L * = 85.15, a * = − 2.18, b * 22.54).

実施例3:
平均粒径4.5μmの無定型シリカ粒子を4.0重量%含むポリエステルチップを用いたということ以外、実施例1と同様の方法でポリエステルフィルムを得た。得られたポリエステルフィルムは、白色のポリエステルフィルムであった。そのポリエステルフィルムについて、実施例1と同様の方法でUV照射行い、カラーチェンジ(着色)性能を評価したところ、黄色着色状態への変化は良好なものであった。
Example 3:
A polyester film was obtained in the same manner as in Example 1 except that a polyester chip containing 4.0% by weight of amorphous silica particles having an average particle diameter of 4.5 μm was used. The obtained polyester film was a white polyester film. The polyester film was subjected to UV irradiation in the same manner as in Example 1 and the color change (coloring) performance was evaluated. As a result, the change to a yellow colored state was satisfactory.

実施例4:
平均粒径9.0μmの無定型シリカ粒子を3.5重量%含むポリエステルチップを用いたということ以外、実施例1と同様の方法でポリエステルフィルムを得た。得られたポリエステルフィルムは、白色のポリエステルフィルムであった。そのポリエステルフィルムについて、実施例1と同様の方法でUV照射行い、カラーチェンジ(着色)性能を評価したところ、黄色着色状態への変化は良好なものであった。
Example 4:
A polyester film was obtained in the same manner as in Example 1 except that a polyester chip containing 3.5% by weight of amorphous silica particles having an average particle size of 9.0 μm was used. The obtained polyester film was a white polyester film. The polyester film was subjected to UV irradiation in the same manner as in Example 1 and the color change (coloring) performance was evaluated. As a result, the change to a yellow colored state was satisfactory.

実施例5:
平均粒径9.0μmの無定型シリカ粒子を9.0重量%含むポリエステルチップを用いたということ以外、実施例1と同様の方法でポリエステルフィルムを得た。得られたポリエステルフィルムは、白色のポリエステルフィルムであった。そのポリエステルフィルムについて、実施例1と同様の方法でUV照射行い、カラーチェンジ(着色)性能を評価したところ、黄色着色状態への変化は良好なものであった。
Example 5:
A polyester film was obtained in the same manner as in Example 1 except that a polyester chip containing 9.0% by weight of amorphous silica particles having an average particle size of 9.0 μm was used. The obtained polyester film was a white polyester film. The polyester film was subjected to UV irradiation in the same manner as in Example 1 and the color change (coloring) performance was evaluated. As a result, the change to a yellow colored state was satisfactory.

実施例6:
平均粒径4.5μmの無定型シリカ粒子を25重量%含むポリエステルチップを用いたということ以外、実施例1と同様の方法でポリエステルフィルムを得た。得られたポリエステルフィルムは、白色のポリエステルフィルムであった。そのポリエステルフィルムについて、実施例1と同様の方法でUV照射行い、カラーチェンジ(着色)性能を評価したところ、黄色着色状態への変化は良好なものであった。
Example 6:
A polyester film was obtained in the same manner as in Example 1 except that a polyester chip containing 25% by weight of amorphous silica particles having an average particle size of 4.5 μm was used. The obtained polyester film was a white polyester film. The polyester film was subjected to UV irradiation in the same manner as in Example 1 and the color change (coloring) performance was evaluated. As a result, the change to a yellow colored state was satisfactory.

比較例1:
実施例1の原料と1,3,3−トリメチルスピロ[インドリン−2,3’−(3H)−ナフト−(2,1−b)(1,4)−オキサジン]の比をそれぞれ90.0:10.0の割合で混合した混合原料を表層の原料として用いて、ポリエステルフィルムを得るということ以外は同様の方法でフィルムを得た。得られたポリエステルフィルムは、黄色の外観の悪いポリエステルフィルムであった。そのポリエステルフィルムについて、実施例1と同様の方法でUV照射行い、カラーチェンジ(着色)性能を評価したところ、黄色着色状態は見た目でかなり強いものとなった。
Comparative Example 1:
The ratio of the raw material of Example 1 to 1,3,3-trimethylspiro [indoline-2,3 ′-(3H) -naphtho- (2,1-b) (1,4) -oxazine] was 90.0, respectively. A film was obtained by the same method except that a polyester film was obtained using a mixed raw material mixed at a ratio of 10.0 as a raw material for the surface layer. The obtained polyester film was a yellow polyester film with poor appearance. The polyester film was irradiated with UV in the same manner as in Example 1, and the color change (coloring) performance was evaluated. As a result, the yellow coloring state was considerably strong in appearance.

比較例2:
実施例1の原料と1,3,3−トリメチルスピロ[インドリン−2,3’−(3H)−ナフト−(2,1−b)(1,4)−オキサジン]の比をそれぞれ99.8:0.2の割合で混合した混合原料を表層の原料として用いて、ポリエステルフィルムを得るということ以外は同様の方法でフィルムを得た。得られたポリエステルフィルムは、白色のポリエステルフィルムであった。そのポリエステルフィルムについて、実施例1と同様の方法でUV照射行い、カラーチェンジ(着色)性能を評価したところ、黄色着色状態への変化はほとんど認められなかった。得られたフィルムの相対輝度は101%、ΔEは1.4(L*=88.30,a*=1.91,b*=0.89)であった。
Comparative Example 2:
The ratio of the raw material of Example 1 to 1,3,3-trimethylspiro [indoline-2,3 ′-(3H) -naphtho- (2,1-b) (1,4) -oxazine] was 99.8, respectively. : A film was obtained in the same manner except that a polyester film was obtained using a mixed raw material mixed at a ratio of 0.2 as a raw material for the surface layer. The obtained polyester film was a white polyester film. The polyester film was irradiated with UV in the same manner as in Example 1 and the color change (coloring) performance was evaluated. As a result, almost no change to a yellow colored state was observed. The relative luminance of the obtained film was 101%, and ΔE was 1.4 (L * = 88.30, a * = 1.91, b * = 0.89).

比較例3:
無定型シリカ粒子の粒径、含有量がもたらすポリエステルフィルムの外観について、比較検討を行った。平均粒径4.5μmの無定型シリカ粒子を2.0重量%含むポリエステルチップを用いたということ以外、実施例1と同様の方法でポリエステルフィルムを得た。得られたポリエステルフィルムは表面粗度が欠ける結果となった。
Comparative Example 3:
A comparative study was conducted on the appearance of the polyester film brought about by the particle size and content of the amorphous silica particles. A polyester film was obtained in the same manner as in Example 1 except that a polyester chip containing 2.0% by weight of amorphous silica particles having an average particle size of 4.5 μm was used. The obtained polyester film resulted in lack of surface roughness.

比較例4:
平均粒径4.5μmの無定型シリカ粒子を32重量%含むポリエステルチップを用いたということ以外、実施例1と同様の方法でポリエステルフィルムを得た。得られたポリエステルフィルムは、外観において凝集物由来の斑があり、また、破断などの生産性の低下が顕著であった。
Comparative Example 4:
A polyester film was obtained in the same manner as in Example 1 except that a polyester chip containing 32% by weight of amorphous silica particles having an average particle diameter of 4.5 μm was used. The obtained polyester film had spots derived from aggregates in appearance, and the reduction in productivity such as breakage was remarkable.

比較例5:
平均粒径2.0μmの無定型シリカ粒子を含むポリエステルチップを用いたということ以外、実施例1と同様の方法でポリエステルフィルムを得た。得られたポリエステルフィルムは表面粗度が欠ける結果となった。
Comparative Example 5:
A polyester film was obtained in the same manner as in Example 1 except that a polyester chip containing amorphous silica particles having an average particle size of 2.0 μm was used. The obtained polyester film resulted in lack of surface roughness.

比較例6:
平均粒径12μmの無定型シリカ粒子を含むポリエステルチップを用いたということ以外、実施例1と同様の方法でポリエステルフィルムを得た。凝集物由来の破断などで、ポリエステルフィルムを得ることが難しかった。
Comparative Example 6:
A polyester film was obtained in the same manner as in Example 1 except that a polyester chip containing amorphous silica particles having an average particle diameter of 12 μm was used. It was difficult to obtain a polyester film due to breakage derived from aggregates.

Figure 0005302756
Figure 0005302756

Figure 0005302756
Figure 0005302756

本発明のUVによりカラーチェンジ性能を有するポリエステルフィルムは、太陽電池をはじめとして、屋外向けの建材など様々な用途で紫外線強度測定に利用できるばかりでなく、インクジェットなどの方法に代わる、生産ラインの何らかの目印になること、また、電子部品におけるUV感光マーカーや光センサー技術としての用途可能性があるばかりではなく、UV感光発光技術を用いた美しい生活用品への応用が期待できる。   The polyester film having the color change performance by UV of the present invention can be used not only for measuring ultraviolet intensity in various applications such as solar cells and building materials for outdoor use, but also for any production line in place of an inkjet method. It can be used as a landmark, and can be used as a UV photosensitive marker and optical sensor technology in electronic parts, and can be expected to be applied to beautiful daily necessities using UV photosensitive light emitting technology.

Claims (1)

表面粗さ(Ra)が0.1〜1,0μmの範囲のフィルム表面を構成するポリエステル層が平均粒径3〜10μmの粒子を3〜30重量%含有する、三層以上の構成の積層ポリエステルフィルであって、当該積層フィルムの表層中に紫外線照射で着色する有機フォトクロミック化合物を含有し、当該有機フォトクロミック化合物のポリエステルフィルム中の含有量が0.05〜1.0重量%であることを特徴とするポリエステルフィルム。 A laminated polyester having three or more layers, wherein the polyester layer constituting the film surface having a surface roughness (Ra) in the range of 0.1 to 1.0 μm contains 3 to 30% by weight of particles having an average particle diameter of 3 to 10 μm. An organic photochromic compound that is a film and is colored by ultraviolet irradiation in the surface layer of the laminated film, and the content of the organic photochromic compound in the polyester film is 0.05 to 1.0% by weight. A polyester film.
JP2009107195A 2009-04-25 2009-04-25 Polyester film Active JP5302756B2 (en)