JP2017105770A - Compound, resin, resist composition, and method for producing resist pattern - Google Patents

Compound, resin, resist composition, and method for producing resist pattern Download PDF

Info

Publication number
JP2017105770A
JP2017105770A JP2016232322A JP2016232322A JP2017105770A JP 2017105770 A JP2017105770 A JP 2017105770A JP 2016232322 A JP2016232322 A JP 2016232322A JP 2016232322 A JP2016232322 A JP 2016232322A JP 2017105770 A JP2017105770 A JP 2017105770A
Authority
JP
Japan
Prior art keywords
group
formula
hydrocarbon group
carbon atoms
structural unit
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2016232322A
Other languages
Japanese (ja)
Other versions
JP6905330B2 (en
Inventor
達郎 増山
Tatsuro Masuyama
達郎 増山
市川 幸司
Koji Ichikawa
幸司 市川
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sumitomo Chemical Co Ltd
Original Assignee
Sumitomo Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sumitomo Chemical Co Ltd filed Critical Sumitomo Chemical Co Ltd
Publication of JP2017105770A publication Critical patent/JP2017105770A/en
Application granted granted Critical
Publication of JP6905330B2 publication Critical patent/JP6905330B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a compound which makes it possible to produce a resist pattern with an excellent focus margin, a resin and a resist composition comprising the resin.SOLUTION: The present invention provides a compound represented by formula (I), a resin comprising a structural unit derived from the compound and a resist composition [where, Rand Rindependently represent a C1-C6 alkyl group which may comprise a halogen atom, a hydrogen atom or a halogen atom. Land Lindependently represent -CHR-CH- or -CH-CHR-. Rand Rindependently represent a C1-C6 alkyl group. Ais a C1-C12 divalent hydrocarbon group having a fluorine atom].SELECTED DRAWING: None

Description

本発明は、化合物、樹脂、該樹脂を含有するレジスト組成物及び該レジスト組成物を用いるレジストパターンの製造方法等に関する。   The present invention relates to a compound, a resin, a resist composition containing the resin, a method for producing a resist pattern using the resist composition, and the like.

特許文献1には、下記化合物に由来する構造単位を含む樹脂を含有するレジスト組成物が記載されている。

Figure 2017105770
Patent Document 1 describes a resist composition containing a resin containing a structural unit derived from the following compound.
Figure 2017105770

特開2012−233181号公報JP 2012-233181 A

上記樹脂を使用したレジスト組成物では、フォーカスマージン(DOF)が必ずしも満足できない場合があった。   A resist composition using the above resin may not always satisfy the focus margin (DOF).

本発明は、以下の発明を含む。
〔1〕式(I)で表される化合物。

Figure 2017105770
[式(I)中、
及びRは、それぞれ独立に、ハロゲン原子を有してもよい炭素数1〜6のアルキル基、水素原子又はハロゲン原子を表す。
及びLは、それぞれ独立に、−CHR−CH−又は−CH−CHR−を表す。
及びRは、それぞれ独立に、炭素数1〜6のアルキル基を表す。
は、フッ素原子を有する炭素数1〜12の2価の炭化水素基を表す。]
〔2〕R及びRが、メチル基である〔1〕記載の化合物。
〔3〕〔1〕又は〔2〕記載の化合物に由来する構造単位を有する樹脂。
〔4〕さらに、フッ素原子を有する構造単位(a4)を有する〔3〕記載の樹脂。
〔5〕〔3〕又は〔4〕記載の樹脂、酸不安定基を有する構造単位を有する樹脂及び酸発生剤を含有するレジスト組成物。
〔6〕酸発生剤が、式(B1)で表される塩である〔5〕記載のレジスト組成物。
Figure 2017105770
[式(B1)中、
1及びQ2は、それぞれ独立に、フッ素原子又は炭素数1〜6のペルフルオロアルキル基を表す。
b1は、置換基を有していてもよい炭素数1〜24の2価の飽和炭化水素基を表し、該2価の飽和炭化水素基に含まれる−CH2−は、−O−又は−CO−に置き換わっていてもよく、該2価の飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基で置換されていてもよい。
Yは、置換基を有していてもよいメチル基又は置換基を有していてもよい炭素数3〜18の1価の脂環式炭化水素基を表し、該メチル基及び該1価の脂環式炭化水素基に含まれる−CH2−は、−O−、−SO2−又は−CO−に置き換わっていてもよい。
+は、有機カチオンを表す。]
〔7〕酸発生剤から発生する酸よりも酸性度の弱い酸を発生する塩をさらに含有する〔5〕又は〔6〕記載のレジスト組成物。
〔8〕(1)〔5〕〜〔7〕のいずれかに記載のレジスト組成物を基板上に塗布する工程、
(2)塗布後の組成物を乾燥させて組成物層を形成する工程、
(3)組成物層に露光する工程、
(4)露光後の組成物層を加熱する工程、及び
(5)加熱後の組成物層を現像する工程を含むレジストパターンの製造方法。 The present invention includes the following inventions.
[1] A compound represented by the formula (I).
Figure 2017105770
[In the formula (I),
R 1 and R 2 each independently represents a C 1-6 alkyl group which may have a halogen atom, a hydrogen atom or a halogen atom.
L 1 and L 2 each independently represent —CHR 3 —CH 2 — or —CH 2 —CHR 4 —.
R 3 and R 4 each independently represents an alkyl group having 1 to 6 carbon atoms.
A 3 represents a divalent hydrocarbon group having 1 to 12 carbon atoms having a fluorine atom. ]
[2] The compound according to [1], wherein R 3 and R 4 are methyl groups.
[3] A resin having a structural unit derived from the compound according to [1] or [2].
[4] The resin according to [3], further comprising a structural unit (a4) having a fluorine atom.
[5] A resist composition comprising the resin according to [3] or [4], a resin having a structural unit having an acid labile group, and an acid generator.
[6] The resist composition according to [5], wherein the acid generator is a salt represented by the formula (B1).
Figure 2017105770
[In the formula (B1),
Q 1 and Q 2 each independently represents a fluorine atom or a C 1-6 perfluoroalkyl group.
L b1 represents a C1-C24 divalent saturated hydrocarbon group which may have a substituent, and —CH 2 — contained in the divalent saturated hydrocarbon group is —O— or -CO- may be substituted, and the hydrogen atom contained in the divalent saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group.
Y represents a methyl group which may have a substituent or a monovalent alicyclic hydrocarbon group having 3 to 18 carbon atoms which may have a substituent, and the methyl group and the monovalent —CH 2 — contained in the alicyclic hydrocarbon group may be replaced with —O—, —SO 2 — or —CO—.
Z + represents an organic cation. ]
[7] The resist composition according to [5] or [6], further comprising a salt that generates an acid having a lower acidity than an acid generated from an acid generator.
[8] (1) A step of applying the resist composition according to any one of [5] to [7] on a substrate,
(2) The process of drying the composition after application | coating and forming a composition layer,
(3) a step of exposing the composition layer;
(4) A method for producing a resist pattern, comprising: a step of heating the composition layer after exposure; and (5) a step of developing the composition layer after heating.

本発明の樹脂を使用したレジスト組成物を用いることにより、フォーカスマージン(DOF)が良好なレジストパターンを作製することができる。   By using a resist composition using the resin of the present invention, a resist pattern having a good focus margin (DOF) can be produced.

本明細書において「(メタ)アクリレート」とは、それぞれ「アクリレート及びメタクリレートの少なくとも一種」を意味する。「(メタ)アクリル酸」や「(メタ)アクリロイル」等の表記も、同様の意味を有する。
また、特に断りのない限り、「脂肪族炭化水素基」のように直鎖状又は分岐状をとり得る基は、そのいずれをも含む。「芳香族炭化水素基」は芳香環に炭化水素基が結合した基をも包含する。立体異性体が存在する場合は、全ての立体異性体を包含する。
本明細書において、「レジスト組成物の固形分」とは、レジスト組成物の総量から、後述する溶剤(E)を除いた成分の合計を意味する。
In the present specification, “(meth) acrylate” means “at least one of acrylate and methacrylate”. The notations such as “(meth) acrylic acid” and “(meth) acryloyl” have the same meaning.
Further, unless otherwise specified, a group that can be linear or branched, such as an “aliphatic hydrocarbon group”, includes both of them. The “aromatic hydrocarbon group” also includes a group in which a hydrocarbon group is bonded to an aromatic ring. When stereoisomers exist, all stereoisomers are included.
In the present specification, the “solid content of the resist composition” means the total of components excluding the solvent (E) described later from the total amount of the resist composition.

〔化合物(I)〕
本発明の化合物は、以下の式で表される((以下「化合物(I)」という場合がある)。

Figure 2017105770
[式(I)中、
及びRは、それぞれ独立に、ハロゲン原子を有してもよい炭素数1〜6のアルキル基、水素原子又はハロゲン原子を表す。
及びLは、それぞれ独立に、−CHR−CH−又は−CH−CHR−を表す。
及びRは、それぞれ独立に、炭素数1〜6のアルキル基を表す。
は、フッ素原子を有する炭素数1〜12の2価の炭化水素基を表す。] [Compound (I)]
The compound of the present invention is represented by the following formula ((hereinafter sometimes referred to as “compound (I)”).
Figure 2017105770
[In the formula (I),
R 1 and R 2 each independently represents a C 1-6 alkyl group which may have a halogen atom, a hydrogen atom or a halogen atom.
L 1 and L 2 each independently represent —CHR 3 —CH 2 — or —CH 2 —CHR 4 —.
R 3 and R 4 each independently represents an alkyl group having 1 to 6 carbon atoms.
A 3 represents a divalent hydrocarbon group having 1 to 12 carbon atoms having a fluorine atom. ]

1、R、R及びRのアルキル基としては、メチル基、エチル基、n−プロピル基、イソプロピル基、n−ブチル基、sec−ブチル基、tert−ブチル基、n−ペンチル基及びn−ヘキシル基等が挙げられ、好ましくは、炭素数1〜4のアルキル基であり、より好ましくは、メチル基及びエチル基である。
1及びRのハロゲン原子としては、フッ素原子、塩素原子、臭素原子及びヨウ素原子が挙げられる。
1及びRのハロゲン原子を有するアルキル基としては、トリフルオロメチル基、ペルフルオロエチル基、ペルフルオロプロピル基、ペルフルオロイソプロピル基、ペルフルオロブチル基、ペルフルオロsec−ブチル基、ペルフルオロtert−ブチル基、ペルフルオロペンチル基、ペルフルオロヘキシル基、ペルクロロメチル基、ペルブロモメチル基及びペルヨードメチル基等が挙げられる。
1及びRは、それぞれ独立して、水素原子又はメチル基であることが好ましい。
及びRは、メチル基であることが好ましい。
Examples of the alkyl group for R 1 , R 2 , R 3 and R 4 include methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, sec-butyl group, tert-butyl group, and n-pentyl group. And an n-hexyl group and the like, preferably an alkyl group having 1 to 4 carbon atoms, and more preferably a methyl group and an ethyl group.
Examples of the halogen atom for R 1 and R 2 include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom.
Examples of the alkyl group having a halogen atom of R 1 and R 2 include trifluoromethyl group, perfluoroethyl group, perfluoropropyl group, perfluoroisopropyl group, perfluorobutyl group, perfluoro sec-butyl group, perfluorotert-butyl group, perfluoropentyl. A group, a perfluorohexyl group, a perchloromethyl group, a perbromomethyl group, a periodiomethyl group, and the like.
R 1 and R 2 are preferably each independently a hydrogen atom or a methyl group.
R 3 and R 4 are preferably methyl groups.

における2価の炭化水素基としては、鎖式及び環式の炭化水素基、これら鎖式及び環式の炭化水素基が組み合わせられたものをも包含する。また、炭素−炭素不飽和結合を有していてもよいが、飽和の炭化水素基が好ましい。
鎖式の炭化水素としては、メチレン基、エチレン基、プロパンジイル基、プロパンジイル基、ブタンジイル基、ペンタンジイル基及びペンタンジイルなどのアルカンジイル基が挙げられる。
環式の炭化水素基は、単環式又は多環式のいずれでもよい。単環式の炭化水素基としては、シクロペンタンジイル基、シクロへキサンジイル基、シクロヘプタンジイル基及びシクロオクタンジイル基などのシクロアルカンジイル基が挙げられる。多環式の炭化水素基としては、デカヒドロナフタレンジイル基、アダマンタンジイル基及びノルボルネンジイル基などが挙げられる。
鎖式及び環式の炭化水素基の組み合わせとしては、例えば、メチルシクロヘキサンジイル基、ジメチルシクロへキシル基、メチルノルボルニル基などが挙げられる。
のフッ素原子を有する2価の炭化水素基は、ここに示した炭化水素基に含まれる水素原子の少なくとも1個がフッ素原子に置換されたものである。
従って、Aのフッ素原子を有する2価の炭化水素基としては、以下で表される基が挙げられる。

Figure 2017105770
Examples of the divalent hydrocarbon group for A 3 include chain and cyclic hydrocarbon groups, and combinations of these chain and cyclic hydrocarbon groups. Moreover, although it may have a carbon-carbon unsaturated bond, a saturated hydrocarbon group is preferable.
Examples of the chain hydrocarbon include alkanediyl groups such as methylene group, ethylene group, propanediyl group, propanediyl group, butanediyl group, pentanediyl group and pentanediyl.
The cyclic hydrocarbon group may be monocyclic or polycyclic. Examples of the monocyclic hydrocarbon group include cycloalkanediyl groups such as cyclopentanediyl group, cyclohexanediyl group, cycloheptanediyl group, and cyclooctanediyl group. Examples of the polycyclic hydrocarbon group include a decahydronaphthalenediyl group, an adamantanediyl group, and a norbornenediyl group.
Examples of the combination of the chain and cyclic hydrocarbon groups include a methylcyclohexanediyl group, a dimethylcyclohexyl group, and a methylnorbornyl group.
The divalent hydrocarbon group having a fluorine atom of A 3 is one in which at least one hydrogen atom contained in the hydrocarbon group shown here is substituted with a fluorine atom.
Accordingly, examples of the divalent hydrocarbon group having a fluorine atom of A 3 include groups represented by the following.
Figure 2017105770

としては、炭素数1〜6のパーフルオロアルカンジイル基が好ましく、炭素数1〜4のパーフルオロアルカンジイル基がより好ましく、炭素数1〜3のパーフルオロアルカンジイル基がさらに好ましく、パーフルオロプロパンジイル基が特に好ましい。 A 3 is preferably a perfluoroalkanediyl group having 1 to 6 carbon atoms, more preferably a perfluoroalkanediyl group having 1 to 4 carbon atoms, still more preferably a perfluoroalkanediyl group having 1 to 3 carbon atoms, A fluoropropanediyl group is particularly preferred.

化合物(I)は、下記式で表される化合物が挙げられる。

Figure 2017105770
Examples of the compound (I) include compounds represented by the following formula.
Figure 2017105770

Figure 2017105770
Figure 2017105770

Figure 2017105770
Figure 2017105770

式(I−1)〜式(I−18)でそれぞれ表される化合物において、R1及びRに相当するメチル基が水素原子で置き換わった化合物も、化合物(I)の具体例として挙げることができる。 In the compounds represented by formulas (I-1) to (I-18), compounds in which methyl groups corresponding to R 1 and R 2 are replaced by hydrogen atoms are also exemplified as specific examples of compound (I). Can do.

<化合物(I)の製造方法>
化合物(I)は、式(I−a1)で表される化合物と、式(I−a2)で表される化合物と、式(I1−b)で表される化合物とを塩基触媒の存在下、溶媒中で、反応させることにより製造することができる。以下の式において、符号は全て上記と同義である。

Figure 2017105770
塩基性触媒としては、ピリジン、ジメチルアミノピリジンなどが挙げられる。
溶媒としては、クロロホルム、テトラヒドロフラン及びトルエンなどが挙げられる。
式(I1−b)で表される化合物としては、例えば、ヘプタフルオロ酪酸無水物等が挙げられ、市場より容易に入手することができる。
(I−a1)及び(I−a2)で表される化合物としては、下記式で表される化合物等が挙げられ、市場より容易に入手することができる。
Figure 2017105770
<Method for Producing Compound (I)>
Compound (I) comprises a compound represented by formula (I-a1), a compound represented by formula (I-a2), and a compound represented by formula (I1-b) in the presence of a base catalyst. It can be produced by reacting in a solvent. In the following formulas, all symbols are as defined above.
Figure 2017105770
Examples of the basic catalyst include pyridine and dimethylaminopyridine.
Examples of the solvent include chloroform, tetrahydrofuran and toluene.
Examples of the compound represented by the formula (I1-b) include heptafluorobutyric anhydride and the like, which can be easily obtained from the market.
Examples of the compounds represented by (I-a1) and (I-a2) include compounds represented by the following formulas and can be easily obtained from the market.
Figure 2017105770

式(I−a1)又は式(I−a2)で表される化合物は、式(I−c1)又は式(I−c2)で表される化合物と式(I−d1)又は式(I−d2)で表される化合物とを、塩基触媒の存在下、溶媒中で、反応させることにより得ることもできる。

Figure 2017105770
溶媒としては、クロロホルム、テトラヒドロフラン及びトルエンなどが挙げられる。
塩基触媒としては、ピリジン、ジメチルアミノピリジンなどが挙げられる。
式(I−c1)及び式(I−c2)で表される化合物としては、下記式で表される化合物等が挙げられ、市場より容易に入手することができる。
Figure 2017105770
式(I−d1)及び式(I−d2)で表される化合物としては、下記式で表される化合物等が挙げられ、市場より容易に入手することができる。
Figure 2017105770
The compound represented by the formula (I-a1) or the formula (I-a2) includes the compound represented by the formula (I-c1) or the formula (I-c2) and the formula (I-d1) or the formula (I- It can also be obtained by reacting the compound represented by d2) in a solvent in the presence of a base catalyst.
Figure 2017105770
Examples of the solvent include chloroform, tetrahydrofuran and toluene.
Examples of the base catalyst include pyridine and dimethylaminopyridine.
Examples of the compound represented by the formula (I-c1) and the formula (I-c2) include a compound represented by the following formula, and can be easily obtained from the market.
Figure 2017105770
Examples of the compound represented by the formula (I-d1) and the formula (I-d2) include compounds represented by the following formulas and can be easily obtained from the market.
Figure 2017105770

〔樹脂(X)〕
樹脂(X)は、化合物(I)に由来する構造単位(以下「構造単位(I)」という場合がある)を含む。構造単位(I)は、2種以上を組み合わせてもよい。
樹脂(X)は、構造単位(I)以外の構造単位を含んでいてもよい。構造単位(I)以外の構造単位としては、フッ素原子を有する構造単位(a4)(但し、式(I)で表される化合物に由来する構造単位を除く。)及び非脱離炭化水素基を有する構造単位(a5)から選ばれる少なくとも一つの構造単位等が挙げられる。さらに、樹脂(X)は、酸不安定基を有する構造単位(以下「構造単位(a1)」という場合がある)、酸不安定基を有さない構造単位(以下「構造単位(s)」という場合がある)及びその他の公知のモノマーに由来する構造単位を含んでいてもよい。
[Resin (X)]
The resin (X) includes a structural unit derived from the compound (I) (hereinafter sometimes referred to as “structural unit (I)”). Two or more structural units (I) may be combined.
Resin (X) may contain structural units other than structural unit (I). Examples of the structural unit other than the structural unit (I) include a structural unit (a4) having a fluorine atom (excluding a structural unit derived from the compound represented by the formula (I)) and a non-leaving hydrocarbon group. And at least one structural unit selected from the structural unit (a5). Further, the resin (X) includes a structural unit having an acid labile group (hereinafter sometimes referred to as “structural unit (a1)”), a structural unit having no acid labile group (hereinafter referred to as “structural unit (s)”). And may contain structural units derived from other known monomers.

樹脂(X)において、構造単位(I)の含有率は、樹脂(X)の全構造単位に対して、1〜10モル%が好ましく、2〜8モル%がより好ましく、2〜6モル%がさらに好ましい。
樹脂(X)が、構造単位(I)以外の構造単位を含む場合、構造単位(a4)を含むことが好ましい。
In the resin (X), the content of the structural unit (I) is preferably 1 to 10 mol%, more preferably 2 to 8 mol%, and more preferably 2 to 6 mol% with respect to all the structural units of the resin (X). Is more preferable.
When resin (X) contains structural units other than structural unit (I), it is preferable that structural unit (a4) is included.

<構造単位(a4)>
構造単位(a4)としては、式(a4−0)で表される構造単位が挙げられる。

Figure 2017105770
[式(a4−0)中、
は、水素原子又はメチル基を表す。
は、単結合又は炭素数1〜4の脂肪族飽和炭化水素基を表す。
は、炭素数1〜8のペルフルオロアルカンジイル基又は炭素数3〜12のペルフルオロシクロアルカンジイル基を表す。
は、水素原子又はフッ素原子を表す。] <Structural unit (a4)>
As the structural unit (a4), a structural unit represented by formula (a4-0) can be given.
Figure 2017105770
[In the formula (a4-0),
R 5 represents a hydrogen atom or a methyl group.
L 4 represents a single bond or an aliphatic saturated hydrocarbon group having 1 to 4 carbon atoms.
L 3 represents a C 1-8 perfluoroalkanediyl group or a C 3-12 perfluorocycloalkanediyl group.
R 6 represents a hydrogen atom or a fluorine atom. ]

の脂肪族飽和炭化水素基としては、炭素数1〜4のアルカンジイル基が挙げられ、例えば、メチレン基、エチレン基、プロパン−1,3−ジイル基、ブタン−1,4−ジイル基等の直鎖状アルカンジイル基、直鎖状アルカンジイル基に、アルキル基(中でも、メチル基、エチル基等)の側鎖を有したもの、エタン−1,1−ジイル基、プロパン−1,2−ジイル基、ブタン−1,3−ジイル基、2−メチルプロパン−1,3−ジイル基及び2−メチルプロパン−1,2−ジイル基等の分岐状アルカンジイル基が挙げられる。 Examples of the aliphatic saturated hydrocarbon group for L 4 include an alkanediyl group having 1 to 4 carbon atoms, such as a methylene group, an ethylene group, a propane-1,3-diyl group, and a butane-1,4-diyl group. Having a side chain of an alkyl group (especially methyl group, ethyl group, etc.), ethane-1,1-diyl group, propane-1, Examples thereof include branched alkanediyl groups such as 2-diyl group, butane-1,3-diyl group, 2-methylpropane-1,3-diyl group and 2-methylpropane-1,2-diyl group.

のペルフルオロアルカンジイル基としては、ジフルオロメチレン基、ペルフルオロエチレン基、ペルフルオロエチルフルオロメチレン基、ペルフルオロプロパン−1,3−ジイル基、ペルフルオロプロパン−1,2−ジイル基、ペルフルオロプロパン−2,2−ジイル基、ペルフルオロブタン−1,4−ジイル基、ペルフルオロブタン−2,2−ジイル基、ペルフルオロブタン−1,2−ジイル基、ペルフルオロペンタン−1,5−ジイル基、ペルフルオロペンタン−2,2−ジイル基、ペルフルオロペンタン−3,3−ジイル基、ペルフルオロヘキサン−1,6−ジイル基、ペルフルオロヘキサン−2,2−ジイル基、ペルフルオロヘキサン−3,3−ジイル基、ペルフルオロヘプタン−1,7−ジイル基、ペルフルオロヘプタン−2,2−ジイル基、ペルフルオロヘプタン−3,4−ジイル基、ペルフルオロヘプタン−4,4−ジイル基、ペルフルオロオクタン−1,8−ジイル基、ペルフルオロオクタン−2,2−ジイル基、ペルフルオロオクタン−3,3−ジイル基、ペルフルオロオクタン−4,4−ジイル基等が挙げられる。
のペルフルオロシクロアルカンジイル基としては、ペルフルオロシクロヘキサンジイル基、ペルフルオロシクロペンタンジイル基、ペルフルオロシクロヘプタンジイル基、ペルフルオロアダマンタンジイル基等が挙げられる。
Examples of the perfluoroalkanediyl group of L 3 include a difluoromethylene group, a perfluoroethylene group, a perfluoroethylfluoromethylene group, a perfluoropropane-1,3-diyl group, a perfluoropropane-1,2-diyl group, and a perfluoropropane-2,2 -Diyl group, perfluorobutane-1,4-diyl group, perfluorobutane-2,2-diyl group, perfluorobutane-1,2-diyl group, perfluoropentane-1,5-diyl group, perfluoropentane-2,2 -Diyl group, perfluoropentane-3,3-diyl group, perfluorohexane-1,6-diyl group, perfluorohexane-2,2-diyl group, perfluorohexane-3,3-diyl group, perfluoroheptane-1,7 -Diyl group, perfluoroheptane-2 , 2-diyl group, perfluoroheptane-3,4-diyl group, perfluoroheptane-4,4-diyl group, perfluorooctane-1,8-diyl group, perfluorooctane-2,2-diyl group, perfluorooctane-3 , 3-diyl group, perfluorooctane-4,4-diyl group, and the like.
Examples of the L 3 perfluorocycloalkanediyl group include a perfluorocyclohexanediyl group, a perfluorocyclopentanediyl group, a perfluorocycloheptanediyl group, and a perfluoroadamantanediyl group.

は、好ましくは単結合、メチレン基又はエチレン基であり、より好ましくは単結合又はメチレン基である。
は、好ましくは炭素数1〜6のペルフルオロアルカンジイル基であり、より好ましくは炭素数1〜3のペルフルオロアルカンジイル基であり、さらに好ましくは炭素数1〜2のペルフルオロアルカンジイル基であり、特に好ましくはジフルオロメチレン基である。
L 4 is preferably a single bond, a methylene group or an ethylene group, and more preferably a single bond or a methylene group.
L 3 is preferably a perfluoroalkanediyl group having 1 to 6 carbon atoms, more preferably a perfluoroalkanediyl group having 1 to 3 carbon atoms, and still more preferably a perfluoroalkanediyl group having 1 to 2 carbon atoms. Particularly preferred is a difluoromethylene group.

構造単位(a4−0)としては、以下に示す構造単位及びR5に相当するメチル基が水素原子で置き換わった構造単位等が挙げられる。

Figure 2017105770
Examples of the structural unit (a4-0) include the structural units shown below and structural units in which a methyl group corresponding to R 5 is replaced with a hydrogen atom.
Figure 2017105770

Figure 2017105770
Figure 2017105770

構造単位(a4)としては、式(a4−1)で表される構造単位が挙げられる。

Figure 2017105770
[式(a4−1)中、
a41は、水素原子又はメチル基を表す。
a42は、置換基を有していてもよい炭素数1〜20の炭化水素基を表し、該炭化水素基に含まれる−CH−は、−O−又は−CO−に置き換わっていてもよい。
a41は、置換基を有していてもよい炭素数1〜6のアルカンジイル基又は式(a−g1)で表される基を表す。]
Figure 2017105770
[式(a−g1)中、
sは、0又は1を表す。
a42及びAa44は、互いに独立に、置換基を有していてもよい炭素数1〜5の脂肪族炭化水素基を表す。
a43は、単結合又は置換基を有していてもよい炭素数1〜5の脂肪族炭化水素基を表す。
a41及びXa42は、互いに独立に、−O−、−CO−、−CO−O−又は−O−CO−を表す。
ただし、Aa42、Aa43、Aa44、Xa41及びXa42の炭素数の合計は7以下である。
*で表される2つの結合手のうち、右側の*が−O−CO−Ra42との結合手である。] As the structural unit (a4), a structural unit represented by formula (a4-1) can be given.
Figure 2017105770
[In the formula (a4-1),
R a41 represents a hydrogen atom or a methyl group.
R a42 represents an optionally substituted hydrocarbon group having 1 to 20 carbon atoms, and —CH 2 — contained in the hydrocarbon group may be replaced by —O— or —CO—. Good.
A a41 represents a C1-C6 alkanediyl group which may have a substituent or a group represented by the formula (a-g1). ]
Figure 2017105770
[In the formula (a-g1),
s represents 0 or 1.
A a42 and A a44 each independently represent a C 1-5 aliphatic hydrocarbon group which may have a substituent.
A a43 represents a C1-C5 aliphatic hydrocarbon group which may have a single bond or a substituent.
X a41 and X a42 each independently represent —O—, —CO—, —CO —O— or —O—CO—.
However, the total number of carbon atoms of A a42 , A a43 , A a44 , X a41 and X a42 is 7 or less.
Among the two bonds represented by *, the * on the right side is a bond with —O—CO—R a42 . ]

a42の炭化水素基としては、鎖式及び環式の脂肪族炭化水素基、芳香族炭化水素基、並びにこれらを組合せることにより形成される基が挙げられる。鎖式の脂肪族炭化水素基としては、メチル基、エチル基、n−プロピル基、n−ブチル基、n−ペンチル基、n−ヘキシル基、n−ヘプチル基、n−オクチル基、n−デシル基、n−ドデシル基、n−ペンタデシル基、n−ヘキサデシル基、n−ヘプタデシル基及びn−オクタデシル基が挙げられる。環式の脂肪族炭化水素基としては、シクロペンチル基、シクロへキシル基、シクロヘプチル基、シクロオクチル基等のシクロアルキル基;デカヒドロナフチル基、アダマンチル基、ノルボルニル基及び下記の基(*は結合手を表す。)等の多環式の脂環式炭化水素基が挙げられる。

Figure 2017105770
Examples of the hydrocarbon group for R a42 include chain and cyclic aliphatic hydrocarbon groups, aromatic hydrocarbon groups, and groups formed by combining these. Examples of chain aliphatic hydrocarbon groups include methyl, ethyl, n-propyl, n-butyl, n-pentyl, n-hexyl, n-heptyl, n-octyl, and n-decyl. Group, n-dodecyl group, n-pentadecyl group, n-hexadecyl group, n-heptadecyl group and n-octadecyl group. Cyclic aliphatic hydrocarbon groups include cyclopentyl group, cyclohexyl group, cycloheptyl group, cyclooctyl group and other cycloalkyl groups; decahydronaphthyl group, adamantyl group, norbornyl group and the following groups (* is a bond) And a polycyclic alicyclic hydrocarbon group such as “represents a hand.”
Figure 2017105770

芳香族炭化水素基としては、フェニル基、ナフチル基、アントリル基、ビフェニリル基、フェナントリル基及びフルオレニル基が挙げられる。   Examples of the aromatic hydrocarbon group include a phenyl group, a naphthyl group, an anthryl group, a biphenylyl group, a phenanthryl group, and a fluorenyl group.

a42の置換基としては、ハロゲン原子又は式(a−g3)で表される基が挙げられる。ハロゲン原子としては、フッ素原子、塩素原子、臭素原子及びヨウ素原子が挙げられ、好ましくはフッ素原子が挙げられる。

Figure 2017105770
[式(a−g3)中、
a43は、酸素原子、カルボニル基、カルボニルオキシ基又はオキシカルボニル基を表す。
a45は、少なくとも1つのハロゲン原子を有する炭素数1〜17の脂肪族炭化水素基を表す。
*は、結合手を表す。] Examples of the substituent for R a42 include a halogen atom or a group represented by the formula (a-g3). As a halogen atom, a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom are mentioned, Preferably a fluorine atom is mentioned.
Figure 2017105770
[In the formula (a-g3),
Xa43 represents an oxygen atom, a carbonyl group, a carbonyloxy group or an oxycarbonyl group.
A a45 represents a C 1-17 aliphatic hydrocarbon group having at least one halogen atom.
* Represents a bond. ]

a45の脂肪族炭化水素基としては、Ra42で例示したものと同様の基が挙げられる。
a42は、ハロゲン原子を有してもよい脂肪族炭化水素基であることが好ましく、ハロゲン原子を有するアルキル基及び/又は式(a−g3)で表される基を有する脂肪族炭化水素基であることがより好ましい。
a42がハロゲン原子を有する脂肪族炭化水素基である場合、好ましくはフッ素原子を有する脂肪族炭化水素基であり、より好ましくはペルフルオロアルキル基又はペルフルオロシクロアルキル基であり、さらに好ましくは炭素数が1〜6のペルフルオロアルキル基であり、とりわけ好ましくは炭素数1〜3のペルフルオロアルキル基である。ペルフルオロアルキル基としては、ペルフルオロメチル基、ペルフルオロエチル基、ペルフルオロプロピル基、ペルフルオロブチル基、ペルフルオロペンチル基、ペルフルオロヘキシル基、ペルフルオロヘプチル基及びペルフルオロオクチル基等が挙げられる。ペルフルオロシクロアルキル基としては、ペルフルオロシクロヘキシル基等が挙げられる。
a42が、式(a−g3)で表される基を有する脂肪族炭化水素基である場合、式(a−g3)で表される基に含まれる炭素数を含めて、脂肪族炭化水素基の総炭素数は、15以下が好ましく、12以下がより好ましい。式(a−g3)で表される基を置換基として有する場合、その数は1個が好ましい。
Examples of the aliphatic hydrocarbon group for A a45 include the same groups as those exemplified for R a42 .
R a42 is preferably an aliphatic hydrocarbon group which may have a halogen atom, an alkyl group having a halogen atom and / or an aliphatic hydrocarbon group having a group represented by the formula (a-g3). It is more preferable that
When R a42 is an aliphatic hydrocarbon group having a halogen atom, it is preferably an aliphatic hydrocarbon group having a fluorine atom, more preferably a perfluoroalkyl group or a perfluorocycloalkyl group, and still more preferably a carbon number. It is a 1-6 perfluoroalkyl group, Most preferably, it is a C1-C3 perfluoroalkyl group. Examples of the perfluoroalkyl group include a perfluoromethyl group, a perfluoroethyl group, a perfluoropropyl group, a perfluorobutyl group, a perfluoropentyl group, a perfluorohexyl group, a perfluoroheptyl group, and a perfluorooctyl group. Examples of the perfluorocycloalkyl group include a perfluorocyclohexyl group.
When R a42 is an aliphatic hydrocarbon group having a group represented by the formula (a-g3), including the number of carbons contained in the group represented by the formula (a-g3), the aliphatic hydrocarbon The total carbon number of the group is preferably 15 or less, more preferably 12 or less. When it has a group represented by the formula (a-g3) as a substituent, the number is preferably 1.

式(a−g3)で表される基を有する脂肪族炭化水素基は、さらに好ましくは式(a−g2)で表される基である。

Figure 2017105770
[式(a−g2)中、
a46は、ハロゲン原子を有していてもよい炭素数1〜17の脂肪族炭化水素基を表す。
a44は、カルボニルオキシ基又はオキシカルボニル基を表す。
a47は、ハロゲン原子を有していてもよい炭素数1〜17の脂肪族炭化水素基を表す。
ただし、Aa46、Aa47及びXa44の炭素数の合計は18以下であり、Aa46及びAa47のうち、少なくとも一方は、少なくとも1つのハロゲン原子を有する。
*はカルボニル基との結合手を表す。] The aliphatic hydrocarbon group having a group represented by the formula (a-g3) is more preferably a group represented by the formula (a-g2).
Figure 2017105770
[In the formula (a-g2),
A a46 represents an aliphatic hydrocarbon group having 1 to 17 carbon atoms which may have a halogen atom.
X a44 represents a carbonyloxy group or an oxycarbonyl group.
A a47 represents an aliphatic hydrocarbon group having 1 to 17 carbon atoms which may have a halogen atom.
However, the total number of carbon atoms of A a46 , A a47 and X a44 is 18 or less, and at least one of A a46 and A a47 has at least one halogen atom.
* Represents a bond with a carbonyl group. ]

a46の脂肪族炭化水素基の炭素数は、1〜6であることが好ましく、1〜3であることがより好ましい。
a47の脂肪族炭化水素基の炭素数は、4〜15であることが好ましく、5〜12であることがより好ましく、シクロヘキシル基又はアダマンチル基であることがさらに好ましい。
The number of carbon atoms of the aliphatic hydrocarbon group for A a46 is preferably 1 to 6, and more preferably 1 to 3.
The carbon number of the aliphatic hydrocarbon group for A a47 is preferably 4 to 15, more preferably 5 to 12, and further preferably a cyclohexyl group or an adamantyl group.

*−Aa46−Xa44−Aa47で表される好ましい構造は、以下の構造である。

Figure 2017105770
A preferred structure represented by * -A a46 -X a44 -A a47 is the following structure.
Figure 2017105770

a41のアルカンジイル基としては、メチレン基、エチレン基、プロパン−1,3−ジイル基、ブタン−1,4−ジイル基、ペンタン−1,5−ジイル基、ヘキサン−1,6−ジイル基等の直鎖状アルカンジイル基;プロパン−1,2−ジイル基、ブタン−1,3−ジイル基、2−メチルプロパン−1,2−ジイル基、1−メチルブタン−1,4−ジイル基、2−メチルブタン−1,4−ジイル基等の分岐状アルカンジイル基が挙げられる。
a41のアルカンジイル基における置換基としては、ヒドロキシ基及び炭素数1〜6のアルコキシ基等が挙げられる。
a41は、好ましくは炭素数1〜4のアルカンジイル基であり、より好ましくは炭素数2〜4のアルカンジイル基であり、さらに好ましくはエチレン基である。
As the alkanediyl group of Aa41 , a methylene group, an ethylene group, a propane-1,3-diyl group, a butane-1,4-diyl group, a pentane-1,5-diyl group, a hexane-1,6-diyl group Linear alkanediyl group such as propane-1,2-diyl group, butane-1,3-diyl group, 2-methylpropane-1,2-diyl group, 1-methylbutane-1,4-diyl group, Examples include branched alkanediyl groups such as 2-methylbutane-1,4-diyl group.
Examples of the substituent in the alkanediyl group of Aa41 include a hydroxy group and an alkoxy group having 1 to 6 carbon atoms.
A a41 is preferably an alkanediyl group having 1 to 4 carbon atoms, more preferably an alkanediyl group having 2 to 4 carbon atoms, and still more preferably an ethylene group.

基(a−g1)におけるAa42〜Aa44の脂肪族炭化水素基は、鎖式及び環式の脂肪族炭化水素基並びにこれらが組合せることにより形成される基が好ましく、炭素−炭素不飽和結合を有していてもよいが、鎖式及び環式の脂肪族飽和炭化水素基並びにこれらを組合せることにより形成される基がより好ましい。
具体的には、メチレン基、エチレン基、プロパン−1,3−ジイル基、プロパン−1,2−ジイル基、ブタン−1,4−ジイル基、1−メチルプロパン−1,3−ジイル基、2−メチルプロパン−1,3−ジイル基、2−メチルプロパン−1,2−ジイル基等が挙げられる。
a42〜Aa44の脂肪族炭化水素基の置換基としては、ヒドロキシ基及び炭素数1〜6のアルコキシ基等が挙げられる。
sは、0であることが好ましい。
The aliphatic hydrocarbon group of A a42 to A a44 in the group (a-g1) is preferably a chain or cyclic aliphatic hydrocarbon group or a group formed by a combination thereof, and is carbon-carbon unsaturated. Although it may have a bond, a chain and a cyclic aliphatic saturated hydrocarbon group and a group formed by combining these are more preferable.
Specifically, methylene group, ethylene group, propane-1,3-diyl group, propane-1,2-diyl group, butane-1,4-diyl group, 1-methylpropane-1,3-diyl group, Examples include 2-methylpropane-1,3-diyl group and 2-methylpropane-1,2-diyl group.
Examples of the substituent for the aliphatic hydrocarbon group of A a42 to A a44 include a hydroxy group and an alkoxy group having 1 to 6 carbon atoms.
s is preferably 0.

a42が酸素原子、カルボニル基、カルボニルオキシ基又はオキシカルボニル基を表す基(a−g1)としては、以下の基等が挙げられる。以下の例示において、*及び**はそれぞれ結合手を表し、**が−O−CO−Ra42との結合手である。 Examples of the group (a-g1) in which X a42 represents an oxygen atom, a carbonyl group, a carbonyloxy group or an oxycarbonyl group include the following groups. In the following examples, * and ** each represent a bond, and ** is a bond with —O—CO—R a42 .

Figure 2017105770
Figure 2017105770

式(a4−1)で表される構造単位としては、式(a4−2)及び式(a4−3)で表される構造単位が好ましい。

Figure 2017105770
[式(a4−2)中、
f1は、水素原子又はメチル基を表す。
f1は、炭素数1〜6のアルカンジイル基を表す。
f2は、フッ素原子を有する炭素数1〜10の炭化水素基を表す。] As the structural unit represented by the formula (a4-1), structural units represented by the formula (a4-2) and the formula (a4-3) are preferable.
Figure 2017105770
[In the formula (a4-2),
R f1 represents a hydrogen atom or a methyl group.
A f1 represents an alkanediyl group having 1 to 6 carbon atoms.
R f2 represents a C 1-10 hydrocarbon group having a fluorine atom. ]

f1のアルカンジイル基としては、メチレン基、エチレン基、プロパン−1,3−ジイル基、プロパン−1,2−ジイル基、ブタン−1,4−ジイル基、ペンタン−1,5−ジイル基、ヘキサン−1,6−ジイル基等の直鎖状アルカンジイル基;1−メチルプロパン−1,3−ジイル基、2−メチルプロパン−1,3−ジイル基、2−メチルプロパン−1,2−ジイル基、1−メチルブタン−1,4−ジイル基、2−メチルブタン−1,4−ジイル基等の分岐状アルカンジイル基が挙げられる。 As the alkanediyl group of A f1 , a methylene group, an ethylene group, a propane-1,3-diyl group, a propane-1,2-diyl group, a butane-1,4-diyl group, a pentane-1,5-diyl group , A straight-chain alkanediyl group such as hexane-1,6-diyl group; 1-methylpropane-1,3-diyl group, 2-methylpropane-1,3-diyl group, 2-methylpropane-1,2 -Branched alkanediyl groups such as a diyl group, 1-methylbutane-1,4-diyl group, 2-methylbutane-1,4-diyl group.

f2の炭化水素基は、脂肪族炭化水素基及び芳香族炭化水素基を包含し、脂肪族炭化水素基は、鎖式、環式及びこれらの組合せることにより形成される基を含む。脂肪族炭化水素基としては、アルキル基、脂環式炭化水素基が好ましい。
アルキル基としては、メチル基、エチル基、n−プロピル基、イソプロピル基、n−ブチル基、sec−ブチル基、tert−ブチル基、n−ペンチル基、n−ヘキシル基、n−オクチル基及び2−エチルヘキシル基が挙げられる。
脂環式炭化水素基は、単環式であってもよいし、多環式であってもよい。単環式の脂環式炭化水素基としては、シクロプロピル基、シクロブチル基、シクロペンチル基、シクロヘキシル基、メチルシクロヘキシル基、ジメチルシクロヘキシル基、シクロヘプチル基、シクロオクチル基、シクロヘプチル基、シクロデシル基等のシクロアルキル基が挙げられる。多環式の脂環式炭化水素基としては、デカヒドロナフチル基、アダマンチル基、2−アルキルアダマンタン−2−イル基、1−(アダマンタン−1−イル)アルカン−1−イル基、ノルボルニル基、メチルノルボルニル基及びイソボルニル基が挙げられる。
The hydrocarbon group of R f2 includes an aliphatic hydrocarbon group and an aromatic hydrocarbon group, and the aliphatic hydrocarbon group includes a chain, a cyclic group, and a group formed by a combination thereof. As the aliphatic hydrocarbon group, an alkyl group and an alicyclic hydrocarbon group are preferable.
Examples of the alkyl group include methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, sec-butyl group, tert-butyl group, n-pentyl group, n-hexyl group, n-octyl group and 2 -An ethylhexyl group is mentioned.
The alicyclic hydrocarbon group may be monocyclic or polycyclic. Examples of the monocyclic alicyclic hydrocarbon group include cyclopropyl group, cyclobutyl group, cyclopentyl group, cyclohexyl group, methylcyclohexyl group, dimethylcyclohexyl group, cycloheptyl group, cyclooctyl group, cycloheptyl group, and cyclodecyl group. A cycloalkyl group is mentioned. Examples of the polycyclic alicyclic hydrocarbon group include decahydronaphthyl group, adamantyl group, 2-alkyladamantan-2-yl group, 1- (adamantan-1-yl) alkane-1-yl group, norbornyl group, A methyl norbornyl group and an isobornyl group are mentioned.

f2のフッ素原子を有する炭化水素基としては、フッ素原子を有するアルキル基、フッ素原子を有する脂環式炭化水素基等が挙げられる。
フッ素原子を有するアルキル基としては、ジフルオロメチル基、トリフルオロメチル基、1,1−ジフルオロエチル基、2,2−ジフルオロエチル基、2,2,2−トリフルオロエチル基、ペルフルオロエチル基、1,1,2,2−テトラフルオロプロピル基、1,1,2,2,3,3−ヘキサフルオロプロピル基、ペルフルオロエチルメチル基、1−(トリフルオロメチル)−1,2,2,2−テトラフルオロエチル基、ペルフルオロプロピル基、1,1,2,2−テトラフルオロブチル基、1,1,2,2,3,3−ヘキサフルオロブチル基、1,1,2,2,3,3,4,4−オクタフルオロブチル基、ペルフルオロブチル基、1,1−ビス(トリフルオロ)メチル−2,2,2−トリフルオロエチル基、2−(ペルフルオロプロピル)エチル基、1,1,2,2,3,3,4,4−オクタフルオロペンチル基、ペルフルオロペンチル基、1,1,2,2,3,3,4,4,5,5−デカフルオロペンチル基、1,1−ビス(トリフルオロメチル)−2,2,3,3,3−ペンタフルオロプロピル基、2−(ペルフルオロブチル)エチル基、1,1,2,2,3,3,4,4,5,5−デカフルオロヘキシル基、1,1,2,2,3,3,4,4,5,5,6,6−ドデカフルオロヘキシル基、ペルフルオロペンチルメチル基及びペルフルオロヘキシル基等のフッ化アルキル基が挙げられる。
フッ素原子を有する脂環式炭化水素基としては、ペルフルオロシクロヘキシル基、ペルフルオロアダマンチル基等のフッ化シクロアルキル基が挙げられる。
Examples of the hydrocarbon group having a fluorine atom for R f2 include an alkyl group having a fluorine atom and an alicyclic hydrocarbon group having a fluorine atom.
Examples of the alkyl group having a fluorine atom include a difluoromethyl group, a trifluoromethyl group, a 1,1-difluoroethyl group, a 2,2-difluoroethyl group, a 2,2,2-trifluoroethyl group, a perfluoroethyl group, 1 , 1,2,2-tetrafluoropropyl group, 1,1,2,2,3,3-hexafluoropropyl group, perfluoroethylmethyl group, 1- (trifluoromethyl) -1,2,2,2- Tetrafluoroethyl group, perfluoropropyl group, 1,1,2,2-tetrafluorobutyl group, 1,1,2,2,3,3-hexafluorobutyl group, 1,1,2,2,3,3 , 4,4-octafluorobutyl group, perfluorobutyl group, 1,1-bis (trifluoro) methyl-2,2,2-trifluoroethyl group, 2- (perfluoropropyl) Ethyl group, 1,1,2,2,3,3,4,4-octafluoropentyl group, perfluoropentyl group, 1,1,2,2,3,3,4,4,5,5-decafluoro Pentyl group, 1,1-bis (trifluoromethyl) -2,2,3,3,3-pentafluoropropyl group, 2- (perfluorobutyl) ethyl group, 1,1,2,2,3,3 4,4,5,5-decafluorohexyl group, 1,1,2,2,3,3,4,4,5,5,6,6-dodecafluorohexyl group, perfluoropentylmethyl group and perfluorohexyl group And a fluorinated alkyl group.
Examples of the alicyclic hydrocarbon group having a fluorine atom include fluorinated cycloalkyl groups such as a perfluorocyclohexyl group and a perfluoroadamantyl group.

式(a4−2)におけるAf1としては、炭素数2〜4のアルカンジイル基が好ましく、エチレン基がより好ましい。
f1としては、炭素数1〜6のフッ化アルキル基が好ましい。
As A f1 in Formula (a4-2), an alkanediyl group having 2 to 4 carbon atoms is preferable, and an ethylene group is more preferable.
R f1 is preferably a fluorinated alkyl group having 1 to 6 carbon atoms.

Figure 2017105770
[式(a4−3)中、
f11は、水素原子又はメチル基を表す。
f11は、炭素数1〜6のアルカンジイル基を表す。
f13は、フッ素原子を有していてもよい炭素数1〜18の脂肪族炭化水素基を表す。
f12は、カルボニルオキシ基又はオキシカルボニル基を表す。
f14は、フッ素原子を有していてもよい炭素数1〜17の脂肪族炭化水素基を表す。
ただし、Af13及びAf14の少なくとも1つは、フッ素原子を有する脂肪族炭化水素基を表す。]
Figure 2017105770
[In the formula (a4-3),
R f11 represents a hydrogen atom or a methyl group.
A f11 represents an alkanediyl group having 1 to 6 carbon atoms.
A f13 represents a C 1-18 aliphatic hydrocarbon group which may have a fluorine atom.
X f12 represents a carbonyloxy group or an oxycarbonyl group.
A f14 represents an aliphatic hydrocarbon group having 1 to 17 carbon atoms which may have a fluorine atom.
However, at least one of A f13 and A f14 represents an aliphatic hydrocarbon group having a fluorine atom. ]

f11のアルカンジイル基としては、Af1のアルカンジイル基と同様の基が挙げられる。
f13の脂肪族炭化水素基は、鎖式及び環式の脂肪族炭化水素基、並びに、これらを組合せることにより形成される2価の脂肪族炭化水素基が包含される。この脂肪族炭化水素は、炭素−炭素不飽和結合を有していてもよいが、好ましくは飽和の脂肪族炭化水素基である。
f13のフッ素原子を有していてもよい脂肪族炭化水素基としては、好ましくはフッ素原子を有していてもよい脂肪族飽和炭化水素基が挙げられ、より好ましくはペルフルオロアルカンジイル基が挙げられる。
フッ素原子を有していてもよい2価の鎖式の脂肪族炭化水素基としては、メチレン基、エチレン基、プロパンジイル基、ブタンジイル基及びペンタンジイル基等のアルカンジイル基;ジフルオロメチレン基、ペルフルオロエチレン基、ペルフルオロプロパンジイル基、ペルフルオロブタンジイル基及びペルフルオロペンタンジイル基等のペルフルオロアルカンジイル基等が挙げられる。
フッ素原子を有していてもよい2価の環式の脂肪族炭化水素基は、単環式及び多環式のいずれを含む基でもよい。単環式の脂肪族炭化水素基としては、シクロヘキサンジイル基及びペルフルオロシクロヘキサンジイル基等が挙げられる。多環式の2価の脂肪族炭化水素基としては、アダマンタンジイル基、ノルボルナンジイル基、ペルフルオロアダマンタンジイル基等が挙げられる。
Examples of the alkanediyl group of A f11 include the same groups as the alkanediyl group of A f1 .
The aliphatic hydrocarbon group for A f13 includes chain and cyclic aliphatic hydrocarbon groups, and divalent aliphatic hydrocarbon groups formed by combining them. The aliphatic hydrocarbon may have a carbon-carbon unsaturated bond, but is preferably a saturated aliphatic hydrocarbon group.
The aliphatic hydrocarbon group which may have a fluorine atom for A f13 preferably includes an aliphatic saturated hydrocarbon group which may have a fluorine atom, and more preferably a perfluoroalkanediyl group. It is done.
Examples of the divalent chain aliphatic hydrocarbon group which may have a fluorine atom include alkanediyl groups such as methylene group, ethylene group, propanediyl group, butanediyl group and pentanediyl group; difluoromethylene group, perfluoroethylene Groups, perfluoroalkanediyl groups such as perfluoropropanediyl group, perfluorobutanediyl group and perfluoropentanediyl group.
The divalent cyclic aliphatic hydrocarbon group which may have a fluorine atom may be a monocyclic or polycyclic group. Examples of the monocyclic aliphatic hydrocarbon group include a cyclohexanediyl group and a perfluorocyclohexanediyl group. Examples of the polycyclic divalent aliphatic hydrocarbon group include an adamantanediyl group, a norbornanediyl group, a perfluoroadamantanediyl group, and the like.

f14の脂肪族炭化水素基としては、鎖式及び環式のいずれか、並びに、これらが組合せることにより形成される脂肪族炭化水素基が包含される。この脂肪族炭化水素は、炭素−炭素不飽和結合を有していてもよいが、好ましくは飽和の脂肪族炭化水素基である。
f14のフッ素原子を有していてもよい脂肪族炭化水素基は、好ましくはフッ素原子を有していてもよい脂肪族飽和炭化水素基である。
フッ素原子を有していてもよい鎖式の脂肪族炭化水素基としては、トリフルオロメチル基、ジフルオロメチル基、メチル基、ペルフルオロエチル基、1,1,1−トリフルオロエチル基、1,1,2,2−テトラフルオロエチル基、エチル基、ペルフルオロプロピル基、1,1,1,2,2−ペンタフルオロプロピル基、プロピル基、ペルフルオロブチル基、1,1,2,2,3,3,4,4−オクタフルオロブチル基、ブチル基、ペルフルオロペンチル基、1,1,1,2,2,3,3,4,4−ノナフルオロペンチル基、ペンチル基、ヘキシル基、ペルフルオロヘキシル基、ヘプチル基、ペルフルオロヘプチル基、オクチル基及びペルフルオロオクチル基等が挙げられる。
フッ素原子を有していてもよい環式の脂肪族炭化水素基は、単環式及び多環式のいずれでもよい。単環式の脂肪族炭化水素基を含む基としては、シクロプロピルメチル基、シクロプロピル基、シクロブチルメチル基、シクロペンチル基、シクロヘキシル基、ペルフルオロシクロヘキシル基が挙げられる。多環式の脂肪族炭化水素基を含む基としては、アダマンチル基、アダマンチルメチル基、ノルボルニル基、ノルボルニルメチル基、ペルフルオロアダマンチル基、ペルフルオロアダマンチルメチル基等が挙げられる。
As the aliphatic hydrocarbon group for A f14 , one of a chain type and a cyclic type, and an aliphatic hydrocarbon group formed by combining them are included. The aliphatic hydrocarbon may have a carbon-carbon unsaturated bond, but is preferably a saturated aliphatic hydrocarbon group.
The aliphatic hydrocarbon group which may have a fluorine atom of A f14 is preferably an aliphatic saturated hydrocarbon group which may have a fluorine atom.
Examples of the chain aliphatic hydrocarbon group which may have a fluorine atom include a trifluoromethyl group, a difluoromethyl group, a methyl group, a perfluoroethyl group, a 1,1,1-trifluoroethyl group, 1,1 , 2,2-tetrafluoroethyl group, ethyl group, perfluoropropyl group, 1,1,1,2,2-pentafluoropropyl group, propyl group, perfluorobutyl group, 1,1,2,2,3,3 , 4,4-octafluorobutyl group, butyl group, perfluoropentyl group, 1,1,1,2,2,3,3,4,4-nonafluoropentyl group, pentyl group, hexyl group, perfluorohexyl group, A heptyl group, a perfluoro heptyl group, an octyl group, a perfluorooctyl group, etc. are mentioned.
The cyclic aliphatic hydrocarbon group which may have a fluorine atom may be monocyclic or polycyclic. Examples of the group containing a monocyclic aliphatic hydrocarbon group include a cyclopropylmethyl group, a cyclopropyl group, a cyclobutylmethyl group, a cyclopentyl group, a cyclohexyl group, and a perfluorocyclohexyl group. Examples of the group containing a polycyclic aliphatic hydrocarbon group include an adamantyl group, an adamantylmethyl group, a norbornyl group, a norbornylmethyl group, a perfluoroadamantyl group, and a perfluoroadamantylmethyl group.

式(a4−3)において、Af11は、エチレン基であることが好ましい。
f13の脂肪族炭化水素基は、炭素数1〜6の脂肪族炭化水素基であることが好ましく、炭素数2〜3の脂肪族炭化水素基であることがさらに好ましい。
f14の脂肪族炭化水素基としては、炭素数3〜12の脂肪族炭化水素基が好ましく、炭素数3〜10の脂肪族炭化水素基がさらに好ましい。なかでも、Af14は、好ましくは炭素数3〜12の脂環式炭化水素基を含む基であり、より好ましくはシクロプロピルメチル基、シクロペンチル基、シクロヘキシル基、ノルボルニル基及びアダマンチル基である。
In the formula (a4-3), A f11 is preferably an ethylene group.
The aliphatic hydrocarbon group for A f13 is preferably an aliphatic hydrocarbon group having 1 to 6 carbon atoms, and more preferably an aliphatic hydrocarbon group having 2 to 3 carbon atoms.
As the aliphatic hydrocarbon group for A f14, an aliphatic hydrocarbon group having 3 to 12 carbon atoms is preferable, and an aliphatic hydrocarbon group having 3 to 10 carbon atoms is more preferable. Among them, A f14 is preferably a group containing an alicyclic hydrocarbon group having 3 to 12 carbon atoms, and more preferably a cyclopropylmethyl group, a cyclopentyl group, a cyclohexyl group, a norbornyl group, and an adamantyl group.

式(a4−2)で表される構造単位としては、以下に示す構造単位及び下記構造単位中のRf1に相当するメチル基が水素原子に置き換わった構成単位が挙げられる。

Figure 2017105770
Examples of the structural unit represented by the formula (a4-2) include structural units shown below and structural units in which a methyl group corresponding to R f1 in the following structural units is replaced with a hydrogen atom.
Figure 2017105770

式(a4−3)で表される構造単位としては、以下に示す構造単位及び下記構造単位中のRf11に相当するメチル基が水素原子に置き換わった構造単位が挙げられる。

Figure 2017105770
The structural unit represented by formula (a4-3), a methyl group have structural units replaced by a hydrogen atom corresponding to R f11 in the structural unit and the following structural units shown below.
Figure 2017105770

Figure 2017105770
Figure 2017105770

構造単位(a4)としては、式(a4−4)で表される構造単位も挙げられる。

Figure 2017105770
[式(a4−4)中、
f21は、水素原子又はメチル基を表す。
f21は、−(CHj1−、−(CHj2−O−(CHj3−又は−(CHj4−CO−O−(CHj5−を表す。
j1〜j5は、互いに独立に、1〜6の整数を表す。
f22は、フッ素原子を有する炭素数1〜10の炭化水素基を表す。] Examples of the structural unit (a4) include a structural unit represented by the formula (a4-4).
Figure 2017105770
[In the formula (a4-4),
R f21 represents a hydrogen atom or a methyl group.
A f21 is, - (CH 2) j1 - , - (CH 2) j2 -O- (CH 2) j3 - or - (CH 2) j4 -CO- O- (CH 2) j5 - represents a.
j1 to j5 each independently represent an integer of 1 to 6.
R f22 represents a C 1-10 hydrocarbon group having a fluorine atom. ]

f22のフッ素原子を有する炭化水素基としては、式(a4−2)におけるRf2の炭化水素基と同じものが挙げられる。Rf22は、フッ素原子を有する炭素数1〜10のアルキル基又はフッ素原子を有する炭素数1〜10の脂環式炭化水素基であることが好ましく、フッ素原子を有する炭素数1〜10のアルキル基であることがより好ましく、フッ素原子を有する炭素数1〜6のアルキル基であることがさらに好ましい。 Examples of the hydrocarbon group having a fluorine atom of R f22 include the same hydrocarbon groups as R f2 in formula (a4-2). R f22 is preferably a C 1-10 alkyl group having a fluorine atom or a C 1-10 alicyclic hydrocarbon group having a fluorine atom, and a C 1-10 alkyl having a fluorine atom. It is more preferably a group, more preferably a C 1-6 alkyl group having a fluorine atom.

式(a4−4)においては、Af21としては、−(CHj1−が好ましく、エチレン基又はメチレン基がより好ましく、メチレン基がさらに好ましい。 In Formula (a4-4), as A f21 , — (CH 2 ) j1 — is preferable, an ethylene group or a methylene group is more preferable, and a methylene group is further preferable.

式(a4−4)で表される構造単位としては、例えば、以下の構造単位及び以下の式で表される構造単位においてはRf21に相当するメチル基が水素原子に置き換わった構造単位が挙げられる。

Figure 2017105770
Examples of the structural unit represented by formula (a4-4) include structural units in which the methyl group corresponding to R f21 is replaced with a hydrogen atom in the following structural units and structural units represented by the following formulas. It is done.
Figure 2017105770

<構造単位(a5)>
構造単位(a5)が有する非脱離炭化水素基としては、直鎖、分岐又は環状の炭化水素基が挙げられる。なかでも、構造単位(a5)は、脂環式炭化水素基を含むことが好ましい。
構造単位(a5)としては、例えば、式(a5−1)で表される構造単位が挙げられる。

Figure 2017105770
[式(a5−1)中、
51は、水素原子又はメチル基を表す。
52は、炭素数3〜18の脂環式炭化水素基を表し、該脂環式炭化水素基に含まれる水素原子は炭素数1〜8の脂肪族炭化水素基又はヒドロキシ基で置換されていてもよい。ただし、L51との結合位置にある炭素原子に結合する水素原子は、炭素数1〜8の脂肪族炭化水素基で置換されない。
51は、単結合又は炭素数1〜18の2価の飽和炭化水素基を表し、該飽和炭化水素基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよい。] <Structural unit (a5)>
Examples of the non-leaving hydrocarbon group that the structural unit (a5) has include a linear, branched, or cyclic hydrocarbon group. Especially, it is preferable that a structural unit (a5) contains an alicyclic hydrocarbon group.
As a structural unit (a5), the structural unit represented by a formula (a5-1) is mentioned, for example.
Figure 2017105770
[In the formula (a5-1),
R 51 represents a hydrogen atom or a methyl group.
R 52 represents an alicyclic hydrocarbon group having 3 to 18 carbon atoms, and a hydrogen atom contained in the alicyclic hydrocarbon group is substituted with an aliphatic hydrocarbon group or hydroxy group having 1 to 8 carbon atoms. May be. However, the hydrogen atom bonded to the carbon atom at the coupling position with the L 51 is not substituted with an aliphatic hydrocarbon group having 1 to 8 carbon atoms.
L 51 represents a single bond or a divalent saturated hydrocarbon group having 1 to 18 carbon atoms, and the methylene group contained in the saturated hydrocarbon group may be replaced with an oxygen atom or a carbonyl group. ]

52の脂環式炭化水素基は、単環式及び多環式のいずれでもよい。単環式の脂環式炭化水素基としては、例えば、シクロプロピル基、シクロブチル基、シクロペンチル基及びシクロヘキシル基が挙げられる。多環式の脂環式炭化水素基としては、例えば、アダマンチル基及びノルボルニル基等が挙げられる。
炭素数1〜8の脂肪族炭化水素基は、例えば、メチル基、エチル基、n−プロピル基、イソプロピル基、n−ブチル基、sec−ブチル基、tert−ブチル基、ペンチル基、ヘキシル基、オクチル基及び2−エチルヘキシル基等のアルキル基が挙げられる。
置換基を有した脂環式炭化水素基としては、3−ヒドロキシアダマンチル基、3−メチルアダマンチル基などが挙げられる。
52は、好ましくは無置換の炭素数3〜18の脂環式炭化水素基であり、より好ましくはアダマンチル基、ノルボルニル基又はシクロヘキシル基である。
The alicyclic hydrocarbon group for R 52 may be either monocyclic or polycyclic. Examples of the monocyclic alicyclic hydrocarbon group include a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, and a cyclohexyl group. Examples of the polycyclic alicyclic hydrocarbon group include an adamantyl group and a norbornyl group.
Examples of the aliphatic hydrocarbon group having 1 to 8 carbon atoms include methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, sec-butyl group, tert-butyl group, pentyl group, hexyl group, Examples thereof include alkyl groups such as octyl group and 2-ethylhexyl group.
Examples of the alicyclic hydrocarbon group having a substituent include a 3-hydroxyadamantyl group and a 3-methyladamantyl group.
R 52 is preferably an unsubstituted alicyclic hydrocarbon group having 3 to 18 carbon atoms, more preferably an adamantyl group, a norbornyl group, or a cyclohexyl group.

51の2価の飽和炭化水素基としては、2価の脂肪族飽和炭化水素基及び2価の脂環式飽和炭化水素基が挙げられ、好ましくは2価の脂肪族飽和炭化水素基が挙げられる。
2価の脂肪族飽和炭化水素基としては、例えば、メチレン基、エチレン基、プロパンジイル基、ブタンジイル基及びペンタンジイル基等のアルカンジイル基が挙げられる。
2価の脂環式飽和炭化水素基は、単環式及び多環式のいずれでもよい。単環式の脂環式飽和炭化水素基としては、シクロペンタンジイル基及びシクロヘキサンジイル基等のシクロアルカンジイル基が挙げられる。多環式の2価の脂環式飽和炭化水素基としては、アダマンタンジイル基及びノルボルナンジイル基等が挙げられる。
Examples of the divalent saturated hydrocarbon group for L 51 include a divalent aliphatic saturated hydrocarbon group and a divalent alicyclic saturated hydrocarbon group, preferably a divalent aliphatic saturated hydrocarbon group. It is done.
Examples of the divalent aliphatic saturated hydrocarbon group include alkanediyl groups such as a methylene group, an ethylene group, a propanediyl group, a butanediyl group, and a pentanediyl group.
The divalent alicyclic saturated hydrocarbon group may be monocyclic or polycyclic. Examples of the monocyclic alicyclic saturated hydrocarbon group include cycloalkanediyl groups such as cyclopentanediyl group and cyclohexanediyl group. Examples of the polycyclic divalent alicyclic saturated hydrocarbon group include an adamantanediyl group and a norbornanediyl group.

飽和炭化水素基に含まれるメチレン基が、酸素原子又はカルボニル基で置き換わった基としては、例えば、式(L1−1)〜式(L1−4)で表される基が挙げられる。下記式中、*は酸素原子との結合手を表す。

Figure 2017105770
[式(L1−1)中、
x1は、カルボニルオキシ基又はオキシカルボニル基を表す。
x1は、炭素数1〜16の2価の脂肪族飽和炭化水素基を表す。
x2は、単結合又は炭素数1〜15の2価の脂肪族飽和炭化水素基を表す。
ただし、Lx1及びLx2の合計炭素数は、16以下である。
式(L1−2)中、
x3は、炭素数1〜17の2価の脂肪族飽和炭化水素基を表す。
x4は、単結合又は炭素数1〜16の2価の脂肪族飽和炭化水素基を表す。
ただし、Lx3及びLx4の合計炭素数は、17以下である。
式(L1−3)中、
x5は、炭素数1〜15の2価の脂肪族飽和炭化水素基を表す。
x6及びLx7は、互いに独立に、単結合又は炭素数1〜14の2価の脂肪族飽和炭化水素基を表す。
ただし、Lx5〜Lx7の合計炭素数は、15以下である。
式(L1−4)中、
x8及びLx9は、互いに独立に、単結合又は炭素数1〜12の2価の脂肪族飽和炭化水素基を表す。
x1は、炭素数3〜15の2価の脂環式飽和炭化水素基を表す。
ただし、Lx8、Lx9及びWx1の合計炭素数は、15以下である。] Examples of the group in which the methylene group contained in the saturated hydrocarbon group is replaced with an oxygen atom or a carbonyl group include groups represented by formulas (L1-1) to (L1-4). In the following formula, * represents a bond with an oxygen atom.
Figure 2017105770
[In the formula (L1-1),
X x1 represents a carbonyloxy group or an oxycarbonyl group.
L x1 represents a divalent aliphatic saturated hydrocarbon group having 1 to 16 carbon atoms.
L x2 represents a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 15 carbon atoms.
However, the total carbon number of L x1 and L x2 is 16 or less.
In formula (L1-2),
L x3 represents a divalent aliphatic saturated hydrocarbon group having 1 to 17 carbon atoms.
L x4 represents a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 16 carbon atoms.
However, the total carbon number of L x3 and L x4 is 17 or less.
In formula (L1-3),
L x5 represents a divalent aliphatic saturated hydrocarbon group having 1 to 15 carbon atoms.
L x6 and L x7 each independently represent a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 14 carbon atoms.
However, the total carbon number of L x5 to L x7 is 15 or less.
In formula (L1-4),
L x8 and L x9 each independently represent a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 12 carbon atoms.
W x1 represents a divalent alicyclic saturated hydrocarbon group having 3 to 15 carbon atoms.
However, the total number of carbon atoms of L x8 , L x9 and W x1 is 15 or less. ]

x1は、好ましくは炭素数1〜8の2価の脂肪族飽和炭化水素基であり、より好ましくはメチレン基又はエチレン基である。
x2は、好ましくは単結合又は炭素数1〜8の2価の脂肪族飽和炭化水素基であり、より好ましくは単結合である。
x3は、好ましくは炭素数1〜8の2価の脂肪族飽和炭化水素基である。
x4は、好ましくは単結合又は炭素数1〜8の2価の脂肪族飽和炭化水素基である。
x5は、好ましくは炭素数1〜8の2価の脂肪族飽和炭化水素基であり、より好ましくはメチレン基又はエチレン基である。
x6は、好ましくは単結合又は炭素数1〜8の2価の脂肪族飽和炭化水素基であり、より好ましくはメチレン基又はエチレン基である。
x7は、好ましくは単結合又は炭素数1〜8の2価の脂肪族飽和炭化水素基である。
x8は、好ましくは単結合又は炭素数1〜8の2価の脂肪族飽和炭化水素基であり、より好ましくは単結合又はメチレン基である。
x9は、好ましくは単結合又は炭素数1〜8の2価の脂肪族飽和炭化水素基であり、より好ましくは単結合又はメチレン基である。
x1は、好ましくは炭素数3〜10の2価の脂環式飽和炭化水素基であり、より好ましくはシクロヘキサンジイル基又はアダマンタンジイル基である。
L x1 is preferably a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms, more preferably a methylene group or an ethylene group.
L x2 is preferably a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms, and more preferably a single bond.
L x3 is preferably a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms.
L x4 is preferably a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms.
L x5 is preferably a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms, more preferably a methylene group or an ethylene group.
L x6 is preferably a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms, more preferably a methylene group or an ethylene group.
L x7 is preferably a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms.
L x8 is preferably a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms, and more preferably a single bond or a methylene group.
L x9 is preferably a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms, and more preferably a single bond or a methylene group.
W x1 is preferably a divalent alicyclic saturated hydrocarbon group having 3 to 10 carbon atoms, and more preferably a cyclohexanediyl group or an adamantanediyl group.

式(L1−1)で表される基としては、例えば、以下に示す2価の基が挙げられる。

Figure 2017105770
As group represented by a formula (L1-1), the bivalent group shown below is mentioned, for example.
Figure 2017105770

式(L1−2)で表される基としては、例えば、以下に示す2価の基が挙げられる。

Figure 2017105770
As group represented by a formula (L1-2), the bivalent group shown below is mentioned, for example.
Figure 2017105770

式(L1−3)で表される基としては、例えば、以下に示す2価の基が挙げられる。

Figure 2017105770
As group represented by a formula (L1-3), the bivalent group shown below is mentioned, for example.
Figure 2017105770

式(L1−4)で表される基としては、例えば、以下に示す2価の基が挙げられる。

Figure 2017105770
As group represented by a formula (L1-4), the bivalent group shown below is mentioned, for example.
Figure 2017105770

51は、好ましくは単結合又は式(L1−1)で表される基である。 L 51 is preferably a single bond or a group represented by the formula (L1-1).

構造単位(a5−1)としては、以下に示す構造単位及び下記構造単位中のR51に相当するメチル基が水素原子に置き換わった構造単位等が挙げられる。

Figure 2017105770
Examples of the structural unit (a5-1) include the following structural units and structural units in which a methyl group corresponding to R 51 in the following structural units is replaced with a hydrogen atom.
Figure 2017105770

樹脂(X)が、構造単位(I)と構造単位(a4)からなる場合、構造単位(a4)の含有率は、樹脂(X)の全構造単位に対して、90〜99モル%が好ましく、92〜98モル%がより好ましく、94〜98モル%がさらに好ましい。
樹脂(X)が、構造単位(a5)を有する場合、その含有率は、樹脂(X)の全構造単位の合計に対して、1〜90モル%であることが好ましく、2〜80モル%であることがより好ましく、3〜70モル%であることがさらに好ましい。
樹脂(X)が、構造単位(a5)を有する場合、構造単位(a4)の含有率は、樹脂(X)の全構造単位の合計に対して、1〜90モル%であることが好ましく、2〜80モル%であることがより好ましく、3〜70モル%であることがさらに好ましい。
樹脂(X)が、構造単位(a5)を有する場合、構造単位(a4)及び構造単位(a5)の合計含有率は、樹脂(X)の全構造単位に対して、90〜99モル%が好ましく、92〜98モル%がより好ましく、94〜98モル%がさらに好ましい。
When the resin (X) is composed of the structural unit (I) and the structural unit (a4), the content of the structural unit (a4) is preferably 90 to 99 mol% with respect to all the structural units of the resin (X). 92-98 mol% is more preferable, and 94-98 mol% is further more preferable.
When resin (X) has a structural unit (a5), it is preferable that the content rate is 1-90 mol% with respect to the sum total of all the structural units of resin (X), and 2-80 mol% It is more preferable that it is 3-70 mol%.
When the resin (X) has the structural unit (a5), the content of the structural unit (a4) is preferably 1 to 90 mol% with respect to the total of all the structural units of the resin (X). More preferably, it is 2-80 mol%, and it is further more preferable that it is 3-70 mol%.
When the resin (X) has the structural unit (a5), the total content of the structural unit (a4) and the structural unit (a5) is 90 to 99 mol% with respect to all the structural units of the resin (X). Preferably, 92 to 98 mol% is more preferable, and 94 to 98 mol% is more preferable.

樹脂(X)を構成する各構造単位は、2種以上を組み合わせてもよく、これら構造単位を誘導するモノマーを用いて、公知の重合法(例えばラジカル重合法)によって製造することができる。樹脂(X)が有する各構造単位の含有率は、重合に用いるモノマーの使用量で調整できる。
なお、樹脂(X)において、式(I)で表される化合物由来の構造単位は、一方の重合性基のみ重合する構造単位と双方の重合性基が重合する構造単位とが混在していてもよい。
樹脂(X)の重量平均分子量は、好ましくは、6,000以上(より好ましくは7,000以上)、80,000以下(より好ましくは60,000以下)である。重量平均分子量は、ゲルパーミエーションクロマトグラフィー分析により、標準ポリスチレン基準の換算値として求められるものであり、該分析の詳細な分析条件は、本願の実施例で詳述する。
Each structural unit constituting the resin (X) may be a combination of two or more, and can be produced by a known polymerization method (for example, radical polymerization method) using a monomer that derives these structural units. The content rate of each structural unit which resin (X) has can be adjusted with the usage-amount of the monomer used for superposition | polymerization.
In addition, in the resin (X), the structural unit derived from the compound represented by the formula (I) is a mixture of a structural unit in which only one polymerizable group is polymerized and a structural unit in which both polymerizable groups are polymerized. Also good.
The weight average molecular weight of the resin (X) is preferably 6,000 or more (more preferably 7,000 or more) and 80,000 or less (more preferably 60,000 or less). A weight average molecular weight is calculated | required as a conversion value of a standard polystyrene reference | standard by gel permeation chromatography analysis, and the detailed analysis conditions of this analysis are explained in full detail in the Example of this application.

<レジスト組成物>
本発明のレジスト組成物は、樹脂(X)、酸不安定基を有する構造単位を有する樹脂(以下「樹脂(A)」という場合がある。)及び酸発生剤(以下「酸発生剤(B)」という場合がある。)を含有する。
また、レジスト組成物は、クエンチャー(以下「クエンチャー(C)」という場合がある)及び/又は溶剤(以下「溶剤(E)」という場合がある)を含有することが好ましい。
<Resist composition>
The resist composition of the present invention comprises a resin (X), a resin having a structural unit having an acid labile group (hereinafter sometimes referred to as “resin (A)”) and an acid generator (hereinafter referred to as “acid generator (B)”. ) ”In some cases.
The resist composition preferably contains a quencher (hereinafter sometimes referred to as “quencher (C)”) and / or a solvent (hereinafter sometimes referred to as “solvent (E)”).

〈樹脂(A)〉
樹脂(A)は、酸不安定基を有する構造単位(以下「構造単位(a1)」という場合がある)を有する。樹脂(A)は、さらに、構造単位(a1)以外の構造単位を含んでいることが好ましい。構造単位(a1)以外の構造単位としては、酸不安定基を有さない構造単位(以下「構造単位(s)」という場合がある)、その他の構造単位(以下「構造単位(t)」という場合がある)及びその他の公知のモノマーに由来する構造単位等が挙げられる。
<Resin (A)>
The resin (A) has a structural unit having an acid labile group (hereinafter sometimes referred to as “structural unit (a1)”). The resin (A) preferably further contains a structural unit other than the structural unit (a1). As the structural unit other than the structural unit (a1), a structural unit having no acid labile group (hereinafter sometimes referred to as “structural unit (s)”), other structural unit (hereinafter referred to as “structural unit (t)”). And structural units derived from other known monomers.

<構造単位(a1)>
構造単位(a1)は、酸不安定基を有するモノマー(以下「モノマー(a1)」という場合がある)から導かれる。
ここでの「酸不安定基」は、脱離基を有し、酸との接触により脱離基が脱離して、親水性基(例えば、ヒドロキシ基又はカルボキシ基)を形成する基を意味する。樹脂(A)においては、構造単位(a1)に含まれる酸不安定基としては、下記の基(1)及び/又は基(2)が好ましい。

Figure 2017105770
[式(1)中、Ra1〜Ra3は、それぞれ独立に、炭素数1〜8のアルキル基、炭素数3〜20の脂環式炭化水素基又はこれらを組み合わせた基を表すか、Ra1及びRa2は互いに結合してそれらが結合する炭素原子とともに炭素数3〜20の2価の脂環式炭化水素基を形成する。
naは、0又は1を表す。
*は結合手を表す。]
Figure 2017105770
[式(2)中、Ra1’及びRa2’は、それぞれ独立に、水素原子又は炭素数1〜12の炭化水素基を表し、Ra3’は、炭素数1〜20の炭化水素基を表すか、Ra2’及びRa3’は互いに結合してそれらが結合する炭素原子及びXとともに炭素数3〜20の2価の複素環基を形成し、該炭化水素基及び該2価の複素環基に含まれる−CH2−は、−O−又は−S−で置き換わってもよい。
Xは、酸素原子又は硫黄原子を表す。
*は結合手を表す。] <Structural unit (a1)>
The structural unit (a1) is derived from a monomer having an acid labile group (hereinafter sometimes referred to as “monomer (a1)”).
The term “acid labile group” as used herein means a group having a leaving group and forming a hydrophilic group (for example, a hydroxy group or a carboxy group) by leaving the leaving group upon contact with an acid. . In the resin (A), the acid labile group contained in the structural unit (a1) is preferably the following group (1) and / or group (2).
Figure 2017105770
[In the formula (1), R a1 to R a3 each independently represents an alkyl group having 1 to 8 carbon atoms, an alicyclic hydrocarbon group having 3 to 20 carbon atoms, or a combination of these, or R a1 and R a2 are bonded to each other to form a divalent alicyclic hydrocarbon group having 3 to 20 carbon atoms together with the carbon atom to which they are bonded.
na represents 0 or 1.
* Represents a bond. ]
Figure 2017105770
[In Formula (2), R a1 ′ and R a2 ′ each independently represent a hydrogen atom or a hydrocarbon group having 1 to 12 carbon atoms, and R a3 ′ represents a hydrocarbon group having 1 to 20 carbon atoms. R a2 ′ and R a3 ′ are bonded to each other to form a divalent heterocyclic group having 3 to 20 carbon atoms together with the carbon atom to which they are bonded and X, and the hydrocarbon group and the divalent —CH 2 — contained in the ring group may be replaced by —O— or —S—.
X represents an oxygen atom or a sulfur atom.
* Represents a bond. ]

a1〜Ra3のアルキル基としては、メチル基、エチル基、プロピル基、n−ブチル基、n−ペンチル基、n−ヘキシル基、n−ヘプチル基、n−オクチル基等が挙げられる。
a1〜Ra3の脂環式炭化水素基としては、単環式及び多環式のいずれでもよい。単環式の脂環式炭化水素基としては、例えば、シクロペンチル基、シクロへキシル基、シクロヘプチル基、シクロオクチル基等のシクロアルキル基が挙げられる。多環式の脂環式炭化水素基としては、例えば、デカヒドロナフチル基、アダマンチル基、ノルボルニル基及び下記の基(*は結合手を表す。)等が挙げられる。Ra1〜Ra3の脂環式炭化水素基は、好ましくは炭素数3〜16である。

Figure 2017105770
アルキル基と脂環式炭化水素基とを組み合わせた基としては、例えば、メチルシクロヘキシル基、ジメチルシクロへキシル基、メチルノルボルニル基、メチルアダマンチル基、シクロヘキシルメチル基、メチルシクロヘキシルメチル基、アダマンチルメチル基、ノルボルニルメチル基等が挙げられる。
naは、好ましくは0である。 Examples of the alkyl group represented by R a1 to R a3 include a methyl group, an ethyl group, a propyl group, an n-butyl group, an n-pentyl group, an n-hexyl group, an n-heptyl group, and an n-octyl group.
The alicyclic hydrocarbon group for R a1 to R a3 may be monocyclic or polycyclic. Examples of the monocyclic alicyclic hydrocarbon group include cycloalkyl groups such as a cyclopentyl group, a cyclohexyl group, a cycloheptyl group, and a cyclooctyl group. Examples of the polycyclic alicyclic hydrocarbon group include a decahydronaphthyl group, an adamantyl group, a norbornyl group, and the following group (* represents a bond). The alicyclic hydrocarbon group of R a1 to R a3 preferably has 3 to 16 carbon atoms.
Figure 2017105770
Examples of the group in which an alkyl group and an alicyclic hydrocarbon group are combined include, for example, methylcyclohexyl group, dimethylcyclohexyl group, methylnorbornyl group, methyladamantyl group, cyclohexylmethyl group, methylcyclohexylmethyl group, and adamantylmethyl. Group, norbornylmethyl group and the like.
na is preferably 0.

a1及びRa2が互いに結合して2価の脂環式炭化水素基を形成する場合の−C(Ra1)(Ra2)(Ra3)としては、例えば、下記の基が挙げられる。2価の脂環式炭化水素基は、好ましくは炭素数3〜12の脂環式炭化水素基である。*は−O−との結合手を表す。

Figure 2017105770
Examples of —C (R a1 ) (R a2 ) (R a3 ) when R a1 and R a2 are bonded to each other to form a divalent alicyclic hydrocarbon group include the following groups. The divalent alicyclic hydrocarbon group is preferably an alicyclic hydrocarbon group having 3 to 12 carbon atoms. * Represents a bond with -O-.
Figure 2017105770

a1'〜Ra3'の炭化水素基としては、例えば、アルキル基、脂環式炭化水素基、芳香族炭化水素基及びこれらを組み合わせることにより形成される基等が挙げられる。
アルキル基及び脂環式炭化水素基は、上記と同様のものが挙げられる。
芳香族炭化水素基としては、フェニル基、ナフチル基、アントリル基、p−メチルフェニル基、p−tert−ブチルフェニル基、p−アダマンチルフェニル基、トリル基、キシリル基、クメニル基、メシチル基、ビフェニル基、フェナントリル基、2,6−ジエチルフェニル基、2−メチル−6−エチルフェニル等のアリール基等が挙げられる。
a2'及びRa3'が互いに結合してそれらが結合する炭素原子及びXとともに形成する2価の複素環基としては、下記の基が挙げられる。*は、結合手を表す。

Figure 2017105770
Examples of the hydrocarbon group of R a1 ′ to R a3 ′ include an alkyl group, an alicyclic hydrocarbon group, an aromatic hydrocarbon group, and a group formed by combining these.
Examples of the alkyl group and alicyclic hydrocarbon group are the same as those described above.
Aromatic hydrocarbon groups include phenyl, naphthyl, anthryl, p-methylphenyl, p-tert-butylphenyl, p-adamantylphenyl, tolyl, xylyl, cumenyl, mesityl, biphenyl Groups, phenanthryl groups, 2,6-diethylphenyl groups, aryl groups such as 2-methyl-6-ethylphenyl, and the like.
Examples of the divalent heterocyclic group formed together with the carbon atom and X to which R a2 ′ and R a3 ′ are bonded to each other and X include the following groups. * Represents a bond.
Figure 2017105770

式(1)で表される基としては、例えば、1,1−ジアルキルアルコキシカルボニル基(式(1)中においてRa1〜Ra3がアルキル基である基、好ましくはtert−ブトキシカルボニル基)、2−アルキルアダマンタン−2−イルオキシカルボニル基(式(1)中、Ra1、Ra2及びこれらが結合する炭素原子がアダマンチル基を形成し、Ra3がアルキル基である基)及び1−(アダマンタン−1−イル)−1−アルキルアルコキシカルボニル基(式(1)中、Ra1及びRa2がアルキル基であり、Ra3がアダマンチル基である基)等が挙げられる。
a1'及びRa2'のうち、少なくとも1つは水素原子であることが好ましい。
Examples of the group represented by the formula (1) include a 1,1-dialkylalkoxycarbonyl group (a group in which R a1 to R a3 are alkyl groups in the formula (1), preferably a tert-butoxycarbonyl group), 2-alkyladamantan-2-yloxycarbonyl group (in the formula (1), R a1 , R a2 and the carbon atom to which they are bonded form an adamantyl group, and R a3 is an alkyl group) and 1- ( And adamantane-1-yl) -1-alkylalkoxycarbonyl group (in the formula (1), R a1 and R a2 are alkyl groups, and R a3 is an adamantyl group).
At least one of R a1 ′ and R a2 ′ is preferably a hydrogen atom.

式(2)で表される基の具体例としては、以下の基が挙げられる。*は結合手を表す。

Figure 2017105770
Specific examples of the group represented by the formula (2) include the following groups. * Represents a bond.
Figure 2017105770

モノマー(a1)は、好ましくは、酸不安定基とエチレン性不飽和結合とを有するモノマー、より好ましくは酸不安定基を有する(メタ)アクリル系モノマーである。   The monomer (a1) is preferably a monomer having an acid labile group and an ethylenically unsaturated bond, more preferably a (meth) acrylic monomer having an acid labile group.

酸不安定基を有する(メタ)アクリル系モノマーのうち、好ましくは、炭素数5〜20の脂環式炭化水素基を有するものが挙げられる。脂環式炭化水素基のような嵩高い構造を有するモノマー(a1)に由来する構造単位を有する樹脂(A)をレジスト組成物に使用すれば、レジストパターンの解像度を向上させることができる。   Among the (meth) acrylic monomers having an acid labile group, those having an alicyclic hydrocarbon group having 5 to 20 carbon atoms are preferable. If the resin (A) having a structural unit derived from the monomer (a1) having a bulky structure such as an alicyclic hydrocarbon group is used in the resist composition, the resolution of the resist pattern can be improved.

樹脂(A)において、構造単位(a1)の含有率は、樹脂(A)の全構造単位に対して、好ましくは30〜90モル%であり、より好ましくは35〜85モル%であり、さらに好ましくは40〜80モル%である。   In the resin (A), the content of the structural unit (a1) is preferably 30 to 90 mol%, more preferably 35 to 85 mol%, based on all the structural units of the resin (A). Preferably it is 40-80 mol%.

式(1)で表される基を有する(メタ)アクリル系モノマーに由来する構造単位として、好ましくは、式(a1−0)で表される構造単位、式(a1−1)で表される構造単位又は式(a1−2)で表される構造単位が挙げられる。これらは単独で使用してもよく、2種以上を併用してもよい。本明細書では、式(a1−0)で表される構造単位、式(a1−1)で表される構造単位及び式(a1−2)で表される構造単位を、それぞれ構造単位(a1−0)、構造単位(a1−1)及び構造単位(a1−2)と、構造単位(a1−0)を誘導するモノマー、構造単位(a1−1)を誘導するモノマー及び構造単位(a1−2)を誘導するモノマーを、それぞれモノマー(a1−0)、モノマー(a1−1)及びモノマー(a1−2)という場合がある。   As a structural unit derived from a (meth) acrylic monomer having a group represented by the formula (1), a structural unit represented by the formula (a1-0) is preferably represented by the formula (a1-1). The structural unit represented by a structural unit or a formula (a1-2) is mentioned. These may be used alone or in combination of two or more. In this specification, the structural unit represented by formula (a1-0), the structural unit represented by formula (a1-1), and the structural unit represented by formula (a1-2) are each represented by structural unit (a1). -0), structural unit (a1-1) and structural unit (a1-2), a monomer for deriving structural unit (a1-0), a monomer for deriving structural unit (a1-1), and a structural unit (a1- The monomer that induces 2) may be referred to as monomer (a1-0), monomer (a1-1), and monomer (a1-2), respectively.

Figure 2017105770
[式(a1−0)中、
a01は、酸素原子又は−O−(CH2k01−CO−O−を表し、k01は1〜7の整数を表し、*はカルボニル基との結合手を表す。
a01は、水素原子又はメチル基を表す。
a02、Ra03及びRa04は、それぞれ独立に、炭素数1〜8のアルキル基、炭素数3〜18の脂環式炭化水素基又はこれらを組み合わせた基を表す。]
Figure 2017105770
[In the formula (a1-0),
L a01 represents an oxygen atom or * —O— (CH 2 ) k01 —CO—O—, k01 represents an integer of 1 to 7, and * represents a bond to a carbonyl group.
R a01 represents a hydrogen atom or a methyl group.
R a02 , R a03 and R a04 each independently represent an alkyl group having 1 to 8 carbon atoms, an alicyclic hydrocarbon group having 3 to 18 carbon atoms, or a combination thereof. ]

Figure 2017105770
[式(a1−1)及び式(a1−2)中、
a1及びLa2は、それぞれ独立に、−O−又は−O−(CH2k1−CO−O−を表し、k1は1〜7の整数を表し、*は−CO−との結合手を表す。
a4及びRa5は、それぞれ独立に、水素原子又はメチル基を表す。
a6及びRa7は、それぞれ独立に、炭素数1〜8のアルキル基、炭素数3〜18の脂環式炭化水素基又はこれらを組み合わせることにより形成される基を表す。
m1は0〜14の整数を表す。
n1は0〜10の整数を表す。
n1’は0〜3の整数を表す。]
Figure 2017105770
[In Formula (a1-1) and Formula (a1-2),
L a1 and L a2 each independently represent —O— or * —O— (CH 2 ) k1 —CO—O—, k1 represents an integer of 1 to 7, and * represents a bond to —CO—. Represents a hand.
R a4 and R a5 each independently represent a hydrogen atom or a methyl group.
R a6 and R a7 each independently represent an alkyl group having 1 to 8 carbon atoms, an alicyclic hydrocarbon group having 3 to 18 carbon atoms, or a group formed by combining these.
m1 represents the integer of 0-14.
n1 represents an integer of 0 to 10.
n1 ′ represents an integer of 0 to 3. ]

a01は、好ましくは、酸素原子又は−O−(CH2k01−CO−O−であり(但しk01は、好ましくは1〜4の整数、より好ましくは1である。)、より好ましくは酸素原子である。
a02、Ra03及びRa04のアルキル基、脂環式炭化水素基及びこれらを組み合わせた基としては、式(1)のRa1〜Ra3で挙げた基と同様の基が挙げられる。
a02、Ra03及びRa04のアルキル基は、好ましくは炭素数6以下である。
a02、Ra03及びRa04の脂環式炭化水素基は、好ましくは炭素数8以下、より好ましくは6以下である。
アルキル基と脂環式炭化水素基とを組み合わせた基は、これらアルキル基と脂環式炭化水素基とを組み合わせた合計炭素数が、18以下であることが好ましい。このような基としては、例えば、メチルシクロヘキシル基、ジメチルシクロへキシル基、メチルノルボルニル基、メチルアダマンチル基、シクロヘキシルメチル基、メチルシクロへキシルメチル基、アダマンチルメチル基、ノルボルニルメチル基等が挙げられる。
a02及びRa03は、好ましくは炭素数1〜6のアルキル基であり、より好ましくはメチル基又はエチル基である。
a04は、好ましくは炭素数1〜6のアルキル基又は炭素数5〜12の脂環式炭化水素基であり、より好ましくはメチル基、エチル基、シクロヘキシル基又はアダマンチル基である。
L a01 is preferably an oxygen atom or * —O— (CH 2 ) k01 —CO—O— (where k01 is preferably an integer of 1 to 4, more preferably 1, and more preferably). Is an oxygen atom.
Examples of the alkyl group of R a02 , R a03, and R a04 , the alicyclic hydrocarbon group, and a group obtained by combining these include the same groups as those described for R a1 to R a3 in formula (1).
The alkyl group for R a02 , R a03 and R a04 preferably has 6 or less carbon atoms.
The alicyclic hydrocarbon group represented by R a02 , R a03 and R a04 preferably has 8 or less carbon atoms, more preferably 6 or less.
The group combining the alkyl group and the alicyclic hydrocarbon group preferably has a total carbon number of 18 or less, combining the alkyl group and the alicyclic hydrocarbon group. Examples of such groups include a methylcyclohexyl group, a dimethylcyclohexyl group, a methylnorbornyl group, a methyladamantyl group, a cyclohexylmethyl group, a methylcyclohexylmethyl group, an adamantylmethyl group, and a norbornylmethyl group. It is done.
R a02 and R a03 are preferably an alkyl group having 1 to 6 carbon atoms, more preferably a methyl group or an ethyl group.
R a04 is preferably an alkyl group having 1 to 6 carbon atoms or an alicyclic hydrocarbon group having 5 to 12 carbon atoms, and more preferably a methyl group, an ethyl group, a cyclohexyl group, or an adamantyl group.

a1及びLa2は、好ましくは、−O−又は−O−(CH2k1’−CO−O−であり(但し、k1’は、1〜4の整数であり、好ましくは1である)、より好ましくは−O−である。
a4及びRa5は、好ましくはメチル基である。
a6及びRa7のアルキル基、脂環式炭化水素基及びこれらを組み合わせることにより形成される基は、式(1)のRa1〜Ra3で挙げた基と同様の基が挙げられる。
a6及びRa7のアルキル基は、好ましくは炭素数6以下である。
a6及びRa7の脂環式炭化水素基は、好ましくは炭素数8以下、より好ましくは6以下である。
m1は、好ましくは0〜3の整数、より好ましくは0又は1である。
n1は、好ましくは0〜3の整数、より好ましくは0又は1である。
n1’は好ましくは0又は1である。
L a1 and L a2 are preferably —O— or * —O— (CH 2 ) k1 ′ —CO—O— (where k1 ′ is an integer of 1 to 4, preferably 1). More preferably -O-.
R a4 and R a5 are preferably methyl groups.
Examples of the alkyl group of R a6 and R a7 , the alicyclic hydrocarbon group, and a group formed by combining these include the same groups as those exemplified for R a1 to R a3 of formula (1).
The alkyl group for R a6 and R a7 preferably has 6 or less carbon atoms.
The alicyclic hydrocarbon group of R a6 and R a7 preferably has 8 or less carbon atoms, more preferably 6 or less.
m1 is preferably an integer of 0 to 3, more preferably 0 or 1.
n1 is preferably an integer of 0 to 3, more preferably 0 or 1.
n1 ′ is preferably 0 or 1.

モノマー(a1−0)としては、例えば、式(a1−0−1)〜式(a1−0−12)のいずれかで表されるモノマーが好ましく、式(a1−0−1)〜式(a1−0−10)のいずれかで表されるモノマーがより好ましい。

Figure 2017105770
As the monomer (a1-0), for example, a monomer represented by any one of the formulas (a1-0-1) to (a1-0-12) is preferable, and the formula (a1-0-1) to the formula ( A monomer represented by any one of a1-0-10) is more preferable.
Figure 2017105770

上記の構造単位において、Ra01に相当するメチル基が水素原子に置き換わった構造単位も、構造単位(a1−0)の具体例として挙げることができる。 In the above structural unit, a structural unit in which a methyl group corresponding to R a01 is replaced with a hydrogen atom can also be given as a specific example of the structural unit (a1-0).

モノマー(a1−1)としては、例えば、特開2010−204646号公報に記載されたモノマーが挙げられる。中でも、式(a1−1−1)〜式(a1−1−8)のいずれかで表されるモノマーが好ましく、式(a1−1−1)〜式(a1−1−4)のいずれかで表されるモノマーがより好ましい。

Figure 2017105770
As a monomer (a1-1), the monomer described in Unexamined-Japanese-Patent No. 2010-204646 is mentioned, for example. Among these, a monomer represented by any one of formula (a1-1-1) to formula (a1-1-8) is preferable, and any one of formula (a1-1-1) to formula (a1-1-4) is preferable. The monomer represented by is more preferable.
Figure 2017105770

モノマー(a1−2)としては、1−メチルシクロペンタン−1−イル(メタ)アクリレート、1−エチルシクロペンタン−1−イル(メタ)アクリレート、1−メチルシクロヘキサン−1−イル(メタ)アクリレート、1−エチルシクロヘキサン−1−イル(メタ)アクリレート、1−エチルシクロヘプタン−1−イル(メタ)アクリレート、1−エチルシクロオクタン−1−イル(メタ)アクリレート、1−イソプロピルシクロペンタン−1−イル(メタ)アクリレート、1−イソプロピルシクロヘキサン−1−イル(メタ)アクリレート等が挙げられる。式(a1−2−1)〜式(a1−2−12)のいずれかで表されるモノマーが好ましく、式(a1−2−3)、式(a1−2−4)、式(a1−2−9)又は式(a1−2−10)で表されるモノマーがより好ましく、式(a1−2−3)又は式(a1−2−9)で表されるモノマーがさらに好ましい。

Figure 2017105770
As the monomer (a1-2), 1-methylcyclopentan-1-yl (meth) acrylate, 1-ethylcyclopentan-1-yl (meth) acrylate, 1-methylcyclohexane-1-yl (meth) acrylate, 1-ethylcyclohexane-1-yl (meth) acrylate, 1-ethylcycloheptan-1-yl (meth) acrylate, 1-ethylcyclooctane-1-yl (meth) acrylate, 1-isopropylcyclopentan-1-yl (Meth) acrylate, 1-isopropylcyclohexane-1-yl (meth) acrylate, etc. are mentioned. A monomer represented by any one of the formulas (a1-2-1) to (a1-2-12) is preferable, and the formula (a1-2-3), the formula (a1-2-4), the formula (a1- The monomer represented by 2-9) or formula (a1-2-10) is more preferred, and the monomer represented by formula (a1-2-3) or formula (a1-2-9) is more preferred.
Figure 2017105770

樹脂(A)が構造単位(a1−0)及び/又は構造単位(a1−1)及び/又は構造単位(a1−2)を含む場合、これらの合計含有率は、樹脂(A)の全構造単位に対して、通常10〜95モル%であり、好ましくは15〜90モル%であり、より好ましくは20〜85モル%である。   When the resin (A) includes the structural unit (a1-0) and / or the structural unit (a1-1) and / or the structural unit (a1-2), the total content thereof is the total structure of the resin (A). It is 10-95 mol% normally with respect to a unit, Preferably it is 15-90 mol%, More preferably, it is 20-85 mol%.

式(2)で表される基を有する(メタ)アクリル系モノマーに由来する構造単位としては、式(a1−5)で表される構造単位(以下「構造単位(a1−5)」という場合がある)も挙げられる。

Figure 2017105770
式(a1−5)中、
a8は、ハロゲン原子を有してもよい炭素数1〜6のアルキル基、水素原子又はハロゲン原子を表す。
a1は、単結合又は*−(CH2h3−CO−L54−を表し、h3は1〜4の整数を表し、*は、L51との結合手を表す。
51、L52、L53及びL54は、それぞれ独立に、−O−又は−S−を表す。
s1は、1〜3の整数を表す。
s1’は、0〜3の整数を表す。 As a structural unit derived from a (meth) acrylic monomer having a group represented by the formula (2), a structural unit represented by the formula (a1-5) (hereinafter referred to as “structural unit (a1-5)”) Is also included).
Figure 2017105770
In formula (a1-5),
R a8 represents a C 1-6 alkyl group optionally having a halogen atom, a hydrogen atom, or a halogen atom.
Z a1 represents a single bond or * — (CH 2 ) h3 —CO—L 54 —, h3 represents an integer of 1 to 4, and * represents a bond to L 51 .
L 51 , L 52 , L 53 and L 54 each independently represent —O— or —S—.
s1 represents an integer of 1 to 3.
s1 ′ represents an integer of 0 to 3.

ハロゲン原子としては、フッ素原子及び塩素原子が挙げられ、フッ素原子が好ましい。
ハロゲン原子を有してもよい炭素数1〜6のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、ヘプチル基、オクチル基、フルオロメチル基及びトリフルオロメチル基が挙げられる。
式(a1−5)においては、Ra8は、水素原子、メチル基又はトリフルオロメチル基が好ましい。
51は、酸素原子が好ましい。
52及びL53は、一方が−O−、他方が−S−であることが好ましい。
s1は、1が好ましい。
s1’は、0〜2の整数が好ましい。
a1は、単結合又は*−CH2−CO−O−が好ましい。*はL51との結合手を表す。
Examples of the halogen atom include a fluorine atom and a chlorine atom, and a fluorine atom is preferable.
Examples of the alkyl group having 1 to 6 carbon atoms which may have a halogen atom include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, a fluoromethyl group and a trifluoromethyl group. Groups.
In formula (a1-5), R a8 is preferably a hydrogen atom, a methyl group or a trifluoromethyl group.
L 51 is preferably an oxygen atom.
One of L 52 and L 53 is preferably —O— and the other is —S—.
s1 is preferably 1.
s1 ′ is preferably an integer of 0 to 2.
Z a1 is preferably a single bond or * —CH 2 —CO—O—. * Represents a bond to L 51.

構造単位(a1−5)を導くモノマーとしては、例えば、特開2010−61117号公報に記載されたモノマーが挙げられる。中でも、式(a1−5−1)〜式(a1−5−4)でそれぞれ表されるモノマーが好ましく、式(a1−5−1)又は式(a1−5−2)で表されるモノマーがより好ましい。

Figure 2017105770
As a monomer which introduce | transduces structural unit (a1-5), the monomer described in Unexamined-Japanese-Patent No. 2010-61117 is mentioned, for example. Among these, monomers represented by formulas (a1-5-1) to (a1-5-4) are preferable, and monomers represented by formula (a1-5-1) or formula (a1-5-2) are preferable. Is more preferable.
Figure 2017105770

樹脂(A)が、構造単位(a1−5)を有する場合、その含有率は、樹脂(A)の全構造単位に対して、1〜50モル%が好ましく、3〜45モル%がより好ましく、5〜40モル%がさらに好ましい。   When resin (A) has a structural unit (a1-5), the content rate is preferable 1-50 mol% with respect to all the structural units of resin (A), and 3-45 mol% is more preferable. 5 to 40 mol% is more preferable.

構造単位(a1)としては、さらに以下の構造単位も挙げられる。

Figure 2017105770
Examples of the structural unit (a1) further include the following structural units.
Figure 2017105770

樹脂(A)中の酸不安定基を有する構造単位(a)としては、構造単位(a1−0)、構造単位(a1−1)、構造単位(a1−2)及び構造単位(a1−5)からなる群から選ばれる少なくとも一種以上が好ましく、少なくとも二種以上がより好ましく、構造単位(a1−1)及び構造単位(a1−2)の組み合わせ、構造単位(a1−1)及び構造単位(a1−5)の組み合わせがさらに好ましい。   The structural unit (a) having an acid labile group in the resin (A) includes the structural unit (a1-0), the structural unit (a1-1), the structural unit (a1-2), and the structural unit (a1-5). ) Is preferably at least one selected from the group consisting of, and more preferably at least two, a combination of structural unit (a1-1) and structural unit (a1-2), structural unit (a1-1) and structural unit ( The combination of a1-5) is more preferable.

〈構造単位(s)〉
構造単位(s)は、酸不安定基を有さないモノマー(以下「モノマー(s)」という場合がある)から導かれる。モノマー(s)は、レジスト分野で公知の酸不安定基を有さないモノマーを使用できる。
構造単位(s)としては、ヒドロキシ基又はラクトン環を有し、かつ酸不安定基を有さない構造単位が好ましい。ヒドロキシ基を有し、かつ酸不安定基を有さない構造単位(以下「構造単位(a2)」という場合がある)及び/又はラクトン環を有し、かつ酸不安定基を有さない構造単位(以下「構造単位(a3)」という場合がある)を有する樹脂を本発明のレジスト組成物に使用すれば、レジストパターンの解像度及び基板との密着性を向上させることができる。
<Structural unit (s)>
The structural unit (s) is derived from a monomer having no acid labile group (hereinafter sometimes referred to as “monomer (s)”). As the monomer (s), a monomer having no acid labile group known in the resist field can be used.
As the structural unit (s), a structural unit having a hydroxy group or a lactone ring and having no acid labile group is preferable. A structure having a hydroxy group and having no acid labile group (hereinafter sometimes referred to as “structural unit (a2)”) and / or a lactone ring and having no acid labile group If a resin having a unit (hereinafter sometimes referred to as “structural unit (a3)”) is used in the resist composition of the present invention, the resolution of the resist pattern and the adhesion to the substrate can be improved.

〈構造単位(a2)〉
構造単位(a2)が有するヒドロキシ基は、アルコール性ヒドロキシ基でも、フェノール性ヒドロキシ基でもよい。
本発明のレジスト組成物からレジストパターンを製造するとき、露光光源としてKrFエキシマレーザ(248nm)、電子線又はEUV(超紫外光)等の高エネルギー線を用いる場合には、構造単位(a2)として、フェノール性ヒドロキシ基を有する構造単位(a2)を用いることが好ましい。また、ArFエキシマレーザ(193nm)等を用いる場合には、構造単位(a2)として、アルコール性ヒドロキシ基を有する構造単位(a2)が好ましく、構造単位(a2−1)を用いることがより好ましい。構造単位(a2)としては、1種を単独で含んでいてもよく、2種以上を含んでいてもよい。
<Structural unit (a2)>
The hydroxy group contained in the structural unit (a2) may be an alcoholic hydroxy group or a phenolic hydroxy group.
When a resist pattern is produced from the resist composition of the present invention, when a high energy beam such as a KrF excimer laser (248 nm), an electron beam or EUV (ultra-ultraviolet light) is used as an exposure light source, the structural unit (a2) It is preferable to use the structural unit (a2) having a phenolic hydroxy group. When an ArF excimer laser (193 nm) or the like is used, the structural unit (a2) having an alcoholic hydroxy group is preferable as the structural unit (a2), and the structural unit (a2-1) is more preferable. As a structural unit (a2), 1 type may be included independently and 2 or more types may be included.

フェノール性ヒドロキシ基有する構造単位(a2)としては、式(a2−0)で表される構造単位(以下「構造単位(a2−0)」という場合がある。)が挙げられる。

Figure 2017105770
[式(a2−0)中、
a30は、水素原子、ハロゲン原子又はハロゲン原子を有してもよい炭素数1〜6のアルキル基を表す。
a31は、ハロゲン原子、ヒドロキシ基、炭素数1〜6のアルキル基、炭素数1〜6のアルコキシ基、炭素数2〜4のアシル基、炭素数2〜4のアシルオキシ基、アクリロイルオキシ基又はメタクリロイルオキシ基を表す。
maは0〜4の整数を表す。maが2以上の整数である場合、複数のRa31は互いに同一であっても異なってもよい。] Examples of the structural unit (a2) having a phenolic hydroxy group include a structural unit represented by the formula (a2-0) (hereinafter sometimes referred to as “structural unit (a2-0)”).
Figure 2017105770
[In the formula (a2-0),
R a30 represents a hydrogen atom, a halogen atom or an alkyl group having 1 to 6 carbon atoms which may have a halogen atom.
R a31 is a halogen atom, a hydroxy group, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, an acyl group having 2 to 4 carbon atoms, an acyloxy group having 2 to 4 carbon atoms, an acryloyloxy group, or Represents a methacryloyloxy group.
ma represents an integer of 0 to 4. When ma is an integer of 2 or more, the plurality of R a31 may be the same as or different from each other. ]

炭素数1〜6のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、n−ペンチル基、n−ヘキシル基等が挙げられる。
ハロゲン原子としては、フッ素原子、塩素原子及び臭素原子等が挙げられる。
a30のハロゲン原子を有してもよい炭素数1〜6のアルキル基としては、トリフルオロメチル基、ジフルオロメチル基、メチル基、ペルフルオロエチル基、1,1,1−トリフルオロエチル基、1,1,2,2−テトラフルオロエチル基、エチル基、ペルフルオロプロピル基、1,1,1,2,2−ペンタフルオロプロピル基、プロピル基、ペルフルオロブチル基、1,1,2,2,3,3,4,4−オクタフルオロブチル基、ブチル基、ペルフルオロペンチル基、1,1,1,2,2,3,3,4,4−ノナフルオロペンチル基、n−ペンチル基、n−ヘキシル基、n−ペルフルオロヘキシル基等が挙げられる。Ra30は、水素原子又は炭素数1〜4のアルキル基が好ましく、水素原子、メチル基又はエチル基がより好ましく、水素原子又はメチル基がさらに好ましい。
アルコキシ基としては、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基、ペンチルオキシ基及びヘキシルオキシ基等が挙げられる。なかでも、炭素数1〜4のアルコキシ基が好ましく、メトキシ基又はエトキシ基がより好ましく、メトキシ基がさらに好ましい。
アシル基としては、アセチル基、プロピオニル基及びブチリル基が挙げられる。
アシルオキシ基としては、アセチルオキシ基、プロピオニルオキシ基、ブチリルオキシ基等が挙げられる。
maは0、1又は2が好ましく、0又は1がより好ましく、0が特に好ましい。
Examples of the alkyl group having 1 to 6 carbon atoms include a methyl group, an ethyl group, a propyl group, a butyl group, an n-pentyl group, and an n-hexyl group.
Examples of the halogen atom include a fluorine atom, a chlorine atom and a bromine atom.
Examples of the alkyl group having 1 to 6 carbon atoms which may have a halogen atom of R a30 include a trifluoromethyl group, a difluoromethyl group, a methyl group, a perfluoroethyl group, a 1,1,1-trifluoroethyl group, 1 , 1,2,2-tetrafluoroethyl group, ethyl group, perfluoropropyl group, 1,1,1,2,2-pentafluoropropyl group, propyl group, perfluorobutyl group, 1,1,2,2,3 , 3,4,4-octafluorobutyl group, butyl group, perfluoropentyl group, 1,1,1,2,2,3,3,4,4-nonafluoropentyl group, n-pentyl group, n-hexyl Group, n-perfluorohexyl group and the like. R a30 is preferably a hydrogen atom or an alkyl group having 1 to 4 carbon atoms, more preferably a hydrogen atom, a methyl group or an ethyl group, and even more preferably a hydrogen atom or a methyl group.
Examples of the alkoxy group include a methoxy group, an ethoxy group, a propoxy group, a butoxy group, a pentyloxy group, and a hexyloxy group. Especially, a C1-C4 alkoxy group is preferable, a methoxy group or an ethoxy group is more preferable, and a methoxy group is further more preferable.
Examples of the acyl group include an acetyl group, a propionyl group, and a butyryl group.
Examples of the acyloxy group include an acetyloxy group, a propionyloxy group, and a butyryloxy group.
ma is preferably 0, 1 or 2, more preferably 0 or 1, and particularly preferably 0.

構造単位(a2−0)を誘導するモノマーとしては、例えば、特開2010−204634号公報に記載されているモノマーが挙げられる。
中でも、構造単位(a2−0)としては、式(a2−0−1)、式(a2−0−2)、式(a2−0−3)及び式(a2−0−4)でそれぞれ表されるものが好ましく、式(a2−0−1)又は式(a2−0−2)で表されるものがより好ましい。

Figure 2017105770
Examples of the monomer that derives the structural unit (a2-0) include monomers described in JP 2010-204634 A.
Among them, the structural unit (a2-0) is represented by formula (a2-0-1), formula (a2-0-2), formula (a2-0-3), and formula (a2-0-4), respectively. What is represented is preferable, and what is represented by a formula (a2-0-1) or a formula (a2-0-2) is more preferable.
Figure 2017105770

構造単位(a2−0)を含む樹脂(A)は、構造単位(a2−0)を誘導するモノマーが有するフェノール性ヒドロキシ基を保護基で保護したモノマーを用いて重合反応を行い、その後脱保護処理することにより製造できる。ただし、脱保護処理を行う際には、構造単位(a1)が有する酸不安定基を著しく損なわないようにして行う必要がある。このような保護基としては、アセチル基等が挙げられる。   The resin (A) containing the structural unit (a2-0) is subjected to a polymerization reaction using a monomer in which the phenolic hydroxy group of the monomer that derives the structural unit (a2-0) is protected with a protective group, and then deprotected. It can be manufactured by processing. However, when the deprotection treatment is performed, the acid labile group of the structural unit (a1) needs to be not significantly impaired. Examples of such protecting groups include acetyl groups.

樹脂(A)が、フェノール性ヒドロキシ基を有する構造単位(a2−0)を有する場合、その含有率は、樹脂(A)の全構造単位に対して、5〜95モル%が好ましく、10〜80モル%がより好ましく、15〜80モル%がさらに好ましい。   When the resin (A) has a structural unit (a2-0) having a phenolic hydroxy group, the content is preferably from 5 to 95 mol% with respect to all the structural units of the resin (A). 80 mol% is more preferable, and 15-80 mol% is further more preferable.

アルコール性ヒドロキシ基を有する構造単位(a2)としては、式(a2−1)で表される構造単位(以下「構造単位(a2−1)」という場合がある。)が挙げられる。

Figure 2017105770
式(a2−1)中、
a3は、−O−又は−O−(CH2k2−CO−O−を表す。
k2は1〜7の整数を表す。*は−CO−との結合手を表す。
a14は、水素原子又はメチル基を表す。
a15及びRa16は、それぞれ独立に、水素原子、メチル基又はヒドロキシ基を表す。
o1は、0〜10の整数を表す。 Examples of the structural unit (a2) having an alcoholic hydroxy group include a structural unit represented by the formula (a2-1) (hereinafter sometimes referred to as “structural unit (a2-1)”).
Figure 2017105770
In formula (a2-1),
L a3 represents —O— or * —O— (CH 2 ) k2 —CO—O—.
k2 represents an integer of 1 to 7. * Represents a bond with -CO-.
R a14 represents a hydrogen atom or a methyl group.
R a15 and R a16 each independently represent a hydrogen atom, a methyl group or a hydroxy group.
o1 represents an integer of 0 to 10.

式(a2−1)では、La3は、好ましくは、−O−、−O−(CH2f1−CO−O−であり(前記f1は、1〜4の整数である)、より好ましくは−O−である。
a14は、好ましくはメチル基である。
a15は、好ましくは水素原子である。
a16は、好ましくは水素原子又はヒドロキシ基である。
o1は、好ましくは0〜3の整数、より好ましくは0又は1である。
In the formula (a2-1), L a3 is preferably, -O -, - O- (CH 2) f1 -CO-O- and is (wherein f1 is an integer from 1 to 4), more preferably Is —O—.
R a14 is preferably a methyl group.
R a15 is preferably a hydrogen atom.
R a16 is preferably a hydrogen atom or a hydroxy group.
o1 is preferably an integer of 0 to 3, more preferably 0 or 1.

構造単位(a2−1)を誘導するモノマーとしては、例えば、特開2010−204646号公報に記載されたモノマーが挙げられる。式(a2−1−1)〜式(a2−1−6)のいずれかで表されるモノマーが好ましく、式(a2−1−1)〜式(a2−1−4)のいずれかで表されるモノマーがより好ましく、式(a2−1−1)又は式(a2−1−3)で表されるモノマーがさらに好ましい。

Figure 2017105770
Examples of the monomer that derives the structural unit (a2-1) include monomers described in JP 2010-204646 A. A monomer represented by any one of formula (a2-1-1) to formula (a2-1-6) is preferable, and represented by any one of formula (a2-1-1) to formula (a2-1-4). The monomer represented by Formula (a2-1-1) or Formula (a2-1-3) is more preferable.
Figure 2017105770

樹脂(A)が構造単位(a2−1)を含む場合、その含有率は、樹脂(A)の全構造単位に対して、通常1〜45モル%であり、好ましくは1〜40モル%であり、より好ましくは1〜35モル%であり、さらに好ましくは2〜20モル%である。   When resin (A) contains a structural unit (a2-1), the content rate is 1-45 mol% normally with respect to all the structural units of resin (A), Preferably it is 1-40 mol%. More preferably, it is 1-35 mol%, More preferably, it is 2-20 mol%.

〈構造単位(a3)〉
構造単位(a3)が有するラクトン環は、β−プロピオラクトン環、γ−ブチロラクトン環、δ−バレロラクトン環のような単環でもよく、単環式のラクトン環と他の環との縮合環でもよい。好ましくは、γ−ブチロラクトン環、アダマンタンラクトン環又は、γ−ブチロラクトン環構造を含む橋かけ環が挙げられる。
<Structural unit (a3)>
The lactone ring of the structural unit (a3) may be a monocycle such as a β-propiolactone ring, γ-butyrolactone ring, or δ-valerolactone ring, or a condensed ring of a monocyclic lactone ring and another ring. But you can. Preferably, a γ-butyrolactone ring, an adamantane lactone ring, or a bridged ring containing a γ-butyrolactone ring structure is used.

構造単位(a3)は、好ましくは、式(a3−1)、式(a3−2)、式(a3−3)又は式(a3−4)で表される構造単位である。これらの1種を単独で含有してもよく、2種以上を含有してもよい。   The structural unit (a3) is preferably a structural unit represented by the formula (a3-1), the formula (a3-2), the formula (a3-3), or the formula (a3-4). These 1 type may be contained independently and 2 or more types may be contained.

Figure 2017105770
[式(a3−1)中、
a4は、−O−又は−O−(CH2k3−CO−O−(k3は1〜7の整数を表す。)で表される基を表す。*はカルボニル基との結合手を表す。
a18は、水素原子又はメチル基を表す。
a21は、炭素数1〜4の脂肪族炭化水素基を表す。
p1は0〜5の整数を表す。p1が2以上のとき、複数のRa21は互いに同一又は相異なる。
式(a3−2)中、
a5は、−O−又は−O−(CH2k3−CO−O−(k3は1〜7の整数を表す。)で表される基を表す。*はカルボニル基との結合手を表す。
a19は、水素原子又はメチル基を表す。
a22は、カルボキシ基、シアノ基又は炭素数1〜4の脂肪族炭化水素基を表す。
q1は、0〜3の整数を表す。q1が2以上のとき、複数のRa22は互いに同一又は相異なる。
式(a3−3)中、
a6は、−O−又は−O−(CH2k3−CO−O−(k3は1〜7の整数を表す。)で表される基を表す。*はカルボニル基との結合手を表す。
a20は、水素原子又はメチル基を表す。
a23は、カルボキシ基、シアノ基又は炭素数1〜4の脂肪族炭化水素基を表す。
r1は、0〜3の整数を表す。r1が2以上のとき、複数のRa23は互いに同一又は相異なる。
式(a3−4)中、
a24は、ハロゲン原子を有してもよい炭素数1〜6のアルキル基、水素原子又はハロゲン原子を表す。
a25は、カルボキシ基、シアノ基又は炭素数1〜4の脂肪族炭化水素基を表す。
w1は、0〜3の整数を表す。w1が2以上のとき、複数のRa25は互いに同一又は相異なる。
a7は、−O−、−O−La8−O−、−O−La8−CO−O−、−O−La8−CO−O−La9−CO−O−又は−O−La8−O−CO−La9−O−を表す。
*はカルボニル基との結合手を表す。
a8及びLa9は、互いに独立に、炭素数1〜6のアルカンジイル基を表す。]
Figure 2017105770
[In the formula (a3-1),
L a4 represents a group represented by —O— or * —O— (CH 2 ) k3 —CO—O— (k3 represents an integer of 1 to 7). * Represents a bond with a carbonyl group.
R a18 represents a hydrogen atom or a methyl group.
R a21 represents an aliphatic hydrocarbon group having 1 to 4 carbon atoms.
p1 represents an integer of 0 to 5. When p1 is 2 or more, the plurality of R a21 are the same or different from each other.
In formula (a3-2),
L a5 represents a group represented by —O— or * —O— (CH 2 ) k3 —CO—O— (k3 represents an integer of 1 to 7). * Represents a bond with a carbonyl group.
R a19 represents a hydrogen atom or a methyl group.
R a22 represents a carboxy group, a cyano group, or an aliphatic hydrocarbon group having 1 to 4 carbon atoms.
q1 represents an integer of 0 to 3. When q1 is 2 or more, the plurality of R a22 are the same or different from each other.
In formula (a3-3),
L a6 represents a group represented by —O— or * —O— (CH 2 ) k3 —CO—O— (k3 represents an integer of 1 to 7). * Represents a bond with a carbonyl group.
R a20 represents a hydrogen atom or a methyl group.
R a23 represents a carboxy group, a cyano group, or an aliphatic hydrocarbon group having 1 to 4 carbon atoms.
r1 represents an integer of 0 to 3. When r1 is 2 or more, the plurality of R a23 are the same or different from each other.
In formula (a3-4),
R a24 represents an alkyl group having 1 to 6 carbon atoms which may have a halogen atom, a hydrogen atom or a halogen atom.
R a25 represents a carboxy group, a cyano group, or an aliphatic hydrocarbon group having 1 to 4 carbon atoms.
w1 represents an integer of 0 to 3. When w1 is 2 or more, the plurality of R a25 are the same or different from each other.
L a7 is —O—, * —O—L a8 —O—, * —O—L a8 —CO—O—, * —O—L a8 —CO—O—L a9 —CO—O— or * —O—L a8 —O—CO—L a9 —O— is represented.
* Represents a bond with a carbonyl group.
L a8 and L a9 each independently represent an alkanediyl group having 1 to 6 carbon atoms. ]

a21、Ra22、Ra23及びRa25の脂肪族炭化水素基としては、メチル基、エチル基、n−プロピル基、イソプロピル基、n−ブチル基、sec−ブチル基及びtert−ブチル基等のアルキル基が挙げられる。
a24のハロゲン原子としては、フッ素原子、塩素原子、臭素原子及びヨウ素原子が挙げられる。
a24のアルキル基としては、メチル基、エチル基、n−プロピル基、イソプロピル基、n−ブチル基、sec−ブチル基、tert−ブチル基、n−ペンチル基及びn−ヘキシル基等が挙げられ、好ましくは炭素数1〜4のアルキル基であり、より好ましくはメチル基又はエチル基である。
a24のハロゲン原子を有するアルキル基としては、トリフルオロメチル基、ペルフルオロエチル基、ペルフルオロプロピル基、ペルフルオロイソプロピル基、ペルフルオロブチル基、ペルフルオロsec−ブチル基、ペルフルオロtert−ブチル基、ペルフルオロペンチル基、ペルフルオロヘキシル基、トリクロロメチル基、トリブロモメチル基、トリヨードメチル基等が挙げられる。
Examples of the aliphatic hydrocarbon group represented by R a21 , R a22 , R a23 and R a25 include methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, sec-butyl group and tert-butyl group. An alkyl group is mentioned.
Examples of the halogen atom for R a24 include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.
Examples of the alkyl group for R a24 include methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, sec-butyl group, tert-butyl group, n-pentyl group, and n-hexyl group. , Preferably it is a C1-C4 alkyl group, More preferably, it is a methyl group or an ethyl group.
Examples of the alkyl group having a halogen atom of R a24 include trifluoromethyl group, perfluoroethyl group, perfluoropropyl group, perfluoroisopropyl group, perfluorobutyl group, perfluorosec-butyl group, perfluorotert-butyl group, perfluoropentyl group, perfluoro group. A hexyl group, a trichloromethyl group, a tribromomethyl group, a triiodomethyl group, etc. are mentioned.

a8及びLa9のアルカンジイル基としては、メチレン基、エチレン基、プロパン−1,3−ジイル基、プロパン−1,2−ジイル基、ブタン−1,4−ジイル基、ペンタン−1,5−ジイル基、ヘキサン−1,6−ジイル基、ブタン−1,3−ジイル基、2−メチルプロパン−1,3−ジイル基、2−メチルプロパン−1,2−ジイル基、ペンタン−1,4−ジイル基及び2−メチルブタン−1,4−ジイル基等が挙げられる。 Examples of the alkanediyl group represented by L a8 and L a9 include a methylene group, an ethylene group, a propane-1,3-diyl group, a propane-1,2-diyl group, a butane-1,4-diyl group, and a pentane-1,5. -Diyl group, hexane-1,6-diyl group, butane-1,3-diyl group, 2-methylpropane-1,3-diyl group, 2-methylpropane-1,2-diyl group, pentane-1, 4-diyl group, 2-methylbutane-1,4-diyl group, etc. are mentioned.

式(a3−1)〜式(a3−3)において、La4〜La6は、それぞれ独立に、好ましくは、−O−又は、k3が1〜4の整数である*−O−(CH2k3−CO−O−で表される基、より好ましくは−O−及び、*−O−CH2−CO−O−、さらに好ましくは酸素原子である。
a18〜Ra21は、好ましくはメチル基である。
a22及びRa23は、それぞれ独立に、好ましくはカルボキシ基、シアノ基又はメチル基である。
p1、q1及びr1は、それぞれ独立に、好ましくは0〜2の整数であり、より好ましくは0又は1である。
In formula (a3-1) to formula (a3-3), L a4 to L a6 are each independently preferably —O— or k— is an integer of 1 to 4 * —O— (CH 2 ) A group represented by k 3 —CO—O—, more preferably —O— and * —O—CH 2 —CO—O—, still more preferably an oxygen atom.
R a18 to R a21 are preferably methyl groups.
R a22 and R a23 are each independently preferably a carboxy group, a cyano group or a methyl group.
p1, q1 and r1 are each independently preferably an integer of 0 to 2, more preferably 0 or 1.

式(a3−4)において、
a24は、好ましくは、水素原子又は炭素数1〜4のアルキル基であり、より好ましくは、水素原子、メチル基又はエチル基であり、さらに好ましくは、水素原子又はメチル基である。
a7は、好ましくは、−O−又は−O−La8−CO−O−であり、より好ましくは、−O−、−O−CH2−CO−O−又は−O−C24−CO−O−である。
a25は、好ましくはカルボキシ基、シアノ基又はメチル基である。
w1は、好ましくは0〜2の整数であり、より好ましくは0又は1である。
特に、式(a3−4)は、式(a3−4)’が好ましい。

Figure 2017105770
(式中、Ra24、La7は、上記と同じ意味を表す。) In formula (a3-4),
R a24 is preferably a hydrogen atom or an alkyl group having 1 to 4 carbon atoms, more preferably a hydrogen atom, a methyl group or an ethyl group, and still more preferably a hydrogen atom or a methyl group.
L a7 is preferably —O— or * —O—L a8 —CO—O—, and more preferably —O—, —O—CH 2 —CO—O— or —O—C 2 H. 4- CO-O-.
R a25 is preferably a carboxy group, a cyano group, or a methyl group.
w1 is preferably an integer of 0 to 2, more preferably 0 or 1.
In particular, the formula (a3-4) is preferably the formula (a3-4) ′.
Figure 2017105770
(Wherein R a24 and L a7 represent the same meaning as described above.)

構造単位(a3)を導くモノマーとしては、特開2010−204646号公報に記載されたモノマー、特開2000−122294号公報に記載されたモノマー、特開2012−41274号公報に記載されたモノマーが挙げられる。構造単位(a3)としては、式(a3−1−1)〜式(a3−1−4)、式(a3−2−1)〜式(a3−2−4)、式(a3−3−1)〜式(a3−3−4)及び式(a3−4−1)〜式(a3−4−6)のいずれかで表される構造単位が好ましく、式(a3−1−1)、式(a3−1−2)及び式(a3−2−3)〜式(a3−2−4)のいずれかで表される構造単位がより好ましく、式(a3−1−1)又は式(a3−2−3)で表される構造単位がさらに好ましい。   As monomers for deriving the structural unit (a3), monomers described in JP 2010-204646 A, monomers described in JP 2000-122294 A, monomers described in JP 2012-41274 A are listed. Can be mentioned. As the structural unit (a3), formula (a3-1-1) to formula (a3-1-4), formula (a3-2-1) to formula (a3-2-4), formula (a3-3) 1) to a structural unit represented by any one of the formula (a3-3-4) and the formula (a3-4-1) to the formula (a3-4-6), the formula (a3-1-1), The structural unit represented by any one of the formula (a3-1-2) and the formula (a3-2-3) to the formula (a3-2-4) is more preferable, and the formula (a3-1-1) or the formula ( The structural unit represented by a3-2-3) is more preferable.

Figure 2017105770
Figure 2017105770

Figure 2017105770
Figure 2017105770

以下の式(a3−4−1)〜式(a3−4−12)で表される構造単位においては、Ra24に相当するメチル基が水素原子に置き換わった化合物も、構造単位(a3−4)の具体例として挙げることができる。

Figure 2017105770
In the structural units represented by the following formulas (a3-4-1) to (a3-4-12), compounds in which the methyl group corresponding to R a24 is replaced with a hydrogen atom are also structural units (a3-4). ).
Figure 2017105770

Figure 2017105770
Figure 2017105770

樹脂(A)が構造単位(a3)を含む場合、その合計含有率は、樹脂(A)の全構造単位に対して、通常5〜70モル%であり、好ましくは10〜65モル%であり、より好ましくは10〜60モル%である。
また、構造単位(a3−1)、構造単位(a3−2)、構造単位(a3−3)及び構造単位(a3−4)の含有率は、それぞれ、樹脂(A)の全構造単位に対して、5〜60モル%が好ましく、5〜50モル%がより好ましく、10〜50モル%がさらに好ましい。
When the resin (A) includes the structural unit (a3), the total content is usually 5 to 70 mol%, preferably 10 to 65 mol%, based on all the structural units of the resin (A). More preferably, it is 10-60 mol%.
Moreover, the content rate of a structural unit (a3-1), a structural unit (a3-2), a structural unit (a3-3), and a structural unit (a3-4) is respectively with respect to all the structural units of resin (A). 5 to 60 mol% is preferable, 5 to 50 mol% is more preferable, and 10 to 50 mol% is more preferable.

〈その他の構造単位(t)〉
構造単位(t)としては、構造単位(a2)及び構造単位(a3)以外に上述した構造単位(a4)及び構造単位(a5)などが挙げられる。
<Other structural units (t)>
Examples of the structural unit (t) include the structural unit (a4) and the structural unit (a5) described above in addition to the structural unit (a2) and the structural unit (a3).

樹脂(A)が、構造単位(a4)を有する場合、その含有率は、樹脂(A)の全構造単位に対して、1〜20モル%が好ましく、2〜15モル%がより好ましく、3〜10モル%がさらに好ましい。   When the resin (A) has a structural unit (a4), the content is preferably 1 to 20 mol%, more preferably 2 to 15 mol%, based on all structural units of the resin (A). More preferably, it is 10 mol%.

樹脂(A)が、構造単位(a5)を有する場合、その含有率は、樹脂(A)の全構造単位に対して、1〜30モル%が好ましく、2〜20モル%がより好ましく、3〜15モル%がさらに好ましい。   When the resin (A) has the structural unit (a5), the content is preferably 1 to 30 mol%, more preferably 2 to 20 mol%, based on all structural units of the resin (A). More preferred is ˜15 mol%.

樹脂(A)は、好ましくは、構造単位(a1)と構造単位(s)とからなる樹脂、すなわち、モノマー(a1)とモノマー(s)との共重合体である。
構造単位(s)は、好ましくは構造単位(a2)及び構造単位(a3)の少なくとも一種である。構造単位(a2)は、好ましくは式(a2−1)で表される構造単位である。構造単位(a3)は、好ましくは式(a3−1)で表される構造単位、式(a3−2)で表される構造単位及び式(a3−4)で表される構造単位から選ばれる少なくとも一種である。
The resin (A) is preferably a resin composed of the structural unit (a1) and the structural unit (s), that is, a copolymer of the monomer (a1) and the monomer (s).
The structural unit (s) is preferably at least one of the structural unit (a2) and the structural unit (a3). The structural unit (a2) is preferably a structural unit represented by the formula (a2-1). The structural unit (a3) is preferably selected from the structural unit represented by the formula (a3-1), the structural unit represented by the formula (a3-2), and the structural unit represented by the formula (a3-4). At least one kind.

樹脂(A)を構成する各構造単位は、2種以上を組み合わせてもよく、これら構造単位を誘導するモノマーを用いて、公知の重合法(例えばラジカル重合法)によって製造することができる。樹脂(A)が有する各構造単位の含有率は、重合に用いるモノマーの使用量で調整できる。
樹脂(A)の重量平均分子量は、好ましくは、2,000以上(より好ましくは2,500以上、さらに好ましくは3,000以上)、50,000以下(より好ましくは30,000以下、さらに好ましくは15,000以下)である。なお、重量平均分子量は、ゲルパーミエーションクロマトグラフィーにより求めた値である。
Each structural unit constituting the resin (A) may be a combination of two or more, and can be produced by a known polymerization method (for example, radical polymerization method) using a monomer that derives these structural units. The content rate of each structural unit which resin (A) has can be adjusted with the usage-amount of the monomer used for superposition | polymerization.
The weight average molecular weight of the resin (A) is preferably 2,000 or more (more preferably 2,500 or more, more preferably 3,000 or more), 50,000 or less (more preferably 30,000 or less, further preferably 15,000 or less). The weight average molecular weight is a value determined by gel permeation chromatography.

レジスト組成物における樹脂(X)含有量は、樹脂(A)100質量部に対して、好ましくは1〜60質量部であり、より好ましくは1〜50質量部であり、さらに好ましくは1〜40質量部であり、特に好ましくは2〜30質量部である。   The resin (X) content in the resist composition is preferably 1 to 60 parts by mass, more preferably 1 to 50 parts by mass, and further preferably 1 to 40 parts by mass with respect to 100 parts by mass of the resin (A). It is a mass part, Most preferably, it is 2-30 mass parts.

樹脂(A)と樹脂(X)との合計含有率は、レジスト組成物の固形分に対して、80質量%以上99質量%以下が好ましい。レジスト組成物の固形分及びこれに対する樹脂の含有率は、液体クロマトグラフィー又はガスクロマトグラフィー等の公知の分析手段で測定することができる。   As for the total content rate of resin (A) and resin (X), 80 to 99 mass% is preferable with respect to solid content of a resist composition. The solid content of the resist composition and the resin content relative thereto can be measured by a known analysis means such as liquid chromatography or gas chromatography.

<酸発生剤(B)>
酸発生剤は、非イオン系とイオン系とに分類されるが、本発明のレジスト組成物の酸発生剤(B)においては、いずれを用いてもよい。非イオン系酸発生剤としては、有機ハロゲン化物、スルホネートエステル類(例えば2−ニトロベンジルエステル、芳香族スルホネート、オキシムスルホネート、N−スルホニルオキシイミド、スルホニルオキシケトン、ジアゾナフトキノン 4−スルホネート)、スルホン類(例えばジスルホン、ケトスルホン、スルホニルジアゾメタン)等が挙げられる。イオン系酸発生剤としては、オニウムカチオンを含むオニウム塩(例えばジアゾニウム塩、ホスホニウム塩、スルホニウム塩、ヨードニウム塩)が代表的である。オニウム塩のアニオンとしては、スルホン酸アニオン、スルホニルイミドアニオン、スルホニルメチドアニオン等が挙げられる。
<Acid generator (B)>
The acid generator is classified into a nonionic type and an ionic type, and any of the acid generators (B) of the resist composition of the present invention may be used. Nonionic acid generators include organic halides, sulfonate esters (for example, 2-nitrobenzyl ester, aromatic sulfonate, oxime sulfonate, N-sulfonyloxyimide, sulfonyloxyketone, diazonaphthoquinone 4-sulfonate), and sulfones. (For example, disulfone, ketosulfone, sulfonyldiazomethane) and the like. Typical examples of the ionic acid generator include onium salts containing onium cations (for example, diazonium salts, phosphonium salts, sulfonium salts, and iodonium salts). Examples of the anion of the onium salt include a sulfonate anion, a sulfonylimide anion, and a sulfonylmethide anion.

酸発生剤(B)としては、特開昭63−26653号、特開昭55−164824号、特開昭62−69263号、特開昭63−146038号、特開昭63−163452号、特開昭62−153853号、特開昭63−146029号、米国特許第3,779,778号、米国特許第3,849,137号、独国特許第3914407号、欧州特許第126,712号等に記載の放射線によって酸を発生する化合物を使用することができる。また、公知の方法で製造した化合物を使用してもよい。酸発生剤(B)は、1種を単独で用いてもよく、2種以上を組み合わせて用いてもよい。   As the acid generator (B), JP-A-63-26653, JP-A-55-164824, JP-A-62-69263, JP-A-63-146038, JP-A-63-163452, Kaisho 62-153853, JP 63-146029, U.S. Pat. No. 3,779,778, U.S. Pat. No. 3,849,137, German Patent 3914407, European Patent 126,712, etc. The compound which generate | occur | produces an acid by the radiation as described in 1 can be used. Moreover, you may use the compound manufactured by the well-known method. An acid generator (B) may be used individually by 1 type, and may be used in combination of 2 or more type.

酸発生剤(B)は、好ましくはフッ素含有酸発生剤であり、より好ましくは式(B1)で表される塩(以下「酸発生剤(B1)」という場合がある)である。

Figure 2017105770
[式(B1)中、
及びQは、互いに独立に、フッ素原子又は炭素数1〜6のペルフルオロアルキル基を表す。
b1は、炭素数1〜24の2価の飽和炭化水素基を表し、該2価の飽和炭化水素基に含まれる−CH−は、−O−又は−CO−に置き換わっていてもよく、該2価の飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基で置換されていてもよい。
Yは、置換基を有していてもよいメチル基又は置換基を有していてもよい炭素数3〜18の1価の脂環式炭化水素基を表し、該アルキル基及び該1価の脂環式炭化水素基に含まれる−CH−は、−O−、−SO−又は−CO−に置き換わっていてもよい。
は、有機カチオンを表す。] The acid generator (B) is preferably a fluorine-containing acid generator, more preferably a salt represented by the formula (B1) (hereinafter sometimes referred to as “acid generator (B1)”).
Figure 2017105770
[In the formula (B1),
Q 1 and Q 2 each independently represent a fluorine atom or a C 1-6 perfluoroalkyl group.
L b1 represents a divalent saturated hydrocarbon group having 1 to 24 carbon atoms, and —CH 2 — contained in the divalent saturated hydrocarbon group may be replaced by —O— or —CO—. The hydrogen atom contained in the divalent saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group.
Y represents a methyl group which may have a substituent or a monovalent alicyclic hydrocarbon group having 3 to 18 carbon atoms which may have a substituent, the alkyl group and the monovalent —CH 2 — contained in the alicyclic hydrocarbon group may be replaced by —O—, —SO 2 — or —CO—.
Z + represents an organic cation. ]

及びQのペルフルオロアルキル基としては、トリフルオロメチル基、ペルフルオロエチル基、ペルフルオロプロピル基、ペルフルオロイソプロピル基、ペルフルオロブチル基、ペルフルオロsec−ブチル基、ペルフルオロtert−ブチル基、ペルフルオロペンチル基及びペルフルオロヘキシル基等が挙げられる。
及びQは、互いに独立に、フッ素原子又はトリフルオロメチル基であることが好ましく、ともにフッ素原子であることがより好ましい。
Examples of the perfluoroalkyl group of Q 1 and Q 2 include a trifluoromethyl group, a perfluoroethyl group, a perfluoropropyl group, a perfluoroisopropyl group, a perfluorobutyl group, a perfluorosec-butyl group, a perfluorotert-butyl group, a perfluoropentyl group, and a perfluoro group. A hexyl group etc. are mentioned.
Q 1 and Q 2 are preferably each independently a fluorine atom or a trifluoromethyl group, and more preferably a fluorine atom.

b1の2価の飽和炭化水素基としては、直鎖状アルカンジイル基、分岐状アルカンジイル基、単環式又は多環式の2価の脂環式飽和炭化水素基が挙げられ、これらの基のうち2種以上を組合せることにより形成される基でもよい。
具体的には、メチレン基、エチレン基、プロパン−1,3−ジイル基、ブタン−1,4−ジイル基、ペンタン−1,5−ジイル基、ヘキサン−1,6−ジイル基、ヘプタン−1,7−ジイル基、オクタン−1,8−ジイル基、ノナン−1,9−ジイル基、デカン−1,10−ジイル基、ウンデカン−1,11−ジイル基、ドデカン−1,12−ジイル基、トリデカン−1,13−ジイル基、テトラデカン−1,14−ジイル基、ペンタデカン−1,15−ジイル基、ヘキサデカン−1,16−ジイル基及びヘプタデカン−1,17−ジイル基等の直鎖状アルカンジイル基;
エタン−1,1−ジイル基、プロパン−1,1−ジイル基、プロパン−1,2−ジイル基、プロパン−2,2−ジイル基、ペンタン−2,4−ジイル基、2−メチルプロパン−1,3−ジイル基、2−メチルプロパン−1,2−ジイル基、ペンタン−1,4−ジイル基、2−メチルブタン−1,4−ジイル基等の分岐状アルカンジイル基;
シクロブタン−1,3−ジイル基、シクロペンタン−1,3−ジイル基、シクロヘキサン−1,4−ジイル基、シクロオクタン−1,5−ジイル基等のシクロアルカンジイル基である単環式の2価の脂環式飽和炭化水素基;
ノルボルナン−1,4−ジイル基、ノルボルナン−2,5−ジイル基、アダマンタン−1,5−ジイル基、アダマンタン−2,6−ジイル基等の多環式の2価の脂環式飽和炭化水素基等が挙げられる。
Examples of the divalent saturated hydrocarbon group for L b1 include a linear alkanediyl group, a branched alkanediyl group, a monocyclic or polycyclic divalent alicyclic saturated hydrocarbon group, and these It may be a group formed by combining two or more of the groups.
Specifically, methylene group, ethylene group, propane-1,3-diyl group, butane-1,4-diyl group, pentane-1,5-diyl group, hexane-1,6-diyl group, heptane-1 , 7-diyl group, octane-1,8-diyl group, nonane-1,9-diyl group, decane-1,10-diyl group, undecane-1,11-diyl group, dodecane-1,12-diyl group , Tridecane-1,13-diyl group, tetradecane-1,14-diyl group, pentadecane-1,15-diyl group, hexadecane-1,16-diyl group and heptadecane-1,17-diyl group Alkanediyl group;
Ethane-1,1-diyl group, propane-1,1-diyl group, propane-1,2-diyl group, propane-2,2-diyl group, pentane-2,4-diyl group, 2-methylpropane- Branched alkanediyl groups such as 1,3-diyl group, 2-methylpropane-1,2-diyl group, pentane-1,4-diyl group, 2-methylbutane-1,4-diyl group;
Monocyclic 2 which is a cycloalkanediyl group such as cyclobutane-1,3-diyl group, cyclopentane-1,3-diyl group, cyclohexane-1,4-diyl group, cyclooctane-1,5-diyl group Valent alicyclic saturated hydrocarbon group;
Polycyclic divalent alicyclic saturated hydrocarbon such as norbornane-1,4-diyl group, norbornane-2,5-diyl group, adamantane-1,5-diyl group, adamantane-2,6-diyl group, etc. Groups and the like.

b1の2価の飽和炭化水素基に含まれる−CH−が−O−又は−CO−で置き換わった基としては、例えば、式(b1−1)〜式(b1−3)のいずれかで表される基が挙げられる。なお、式(b1−1)〜式(b1−3)及び下記の具体例において、*は−Yとの結合手を表す。

Figure 2017105770
[式(b1−1)中、
b2は、単結合又は炭素数1〜22の2価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子に置換されていてもよい。
b3は、単結合又は炭素数1〜22の2価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよく、該飽和炭化水素基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよい。
ただし、Lb2とLb3との炭素数合計は、22以下である。
式(b1−2)中、
b4は、単結合又は炭素数1〜22の2価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子に置換されていてもよい。
b5は、単結合又は炭素数1〜22の2価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよく、該飽和炭化水素基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよい。
ただし、Lb4とLb5との炭素数合計は、22以下である。
式(b1−3)中、
b6は、単結合又は炭素数1〜23の2価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよい。
b7は、単結合又は炭素数1〜23の2価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよく、該飽和炭化水素基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよい。
ただし、Lb6とLb7との炭素数合計は、23以下である。] Examples of the group in which —CH 2 — contained in the divalent saturated hydrocarbon group of L b1 is replaced by —O— or —CO— include any of formulas (b1-1) to (b1-3) The group represented by these is mentioned. In the formulas (b1-1) to (b1-3) and the following specific examples, * represents a bond with -Y.
Figure 2017105770
[In the formula (b1-1),
L b2 represents a single bond or a divalent saturated hydrocarbon group having 1 to 22 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom.
L b3 represents a single bond or a divalent saturated hydrocarbon group having 1 to 22 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group, and the saturated The methylene group contained in the hydrocarbon group may be replaced with an oxygen atom or a carbonyl group.
However, the total number of carbon atoms of L b2 and L b3 is 22 or less.
In formula (b1-2),
L b4 represents a single bond or a divalent saturated hydrocarbon group having 1 to 22 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom.
L b5 represents a single bond or a divalent saturated hydrocarbon group having 1 to 22 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group, and the saturated The methylene group contained in the hydrocarbon group may be replaced with an oxygen atom or a carbonyl group.
However, the total number of carbon atoms of L b4 and L b5 is 22 or less.
In formula (b1-3),
L b6 represents a single bond or a divalent saturated hydrocarbon group having 1 to 23 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group.
L b7 represents a single bond or a divalent saturated hydrocarbon group having 1 to 23 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group, and the saturated The methylene group contained in the hydrocarbon group may be replaced with an oxygen atom or a carbonyl group.
However, the total number of carbon atoms of L b6 and L b7 is 23 or less. ]

式(b1−1)〜式(b1−3)においては、飽和炭化水素基に含まれるメチレン基が酸素原子又はカルボニル基に置き換わっている場合、置き換わる前の炭素数を該飽和炭化水素基の炭素数とする。
2価の飽和炭化水素基としては、Lb1の2価の飽和炭化水素基と同様のものが挙げられる。
In Formula (b1-1) to Formula (b1-3), when the methylene group contained in the saturated hydrocarbon group is replaced with an oxygen atom or a carbonyl group, the number of carbons before the replacement is represented by the carbon number of the saturated hydrocarbon group. It is a number.
Examples of the divalent saturated hydrocarbon group include those similar to the divalent saturated hydrocarbon group of L b1 .

b2は、好ましくは単結合である。
b3は、好ましくは炭素数1〜4の2価の飽和炭化水素基である。
b4は、好ましくは炭素数1〜8の2価の飽和炭化水素基であり、該2価の飽和炭化水素基に含まれる水素原子はフッ素原子に置換されていてもよい。
b5は、好ましくは単結合又は炭素数1〜8の2価の飽和炭化水素基である。
b6は、好ましくは単結合又は炭素数1〜4の2価の飽和炭化水素基であり、該飽和炭化水素基に含まれる水素原子はフッ素原子に置換されていてもよい。
b7は、好ましくは単結合又は炭素数1〜18の2価の飽和炭化水素基であり、該飽和炭化水素基に含まれる水素原子はフッ素原子又はヒドロキシ基に置換されていてもよく、該2価の飽和炭化水素基に含まれるメチレン基は酸素原子又はカルボニル基に置き換わっていてもよい。
L b2 is preferably a single bond.
L b3 is preferably a divalent saturated hydrocarbon group having 1 to 4 carbon atoms.
L b4 is preferably a divalent saturated hydrocarbon group having 1 to 8 carbon atoms, and the hydrogen atom contained in the divalent saturated hydrocarbon group may be substituted with a fluorine atom.
L b5 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 8 carbon atoms.
L b6 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 4 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom.
L b7 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 18 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group, The methylene group contained in the divalent saturated hydrocarbon group may be replaced with an oxygen atom or a carbonyl group.

b1の2価の飽和炭化水素基に含まれる−CH−が−O−又は−CO−で置き換わった基としては、式(b1−1)又は式(b1−3)で表される基が好ましい。 As the group in which —CH 2 — contained in the divalent saturated hydrocarbon group of L b1 is replaced by —O— or —CO—, a group represented by the formula (b1-1) or the formula (b1-3) Is preferred.

式(b1−1)としては、式(b1−4)〜式(b1−8)でそれぞれ表される基が挙げられる。

Figure 2017105770
[式(b1−4)中、
b8は、単結合又は炭素数1〜22の2価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよい。
式(b1−5)中、
b9は、炭素数1〜20の2価の飽和炭化水素基を表す。
b10は、単結合又は炭素数1〜19の2価の飽和炭化水素基を表し、該2価の飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよい。
ただし、Lb9及びLb10の合計炭素数は20以下である。
式(b1−6)中、
b11は、炭素数1〜21の2価の飽和炭化水素基を表す。
b12は、単結合又は炭素数1〜20の2価の飽和炭化水素基を表し、該2価の飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよい。
ただし、Lb11及びLb12の合計炭素数は21以下である。
式(b1−7)中、
b13は、炭素数1〜19の2価の飽和炭化水素基を表す。
b14は、単結合又は炭素数1〜18の2価の飽和炭化水素基を表す。
b15は、単結合又は炭素数1〜18の2価の飽和炭化水素基を表し、該2価の飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよい。
ただし、Lb13〜Lb15の合計炭素数は19以下である。
式(b1−8)中、
b16は、炭素数1〜18の2価の飽和炭化水素基を表す。
b17は、炭素数1〜18の2価の飽和炭化水素基を表す。
b18は、単結合又は炭素数1〜17の2価の飽和炭化水素基を表し、該2価の飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよい。
ただし、Lb16〜Lb18の合計炭素数は19以下である。] Examples of formula (b1-1) include groups represented by formula (b1-4) to formula (b1-8).
Figure 2017105770
[In the formula (b1-4),
L b8 represents a single bond or a divalent saturated hydrocarbon group having 1 to 22 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group.
In formula (b1-5),
Lb9 represents a C1-C20 bivalent saturated hydrocarbon group.
L b10 represents a single bond or a divalent saturated hydrocarbon group having 1 to 19 carbon atoms, and the hydrogen atom contained in the divalent saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group. .
However, the total carbon number of L b9 and L b10 is 20 or less.
In formula (b1-6),
L b11 represents a C1-C21 divalent saturated hydrocarbon group.
L b12 represents a single bond or a divalent saturated hydrocarbon group having 1 to 20 carbon atoms, and the hydrogen atom contained in the divalent saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group. .
However, the total carbon number of L b11 and L b12 is 21 or less.
In formula (b1-7),
L b13 represents a divalent saturated hydrocarbon group having 1 to 19 carbon atoms.
L b14 represents a single bond or a divalent saturated hydrocarbon group having 1 to 18 carbon atoms.
L b15 represents a single bond or a divalent saturated hydrocarbon group having 1 to 18 carbon atoms, and the hydrogen atom contained in the divalent saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group. .
However, the total carbon number of L b13 to L b15 is 19 or less.
In formula (b1-8),
L b16 represents a C1-C18 divalent saturated hydrocarbon group.
L b17 represents a C1- C18 divalent saturated hydrocarbon group.
L b18 represents a single bond or a divalent saturated hydrocarbon group having 1 to 17 carbon atoms, and the hydrogen atom contained in the divalent saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group. .
However, the total carbon number of L b16 to L b18 is 19 or less. ]

b8は、好ましくは炭素数1〜4の2価の飽和炭化水素基である。
b9は、好ましくは炭素数1〜8の2価の飽和炭化水素基である。
b10は、好ましくは単結合又は炭素数1〜19の2価の飽和炭化水素基であり、より好ましくは単結合又は炭素数1〜8の2価の飽和炭化水素基である。
b11は、好ましくは炭素数1〜8の2価の飽和炭化水素基である。
b12は、好ましくは単結合又は炭素数1〜8の2価の飽和炭化水素基である。
b13は、好ましくは炭素数1〜12の2価の飽和炭化水素基である。
b14は、好ましくは単結合又は炭素数1〜6の2価の飽和炭化水素基である。
b15は、好ましくは単結合又は炭素数1〜18の2価の飽和炭化水素基であり、より好ましくは単結合又は炭素数1〜8の2価の飽和炭化水素基である。
b16は、好ましくは炭素数1〜12の2価の飽和炭化水素基である。
b17は、好ましくは炭素数1〜6の2価の飽和炭化水素基である。
b18は、好ましくは単結合又は炭素数1〜17の2価の飽和炭化水素基であり、より好ましくは単結合又は炭素数1〜4の2価の飽和炭化水素基である。
L b8 is preferably a divalent saturated hydrocarbon group having 1 to 4 carbon atoms.
L b9 is preferably a C 1-8 divalent saturated hydrocarbon group.
L b10 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 19 carbon atoms, and more preferably a single bond or a divalent saturated hydrocarbon group having 1 to 8 carbon atoms.
L b11 is preferably a divalent saturated hydrocarbon group having 1 to 8 carbon atoms.
L b12 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 8 carbon atoms.
L b13 is preferably a divalent saturated hydrocarbon group having 1 to 12 carbon atoms.
L b14 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 6 carbon atoms.
L b15 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 18 carbon atoms, and more preferably a single bond or a divalent saturated hydrocarbon group having 1 to 8 carbon atoms.
L b16 is preferably a divalent saturated hydrocarbon group having 1 to 12 carbon atoms.
L b17 is preferably a C 1-6 divalent saturated hydrocarbon group.
L b18 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 17 carbon atoms, and more preferably a single bond or a divalent saturated hydrocarbon group having 1 to 4 carbon atoms.

式(b1−3)としては、式(b1−9)〜式(b1−11)でそれぞれ表される基が挙げられる。

Figure 2017105770
[式(b1−9)中、
b19は、単結合又は炭素数1〜23の2価の飽和炭化水素基を表し、該2価の飽和炭化水素基に含まれる水素原子は、フッ素原子に置換されていてもよい。
b20は、単結合又は炭素数1〜23の2価の飽和炭化水素基を表し、該2価の飽和炭化水素基に含まれる水素原子はフッ素原子、ヒドロキシ基又はアシルオキシ基に置換されていてもよい。該アシルオキシ基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよく、該アシルオキシ基に含まれる水素原子は、ヒドロキシ基に置換されていてもよい。
ただし、Lb19及びLb20の合計炭素数は23以下である。
式(b1−10)中、
b21は、単結合又は炭素数1〜21の2価の飽和炭化水素基を表し、該2価の飽和炭化水素基に含まれる水素原子は、フッ素原子に置換されていてもよい。
b22は、単結合又は炭素数1〜21の2価の飽和炭化水素基を表す。
b23は、単結合又は炭素数1〜21の2価の飽和炭化水素基を表し、該2価の飽和炭化水素基に含まれる水素原子は、フッ素原子、ヒドロキシ基又はアシルオキシ基に置換されていてもよい。該アシルオキシ基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよく、該アシルオキシ基に含まれる水素原子は、ヒドロキシ基に置換されていてもよい。
ただし、Lb21〜Lb23の合計炭素数は21以下である。
式(b1−11)中、
b24は、単結合又は炭素数1〜20の2価の飽和炭化水素基を表し、該2価の飽和炭化水素基に含まれる水素原子は、フッ素原子に置換されていてもよい。
b25は、炭素数1〜21の2価の飽和炭化水素基を表す。
b26は、単結合又は炭素数1〜20の2価の飽和炭化水素基を表し、該2価の飽和炭化水素基に含まれる水素原子は、フッ素原子、ヒドロキシ基又はアシルオキシ基に置換されていてもよい。該アシルオキシ基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよく、該アシルオキシ基に含まれる水素原子は、ヒドロキシ基に置換されていてもよい。
ただし、Lb24〜Lb26の合計炭素数は21以下である。] Examples of formula (b1-3) include groups represented by formula (b1-9) to formula (b1-11), respectively.
Figure 2017105770
[In the formula (b1-9),
L b19 represents a single bond or a C1-C23 divalent saturated hydrocarbon group, and the hydrogen atom contained in the divalent saturated hydrocarbon group may be substituted with a fluorine atom.
L b20 represents a single bond or a divalent saturated hydrocarbon group having 1 to 23 carbon atoms, and the hydrogen atom contained in the divalent saturated hydrocarbon group is substituted with a fluorine atom, a hydroxy group, or an acyloxy group. Also good. The methylene group contained in the acyloxy group may be replaced with an oxygen atom or a carbonyl group, and the hydrogen atom contained in the acyloxy group may be substituted with a hydroxy group.
However, the total carbon number of L b19 and L b20 is 23 or less.
In formula (b1-10),
L b21 represents a single bond or a C1-C21 divalent saturated hydrocarbon group, and the hydrogen atom contained in the divalent saturated hydrocarbon group may be substituted with a fluorine atom.
L b22 represents a single bond or a divalent saturated hydrocarbon group having 1 to 21 carbon atoms.
L b23 represents a single bond or a divalent saturated hydrocarbon group having 1 to 21 carbon atoms, and the hydrogen atom contained in the divalent saturated hydrocarbon group is substituted with a fluorine atom, a hydroxy group, or an acyloxy group. May be. The methylene group contained in the acyloxy group may be replaced with an oxygen atom or a carbonyl group, and the hydrogen atom contained in the acyloxy group may be substituted with a hydroxy group.
However, the total carbon number of L b21 to L b23 is 21 or less.
In formula (b1-11),
L b24 represents a single bond or a divalent saturated hydrocarbon group having 1 to 20 carbon atoms, and the hydrogen atom contained in the divalent saturated hydrocarbon group may be substituted with a fluorine atom.
L b25 represents a divalent saturated hydrocarbon group having 1 to 21 carbon atoms.
L b26 represents a single bond or a divalent saturated hydrocarbon group having 1 to 20 carbon atoms, and the hydrogen atom contained in the divalent saturated hydrocarbon group is substituted with a fluorine atom, a hydroxy group, or an acyloxy group. May be. The methylene group contained in the acyloxy group may be replaced with an oxygen atom or a carbonyl group, and the hydrogen atom contained in the acyloxy group may be substituted with a hydroxy group.
However, the total number of carbon atoms of L b24 ~L b26 is 21 or less. ]

式(b1−9)から式(b1−11)においては、2価の飽和炭化水素基に含まれる水素原子がアシルオキシ基に置換されている場合、アシルオキシ基の炭素数、エステル結合中のCO及びOの数をも含めて、該2価の飽和炭化水素基の炭素数とする。   In formulas (b1-9) to (b1-11), when a hydrogen atom contained in a divalent saturated hydrocarbon group is substituted with an acyloxy group, the number of carbon atoms in the acyloxy group, CO in the ester bond, and The number of carbon atoms of the divalent saturated hydrocarbon group including the number of O is used.

アシルオキシ基としては、アセチルオキシ基、プロピオニルオキシ基、ブチリルオキシ基、シクロヘキシルカルボニルオキシ基、アダマンチルカルボニルオキシ基等が挙げられる。
置換基を有するアシルオキシ基としては、オキソアダマンチルカルボニルオキシ基、ヒドロキシアダマンチルカルボニルオキシ基、オキソシクロヘキシルカルボニルオキシ基、ヒドロキシシクロヘキシルカルボニルオキシ基等が挙げられる。
Examples of the acyloxy group include an acetyloxy group, a propionyloxy group, a butyryloxy group, a cyclohexylcarbonyloxy group, and an adamantylcarbonyloxy group.
Examples of the acyloxy group having a substituent include an oxoadamantylcarbonyloxy group, a hydroxyadamantylcarbonyloxy group, an oxocyclohexylcarbonyloxy group, and a hydroxycyclohexylcarbonyloxy group.

式(b1−1)で表される基のうち、式(b1−4)で表される基としては、以下のものが挙げられる。

Figure 2017105770
Of the groups represented by formula (b1-1), examples of the group represented by formula (b1-4) include the following.
Figure 2017105770

式(b1−1)で表される基のうち、式(b1−5)で表される基としては、以下のものが挙げられる。

Figure 2017105770
Of the groups represented by the formula (b1-1), examples of the group represented by the formula (b1-5) include the following.
Figure 2017105770

式(b1−1)で表される基のうち、式(b1−6)で表される基としては、以下のものが挙げられる。

Figure 2017105770
Of the groups represented by formula (b1-1), examples of the group represented by formula (b1-6) include the following.
Figure 2017105770

式(b1−1)で表される基のうち、式(b1−7)で表される基としては、以下のものが挙げられる。

Figure 2017105770
Of the groups represented by the formula (b1-1), examples of the group represented by the formula (b1-7) include the following.
Figure 2017105770

式(b1−1)で表される基のうち、式(b1−8)で表される基としては、以下のものが挙げられる。

Figure 2017105770
Of the groups represented by the formula (b1-1), examples of the group represented by the formula (b1-8) include the following.
Figure 2017105770

式(b1−2)で表される基としては、以下のものが挙げられる。

Figure 2017105770
Examples of the group represented by the formula (b1-2) include the following.
Figure 2017105770

式(b1−3)で表される基のうち、式(b1−9)で表される基としては、以下のものが挙げられる。

Figure 2017105770
Of the groups represented by formula (b1-3), examples of the group represented by formula (b1-9) include the following.
Figure 2017105770

式(b1−3)で表される基のうち、式(b1−10)で表される基としては、以下のものが挙げられる。

Figure 2017105770
Of the groups represented by the formula (b1-3), examples of the group represented by the formula (b1-10) include the following.
Figure 2017105770

Figure 2017105770
Figure 2017105770

式(b1−3)で表される基のうち、式(b1−11)で表される基としては、以下のものが挙げられる。

Figure 2017105770
Of the groups represented by formula (b1-3), examples of the group represented by formula (b1-11) include the following.
Figure 2017105770

Yで表される1価の脂環式炭化水素基としては、式(Y1)〜式(Y11)で表される基が挙げられる。
Yで表される1価の脂環式炭化水素基に含まれる−CH−が−O−、−SO−又は−CO−で置き換わる場合、その数は1つでもよいし、2以上の複数でもよい。そのような基としては、式(Y12)〜式(Y35)で表される基が挙げられる。
Examples of the monovalent alicyclic hydrocarbon group represented by Y include groups represented by formulas (Y1) to (Y11).
When —CH 2 — contained in the monovalent alicyclic hydrocarbon group represented by Y is replaced by —O—, —SO 2 — or —CO—, the number may be one, or two or more There may be multiple. Examples of such a group include groups represented by formula (Y12) to formula (Y35).

Figure 2017105770
Figure 2017105770

Figure 2017105770
Figure 2017105770

つまり、Yは、脂環式炭化水素基に含まれる水素原子2つがそれぞれ、酸素原子に置換され、その2つの酸素原子が炭素数1〜8のアルカンジイル基と一緒になってケタール環を形成してもよいし、異なる炭素原子にそれぞれ酸素原子が結合した構造を含んでいてもよい。ただし、式(Y28)〜式(Y38)等のスピロ環を構成する場合には、2つの酸素間のアルカンジイル基は、1以上のフッ素原子を有することが好ましい。また、ケタール構造に含まれるアルカンジイル基のうち、酸素原子に隣接するメチレン基には、フッ素原子が置換されていないものが好ましい。   That is, Y represents a hydrogen atom contained in an alicyclic hydrocarbon group, each substituted with an oxygen atom, and the two oxygen atoms together with an alkanediyl group having 1 to 8 carbon atoms form a ketal ring. Alternatively, a structure in which an oxygen atom is bonded to each of different carbon atoms may be included. However, in the case of constituting a spiro ring such as formula (Y28) to formula (Y38), the alkanediyl group between two oxygens preferably has one or more fluorine atoms. Of the alkanediyl groups contained in the ketal structure, those in which the methylene group adjacent to the oxygen atom is not substituted with a fluorine atom are preferred.

中でも、好ましくは式(Y1)〜式(Y20)、式(Y30)、式(Y31)のいずれかで表される基が挙げられ、より好ましくは式(Y11)、式(Y15)、式(Y16)、式(Y20)、式(Y30)又は式(Y31)で表される基が挙げられ、さらに好ましくは式(Y11)、式(Y15)又は式(Y30)で表される基が挙げられる。   Among them, a group represented by any one of Formula (Y1) to Formula (Y20), Formula (Y30), and Formula (Y31) is preferable, and Formula (Y11), Formula (Y15), and Formula (Y Y16), a group represented by the formula (Y20), a formula (Y30) or a formula (Y31) can be mentioned, and a group represented by the formula (Y11), the formula (Y15) or the formula (Y30) is more preferable. It is done.

Yで表されるメチル基の置換基としては、ハロゲン原子、ヒドロキシ基、炭素数3〜16の1価のn脂環式炭化水素基、炭素数6〜18の1価の芳香族炭化水素基、グリシジルオキシ基又は−(CHja−O−CO−Rb1基(式中、Rb1は、炭素数1〜16のアルキル基、炭素数3〜16の1価の脂環式炭化水素基又は炭素数6〜18の1価の芳香族炭化水素基を表す。jaは、0〜4の整数を表す)等が挙げられる。
Yで表される1価の脂環式炭化水素基の置換基としては、ハロゲン原子、ヒドロキシ基、炭素数1〜12のアルキル基、ヒドロキシ基含有炭素数1〜12のアルキル基、炭素数3〜16の1価の脂環式炭化水素基、炭素数1〜12のアルコキシ基、炭素数6〜18の1価の芳香族炭化水素基、炭素数7〜21のアラルキル基、炭素数2〜4のアシル基、グリシジルオキシ基又は−(CHja−O−CO−Rb1基(式中、Rb1は、炭素数1〜16のアルキル基、炭素数3〜16の1価の脂環式炭化水素基又は炭素数6〜18の1価の芳香族炭化水素基を表す。jaは、0〜4の整数を表す)等が挙げられる。
Examples of the substituent of the methyl group represented by Y include a halogen atom, a hydroxy group, a monovalent n-alicyclic hydrocarbon group having 3 to 16 carbon atoms, and a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms. , A glycidyloxy group or — (CH 2 ) ja —O—CO—R b1 group (wherein R b1 is an alkyl group having 1 to 16 carbon atoms and a monovalent alicyclic hydrocarbon having 3 to 16 carbon atoms) Represents a group or a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms, and ja represents an integer of 0 to 4).
Examples of the substituent for the monovalent alicyclic hydrocarbon group represented by Y include a halogen atom, a hydroxy group, an alkyl group having 1 to 12 carbon atoms, a hydroxy group-containing alkyl group having 1 to 12 carbon atoms, and 3 carbon atoms. -16 monovalent alicyclic hydrocarbon group, C1-C12 alkoxy group, C6-C18 monovalent aromatic hydrocarbon group, C7-C21 aralkyl group, C2-C2 4 acyl group, glycidyloxy group or — (CH 2 ) ja —O—CO—R b1 group (wherein R b1 is an alkyl group having 1 to 16 carbon atoms, monovalent fat having 3 to 16 carbon atoms) Represents a cyclic hydrocarbon group or a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms, and ja represents an integer of 0 to 4).

ヒドロキシ基含有アルキル基としては、ヒドロキシメチル基、ヒドロキシエチル基等が挙げられる。
アルコキシ基としては、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基、ペンチルオキシ基、ヘキシルオキシ基、ヘプチルオキシ基、オクチルオキシ基、デシルオキシ基及びドデシルオキシ基等が挙げられる。
1価の芳香族炭化水素基としては、フェニル基、ナフチル基、アントリル基、p−メチルフェニル基、p−tert−ブチルフェニル基、p−アダマンチルフェニル基;トリル基、キシリル基、クメニル基、メシチル基、ビフェニル基、フェナントリル基、2,6−ジエチルフェニル基、2−メチル−6−エチルフェニル等のアリール基等が挙げられる。
アラルキル基としては、ベンジル基、フェネチル基、フェニルプロピル基、ナフチルメチル基及びナフチルエチル基等が挙げられる。
アシル基としては、例えば、アセチル基、プロピオニル基及びブチリル基等が挙げられる。
ハロゲン原子としては、フッ素原子、塩素原子、臭素原子及びヨウ素原子等が挙げられる。
Examples of the hydroxy group-containing alkyl group include a hydroxymethyl group and a hydroxyethyl group.
Examples of the alkoxy group include methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, heptyloxy group, octyloxy group, decyloxy group and dodecyloxy group.
Examples of the monovalent aromatic hydrocarbon group include phenyl group, naphthyl group, anthryl group, p-methylphenyl group, p-tert-butylphenyl group, p-adamantylphenyl group; tolyl group, xylyl group, cumenyl group, mesityl group. Groups, biphenyl groups, phenanthryl groups, 2,6-diethylphenyl groups, aryl groups such as 2-methyl-6-ethylphenyl, and the like.
Examples of the aralkyl group include benzyl group, phenethyl group, phenylpropyl group, naphthylmethyl group, and naphthylethyl group.
Examples of the acyl group include an acetyl group, a propionyl group, and a butyryl group.
Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom.

Yとしては、以下のものが挙げられる。

Figure 2017105770
Examples of Y include the following.
Figure 2017105770

なお、Yがメチル基であり、かつLb1が炭素数1〜17の2価の直鎖状又は分岐状飽和炭化水素基である場合、Yとの結合位置にある該2価の飽和炭化水素基の−CH−は、−O−又は−CO−に置き換わっていることが好ましい。この場合、Yのアルキル基に含まれる−CH−は、−O−又は−CO−に置き換わらない。 In addition, when Y is a methyl group and L b1 is a C1-C17 divalent linear or branched saturated hydrocarbon group, the divalent saturated hydrocarbon at the bonding position with Y The group —CH 2 — is preferably replaced by —O— or —CO—. In this case, —CH 2 — contained in the alkyl group of Y is not replaced with —O— or —CO—.

Yは、好ましくは置換基を有していてもよい炭素数3〜18の1価の脂環式炭化水素基であり、より好ましく置換基を有していてもよいアダマンチル基であり、これらの基を構成するメチレン基は、酸素原子、スルホニル基又はカルボニル基に置き換わっていてもよい。Yは、さらに好ましくはアダマンチル基、ヒドロキシアダマンチル基又はオキソアダマンチル基又は下記で表される基である。

Figure 2017105770
Y is preferably a monovalent alicyclic hydrocarbon group having 3 to 18 carbon atoms which may have a substituent, and more preferably an adamantyl group which may have a substituent. The methylene group constituting the group may be replaced with an oxygen atom, a sulfonyl group or a carbonyl group. Y is more preferably an adamantyl group, a hydroxyadamantyl group, an oxoadamantyl group, or a group represented by the following.
Figure 2017105770

式(B1)で表される塩におけるスルホン酸アニオンとしては、式(B1−A−1)〜式(B1−A−46)で表されるアニオン〔以下、式番号に応じて「アニオン(B1−A−1)」等という場合がある。〕が好ましく、式(B1−A−1)〜式(B1−A−4)、式(B1−A−9)、式(B1−A−10)、式(B1−A−24)〜式(B1−A−33)、式(B1−A−36)〜式(B1−A−40)のいずれかで表されるアニオンがより好ましい。

Figure 2017105770
As the sulfonate anion in the salt represented by the formula (B1), an anion represented by the formula (B1-A-1) to the formula (B1-A-46) [hereinafter, anion (B1 -A-1) "or the like. ] Is preferable, Formula (B1-A-1)-Formula (B1-A-4), Formula (B1-A-9), Formula (B1-A-10), Formula (B1-A-24)-Formula An anion represented by any one of (B1-A-33) and formulas (B1-A-36) to (B1-A-40) is more preferable.
Figure 2017105770

Figure 2017105770
Figure 2017105770

Figure 2017105770
Figure 2017105770

Figure 2017105770
Figure 2017105770

Figure 2017105770
Figure 2017105770

Figure 2017105770
Figure 2017105770

Figure 2017105770
Figure 2017105770

Figure 2017105770
Figure 2017105770

ここでRi2〜Ri7は、例えば、炭素数1〜4のアルキル基、好ましくはメチル基又はエチル基である。
i8は、例えば、炭素数1〜12の脂肪族炭化水素基であり、好ましくは炭素数1〜4のアルキル基、炭素数5〜12の1価の脂環式炭化水素基又はこれらを組合せることにより形成される基であり、より好ましくはメチル基、エチル基、シクロヘキシル基又はアダマンチル基である。
は、単結合又は炭素数1〜4のアルカンジイル基である。
及びQは、上記と同じである。
式(B1)で表される塩におけるスルホン酸アニオンとしては、具体的には、特開2010−204646号公報に記載されたアニオンが挙げられる。
Here, R i2 to R i7 are, for example, an alkyl group having 1 to 4 carbon atoms, preferably a methyl group or an ethyl group.
R i8 is, for example, an aliphatic hydrocarbon group having 1 to 12 carbon atoms, preferably an alkyl group having 1 to 4 carbon atoms, a monovalent alicyclic hydrocarbon group having 5 to 12 carbon atoms, or a combination thereof. More preferably a methyl group, an ethyl group, a cyclohexyl group or an adamantyl group.
L 4 is a single bond or an alkanediyl group having 1 to 4 carbon atoms.
Q 1 and Q 2 are the same as described above.
Specific examples of the sulfonate anion in the salt represented by the formula (B1) include the anions described in JP 2010-204646 A.

好ましい式(B1)で表される塩におけるスルホン酸アニオンとしては、式(B1a−1)〜式(B1a−22)でそれぞれ表されるアニオンが挙げられる。

Figure 2017105770
Examples of the sulfonate anion in the salt represented by the preferable formula (B1) include anions represented by the formulas (B1a-1) to (B1a-22), respectively.
Figure 2017105770

Figure 2017105770
Figure 2017105770

なかでも、式(B1a−1)〜式(B1a−3)及び式(B1a−7)〜式(B1a−16)、式(B1a−18)、式(B1a−19)、式(B1a−22)のいずれかで表されるアニオンが好ましい。
の有機カチオンとしては、有機オニウムカチオン、例えば、有機スルホニウムカチオン、有機ヨードニウムカチオン、有機アンモニウムカチオン、ベンゾチアゾリウムカチオン、有機ホスホニウムカチオン等が挙げられ、好ましくは有機スルホニウムカチオン又は有機ヨードニウムカチオンが挙げられ、より好ましくはアリールスルホニウムカチオンが挙げられる。
式(B1)中のZは、好ましくは式(b2−1)〜式(b2−4)のいずれかで表されるカチオン〔以下、式番号に応じて「カチオン(b2−1)」等という場合がある。〕である。
Especially, Formula (B1a-1)-Formula (B1a-3) and Formula (B1a-7)-Formula (B1a-16), Formula (B1a-18), Formula (B1a-19), Formula (B1a-22) ) Is preferable.
Examples of the organic cation of Z + include organic onium cations such as organic sulfonium cation, organic iodonium cation, organic ammonium cation, benzothiazolium cation, and organic phosphonium cation, and preferably organic sulfonium cation or organic iodonium cation. More preferably, an arylsulfonium cation is mentioned.
Z + in the formula (B1) is preferably a cation represented by any one of the formulas (b2-1) to (b2-4) [hereinafter referred to as “cation (b2-1)” or the like depending on the formula number, etc. There is a case. ].

Figure 2017105770
[式(b2−1)〜式(b2−4)において、
b4〜Rb6は、互いに独立に、炭素数1〜30の1価の脂肪族炭化水素基、炭素数3〜36の1価の脂環式炭化水素基又は炭素数6〜36の1価の芳香族炭化水素基を表し、該1価の脂肪族炭化水素基に含まれる水素原子は、ヒドロキシ基、炭素数1〜12のアルコキシ基、炭素数3〜12の1価の脂環式炭化水素基又は炭素数6〜18の1価の芳香族炭化水素基で置換されていてもよく、該1価の脂環式炭化水素基に含まれる水素原子は、ハロゲン原子、炭素数1〜18の1価の脂肪族炭化水素基、炭素数2〜4のアシル基又はグリシジルオキシ基で置換されていてもよく、該1価の芳香族炭化水素基に含まれる水素原子は、ハロゲン原子、ヒドロキシ基又は炭素数1〜12のアルコキシ基で置換されていてもよい。
b4とRb5とは、それらが結合する硫黄原子とともに環を形成してもよく、該環に含まれる−CH−は、−O−、−SO−又は−CO−に置き換わってもよい。
b7及びRb8は、互いに独立に、ヒドロキシ基、炭素数1〜12の1価の脂肪族炭化水素基又は炭素数1〜12のアルコキシ基を表す。
m2及びn2は、互いに独立に、0〜5の整数を表す。
m2が2以上のとき、複数のRb7は同一であっても異なってもよく、n2が2以上のとき、複数のRb8は同一であっても異なってもよい。
b9及びRb10は、互いに独立に、炭素数1〜36の1価の脂肪族炭化水素基又は炭素数3〜36の1価の脂環式炭化水素基を表す。
b9とRb10とは、それらが結合する硫黄原子とともに環を形成してもよく、該環に含まれる−CH−は、−O−、−SO−又は−CO−に置き換わってもよい。
b11は、水素原子、炭素数1〜36の1価の脂肪族炭化水素基、炭素数3〜36の1価の脂環式炭化水素基又は炭素数6〜18の1価の芳香族炭化水素基を表す。
b12は、炭素数1〜12の1価の脂肪族炭化水素基、炭素数3〜18の1価の脂環式炭化水素基又は炭素数6〜18の1価の芳香族炭化水素基を表し、該1価の脂肪族炭化水素に含まれる水素原子は、炭素数6〜18の1価の芳香族炭化水素基で置換されていてもよく、該1価の芳香族炭化水素基に含まれる水素原子は、炭素数1〜12のアルコキシ基又は炭素数1〜12のアルキルカルボニルオキシ基で置換されていてもよい。
b11とRb12とは、一緒になってそれらが結合する−CH−CO−を含む環を形成していてもよく、該環に含まれる−CH−は、−O−、−SO−又は−CO−に置き換わってもよい。
b13〜Rb18は、互いに独立に、ヒドロキシ基、炭素数1〜12の1価の脂肪族炭化水素基又は炭素数1〜12のアルコキシ基を表す。
b31は、−S−又は−O−を表す。
o2、p2、s2、及びt2は、互いに独立に、0〜5の整数を表す。
q2及びr2は、互いに独立に、0〜4の整数を表す。
u2は、0又は1を表す。
o2が2以上のとき、複数のRb13は同一であっても異なってもよく、p2が2以上のとき、複数のRb14は同一であっても異なってもよく、q2が2以上のとき、複数のRb15は同一であっても異なってもよく、r2が2以上のとき、複数のRb16は同一であっても異なってもよく、s2が2以上のとき、複数のRb17は同一であっても異なってもよく、t2が2以上のとき、複数のRb18は同一であっても異なってもよい。]
Figure 2017105770
[In Formula (b2-1)-Formula (b2-4),
R b4 to R b6 are each independently a monovalent aliphatic hydrocarbon group having 1 to 30 carbon atoms, a monovalent alicyclic hydrocarbon group having 3 to 36 carbon atoms, or a monovalent group having 6 to 36 carbon atoms. The hydrogen atom contained in the monovalent aliphatic hydrocarbon group is a hydroxy group, an alkoxy group having 1 to 12 carbon atoms, or a monovalent alicyclic carbon group having 3 to 12 carbon atoms. It may be substituted with a hydrogen group or a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms, and the hydrogen atom contained in the monovalent alicyclic hydrocarbon group is a halogen atom or a carbon number 1 to 18 Which may be substituted with a monovalent aliphatic hydrocarbon group, an acyl group having 2 to 4 carbon atoms or a glycidyloxy group, the hydrogen atom contained in the monovalent aromatic hydrocarbon group is a halogen atom, hydroxy Group or an alkoxy group having 1 to 12 carbon atoms may be substituted.
R b4 and R b5 may form a ring together with the sulfur atom to which they are bonded, and —CH 2 — contained in the ring may be replaced with —O—, —SO— or —CO—. .
R b7 and R b8 each independently represent a hydroxy group, a monovalent aliphatic hydrocarbon group having 1 to 12 carbon atoms, or an alkoxy group having 1 to 12 carbon atoms.
m2 and n2 represent the integer of 0-5 independently of each other.
When m2 is 2 or more, the plurality of R b7 may be the same or different, and when n2 is 2 or more, the plurality of R b8 may be the same or different.
R b9 and R b10 each independently represent a monovalent aliphatic hydrocarbon group having 1 to 36 carbon atoms or a monovalent alicyclic hydrocarbon group having 3 to 36 carbon atoms.
R b9 and R b10 may form a ring together with the sulfur atom to which they are bonded, and —CH 2 — contained in the ring may be replaced with —O—, —SO— or —CO—. .
R b11 represents a hydrogen atom, a monovalent aliphatic hydrocarbon group having 1 to 36 carbon atoms, a monovalent alicyclic hydrocarbon group having 3 to 36 carbon atoms, or a monovalent aromatic carbon group having 6 to 18 carbon atoms. Represents a hydrogen group.
R b12 represents a monovalent aliphatic hydrocarbon group having 1 to 12 carbon atoms, a monovalent alicyclic hydrocarbon group having 3 to 18 carbon atoms, or a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms. And a hydrogen atom contained in the monovalent aliphatic hydrocarbon may be substituted with a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms, and is contained in the monovalent aromatic hydrocarbon group The hydrogen atom to be substituted may be substituted with an alkoxy group having 1 to 12 carbon atoms or an alkylcarbonyloxy group having 1 to 12 carbon atoms.
R b11 and R b12 may together form a ring containing —CH—CO— to which they are bonded, and —CH 2 — contained in the ring is —O—, —SO—. Alternatively, it may be replaced by -CO-.
R b13 to R b18 each independently represent a hydroxy group, a monovalent aliphatic hydrocarbon group having 1 to 12 carbon atoms, or an alkoxy group having 1 to 12 carbon atoms.
L b31 represents -S- or -O-.
o2, p2, s2, and t2 each independently represent an integer of 0 to 5.
q2 and r2 each independently represents an integer of 0 to 4.
u2 represents 0 or 1.
When o2 is 2 or more, the plurality of R b13 may be the same or different. When p2 is 2 or more, the plurality of R b14 may be the same or different. When q2 is 2 or more The plurality of R b15 may be the same or different. When r2 is 2 or more, the plurality of R b16 may be the same or different. When s2 is 2 or more, the plurality of R b17 is They may be the same or different, and when t2 is 2 or more, the plurality of R b18 may be the same or different. ]

1価の脂肪族炭化水素基としては、メチル基、エチル基、n−プロピル基、イソプロピル基、n−ブチル基、sec−ブチル基、tert−ブチル基、ペンチル基、ヘキシル基、オクチル基及び2−エチルヘキシル基のアルキル基が挙げられる。中でも、Rb9〜Rb12の1価の脂肪族炭化水素基は、好ましくは炭素数1〜12である。
1価の脂環式炭化水素基は、単環式又は多環式のいずれでもよく、単環式の1価の脂環式炭化水素基としては、シクロプロピル基、シクロブチル基、シクロペンチル基、シクロへキシル基、シクロヘプチル基、シクロオクチル基、シクロデシル基等のシクロアルキル基が挙げられる。多環式の1価の脂環式炭化水素基としては、デカヒドロナフチル基、アダマンチル基、ノルボルニル基及び下記の基等が挙げられる。

Figure 2017105770
中でも、Rb9〜Rb12の1価の脂環式炭化水素基の炭素数は、好ましくは3〜18であり、より好ましくは4〜12である。 Monovalent aliphatic hydrocarbon groups include methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, pentyl, hexyl, octyl and 2 -The alkyl group of an ethylhexyl group is mentioned. Among these, the monovalent aliphatic hydrocarbon group of R b9 to R b12 preferably has 1 to 12 carbon atoms.
The monovalent alicyclic hydrocarbon group may be either monocyclic or polycyclic, and examples of the monocyclic monovalent alicyclic hydrocarbon group include a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclo And cycloalkyl groups such as a hexyl group, a cycloheptyl group, a cyclooctyl group, and a cyclodecyl group. Examples of the polycyclic monovalent alicyclic hydrocarbon group include a decahydronaphthyl group, an adamantyl group, a norbornyl group, and the following groups.
Figure 2017105770
Among them, the number of carbon atoms of the monovalent alicyclic hydrocarbon group R b9 to R b12 is preferably 3 to 18, more preferably from 4 to 12.

水素原子が脂肪族炭化水素基で置換された1価の脂環式炭化水素基としては、例えば、メチルシクロヘキシル基、ジメチルシクロへキシル基、2−アルキルアダマンタン−2−イル基、メチルノルボルニル基、イソボルニル基等が挙げられる。水素原子が1価の脂肪族炭化水素基で置換された1価の脂環式炭化水素基においては、1価の脂環式炭化水素基と1価の脂肪族炭化水素基との合計炭素数が好ましくは20以下である。   Examples of the monovalent alicyclic hydrocarbon group in which a hydrogen atom is substituted with an aliphatic hydrocarbon group include a methylcyclohexyl group, a dimethylcyclohexyl group, a 2-alkyladamantan-2-yl group, and a methylnorbornyl group. Group, isobornyl group and the like. In the monovalent alicyclic hydrocarbon group in which the hydrogen atom is substituted with a monovalent aliphatic hydrocarbon group, the total number of carbon atoms of the monovalent alicyclic hydrocarbon group and the monovalent aliphatic hydrocarbon group Is preferably 20 or less.

1価の芳香族炭化水素基としては、フェニル基、トリル基、キシリル基、クメニル基、メシチル基、p−エチルフェニル基、p−tert−ブチルフェニル基、p−シクロへキシルフェニル基、p−アダマンチルフェニル基、ビフェニリル基、ナフチル基、フェナントリル基、2,6−ジエチルフェニル基、2−メチル−6−エチルフェニル基等のアリール基が挙げられる。
1価の芳香族炭化水素基に、1価の脂肪族炭化水素基又は1価の脂環式炭化水素基が含まれる場合は、炭素数1〜18の1価の脂肪族炭化水素基または炭素数3〜18の1価の脂環式炭化水素基が好ましい。
水素原子がアルコキシ基で置換された1価の芳香族炭化水素基としては、p−メトキシフェニル基等が挙げられる。
水素原子が芳香族炭化水素基で置換された1価の脂肪族炭化水素基としては、ベンジル基、フェネチル基、フェニルプロピル基、トリチル基、ナフチルメチル基、ナフチルエチル基等のアラルキル基が挙げられる。
Examples of the monovalent aromatic hydrocarbon group include phenyl group, tolyl group, xylyl group, cumenyl group, mesityl group, p-ethylphenyl group, p-tert-butylphenyl group, p-cyclohexylphenyl group, p- Examples thereof include aryl groups such as an adamantylphenyl group, a biphenylyl group, a naphthyl group, a phenanthryl group, a 2,6-diethylphenyl group, and a 2-methyl-6-ethylphenyl group.
When the monovalent aromatic hydrocarbon group includes a monovalent aliphatic hydrocarbon group or a monovalent alicyclic hydrocarbon group, the monovalent aliphatic hydrocarbon group or carbon having 1 to 18 carbon atoms A monovalent alicyclic hydrocarbon group having a number of 3 to 18 is preferred.
Examples of the monovalent aromatic hydrocarbon group in which a hydrogen atom is substituted with an alkoxy group include a p-methoxyphenyl group.
Examples of the monovalent aliphatic hydrocarbon group in which a hydrogen atom is substituted with an aromatic hydrocarbon group include aralkyl groups such as a benzyl group, a phenethyl group, a phenylpropyl group, a trityl group, a naphthylmethyl group, and a naphthylethyl group. .

アルコキシ基としては、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基、ペンチルオキシ基、ヘキシルオキシ基、ヘプチルオキシ基、オクチルオキシ基、デシルオキシ基及びドデシルオキシ基等が挙げられる。
アシル基としては、アセチル基、プロピオニル基及びブチリル基等が挙げられる。
ハロゲン原子としては、フッ素原子、塩素原子、臭素原子及びヨウ素原子等が挙げられる。
アルキルカルボニルオキシ基としては、メチルカルボニルオキシ基、エチルカルボニルオキシ基、n−プロピルカルボニルオキシ基、イソプロピルカルボニルオキシ基、n−ブチルカルボニルオキシ基、sec−ブチルカルボニルオキシ基、tert−ブチルカルボニルオキシ基、ペンチルカルボニルオキシ基、ヘキシルカルボニルオキシ基、オクチルカルボニルオキシ基及び2−エチルヘキシルカルボニルオキシ基等が挙げられる。
Examples of the alkoxy group include methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, heptyloxy group, octyloxy group, decyloxy group and dodecyloxy group.
Examples of the acyl group include an acetyl group, a propionyl group, and a butyryl group.
Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom.
Examples of the alkylcarbonyloxy group include a methylcarbonyloxy group, an ethylcarbonyloxy group, an n-propylcarbonyloxy group, an isopropylcarbonyloxy group, an n-butylcarbonyloxy group, a sec-butylcarbonyloxy group, a tert-butylcarbonyloxy group, Examples thereof include a pentylcarbonyloxy group, a hexylcarbonyloxy group, an octylcarbonyloxy group, and a 2-ethylhexylcarbonyloxy group.

b4とRb5とがそれらが結合している硫黄原子とともに形成してもよい環は、単環式、多環式、芳香族性、非芳香族性、飽和及び不飽和のいずれの環であってもよい。この環としては、炭素数3〜18の環が挙げられ、好ましくは炭素数4〜18の環が挙げられる。また、硫黄原子を含む環としては、3員環〜12員環が挙げられ、好ましくは3員環〜7員環が挙げられ、具体的には下記の環が挙げられる。

Figure 2017105770
The ring that R b4 and R b5 may form together with the sulfur atom to which they are bonded is any of monocyclic, polycyclic, aromatic, non-aromatic, saturated and unsaturated rings. There may be. As this ring, a C3-C18 ring is mentioned, Preferably a C4-C18 ring is mentioned. Moreover, as a ring containing a sulfur atom, 3-membered ring-12-membered ring are mentioned, Preferably 3-membered ring-7-membered ring are mentioned, Specifically, the following ring is mentioned.
Figure 2017105770

b9とRb10とがそれらが結合している硫黄原子とともに形成する環は、単環式、多環式、芳香族性、非芳香族性、飽和及び不飽和のいずれの環であってもよい。この環としては、3員環〜12員環が挙げられ、好ましくは3員環〜7員環が挙げられ、例えば、チオラン−1−イウム環(テトラヒドロチオフェニウム環)、チアン−1−イウム環、1,4−オキサチアン−4−イウム環等が挙げられる。
b11とRb12とが一緒になって形成する環は、単環式、多環式、芳香族性、非芳香族性、飽和及び不飽和のいずれの環であってもよい。この環としては、3員環〜12員環が挙げられ、好ましくは3員環〜7員環が挙げられ、例えば、オキソシクロヘプタン環、オキソシクロヘキサン環、オキソノルボルナン環、オキソアダマンタン環等が挙げられる。
The ring formed by R b9 and R b10 together with the sulfur atom to which they are bonded may be any of monocyclic, polycyclic, aromatic, non-aromatic, saturated and unsaturated rings. Good. Examples of the ring include a 3-membered ring to a 12-membered ring, preferably a 3-membered ring to a 7-membered ring. Examples thereof include a thiolane-1-ium ring (tetrahydrothiophenium ring) and thian-1-ium ring. Ring, 1,4-oxathian-4-ium ring and the like.
The ring formed by combining R b11 and R b12 may be any of monocyclic, polycyclic, aromatic, non-aromatic, saturated and unsaturated rings. Examples of the ring include a 3-membered ring to a 12-membered ring, preferably a 3-membered ring to a 7-membered ring. Examples thereof include an oxocycloheptane ring, an oxocyclohexane ring, an oxonorbornane ring, and an oxoadamantane ring. It is done.

カチオン(b2−1)〜カチオン(b2−4)の中で、好ましくはカチオン(b2−1)が挙げられる。   Among cations (b2-1) to cations (b2-4), cations (b2-1) are preferable.

カチオン(b2−1)としては、以下のカチオンが挙げられる。

Figure 2017105770
Examples of the cation (b2-1) include the following cations.
Figure 2017105770

Figure 2017105770
Figure 2017105770

Figure 2017105770
Figure 2017105770

カチオン(b2−2)としては、以下のカチオンが挙げられる。

Figure 2017105770
Examples of the cation (b2-2) include the following cations.
Figure 2017105770

カチオン(b2−3)としては、以下のカチオンが挙げられる。

Figure 2017105770
Examples of the cation (b2-3) include the following cations.
Figure 2017105770

カチオン(b2−4)のとしては、以下のカチオンが挙げられる。

Figure 2017105770
Examples of the cation (b2-4) include the following cations.
Figure 2017105770

酸発生剤(B1)は、上述のスルホン酸アニオン及び上述の有機カチオンの組合せであり、これらは任意に組合せることができる。酸発生剤(B1)としては、好ましくは式(B1a−1)〜式(B1a−3)及び式(B1a−7)〜式(B1a−15)のいずれかで表されるアニオンとカチオン(b2−1)又はカチオン(b2−3)との組合せが挙げられる。   The acid generator (B1) is a combination of the above-described sulfonate anion and the above-mentioned organic cation, and these can be arbitrarily combined. The acid generator (B1) is preferably an anion and a cation (b2) represented by any of the formulas (B1a-1) to (B1a-3) and (B1a-7) to (B1a-15). -1) or a combination with a cation (b2-3).

酸発生剤(B1)としては、好ましくは式(B1−1)〜式(B1−40)でそれぞれ表されるものが挙げられ、好ましくはアリールスルホニウムカチオンを含む式(B1−1)、式(B1−2)、式(B1−3)、式(B1−5)、式(B1−6)、式(B1−7)、式(B1−11)、式(B1−12)、式(B1−13)、式(B1−14)、式(B1−13)、式(B1−20)、式(B1−21)、式(B1−23)、式(B1−24)、式(B1−25)、式(B1−26)、式(B1−29)、式(B1−31)、式(B1−32)、式(B1−33)、式(B1−34)、式(B1−35)、式(B1−36)、式(B1−37)、式(B1−38)、式(B1−39)又は式(B1−40)でそれぞれ表されるものが挙げられる。   Preferred examples of the acid generator (B1) include those represented by formulas (B1-1) to (B1-40), and preferably include formulas (B1-1) and formula (B) containing an arylsulfonium cation. B1-2), formula (B1-3), formula (B1-5), formula (B1-6), formula (B1-7), formula (B1-11), formula (B1-12), formula (B1) -13), formula (B1-14), formula (B1-13), formula (B1-20), formula (B1-21), formula (B1-23), formula (B1-24), formula (B1- 25), Formula (B1-26), Formula (B1-29), Formula (B1-31), Formula (B1-32), Formula (B1-33), Formula (B1-34), Formula (B1-35) ), Formula (B1-36), formula (B1-37), formula (B1-38), formula (B1-39) or formula (B1-40). It is.

Figure 2017105770
Figure 2017105770

Figure 2017105770
Figure 2017105770

Figure 2017105770
Figure 2017105770

Figure 2017105770
Figure 2017105770

Figure 2017105770
Figure 2017105770

酸発生剤(B1)の含有率は、酸発生剤(B)の総量に対して、30質量%以上100質量%以下であることが好ましく、50質量%以上100質量%以下であることがより好ましく、実質的に酸発生剤(B1)のみであることがさらに好ましい。
酸発生剤(B)の含有量は、樹脂(A)100質量部に対して、好ましくは1質量部以上(より好ましくは3質量部以上)、好ましくは30質量部以下(より好ましくは25質量部以下)である。本発明のレジスト組成物は、酸発生剤(B)の1種を含有してもよく、複数種を含有してもよい。
The content of the acid generator (B1) is preferably 30% by mass or more and 100% by mass or less, and more preferably 50% by mass or more and 100% by mass or less, with respect to the total amount of the acid generator (B). Preferably, it is more preferably substantially only the acid generator (B1).
The content of the acid generator (B) is preferably 1 part by mass or more (more preferably 3 parts by mass or more), preferably 30 parts by mass or less (more preferably 25 parts by mass) with respect to 100 parts by mass of the resin (A). Part or less). The resist composition of the present invention may contain one or more acid generators (B).

〈溶剤(E)〉
溶剤(E)の含有率は、通常、レジスト組成物中90質量%以上、好ましくは92質量%以上、より好ましくは94質量%以上であり、99.9質量%以下、好ましくは99質量%以下である。溶剤(E)の含有率は、例えば液体クロマトグラフィー又はガスクロマトグラフィー等の公知の分析手段で測定できる。
<Solvent (E)>
The content of the solvent (E) is usually 90% by mass or more, preferably 92% by mass or more, more preferably 94% by mass or more, and 99.9% by mass or less, preferably 99% by mass or less in the resist composition. It is. The content rate of a solvent (E) can be measured by well-known analysis means, such as a liquid chromatography or a gas chromatography, for example.

溶剤(E)としては、エチルセロソルブアセテート、メチルセロソルブアセテート及びプロピレングリコールモノメチルエーテルアセテート等のグリコールエーテルエステル類;プロピレングリコールモノメチルエーテル等のグリコールエーテル類;乳酸エチル、酢酸ブチル、酢酸アミル及びピルビン酸エチル等のエステル類;アセトン、メチルイソブチルケトン、2−ヘプタノン及びシクロヘキサノン等のケトン類;γ−ブチロラクトン等の環状エステル類;等を挙げることができる。溶剤(E)の1種を単独で含有してもよく、2種以上を含有してもよい。   Examples of the solvent (E) include glycol ether esters such as ethyl cellosolve acetate, methyl cellosolve acetate and propylene glycol monomethyl ether acetate; glycol ethers such as propylene glycol monomethyl ether; ethyl lactate, butyl acetate, amyl acetate and ethyl pyruvate Esters such as acetone, methyl isobutyl ketone, ketones such as 2-heptanone and cyclohexanone; cyclic esters such as γ-butyrolactone; and the like. One kind of the solvent (E) may be contained alone, or two or more kinds may be contained.

〈クエンチャー(C)〉
本発明のレジスト組成物は、クエンチャー(以下「クエンチャー(C)」という場合がある)を含有していてもよい。クエンチャー(C)は、塩基性の含窒素有機化合物又は酸発生剤(B)よりも酸性度の弱い酸を発生する塩が挙げられる。
<Quencher (C)>
The resist composition of the present invention may contain a quencher (hereinafter sometimes referred to as “quencher (C)”). The quencher (C) may be a basic nitrogen-containing organic compound or a salt that generates an acid having a lower acidity than the acid generator (B).

〈塩基性の含窒素有機化合物〉
塩基性の含窒素有機化合物としては、アミン及びアンモニウム塩が挙げられる。アミンとしては、脂肪族アミン及び芳香族アミンが挙げられる。脂肪族アミンとしては、第一級アミン、第二級アミン及び第三級アミンが挙げられる。
<Basic nitrogen-containing organic compound>
Examples of the basic nitrogen-containing organic compound include amines and ammonium salts. Examples of amines include aliphatic amines and aromatic amines. Aliphatic amines include primary amines, secondary amines and tertiary amines.

具体的には、1−ナフチルアミン、2−ナフチルアミン、アニリン、ジイソプロピルアニリン、2−,3−又は4−メチルアニリン、4−ニトロアニリン、N−メチルアニリン、N,N−ジメチルアニリン、ジフェニルアミン、ヘキシルアミン、ヘプチルアミン、オクチルアミン、ノニルアミン、デシルアミン、ジブチルアミン、ジペンチルアミン、ジヘキシルアミン、ジヘプチルアミン、ジオクチルアミン、ジノニルアミン、ジデシルアミン、トリエチルアミン、トリメチルアミン、トリプロピルアミン、トリブチルアミン、トリペンチルアミン、トリヘキシルアミン、トリヘプチルアミン、トリオクチルアミン、トリノニルアミン、トリデシルアミン、メチルジブチルアミン、メチルジペンチルアミン、メチルジヘキシルアミン、メチルジシクロヘキシルアミン、メチルジヘプチルアミン、メチルジオクチルアミン、メチルジノニルアミン、メチルジデシルアミン、エチルジブチルアミン、エチルジペンチルアミン、エチルジヘキシルアミン、エチルジヘプチルアミン、エチルジオクチルアミン、エチルジノニルアミン、エチルジデシルアミン、ジシクロヘキシルメチルアミン、トリス〔2−(2−メトキシエトキシ)エチル〕アミン、トリイソプロパノールアミン、エチレンジアミン、テトラメチレンジアミン、ヘキサメチレンジアミン、4,4’−ジアミノ−1,2−ジフェニルエタン、4,4’−ジアミノ−3,3’−ジメチルジフェニルメタン、4,4’−ジアミノ−3,3’−ジエチルジフェニルメタン、2,2’−メチレンビスアニリン、イミダゾール、4−メチルイミダゾール、ピリジン、4−メチルピリジン、1,2−ジ(2−ピリジル)エタン、1,2−ジ(4−ピリジル)エタン、1,2−ジ(2−ピリジル)エテン、1,2−ジ(4−ピリジル)エテン、1,3−ジ(4−ピリジル)プロパン、1,2−ジ(4−ピリジルオキシ)エタン、ジ(2−ピリジル)ケトン、4,4’−ジピリジルスルフィド、4,4’−ジピリジルジスルフィド、2,2’−ジピリジルアミン、2,2’−ジピコリルアミン、ビピリジン等が挙げられ、好ましくはジイソプロピルアニリンが挙げられ、特に好ましくは2,6−ジイソプロピルアニリンが挙げられる。   Specifically, 1-naphthylamine, 2-naphthylamine, aniline, diisopropylaniline, 2-, 3- or 4-methylaniline, 4-nitroaniline, N-methylaniline, N, N-dimethylaniline, diphenylamine, hexylamine , Heptylamine, octylamine, nonylamine, decylamine, dibutylamine, dipentylamine, dihexylamine, diheptylamine, dioctylamine, dinonylamine, didecylamine, triethylamine, trimethylamine, tripropylamine, tributylamine, tripentylamine, trihexylamine, Triheptylamine, trioctylamine, trinonylamine, tridecylamine, methyldibutylamine, methyldipentylamine, methyldihexylamine, methyl Cyclohexylamine, methyldiheptylamine, methyldioctylamine, methyldinonylamine, methyldidecylamine, ethyldibutylamine, ethyldipentylamine, ethyldihexylamine, ethyldiheptylamine, ethyldioctylamine, ethyldinonylamine, ethyldinonylamine Decylamine, dicyclohexylmethylamine, tris [2- (2-methoxyethoxy) ethyl] amine, triisopropanolamine, ethylenediamine, tetramethylenediamine, hexamethylenediamine, 4,4′-diamino-1,2-diphenylethane, 4 , 4'-diamino-3,3'-dimethyldiphenylmethane, 4,4'-diamino-3,3'-diethyldiphenylmethane, 2,2'-methylenebisaniline, imidazole, 4-methyl Imidazole, pyridine, 4-methylpyridine, 1,2-di (2-pyridyl) ethane, 1,2-di (4-pyridyl) ethane, 1,2-di (2-pyridyl) ethene, 1,2-di (4-pyridyl) ethene, 1,3-di (4-pyridyl) propane, 1,2-di (4-pyridyloxy) ethane, di (2-pyridyl) ketone, 4,4′-dipyridyl sulfide, 4, 4'-dipyridyl disulfide, 2,2'-dipyridylamine, 2,2'-dipicolylamine, bipyridine and the like are preferable, diisopropylaniline is preferable, and 2,6-diisopropylaniline is particularly preferable.

アンモニウム塩としては、テトラメチルアンモニウムヒドロキシド、テトライソプロピルアンモニウムヒドロキシド、テトラブチルアンモニウムヒドロキシド、テトラヘキシルアンモニウムヒドロキシド、テトラオクチルアンモニウムヒドロキシド、フェニルトリメチルアンモニウムヒドロキシド、3−(トリフルオロメチル)フェニルトリメチルアンモニウムヒドロキシド、テトラ−n−ブチルアンモニウムサリチラート及びコリン等が挙げられる。   As ammonium salts, tetramethylammonium hydroxide, tetraisopropylammonium hydroxide, tetrabutylammonium hydroxide, tetrahexylammonium hydroxide, tetraoctylammonium hydroxide, phenyltrimethylammonium hydroxide, 3- (trifluoromethyl) phenyltrimethyl Ammonium hydroxide, tetra-n-butylammonium salicylate, choline and the like can be mentioned.

〈酸性度の弱い塩〉
酸発生剤から発生する酸よりも酸性度の弱い酸を発生する塩における酸性度は酸解離定数(pKa)で示される。酸発生剤から発生する酸よりも酸性度の弱い塩は、該塩から発生する酸のpKaが、通常−3<pKaの塩であり、好ましくは−1<pKa<7の塩であり、より好ましくは0<pKa<5の塩である。酸発生剤から発生する酸よりも弱い塩としては、下記式で表される塩、式(D)で表される弱酸分子内塩、並びに特開2012−229206号公報、特開2012−6908号公報、特開2012−72109号公報、特開2011−39502号公報及び特開2011−191745号公報記載の塩が挙げられる。

Figure 2017105770
<Slightly acidic salt>
The acidity in a salt that generates an acid having a weaker acidity than the acid generated from the acid generator is indicated by an acid dissociation constant (pKa). The salt having a lower acidity than the acid generated from the acid generator is a salt in which the pKa of the acid generated from the salt is usually -3 <pKa, preferably -1 <pKa <7, A salt of 0 <pKa <5 is preferable. Examples of the salt weaker than the acid generated from the acid generator include a salt represented by the following formula, a weak acid inner salt represented by the formula (D), and JP 2012-229206 A and JP 2012-6908 A. Examples thereof include salts described in JP-A No. 2012-72109, JP-A 2011-39502 and JP-A 2011-191745.
Figure 2017105770

Figure 2017105770
Figure 2017105770

Figure 2017105770
[式(D)中、
D1及びRD2は、それぞれ独立に、炭素数1〜12の1価の炭化水素基、炭素数1〜6のアルコキシ基、炭素数2〜7のアシル基、炭素数2〜7のアシルオキシ基、炭素数2〜7のアルコキシカルボニル基、ニトロ基又はハロゲン原子を表す。
m’及びn’は、それぞれ独立に、0〜4の整数を表し、m’が2以上の場合、複数のRD1は同一又は相異なり、n’が2以上の場合、複数のRD2は同一又は相異なる。]
Figure 2017105770
[In the formula (D),
R D1 and R D2 are each independently a monovalent hydrocarbon group having 1 to 12 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, an acyl group having 2 to 7 carbon atoms, or an acyloxy group having 2 to 7 carbon atoms. Represents an alkoxycarbonyl group having 2 to 7 carbon atoms, a nitro group, or a halogen atom.
m ′ and n ′ each independently represents an integer of 0 to 4, and when m ′ is 2 or more, the plurality of R D1 are the same or different, and when n ′ is 2 or more, the plurality of R D2 are Same or different. ]

式(D)で表される化合物におけるRD1及びRD2の炭化水素基としては、1価の脂肪族炭化水素基、1価の脂環式炭化水素基、1価の芳香族炭化水素基及びこれらの組み合わせることにより形成される基等が挙げられる。
1価の脂肪族炭化水素基としては、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、tert−ブチル基、ペンチル基、ヘキシル基、ノニル基等のアルキル基が挙げられる。
1価の脂環式炭化水素基としては、単環式及び多環式のいずれでもよく、飽和及び不飽和のいずれでもよい。シクロプロピル基、シクロブチル基、シクロペンチル基、シクロへキシル基、シクロノニル基、シクロドデシル基等のシクロアルキル基、ノルボニル基、アダマンチル基等が挙げられる。
1価の芳香族炭化水素基としては、フェニル基、1−ナフチル基、2−ナフチル基、2−メチルフェニル基、3−メチルフェニル基、4−メチルフェニル基、4−エチルフェニル基、4−プロピルフェニル基、4−イソプロピルフェニル基、4−ブチルフェニル基、4−t−ブチルフェニル基、4−ヘキシルフェニル基、4−シクロヘキシルフェニル基、アントリル基、p−アダマンチルフェニル基、トリル基、キシリル基、クメニル基、メシチル基、ビフェニル基、フェナントリル基、2,6−ジエチルフェニル基、2−メチル−6−エチルフェニル等のアリール基等が挙げられる。
これらを組み合わせることにより形成される基としては、アルキル−シクロアルキル基、シクロアルキル−アルキル基、アラルキル基(例えば、フェニルメチル基、1−フェニルエチル基、2−フェニルエチル基、1−フェニル−1−プロピル基、1−フェニル−2−プロピル基、2−フェニル−2−プロピル基、3−フェニル−1−プロピル基、4−フェニル−1−ブチル基、5−フェニル−1−ペンチル基、6−フェニル−1−ヘキシル基等)等が挙げられる。
Examples of the hydrocarbon group represented by R D1 and R D2 in the compound represented by the formula (D) include a monovalent aliphatic hydrocarbon group, a monovalent alicyclic hydrocarbon group, a monovalent aromatic hydrocarbon group, and Examples include groups formed by combining these.
Examples of the monovalent aliphatic hydrocarbon group include alkyl groups such as methyl group, ethyl group, propyl group, isopropyl group, butyl group, isobutyl group, tert-butyl group, pentyl group, hexyl group, and nonyl group.
The monovalent alicyclic hydrocarbon group may be monocyclic or polycyclic, and may be either saturated or unsaturated. Examples thereof include cycloalkyl groups such as cyclopropyl group, cyclobutyl group, cyclopentyl group, cyclohexyl group, cyclononyl group, and cyclododecyl group, norbornyl group, adamantyl group, and the like.
Examples of the monovalent aromatic hydrocarbon group include phenyl group, 1-naphthyl group, 2-naphthyl group, 2-methylphenyl group, 3-methylphenyl group, 4-methylphenyl group, 4-ethylphenyl group, 4- Propylphenyl group, 4-isopropylphenyl group, 4-butylphenyl group, 4-t-butylphenyl group, 4-hexylphenyl group, 4-cyclohexylphenyl group, anthryl group, p-adamantylphenyl group, tolyl group, xylyl group , Aryl groups such as cumenyl group, mesityl group, biphenyl group, phenanthryl group, 2,6-diethylphenyl group, 2-methyl-6-ethylphenyl, and the like.
Examples of the group formed by combining these include an alkyl-cycloalkyl group, a cycloalkyl-alkyl group, an aralkyl group (for example, phenylmethyl group, 1-phenylethyl group, 2-phenylethyl group, 1-phenyl-1 -Propyl group, 1-phenyl-2-propyl group, 2-phenyl-2-propyl group, 3-phenyl-1-propyl group, 4-phenyl-1-butyl group, 5-phenyl-1-pentyl group, 6 -Phenyl-1-hexyl group, etc.).

アルコキシ基としては、メトキシ基、エトキシ基等が挙げられる。
アシル基としては、アセチル基、プロパノイル基、ベンゾイル基、シクロヘキサンカルボニル基等が挙げられる。
アシルオキシ基としては、上記アシル基にオキシ基(−O−)が結合した基等が挙げられる。
アルコキシカルボニル基としては、上記アルコキシ基にカルボニル基(−CO−)が結合した基等が挙げられる。
ハロゲン原子としては、フッ素原子、塩素原子、臭素原子等が挙げられる。
Examples of the alkoxy group include a methoxy group and an ethoxy group.
Examples of the acyl group include an acetyl group, a propanoyl group, a benzoyl group, and a cyclohexanecarbonyl group.
Examples of the acyloxy group include a group in which an oxy group (—O—) is bonded to the acyl group.
Examples of the alkoxycarbonyl group include a group in which a carbonyl group (—CO—) is bonded to the above alkoxy group.
Examples of the halogen atom include a fluorine atom, a chlorine atom, and a bromine atom.

式(D)においては、RD1及びRD2は、それぞれ独立に、炭素数1〜8のアルキル基、炭素数3〜10のシクロアルキル基、炭素数1〜6のアルコキシ基、炭素数2〜4のアシル基、炭素数2〜4のアシルオキシ基、炭素数2〜4のアルコキシカルボニル基、ニトロ基又はハロゲン原子が好ましい。
m’及びn’は、それぞれ独立に、0〜2の整数が好ましく、0がより好ましい。m’が2以上の場合、複数のRD1は同一又は相異なり、n’が2以上の場合、複数のRD2は同一又は相異なる。
In the formula (D), R D1 and R D2 each independently represent an alkyl group having 1 to 8 carbon atoms, a cycloalkyl group having 3 to 10 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or 2 to 2 carbon atoms. Preferred are an acyl group having 4 carbon atoms, an acyloxy group having 2 to 4 carbon atoms, an alkoxycarbonyl group having 2 to 4 carbon atoms, a nitro group, or a halogen atom.
m ′ and n ′ are each independently preferably an integer of 0 to 2, and more preferably 0. When m ′ is 2 or more, the plurality of R D1 are the same or different, and when n ′ is 2 or more, the plurality of R D2 are the same or different.

弱酸分子内塩(D)としては、以下の化合物が挙げられる。

Figure 2017105770
Examples of the weak acid inner salt (D) include the following compounds.
Figure 2017105770

弱酸分子内塩(D)は、「Tetrahedron Vol. 45, No. 19, p6281-6296」に記載の方法で製造することができる。また、弱酸分子内塩(D)は、市販されている化合物を用いることができる。   The weak acid inner salt (D) can be produced by the method described in “Tetrahedron Vol. 45, No. 19, p6281-6296”. A commercially available compound can be used as the weak acid inner salt (D).

クエンチャー(C)の含有率は、レジスト組成物の固形分中、好ましくは、0.01〜5質量%であり、より好ましく0.01〜4質量%であり、特に好ましく0.01〜3質量%である。   The content of the quencher (C) is preferably 0.01 to 5% by mass, more preferably 0.01 to 4% by mass, and particularly preferably 0.01 to 3% by mass in the solid content of the resist composition. % By mass.

〈その他の成分〉
本発明のレジスト組成物は、必要に応じて、上述の成分以外の成分(以下「その他の成分(F)」という場合がある。)を含有していてもよい。その他の成分(F)に特に限定はなく、レジスト分野で公知の添加剤、例えば、増感剤、溶解抑止剤、界面活性剤、安定剤、染料等を利用できる。
<Other ingredients>
The resist composition of the present invention may contain components other than the above components (hereinafter sometimes referred to as “other components (F)”) as necessary. The other component (F) is not particularly limited, and additives known in the resist field, such as sensitizers, dissolution inhibitors, surfactants, stabilizers, dyes, and the like can be used.

〈レジスト組成物の調製〉
本発明のレジスト組成物は、本発明の樹脂(X)、樹脂(A)及び酸発生剤(B)、並びに、必要に応じて用いられるクエンチャー(C)、溶剤(E)及びその他の成分(F)を混合することにより調製することができる。混合順は任意であり、特に限定されるものではない。混合する際の温度は、10〜40℃から、樹脂等の種類や樹脂等の溶剤(E)に対する溶解度等に応じて適切な温度を選ぶことができる。混合時間は、混合温度に応じて、0.5〜24時間の中から適切な時間を選ぶことができる。なお、混合手段も特に制限はなく、攪拌混合等を用いることができる。
各成分を混合した後は、孔径0.003〜0.2μm程度のフィルターを用いてろ過することが好ましい。
<Preparation of resist composition>
The resist composition of the present invention comprises the resin (X), the resin (A) and the acid generator (B) of the present invention, and the quencher (C), solvent (E) and other components used as necessary. It can be prepared by mixing (F). The mixing order is arbitrary and is not particularly limited. The temperature at the time of mixing can select an appropriate temperature from 10-40 degreeC according to the kind etc. of resin etc., the solubility with respect to solvents (E), such as resin. An appropriate mixing time can be selected from 0.5 to 24 hours depending on the mixing temperature. The mixing means is not particularly limited, and stirring and mixing can be used.
After mixing each component, it is preferable to filter using a filter having a pore size of about 0.003 to 0.2 μm.

〈レジストパターンの製造方法〉
本発明のレジストパターンの製造方法は、
(1)本発明のレジスト組成物を基板上に塗布する工程、
(2)塗布後の組成物を乾燥させて組成物層を形成する工程、
(3)組成物層に露光する工程、
(4)露光後の組成物層を加熱する工程、及び
(5)加熱後の組成物層を現像する工程を含む。
<Method for producing resist pattern>
The method for producing a resist pattern of the present invention comprises:
(1) A step of applying the resist composition of the present invention on a substrate,
(2) The process of drying the composition after application | coating and forming a composition layer,
(3) a step of exposing the composition layer;
(4) a step of heating the composition layer after exposure, and (5) a step of developing the composition layer after heating.

レジスト組成物を基板上に塗布するには、スピンコーター等、通常、用いられる装置によって行うことができる。基板としては、シリコンウェハ等の無機基板が挙げられる。レジスト組成物を塗布する前に、基板を洗浄してもよいし、基板上に反射防止膜等を形成してもよい。   The resist composition can be applied onto the substrate by a commonly used apparatus such as a spin coater. Examples of the substrate include an inorganic substrate such as a silicon wafer. Before applying the resist composition, the substrate may be washed, or an antireflection film or the like may be formed on the substrate.

塗布後の組成物を乾燥することにより、溶剤を除去し、組成物層を形成する。乾燥は、例えば、ホットプレート等の加熱装置を用いて溶剤を蒸発させること(いわゆるプリベーク)により行うか、あるいは減圧装置を用いて行う。加熱温度は50〜200℃が好ましく、加熱時間は10〜180秒間が好ましい。また、減圧乾燥する際の圧力は、1〜1.0×105Pa程度が好ましい。 By drying the composition after coating, the solvent is removed and a composition layer is formed. Drying is performed, for example, by evaporating the solvent using a heating device such as a hot plate (so-called pre-baking), or using a decompression device. The heating temperature is preferably 50 to 200 ° C., and the heating time is preferably 10 to 180 seconds. The pressure during drying under reduced pressure is preferably about 1 to 1.0 × 10 5 Pa.

得られた組成物層に、通常、露光機を用いて露光する。露光機は、液浸露光機であってもよい。露光光源としては、KrFエキシマレーザ(波長248nm)、ArFエキシマレーザ(波長193nm)、F2エキシマレーザ(波長157nm)のような紫外域のレーザ光を放射するもの、固体レーザ光源(YAG又は半導体レーザ等)からのレーザ光を波長変換して遠紫外域または真空紫外域の高調波レーザ光を放射するもの、電子線や、超紫外光(EUV)を照射するもの等、種々のものを用いることができる。尚、本明細書において、これらの放射線を照射することを総称して「露光」という場合がある。露光の際、通常、求められるパターンに相当するマスクを介して露光が行われる。露光光源が電子線の場合は、マスクを用いずに直接描画により露光してもよい。 The obtained composition layer is usually exposed using an exposure machine. The exposure machine may be an immersion exposure machine. Exposure light sources include those that emit laser light in the ultraviolet region such as KrF excimer laser (wavelength 248 nm), ArF excimer laser (wavelength 193 nm), F 2 excimer laser (wavelength 157 nm), solid-state laser light source (YAG or semiconductor laser) Etc.) Using various lasers such as those that convert wavelength of laser light from the laser and emit harmonic laser light in the far-ultraviolet region or vacuum ultraviolet region, those that irradiate electron beams or extreme ultraviolet light (EUV), etc. Can do. In this specification, the irradiation of these radiations may be collectively referred to as “exposure”. At the time of exposure, exposure is usually performed through a mask corresponding to a required pattern. When the exposure light source is an electron beam, exposure may be performed by direct drawing without using a mask.

露光後の組成物層を、酸不安定基における脱保護反応を促進するために加熱処理(いわゆるポストエキスポジャーベーク)を行う。加熱温度は、通常50〜200℃程度、好ましくは70〜150℃程度である。   The composition layer after exposure is subjected to heat treatment (so-called post-exposure baking) in order to promote the deprotection reaction in the acid labile group. The heating temperature is usually about 50 to 200 ° C, preferably about 70 to 150 ° C.

加熱後の組成物層を、通常、現像装置を用いて、現像液を利用して現像する。現像方法としては、ディップ法、パドル法、スプレー法、ダイナミックディスペンス法等が挙げられる。現像温度は5〜60℃が好ましく、現像時間は5〜300秒間が好ましい。現像液の種類を以下のとおりに選択することにより、ポジ型レジストパターン又はネガ型レジストパターンを製造できる。   The heated composition layer is usually developed using a developer using a developing device. Examples of the developing method include a dipping method, a paddle method, a spray method, and a dynamic dispensing method. The development temperature is preferably 5 to 60 ° C., and the development time is preferably 5 to 300 seconds. A positive resist pattern or a negative resist pattern can be produced by selecting the type of developer as follows.

本発明のレジスト組成物からポジ型レジストパターンを製造する場合は、現像液としてアルカリ現像液を用いる。アルカリ現像液は、この分野で用いられる各種のアルカリ性水溶液であればよい。例えば、テトラメチルアンモニウムヒドロキシドや(2−ヒドロキシエチル)トリメチルアンモニウムヒドロキシド(通称コリン)の水溶液等が挙げられる。アルカリ現像液には、界面活性剤が含まれていてもよい。
現像後レジストパターンを超純水で洗浄し、次いで、基板及びパターン上に残った水を除去することが好ましい。
When producing a positive resist pattern from the resist composition of the present invention, an alkaline developer is used as the developer. The alkaline developer may be various alkaline aqueous solutions used in this field. Examples thereof include an aqueous solution of tetramethylammonium hydroxide and (2-hydroxyethyl) trimethylammonium hydroxide (commonly called choline). The alkali developer may contain a surfactant.
It is preferable to wash the resist pattern with ultrapure water after development, and then remove the water remaining on the substrate and the pattern.

本発明のレジスト組成物からネガ型レジストパターンを製造する場合は、現像液として有機溶剤を含む現像液(以下「有機系現像液」という場合がある)を用いる。
有機系現像液に含まれる有機溶剤としては、2−ヘキサノン、2−ヘプタノン等のケトン溶剤;プロピレングリコールモノメチルエーテルアセテート等のグリコールエーテルエステル溶剤;酢酸ブチル等のエステル溶剤;プロピレングリコールモノメチルエーテル等のグリコールエーテル溶剤;N,N−ジメチルアセトアミド等のアミド溶剤;アニソール等の芳香族炭化水素溶剤等が挙げられる。
有機系現像液中、有機溶剤の含有率は、90質量%以上100質量%以下が好ましく、95質量%以上100質量%以下がより好ましく、実質的に有機溶剤のみであることがさらに好ましい。
中でも、有機系現像液としては、酢酸ブチル及び/又は2−ヘプタノンを含む現像液が好ましい。有機系現像液中、酢酸ブチル及び2−ヘプタノンの合計含有率は、50質量%以上100質量%以下が好ましく、90質量%以上100質量%以下がより好ましく、実質的に酢酸ブチル及び/又は2−ヘプタノンのみであることがさらに好ましい。
有機系現像液には、界面活性剤が含まれていてもよい。また、有機系現像液には、微量の水分が含まれていてもよい。
現像の際、有機系現像液とは異なる種類の溶剤に置換することにより、現像を停止してもよい。
In the case of producing a negative resist pattern from the resist composition of the present invention, a developer containing an organic solvent as a developer (hereinafter sometimes referred to as “organic developer”) is used.
Organic solvents contained in the organic developer include ketone solvents such as 2-hexanone and 2-heptanone; glycol ether ester solvents such as propylene glycol monomethyl ether acetate; ester solvents such as butyl acetate; glycols such as propylene glycol monomethyl ether Examples include ether solvents; amide solvents such as N, N-dimethylacetamide; aromatic hydrocarbon solvents such as anisole.
In the organic developer, the content of the organic solvent is preferably 90% by mass or more and 100% by mass or less, more preferably 95% by mass or more and 100% by mass or less, and still more preferably only the organic solvent.
Among them, the organic developer is preferably a developer containing butyl acetate and / or 2-heptanone. In the organic developer, the total content of butyl acetate and 2-heptanone is preferably 50% by mass to 100% by mass, more preferably 90% by mass to 100% by mass, and substantially butyl acetate and / or 2 -More preferred is heptanone alone.
The organic developer may contain a surfactant. The organic developer may contain a trace amount of water.
At the time of development, the development may be stopped by substituting a solvent of a different type from the organic developer.

現像後のレジストパターンをリンス液で洗浄することが好ましい。リンス液としては、レジストパターンを溶解しないものであれば特に制限はなく、一般的な有機溶剤を含む溶液を使用することができ、好ましくはアルコール溶剤又はエステル溶剤である。
洗浄後は、基板及びパターン上に残ったリンス液を除去することが好ましい。
It is preferable to wash the developed resist pattern with a rinse solution. The rinsing liquid is not particularly limited as long as it does not dissolve the resist pattern, and a solution containing a general organic solvent can be used, and an alcohol solvent or an ester solvent is preferable.
After the cleaning, it is preferable to remove the rinse solution remaining on the substrate and the pattern.

〈用途〉
本発明のレジスト組成物は、KrFエキシマレーザ露光用のレジスト組成物、ArFエキシマレーザ露光用のレジスト組成物、電子線(EB)露光用のレジスト組成物又はEUV露光用のレジスト組成物、特にArFエキシマレーザ液浸露光用のレジスト組成物として好適であり、半導体の微細加工に有用である。
<Application>
The resist composition of the present invention includes a resist composition for KrF excimer laser exposure, a resist composition for ArF excimer laser exposure, a resist composition for electron beam (EB) exposure, or a resist composition for EUV exposure, particularly ArF. It is suitable as a resist composition for excimer laser immersion exposure and useful for fine processing of semiconductors.

実施例を挙げて、本発明をさらに具体的に説明する。例中、含有量ないし使用量を表す「%」及び「部」は、特記しないかぎり質量基準である。
重量平均分子量は、ゲルパーミエーションクロマトグラフィーで下記条件により求めた値である。
装置:HLC−8120GPC型(東ソー社製)
カラム:TSKgel Multipore HXL-M x 3 + guardcolumn(東ソー社製)
溶離液:テトラヒドロフラン
流量:1.0mL/min
検出器:RI検出器
カラム温度:40℃
注入量:100μl
分子量標準:標準ポリスチレン(東ソー社製)
The present invention will be described more specifically with reference to examples. In the examples, “%” and “parts” representing the content or amount used are based on mass unless otherwise specified.
The weight average molecular weight is a value determined by gel permeation chromatography under the following conditions.
Apparatus: HLC-8120GPC type (manufactured by Tosoh Corporation)
Column: TSKgel Multipore H XL -M x 3 + guardcolumn (manufactured by Tosoh Corporation)
Eluent: Tetrahydrofuran Flow rate: 1.0 mL / min
Detector: RI detector Column temperature: 40 ° C
Injection volume: 100 μl
Molecular weight standard: Standard polystyrene (manufactured by Tosoh Corporation)

また、化合物の構造は、質量分析(LCはAgilent製1100型、MASSはAgilent製LC/MSD型)を用い、分子ピークを測定することで確認した。以下の実施例ではこの分子ピークの値を「MASS」で示す。   The structure of the compound was confirmed by measuring molecular peaks using mass spectrometry (LC: Agilent model 1100, MASS: Agilent LC / MSD model). In the following examples, the value of this molecular peak is indicated by “MASS”.

実施例1〔式(I−2)で表される化合物の合成〕

Figure 2017105770
式(I−2−a)で表される化合物49.36部、テトラヒドロフラン135部、ピリジン15.39部及びジメチルアミノピリジン0.79部を添加し、23℃で30分間攪拌した。得られた混合溶液を5℃まで冷却し、式(I−2−b)で表される化合物20部を30分かけて添加した。その後、さらに、23℃で1時間攪拌した。得られた反応物に、酢酸エチル380部及び5%塩酸171部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を洗浄した。回収された有機層に、イオン交換水77部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、10%炭酸カリウム水溶液54部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、イオン交換水115部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。このような水洗操作を4回繰り返した。回収された有機層を濃縮した。得られた濃縮マスをカラム(関東化学 シリカゲル60N(球状、中性)100−210μm 展開溶媒:n−ヘプタン/酢酸エチル=1/1)分取することにより、回収された有機層を濃縮することにより、式(I−2−c)で表される化合物38.48部を得た。 Example 1 [Synthesis of Compound Represented by Formula (I-2)]
Figure 2017105770
49.36 parts of the compound represented by the formula (I-2-a), 135 parts of tetrahydrofuran, 15.39 parts of pyridine and 0.79 part of dimethylaminopyridine were added and stirred at 23 ° C. for 30 minutes. The obtained mixed solution was cooled to 5 ° C., and 20 parts of the compound represented by the formula (I-2-b) were added over 30 minutes. Thereafter, the mixture was further stirred at 23 ° C. for 1 hour. The obtained reaction product was charged with 380 parts of ethyl acetate and 171 parts of 5% hydrochloric acid, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer. The recovered organic layer was charged with 77 parts of ion exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 54 parts of a 10% aqueous potassium carbonate solution, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 115 parts of ion-exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. Such water washing operation was repeated 4 times. The collected organic layer was concentrated. The recovered organic layer is concentrated by fractionating the obtained concentrated mass into a column (Kanto Kagaku Silica Gel 60N (spherical, neutral) 100-210 μm developing solvent: n-heptane / ethyl acetate = 1/1). Gave 38.48 parts of the compound represented by the formula (I-2-c).

Figure 2017105770
式(I―2−c)で表される化合物4.71部、テトラヒドロフラン30部及びピリジン3.10部を反応器に仕込み、23℃で30分間攪拌し、式(I−2−d)で表される化合物3.63部を添加した。その後、温度を上昇させ、40℃で3時間攪拌した。得られた反応物に、酢酸エチル120部及び5%塩酸水溶液8.58部を加え、23℃で30分間攪拌し、静置、分液した。回収された有機層に、飽和炭酸水素ナトリウム水溶液30部を加え、23℃で30分間攪拌し、静置、分液することにより有機層を回収した。回収された有機層に、イオン交換水30部を加え、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。この水洗操作を5回繰り返した。水洗した有機層を濃縮し、カラム分取(固定床:メルク社製シリカゲル60−200メッシュ 展開溶媒:酢酸エチル)することにより、式(I−2)で表される化合物5.58部を得た。
MS(質量分析):492.1(分子イオンピーク)
Figure 2017105770
4.71 parts of a compound represented by the formula (I-2-c), 30 parts of tetrahydrofuran and 3.10 parts of pyridine were charged into a reactor, stirred at 23 ° C. for 30 minutes, and represented by the formula (I-2-d) 3.63 parts of the compound represented were added. Thereafter, the temperature was raised and the mixture was stirred at 40 ° C. for 3 hours. To the obtained reaction product, 120 parts of ethyl acetate and 8.58 parts of 5% hydrochloric acid aqueous solution were added, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated. To the recovered organic layer, 30 parts of a saturated aqueous sodium hydrogen carbonate solution was added, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to recover the organic layer. To the recovered organic layer, 30 parts of ion exchange water was added, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. This washing operation was repeated 5 times. The organic layer washed with water is concentrated and subjected to column fractionation (fixed bed: silica gel 60-200 mesh manufactured by Merck & Co., Ltd. developing solvent: ethyl acetate) to obtain 5.58 parts of the compound represented by the formula (I-2). It was.
MS (mass spectrometry): 492.1 (molecular ion peak)

実施例2〔式(I−1)で表される化合物の合成〕

Figure 2017105770
式(I―1−c)で表される化合物4.71部、テトラヒドロフラン30部及びピリジン3.10部を反応器に仕込み、23℃で30分間攪拌し、式(I−1−d)で表される化合物3.63部を添加した。その後、温度を上昇させ、40℃で3時間攪拌した。得られた反応物に、酢酸エチル120部及び5%塩酸水溶液8.58部を加え、23℃で30分間攪拌し、静置、分液した。回収された有機層に、飽和炭酸水素ナトリウム水溶液30部を加え、23℃で30分間攪拌し、静置、分液することにより有機層を回収した。回収された有機層に、イオン交換水30部を加え、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。この水洗操作を5回繰り返した。水洗した有機層を濃縮し、カラム分取(固定床:メルク社製シリカゲル60−200メッシュ 展開溶媒:酢酸エチル)することにより、式(I−1)で表される化合物5.58部を得た。
MS(質量分析):492.1(分子イオンピーク) Example 2 [Synthesis of Compound Represented by Formula (I-1)]
Figure 2017105770
4.71 parts of a compound represented by the formula (I-1-c), 30 parts of tetrahydrofuran and 3.10 parts of pyridine are charged into a reactor, stirred at 23 ° C. for 30 minutes, and expressed by the formula (I-1-d). 3.63 parts of the compound represented were added. Thereafter, the temperature was raised and the mixture was stirred at 40 ° C. for 3 hours. To the obtained reaction product, 120 parts of ethyl acetate and 8.58 parts of 5% hydrochloric acid aqueous solution were added, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated. To the recovered organic layer, 30 parts of a saturated aqueous sodium hydrogen carbonate solution was added, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to recover the organic layer. To the recovered organic layer, 30 parts of ion exchange water was added, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. This washing operation was repeated 5 times. The organic layer washed with water is concentrated and subjected to column fractionation (fixed bed: silica gel 60-200 mesh manufactured by Merck & Co., Ltd. developing solvent: ethyl acetate) to obtain 5.58 parts of the compound represented by the formula (I-1). It was.
MS (mass spectrometry): 492.1 (molecular ion peak)

実施例3〔式(I−8)で表される化合物の合成〕

Figure 2017105770
式(I−8−a)で表される化合物58.45部、テトラヒドロフラン135部、ピリジン15.39部及びジメチルアミノピリジン0.79部を添加し、23℃で30分間攪拌した。得られた混合溶液を5℃まで冷却し、式(I−8−b)で表される化合物20.00部を30分かけて添加した。その後、さらに、23℃で1時間攪拌した。得られた反応物に、酢酸エチル380部及び5%塩酸171部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を洗浄した。回収された有機層に、イオン交換水77部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、10%炭酸カリウム水溶液54部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、イオン交換水115部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。このような水洗操作を4回繰り返した。回収された有機層を濃縮した。得られた濃縮マスをカラム(関東化学 シリカゲル60N(球状、中性)100−210μm 展開溶媒:n−ヘプタン/酢酸エチル=1/1)分取することにより、回収された有機層を濃縮することにより、式(I−8−c)で表される化合物44.62部を得た。 Example 3 [Synthesis of Compound Represented by Formula (I-8)]
Figure 2017105770
58.45 parts of the compound represented by the formula (I-8-a), 135 parts of tetrahydrofuran, 15.39 parts of pyridine and 0.79 part of dimethylaminopyridine were added and stirred at 23 ° C. for 30 minutes. The obtained mixed solution was cooled to 5 ° C., and 20.00 parts of the compound represented by the formula (I-8-b) were added over 30 minutes. Thereafter, the mixture was further stirred at 23 ° C. for 1 hour. The obtained reaction product was charged with 380 parts of ethyl acetate and 171 parts of 5% hydrochloric acid, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer. The recovered organic layer was charged with 77 parts of ion exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 54 parts of a 10% aqueous potassium carbonate solution, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 115 parts of ion-exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. Such water washing operation was repeated 4 times. The collected organic layer was concentrated. The recovered organic layer is concentrated by fractionating the obtained concentrated mass into a column (Kanto Kagaku Silica Gel 60N (spherical, neutral) 100-210 μm developing solvent: n-heptane / ethyl acetate = 1/1). Gave 44.62 parts of the compound represented by the formula (I-8-c).

Figure 2017105770
式(I―8−c)で表される化合物5.17部、テトラヒドロフラン30部及びピリジン3.10部を反応器に仕込み、23℃で30分間攪拌し、式(I−8−d)で表される化合物3.63部を添加した。その後、温度を上昇させ、40℃で3時間攪拌した。得られた反応物に、酢酸エチル120部及び5%塩酸水溶液8.58部を加え、23℃で30分間攪拌し、静置、分液した。回収された有機層に、飽和炭酸水素ナトリウム水溶液30部を加え、23℃で30分間攪拌し、静置、分液することにより有機層を回収した。回収された有機層に、イオン交換水30部を加え、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。この水洗操作を5回繰り返した。水洗した有機層を濃縮し、カラム分取(固定床:メルク社製シリカゲル60−200メッシュ 展開溶媒:酢酸エチル)することにより、式(I−8)で表される化合物5.44部を得た。
MS(質量分析):520.2(分子イオンピーク)
Figure 2017105770
5.17 parts of a compound represented by the formula (I-8-c), 30 parts of tetrahydrofuran and 3.10 parts of pyridine are charged into a reactor, stirred at 23 ° C. for 30 minutes, and expressed by the formula (I-8-d). 3.63 parts of the compound represented were added. Thereafter, the temperature was raised and the mixture was stirred at 40 ° C. for 3 hours. To the obtained reaction product, 120 parts of ethyl acetate and 8.58 parts of 5% hydrochloric acid aqueous solution were added, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated. To the recovered organic layer, 30 parts of a saturated aqueous sodium hydrogen carbonate solution was added, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to recover the organic layer. To the recovered organic layer, 30 parts of ion exchange water was added, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. This washing operation was repeated 5 times. The organic layer washed with water is concentrated and subjected to column fractionation (fixed bed: silica gel 60-200 mesh manufactured by Merck & Co., Ltd. developing solvent: ethyl acetate) to obtain 5.44 parts of the compound represented by the formula (I-8). It was.
MS (mass spectrometry): 520.2 (molecular ion peak)

実施例4〔式(I−7)で表される化合物の合成〕

Figure 2017105770
式(I―7−c)で表される化合物5.17部、テトラヒドロフラン30部及びピリジン3.10部を反応器に仕込み、23℃で30分間攪拌し、式(I−7−d)で表される化合物3.63部を添加した。その後、温度を上昇させ、40℃で3時間攪拌した。得られた反応物に、酢酸エチル120部及び5%塩酸水溶液8.58部を加え、23℃で30分間攪拌し、静置、分液した。回収された有機層に、飽和炭酸水素ナトリウム水溶液30部を加え、23℃で30分間攪拌し、静置、分液することにより有機層を回収した。回収された有機層に、イオン交換水30部を加え、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。この水洗操作を5回繰り返した。水洗した有機層を濃縮し、カラム分取(固定床:メルク社製シリカゲル60−200メッシュ 展開溶媒:酢酸エチル)することにより、式(I−7)で表される化合物4.98部を得た。
MS(質量分析):520.2(分子イオンピーク) Example 4 [Synthesis of Compound Represented by Formula (I-7)]
Figure 2017105770
5.17 parts of a compound represented by the formula (I-7-c), 30 parts of tetrahydrofuran and 3.10 parts of pyridine are charged into a reactor, stirred at 23 ° C. for 30 minutes, and expressed by the formula (I-7-d). 3.63 parts of the compound represented were added. Thereafter, the temperature was raised and the mixture was stirred at 40 ° C. for 3 hours. To the obtained reaction product, 120 parts of ethyl acetate and 8.58 parts of 5% hydrochloric acid aqueous solution were added, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated. To the recovered organic layer, 30 parts of a saturated aqueous sodium hydrogen carbonate solution was added, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to recover the organic layer. To the recovered organic layer, 30 parts of ion exchange water was added, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. This washing operation was repeated 5 times. The organic layer washed with water is concentrated and subjected to column fractionation (fixed bed: silica gel 60-200 mesh manufactured by Merck & Co., Ltd. developing solvent: ethyl acetate) to obtain 4.98 parts of the compound represented by the formula (I-7). It was.
MS (mass spectrometry): 520.2 (molecular ion peak)

合成例1〔式(a4−1−x1)で表される化合物の合成〕

Figure 2017105770
式(a4−1−x1−a)で表される化合物30.68部、テトラヒドロフラン155部及びピリジン9.57部を添加し、23℃で30分間攪拌した。得られた混合溶液を5℃まで冷却し、式(a4−1−x1−b)で表される化合物25部を30分かけて添加した。その後、さらに、23℃で1時間攪拌した。得られた反応物に、酢酸エチル685部及び5%塩酸106部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を洗浄した。回収された有機層に、イオン交換水140部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、10%炭酸カリウム水溶液112部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、イオン交換水140部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。このような水洗操作を4回繰り返した。回収された有機層を濃縮した。得られた濃縮マスをカラム(関東化学 シリカゲル60N(球状、中性)100−210μm 展開溶媒:n−ヘプタン/酢酸エチル=1/1)分取することにより、回収された有機層を濃縮することにより、式(a4−1−x1−c)で表される化合物10.40部を得た。 Synthesis Example 1 [Synthesis of Compound Represented by Formula (a4-1-x1)]
Figure 2017105770
30.68 parts of the compound represented by the formula (a4-1-x1-a), 155 parts of tetrahydrofuran and 9.57 parts of pyridine were added and stirred at 23 ° C. for 30 minutes. The obtained mixed solution was cooled to 5 ° C., and 25 parts of the compound represented by the formula (a4-1-x1-b) was added over 30 minutes. Thereafter, the mixture was further stirred at 23 ° C. for 1 hour. The obtained reaction product was charged with 685 parts of ethyl acetate and 106 parts of 5% hydrochloric acid, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer. The recovered organic layer was charged with 140 parts of ion-exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 112 parts of a 10% aqueous potassium carbonate solution, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 140 parts of ion-exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. Such water washing operation was repeated 4 times. The collected organic layer was concentrated. The recovered organic layer is concentrated by fractionating the obtained concentrated mass into a column (Kanto Kagaku Silica Gel 60N (spherical, neutral) 100-210 μm developing solvent: n-heptane / ethyl acetate = 1/1). Thereby obtaining 10.40 parts of a compound represented by the formula (a4-1-x1-c).

Figure 2017105770
式(a4−1−x1−c)で表される化合物10.39部、テトラヒドロフラン125部、ピリジン2.24部及びジメチルアミノピリジン0.29部を添加し、23℃で30分間攪拌した。得られた混合溶液を5℃まで冷却し、式(a4−1−x1−d)で表される化合物7.57部を30分かけて添加した。その後、さらに、23℃で1時間攪拌した。得られた反応物に、酢酸エチル480部及び5%塩酸50部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を洗浄した。回収された有機層に、イオン交換水100部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、10%炭酸カリウム水溶液21部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、イオン交換水140部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。このような水洗操作を4回繰り返した。回収された有機層を濃縮した。得られた濃縮マスをカラム(関東化学 シリカゲル60N(球状、中性)100−210μm 展開溶媒:n−ヘプタン/酢酸エチル=1/1)分取することにより、式(a4−1−x1)で表される化合物10.82部を得た。
MS(質量分析):290.1(分子イオンピーク)
Figure 2017105770
10.39 parts of a compound represented by the formula (a4-1-x1-c), 125 parts of tetrahydrofuran, 2.24 parts of pyridine and 0.29 part of dimethylaminopyridine were added and stirred at 23 ° C. for 30 minutes. The obtained mixed solution was cooled to 5 ° C., and 7.57 parts of a compound represented by the formula (a4-1-x1-d) was added over 30 minutes. Thereafter, the mixture was further stirred at 23 ° C. for 1 hour. The obtained reaction product was charged with 480 parts of ethyl acetate and 50 parts of 5% hydrochloric acid, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer. The recovered organic layer was charged with 100 parts of ion exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 21 parts of a 10% aqueous potassium carbonate solution, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 140 parts of ion-exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. Such water washing operation was repeated 4 times. The collected organic layer was concentrated. The obtained concentrated mass is fractionated by a column (Kanto Kagaku Silica Gel 60N (spherical, neutral) 100-210 μm developing solvent: n-heptane / ethyl acetate = 1/1) to obtain the formula (a4-1-x1). 10.82 parts of the compound represented are obtained.
MS (mass spectrometry): 290.1 (molecular ion peak)

合成例2〔式(a4−1−x2)で表される化合物の合成〕

Figure 2017105770
式(a4−1−x2−a)で表される化合物49.36部、テトラヒドロフラン135部、ピリジン15.39部及びジメチルアミノピリジン0.79部を添加し、23℃で30分間攪拌した。得られた混合溶液を5℃まで冷却し、式(a4−1−x2−b)で表される化合物20.00部を30分かけて添加した。その後、さらに、23℃で1時間攪拌した。得られた反応物に、酢酸エチル380部及び5%塩酸171部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を洗浄した。回収された有機層に、イオン交換水77部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、10%炭酸カリウム水溶液54部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、イオン交換水115部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。このような水洗操作を4回繰り返した。回収された有機層を濃縮した。得られた濃縮マスをカラム(関東化学 シリカゲル60N(球状、中性)100−210μm 展開溶媒:n−ヘプタン/酢酸エチル=1/1)分取することにより、回収された有機層を濃縮することにより、式(a4−1−x2−c)で表される化合物38.48部を得た。 Synthesis Example 2 [Synthesis of Compound Represented by Formula (a4-1-x2)]
Figure 2017105770
49.36 parts of the compound represented by the formula (a4-1-x2-a), 135 parts of tetrahydrofuran, 15.39 parts of pyridine and 0.79 part of dimethylaminopyridine were added, and the mixture was stirred at 23 ° C. for 30 minutes. The obtained mixed solution was cooled to 5 ° C., and 20.00 parts of the compound represented by the formula (a4-1-x2-b) were added over 30 minutes. Thereafter, the mixture was further stirred at 23 ° C. for 1 hour. The obtained reaction product was charged with 380 parts of ethyl acetate and 171 parts of 5% hydrochloric acid, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer. The recovered organic layer was charged with 77 parts of ion exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 54 parts of a 10% aqueous potassium carbonate solution, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 115 parts of ion-exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. Such water washing operation was repeated 4 times. The collected organic layer was concentrated. The recovered organic layer is concentrated by fractionating the obtained concentrated mass into a column (Kanto Kagaku Silica Gel 60N (spherical, neutral) 100-210 μm developing solvent: n-heptane / ethyl acetate = 1/1). Gave 38.48 parts of the compound represented by the formula (a4-1-x2-c).

Figure 2017105770
式(a4−1−x2−c)で表される化合物12.77部、テトラヒドロフラン105部及びピリジン8.41部を添加し、23℃で30分間攪拌した。得られた混合溶液を5℃まで冷却し、式(a4−1−x2−d)で表される化合物32.95部を30分かけて添加した。その後、さらに、23℃で1時間攪拌した。得られた反応物に、酢酸エチル530部及び5%塩酸93部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を洗浄した。回収された有機層に、イオン交換水105部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、10%炭酸カリウム水溶液44部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、イオン交換水160部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。このような水洗操作を4回繰り返した。回収された有機層を濃縮した。得られた濃縮マスをカラム(関東化学 シリカゲル60N(球状、中性)100−210μm 展開溶媒:n−ヘプタン/酢酸エチル=1/1)分取することにより、式(a4−1−x2)で表される化合物16.48部を得た。
MS(質量分析):290.1(分子イオンピーク)
Figure 2017105770
12.77 parts of a compound represented by the formula (a4-1-x2-c), 105 parts of tetrahydrofuran and 8.41 parts of pyridine were added and stirred at 23 ° C. for 30 minutes. The obtained mixed solution was cooled to 5 ° C., and 32.95 parts of the compound represented by the formula (a4-1-x2-d) was added over 30 minutes. Thereafter, the mixture was further stirred at 23 ° C. for 1 hour. To the obtained reaction product, 530 parts of ethyl acetate and 93 parts of 5% hydrochloric acid were added, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer. The recovered organic layer was charged with 105 parts of ion-exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 44 parts of a 10% aqueous potassium carbonate solution, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 160 parts of ion exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. Such water washing operation was repeated 4 times. The collected organic layer was concentrated. The obtained concentrated mass is fractionated by a column (Kanto Kagaku Silica Gel 60N (spherical, neutral) 100-210 μm developing solvent: n-heptane / ethyl acetate = 1/1) to obtain the formula (a4-1-x2) 16.48 parts of the compound represented were obtained.
MS (mass spectrometry): 290.1 (molecular ion peak)

合成例3〔式(a4−1−x7)で表される化合物の合成〕

Figure 2017105770
式(a4−1−x7−a)で表される化合物36.33部、テトラヒドロフラン155部及びピリジン9.57部を添加し、23℃で30分間攪拌した。得られた混合溶液を5℃まで冷却し、式(a4−1−x7−b)で表される化合物25.00部を30分かけて添加した。その後、さらに、23℃で1時間攪拌した。得られた反応物に、酢酸エチル685部及び5%塩酸106部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を洗浄した。回収された有機層に、イオン交換水140部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、10%炭酸カリウム水溶液112部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、イオン交換水140部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。このような水洗操作を4回繰り返した。回収された有機層を濃縮した。得られた濃縮マスをカラム(関東化学 シリカゲル60N(球状、中性)100−210μm 展開溶媒:n−ヘプタン/酢酸エチル=1/1)分取することにより、回収された有機層を濃縮することにより、式(a4−1−x7−c)で表される化合物12.48部を得た。
Figure 2017105770
式(a4−1−x7−c)で表される化合物11.05部、テトラヒドロフラン125部、ピリジン2.24部及びジメチルアミノピリジン0.29部を添加し、23℃で30分間攪拌した。得られた混合溶液を5℃まで冷却し、式(a4−1−x7−d)で表される化合物7.57部を30分かけて添加した。その後、さらに、23℃で1時間攪拌した。得られた反応物に、酢酸エチル480部及び5%塩酸50部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を洗浄した。回収された有機層に、イオン交換水100部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、10%炭酸カリウム水溶液21部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、イオン交換水140部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。このような水洗操作を4回繰り返した。回収された有機層を濃縮した。得られた濃縮マスをカラム(関東化学 シリカゲル60N(球状、中性)100−210μm 展開溶媒:n−ヘプタン/酢酸エチル=1/1)分取することにより、式(a4−1−x7)で表される化合物10.98部を得た。
MS(質量分析):304.1(分子イオンピーク) Synthesis Example 3 [Synthesis of Compound Represented by Formula (a4-1-x7)]
Figure 2017105770
36.33 parts of a compound represented by the formula (a4-1-x7-a), 155 parts of tetrahydrofuran and 9.57 parts of pyridine were added and stirred at 23 ° C. for 30 minutes. The obtained mixed solution was cooled to 5 ° C., and 25.00 parts of the compound represented by the formula (a4-1-x7-b) were added over 30 minutes. Thereafter, the mixture was further stirred at 23 ° C. for 1 hour. The obtained reaction product was charged with 685 parts of ethyl acetate and 106 parts of 5% hydrochloric acid, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer. The recovered organic layer was charged with 140 parts of ion-exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 112 parts of a 10% aqueous potassium carbonate solution, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 140 parts of ion-exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. Such water washing operation was repeated 4 times. The collected organic layer was concentrated. The recovered organic layer is concentrated by fractionating the obtained concentrated mass into a column (Kanto Kagaku Silica Gel 60N (spherical, neutral) 100-210 μm developing solvent: n-heptane / ethyl acetate = 1/1). Thereby obtaining 12.48 parts of a compound represented by the formula (a4-1-x7-c).
Figure 2017105770
11.05 parts of a compound represented by the formula (a4-1-x7-c), 125 parts of tetrahydrofuran, 2.24 parts of pyridine and 0.29 part of dimethylaminopyridine were added and stirred at 23 ° C. for 30 minutes. The obtained mixed solution was cooled to 5 ° C., and 7.57 parts of a compound represented by the formula (a4-1-x7-d) was added over 30 minutes. Thereafter, the mixture was further stirred at 23 ° C. for 1 hour. The obtained reaction product was charged with 480 parts of ethyl acetate and 50 parts of 5% hydrochloric acid, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer. The recovered organic layer was charged with 100 parts of ion exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 21 parts of a 10% aqueous potassium carbonate solution, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 140 parts of ion-exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. Such water washing operation was repeated 4 times. The collected organic layer was concentrated. The obtained concentrated mass is fractionated by a column (Kanto Chemical Silica Gel 60N (spherical, neutral) 100-210 μm developing solvent: n-heptane / ethyl acetate = 1/1) to obtain the formula (a4-1-x7). 10.98 parts of the compound represented were obtained.
MS (mass spectrometry): 304.1 (molecular ion peak)

合成例4〔式(a4−1−x8)で表される化合物の合成〕

Figure 2017105770
式(a4−1−x8−a)で表される化合物58.45部、テトラヒドロフラン135部、ピリジン15.39部及びジメチルアミノピリジン0.79部を添加し、23℃で30分間攪拌した。得られた混合溶液を5℃まで冷却し、式(a4−1−x8−b)で表される化合物20.00部を30分かけて添加した。その後、さらに、23℃で1時間攪拌した。得られた反応物に、酢酸エチル380部及び5%塩酸171部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を洗浄した。回収された有機層に、イオン交換水77部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、10%炭酸カリウム水溶液54部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、イオン交換水115部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。このような水洗操作を4回繰り返した。回収された有機層を濃縮した。得られた濃縮マスをカラム(関東化学 シリカゲル60N(球状、中性)100−210μm 展開溶媒:n−ヘプタン/酢酸エチル=1/1)分取することにより、回収された有機層を濃縮することにより、式(a4−1−x8−c)で表される化合物44.62部を得た。
Figure 2017105770
式(a4−1−x8−c)で表される化合物14.01部、テトラヒドロフラン105部及びピリジン8.41部を添加し、23℃で30分間攪拌した。得られた混合溶液を5℃まで冷却し、式(a4−1−x8−d)で表される化合物32.95部を30分かけて添加した。その後、さらに、23℃で1時間攪拌した。得られた反応物に、酢酸エチル530部及び5%塩酸93部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を洗浄した。回収された有機層に、イオン交換水105部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、10%炭酸カリウム水溶液44部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。回収された有機層に、イオン交換水160部を仕込み、23℃で30分間攪拌し、静置、分液することにより有機層を水洗した。このような水洗操作を4回繰り返した。回収された有機層を濃縮した。得られた濃縮マスをカラム(関東化学 シリカゲル60N(球状、中性)100−210μm 展開溶媒:n−ヘプタン/酢酸エチル=1/1)分取することにより、式(a4−1−x8)で表される化合物16.19部を得た。
MS(質量分析):304.1(分子イオンピーク) Synthesis Example 4 [Synthesis of Compound Represented by Formula (a4-1-x8)]
Figure 2017105770
58.45 parts of the compound represented by the formula (a4-1-x8-a), 135 parts of tetrahydrofuran, 15.39 parts of pyridine and 0.79 part of dimethylaminopyridine were added and stirred at 23 ° C. for 30 minutes. The obtained mixed solution was cooled to 5 ° C., and 20.00 parts of the compound represented by the formula (a4-1-x8-b) were added over 30 minutes. Thereafter, the mixture was further stirred at 23 ° C. for 1 hour. The obtained reaction product was charged with 380 parts of ethyl acetate and 171 parts of 5% hydrochloric acid, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer. The recovered organic layer was charged with 77 parts of ion exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 54 parts of a 10% aqueous potassium carbonate solution, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 115 parts of ion-exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. Such water washing operation was repeated 4 times. The collected organic layer was concentrated. The recovered organic layer is concentrated by fractionating the obtained concentrated mass into a column (Kanto Kagaku Silica Gel 60N (spherical, neutral) 100-210 μm developing solvent: n-heptane / ethyl acetate = 1/1). Thereby obtaining 44.62 parts of a compound represented by the formula (a4-1-x8-c).
Figure 2017105770
14.01 parts of a compound represented by the formula (a4-1-x8-c), 105 parts of tetrahydrofuran and 8.41 parts of pyridine were added and stirred at 23 ° C. for 30 minutes. The obtained mixed solution was cooled to 5 ° C., and 32.95 parts of the compound represented by the formula (a4-1-x8-d) was added over 30 minutes. Thereafter, the mixture was further stirred at 23 ° C. for 1 hour. To the obtained reaction product, 530 parts of ethyl acetate and 93 parts of 5% hydrochloric acid were added, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer. The recovered organic layer was charged with 105 parts of ion-exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 44 parts of a 10% aqueous potassium carbonate solution, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. The recovered organic layer was charged with 160 parts of ion exchanged water, stirred at 23 ° C. for 30 minutes, allowed to stand, and separated to wash the organic layer with water. Such water washing operation was repeated 4 times. The collected organic layer was concentrated. The obtained concentrated mass is fractionated by a column (Kanto Kagaku Silica Gel 60N (spherical, neutral) 100-210 μm developing solvent: n-heptane / ethyl acetate = 1/1) to obtain the formula (a4-1-x8). 16.19 parts of the compound represented were obtained.
MS (mass spectrometry): 304.1 (molecular ion peak)

合成例5〔式(B1−5)で表される塩の合成〕

Figure 2017105770
式(B1−5−a)で表される塩50.49部及びクロロホルム252.44部を反応器に仕込み、23℃で30分間攪拌し、式(B1−5−b)で表される化合物16.27部を滴下し、23℃で1時間攪拌することにより、式(B1−5−c)で表される塩を含む溶液を得た。得られた式(B1−5−c)で表される塩を含む溶液に、式(B1−5−d)で表される塩48.80部及びイオン交換水84.15部を添加し、23℃で12時間攪拌した。得られた反応液が2層に分離していたので、クロロホルム層を分液して取り出し、さらに、該クロロホルム層にイオン交換水84.15部を添加し、水洗した。この操作を5回繰り返した。得られたクロロホルム層に、活性炭3.88部を添加攪拌した後、ろ過した。回収されたろ液を濃縮し、得られた残渣に、アセトニトリル125.87部を添加攪拌し、濃縮した。得られた残渣に、アセトニトリル20.62部及びtert−ブチルメチルエーテル309.30部を加えて23℃で30分間攪拌し、上澄み液を除去し、濃縮した。得られた残渣に、n−ヘプタン200部を添加、23℃で30分間攪拌し、ろ過することにより、式(B1−5)で表される塩61.54部を得た。 Synthesis Example 5 [Synthesis of salt represented by formula (B1-5)]
Figure 2017105770
A compound represented by the formula (B1-5-b) was prepared by charging 50.49 parts of the salt represented by the formula (B1-5-a) and 252.44 parts of chloroform with stirring at 23 ° C for 30 minutes. 16.27 parts was dripped, and the solution containing the salt represented by a formula (B1-5-c) was obtained by stirring at 23 degreeC for 1 hour. To the obtained solution containing the salt represented by the formula (B1-5-c), 48.80 parts of the salt represented by the formula (B1-5-d) and 84.15 parts of ion-exchanged water are added, The mixture was stirred at 23 ° C. for 12 hours. Since the obtained reaction liquid was separated into two layers, the chloroform layer was separated and taken out, and 84.15 parts of ion-exchanged water was further added to the chloroform layer and washed with water. This operation was repeated 5 times. To the obtained chloroform layer, 3.88 parts of activated carbon was added and stirred, followed by filtration. The collected filtrate was concentrated, and 125.87 parts of acetonitrile was added to the resulting residue, and the mixture was stirred and concentrated. To the obtained residue, 20.62 parts of acetonitrile and 309.30 parts of tert-butyl methyl ether were added and stirred at 23 ° C. for 30 minutes, and the supernatant was removed and concentrated. To the obtained residue, 200 parts of n-heptane was added, stirred at 23 ° C. for 30 minutes, and filtered to obtain 61.54 parts of the salt represented by the formula (B1-5).

MASS(ESI(+)Spectrum):M 375.2
MASS(ESI(−)Spectrum):M 339.1
MASS (ESI (+) Spectrum): M + 375.2
MASS (ESI (−) Spectrum): M - 339.1

合成例6[式(B1−21)で表される塩の合成]

Figure 2017105770
Synthesis Example 6 [Synthesis of Salt Represented by Formula (B1-21)]
Figure 2017105770

特開2008−209917号公報に記載された方法によって得られた式(B1−21−b)で表される化合物30.00部、式(B1−21−a)で表される塩35.50部、クロロホルム100部及びイオン交換水50部を仕込み、23℃で15時間攪拌した。得られた反応液が2層に分離していたので、クロロホルム層を分液して取り出し、更に、該クロロホルム層にイオン交換水30部を添加し、水洗した。この操作を5回繰り返した。クロロホルム層を濃縮し、得られた残渣に、tert−ブチルメチルエーテル100部を加えて23℃で30分間攪拌した後、ろ過することにより、式(B1−21−c)で表される塩48.57部を得た。   30.00 parts of a compound represented by the formula (B1-21-b) obtained by the method described in JP-A-2008-209917, and a salt 35.50 represented by the formula (B1-21-a). Part, 100 parts of chloroform, and 50 parts of ion-exchanged water were stirred at 23 ° C. for 15 hours. Since the obtained reaction solution was separated into two layers, the chloroform layer was separated and taken out, and 30 parts of ion-exchanged water was further added to the chloroform layer and washed with water. This operation was repeated 5 times. The chloroform layer was concentrated, 100 parts of tert-butyl methyl ether was added to the resulting residue, and the mixture was stirred at 23 ° C. for 30 minutes, and then filtered to obtain the salt 48 represented by the formula (B1-21-c). .57 parts were obtained.

Figure 2017105770
式(B1−21−c)で表される塩20.00部、式(B1−21−d)で表される化合物2.84部及びモノクロロベンゼン250部を仕込み、23℃で30分間攪拌した。得られた混合液に、二安息香酸銅(II)0.21部を添加した後、更に、100℃で1時間攪拌した。得られた反応溶液を濃縮した後、得られた残渣に、クロロホルム200部及びイオン交換水50部を加えて23℃で30分間攪拌した後、分液して有機層を取り出した。回収された有機層にイオン交換水50部を加えて23℃で30分間攪拌した後、分液して有機層を取り出した。この水洗操作を5回繰り返した。得られた有機層を濃縮した後、得られた残渣を、アセトニトリル53.51部に溶解し、濃縮した後、tert−ブチルメチルエーテル113.05部を加えて攪拌した後、ろ過することにより、式(B1−21)で表される塩10.47部を得た。
Figure 2017105770
20.00 parts of a salt represented by the formula (B1-21-c), 2.84 parts of a compound represented by the formula (B1-21-d) and 250 parts of monochlorobenzene were charged and stirred at 23 ° C. for 30 minutes. . After adding 0.21 part of copper (II) dibenzoate to the obtained liquid mixture, it stirred at 100 degreeC for further 1 hour. After concentrating the obtained reaction solution, 200 parts of chloroform and 50 parts of ion-exchanged water were added to the obtained residue and stirred at 23 ° C. for 30 minutes, followed by liquid separation to take out an organic layer. 50 parts of ion-exchanged water was added to the collected organic layer and stirred at 23 ° C. for 30 minutes, followed by liquid separation to take out the organic layer. This washing operation was repeated 5 times. After concentrating the obtained organic layer, the obtained residue was dissolved in 53.51 parts of acetonitrile, concentrated, added with 113.05 parts of tert-butyl methyl ether, stirred, and then filtered. 10.47 parts of the salt represented by the formula (B1-21) were obtained.

MASS(ESI(+)Spectrum):M 237.1
MASS(ESI(−)Spectrum):M 339.1
MASS (ESI (+) Spectrum): M + 237.1
MASS (ESI (−) Spectrum): M - 339.1

合成例7[式(B1−22)で表される塩の合成]

Figure 2017105770
Synthesis Example 7 [Synthesis of salt represented by formula (B1-22)]
Figure 2017105770

式(B1−22−a)で表される塩11.26部、式(B1−22−b)で表される化合物10.00部、クロロホルム50部及びイオン交換水25部を仕込み、23℃で15時間攪拌した。得られた反応液が2層に分離していたので、クロロホルム層を分液して取り出し、更に、該クロロホルム層にイオン交換水15部を添加し、水洗した。この操作を5回繰り返した。クロロホルム層を濃縮し、得られた残渣に、tert−ブチルメチルエーテル50部を加えて23℃で30分間攪拌した後、ろ過することにより、式(B1−22−c)で表される塩11.75部を得た。   11.26 parts of a salt represented by the formula (B1-22-a), 10.00 parts of a compound represented by the formula (B1-22-b), 50 parts of chloroform and 25 parts of ion-exchanged water were charged at 23 ° C. For 15 hours. Since the obtained reaction liquid was separated into two layers, the chloroform layer was separated and taken out, and further 15 parts of ion-exchanged water was added to the chloroform layer and washed with water. This operation was repeated 5 times. The chloroform layer was concentrated, 50 parts of tert-butyl methyl ether was added to the resulting residue, the mixture was stirred at 23 ° C. for 30 minutes, and then filtered to obtain the salt 11 represented by the formula (B1-22-c). .75 parts were obtained.

Figure 2017105770
式(B1−22−c)で表される塩11.71部、式(B1−22−d)で表される化合物1.70部及びモノクロロベンゼン46.84部を仕込み、23℃で30分間攪拌した。得られた混合液に、二安息香酸銅(II)0.12部を添加し、更に、100℃で30分間攪拌した。得られた反応溶液を濃縮した。得られた残渣に、クロロホルム50部及びイオン交換水12.50部を加えて23℃で30分間攪拌した後、分液して有機層を取り出した。回収された有機層にイオン交換水12.50部を加えて23℃で30分間攪拌し、分液して有機層を取り出した。この水洗操作を8回繰り返した。得られた有機層を濃縮した。得られた残渣に、tert−ブチルメチルエーテル50部を加えて攪拌し、ろ過することにより、式(B1−22)で表される塩6.84部を得た。
Figure 2017105770
11.71 parts of a salt represented by the formula (B1-22-c), 1.70 parts of a compound represented by the formula (B1-22-d) and 46.84 parts of monochlorobenzene were charged, and the mixture was charged at 23 ° C. for 30 minutes. Stir. To the obtained mixed liquid, 0.12 part of copper (II) dibenzoate was added, and the mixture was further stirred at 100 ° C. for 30 minutes. The resulting reaction solution was concentrated. To the obtained residue, 50 parts of chloroform and 12.50 parts of ion-exchanged water were added and stirred at 23 ° C. for 30 minutes, followed by liquid separation to take out the organic layer. 12.50 parts of ion-exchanged water was added to the collected organic layer, stirred at 23 ° C. for 30 minutes, and separated to take out the organic layer. This washing operation was repeated 8 times. The obtained organic layer was concentrated. To the obtained residue, 50 parts of tert-butyl methyl ether was added, stirred, and filtered to obtain 6.84 parts of the salt represented by the formula (B1-22).

MASS(ESI(+)Spectrum):M 237.1
MASS(ESI(−)Spectrum):M 323.0
MASS (ESI (+) Spectrum): M + 237.1
MASS (ESI (-) Spectrum): M - 323.0

樹脂の合成
樹脂の合成において使用した化合物(モノマー)を下記に示す。

Figure 2017105770
以下、これらのモノマーを式番号に応じて「モノマー(a1−1−3)」等という。 Resin Synthesis The compounds (monomers) used in the resin synthesis are shown below.
Figure 2017105770
Hereinafter, these monomers are referred to as “monomer (a1-1-3)” or the like according to the formula number.

合成例8〔樹脂A1の合成〕
モノマーとして、モノマー(a1−1−3)、モノマー(a1−2−9)、モノマー(a2−1−3)及びモノマー(a3−4−2)を用い、そのモル比〔モノマー(a1−1−3):モノマー(a1−2−9):モノマー(a2−1−3):モノマー(a3−4−2)〕が45:14:2.5:38.5となるように混合し、全モノマー量の1.5質量倍のプロピレングリコールモノメチルエーテルアセテートを加えて溶液とした。この溶液に、開始剤としてアゾビスイソブチロニトリル及びアゾビス(2,4−ジメチルバレロニトリル)を全モノマー量に対して各々、1mol%及び3mol%添加し、これらを73℃で約5時間加熱した。得られた反応混合物を、大量のメタノール/水混合溶媒に注いで樹脂を沈殿させ、この樹脂をろ過した。得られた樹脂を再び、プロピレングリコールモノメチルエーテルアセテートに溶解させて得られる溶解液をメタノール/水混合溶媒に注いで樹脂を沈殿させ、この樹脂をろ過するという再沈殿操作を2回行い、重量平均分子量7.6×103の樹脂A1(共重合体)を収率68%で得た。この樹脂A1は、以下の構造単位を有するものである。

Figure 2017105770
Synthesis Example 8 [Synthesis of Resin A1]
As the monomer, monomer (a1-1-3), monomer (a1-2-9), monomer (a2-1-3) and monomer (a3-4-2) were used, and the molar ratio [monomer (a1-1 -3): Monomer (a1-2-9): Monomer (a2-1-3): Monomer (a3-4-2)] are mixed at 45: 14: 2.5: 38.5, A solution was prepared by adding propylene glycol monomethyl ether acetate of 1.5 mass times the total monomer amount. To this solution, 1 mol% and 3 mol% of azobisisobutyronitrile and azobis (2,4-dimethylvaleronitrile) as initiators were added to the total monomer amount, respectively, and these were heated at 73 ° C. for about 5 hours. did. The obtained reaction mixture was poured into a large amount of methanol / water mixed solvent to precipitate the resin, and this resin was filtered. The obtained resin was again dissolved in propylene glycol monomethyl ether acetate, and the resulting solution was poured into a methanol / water mixed solvent to precipitate the resin, followed by reprecipitation operation of filtering the resin twice. Resin A1 (copolymer) having a molecular weight of 7.6 × 10 3 was obtained in a yield of 68%. This resin A1 has the following structural units.
Figure 2017105770

実施例5〔樹脂X1の合成〕
モノマーとして、モノマー(I−1)及びモノマー(a4−1−x1)を用い、そのモル比〔モノマー(I−1):モノマー(a4−1−x1)〕が3:97となるように混合し、全モノマー量の1.5質量倍のプロピレングリコールモノメチルエーテルアセテートを加えて溶液とした。この溶液に、開始剤としてアゾビスイソブチロニトリルを全モノマー量に対して、12mol%添加し、これらを75℃で約5時間加熱した。得られた反応混合物を、大量のメタノール/水混合溶媒に注いで樹脂を沈殿させ、この樹脂をろ過した。得られた樹脂を再び、メタノールに注いでリパルプし、この樹脂をろ過することにより、重量平均分子量1.1×10の樹脂X1を収率73%で得た。この樹脂X1は、以下の構造単位を有するものである。

Figure 2017105770
Example 5 [Synthesis of Resin X1]
Monomer (I-1) and monomer (a4-1-x1) are used as monomers and mixed so that the molar ratio [monomer (I-1): monomer (a4-1-x1)] is 3:97. Then, 1.5 mass times propylene glycol monomethyl ether acetate of the total monomer amount was added to make a solution. To this solution, 12 mol% of azobisisobutyronitrile as an initiator was added with respect to the total monomer amount, and these were heated at 75 ° C. for about 5 hours. The obtained reaction mixture was poured into a large amount of methanol / water mixed solvent to precipitate the resin, and this resin was filtered. The obtained resin was again poured into methanol and repulped, and this resin was filtered to obtain a resin X1 having a weight average molecular weight of 1.1 × 10 4 in a yield of 73%. This resin X1 has the following structural units.
Figure 2017105770

実施例6〔樹脂X2の合成〕
モノマーとして、モノマー(I−1)及びモノマー(a4−1−4)を用い、そのモル比(モノマー(I−1):モノマー(a4−1−4))が2:98となるように混合し、全モノマー量の1.5質量倍のメチルイソブチルケトンを加えて溶液とした。この溶液に、開始剤としてアゾビスイソブチロニトリルを全モノマー量に対して、10mol%添加し、これらを75℃で約5時間加熱した。得られた反応混合物を、大量のメタノール/水混合溶媒に注いで樹脂を沈殿させ、この樹脂をろ過し、重量平均分子量1.2×10の樹脂X2(共重合体)を収率75%で得た。この樹脂X2は、以下の構造単位を有するものである。

Figure 2017105770
Example 6 [Synthesis of Resin X2]
Monomer (I-1) and monomer (a4-1-4) are used as monomers and mixed so that the molar ratio (monomer (I-1): monomer (a4-1-4)) is 2:98. Then, 1.5 mass times methyl isobutyl ketone of the total monomer amount was added to make a solution. To this solution, 10 mol% of azobisisobutyronitrile as an initiator was added with respect to the total monomer amount, and these were heated at 75 ° C. for about 5 hours. The obtained reaction mixture was poured into a large amount of methanol / water mixed solvent to precipitate a resin, and this resin was filtered to obtain a resin X2 (copolymer) having a weight average molecular weight of 1.2 × 10 4 with a yield of 75%. Got in. This resin X2 has the following structural units.
Figure 2017105770

実施例7〔樹脂X3の合成〕
モノマーとして、モノマー(I−2)及びモノマー(a4−1−x2)を用い、そのモル比〔モノマー(I−2):モノマー(a4−1−x2)〕が3:97となるように混合し、全モノマー量の1.5質量倍のプロピレングリコールモノメチルエーテルアセテートを加えて溶液とした。この溶液に、開始剤としてアゾビスイソブチロニトリルを全モノマー量に対して、12mol%添加し、これらを75℃で約5時間加熱した。得られた反応混合物を、大量のメタノール/水混合溶媒に注いで樹脂を沈殿させ、この樹脂をろ過した。得られた樹脂を再び、メタノールに注いでリパルプし、この樹脂をろ過することにより、重量平均分子量1.0×10の樹脂X3を収率70%で得た。この樹脂X3は、以下の構造単位を有するものである。

Figure 2017105770
Example 7 [Synthesis of Resin X3]
Monomer (I-2) and monomer (a4-1-x2) are used as monomers and mixed so that the molar ratio [monomer (I-2): monomer (a4-1-x2)] is 3:97. Then, 1.5 mass times propylene glycol monomethyl ether acetate of the total monomer amount was added to make a solution. To this solution, 12 mol% of azobisisobutyronitrile as an initiator was added with respect to the total monomer amount, and these were heated at 75 ° C. for about 5 hours. The obtained reaction mixture was poured into a large amount of methanol / water mixed solvent to precipitate the resin, and this resin was filtered. The obtained resin was again poured into methanol and repulped, and this resin was filtered to obtain Resin X3 having a weight average molecular weight of 1.0 × 10 4 in a yield of 70%. This resin X3 has the following structural units.
Figure 2017105770

実施例8〔樹脂X4の合成〕
モノマーとして、モノマー(I−2)及びモノマー(a4−1−4)を用い、そのモル比(モノマー(I−2):モノマー(a4−1−4))が2:98となるように混合し、全モノマー量の1.5質量倍のメチルイソブチルケトンを加えて溶液とした。この溶液に、開始剤としてアゾビスイソブチロニトリルを全モノマー量に対して、10mol%添加し、これらを75℃で約5時間加熱した。得られた反応混合物を、大量のメタノール/水混合溶媒に注いで樹脂を沈殿させ、この樹脂をろ過し、重量平均分子量1.1×10の樹脂X4(共重合体)を収率73%で得た。この樹脂X4は、以下の構造単位を有するものである。

Figure 2017105770
Example 8 [Synthesis of Resin X4]
Monomer (I-2) and monomer (a4-1-4) are used as monomers and mixed so that the molar ratio (monomer (I-2): monomer (a4-1-4)) is 2:98. Then, 1.5 mass times methyl isobutyl ketone of the total monomer amount was added to make a solution. To this solution, 10 mol% of azobisisobutyronitrile as an initiator was added with respect to the total monomer amount, and these were heated at 75 ° C. for about 5 hours. The obtained reaction mixture was poured into a large amount of methanol / water mixed solvent to precipitate a resin, and this resin was filtered to obtain a resin X4 (copolymer) having a weight average molecular weight of 1.1 × 10 4 in a yield of 73%. Got in. This resin X4 has the following structural units.
Figure 2017105770

実施例9〔樹脂X5の合成〕
モノマーとして、モノマー(I−7)及びモノマー(a4−1−x7)を用い、そのモル比〔モノマー(I−7):モノマー(a4−1−x7)〕が3:97となるように混合し、全モノマー量の1.5質量倍のプロピレングリコールモノメチルエーテルアセテートを加えて溶液とした。この溶液に、開始剤としてアゾビスイソブチロニトリルを全モノマー量に対して、12mol%添加し、これらを75℃で約5時間加熱した。得られた反応混合物を、大量のメタノール/水混合溶媒に注いで樹脂を沈殿させ、この樹脂をろ過した。得られた樹脂を再び、メタノールに注いでリパルプし、この樹脂をろ過することにより、重量平均分子量9.9×10の樹脂X5を収率68%で得た。この樹脂X5は、以下の構造単位を有するものである。

Figure 2017105770
Example 9 [Synthesis of Resin X5]
Monomer (I-7) and monomer (a4-1-x7) are used as monomers and mixed so that the molar ratio [monomer (I-7): monomer (a4-1-x7)] is 3:97. Then, 1.5 mass times propylene glycol monomethyl ether acetate of the total monomer amount was added to make a solution. To this solution, 12 mol% of azobisisobutyronitrile as an initiator was added with respect to the total monomer amount, and these were heated at 75 ° C. for about 5 hours. The obtained reaction mixture was poured into a large amount of methanol / water mixed solvent to precipitate the resin, and this resin was filtered. The obtained resin was again poured into methanol and repulped, and this resin was filtered to obtain Resin X5 having a weight average molecular weight of 9.9 × 10 3 in a yield of 68%. This resin X5 has the following structural units.
Figure 2017105770

実施例10〔樹脂X6の合成〕
モノマーとして、モノマー(I−8)及びモノマー(a4−1−x8)を用い、そのモル比〔モノマー(I−8):モノマー(a4−1−x8)〕が3:97となるように混合し、全モノマー量の1.5質量倍のプロピレングリコールモノメチルエーテルアセテートを加えて溶液とした。この溶液に、開始剤としてアゾビスイソブチロニトリルを全モノマー量に対して、12mol%添加し、これらを75℃で約5時間加熱した。得られた反応混合物を、大量のメタノール/水混合溶媒に注いで樹脂を沈殿させ、この樹脂をろ過した。得られた樹脂を再び、メタノールに注いでリパルプし、この樹脂をろ過することにより、重量平均分子量9.2×10の樹脂X6を収率63%で得た。この樹脂X6は、以下の構造単位を有するものである。

Figure 2017105770
Example 10 [Synthesis of Resin X6]
Monomer (I-8) and monomer (a4-1-x8) are used as monomers and mixed so that the molar ratio [monomer (I-8): monomer (a4-1-x8)] is 3:97. Then, 1.5 mass times propylene glycol monomethyl ether acetate of the total monomer amount was added to make a solution. To this solution, 12 mol% of azobisisobutyronitrile as an initiator was added with respect to the total monomer amount, and these were heated at 75 ° C. for about 5 hours. The obtained reaction mixture was poured into a large amount of methanol / water mixed solvent to precipitate the resin, and this resin was filtered. The obtained resin was again poured into methanol and repulped, and this resin was filtered to obtain Resin X6 having a weight average molecular weight of 9.2 × 10 3 in a yield of 63%. This resin X6 has the following structural units.
Figure 2017105770

合成例9〔樹脂XX1の合成〕
モノマーとして、モノマー(IX−1)及びモノマー(a4−1−7)を用い、そのモル比(モノマー(IX−1):モノマー(a4−1−7))が2:98となるように混合し、全モノマー量の1.5質量倍のメチルイソブチルケトンを加えて溶液とした。この溶液に、開始剤としてアゾビスイソブチロニトリルを全モノマー量に対して、10mol%添加し、これらを75℃で約5時間加熱した。得られた反応混合物を、大量のメタノール/水混合溶媒に注いで樹脂を沈殿させ、この樹脂をろ過し、重量平均分子量1.2×10の樹脂XX1(共重合体)を収率83%で得た。この樹脂XX1は、以下の構造単位を有するものである。

Figure 2017105770
Synthesis Example 9 [Synthesis of Resin XX1]
Monomer (IX-1) and monomer (a4-1-7) are used as monomers and mixed so that the molar ratio (monomer (IX-1): monomer (a4-1-7)) is 2:98. Then, 1.5 mass times methyl isobutyl ketone of the total monomer amount was added to make a solution. To this solution, 10 mol% of azobisisobutyronitrile as an initiator was added with respect to the total monomer amount, and these were heated at 75 ° C. for about 5 hours. The obtained reaction mixture was poured into a large amount of methanol / water mixed solvent to precipitate a resin, and this resin was filtered to obtain a resin XX1 (copolymer) having a weight average molecular weight of 1.2 × 10 4 in a yield of 83%. I got it. This resin XX1 has the following structural units.
Figure 2017105770

<レジスト組成物の調製>
以下に示す成分の各々を表1に示す質量部で混合して溶剤に溶解し、孔径0.2μmのフッ素樹脂製フィルターでろ過して、レジスト組成物を調製した。
<Preparation of resist composition>
Each of the components shown below was mixed in parts by mass shown in Table 1, dissolved in a solvent, and filtered through a fluororesin filter having a pore size of 0.2 μm to prepare a resist composition.

Figure 2017105770
Figure 2017105770

<樹脂(A)>
A1、X1〜X6、XX1:樹脂A1、樹脂X1〜樹脂X6、樹脂XX1
<Resin (A)>
A1, X1 to X6, XX1: Resin A1, Resin X1 to Resin X6, Resin XX1

<酸発生剤(B)>
B1−5:式(B1−5)で表される塩
B1−21:式(B1−21)で表される塩
B1−22:式(B1−22)で表される塩
B1−3:特開2010−152341号公報の実施例に従って合成

Figure 2017105770
<Acid generator (B)>
B1-5: salt represented by formula (B1-5) B1-21: salt represented by formula (B1-21) B1-22: salt represented by formula (B1-22) B1-3: special Synthesis according to the examples of JP 2010-152341
Figure 2017105770

<クエンチャー(C)>
D1:(東京化成工業(株)製)

Figure 2017105770
<Quencher (C)>
D1: (Tokyo Chemical Industry Co., Ltd.)
Figure 2017105770

<溶剤>
プロピレングリコールモノメチルエーテルアセテート 265部
プロピレングリコールモノメチルエーテル 20部
2−ヘプタノン 20部
γ−ブチロラクトン 3.5部
<Solvent>
Propylene glycol monomethyl ether acetate 265 parts Propylene glycol monomethyl ether 20 parts 2-heptanone 20 parts γ-butyrolactone 3.5 parts

<レジスト組成物の液浸露光評価>
シリコンウェハに、有機反射防止膜用組成物(ARC−29;日産化学(株)製)を塗布して、205℃、60秒の条件でベークすることによって、厚さ78nmの有機反射防止膜を形成した。次いで、この有機反射防止膜の上に、上記のレジスト組成物を乾燥後の膜厚が85nmとなるようにスピンコートした。レジスト組成物を塗布したシリコンウェハをダイレクトホットプレート上にて、表1の「PB」欄に記載された温度で60秒間プリベークし、レジスト組成物層を形成した。レジスト組成物層が形成されたシリコンウェハに、液浸露光用ArFエキシマステッパー(XT:1900Gi;ASML社製、NA=1.35、3/4Annular X−Y偏光)で、コンタクトホールパターン(ホールピッチ100nm/ホール径70nm)を形成するためのマスクを用いて、露光量を段階的に変化させて露光した。なお、液浸媒体としては超純水を使用した。
露光後、前記シリコンウェハを、ホットプレート上にて、表1の「PEB」欄に記載された温度で60秒間ポストエキスポジャーベーク処理した。次いでこのシリコンウェハを、2.38%テトラメチルアンモニウムヒドロキシド水溶液で60秒間のパドル現像を行った。
<Immersion exposure evaluation of resist composition>
An organic antireflective coating composition (ARC-29; manufactured by Nissan Chemical Co., Ltd.) is applied to a silicon wafer and baked at 205 ° C. for 60 seconds to form an organic antireflective coating having a thickness of 78 nm. Formed. Next, the above resist composition was spin-coated on this organic antireflection film so that the film thickness after drying was 85 nm. The silicon wafer coated with the resist composition was pre-baked on a direct hot plate at the temperature described in the “PB” column of Table 1 for 60 seconds to form a resist composition layer. A contact hole pattern (hole pitch) is formed on a silicon wafer on which a resist composition layer has been formed using an ArF excimer stepper for immersion exposure (XT: 1900 Gi; manufactured by ASML, NA = 1.35, 3/4 Annular XY polarized light). Using a mask for forming (100 nm / hole diameter 70 nm), the exposure amount was changed stepwise to perform exposure. Note that ultrapure water was used as the immersion medium.
After the exposure, the silicon wafer was post-exposure baked on a hot plate at a temperature described in the “PEB” column of Table 1 for 60 seconds. Next, this silicon wafer was subjected to paddle development for 60 seconds with a 2.38% tetramethylammonium hydroxide aqueous solution.

各レジスト組成物層から、ホール径70nmのマスクで形成したパターンのホール径が55nmとなる露光量を実効感度とした。   From each resist composition layer, an exposure amount at which the hole diameter of a pattern formed with a mask having a hole diameter of 70 nm was 55 nm was defined as effective sensitivity.

<フォーカスマージン評価(DOF)>
実効感度において、フォーカスを振った場合、線幅が55nm±5%の幅にある範囲(52.5〜57.7nm)をDOFとした。結果を表2に示す。
<Focus margin evaluation (DOF)>
In the effective sensitivity, when the focus is shaken, a range (52.5 to 57.7 nm) in which the line width is 55 nm ± 5% is defined as DOF. The results are shown in Table 2.

Figure 2017105770
Figure 2017105770

上記の結果から、本発明の化合物に由来する構造単位を有する樹脂レジスト組成物によれば、フォーカスマージンが良好であることがわかる。   From the above results, it is understood that the focus margin is good according to the resin resist composition having a structural unit derived from the compound of the present invention.

本発明のレジスト組成物は、フォーカスマージンが良好であり、半導体の微細加工に有用である。   The resist composition of the present invention has a good focus margin and is useful for fine processing of semiconductors.

Claims (8)

式(I)で表される化合物。
Figure 2017105770
[式(I)中、
及びRは、それぞれ独立に、ハロゲン原子を有してもよい炭素数1〜6のアルキル基、水素原子又はハロゲン原子を表す。
及びLは、それぞれ独立に、−CHR−CH−又は−CH−CHR−を表す。
及びRは、それぞれ独立に、炭素数1〜6のアルキル基を表す。
は、フッ素原子を有する炭素数1〜12の2価の炭化水素基を表す。]
A compound represented by formula (I).
Figure 2017105770
[In the formula (I),
R 1 and R 2 each independently represents a C 1-6 alkyl group which may have a halogen atom, a hydrogen atom or a halogen atom.
L 1 and L 2 each independently represent —CHR 3 —CH 2 — or —CH 2 —CHR 4 —.
R 3 and R 4 each independently represents an alkyl group having 1 to 6 carbon atoms.
A 3 represents a divalent hydrocarbon group having 1 to 12 carbon atoms having a fluorine atom. ]
及びRが、メチル基である請求項1記載の化合物。 The compound according to claim 1, wherein R 3 and R 4 are methyl groups. 請求項1又は2記載の化合物に由来する構造単位を有する樹脂。   A resin having a structural unit derived from the compound according to claim 1. さらに、フッ素原子を有する構造単位(a4)を有する請求項3記載の樹脂。   Furthermore, resin which has a structural unit (a4) which has a fluorine atom. 請求項3又は4記載の樹脂、酸不安定基を有する構造単位を有する樹脂及び酸発生剤を含有するレジスト組成物。   A resist composition comprising the resin according to claim 3, the resin having a structural unit having an acid labile group, and an acid generator. 酸発生剤が、式(B1)で表される塩である請求項5記載のレジスト組成物。
Figure 2017105770
[式(B1)中、
1及びQ2は、それぞれ独立に、フッ素原子又は炭素数1〜6のペルフルオロアルキル基を表す。
b1は、置換基を有していてもよい炭素数1〜24の2価の飽和炭化水素基を表し、該2価の飽和炭化水素基に含まれる−CH2−は、−O−又は−CO−に置き換わっていてもよく、該2価の飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基で置換されていてもよい。
Yは、置換基を有していてもよいメチル基又は置換基を有していてもよい炭素数3〜18の1価の脂環式炭化水素基を表し、該メチル基及び該1価の脂環式炭化水素基に含まれる−CH2−は、−O−、−SO2−又は−CO−に置き換わっていてもよい。
+は、有機カチオンを表す。]
The resist composition according to claim 5, wherein the acid generator is a salt represented by the formula (B1).
Figure 2017105770
[In the formula (B1),
Q 1 and Q 2 each independently represents a fluorine atom or a C 1-6 perfluoroalkyl group.
L b1 represents a C1-C24 divalent saturated hydrocarbon group which may have a substituent, and —CH 2 — contained in the divalent saturated hydrocarbon group is —O— or -CO- may be substituted, and the hydrogen atom contained in the divalent saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group.
Y represents a methyl group which may have a substituent or a monovalent alicyclic hydrocarbon group having 3 to 18 carbon atoms which may have a substituent, and the methyl group and the monovalent —CH 2 — contained in the alicyclic hydrocarbon group may be replaced with —O—, —SO 2 — or —CO—.
Z + represents an organic cation. ]
酸発生剤から発生する酸よりも酸性度の弱い酸を発生する塩をさらに含有する請求項5又は6記載のレジスト組成物。   The resist composition according to claim 5 or 6, further comprising a salt that generates an acid having a lower acidity than an acid generated from the acid generator. (1)請求項5〜7のいずれかに記載のレジスト組成物を基板上に塗布する工程、
(2)塗布後の組成物を乾燥させて組成物層を形成する工程、
(3)組成物層に露光する工程、
(4)露光後の組成物層を加熱する工程、及び
(5)加熱後の組成物層を現像する工程、
を含むレジストパターンの製造方法。
(1) The process of apply | coating the resist composition in any one of Claims 5-7 on a board | substrate,
(2) The process of drying the composition after application | coating and forming a composition layer,
(3) a step of exposing the composition layer;
(4) a step of heating the composition layer after exposure, and (5) a step of developing the composition layer after heating,
A method for producing a resist pattern including:
JP2016232322A 2015-12-09 2016-11-30 Method for producing compound, resin, resist composition and resist pattern Active JP6905330B2 (en)