JP2010247436A - Synthetic resin laminated sheet and usage of the same - Google Patents

Synthetic resin laminated sheet and usage of the same Download PDF

Info

Publication number
JP2010247436A
JP2010247436A JP2009099628A JP2009099628A JP2010247436A JP 2010247436 A JP2010247436 A JP 2010247436A JP 2009099628 A JP2009099628 A JP 2009099628A JP 2009099628 A JP2009099628 A JP 2009099628A JP 2010247436 A JP2010247436 A JP 2010247436A
Authority
JP
Japan
Prior art keywords
synthetic resin
sheet
layer
magnetic
resin laminated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2009099628A
Other languages
Japanese (ja)
Inventor
Katsunori Ishii
勝徳 石井
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MAG LIFE KK
Original Assignee
MAG LIFE KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MAG LIFE KK filed Critical MAG LIFE KK
Priority to JP2009099628A priority Critical patent/JP2010247436A/en
Publication of JP2010247436A publication Critical patent/JP2010247436A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a synthetic resin laminated sheet for general purposes, capable of realizing adsorption through strong adhesion and preparing a beautiful printing whereby the sheet can be used for various kind of usages. <P>SOLUTION: A synthetic resin laminated sheet 11 consists only of a magnetic layer 12 having a pre-determined thickness which is prepared from a flexible synthetic resin containing magnetic powder 12a, and of a flexible printable layer 13 having a smaller thickness than the magnetic layer 12 which is prepared from a white synthetic resin on which printing by a non-aqueous inkjet printer can be conducted and which is laminated only on one surface of the magnetic layer 12. The sheet can be used as an adsorption sheet to be adsorbed to a sheet opposite against the magnetic sheet, as a tapestry, an indication board and the like. <P>COPYRIGHT: (C)2011,JPO&INPIT

Description

この発明は、たとえば、掲示、広告、案内、装飾などに用いられるほか、日用品や学習教材の資材としても幅広く好適に活用できるような合成樹脂積層シートに関し、より詳しくは磁性体を有する合成樹脂積層シートに関する。   The present invention relates to a synthetic resin laminated sheet that can be used for, for example, posting, advertisement, guidance, decoration, etc., as well as materials for daily necessities and learning materials. More specifically, the present invention relates to a synthetic resin laminated sheet having a magnetic material. Regarding the sheet.

磁性体を有する被吸着シートやマグネットシートは、様々に使用されている。たとえば、磁化されてない非磁化状態の磁性体を有する被吸着シートの場合には、掲示板のための資材や壁紙等としての利用が提案されている。このようなものとしては下記特許文献1、2、3、4に開示されたものがある。   Adsorbed sheets and magnetic sheets having a magnetic material are used in various ways. For example, in the case of an adsorbed sheet having a non-magnetized magnetic material that is not magnetized, use as a material for a bulletin board, wallpaper, or the like has been proposed. As such a thing, there exists what was disclosed by the following patent documents 1, 2, 3, and 4. FIG.

これらの被吸着シートの磁性体は、粉状のもので構成され塗料に混合してシート材に塗布したり(特許文献3、4参照)、金属箔で構成されてシート材に貼り付けられたり(特許文献1、2参照)して、被吸着シートの一部に層状に付与される。しかし、これらのようにして構成されているので、磁性体を有する層は薄く、磁石に引き付けられる力が弱かった。   The magnetic material of these adsorbed sheets is composed of powder and mixed with paint and applied to the sheet material (see Patent Documents 3 and 4), or composed of metal foil and attached to the sheet material. (See Patent Documents 1 and 2), and is applied in a layered manner to a part of the adsorbed sheet. However, since it is configured as described above, the layer having the magnetic material is thin, and the force attracted to the magnet is weak.

磁化された磁性体を有するマグネットシートの場合には、広告等の表示のために掲示板や自動車のボディー等の磁石が吸着可能な場所に貼り付けて用いられている。このようなものとしては下記特許文献5、6に開示されたものがある。   In the case of a magnet sheet having a magnetized magnetic material, it is used by being attached to a place where a magnet such as a bulletin board or a car body can be adsorbed for displaying advertisements or the like. Examples of this include those disclosed in Patent Documents 5 and 6 below.

これらのマグネットシートの磁性体は、粉状のもので構成され、合成樹脂に混合してシート状に形成して、マグネットシートの一部に磁石層として付与される。   The magnetic material of these magnet sheets is composed of a powdery material, mixed with a synthetic resin, formed into a sheet shape, and applied as a magnet layer to a part of the magnet sheet.

このマグネットシートでは、他の磁性体を吸着してその吸着状態を維持しなければならないので、強い磁力を持つことが望ましいが、広告等の表示のために印刷が行えるようにするには、少なくとも所定の厚さ以下であることが必要である。このため、磁性体を有する磁石層を厚くして磁力を高めるにも限界がある。一方で、高めにくい磁力を減殺させずに吸着力を得るためには、マグネットシートの軽さも必要である。しかしまた、美麗な印刷を可能にするには、印刷を行う部分の厚さもある程度は必要となる。   In this magnetic sheet, it is desirable to have a strong magnetic force because other magnetic materials must be adsorbed to maintain the adsorbed state, but at least in order to be able to perform printing for displaying advertisements, etc. It is necessary to have a predetermined thickness or less. For this reason, there is a limit in increasing the magnetic force by increasing the thickness of the magnet layer having the magnetic material. On the other hand, the magnet sheet needs to be light in order to obtain an attractive force without diminishing the magnetic force that is difficult to increase. However, in order to enable beautiful printing, the thickness of the portion to be printed is also required to some extent.

これらのような相矛盾する要求を実現することは難しく、前記特許文献5、6に開示されたようなマグネットシートでは満足が得られるものではなかったところ、本出願人は、そのような問題を解決できる大型インクジェットプリンタ用マグネットシート(下記特許文献7参照)を提案した。このシートは、屋外広告用のマグネットシートで、強い吸着力が得られ、美麗な印刷が可能にしたもので、厚さ0.4mmの磁石層と厚さ0.1mmの塩化ビニルからなる印刷層を有するものである。   It is difficult to realize such contradictory requirements, and the applicant has not been satisfied with the magnet sheet disclosed in Patent Documents 5 and 6, but the present applicant has found such a problem. A magnetic sheet for a large-scale inkjet printer that can be solved (see Patent Document 7 below) has been proposed. This sheet is a magnetic sheet for outdoor advertising, which has a strong adsorptive power and enables beautiful printing. A printing layer comprising a 0.4 mm thick magnet layer and a 0.1 mm thick vinyl chloride It is what has.

特開2001−166719号公報JP 2001-166719 A 特開2005−274660号公報JP 2005-274660 A 特開平11−272217号公報Japanese Patent Laid-Open No. 11-272217 特開平9−1743号公報JP-A-9-1743 特開2004−29095号公報Japanese Patent Laid-Open No. 2004-29095 特許第2848582号公報Japanese Patent No. 2848582 登録実用新案第3117937号公報Registered Utility Model No. 3117937

このマグネットシートによれば、所期の目的を達成できて実用的価値が高いものの、このマグネットシートが吸着する相手方は、前述例のような掲示板や自動車のボディーなどのような硬い部分に限られていた。前述したように、非磁化状態の磁性体を有する被吸着シートが強い吸着力を発揮させられないからである。   According to this magnet sheet, the intended purpose can be achieved and the practical value is high, but the opponent to which this magnet sheet is adsorbed is limited to hard parts such as bulletin boards and automobile bodies as in the above example. It was. This is because, as described above, the attracted sheet having the non-magnetized magnetic material cannot exert a strong attracting force.

また、特に非磁化状態の磁性体を有する被吸着シートにおいては、たとえば掲示用などと用途が限定されており、汎用性のあるものではなかった。前記特許文献1などのように接着剤層が備えられたものではさらに、接着剤の種類によって貼り付け可能な対象が限定されたり、再粘着ができなかったりと、使い方まで制限され、自由な使用ができなかった。   In particular, the attracted sheet having a magnetic material in a non-magnetized state is not versatile because its use is limited, for example, for posting. In the case where the adhesive layer is provided as in the above-mentioned Patent Document 1, the object that can be pasted is limited depending on the type of the adhesive, or it cannot be re-adhered, and the usage is limited. I could not.

そこで、この発明は、強い吸着力による吸着を可能にできるとともに必要であるなら美麗な印刷も可能であって、必要に応じて様々に自由度高く使用できる汎用性のある合成樹脂積層シートとその使用方法の提供を主たる目的とする。   Therefore, the present invention is capable of adsorbing with a strong adsorbing force and capable of beautiful printing if necessary, and a versatile synthetic resin laminated sheet that can be used in various degrees of freedom as required, and its The main purpose is to provide usage.

そのための手段は、磁性粉体を含有し可撓性を有する合成樹脂製で一定の厚さを有する磁性層と、該磁性層の片面のみにラミネートされて、非水性インクジェットプリンタによる印刷が可能な白色を呈する合成樹脂製で前記磁性層よりも薄く可撓性を有する印刷許容層のみからなる合成樹脂積層シートである。   For this purpose, a magnetic layer containing a magnetic powder and made of a flexible synthetic resin and having a certain thickness is laminated on only one surface of the magnetic layer so that printing by a non-aqueous inkjet printer is possible. It is a synthetic resin laminated sheet made of a synthetic resin exhibiting white and made of only a print-allowing layer that is thinner than the magnetic layer and has flexibility.

前記非水性シンクジェットプリンタのインクには、ソルベントインク(溶剤系インク)やUV硬化型インク、ミューバイオインク(環境対応型インク)などがある。   Examples of the ink of the non-aqueous sink jet printer include solvent ink (solvent ink), UV curable ink, and mu bio ink (environment-friendly ink).

前記磁性粉体には、磁性ナノ粒子が好適に用いられる。   Magnetic nanoparticles are preferably used for the magnetic powder.

前記磁性層は磁石に吸着されたり磁石として他の部材を吸着したり、印刷許容層を支持したりする機能を果たす。一方、前記印刷許容層は、磁性層を隠蔽したり必要に応じて印刷のインキをのせたりするなどの機能を果たす。印刷許容層は磁性層よりも薄く、非水性インクジェットプリンタによる印刷が可能な範囲内でそれぞれの層が必要な機能を果たせるように各層の厚さは設定される。   The magnetic layer functions to be adsorbed by a magnet, to adsorb another member as a magnet, and to support a print permitting layer. On the other hand, the print-accepting layer functions to conceal the magnetic layer and to apply printing ink as necessary. The print-allowable layer is thinner than the magnetic layer, and the thickness of each layer is set so that each layer can perform a necessary function within a range in which printing by a non-aqueous inkjet printer is possible.

このような合成樹脂積層シートは、必要に応じて印刷許容層に所望の印刷をし、また必要に応じて適宜裁断して使用される。磁性層が磁化状態であれば掲示板や自動車のボディー等にそのまま固定することができ、磁性層が非磁化状態であればマグネットシート等にそのまま固定することができる。必要ならば磁性層または印刷許容層の表面に粘着剤を塗布するなどして壁面やガラス面等に固定することも可能である。また硬質のシート材等に貼り合わせて、カッターマットや粘土板、画板、遊戯板、教材など、日用品や学習教材等の資材として使用することもできる。貼り合わせる部材は、たとえば壁紙等の柔軟なシート材であるもよい。   Such a synthetic resin laminated sheet is used by performing desired printing on the print permitting layer as necessary, and appropriately cutting as necessary. If the magnetic layer is in a magnetized state, it can be fixed as it is to a bulletin board or an automobile body, and if the magnetic layer is in a non-magnetized state, it can be fixed as it is to a magnet sheet or the like. If necessary, it can be fixed to a wall surface, a glass surface or the like by applying an adhesive to the surface of the magnetic layer or the printable layer. It can also be used as a material for daily necessities and learning materials such as cutter mats, clay plates, drawing boards, game boards, educational materials, etc. by bonding them to hard sheet materials. The member to be bonded may be a flexible sheet material such as wallpaper.

特に、前述のように壁面等に固定するほかに、当該合成樹脂積層シートの前記印刷許容層に印刷をしたのち、合成樹脂積層シートの上下両端部に、合成樹脂積層シートを張設するための張設用部材を取り付けて張設して使用すると、壁面を損傷したりすることなく、掲示板機能や装飾機能などを発揮させることができる。この場合には、特に、展示会や見本市などの展示ブースの壁面に取り付けるようにすると、展示ブースの準備や後片付けが簡易迅速に行えるようになるほか、展示内容の変更も容易であり、さらに展示ブースのパネルを傷めたりすることを回避できる。   In particular, in addition to fixing to a wall surface or the like as described above, after printing on the print-allowable layer of the synthetic resin laminated sheet, the synthetic resin laminated sheet is stretched on both upper and lower ends of the synthetic resin laminated sheet. When the tension member is attached and stretched, the bulletin board function and the decoration function can be exhibited without damaging the wall surface. In this case, especially if it is attached to the wall of an exhibition booth such as an exhibition or trade show, the exhibition booth can be easily prepared and cleaned up, and the contents of the exhibition can be easily changed. You can avoid damaging the booth panel.

以上のように、この発明によれば、強い吸着力による吸着を可能にできるとともに、必要であるなら美麗な印刷も可能である。また、磁性層と印刷許容層のみからなるので、必要に応じて様々に自由度高く使用できる汎用性のある合成樹脂積層シートとなる。   As described above, according to the present invention, it is possible to perform adsorption by a strong adsorption force, and it is possible to perform beautiful printing if necessary. Moreover, since it consists only of a magnetic layer and a printing permissible layer, it becomes a versatile synthetic resin laminated sheet that can be used with various degrees of freedom as required.

合成樹脂積層シートの斜視図と断面図。The perspective view and sectional drawing of a synthetic resin laminated sheet. 吸着力の試験方法と試験結果。Adsorption power test method and test results. 合成樹脂積層シートの断面図。Sectional drawing of a synthetic resin laminated sheet. 大型インクジェットプリンタの概略構成図。1 is a schematic configuration diagram of a large inkjet printer. 印刷時の状態を示す断面図。Sectional drawing which shows the state at the time of printing. バナーとしての使用方法を示す合成樹脂シートの斜視図。The perspective view of the synthetic resin sheet which shows the usage method as a banner. タペストリしての使用方法を示す斜視図。The perspective view which shows the usage method by tapestry. タペストリとしての展示ブースでの使用方法を示す斜視図。The perspective view which shows the usage method in the exhibition booth as a tapestry. タペストリとしての使用方法の一例を示す斜視図。The perspective view which shows an example of the usage method as a tapestry. タペストリとしての使用方法の一例を示す斜視図。The perspective view which shows an example of the usage method as a tapestry. 他の例に係る合成樹脂積層シートとマグネットシートの断面図。Sectional drawing of the synthetic resin laminated sheet and magnet sheet which concern on another example. 他の使用方法を示す断面図。Sectional drawing which shows the other usage method. 他の使用方法を示す断面図。Sectional drawing which shows the other usage method. 他の使用方法を示す断面図。Sectional drawing which shows the other usage method. 掲示板を示す斜視図と断面図。The perspective view and sectional drawing which show a bulletin board. 他の例の掲示板を示す斜視図。The perspective view which shows the bulletin board of another example. お風呂で使えるマルチボードの斜視図。A perspective view of a multi-board that can be used in a bath. カッターマットと定規の斜視図。The perspective view of a cutter mat and a ruler. 作品展示用シートの斜視図。The perspective view of the sheet | seat for work display.

この発明を実施するための一形態を、以下図面を用いて説明する。
図1は、合成樹脂積層シート11の斜視図とその断面構造を示す一部拡大断面図であり、この図に示すように、合成樹脂積層シート11はロール状に巻取り可能な柔軟性を有する可撓性シートで、特に大型インクジェットプリンタで印刷するのに適した1000mmほどの幅広に形成され、磁性層12と、この磁性層12の片面のみにラミネートされた印刷許容層13のみからなる。
An embodiment for carrying out the present invention will be described below with reference to the drawings.
FIG. 1 is a perspective view of a synthetic resin laminate sheet 11 and a partially enlarged sectional view showing a sectional structure thereof. As shown in this figure, the synthetic resin laminate sheet 11 has a flexibility that can be wound into a roll. The flexible sheet is formed of a magnetic layer 12 and a print-allowable layer 13 laminated on only one surface of the magnetic layer 12 and is formed to have a width of about 1000 mm suitable for printing with a large ink jet printer.

前記磁性層12は、磁性粉体12aを含有する可撓性を有した合成樹脂製で、カレンダー加工により一定の厚さtに成形されている。磁性粉体12aには、たとえば酸化鉄などの適宜の粉体を用いることができる。なかでも、磁性ナノ粒子(MnZnFe)を用いるのがよい。通常の鉄粉に比べて微細であり、吸着力を向上できるからである。 The magnetic layer 12 is made of synthetic resin having flexibility for containing the magnetic powder 12a, it is formed at a constant thickness t 1 by calendering. An appropriate powder such as iron oxide can be used for the magnetic powder 12a. Of these, magnetic nanoparticles (MnZnFe 2 O 4 ) are preferably used. This is because it is finer than normal iron powder and can improve the adsorption power.

磁性粉体12aを含む合成樹脂には、軟質のものを用い、たとえば塩素化ポリエチレン等が好適に用いられる。   As the synthetic resin including the magnetic powder 12a, a soft resin is used, and for example, chlorinated polyethylene is preferably used.

磁性粉体12aとして磁性ナノ粒子(MnZnFe)を用いる方が吸着力を向上できることの事実を示す試験をしたので、次に説明する。
前記磁性層12のみからなるシートが磁石に引き付けられる力を調べるべく、図2(a)に示したような装置21を用いて試験を行った。装置21のうち、22はロードセルで、23はウエイトメータ、24はマグネットシート、25は前記磁性層12のみからなる被吸着シートである。被吸着シート25をマグネットシート24に密着して吸着させ、この状態の被吸着シート25をマグネットシート24から引き離すのに必要な力を計測した。
A test was conducted to show the fact that the use of magnetic nanoparticles (MnZnFe 2 O 4 ) as the magnetic powder 12a can improve the adsorptive power.
In order to examine the force with which the sheet made of only the magnetic layer 12 is attracted to the magnet, a test was performed using an apparatus 21 as shown in FIG. In the apparatus 21, 22 is a load cell, 23 is a weight meter, 24 is a magnet sheet, and 25 is an adsorbed sheet made of only the magnetic layer 12. The attracted sheet 25 was brought into close contact with the magnet sheet 24 and attracted thereto, and the force required to separate the attracted sheet 25 in this state from the magnet sheet 24 was measured.

前記被吸着シート25には、磁性ナノ粒子を含有した試料1と、鉄粉を含有した試料2を用意した。いずれも、厚さは0.4mmである。また組成については、試料1が、磁性ナノ粒子(MnZnFe)を88.90%、塩素化ポリエチレンを8.53%、添加物を2.57%とするものである。一方、試料2は、鉄粉を89%、塩素化ポリエチレンを10%、添加物を1%とするものである。なお、いずれも重量%である。 For the adsorbed sheet 25, a sample 1 containing magnetic nanoparticles and a sample 2 containing iron powder were prepared. In either case, the thickness is 0.4 mm. As for the composition, Sample 1 contains 88.90% magnetic nanoparticles (MnZnFe 2 O 4 ), 8.53% chlorinated polyethylene, and 2.57% additive. On the other hand, Sample 2 contains 89% iron powder, 10% chlorinated polyethylene, and 1% additive. In addition, all are weight%.

また試験では、吸着力の差による違いについても観察すべく、同一組成の厚さの異なる2種類のマグネットシート24を用いた。マグネットシート24の吸着力は厚さが厚いほど高いからである。   In the test, two types of magnet sheets 24 having the same composition and different thicknesses were used in order to observe the difference due to the difference in attraction force. This is because the attracting force of the magnet sheet 24 increases as the thickness increases.

その結果、図2(b)に示したように、吸着力の異なる2種類のマグネットシート24のいずれにおいても、磁性ナノ粒子を含有した試料1のほうが、鉄粉を含有した試料2よりも磁石に引き付けられる力が強かった。また、マグネットシート24の吸着力が高いほど、被吸着シート25が引き付けられる力も強いことが分かる。   As a result, as shown in FIG. 2B, in any of the two types of magnet sheets 24 having different attractive forces, the sample 1 containing magnetic nanoparticles is more magnet than the sample 2 containing iron powder. The power attracted by was strong. Further, it can be seen that the higher the attractive force of the magnet sheet 24, the stronger the attractive force of the attracted sheet 25 is.

前記印刷許容層13は、非水性インクジェットプリンタによる印刷が可能な白色を呈する合成樹脂で成形されている。合成樹脂には、塩化ビニルが用いられる。PET(ポリエチレンテレフタレート)等を用いることもできる。印刷許容層13はカレンダー加工によって一定の厚さtに成形され、その厚さtは、磁性層の厚さtよりも薄い。また、表面は水性インクジェットプリンタで印刷する場合に必要なインク受理層のためのコート層を有しないが、微細な凹凸が形成され、外観上マット調に仕上げられている。 The print-allowable layer 13 is formed of a synthetic resin exhibiting a white color that can be printed by a non-aqueous inkjet printer. Vinyl chloride is used as the synthetic resin. PET (polyethylene terephthalate) or the like can also be used. The print-allowable layer 13 is formed to a constant thickness t 2 by calendering, and the thickness t 2 is thinner than the thickness t 1 of the magnetic layer. Further, the surface does not have a coating layer for an ink receiving layer necessary for printing with a water-based ink jet printer, but fine irregularities are formed and the appearance is matte.

前記磁性層12と印刷許容層13は、ラミネート加工(加熱圧着)により貼り合わせられる。磁性層12は非磁化状態である。   The magnetic layer 12 and the print permitting layer 13 are bonded together by laminating (heat pressing). The magnetic layer 12 is in a non-magnetized state.

なお、大型インクジェットプリンタで印刷をするには、磁性層12と印刷許容層13を合わせて0.5mmとするのが好ましく、具体的には磁性層12の厚さtを0.4mm、印刷許容層の厚さtを0.1mmにするのがよい。 For printing with a large ink jet printer, it is preferable that the magnetic layer 12 and the print permitting layer 13 are combined to 0.5 mm. Specifically, the thickness t 1 of the magnetic layer 12 is 0.4 mm. the permissible layer thickness t 2 it is preferable to 0.1 mm.

このように構成された合成樹脂積層シート11は、図3(a)に示したように印刷許容層13に印刷を行ったり、図3(b)に示したように磁性層12に別体のシート材14を貼ったり、図3(c)に示したように印刷許容層13に別体のシート材14を貼ったりして、あるいは何もせずに適宜裁断して使用される。図3(a)中、15はインクである。   The synthetic resin laminated sheet 11 configured in this way is printed on the print-allowable layer 13 as shown in FIG. 3A, or separated from the magnetic layer 12 as shown in FIG. 3B. The sheet material 14 is affixed, or a separate sheet material 14 is affixed to the print permitting layer 13 as shown in FIG. 3C, or the sheet material 14 is appropriately cut without being used. In FIG. 3A, reference numeral 15 denotes ink.

まず、印刷許容層13に印刷をすることについて説明する(図3(a)参照)。
図4は、溶剤系大型インクジェットプリンタ21(以下、プリンタという)の概略構成を示す。
First, printing on the print-allowable layer 13 will be described (see FIG. 3A).
FIG. 4 shows a schematic configuration of a solvent-based large-sized inkjet printer 21 (hereinafter referred to as a printer).

プリンタ21は、ロール状に巻かれた合成樹脂積層シート11を一対の送りローラ22,23で搬送面24上に送り込み、水平に搬送しながら搬送面24上方に配置されたプリントヘッド25で印刷を行い、印刷をしてから合成樹脂積層シート11を送り出す。入口側に設けられた受け板26の下と、搬送面24の下におけるプリントヘッド25に対応する位置にはヒータ27,28が設けられ、合成樹脂積層シート11を加熱してソルベントインクの定着が良好に行われるように構成される。図中29は、出口側に設けられた受け板である。   The printer 21 feeds the synthetic resin laminated sheet 11 wound in a roll shape onto the conveying surface 24 with a pair of feed rollers 22 and 23, and performs printing with a print head 25 disposed above the conveying surface 24 while being conveyed horizontally. After performing and printing, the synthetic resin laminated sheet 11 is sent out. Heaters 27 and 28 are provided at positions corresponding to the print head 25 below the receiving plate 26 provided on the entrance side and below the conveying surface 24, and the synthetic resin laminated sheet 11 is heated to fix the solvent ink. Configured to perform well. In the figure, reference numeral 29 denotes a receiving plate provided on the outlet side.

図5に示したように、上記搬送面24とプリントヘッド25との間H1は、一般的なプリンタでは、2mm程度に設定されている。このため、上記のような0.5mm厚の合成樹脂積層シート11を搬送すると、プリントヘッド25との間に約1.5mmの隙間H2が残る。   As shown in FIG. 5, the distance H1 between the transport surface 24 and the print head 25 is set to about 2 mm in a general printer. For this reason, when the synthetic resin laminated sheet 11 having a thickness of 0.5 mm as described above is conveyed, a gap H <b> 2 of about 1.5 mm remains between the print head 25.

上記ヒータ27,28による加熱で合成樹脂積層シート11は緩み、浮くような変形をするが、1.5mmも浮き上がることは決してなく、搬送中に合成樹脂積層シート11の引っ掛かりは発生しない。このため、プリントヘッド25の高さを調整する必要はなく、印刷作業は簡単に行える。   Although the synthetic resin laminate sheet 11 is loosened by the heating by the heaters 27 and 28 and is deformed to float, the synthetic resin laminate sheet 11 never lifts by 1.5 mm, and the synthetic resin laminate sheet 11 is not caught during the conveyance. For this reason, it is not necessary to adjust the height of the print head 25, and the printing operation can be easily performed.

合成樹脂積層シート11は搬送されながら、プリントヘッド25から吐出されるインクを受け、印刷表示が形成される。このとき、プリントヘッド25と印刷許容層13との間の距離が離れすぎることはないので、インクの定着性も所望通り良好に行え、鮮明な印刷表示を得ることができる。インクの定着性は、印刷許容層13の表面がマット調であることによっても高められる。   The synthetic resin laminated sheet 11 receives ink ejected from the print head 25 while being conveyed, and a print display is formed. At this time, since the distance between the print head 25 and the print permitting layer 13 is not too far away, the ink can be fixed well as desired, and a clear print display can be obtained. The fixability of the ink can also be improved by the matte surface of the print permitting layer 13.

また、印刷に際してヒータ27,28の温度設定を合成樹脂積層シート11にあわせて変更することも不要である。すなわち、合成樹脂積層シート11が0.8mmや1mmなどというように厚いものではなく、0.5mmであるので、ヒータ27,28からの熱伝導は良好であって、インクの乾燥性や定着性がよいうえに、印刷ムラも発生しないからである。   Further, it is not necessary to change the temperature settings of the heaters 27 and 28 in accordance with the synthetic resin laminated sheet 11 during printing. That is, since the synthetic resin laminated sheet 11 is not as thick as 0.8 mm or 1 mm but 0.5 mm, the heat conduction from the heaters 27 and 28 is good, and the drying property and fixing property of ink. This is because printing unevenness does not occur.

プリントヘッド25の高さ調整やヒータ27,28の温度設定の変更は、つぎに別の種類の印刷シートに対して印刷するときのことを考慮すると、その作業が大変煩雑であるのでしないほうが理想的である。この点、上記合成樹脂積層シート11を用いれば、それらの変更が不要であるため、印刷作業は容易である。合成樹脂積層シート11の厚さが0.5mmを越えると、そのメリットは得られない。   Ideally, the adjustment of the height of the print head 25 and the change of the temperature setting of the heaters 27 and 28 should not be performed because the operation is very complicated in consideration of the next printing on another type of printing sheet. Is. In this regard, if the synthetic resin laminate sheet 11 is used, it is not necessary to change them, so that the printing operation is easy. If the thickness of the synthetic resin laminated sheet 11 exceeds 0.5 mm, the advantage cannot be obtained.

なお、インクにソルベントインクを用いるので、印刷終了後乾燥すると、印刷許容層の収縮が起こるものであるが、0.4mm厚の磁性層12が印刷許容層13をしっかりと強固に支持し、また印刷許容層13も0.1mmであって、インクが印刷許容層13を侵す厚さである10μmに比して充分な厚さを有するので、必要以上の収縮を抑えることができる。このため、収縮による不良品の発生をなくすことができるとともに、所望サイズの印刷表示を得られる。収縮がなく所望サイズの印刷表示が得られるため、分割出力された合成樹脂積層シート11同士をシームして大型の合成樹脂積層シートにしたときに印刷表示にずれが生じるようなことはない。   In addition, since solvent ink is used for the ink, shrinkage of the print-allowable layer occurs when drying after the printing is finished, but the 0.4 mm-thick magnetic layer 12 supports the print-allowable layer 13 firmly and firmly. The print-allowable layer 13 is also 0.1 mm, and has a sufficient thickness as compared with 10 μm, which is the thickness at which the ink penetrates the print-allowable layer 13, so that the shrinkage more than necessary can be suppressed. For this reason, generation | occurrence | production of the inferior goods by shrinkage | contraction can be eliminated and the printed display of desired size can be obtained. Since there is no shrinkage and print display of a desired size is obtained, when the synthetic resin laminated sheets 11 that have been divided and output are seamed together to form a large synthetic resin laminated sheet, there will be no deviation in the printed display.

そして、その磁性層12は0.4mmと、比較的厚く形成されているので、前述のように磁性ナノ粒子を用いたことと相俟って、磁石に吸着される力は強い。しかも、その特異な厚さゆえに、製造に困難性はなく廉価に生産でき、低価格化を図ることができる。低価格化は、印刷許容層13が表面にインク受理層を有しない塩化ビニルからなるものであるためコストを抑えることができることによっても実現できる。   And since the magnetic layer 12 is formed with a relatively large thickness of 0.4 mm, the force attracted to the magnet is strong in combination with the use of the magnetic nanoparticles as described above. In addition, due to the unique thickness, there is no difficulty in manufacturing, and it can be produced at a low price, and the price can be reduced. The price reduction can also be realized by reducing the cost because the printing allowable layer 13 is made of vinyl chloride having no ink receiving layer on the surface.

また、磁性層12を0.4mm厚としたので合成樹脂積層シート11の重さを抑えることができる。この結果、印刷時の搬送に際してプリンタ21の搬送装置に負担をかけず、搬送に際して速度差を生じさせないようにすることができる。このため、印刷初期の印刷表示と印刷終期の印刷表示にずれが生じないようにすることが可能である。印刷表示にずれがないので、分割出力された合成樹脂積層シート11同士をシームする場合でも何ら支障はなく、印刷表示が合った美麗な大型の合成樹脂積層シートを得ることができる。   Moreover, since the magnetic layer 12 is 0.4 mm thick, the weight of the synthetic resin laminated sheet 11 can be suppressed. As a result, it is possible to prevent a load on the transport device of the printer 21 during transport during printing and to prevent a speed difference during transport. For this reason, it is possible to prevent a deviation between the initial print display and the final print display. Since there is no deviation in the printed display, there is no problem even when the synthetic resin laminated sheets 11 that are divided and output are seamed together, and a beautiful large synthetic resin laminated sheet with the printed display can be obtained.

次に、磁性層12に別体のシート材14を貼ることと、印刷許容層13に別体のシート材14を貼ることについて説明する(図3(b)(c)参照)。   Next, sticking a separate sheet material 14 to the magnetic layer 12 and sticking a separate sheet material 14 to the print-allowable layer 13 will be described (see FIGS. 3B and 3C).

別体のシート材14は、磁性層12や印刷許容層13の全面を覆う大きさのものであるも、一部を覆う大きさのものであるも、いずれでも良い。前者の場合には、マーカによる書き消しを可能にするフィルム(ホワイトボード用フィルム)や壁紙などの既存のシートや、好みのメディアに印刷された印刷シートなど、後者の場合には、カット文字やシールなどがある。接着剤による接着やラミネート(加熱圧着)等の適宜手段によって貼り付けることができる。   The separate sheet material 14 may be of a size that covers the entire surface of the magnetic layer 12 or the print-allowable layer 13 or may be a size that covers a part of the magnetic material. In the former case, an existing sheet such as a film (whiteboard film) or wallpaper that can be erased by a marker, or a printed sheet printed on a favorite medium. In the latter case, a cut character or There are seals. It can be attached by an appropriate means such as adhesion with an adhesive or lamination (thermocompression bonding).

最後に、何もせずに適宜裁断して使用することについて説明する。   Finally, it will be described how to cut and use as appropriate without doing anything.

合成樹脂積層シート11は、前述のように可撓性を有し柔軟な合成樹脂製であるので、カッター等で容易に裁断・切断できる。裁断・切断後は、印刷許容層13に印刷や文字や図などの記入をすることが可能である。   Since the synthetic resin laminated sheet 11 is made of flexible and soft synthetic resin as described above, it can be easily cut and cut with a cutter or the like. After cutting / cutting, it is possible to enter prints, characters, drawings, and the like on the print permission layer 13.

以上のような合成樹脂積層シート11の使用方法について次に説明する。
まず、いわゆるバナーやタペストリの形で使用する方法について説明する。このようなものとして使用するには、合成樹脂積層シート11の上下両端部に、合成樹脂積層シート11を張設するための張設用部材を取り付けて張設できるようにする。
Next, the usage method of the above synthetic resin laminated sheets 11 is demonstrated.
First, a method of using it in the form of a so-called banner or tapestry will be described. In order to use as such, a tensioning member for tensioning the synthetic resin laminated sheet 11 is attached to the upper and lower ends of the synthetic resin laminated sheet 11 so that the synthetic resin laminated sheet 11 can be tensioned.

図6は、バナー41としての使用状態を示し、このバナー41は合成樹脂積層シート11とバナー用スタンド32で構成される。合成樹脂積層シート11に対して、まず、それの印刷許容層13に所望の表示内容を印刷してから、前記張設用部材としてのハトメ31を四隅に固定する。   FIG. 6 shows a usage state as the banner 41, and the banner 41 includes the synthetic resin laminated sheet 11 and the banner stand 32. First, a desired display content is printed on the synthetic resin laminated sheet 11 on the print permitting layer 13 thereof, and then the eyelets 31 as the tension members are fixed to the four corners.

このあとは、既存のバナー用スタンド32を用い、スタンド32のフック32aに前記ハトメ31を挿嵌して張って展示すれば、印刷内容を表示し伝達するとともに、磁石やマグネットシート16に吸着されるバナー41となる。   After that, if the existing banner stand 32 is used and the eyelet 31 is inserted and stretched on the hook 32a of the stand 32, the printed content is displayed and transmitted, and is attracted to the magnet or the magnet sheet 16. Banner 41.

図7は、タペストリ42の形での使用状態を示し、このタペストリ42は合成樹脂積層シート11とバー33で構成される。合成樹脂積層シート11に対しては、まず、図6に示したものと同様に、それの印刷許容層13に表示内容を印刷してから、前記張設用部材としての前記バー33を上下両端縁に固定する。バー33には既存のものを適宜使用できる。バー33は、上端面に設けられた挿通孔33aを利用して吊り下げられたりして適宜場所に取り付けられる。挿通孔33aではなく紐による取り付けでもよい。   FIG. 7 shows the state of use in the form of a tapestry 42, which is composed of the synthetic resin laminated sheet 11 and the bar 33. For the synthetic resin laminated sheet 11, first, as shown in FIG. 6, the display content is printed on the print permitting layer 13, and then the bar 33 as the tension member is placed on the upper and lower ends. Secure to the edge. An existing bar 33 can be used as appropriate. The bar 33 is attached to an appropriate place by being suspended using an insertion hole 33a provided on the upper end surface. Attachment with a string may be used instead of the insertion hole 33a.

このようにしてタペストリ42の形で使用する合成樹脂積層シート11は、様々な場面で使用できるが、特に、図8に示したように、展示会や見本市での展示ブース34において使用するとよい。つまり、合成樹脂積層シート11を、展示ブース34のパネル35の表面に、その表面を覆うように取り付けて使用するのである。   Thus, the synthetic resin laminated sheet 11 used in the form of the tapestry 42 can be used in various scenes. In particular, as shown in FIG. 8, the synthetic resin laminated sheet 11 may be used in an exhibition booth 34 at an exhibition or trade show. That is, the synthetic resin laminated sheet 11 is used by being attached to the surface of the panel 35 of the exhibition booth 34 so as to cover the surface.

展示ブース34では、釘打ちなどが禁止されているため、たとえばポスターや発泡ボードを貼る場合には、両面テープが用いられる。しかし、展示が終わって剥がすときに、両面テープによってポスター等が損傷するので、そのポスターを再度使用することはできない。このため、同一内容の展示を行う展示会等が複数の会場で行われる場合でも、必要なポスター等を作り変えなければならない。このほかにも、パネル35を損傷しないよう細心の注意を払う必要もあり、便利さに欠ける難点がこれまでにはあった。   Since nailing and the like are prohibited at the exhibition booth 34, for example, a double-sided tape is used when a poster or a foam board is pasted. However, when the exhibition is finished and peeled off, the poster or the like is damaged by the double-sided tape, and the poster cannot be used again. For this reason, even when an exhibition or the like for exhibiting the same content is held at a plurality of venues, necessary posters or the like must be remade. In addition to this, it is necessary to pay close attention not to damage the panel 35, and there has been a difficulty that is not convenient.

しかし、この発明の合成樹脂積層シート11をタペストリの形で使用すれば、準備に当たっては合成樹脂シート11を吊り下げるなどしてパネル35の表面や会場の壁面等、利用可能な壁面に取り付けるだけでよいので、準備も後片付けも簡易迅速に行える。特に、展示会等が終わった後の搬出には時間厳守が求められるので、大変メリットがある。   However, if the synthetic resin laminate sheet 11 of the present invention is used in the form of a tapestry, the preparation can be made by simply hanging the synthetic resin sheet 11 and attaching it to an available wall surface such as the surface of the panel 35 or the wall surface of the venue. Since it is good, preparation and clean-up can be done easily and quickly. In particular, there is a great merit because it is required to strictly observe the export after the exhibition.

そして、展示内容については、図8に示したように、たとえば「わが社の新製品」、「会社概要」、「実績」などと、予め所定の内容を印刷しておき、展示のたびに更新すべき部分には、マグネットシート16にその内容を印刷して合成樹脂積層シート11に貼り付けられるようにしておけば、一つの合成樹脂積層シート11を継続して使用することができ、無駄がない。また、印刷した部分であっても、その上から別の印刷内容を有するマグネットシート16を取り付ければ、表示内容の変更もでき、この点でも無駄がない。   As shown in FIG. 8, for example, “Present products of our company”, “Company overview”, “Achievements”, etc. are printed in advance and updated at each exhibition. If the contents should be printed on the magnet sheet 16 and pasted on the synthetic resin laminated sheet 11, one synthetic resin laminated sheet 11 can be used continuously and wasteful. Absent. Moreover, even if it is a printed part, if the magnetic sheet 16 which has another printing content from the top is attached, a display content can also be changed and there is no waste also in this point.

また、マグネットシートの表面にチラシやサービス券などのようなシート片を保持できるようなポケットを固定することもできるので、展示の仕方も広がる。   In addition, a pocket that can hold a sheet piece such as a leaflet or a service ticket can be fixed on the surface of the magnetic sheet, so that the way of display can be expanded.

これまで、展示ブース34のパネル35をタペストリで覆って展示をすることは無かった。これは、タペストリやバナーを構成する本体シートが布やターポリン、熱転写シートで構成されており、一度行った印刷表示の表示内容を変更することができないことは勿論のこと、たとえばポケットなどの別部材を取り付けようとする場合には縫い付けや接着をしなければならず、不自由なものであったからであると思われるが、そのような先入観が支配する情況下では、必然的なことでもある。   Until now, the panel 35 of the exhibition booth 34 was not covered with tapestry. This is because the main body sheet constituting the tapestry and banner is composed of cloth, tarpaulin, and thermal transfer sheet, and the display contents of the printed display once performed cannot be changed, for example, another member such as a pocket It seems that this was because it was inconvenient because it had to be sewn or glued when trying to attach it, but it was inevitable in the situation where such preconceptions dominate .

しかし、この点、この発明の合成樹脂積層シート11を用いたタペストリ42や前記バナー41では、前述のように様々な効果が得られ、きわめて便利に使用でき、実用的な価値も高いものとなる。   However, in this respect, the tapestry 42 and the banner 41 using the synthetic resin laminated sheet 11 of the present invention can obtain various effects as described above, can be used very conveniently, and have high practical value. .

特に、磁性層12には鉄粉などの磁性粉体を含有しているので、防炎効果も有する。このため、展示会等で壁面等を覆う場合に、好適に使用できる。   In particular, since the magnetic layer 12 contains magnetic powder such as iron powder, it also has a flameproof effect. For this reason, when covering a wall surface etc. in an exhibition etc., it can be used conveniently.

さらに、前述のようにして合成樹脂積層シート11をタペストリの形で展示を行うと、展示の仕方の幅が広がる上に出っ張りを少なくしてよりコンパクトに展示が行える。このため、限られたスペースを有効に利用してゆとりあるレイアウトが実現でき、効果的な展示も可能である。特に、車椅子使用者や杖使用者が訪れる展示会等では、ゆとりをもってみてもらえるようなスマートな展示が求められており、この点を考慮して来場者に対する行き届いたサービスも可能である。   Furthermore, when the synthetic resin laminated sheet 11 is displayed in the form of a tapestry as described above, the width of the display method can be widened and the protrusion can be reduced to make the display more compact. For this reason, a spacious layout can be realized by effectively using the limited space, and an effective display is possible. In particular, at exhibitions where wheelchair users and cane users visit, smart exhibitions that can be seen with ease are required. Considering this point, it is possible to provide attentive services to visitors.

このような活用の仕方の一例を、図9、図10を用いて説明する。
図9と図10は、飲食店の店頭に展示するタペストリ42の形で使用する合成樹脂積層シート11であって、印刷許容層13には、ランチメニューが印刷されている。
An example of such utilization will be described with reference to FIGS.
FIG. 9 and FIG. 10 show the synthetic resin laminated sheet 11 used in the form of a tapestry 42 displayed at a restaurant front, and the lunch menu is printed on the print-allowable layer 13.

図9の合成樹脂積層シート11は、「本日のサービス定食」の部分を毎日適宜設定できるようにしたものである。つまり、合成樹脂積層シート11には、「本日のサービス定食」の部分を空欄にしておき、他の部分にはその他の定食メニューを、その名称と写真と金額入りで印刷表示している。そして、「本日のサービス定食」の部分に貼り付ける必要内容を印刷したマグネットシート16を、複数枚付属している。マグネットシート16に対する印刷は簡単に行えるので、その日の食材に応じて容易に対応できる。   The synthetic resin laminate sheet 11 of FIG. 9 is configured such that the “today's service set meal” portion can be appropriately set every day. That is, on the synthetic resin laminated sheet 11, the “Today's service set meal” portion is left blank, and other set meal menus are printed and displayed on the other portions with their names, photos, and amounts. A plurality of magnet sheets 16 on which necessary contents to be pasted on the “Today's service set meal” portion are printed are attached. Since printing on the magnet sheet 16 can be easily performed, it can be easily handled according to the food of the day.

図10の合成樹脂積層シート11は、予め用意されている定食から、「本日のおすすめ」を適宜設定できるようにしたものである。つまり、合成樹脂積層シート11には、すべての定食メニューを、その名称と写真と金額入りで印刷表示している。そして、「本日のおすすめ」と表示した枠状のマグネットシート16aと、金額を表示した複数枚のマグネットシート16bを付属している。その日ごとに適宜の定食メニューを囲むように枠状のマグネットシート16aを貼り付けるとともに、印刷表示されている金額の上に、正しい金額のマグネットシート16bを貼り付けて使用する。   The synthetic resin laminate sheet 11 of FIG. 10 is configured such that “today's recommendation” can be appropriately set from a set meal prepared in advance. That is, on the synthetic resin laminated sheet 11, all set meal menus are printed and displayed with their names, photos, and amounts. A frame-shaped magnet sheet 16a displaying "Recommend of the day" and a plurality of magnet sheets 16b displaying the amount of money are attached. For each day, a frame-shaped magnet sheet 16a is pasted so as to surround an appropriate set menu, and a correct amount of magnet sheet 16b is pasted on the printed amount.

これらのほか、印刷許容層に様々なデザインの印刷をして、店や商店街等の装飾や模様替えなどに用いることができる。近年の印刷はとても美麗に行えるので、装飾に有効である。そのうえ、そのための作業も容易である。   In addition to these, it is possible to print various designs on the print-allowable layer and use them for decorations and redesigns of shops and shopping streets. Printing in recent years can be done very beautifully and is effective for decoration. In addition, the work for that is also easy.

なお、図6〜図10に示した例では、合成樹脂積層シート11の磁性層12が磁化されていないものを例に示したが、図11に示したように、合成樹脂積層シート11には、磁性層12を磁化したものを使用することもできる。この場合、吸着させる被吸着シート17には、磁性層12が磁化されていない、前述の合成樹脂積層シート11と同一構成の合成樹脂積層シート11を使用できる。   In the example shown in FIGS. 6 to 10, the synthetic resin laminated sheet 11 is shown as an example in which the magnetic layer 12 is not magnetized. However, as shown in FIG. In addition, a magnetized magnetic layer 12 can be used. In this case, the synthetic resin laminate sheet 11 having the same configuration as the above-described synthetic resin laminate sheet 11 in which the magnetic layer 12 is not magnetized can be used as the attracted sheet 17 to be adsorbed.

図11において仮想線で描いた矢印は、磁化状態のものに向けている。また、前記合成樹脂積層シート11と同一構成の合成樹脂積層シート11を被吸着シートとして用いるほか、金属粉を塗布した被吸着シートや金属箔を貼り付けたその他の被吸着シートを使用してもよい。以下に示す例においても同様である。   In FIG. 11, the arrows drawn with phantom lines are directed to the magnetized state. In addition to using the synthetic resin laminated sheet 11 having the same configuration as the synthetic resin laminated sheet 11 as an adsorbed sheet, an adsorbed sheet coated with metal powder or other adsorbed sheet attached with metal foil may be used. Good. The same applies to the examples shown below.

つぎに、前述のような張設用部材を使用しないで使用する方法について説明する。   Next, a method of using the tension member as described above without using it will be described.

図12は、合成樹脂積層シート11の印刷許容層13に、たとえば適宜の文字や図柄等を印刷して、壁面や床面、天井面等の被貼り付け面36に貼り付ける使用方法を示している。すなわち、印刷許容層13に印刷を施した後、所望する被貼り付け面36に適した接着剤18を磁性層12に塗布して壁面等の被貼り付け面36に貼り付ける。図12中、15はインクである。   FIG. 12 shows a usage method in which, for example, an appropriate character or design is printed on the print-allowable layer 13 of the synthetic resin laminated sheet 11 and is pasted on a surface to be attached 36 such as a wall surface, a floor surface, or a ceiling surface. Yes. That is, after printing on the print permitting layer 13, the adhesive 18 suitable for the desired surface to be attached 36 is applied to the magnetic layer 12 and attached to the surface to be attached 36 such as a wall surface. In FIG. 12, 15 is ink.

前述のように近年の印刷はとても美麗に行えるので、見栄えのする表示が行える上に、壁紙や天井に適した模様を印刷したり、たとえば誘導用の表示をしたりと、自由に使用できる。しかも、マグネットシート16を貼り付けられるので、多彩な表示や表示内容の変更も可能であり、さらに紙片等をピンで固定することも可能である。   As described above, recent printing can be performed very beautifully, so that it can be displayed freely, and can be freely used for printing a pattern suitable for wallpaper or ceiling, for example, for guidance display. In addition, since the magnet sheet 16 can be attached, various displays and display contents can be changed, and a piece of paper or the like can be fixed with a pin.

また、壁面や床面等の被貼り付け面36の性質に合わせて接着剤18を選べるので、良好な固定状態が得られる。接着剤18には、再粘着性を有するものを使用することもでき、この場合には、剥がすことが必要な場合の使用に便利である。   Moreover, since the adhesive 18 can be selected according to the property of the to-be-attached surface 36, such as a wall surface and a floor surface, a favorable fixed state is obtained. The adhesive 18 may be one having re-tackiness, and in this case, it is convenient for use when it is necessary to remove it.

図13は、合成樹脂積層シート11の磁性層12に、壁紙や、ホワイトボード用フィルム、コルクシート、化粧フィルム等のシート材14を貼り付けて、壁面等の被貼り付け面36に貼り付ける使用方法を示している。すなわち、磁性層12に所望するシート材14を貼り付けた後、所望する被貼り付け面36に適した接着剤18を印刷許容層13に塗布し、壁面等の被貼り付け面36に貼り付ける。接着剤18は被貼り付け面36に塗布して貼り付けを行うもよい。   FIG. 13 illustrates a use in which a sheet material 14 such as wallpaper, a whiteboard film, a cork sheet, or a decorative film is pasted on the magnetic layer 12 of the synthetic resin laminated sheet 11 and is pasted on a surface to be pasted 36 such as a wall surface. Shows how. That is, after the desired sheet material 14 is attached to the magnetic layer 12, the adhesive 18 suitable for the desired attachment surface 36 is applied to the print permission layer 13 and attached to the attachment surface 36 such as a wall surface. . The adhesive 18 may be applied to the surface to be attached 36 for pasting.

前述したような印刷による方法では感触が良くないと思う場合や、ホワイトボードのように使用したいと思う場合、印刷許容層13に対する印刷では所望する色目が出ない場合などに好適である。   This method is suitable when the printing method as described above does not feel good, when the user wants to use the printer like a whiteboard, or when the desired color is not obtained by printing on the print permitting layer 13.

この場合もマグネットシート16を貼り付けることが可能であるが、シート材14側から貼り付けるので、印刷許容層13側からマグネットシート16を貼り付ける場合に比して、磁性層12までの距離を短くすることができ、強力な吸着が可能である。   In this case as well, the magnet sheet 16 can be pasted, but since the sheet is pasted from the sheet material 14 side, the distance to the magnetic layer 12 is larger than when the magnet sheet 16 is pasted from the print permitting layer 13 side. It can be shortened and strong adsorption is possible.

また、この場合も壁面等の性質に合わせて接着剤18を選べるので、良好な固定状態が得られる。接着剤18には、再粘着性を有するものを使用することもできる。   Also in this case, since the adhesive 18 can be selected according to the properties of the wall surface or the like, a good fixed state can be obtained. As the adhesive 18, an adhesive having re-tackiness can be used.

図14は、合成樹脂シート11の印刷許容層13に、広告などのために文字や模様を印刷したり、カット文字を貼り付けたりして、建物や自動車などのガラス面36aに貼り付ける使用方法を示している。すなわち、図14(a)に示したように、印刷許容層13に所望する印刷表示をした後、ガラス面36aに対する固定に適した透明の接着剤18を印刷許容層13に塗布して、ガラス面36aに貼り付ける。   FIG. 14 shows a usage method in which characters or patterns are printed for advertisements or pasted on the print-allowable layer 13 of the synthetic resin sheet 11 and pasted on a glass surface 36a of a building or a car. Is shown. That is, as shown in FIG. 14 (a), after a desired print indication is made on the print-allowable layer 13, a transparent adhesive 18 suitable for fixing to the glass surface 36a is applied to the print-allowable layer 13, and the glass Affixed to the surface 36a.

このような使用方法によれば、窓等のガラスを利用して外部への広告が容易にできる上に、目隠し等の機能も持たせることができる。接着剤18に再粘着性を有するものを使用すれば、一時的な使用が可能である。   According to such a method of use, advertisements to the outside can be easily performed using glass such as windows, and functions such as blindfolding can be provided. If the adhesive 18 has re-tackiness, it can be used temporarily.

図14(b)に示したように、磁性層12に壁紙や、書き消し可能にするフィルム等のシート材14を貼り付けたり、適宜の模様等を印刷したりして表層部19を形成すると、室内においては装飾や掲示、マグネットシート16の貼り付けなどの、実用的な利用も可能である。   As shown in FIG. 14B, when the surface layer portion 19 is formed by pasting a sheet material 14 such as wallpaper or erasable film on the magnetic layer 12 or printing an appropriate pattern or the like. In the room, practical use such as decoration, posting, and sticking of the magnet sheet 16 is also possible.

つづいて、日用品や学習教材等の資材として使用する方法について説明する。   Next, a method for using as a material for daily necessities and learning materials will be described.

図15(a)は、磁石やマグネットシート16のほか、押しピン51も使用できるコルクボード調の掲示板45の斜視図であり、図15(b)は、その一部断面図である。   FIG. 15A is a perspective view of a cork board-like bulletin board 45 that can use a push pin 51 in addition to a magnet and a magnet sheet 16, and FIG. 15B is a partial cross-sectional view thereof.

掲示板45は、枠材45aと、この内側に収められ層状をなす前記合成樹脂積層シート11および支持板45bを有する。枠材45aも支持板45bも適宜の材料で構成される。合成樹脂積層シート11は、印刷許容層13にコルクの模様が非水性インクで印刷されている。   The bulletin board 45 includes the frame material 45a, and the synthetic resin laminated sheet 11 and the support plate 45b which are housed inside and form a layer shape. Both the frame member 45a and the support plate 45b are made of appropriate materials. In the synthetic resin laminated sheet 11, a cork pattern is printed on the print-allowable layer 13 with non-aqueous ink.

このような掲示板45では、印刷許容層13への印刷により、外観上はコルクのように見える上に、実際にコルクボードのように押しピン51を用いることができる。しかも、磁石やマグネットシート16を貼り付けることができる。このため、コルクボードよりも幅広い使い方ができる。しかも、印刷許容層13は合成樹脂製であるので、コルクのように割れたりすることはなく、美麗な状態のまま使い続けることができる。   In such a bulletin board 45, by printing on the print permitting layer 13, the appearance looks like a cork, and the push pin 51 can actually be used like a cork board. Moreover, a magnet or magnet sheet 16 can be attached. For this reason, it can be used in a wider range than the cork board. Moreover, since the print permitting layer 13 is made of a synthetic resin, it is not broken like a cork and can be used in a beautiful state.

図16は、ホワイトボードのように使用できる掲示板45の斜視図であり、一部を拡大した断面図に示すように、掲示板45は合成樹脂積層シート11と、この合成樹脂積層シート11の柔らかさを補って適宜の強度を持たせる支持板45bを重合して構成される。支持板45bは適宜の合成樹脂板等で構成すればよい。また、合成樹脂積層シート11の印刷許容層13には、ホワイトボード用フィルム14aがラミネートされている。   FIG. 16 is a perspective view of a bulletin board 45 that can be used like a white board. As shown in a partially enlarged sectional view, the bulletin board 45 is composed of the synthetic resin laminated sheet 11 and the softness of the synthetic resin laminated sheet 11. The support plate 45b is made up of a suitable strength by compensating for the above. The support plate 45b may be composed of an appropriate synthetic resin plate or the like. Further, a whiteboard film 14 a is laminated on the print permitting layer 13 of the synthetic resin laminated sheet 11.

この掲示板45は、たとえば仮想線で示したように紐45cにより適宜の場所に吊り下げて使用できるほか、前記支持板45bの硬さが丸めることを許容するものである場合には、丸めてコンパクトに持ち運びでき、筆談等に便利である。また、支持板45の硬さをたとえば合板のように硬くした場合には、画板のような使用も可能となる。   The bulletin board 45 can be used by being hung at an appropriate place by a string 45c as shown by an imaginary line, for example. If the hardness of the support plate 45b is allowed to be rounded, the bulletin board 45 is rounded and compact. It is convenient for writing conversations. Further, when the support plate 45 is hardened, for example, like a plywood, it can be used like a drawing board.

マーカによる書き消しができる上に磁石やマグネットシート16が使えるので、自由に様々な利用ができる掲示板となる。   In addition to being erasable with a marker, the magnet and the magnet sheet 16 can be used, so that the bulletin board can be freely used in various ways.

また、図17に示したように、前記合成樹脂積層シート11の磁性層12に、水を含むと壁面等に吸着するスポンジ状の機能性シート材46aを積層すれば、お風呂でも遊べる遊戯具や学習用具として使えるマルチボード46となる。つまり、貼り付けるマグネットシート16として、図示例のような様々な形状のマグネットシート16を付属すれば、積み木遊び等として、また、図示はしないが文字や数字のマグネットシートを付属すれば学習用具として使用できる。   In addition, as shown in FIG. 17, if a magnetic layer 12 of the synthetic resin laminate sheet 11 is laminated with a sponge-like functional sheet material 46 a that adsorbs to a wall surface or the like when it contains water, it can be played in a bath. Or a multi-board 46 that can be used as a learning tool. In other words, if a magnet sheet 16 having various shapes as shown in the figure is attached as the magnet sheet 16 to be attached, it will be used as a play for building, etc. Can be used.

図18(a)は、カッターマット47の斜視図である。このカッターマット47は、前記合成樹脂積層シート11の印刷許容層13に、カッターマットとして必要な線の印刷をした後、合成樹脂積層シート11に剛性を付与するための支持板47aを磁性層12に重合する。この後、適宜裁断し、所定大のカッターマット47にする。   FIG. 18A is a perspective view of the cutter mat 47. The cutter mat 47 is formed by printing a line necessary for the cutter mat on the print-allowable layer 13 of the synthetic resin laminate sheet 11 and then providing a support plate 47a for giving rigidity to the synthetic resin laminate sheet 11 as the magnetic layer 12. To polymerize. Thereafter, it is appropriately cut to obtain a cutter mat 47 having a predetermined size.

このようなカッターマット47では、図18に示したように下面に磁石板48aを備えた定規48を用いて、カッターによる切断を行う。定規48はカッターマット47に対して位置や向きにかかわらず良好に吸着するので、使用しやすい。   In such a cutter mat 47, as shown in FIG. 18, a ruler 48 having a magnet plate 48a on the lower surface is used to perform cutting with a cutter. The ruler 48 is easy to use because it adheres well to the cutter mat 47 regardless of its position and orientation.

なお、図18(b)の断面図に示したように、カッターマット47は、合成樹脂積層シート11の両面に別部材を重合して構成することもできる。すなわち、前記支持板47aを印刷許容層13側の面に重合することに加えて、磁性層12側の面には、カッターの刃が刺さっても傷を目立たなくする柔軟なカバーシート14bを重合する。前述の必要な線は、このカバーシート14bに印刷しておく。   As shown in the cross-sectional view of FIG. 18B, the cutter mat 47 can be configured by superposing different members on both surfaces of the synthetic resin laminated sheet 11. That is, in addition to polymerizing the support plate 47a on the surface of the print-allowable layer 13, the surface of the magnetic layer 12 is polymerized with a flexible cover sheet 14b that makes the scratches inconspicuous even if the cutter blade is stabbed. To do. The necessary lines are printed on the cover sheet 14b.

このように構成すると、カッターによる傷を積極的に目立たなくすることができる。   If comprised in this way, the damage | wound by a cutter can be made inconspicuous actively.

なお、図18(b)に示した断面構造のカッターマットにおいて、たとえば印刷許容層13に適宜の印刷表示をしておき、支持板47aに透明の板材を使用すると、裏返したときに印刷表示が見える状態で使用できる粘土板などとしても使用可能なマットとなる。   Note that, in the cutter mat having the cross-sectional structure shown in FIG. 18B, for example, if an appropriate print display is provided on the print permitting layer 13 and a transparent plate material is used for the support plate 47a, the print display is displayed when turned over. The mat can be used as a clay plate that can be used in a visible state.

図19は、新規な作品展示用マット49の斜視図である。この作品展示用マット49は、前記合成樹脂積層シート11の印刷許容層13に、ホワイトボード用フィルム14aがラミネートされ、適宜大に形成されている。形状は、図示例においては長方形であるものを示したが、たとえば木の形など、適宜の形状であるもよい。また、必要に応じて好みの形状に切断するものであるもよい。   FIG. 19 is a perspective view of a new work display mat 49. The work display mat 49 is appropriately formed large by laminating a whiteboard film 14 a on the print permitting layer 13 of the synthetic resin laminate sheet 11. In the illustrated example, the shape is rectangular, but the shape may be an appropriate shape such as a tree. Moreover, you may cut | disconnect to a favorite shape as needed.

このような作品展示用マット48は、図19(a)に示したように、粘土細工等の作品52を乗せるとともに、所望する絵53をマーカによって描く。絵53のほかに、必要に応じて作者を特定する個人名等の必要事項を記載する。また、底面にマグネットシート54aを有する装飾部材54を取り付けて、作品52を飾りつける。なお、予め必要な文字や模様、線などを印刷許容層13に印刷しておくもよい。   As shown in FIG. 19A, such a work display mat 48 carries a work 52 such as clay work and draws a desired picture 53 with a marker. In addition to the picture 53, necessary items such as an individual name for identifying the author are described as necessary. Further, a decoration member 54 having a magnet sheet 54a is attached to the bottom surface to decorate the work 52. Note that necessary characters, patterns, lines, and the like may be printed on the print permission layer 13 in advance.

このようにして作品52を単独で展示するのではなく、絵53や装飾部材54によって引き立てることができる。換言すれば、絵53や装飾部材54等をあわせて一つの作品とすることができる。   In this way, the work 52 is not displayed alone but can be enhanced by the picture 53 or the decorative member 54. In other words, the picture 53 and the decoration member 54 can be combined into one piece.

この作品展示用マット48は、図19(b)に示したように丸めることができるので、展示会等への移動にも便利である。   Since the work display mat 48 can be rolled as shown in FIG. 19B, it is convenient to move to an exhibition or the like.

これらのほか、たとえば支持板に剛性の有るものを使用して粘土板を得るなど、様々な教材や遊戯板などに利用できる。   In addition to these, for example, a clay plate can be obtained by using a rigid support plate, which can be used for various educational materials and play boards.

以上説明したように、この発明の合成樹脂積層シート11は、特異な磁性層12と、これの片面にのみラミネートされた印刷許容層13のみからなるので、マグネットシートの相手方として、あるいはマグネットシートとして、磁力による強い吸着力や被吸着力を得ることができるとともに、必要に応じて非水性大型インクジェットプリンタによる印刷が可能である。その上、二層のみからなるので、必要に応じて広告等の表示などに利用できるほか、日用品や学習教材等の物品の資材としても利用でき、高い自由度で様々に使用できるこれまでにない利汎用性ある合成樹脂積層シート11である。   As described above, the synthetic resin laminated sheet 11 of the present invention comprises only the unique magnetic layer 12 and the print permitting layer 13 laminated only on one side thereof, so that it can be used as a counterpart to the magnet sheet or as a magnet sheet. In addition to obtaining a strong attracting force and attracting force due to magnetic force, printing with a non-aqueous large-scale ink jet printer is possible as required. In addition, since it consists of only two layers, it can be used for displaying advertisements, etc. as necessary, and can also be used as materials for articles such as daily necessities and learning materials, and it can be used in various ways with a high degree of freedom. This is a versatile synthetic resin laminated sheet 11.

特に、タペストリ42の形で使用して展示会等の展示ブース34を飾れば、パネル35を傷つけるようなこともなく、スマートな展示を実現できる。しかも、簡易迅速に設営や撤去が可能であって、至便である。   In particular, if the display booth 34 such as an exhibition is used in the form of a tapestry 42, a smart display can be realized without damaging the panel 35. Moreover, it can be easily and quickly installed and removed, which is convenient.

また、磁性層12が鉄粉などの磁性粉体12aを含有するので、防炎効果が得られる。このため、特に展示会などのように多くの人が集まる場所で壁面等を覆うようにして使用をする場合に好適である。   Moreover, since the magnetic layer 12 contains magnetic powder 12a such as iron powder, a flameproof effect is obtained. For this reason, it is particularly suitable for use in a place where many people gather, such as an exhibition, so as to cover the wall surface.

この発明の構成と、前述の一形態の構成との対応において、
この発明の張設用部材は、前述のハトメ31、バー33に対応するも、
この発明は、前述の構成のみに限定されるものではなく、その他の形態を採用することができる。
In the correspondence between the configuration of the present invention and the configuration of the above-described embodiment,
The tension member of the present invention corresponds to the eyelet 31 and the bar 33 described above,
The present invention is not limited to the above-described configuration, and other forms can be adopted.

11…合成樹脂積層シート
12…磁性層
12a…磁性粉体
13…印刷許容層
31…ハトメ
33…バー
34…展示ブース
41…バナー
42…タペストリ
DESCRIPTION OF SYMBOLS 11 ... Synthetic resin laminated sheet 12 ... Magnetic layer 12a ... Magnetic powder 13 ... Printing permission layer 31 ... Eyelet 33 ... Bar 34 ... Exhibition booth 41 ... Banner 42 ... Tapestry

Claims (6)

磁性粉体を含有し可撓性を有する合成樹脂製で一定の厚さを有する磁性層と、
該磁性層の片面のみにラミネートされて、非水性インクジェットプリンタによる印刷が可能な白色を呈する合成樹脂製で前記磁性層よりも薄く可撓性を有する印刷許容層のみからなる
合成樹脂積層シート。
A magnetic layer containing a magnetic powder and made of flexible synthetic resin and having a certain thickness;
A synthetic resin laminate sheet comprising only a printable layer made of a synthetic resin which is laminated on only one side of the magnetic layer and exhibits a white color that can be printed by a non-aqueous inkjet printer and is thinner than the magnetic layer.
前記磁性粉体が、磁性ナノ粒子である
請求項1に記載の合成樹脂積層シート。
The synthetic resin laminated sheet according to claim 1, wherein the magnetic powder is magnetic nanoparticles.
前記磁性層が、非磁化状態である
請求項1または請求項2に記載の合成樹脂積層シート。
The synthetic resin laminate sheet according to claim 1, wherein the magnetic layer is in a non-magnetized state.
非磁化状態の前記合成樹脂積層シート又は磁化状態の前記合成樹脂積層シートに、磁化状態の前記合成樹脂積層シート又は非磁化状態の前記合成樹脂積層シートが付属された
請求項1から請求項3のうちのいずれか一項に記載の合成樹脂積層シート。
The synthetic resin laminate sheet in a magnetized state or the synthetic resin laminate sheet in a non-magnetized state is attached to the synthetic resin laminate sheet in a non-magnetized state or the synthetic resin laminate sheet in a magnetized state. The synthetic resin lamination sheet as described in any one of them.
前記請求項1から請求項4のうちのいずれか一項に記載の合成樹脂積層シートの前記印刷許容層に印刷をしたのち、
合成樹脂積層シートの上下両端部に、合成樹脂積層シートを張設するための張設用部材を取り付けて張設して使用する
合成樹脂積層シートの使用方法。
After printing on the print-allowable layer of the synthetic resin laminate sheet according to any one of claims 1 to 4,
A method of using a synthetic resin laminate sheet, wherein a tension member for stretching the synthetic resin laminate sheet is attached to and stretched at both upper and lower ends of the synthetic resin laminate sheet.
展示ブースの壁面に取り付ける
請求項5に記載の合成樹脂積層シートの使用方法。
The method for using a synthetic resin laminate sheet according to claim 5, which is attached to a wall of an exhibition booth.
JP2009099628A 2009-04-16 2009-04-16 Synthetic resin laminated sheet and usage of the same Pending JP2010247436A (en)