JP3776742B2 - Intermediate transfer recording medium and image forming method - Google Patents
Intermediate transfer recording medium and image forming method Download PDFInfo
- Publication number
- JP3776742B2 JP3776742B2 JP2001102763A JP2001102763A JP3776742B2 JP 3776742 B2 JP3776742 B2 JP 3776742B2 JP 2001102763 A JP2001102763 A JP 2001102763A JP 2001102763 A JP2001102763 A JP 2001102763A JP 3776742 B2 JP3776742 B2 JP 3776742B2
- Authority
- JP
- Japan
- Prior art keywords
- transfer
- layer
- recording medium
- intermediate transfer
- image
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】
【発明の属する技術分野】
本発明は、基材フィルム上に剥離可能に、少なくとも受容層からなる転写部を設けた中間転写記録媒体と、その中間転写記録媒体を用いる画像形成方法に関するものである。
【０００２】
【従来の技術】
従来、簡便な印刷方法として熱転写方法が広く使用されるようになってきた。熱転写方法は、基材シートの一方の面に色材層が設けられた熱転写シートと、必要に応じて画像受容層が設けられた熱転写受像シートを重ね合わせ、サーマルヘッド等の加熱手段により熱転写シートの背面を画像状に加熱して、色材層に含まれる色材を選択的に移行させて、熱転写受像シート上に画像を形成する方法である。
【０００３】
熱転写方法は、溶融転写方式と昇華転写方式に分けられる。溶融転写方式は顔料等の色材を熱溶融性のワックスや樹脂等のバインダーに分散させた熱溶融インキ層をＰＥＴフィルム等の基材シートに担持させた熱転写シートを用い、サーマルヘッド等の加熱手段に画像情報に応じたエネルギーを印加し、紙やプラスチックシート等の熱転写受像シート上に、色材をバインダーと共に転写する画像形成方法である。溶融転写方式による画像は、高濃度で鮮鋭性に優れ、文字等の２値画像の記録に適している。
【０００４】
一方、昇華転写方式は主に昇華により熱移行する染料を樹脂バインダー中に溶解或いは分散させた染料層をＰＥＴフィルム等の基材シートに担持させた熱転写シートを用い、サーマルヘッド等の加熱手段に画像情報に応じたエネルギーを印加し、紙やプラスチック等の基材シートに必要に応じて染料受容層を設けなる熱転写受像シート上に、染料のみを転写移行させる画像形成方法である。昇華転写方式は、印加されるエネルギー量に応じて染料の移行量を制御できるため、サーマルヘッドのドット毎に画像濃度を制御した階調画像の形成を行なうことができる。また、使用する色材が染料であるため、形成される画像には透明性があり、異なる色の染料を重ねた場合の中間色の再現性が優れている。したがって、イエロー、マゼンタ、シアン、ブラック等の異なる色の熱転写シートを用い、熱転写受像シート上に各色染料を重ねて転写する際にも、中間色の再現性に優れた高画質な写真調フルカラー画像の形成が可能である。
【０００５】
このような熱転写方法による熱転写受像シートの具体的な用途は、多岐にわたっている。代表的なものとしては、印刷の校正刷り、画像の出力、ＣＡＤ／ＣＡＭなどの設計およびデザインなどの出力、ＣＴスキャンや内視鏡カメラなどの各種医療用分析機器、測定機器の出力用途そしてインスタント写真の代替として、また身分証明書やＩＤカード、クレジットカード、その他カード類への顔写真などの出力、さらに遊園地、ゲームセンター、博物館、水族館などのアミューズメント施設における合成写真、記念写真としての用途などをあげることができる。上記のような用途の多様化に伴い、任意の対象物に熱転写画像を形成する要求が高まり、その対応の一つとして、受容層が基材上に剥離可能に設けられた中間転写記録媒体で、その受容層に染料層や熱溶融性インキ層を有する熱転写シートを用いて、染料、顔料などの着色剤を転写して画像を形成し、その後に中間転写記録媒体を加熱して、受容層を被転写体上に転写する方法が提案されている。（特開昭６２−２３８７９１号等）
【０００６】
また、上記の中間転写記録媒体を用いることは、受容層を被転写体に転写することができるので、色材が移行しにくく、高画質の画像を直接形成できない被転写体や、熱転写時に色材層と融着し易い被転写体等に対して、好ましく用いられている。そのため、中間転写記録媒体は、パスポート等の身分証明書やクレジットカード・ＩＤカード等の印画物の作成に対して好ましく用いられている。
【０００７】
【発明が解決しようとする課題】
ところが、上記のような中間転写記録媒体を用いて被転写体に受容層を転写する場合、四角形や丸型等の外形で全面ベタ状の単純な形状で転写する際には、あまり問題にはならないが、転写部において中抜きの部分を設けたり、外縁の形状が複雑な場合等には、被転写体へ転写される受容層のエッジがシャープでなく、転写されるべきでない部分が転写したり、転写すべき部分が転写されなかったりして、受容層転写性が不安定であるという問題がある。
特に、上記の受容層の転写されるべきでない部分が、例えば、住所や氏名等の記入欄であったり、あるいは記入者や発行者の捺印欄の場合、その部分に受容層が少しでも転写されていると、記入した内容や捺印が不鮮明になり、判読できないという大きな問題となる。
【０００８】
上記の受容層転写性の不安定に対して、一旦受容層を四角形や円形等の単純な形状で転写した後に、筆記や捺印が出来る専用の層を追加して印刷等の方法で設けることが挙げられる。ところが、この場合は専用層を追加するには手間と労力がかかり、製造コストが非常に高くなってしまうという問題がある。
したがって、本発明は、上記のような問題点を解決し、基材フィルム上に剥離可能に、少なくとも受容層からなる転写部を設けた中間転写記録媒体を用いて、該転写部に熱転写画像を形成し、該転写部を被転写体に再転写する時に、被転写体に部分的に転写されない部分を正確に、安定して形成でき、また最終印画物を得るために製造コストアップすることのない中間転写記録媒体及びそれを用いた画像形成方法を提供することを目的とする。
【０００９】
【課題を解決するための手段】
上記目的を達成するために、本発明では、被転写体の一部分に、基材フィルム上に剥離可能に、離型層と受容層からなる転写部を設けた中間転写記録媒体を用いて画像形成する際に、基材フィルムの一方の面で、部分的にマスキング層を設け、該マスキング層の上と基材フィルムの上に、全面で離型層を設け、さらに該離型層の上に受容層を設けた中間転写記録媒体において、マスキング層が熱を吸収あるいは遮断するものであり、かつ該転写部を被転写体へ再転写する時に、該転写部の下層部にマスキング層を設けている部分は、被転写体に転写されない被転写体への再転写しない領域を形成する構成とした。前記のマスキング層を部分的に形成した部分と、同期した検知マークを有することが好ましく、中間転写記録媒体上の指定した位置（受容層を再転写しない領域を除いた領域）に熱転写画像を形成し、また被転写体へ熱転写画像の形成された受容層を再転写する際に、受容層を転写する部分と、転写しない部分を正確に、また位置精度を高く、分けて形成することができる。
【００１０】
本発明では、被転写体の両面に、基材フィルム上に剥離可能に、離型層と受容層からなる転写部を設けた中間転写記録媒体を用いて画像形成する際に、被転写体の少なくとも片面の一部分に受容層を再転写しない領域を形成するため、検知マークで区切られた画面単位で、少なくとも片面単位の一部分に被転写体へ再転写しない領域を設け、すなわち基材フィルム上に、部分的にマスキング層を設け、該マスキング層の上と基材フィルムの上に、全面で離型層を設け、さらに該離型層の上に受容層を設けた構成で、該マスキング層の形成された部分が、被転写体へ再転写しない領域であり、かつマスキング層が熱を吸収あるいは遮断するものである構成とした。これにより、被転写体の片面あるいは両面の一部分の個所に受容層の再転写しない領域と、熱転写画像の形成された受容層の再転写される領域を、一つの中間転写記録媒体により、簡単に形成することができる。本発明の画像形成方法は、上記に記載するいずれか一つの中間転写記録媒体を用いて、被転写体上に部分的に受容層が再転写しない領域を形成することを特徴とする。
【００１１】
すなわち、本発明の画像形成方法は、被転写体の一部分に受容層を再転写しない領域を形成するため、基材フィルム上に剥離可能に、離型層と受容層からなる転写部を設けた中間転写記録媒体を用いて画像形成する際に、基材フィルムの一方の面で、部分的にマスキング層を設け、該マスキング層の上と基材フィルムの上に、全面で離型層を設け、さらに該離型層の上に受容層を設けた中間転写記録媒体において、マスキング層が熱を吸収あるいは遮断するものであり、かつ該転写部を被転写体へ再転写する時に、該転写部の下層部にマスキング層を設けている部分は、被転写体に転写されない被転写体への再転写しない領域を形成する。被転写体に対し、受容層の転写されるべきでない部分を、中間転写記録媒体で、転写時の熱を吸収あるいは遮断する働きにより、簡単に、また確実に形成できる。
【００１２】
【発明の実施の形態】
図１は、本発明の中間転写記録媒体１である一つの実施形態を示す概略断面図であり、基材フィルム２の一方の面で部分的ににマスキング層４を設け、そのマスキング層４の上と基材フィルム２の上に、全面で離型層５を設け、さらにその離型層５の上に受容層３を設けている。すなわち、図１に示す中間転写記録媒体１の実施形態は、離型層５と受容層３からなる転写部の下層部に、被転写体に再転写する時に、被転写体に部分的に転写されない部分を形成するマスキング層４が形成されたものである。つまり、マスキング層４が被転写体への再転写時に、基材フィルム２と密着して被転写体へは転写されない。
【００１３】
図２は、本発明の中間転写記録媒体１の参考例となる実施形態を示す概略断面図であり、基材フィルム２の一方の全面に、離型層５を設け、その離型層５の上に受容層３を設け、その受容層３の上で部分的に、マスキング層４を設けた構成である。すなわち、図２に示す中間転写記録媒体１の実施形態は、離型層５と受容層３からなる転写部の上層部に、被転写体に再転写する時に、被転写体に部分的に転写されない部分を形成するマスキング層４が形成されたものである。この場合は、マスキング層４が被転写体と接着しないため、再転写時に被転写体へはマスキング層４の部分は転写されない。更に、図３は本発明の中間転写記録媒体１の参考例となる他の実施形態を示す概略図であり、図３（１）は中間転写記録媒体の概略平面図であり、図３（２）は図３（１）のＡ−Ａ′の概略断面図を示す。図３で示した実施形態の中間転写記録媒体１は、受容層の再転写しない領域としてのマスキング層４が、受容層転写部において中抜きの部分であり、この例では１画面につき２ヶ所の中抜き部分がマスキング層４である。マスキング層４を部分的に形成した部分と同期した検知マーク６は、１画面につき１ヶ所に形成することが通常行なわれる。基材フィルム２の一方の全面に受容層３が設けられ、その受容層３の上に、つまり中間転写記録媒体１の最上層に、この図示した検知マーク６が形成されている。
【００１４】
図４は、本発明の中間転写記録媒体１の参考例となる他の実施形態を示す概略図であり、図４（１）は中間転写記録媒体の概略平面図であり、図４（２）は図４（１）のＢ−Ｂ′の概略断面図を示す。図４に示した中間転写記録媒体１は、被転写体の両面に、受容層を再転写して画像形成するものである。中間転写記録媒体１は、基材フィルム２の一方の面に離型層５と受容層３を設け、検知マーク６で区切られた画面単位で、被転写体のおもて面用の転写層Ａと被転写体の裏面用の転写層ＢとをＡＢＡＢＡＢＡ・・と繰り返し形成している。おもて面用の転写層Ａには受容層３の上には何も形成されていない。それに対し、裏面用の転写層Ｂには、被転写体に対し受容層の再転写しない領域として、受容層３の上にマスキング層４を部分的に形成している。
【００１５】
その受容層の再転写しない領域であるマスキング層４は、受容層転写部における四角い中抜きの形状を有し、おもて面用の転写層Ａを間にして、１画面の間隔をおいて、繰り返し形成してある。尚、検知マーク６は、中間転写記録媒体１の受容層３の上に設けられている。この例の中間転写記録媒体を用いれば、被転写体の裏面側の一部分の個所に受容層の再転写しない領域を設け、被転写体の両面に熱転写画像の形成を簡単に形成することができる。検知マーク６によりおもて面と裏面の各転写層の位置を検出させ、被転写体に正確な位置で熱転写画像を形成できる。
以上のように、マスキング層は図示したように、少なくとも受容層からなる転写部の上層部あるいは下層部に、形成されている。
【００１６】
（基材フィルム）
中間転写記録媒体で使用する基材フィルム２は、従来の中間転写記録媒体に使用されているものと同じ基材フィルムをそのまま用いることができ、特に限定するものではない。好ましい基材フィルムの具体例としては、グラシン紙、コンデンサー紙またはパラフィン紙等の薄紙、あるいは、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリブチレンテレフタレート、ポリフェニレンサルファイド、ポリエーテルケトンもしくはポリエーテルサルホン等の耐熱性の高いポリエステル、ポリプロピレン、ポリカーボネート、酢酸セルロース、ポリエチレン誘導体、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリスチレン、ポリアミド、ポリイミド、ポリメチルペンテンまたはアイオノマー等のプラスチックの延伸または未延伸フィルムが挙げられる。また、これらの材料を２種以上積層した複合フィルムも使用することができる。基材フィルムの厚さは、その強度及び耐熱性等が適切になるように、材料に応じて適宜選択することができるが、通常は１〜１００μｍ程度のものが好ましく用いられる。
【００１７】
（受容層）
受容層は、中間転写記録媒体を構成する転写部の主要な部分である。この受容層上には、熱転写によって、色材層を有する熱転写シートから熱転写法によって画像が形成される。そして、画像が形成された中間転写記録媒体の転写部は、被転写体に転写され、その結果、印画物が形成される。
このため、受容層を形成するための材料としては、昇華性染料または熱溶融性インキ等の熱移行性の色材を受容し易い従来公知の樹脂材料を使用することができる。例えば、ポリプロピレン等のポリオレフィン系樹脂、ポリ塩化ビニルもしくはポリ塩化ビニリデン等のハロゲン化樹脂、ポリ酢酸ビニル、塩化ビニル−酢酸ビニル系共重合体、エチレン−酢酸ビニル共重合体もしくはポリアクリル酸エステル等のビニル系樹脂、ポリエチレンテレフタレートもしくはポリブチレンテレフタレート等のポリエステル樹脂、ポリスチレン系樹脂、ポリアミド系樹脂、エチレンもしくはプロピレン等のオレフィンと他のビニルポリマーとの共重合体系樹脂、アイオノマーもしくはセルロースジアスターゼ等のセルロース系樹脂、ポリカーボネイト等が挙げられ、特に、塩化ビニル系樹脂、アクリル−スチレン系樹脂またはポリエステル樹脂が好ましい。
【００１８】
受容層が接着層を介して被転写体に転写される場合には、受容層自体の接着性は必ずしも要求されない。しかし、受容層が接着層を介さないで被転写体に転写される場合には、塩化ビニル−酢酸ビニル共重合体などの接着性を有する樹脂材料を用いて受容層を形成することが好ましい。
受容層は、上述の材料の中から選択された単独または複数の材料および必要に応じて各種添加剤等を加え、水または有機溶剤等の適当な溶剤に溶解または分散させて受容層用塗工液を調製し、これをグラビア印刷法、スクリーン印刷法またはグラビア版を用いたリバースコーティング法等の手段により、塗布、乾燥して形成することができる。その厚さは、乾燥状態で１〜１０ｇ／ｍ2程度である。
【００１９】
（マスキング層）
本発明で使用するマスキング層４は、中間転写記録媒体の転写部の下層部に設けられ、該転写部を被転写体に転写しようとしても、マスキング層が転写時の熱を吸収あるいは遮断して、被転写体にその転写部を転写させなくするものである。マスキング層に使用するバインダー樹脂としては、アクリル系樹脂、アクリルセルロール樹脂、セルロース系樹脂、ポリスチレン系樹脂、ポリウレタン系樹脂、ポリエステル系樹脂、ポリカーボネート系樹脂、ポリアミド系樹脂、ポリスルフォン系樹脂、ポリ塩化ビニル樹脂、ポリ酢酸ビニル樹脂、塩化ビニル−酢酸ビニル共重合体樹脂、ポリビニルアセタール樹脂、ポリビニルブチラール樹脂、ポリビニルアルコール樹脂、エポキシ樹脂、エチレン−酢酸ビニル共重合体樹脂、ポリエチレン系樹脂、ポリプロピレン系樹脂等が挙げられ、これらの樹脂のうちの活性水素を有するものについては、さらにそれらのイソシアネート架橋物をバインダーとすることもできる。
【００２０】
また、マスキング層中には充填剤を含有させることができる。充填剤としては、例えば、シリカ、アルミナ、クレイ、タルク、炭酸カルシウム、硫酸バリウム等の無機充填剤、酸化チタン、酸化亜鉛等の白色顔料、アクリル樹脂、エポキシ樹脂、ポリウレタン樹脂、フェノール樹脂、メラミン樹脂、ベンゾグアナミン樹脂、フッ素樹脂、シリコーン樹脂等の樹脂粒子（プラスチックピグメント）若しくはポリエチレンワックス、パラフィンワックス、カルナバワックス、マイクロクリスタリンワックス、木ロウ、ミツロウ、鯨ロウ、イボタロウ、羊毛ロウ、キャンデリラワックス、一部変性ワックス、脂肪酸アミド等種々の公知のワックス粒子が挙げられる。上記のマスキング層中に気泡または発泡剤を含有させたり、充填剤を含有させる場合、マスキング層バインダー樹脂に対して、０．０１〜２００重量％程度で添加する。
【００２１】
また、以下に示す海島構造の多孔質のマスキング層を設けることができる。多孔質の製法として、湿式凝固法が一般的であり、溶解度パラメータの大きく異なる２種以上の多孔質形成樹脂成分を溶媒に溶解し、基材フィルムに塗布した後、前記溶媒とは混合できるが、前記樹脂成分を溶解しない溶媒中に通すことで、溶媒置換を行う。その結果、置換された溶媒下では、多孔質形成樹脂成分の溶解度パラメータが大きく異なるため、２種以上の樹脂が海島構造を形成する。その後、熱浴に通すことで、前記海島構造の島部分が更に熱収縮し、多孔化が進む。その際に、島部分が有機微粒子となる。その後、脱離、乾燥させ、多孔質のマスキング層が得られる。この多孔質のマスキング層の場合、断熱効果を出すために、島部分の大きさや密度、非転写層の厚さを調製する必要がある。
以上のようなマスキング層は、グラビアコート、グラビアリバースコート、ロールコート等の公知の塗工手段により、乾燥時で０．０５〜５．０ｇ／ｍ2程度の厚さで形成する。
【００２２】
本発明の中間転写記録媒体では、必要に応じて、基材フィルムの受容層の設けてある側と反対面に、サーマルヘッドやヒートロール等の加熱手段との融着を防止し、摺動性を向上させるために、背面層を設けてもよい。
【００２３】
（離型層）
本発明の中間転写記録媒体では、被転写体への再転写時に受容層の基材フィルムからの剥離性を向上させるために、離型層５を設けることができる。
離型層は、基材フィルムと受容層の材料の組み合わせによって、受容層の被転写体への熱転写時の離型性が十分でない場合に設けるものである。このような離型層は、ワックス類、シリコーンワックス、シリコーン系樹脂等の離型剤を使用して形成することもできるし、特開平４−１４２９８８号に記載の親水性樹脂や各種の硬化性樹脂等を、基材フィルムと非転写層の特性に合わせて適宜選択して使用することができ、特に限定されない。離型層の形成は、上記のような離型剤に必要な添加剤を加えたものを適当な溶剤に溶解または分散して調製したインキを、基材フィルム上に公知の手段により塗布、乾燥させて行なうことができ、厚みは乾燥時０．１〜５ｇ／ｍ2程度が好ましい。
【００２４】
（検知マーク）
中間転写記録媒体のマスキング層を部分的に形成した部分と同期した検知マーク６の形状や色等の形態は、検知器によって検知可能であればよく、限定されるものではない。形状では、例えば、四角形でも、あるいは丸形やバーコードや、中間転写記録媒体の幅方向の端から端までのライン状等が挙げられる。検知マークの色は、検知器で検知可能であればよく、例えば光透過型検知器であれば、隠蔽性の高い銀色、黒色等が挙げられ、光反射型検知器であれば、光反射性の高い金属光沢の色調等が挙げられる。
また、検知マークとして、ホログラムや回折格子を用いたマークを使用することができる。このホログラムマークの形成方法は、従来公知のホログラムパターン形成方法が挙げられ、例えばホログラムの干渉縞の凹凸パターンを設けた原版を用い、微細凹凸をエンボス加工によって形成する。このホログラムマークのセンサーとして、いわゆるホログラムセンサーが利用でき、発光素子から発せられた光がホログラムマークによって乱反射し、回折光を発する。その回折光を受光素子で検知することで、ホログラムマークの位置が検知できる。
尚、検知マークの設ける位置について、図示したものに限定されず、例えば、フィルム基材が透明性を有するものであれば、フィルム基材の受容層が設けられる面と反対側の面に、検知マークを設けることができる。また、図示したものは、受容層の上に検知マークを設けているが、それに限定されず、フィルム基材と離型層との間に検知マークを設けたり、適宜選択できる。
【００２５】
本発明の中間転写記録媒体で使用する検知マークは、マスキング層を部分的に形成した部分と、つまり受容層の再転写しない領域と同期したもので、その受容層の再転写しない領域の指定位置（例えば、その領域の開始位置など）と検知マーク間の距離を一定にして、マークを検出して受容層の再転写を被転写体の一定位置で開始するようにして、受容層の再転写しない領域を被転写体の規定した位置に正確に収めることができる。通常、マスキング層を部分的に形成した部分と同期した検知マークは、１画面につき１ヶ所に形成される。
【００２６】
（被転写体）
次に、被転写体について説明する。被転写体上には、上述した中間転写記録媒体の熱転写画像の形成された転写部が転写される。但し、マスキング層を有する部分は被転写体には転写されない。
本発明で使用される被転写体は特に限定されず、例えば天燃パルプ紙、コート紙、トレーシングペーパー、転写時の熱で変形しないプラスチックフィルム、ガラス、金属、セラミックス、木材、布等いずれのものでもよい。
但し、被転写体でマスキング層を用いて、中間転写記録媒体の転写されない部分が、例えば、住所や氏名等の記入欄であったり、あるいは記入者や発行者の捺印欄の場合、被転写体は筆記適性や捺印適性を有した天燃パルプ紙が好ましい。
天然パルプ紙は特に限定されず、例えば、上質紙、アート紙、軽量コート紙、微塗工紙、コート紙、キャストコート紙、合成樹脂又はエマルジョン含浸紙、合成ゴムラテックス含浸紙、合成樹脂内添紙、熱転写用紙等が挙げられる。
【００２７】
被転写体の形状・用途についても、株券、証券、証書、通帳類、乗車券、車馬券、印紙、切手、鑑賞券、入場券、チケット等の金券類、キャッシュカード、クレジットカード、プリペイドカード、メンバーズカード、グリーティングカード、ハガキ、名刺、運転免許証、ＩＣカード、光カードなどのカード類、カートン、容器等のケース類、バッグ類、帳票類、封筒、タグ、ＯＨＰシート、スライドフィルム、しおり、カレンダー、ポスター、パンフレット、メニュー、パスポート、ＰＯＰ用品、コースター、ディスプレイ、ネームプレート、キーボード、化粧品、腕時計、ライター等の装身具、文房具、レポート用紙など文具類、建材、パネル、エンブレム、キー、布、衣類、履物、ラジオ、テレビ、電卓、ＯＡ機器等の装置類、各種見本帳、アルバム、また、コンピュータグラフィックスの出力、医療画像出力等、種類を問うものではない。
【００２８】
（画像形成方法）
次に、上記の中間転写記録媒体を用いて、任意の被転写体に中抜きの部分を有したり、外縁の形状が複雑なものであるような、被転写体上に部分的に受容層が再転写しない領域を形成する、本発明の画像形成方法について説明する。上述した、基材フィルム上に剥離可能に、離型層と受容層からなる転写部を設けた中間転写記録媒体を用いて画像形成する際に、基材フィルムの一方の面で、部分的にマスキング層を設け、該マスキング層の上と基材フィルムの上に、全面で離型層を設け、さらに該離型層の上に受容層を設けた中間転写記録媒体において、マスキング層が熱を吸収あるいは遮断するものであり、かつ該転写部を被転写体へ再転写する時に、該転写部の下層部にマスキング層を設けている部分は、被転写体に転写されない被転写体への再転写しない領域を形成するものである。その中間転写記録媒体の受容層に熱転写シートから、染料層や熱溶融性インキ層をサーマルヘッド等の加熱手段により転写して画像形成する。次に被転写体上に、その中間転写記録媒体の画像形成された転写部をヒートロール等の加熱手段により再転写する。その再転写の時に、中間転写記録媒体のマスキング層を設けた部分が被転写体には転写されず、それ以外の再転写、加熱部分が転写される。
【００２９】
本発明の画像形成方法では、検知マークで区切られた画面単位で、少なくとも片面単位の一部分に被転写体へ再転写しない領域を設けた中間転写記録媒体を用いて、被転写体の片面あるいは両面の一部分に受容層の再転写しない領域と、熱転写画像の形成された受容層の再転写される領域を区分けして正確な位置精度をもって形成できる。
その検知マークは、被転写体のおもて面用転写層あるいは同じく裏面用転写層の区別（おもて面用と裏面用の区別を、例えば図４に示したような、１本と２本のストライプ状の検知マークにしたりする）や、その層の位置検出のために使用され、被転写体への画像形成時に、指定した面に受容層の再転写しない領域を設け、また指定された熱転写画像を有する受容層の再転写する領域を正確に区分けして、被転写体へ転写された受容層のエッジがシャープであり、転写されるべきでない部分が転写されることなく、安定した受容層の転写性が得られる。
このように中間転写記録媒体に有する検知マークを、プリンター側の検出器で検知し、プリンターと連動させて、中間転写記録媒体上の熱転写画像の位置と、被転写体への転写部の再転写の位置を合わせることができる。
【００３０】
（参考例１）
先ず、厚さ１２μｍで透明なポリエチレンテレフタレートを基材フィルムとして用い、その表面に、以下に示す離型層用塗工液を塗布、乾燥して、基材フィルム上に乾燥時で厚さ２．０ｇ／ｍ2の離型層を形成した。そして、その離型層の上に、以下に示す受容層用塗工液を塗布、乾燥して、乾燥時で厚さ２．０ｇ／ｍ2の受容層を形成した。尚、文中、部または％とあるのは、特に断りのない限り、重量基準である。
（離型層用塗工液）
アクリル樹脂（三菱レイヨン（株）製、ＢＲ−８３） ８８部
ポリエステル樹脂 １部
ポリエチレンワックス １１部
メチルエチルケトン ５０部
トルエン ５０部
【００３１】
（受容層用塗工液）
塩化ビニル−酢酸ビニル共重合体 ４０部
アクリルシリコーン １．５部
メチルエチルケトン ５０部
トルエン ５０部
【００３２】
次いで、上記の受容層上に、下記組成のマスキング層用インキを図３に示すようなパターンで、グラビア印刷機で、乾燥時で厚さ２．０ｇ／ｍ2のマスキング層を形成した。
（マスキング層用インキ）
アクリル樹脂 ５０部
ポリエチレンワックス ５０部
メチルエチルケトン ２５部
トルエン ２５部
【００３３】
さらに、下記組成の検知マーク用インキを図３に示すようなパターンで、グラビア印刷機で、乾燥時で厚さ１．５ｇ／ｍ2の検知マークを形成し、参考例１の中間転写記録媒体を作製した。
（検知マーク用インキ）
カーボンブラック ８．０部
ウレタン樹脂（日本ポリウレタン（株）製、ＨＭＳ−２０） ５．０部
メチルエチルケトン ３８．５部
トルエン ３８．５部
【００３４】
上記の得られた参考例１の中間転写記録媒体の受容層上に（マスキング層にかからない部分の受容層上に）、市販のサーマルヘッドを搭載した熱転写プリンターを用いて、その熱転写プリンター専用の昇華型熱転写シートを用いて、フルカラーの写真調の画像を形成した。その画像形成の際に、中間転写記録媒体に有する検知マークをプリンター側で検出して、受容層上の画像の位置合わせを行なった。その後に、厚み６００μｍの白色のＰＥＴ−Ｇシート（三菱樹脂（株）製：ＰＥＴ−Ｇ、ディアフィクスＰＧ−Ｗ）の指定した位置に、上記の画像形成された転写部を、ヒートロールを常設した市販のラミネーターを用いて、再転写して、印画物を得た。但し、上記のＰＥＴ−Ｇシートの転写面の住所、氏名の手書き記入欄と、捺印欄に相当する位置には予めサインパネルの処理を施していて、上記マスキング層の部分と、サインパネルの欄との位置合わせを行なった。尚、被転写体へ中間転写記録媒体の転写部を再転写する際に、中間転写記録媒体に有する検知マークをプリンター側で検出して、位置合わせを行なった。
【００３５】
上記参考例１で得られた印画物は、中間転写記録媒体の転写部で、マスキング層の転写した部分のみが、被転写体に転写されずに、そして手書き記入欄と捺印欄の中抜きの部分を除いた部分で、熱転写画像が形成されているものであった。その手書き記入欄にボールペンで記入し、全く不鮮明な部分が生じなかった。さらに、捺印欄に朱肉で印鑑を押したところ、全く不鮮明な部分が生じなかった。また、熱転写画像は鮮明であり、優れた品質のものであった。
【００３６】
（参考例２）参考例１と同様の基材フィルムを用いて、その基材フィルムの表面に、参考例１で使用した同様の離型層用塗工液を塗布、乾燥して、基材フィルム上に乾燥時で厚さ２．０ｇ／ｍ2の離型層を形成した。次いで、上記離型層上に、参考例１で使用した同様の受容層用塗工液を塗布、乾燥して、基材フィルム上に乾燥時で厚さ２．０ｇ／ｍ2の受容層を形成した。そして、その受容層上に、参考例１で使用した同様のマスキング層用インキを図４に示すようなパターンで、グラビア印刷機で、乾燥時で厚さ２．０ｇ／ｍ2のマスキング層を形成した。さらに、参考例１で使用した同様の検知マーク用インキを図４に示すようなパターンで、グラビア印刷機で、乾燥時で厚さ１．５ｇ／ｍ2の検知マークを形成し、被転写体おもて面用の画像形成単位の転写層Ａと被転写体裏面用の画像形成単位の転写層Ｂとを、ＡＢＡＢＡＢと繰り返し形成した。尚、マスキング層は被転写体裏面用の画像形成単位の転写層Ｂ側のみに形成されている。このようにして、参考例２の中間転写記録媒体を作製した。
【００３７】
上記の得られた参考例２の中間転写記録媒体の被転写体おもて面用の画像形成単位の転写層Ａ上に、参考例１で使用した同じ熱転写プリンター専用の昇華型熱転写シートを用いて、フルカラーの写真調の画像と、熱溶融型熱転写シートを用いて、溶融転写の文字画像の熱転写画像を、上記の熱転写プリンターで形成した。次に、上記の被転写体のおもて面に転写される転写部Ａに隣接して、被転写体の裏面に転写される転写部Ｂに対して、上記と同様の熱溶融型熱転写シートを用いて、上記で使用した熱転写プリンターにより、溶融転写の文字画像の熱転写画像を形成した。但し、その際に溶融転写の文字画像は、マスキング層の印刷されていない部分に形成した。その画像形成の際に、中間転写記録媒体に有する被転写体おもて面用の検知マーク及び被転写体の裏面用の検知マークをプリンター側で検出して、受容層上の被転写体へ転写されるおもて面と裏面の画像の位置合わせを行なった。
【００３８】
その後に、参考例１で使用した被転写体と同様の白色ＰＥＴ−Ｇシートのおもて面の指定した位置に、上記の画像形成されたおもて面用の転写部を、ヒートロールを常設した市販のラミネーターを用いて、再転写して、印画物を得た。次に、おもて面に画像転写された白色ＰＥＴ−Ｇシートの裏面側の指定した位置に、上記の画像形成された裏面用の転写部を、ヒートロールを常設した市販のラミネーターを用いて、再転写して、両面に画像を有する印画物を得た。但し、上記のＰＥＴ−Ｇシートの裏面である転写面の住所、氏名の手書き記入欄に相当する位置には予めサインパネルの処理を施していて、上記マスキング層の部分と、サインパネルの欄との位置合わせを行なった。尚、被転写体へ中間転写記録媒体の転写部を再転写する際に、中間転写記録媒体に有する被転写体のおもて面用転写層の検知マーク及び被転写体の裏面用転写層の検知マークを、それぞれプリンター側で検出して、中間転写記録媒体の画像形成された転写部を、被転写体のおもて面と裏面に指定した部分に、位置を合わて再転写した。
【００３９】
上記参考例２で得られた印画物は、裏面において、中間転写記録媒体の転写部で、マスキング層の転写した部分のみが、被転写体に転写されずに、手書き記入欄の中抜きの部分を除いた部分で、熱転写画像が形成されているものであった。そして、その手書き記入欄にボールペンで記入して、全く不鮮明な部分が生じなかった。また、参考例２で得られた印画物のおもて面及び裏面の熱転写画像は鮮明であり、優れた品質のものであった。
【００４０】
（比較例１）
参考例１と同様の基材フィルムを用いて、その基材フィルムの表面に、参考例１で使用した同様の離型層用塗工液を塗布、乾燥して、基材フィルム上に乾燥時で厚さ２．０ｇ／ｍ2の離型層を形成した。次いで、上記離型層上に、参考例１で使用した同様の受容層用塗工液を塗布、乾燥して、基材フィルム上に乾燥時で厚さ２．０ｇ／ｍ2の受容層を形成し、比較例１の中間転写記録媒体を作製した。上記の得られた中間転写記録媒体の受容層上に、参考例で使用したものと同じ熱転写プリンターと熱転写シートを用いて、昇華転写の写真調の画像と、溶融転写の文字画像の熱転写画像を形成した。次に、参考例１で使用した同様のＰＥＴ−Ｇシートと、上記の画像形成された転写部を重ね、住所、氏名の手書き記入欄と、捺印欄に相当する位置を除いた部分が加熱及び加圧される、所定のパターンを有するホットスタンプ用凸版により、熱プレスを行ない、被転写体に転写部を再転写して、印画物を得た。上記の比較例１で得られた印画物は、手書き記入欄の位置にボールペンで記入したところ、部分的にインキがはじかれ、不鮮明な部分が生じた。さらに、捺印欄に朱肉で印鑑を押したところ、朱肉がはじかれる部分が生じて、不鮮明であった。
【００４１】
【発明の効果】
以上説明したように、本発明の画像形成方法により、被転写体の一部分に受容層を再転写しない領域を形成するため、基材フィルム上に剥離可能に、離型層と受容層からなる転写部を設けた中間転写記録媒体を用いて画像形成する際に、基材フィルムの一方の面で、部分的にマスキング層を設け、該マスキング層の上と基材フィルムの上に、全面で離型層を設け、さらに該離型層の上に受容層を設けた中間転写記録媒体において、マスキング層が熱を吸収あるいは遮断するものであり、かつ該転写部を被転写体へ再転写する時に、該転写部の下層部にマスキング層を設けている部分は、被転写体に転写されない被転写体への再転写しない領域を形成する。被転写体に対し、受容層の転写されるべきでない部分を、中間転写記録媒体で、転写時の熱を吸収あるいは遮断する働きにより、簡単に、また確実に形成できた。
【図面の簡単な説明】
【図１】 本発明の中間転写記録媒体である一つの実施形態を示す概略断面図である。
【図２】 本発明の中間転写記録媒体の参考例となる実施形態を示す概略断面図である。
【図３】 本発明の中間転写記録媒体の参考例となる実施形態を示す概略図である。
【図４】 本発明の中間転写記録媒体の参考例となる実施形態を示す概略図である。
【符号の説明】
１ 中間転写記録媒体
２ 基材フィルム
３ 受容層
４ マスキング層
５ 離型層
６ 検知マーク
Ａ 被転写体おもて面用の転写層
Ｂ 被転写体裏面用の転写層[0001]
BACKGROUND OF THE INVENTION
The present invention relates to an intermediate transfer recording medium provided with a transfer portion comprising at least a receiving layer so as to be peelable on a base film, and an image forming method using the intermediate transfer recording medium.
[0002]
[Prior art]
Conventionally, a thermal transfer method has been widely used as a simple printing method. In the thermal transfer method, a thermal transfer sheet provided with a color material layer on one surface of a base sheet and a thermal transfer image receiving sheet provided with an image receiving layer as necessary are superposed, and the thermal transfer sheet is heated by a heating means such as a thermal head. In this method, an image is formed on a thermal transfer image receiving sheet by heating the back surface of the image to an image and selectively transferring the color material contained in the color material layer.
[0003]
Thermal transfer methods are classified into a melt transfer method and a sublimation transfer method. The melt transfer method uses a thermal transfer sheet in which a heat melt ink layer in which a color material such as a pigment is dispersed in a binder such as a heat meltable wax or resin is supported on a base sheet such as a PET film, and heats a thermal head or the like. In this image forming method, energy is applied to the means in accordance with image information, and a color material is transferred together with a binder onto a thermal transfer image receiving sheet such as paper or a plastic sheet. An image obtained by the melt transfer method has a high density and excellent sharpness, and is suitable for recording binary images such as characters.
[0004]
On the other hand, the sublimation transfer method uses a thermal transfer sheet in which a dye layer in which a dye that transfers heat by sublimation is dissolved or dispersed in a resin binder is supported on a base sheet such as a PET film, and is used as a heating means such as a thermal head. In this image forming method, energy is applied according to image information, and only a dye is transferred onto a thermal transfer image receiving sheet in which a dye receiving layer is provided on a base sheet such as paper or plastic as required. In the sublimation transfer method, the amount of dye transfer can be controlled in accordance with the amount of energy applied, so that it is possible to form a gradation image in which the image density is controlled for each dot of the thermal head. Further, since the color material to be used is a dye, the formed image is transparent, and the reproducibility of intermediate colors when dyes of different colors are superimposed is excellent. Therefore, when using thermal transfer sheets of different colors such as yellow, magenta, cyan, black, etc., and transferring each color dye on the thermal transfer image receiving sheet, high-quality photographic tone full-color images with excellent reproducibility of intermediate colors can be obtained. Formation is possible.
[0005]
Specific uses of the thermal transfer image receiving sheet by such a thermal transfer method are various. Typical examples include printing proofs, image output, CAD / CAM design and design output, various medical analytical instruments such as CT scans and endoscopic cameras, measuring instrument output applications and instant As an alternative to photos, output of ID cards, ID cards, credit cards, other face photos on cards, etc., as well as composite photos and amusement photos at amusement facilities such as amusement parks, game centers, museums, and aquariums Etc. With the diversification of applications as described above, there is an increasing demand for forming a thermal transfer image on an arbitrary object, and as one of the countermeasures, an intermediate transfer recording medium in which a receiving layer is detachably provided on a substrate is used. Using a thermal transfer sheet having a dye layer or a heat-meltable ink layer as the receiving layer, a colorant such as a dye or pigment is transferred to form an image, and then the intermediate transfer recording medium is heated to form a receiving layer. There has been proposed a method of transferring the image onto the transfer medium. (Japanese Patent Laid-Open No. 62-238791 etc.)
[0006]
In addition, the use of the above intermediate transfer recording medium can transfer the receiving layer to the transfer target, so that the color material is difficult to move and a high-quality image cannot be directly formed. It is preferably used for an object to be transferred which is easily fused with the material layer. For this reason, the intermediate transfer recording medium is preferably used for creating an identification card such as a passport or a printed matter such as a credit card / ID card.
[0007]
[Problems to be solved by the invention]
However, when transferring the receiving layer to the transfer medium using the intermediate transfer recording medium as described above, there are not so many problems when transferring in a simple shape with a solid shape such as a square or a round shape. However, if there is a hollow part in the transfer part or the outer edge is complicated, the edge of the receiving layer transferred to the transfer target is not sharp and the part that should not be transferred is transferred. There is a problem that the transferability of the receiving layer is unstable because the portion to be transferred is not transferred.
In particular, if the portion of the receiving layer that should not be transferred is, for example, an entry field such as an address or name, or a seal of an entry or issuer, the receiving layer is transferred to that part even a little. If this is the case, the written content and seal will be unclear and this will cause a serious problem that it cannot be read.
[0008]
Against the above unstable transferability of the receiving layer, it is possible to transfer the receiving layer once in a simple shape such as a square or a circle, and then add a dedicated layer that can be used for writing or stamping and providing it by a method such as printing. Can be mentioned. However, in this case, it takes time and labor to add a dedicated layer, and there is a problem that the manufacturing cost becomes very high.
Accordingly, the present invention solves the above-described problems, and uses an intermediate transfer recording medium provided with a transfer portion comprising at least a receiving layer so as to be peelable on a base film, and a thermal transfer image is transferred to the transfer portion. When forming and re-transferring the transfer part to the transfer object, the part that is not partially transferred to the transfer object can be formed accurately and stably, and the manufacturing cost can be increased to obtain the final print product. It is an object to provide a non-intermediate transfer recording medium and an image forming method using the same.
[0009]
[Means for Solving the Problems]
In order to achieve the above-mentioned object, in the present invention, a part of a transfer object can be peeled off on a base film, When forming an image using an intermediate transfer recording medium provided with a transfer portion comprising a release layer and a receiving layer, a masking layer is partially provided on one side of the substrate film, A release layer is provided on the entire surface of the material film, and a receiving layer is provided on the release layer. In the intermediate transfer recording medium provided with The masking layer absorbs or blocks heat, and the transfer portion is When re-transferring to the transfer target, The portion where the masking layer is provided in the lower layer of the transfer portion forms a region that is not transferred to the transfer target and is not retransferred to the transfer target. The configuration. It is preferable to have a detection mark that is synchronized with the part where the masking layer is partially formed, and a thermal transfer image is formed at the specified position on the intermediate transfer recording medium (excluding the area where the receiving layer is not re-transferred). In addition, when re-transferring the receiving layer on which the thermal transfer image is formed to the transfer target, the portion to which the receiving layer is transferred and the portion to which the transfer is not transferred can be formed accurately and with high positional accuracy. .
[0010]
In the present invention, on both sides of the transfer object, it can be peeled off on the base film, Transfer area consisting of release layer and receptor layer When forming an image using an intermediate transfer recording medium provided with an image recording medium, at least a single-sided unit in screen units delimited by detection marks to form a region where the receiving layer is not re-transferred on at least a part of one side of the transfer object An area that does not retransfer to the transfer target is provided in a part of That is, a masking layer was partially provided on the base film, a release layer was provided on the entire surface of the masking layer and the base film, and a receiving layer was further provided on the release layer. In the configuration, the portion where the masking layer is formed is a region where retransfer is not performed on the transfer target, and the masking layer absorbs or blocks heat. The configuration. As a result, the area where the receptive layer is not re-transferred and the area where the thermal transfer image is formed on the re-transfer area can be easily separated by using a single intermediate transfer recording medium. Can be formed. The image forming method of the present invention is characterized in that, using any one of the above-described intermediate transfer recording media, a region where the receiving layer is not retransferred partially is formed on the transfer target.
[0011]
That is, the image forming method of the present invention forms a region where the receiving layer is not retransferred on a part of the transfer target, so that it can be peeled off on the base film. When forming an image using an intermediate transfer recording medium provided with a transfer portion comprising a release layer and a receiving layer, a masking layer is partially provided on one side of the substrate film, A release layer is provided on the entire surface of the material film, and a receiving layer is provided on the release layer. In the intermediate transfer recording medium provided with The masking layer absorbs or blocks heat, and the transfer portion is When re-transferring to the transfer target, The portion where the masking layer is provided in the lower layer of the transfer portion forms a region that is not retransferred to the transfer target that is not transferred to the transfer target. The portion of the receiving layer that is not to be transferred can be easily and reliably formed on the transfer medium by the function of absorbing or blocking heat during transfer with the intermediate transfer recording medium.
[0012]
DETAILED DESCRIPTION OF THE INVENTION
FIG. 1 is a schematic cross-sectional view showing an embodiment which is an intermediate
[0013]
FIG. 2 shows the intermediate
[0014]
FIG. 4 shows the intermediate
[0015]
The
As described above, as shown in the drawing, the masking layer is formed at least in the upper layer portion or the lower layer portion of the transfer portion composed of the receiving layer.
[0016]
(Base film)
As the
[0017]
(Receptive layer)
The receiving layer is a main part of the transfer portion constituting the intermediate transfer recording medium. On this receiving layer, an image is formed by thermal transfer from a thermal transfer sheet having a color material layer by thermal transfer. Then, the transfer portion of the intermediate transfer recording medium on which the image is formed is transferred to the transfer target, and as a result, a printed matter is formed.
For this reason, as a material for forming the receiving layer, a conventionally known resin material that can easily receive a heat transferable color material such as a sublimation dye or a heat-meltable ink can be used. For example, polyolefin resin such as polypropylene, halogenated resin such as polyvinyl chloride or polyvinylidene chloride, polyvinyl acetate, vinyl chloride-vinyl acetate copolymer, ethylene-vinyl acetate copolymer or polyacrylate Vinyl resins, polyester resins such as polyethylene terephthalate or polybutylene terephthalate, polystyrene resins, polyamide resins, copolymers of olefins such as ethylene or propylene and other vinyl polymers, cellulose resins such as ionomers or cellulose diastase Polycarbonate, etc., and vinyl chloride resin, acrylic-styrene resin or polyester resin is particularly preferable.
[0018]
When the receiving layer is transferred to the transfer medium via the adhesive layer, the adhesiveness of the receiving layer itself is not necessarily required. However, when the receptor layer is transferred to the transfer medium without passing through the adhesive layer, it is preferable to form the receptor layer using an adhesive resin material such as vinyl chloride-vinyl acetate copolymer.
The receiving layer is a coating for the receiving layer, which is prepared by adding one or more materials selected from the above materials and various additives as necessary, and dissolving or dispersing them in an appropriate solvent such as water or an organic solvent. A liquid can be prepared, and this can be formed by applying and drying by means of a gravure printing method, a screen printing method or a reverse coating method using a gravure plate. The thickness is 1 to 10 g / m in a dry state. 2 Degree.
[0019]
(Masking layer)
The
[0020]
Moreover, a filler can be contained in the masking layer. Examples of the filler include inorganic fillers such as silica, alumina, clay, talc, calcium carbonate, and barium sulfate, white pigments such as titanium oxide and zinc oxide, acrylic resins, epoxy resins, polyurethane resins, phenol resins, and melamine resins. , Resin particles (plastic pigment) such as benzoguanamine resin, fluororesin, silicone resin or polyethylene wax, paraffin wax, carnauba wax, microcrystalline wax, wood wax, beeswax, whale wax, ibota wax, wool wax, candelilla wax, some Various known wax particles such as modified waxes and fatty acid amides can be mentioned. When air bubbles or a foaming agent is contained in the masking layer, or a filler is contained, it is added at about 0.01 to 200% by weight with respect to the masking layer binder resin.
[0021]
In addition, a porous masking layer having a sea-island structure shown below can be provided. As a porous manufacturing method, a wet coagulation method is generally used, and two or more porous forming resin components having greatly different solubility parameters can be dissolved in a solvent and applied to a base film, and then mixed with the solvent. The solvent substitution is performed by passing the resin component through a solvent that does not dissolve the resin component. As a result, under the substituted solvent, the solubility parameter of the porous forming resin component is greatly different, so that two or more kinds of resins form a sea-island structure. Thereafter, by passing through a heat bath, the island portion of the sea-island structure is further heat-shrinked and the porosity is increased. At that time, the island portion becomes organic fine particles. Thereafter, desorption and drying are performed to obtain a porous masking layer. In the case of this porous masking layer, it is necessary to adjust the size and density of the island portion and the thickness of the non-transfer layer in order to provide a heat insulating effect.
The masking layer as described above is 0.05 to 5.0 g / m at the time of drying by known coating means such as gravure coating, gravure reverse coating, and roll coating. 2 It is formed with a thickness of about.
[0022]
In the intermediate transfer recording medium of the present invention, if necessary, it is possible to prevent fusion with a heating means such as a thermal head or a heat roll on the surface opposite to the side on which the receiving layer of the base film is provided, and slidability. In order to improve this, a back layer may be provided.
[0023]
(Release layer)
In the intermediate transfer recording medium of the present invention, a
The release layer is provided when the release property at the time of thermal transfer of the receiving layer to the transfer target is not sufficient due to the combination of the material of the base film and the receiving layer. Such a release layer can be formed by using a release agent such as waxes, silicone waxes, silicone resins, or the like, or hydrophilic resins described in JP-A-4-142898 and various curable properties. Resins and the like can be appropriately selected and used according to the characteristics of the base film and the non-transfer layer, and are not particularly limited. The release layer is formed by applying an ink prepared by dissolving or dispersing an additive necessary for the release agent as described above in an appropriate solvent, and drying it on a base film by a known means. The thickness is 0.1 to 5 g / m when dried. 2 The degree is preferred.
[0024]
(Detection mark)
The shape, color, and the like of the
Further, a mark using a hologram or a diffraction grating can be used as the detection mark. As a method for forming this hologram mark, there is a conventionally known hologram pattern forming method. For example, a fine plate is formed by embossing using an original plate provided with an uneven pattern of hologram interference fringes. As this hologram mark sensor, a so-called hologram sensor can be used, and light emitted from the light emitting element is irregularly reflected by the hologram mark to emit diffracted light. The position of the hologram mark can be detected by detecting the diffracted light with a light receiving element.
In addition, the position where the detection mark is provided is not limited to the illustrated one. For example, if the film substrate has transparency, the detection is performed on the surface of the film substrate opposite to the surface on which the receiving layer is provided. Marks can be provided. Moreover, although what was illustrated has provided the detection mark on the receiving layer, it is not limited to it, A detection mark can be provided between a film base material and a mold release layer, or it can select suitably.
[0025]
The detection mark used in the intermediate transfer recording medium of the present invention is synchronized with the portion where the masking layer is partially formed, that is, the region where the receptive layer is not retransferred, and the designated position of the region where the receptive layer is not retransferred. The distance between the detection mark (for example, the start position of the area) and the detection mark is fixed, the mark is detected, and the retransfer of the receiving layer is started at a fixed position of the transfer target, so that the retransfer of the receiving layer is performed. The area that is not to be transferred can be accurately placed at the specified position of the transfer object. Usually, the detection mark synchronized with the part in which the masking layer is partially formed is formed at one place per screen.
[0026]
(Transfer material)
Next, the transfer target will be described. The transfer portion on which the above-described thermal transfer image of the intermediate transfer recording medium is formed is transferred onto the transfer medium. However, the portion having the masking layer is not transferred to the transfer target.
The material to be transferred used in the present invention is not particularly limited. For example, natural pulp paper, coated paper, tracing paper, plastic film that is not deformed by heat during transfer, glass, metal, ceramics, wood, cloth, etc. It may be a thing.
However, if the portion of the intermediate transfer recording medium that is not transferred by using a masking layer on the transfer object is, for example, an entry field such as an address or name, or a stamp field of the writer or issuer, the transfer object Is preferably natural pulp paper having a writing ability and a printing ability.
Natural pulp paper is not particularly limited, for example, fine paper, art paper, lightweight coated paper, fine coated paper, coated paper, cast coated paper, synthetic resin or emulsion impregnated paper, synthetic rubber latex impregnated paper, synthetic resin internal additive Examples thereof include paper and thermal transfer paper.
[0027]
Regarding the shape and use of the transferred object, stock certificates, securities, certificates, passbooks, boarding tickets, car horse tickets, stamps, stamps, appreciation tickets, admission tickets, tickets, etc., cash cards, credit cards, prepaid cards, Cards such as members cards, greeting cards, postcards, business cards, driver's licenses, IC cards, optical cards, cases such as cartons, containers, bags, forms, envelopes, tags, OHP sheets, slide films, bookmarks, Calendars, posters, brochures, menus, passports, POP supplies, coasters, displays, nameplates, keyboards, cosmetics, wristwatches, lighters and other accessories, stationery, report paper and other stationery, building materials, panels, emblems, keys, cloth, clothing , Footwear, radio, TV, calculator, OA equipment, etc., various samples , Album, In addition, computer graphics output, medical image output, etc., do not ask the kind.
[0028]
(Image forming method)
Next, using the above-described intermediate transfer recording medium, a receiving layer is partially formed on the transferred body having a hollow portion on an arbitrary transferred body or having a complicated outer edge shape. The image forming method of the present invention for forming a region that is not retransferred will be described. Mentioned above, When forming an image using an intermediate transfer recording medium provided with a transfer part composed of a release layer and a receiving layer so as to be peelable on the base film, a masking layer is partially formed on one side of the base film. In the intermediate transfer recording medium in which a release layer is provided on the entire surface of the masking layer and the base film, and a receiving layer is provided on the release layer, the masking layer absorbs or blocks heat. When the transfer part is re-transferred to the transfer object, the part where the masking layer is provided in the lower part of the transfer part is a region that is not transferred to the transfer object that is not transferred to the transfer object. Is formed. That An image is formed by transferring a dye layer or a heat-meltable ink layer from a thermal transfer sheet to a receiving layer of an intermediate transfer recording medium by a heating means such as a thermal head. Next, the image-formed transfer portion of the intermediate transfer recording medium is retransferred onto the transfer medium by a heating means such as a heat roll. At the time of the retransfer, the portion provided with the masking layer of the intermediate transfer recording medium is not transferred to the transfer target, and the other retransfer and heated portions are transferred.
[0029]
In the image forming method of the present invention, one or both sides of a transfer object are used by using an intermediate transfer recording medium in which a region that is not retransferred to the transfer object is provided on at least a part of the single-sided unit on a screen divided by detection marks. A region where the receptive layer of the receiving layer is not retransferred and a region where the receptive layer on which the thermal transfer image is formed are re-transferred can be separated into a part of the image forming portion with accurate positional accuracy.
The detection mark is a distinction between the transfer layer for the front surface of the transfer object or the transfer layer for the back surface (the distinction between the front surface and the back surface is shown in FIG. It is used to detect the position of the layer), and when the image is formed on the transfer target, an area where the receiving layer is not retransferred is provided on the specified surface. The re-transfer area of the receiving layer having the thermal transfer image is accurately divided, the edge of the receiving layer transferred to the transfer object is sharp, and the portion that should not be transferred is not transferred and stable. Transferability of the receiving layer can be obtained.
In this way, the detection mark on the intermediate transfer recording medium is detected by a detector on the printer side, and in conjunction with the printer, the position of the thermal transfer image on the intermediate transfer recording medium and the retransfer of the transfer portion to the transfer object Can be aligned.
[0030]
( Reference example 1 )
First, a transparent polyethylene terephthalate having a thickness of 12 μm is used as a base film, and a release layer coating liquid shown below is applied to the surface of the base film, followed by drying. 0g / m 2 The release layer was formed. Then, on the release layer, the following receiving layer coating solution was applied and dried, and when dried, the thickness was 2.0 g / m. 2 A receptive layer was formed. In the text, “part” or “%” is based on weight unless otherwise specified.
(Release layer coating solution)
Acrylic resin (Mitsubishi Rayon Co., Ltd., BR-83) 88 parts
1 part of polyester resin
11 parts of polyethylene wax
50 parts of methyl ethyl ketone
50 parts of toluene
[0031]
(Coating fluid for receiving layer)
40 parts of vinyl chloride-vinyl acetate copolymer
Acrylic silicone 1.5 parts
50 parts of methyl ethyl ketone
50 parts of toluene
[0032]
Next, a masking layer ink having the following composition is formed on the above receiving layer in a pattern as shown in FIG. 2 A masking layer was formed.
(Ink for masking layer)
50 parts of acrylic resin
50 parts of polyethylene wax
Methyl ethyl ketone 25 parts
25 parts of toluene
[0033]
Furthermore, the ink for detection marks having the following composition has a pattern as shown in FIG. 3 and a thickness of 1.5 g / m when dried on a gravure printing machine. 2 The detection mark of Reference example 1 An intermediate transfer recording medium was prepared.
(Detection mark ink)
Carbon black 8.0 parts
Urethane resin (Nippon Polyurethane Co., Ltd., HMS-20) 5.0 parts
Methyl ethyl ketone 38.5 parts
Toluene 38.5 parts
[0034]
Obtained above Reference example 1 Use a thermal transfer printer equipped with a commercially available thermal head on the receiving layer of the intermediate transfer recording medium (on the receiving layer that does not cover the masking layer), and use a sublimation type thermal transfer sheet dedicated to the thermal transfer printer. A photographic tone image was formed. During the image formation, a detection mark on the intermediate transfer recording medium was detected on the printer side, and the image on the receiving layer was aligned. Thereafter, the above-mentioned image-formed transfer portion is permanently installed on the designated position of a white PET-G sheet (Mitsubishi Resin Co., Ltd .: PET-G, Diafix PG-W) having a thickness of 600 μm. Using a commercially available laminator, retransfer was carried out to obtain a printed product. However, the address on the transfer surface of the PET-G sheet, the handwritten entry field of the name, and the position corresponding to the seal field are pre-treated with the sign panel, and the masking layer part and the sign panel field Was aligned. When the transfer portion of the intermediate transfer recording medium was retransferred to the transfer target, a detection mark on the intermediate transfer recording medium was detected on the printer side, and alignment was performed.
[0035]
the above Reference example 1 The printed matter obtained in the above is the transfer portion of the intermediate transfer recording medium, and only the transferred portion of the masking layer is not transferred to the transfer body, and the handwritten entry column and the stamped column are omitted. A thermal transfer image was formed at a portion. The handwritten entry field was filled with a ballpoint pen, and no unclear part was produced. Furthermore, when the stamp was pressed with vermilion in the stamping column, no unclear part was produced. Further, the thermal transfer image was clear and of excellent quality.
[0036]
( Reference example 2 ) Reference example 1 Using the same base film as on the surface of the base film, Reference example 1 Apply the same release layer coating liquid used in the above, dry it, and dry it onto the substrate film at a thickness of 2.0 g / m 2 The release layer was formed. Next, on the release layer, Reference example 1 The same coating solution for the receiving layer used in the above was applied, dried, and dried onto the base film at a thickness of 2.0 g / m. 2 A receptive layer was formed. And on that receptive layer, Reference example 1 The same masking layer ink used in Fig. 4 has a pattern as shown in Fig. 4 and a gravure printing machine with a thickness of 2.0 g / m when dried. 2 A masking layer was formed. further, Reference example 1 The same detection mark ink used in Fig. 4 has a pattern as shown in Fig. 4 and is a gravure printing machine with a thickness of 1.5 g / m when dried. 2 The transfer layer A of the image forming unit for the front surface of the transfer body and the transfer layer B of the image forming unit for the back surface of the transfer body were repeatedly formed as ABABAB. The masking layer is formed only on the transfer layer B side of the image forming unit for the back surface of the transfer target. In this way Reference example 2 An intermediate transfer recording medium was prepared.
[0037]
Obtained above Reference example 2 On the transfer layer A of the image forming unit for the front surface of the intermediate transfer recording medium, Reference example 1 Using the sublimation type thermal transfer sheet dedicated to the same thermal transfer printer used in the above, a full color photographic image and a thermal transfer image of the melt transfer character image were formed with the thermal transfer printer using the thermal fusion type thermal transfer sheet. . Next, for the transfer part B transferred to the back surface of the transfer object adjacent to the transfer part A transferred to the front surface of the transfer object, the same hot-melt thermal transfer sheet as above A thermal transfer image of a melt-transfer character image was formed using the thermal transfer printer used above. However, at that time, the character image of the melt transfer was formed on the portion where the masking layer was not printed. When the image is formed, the detection mark for the front surface of the transfer medium and the detection mark for the back surface of the transfer medium included in the intermediate transfer recording medium are detected on the printer side and transferred to the transfer medium on the receiving layer. The front and back images to be transferred were aligned.
[0038]
Then Reference example 1 A commercially available laminator in which the above-mentioned image-formed transfer portion for the front surface is installed at the designated position on the front surface of the white PET-G sheet similar to the transfer material used in the above, is installed. And re-transferred to obtain a print. Next, on the back side of the white PET-G sheet image-transferred on the front side, the transfer part for the back side on which the image is formed, using a commercially available laminator with a permanent heat roll And retransferred to obtain a printed material having images on both sides. However, the address of the transfer surface, which is the back side of the PET-G sheet, and the position corresponding to the handwritten entry field of the name are pre-treated with the sign panel, the masking layer part, the sign panel field, Was aligned. When the transfer portion of the intermediate transfer recording medium is retransferred to the transfer target, the detection mark of the transfer layer for the front surface of the transfer target included in the intermediate transfer recording medium and the transfer layer for the back surface of the transfer target The detection marks were respectively detected on the printer side, and the transfer portion on which the image was formed on the intermediate transfer recording medium was re-transferred with the positions designated on the front surface and the back surface of the transfer target.
[0039]
the above Reference example 2 The printed matter obtained in
[0040]
(Comparative Example 1)
Reference example 1 Using the same base film as on the surface of the base film, Reference example 1 Apply the same release layer coating liquid used in the above, dry it, and dry it onto the substrate film at a thickness of 2.0 g / m 2 The release layer was formed. Next, on the release layer, Reference example 1 The same coating solution for the receiving layer used in the above was applied, dried, and dried onto the base film at a thickness of 2.0 g / m. 2 The intermediate transfer recording medium of Comparative Example 1 was produced. On the receiving layer of the intermediate transfer recording medium obtained above, Reference example Using the same thermal transfer printer and thermal transfer sheet as used in Example 1, a sublimation transfer photographic image and a heat transfer image of a melt transfer character image were formed. next, Reference example 1 The same PET-G sheet used in the above and the image-formed transfer portion are overlapped, and the portion excluding the position corresponding to the address and name handwritten entry column and the stamp column is heated and pressurized. Using a relief stamp for hot stamping having the above pattern, hot pressing was performed, and the transfer portion was retransferred to the transfer medium to obtain a printed matter. When the printed matter obtained in the above Comparative Example 1 was entered with a ballpoint pen at the position of the handwritten entry field, the ink was partially repelled, resulting in an unclear portion. Furthermore, when a stamp was pressed with vermilion in the stamping column, a portion where vermilion was repelled occurred and was unclear.
[0041]
【The invention's effect】
As described above, by the image forming method of the present invention, in order to form a region where the receiving layer is not re-transferred on a part of the transfer object, it can be peeled off on the base film. When forming an image using an intermediate transfer recording medium provided with a transfer portion comprising a release layer and a receiving layer, a masking layer is partially provided on one side of the substrate film, In an intermediate transfer recording medium in which a release layer is provided on the entire surface of a material film, and a receiving layer is provided on the release layer, the masking layer absorbs or blocks heat, and the transfer portion When the image is retransferred to the transfer object, the portion where the masking layer is provided in the lower layer of the transfer part forms a region that is not transferred to the transfer object that is not transferred to the transfer object. The portion of the receiving layer that should not be transferred can be easily and reliably formed on the transfer medium by absorbing or blocking heat at the time of transfer on the intermediate transfer recording medium.
[Brief description of the drawings]
FIG. 1 is a schematic cross-sectional view showing one embodiment which is an intermediate transfer recording medium of the present invention.
FIG. 2 is an intermediate transfer recording medium of the present invention. A reference example It is a schematic sectional drawing which shows embodiment.
FIG. 3 is an intermediate transfer recording medium of the present invention. A reference example It is the schematic which shows embodiment.
FIG. 4 is an intermediate transfer recording medium of the present invention. A reference example It is the schematic which shows embodiment.
[Explanation of symbols]
1 Intermediate transfer recording medium
2 Base film
3 Receptive layer
4 Masking layer
5 Release layer
6 Detection mark
A Transfer layer for the front surface of the transfer target
B Transfer layer for the back side of the transfer target
Claims (4)