Prior art keywords
waterproof sheet
ridge
sheet
roof
building
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2008270757A
Other languages
Japanese (ja)
Other versions
JP2010037930A (en
JP4925222B2 (en
Filing date
Publication date
Application filed filed Critical
Priority to JP2008270757A priority Critical patent/JP4925222B2/en
Priority claimed from JP2008270757A external-priority patent/JP4925222B2/en
Publication of JP2010037930A publication Critical patent/JP2010037930A/en
Publication of JP2010037930A5 publication Critical patent/JP2010037930A5/ja
Application granted granted Critical
Publication of JP4925222B2 publication Critical patent/JP4925222B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Description

棟用防水シート、棟用防水シートの設置方法、棟用防水シートを用いた棟施工ユニットBuilding waterproof sheet, installation method of building waterproof sheet, building construction unit using building waterproof sheet

本発明は、建造物の屋根のうち棟部の被覆に用いられる棟用防水シートに関し、特に複雑な形状の被覆領域に対しても非常に長期間に渡って保形性と防水性を維持できる棟用防水シートに関する。また、本発明は、建造物の屋根のうち棟部に棟用防水シートを用いて施工する棟用防水シートの設置方法に関する。さらに、本発明は、建造物の屋根のうち棟部に棟用防水シートを用いた棟施工ユニットに関する。 The present invention relates to a waterproof sheet for a building used for covering a building part of a roof of a building, and can maintain shape retention and waterproofing for a very long time even for a covering region having a complicated shape. It is related with the waterproof sheet for buildings. Moreover, this invention relates to the installation method of the waterproof sheet for ridges constructed using the waterproof sheet for ridges in a ridge part among the roofs of a building. Furthermore, this invention relates to the building construction unit which used the building waterproof sheet for the building part among the roofs of a building.

従来の日本における木造一戸建て住宅や土蔵等の木造建築物においては、瓦屋根の棟部や壁まわりに使用する面戸材として、石灰と砂と粘土等を混練した、屋根土が一般的に用いられている(特許文献1参照)。このように屋根土が用いられているのは、日本においては良質の粘土が容易に得られていた為であり、このような事情は地域的・文化的事情が共通している韓国や中国においても同様であると考えられている。   In traditional wooden single-family houses and wooden structures in Japan, roof soil, which is a mixture of lime, sand, clay, etc., is commonly used as a face door material used around tiled ridges and walls. (See Patent Document 1). The reason why roof soil is used in this way is because high-quality clay was easily obtained in Japan, and this situation is common in Korea and China where regional and cultural circumstances are common. Is also considered to be the same.

他方、ヨーロッパにおいては事情が異なり、特にドイツのように日本と比較して寒冷な地域では、暖房のための暖炉の煙突が屋根から突出した形態となるため、瓦屋根と煙突との接合部に、ポリイソブチレン樹脂とアルミの金属網を積層した壁際用の防水シートを使用することが提案されている(特許文献3)。また、棟用の屋根用防水シートとして、PET(Polyethylene terephthalate・ポリエチレンテレフタラート)樹脂とアルミ箔を貼り合わせた通気性を有する棟用の防水シートを使用することが提案されている(特許文献4)。また日本においても、屋根に換気用開口部を設ける類型の住宅が提案されており、このような換気用開口部の防水シール材として、スポンジを用いた面戸材(特許文献2)が提案されている。このようなスポンジには、例えばEPDM(Ethylene Propylene Methylene Linkage・エチレンプロピレンゴム)やブチルゴムなどの合成ゴムを材料とするスポンジが用いられる(特許文献5[0021]参照)。   On the other hand, in Europe, the situation is different, especially in areas that are colder than Japan, such as Germany, because the chimney of the fireplace for heating protrudes from the roof, so at the junction between the tile roof and the chimney It has been proposed to use a waterproof sheet for a wall in which a polyisobutylene resin and an aluminum metal net are laminated (Patent Document 3). In addition, as a roof waterproof sheet for a building, it has been proposed to use a waterproof sheet for a building having air permeability in which a PET (Polyethylene terephthalate) resin and an aluminum foil are bonded together (Patent Document 4). ). Also in Japan, a type of house in which a ventilation opening is provided on the roof has been proposed, and a face door material using a sponge (Patent Document 2) has been proposed as a waterproof sealant for such a ventilation opening. ing. As such a sponge, for example, a sponge made of synthetic rubber such as EPDM (Ethylene Propylene Methylene Linkage / ethylene propylene rubber) or butyl rubber is used (see Patent Document 5 [0021]).

さらに、屋根に天窓を設ける類型のプレハブ住宅が提案されており、このような天窓用には屋根土と比較して軽量である防水シートが提案されている(特許文献5)。この天窓用防水シートは、架橋ゴム又は樹脂製シートに対して、変形可能で自己保形性を備えた金属シートを積層固定した屋根用防水シートにおいて、幅方向から直交する方向に亙って折り返し重合部を形成したものである。   Furthermore, a type of prefabricated house in which a skylight is provided on the roof has been proposed, and a waterproof sheet that is lighter than roof soil has been proposed for such a skylight (Patent Document 5). This skylight waterproof sheet is a roof waterproof sheet in which a deformable and self-holding metal sheet is laminated and fixed to a crosslinked rubber or resin sheet, and then folded back in the direction perpendicular to the width direction. A polymerization part is formed.

特許第3196058号Japanese Patent No. 3196058 特開2005−325592JP 2005-325592 A DE 3642063A1DE 3642063A1 WO 2004/022878 A1WO 2004/022878 A1 特許第3702277号Japanese Patent No. 3702277

現在、屋根の棟部や壁際の防水施工には、大きく分けて二種類の材料と工法が存在しており、その夫々で課題が存在している。第一類型は、湿式施工である(特許文献1)。しかし、湿式施工における内在的制約として、使用されている屋根土は、施工に作業者の技能と施工時間を要すると共に、重量物であるため、木造建築物の耐震性を弱める原因となっていた。また、良質の粘土が長年の採掘によって掘り尽くされてきており、原材料の手配が困難になりつつある。   Currently, there are roughly two types of materials and construction methods for waterproofing construction on roof ridges and walls, each of which has a problem. The first type is wet construction (Patent Document 1). However, as an inherent restriction in wet construction, the roof soil used requires the operator's skill and construction time for construction, and because it is heavy, it has been a cause of weakening the earthquake resistance of wooden buildings . In addition, high-quality clay has been mined by years of mining, making it difficult to arrange raw materials.

第二類型は、乾式施工であり、上記の特許文献2〜5で、各々の提案がされているが、各乾式施工は完璧なものではなく、其々固有の課題を有している。まず、特許文献2で開示されているスポンジを用いた面戸材に関しては、スポンジ部分が鳥によって突かれるという鳥害があることに加え、屋根材の凹凸に隙間なく施工することが困難という課題もあった。   The second type is dry construction, and each proposal is made in Patent Documents 2 to 5, but each dry construction is not perfect and has its own problems. First, regarding the face door material using the sponge disclosed in Patent Document 2, in addition to the bird damage that the sponge part is struck by birds, it is difficult to construct the roofing material without any gaps There was also.

次に、特許文献4で開示されている防水シートでは、長手方向へのプリーツ加工による延伸と、切込みを入れたことで横手方向への延伸を可能にした防水シートは、様々な棟の高さの差異に対応できるように横手(幅)方向に広いシートとなっている。そこで、欧州のキリスト教文化圏のように住宅の屋根形状や色彩が地域の建築規制によって統一されている場合や、日本のプレハブ住宅のように画一化された量産型住宅には適している。しかし、日本の在来型建築物は注文主の個性が出現しやすい類型であり、また地域の特性に応じた建築物類型が存在すると共に、建築物においては敷地形状と建築基準法や都市計画法による建築規制があり、現実に建築される木造建築物は多様な個性を有しているのが実情である。そこで、屋根形状も区々となり、設置時に作業者が現場の棟包の内側に納まるよう、防水シートの折り曲げ作業が必要であった。また、強風を伴う雨が切込みによる開口部を介して、直接繊維部分に当たる可能性があるため、切込み部から建築物の屋根の内側に浸水の蓋然性が存在していた。   Next, in the waterproof sheet disclosed in Patent Document 4, the waterproof sheet that can be stretched in the lateral direction by stretching by pleating in the longitudinal direction and by making a cut, has various ridge heights. The sheet is wide in the lateral (width) direction so that it can cope with the difference. Therefore, it is suitable for cases where the roof shape and color of houses are standardized by local building regulations, such as European Christian cultural areas, and for mass-produced houses, such as prefabricated houses in Japan. . However, conventional buildings in Japan are the types in which the individuality of the orderer is likely to appear, and there are building types according to the characteristics of the region. The actual situation is that wooden buildings that are actually built have various individualities due to legal restrictions on construction. Therefore, the roof shape also varies, and it is necessary to bend the waterproof sheet so that the worker can fit inside the building parcel at the time of installation. Moreover, since rain accompanied by strong winds may directly hit the fiber portion through the opening formed by the cut, there is a possibility of flooding from the cut to the inside of the roof of the building.

続いて、特許文献5で開示されている防水シートでは、耐水性を備えた可撓性シートを長手方向に対し、直角方向に屈折積層し、壁と瓦との防水材に使用するものである。しかし、屋根の棟や壁際への防水シートの設置を検討する場合、上述したように、様々な意匠の屋根材や屋根勾配があるため、高さの調整ができることが望ましい。また、屋根の棟や壁際は一般的に作業者が手で屋根材の凹凸に沿わせて施工するが、木槌などで軽く叩いて防水シートを整形することが好ましい場合もあるところ、防水シートの材質が厚く硬いと、折り返し重合部の間隔も大きくせざるを得ず、作業者が隙間無く防水シートを延伸する作業は容易ではない。   Subsequently, in the waterproof sheet disclosed in Patent Document 5, a flexible sheet having water resistance is refracted and laminated in a direction perpendicular to the longitudinal direction and used as a waterproof material for walls and roof tiles. . However, when considering the installation of the waterproof sheet on the roof ridge or near the wall, it is desirable that the height can be adjusted because there are roof materials and roof gradients of various designs as described above. In addition, the roof ridge and walls are generally constructed by the operator along the unevenness of the roof material by hand, but sometimes it is preferable to shape the waterproof sheet by tapping with a wooden mallet, etc. If the material is thick and hard, the space between the folded overlap portions must be increased, and it is not easy for the operator to stretch the waterproof sheet without any gaps.

さらに、防水シートのアルミ箔は、屋根のように直射日光が照射される過酷な環境のもとで、数十年にわたりその防水性能を維持することが望ましいが、数十年というスパンではアルミ箔は湿気等に対して腐食してしまい、再度の施工に耐えることが出来ないという課題がある。従来の日本においては、住宅の量的充足が叫ばれ、その寿命に関しては木造住宅の固定資産税の評価上の耐用年数である23年程度確保されれば足りるとする見解もあったが、近年の資源価格の高騰などから百年住宅の必要性も認識されつつあり、防水シートにおいても寿命が長いほうが良いことは言うまでもない。   Furthermore, it is desirable to maintain the waterproof performance of aluminum sheets for waterproof sheets for decades in a harsh environment that is exposed to direct sunlight like a roof. Has a problem that it cannot corrode against moisture and cannot withstand re-installation. In conventional Japan, there has been an advocacy for the quantitative fulfillment of houses, and there was a view that it would be sufficient if the life span was about 23 years, which is the useful life in the evaluation of the property tax of wooden houses. Needs for a 100-year house are also being recognized due to soaring resource prices, and it goes without saying that the waterproof sheet should have a longer lifetime.

さらに、乾式施工に共通する課題として、次の課題があった。
(1)いずれもブチルテープやアクリルテープなどの粘着剤を瓦等の屋根材に接着させる工法を採用するのが一般的であるため、経年後の屋根材からの剥離が生じる。
(2)金属性の棟木支持材を使用しているため、積雪時や強風時には、棟木支持材に負荷が掛かって曲がり、棟包と乾式材料が負荷の掛かった方向に倒れてしまうことがある。
Furthermore, there were the following issues as common issues in dry construction.
(1) Since it is common to employ a construction method in which an adhesive such as butyl tape or acrylic tape is adhered to a roof material such as a tile, peeling from the roof material after aging occurs.
(2) Since a metal purlin support material is used, the load on the purlin support material may bend and bend during snow and strong winds, and the wrapping and dry material may fall in the direction of the load. .

本発明は上述した課題を解決するもので、第の発明は、屋根用防水シートを用いて、屋根の棟部への防水シートの設置が現場設置形状に適合するように、容易に施工できる棟用防水シートを提供することを目的とする。第の発明は、建造物の棟部に棟用防水シートを用いて施工する場合に用いて好適な、棟用防水シートの設置方法を提供することを目的とする。第の発明は、建造物の棟部に用いて好適な、棟用防水シートを用いた棟施工ユニットを提供することを目的とする。 The present invention solves the above-mentioned problems, and the first invention can be easily constructed by using a waterproof sheet for a roof so that the installation of the waterproof sheet on the roof ridge conforms to the on-site installation shape. The purpose is to provide a waterproof sheet for buildings. The second aspect of the invention is to provide a method for installing a waterproof sheet for a building that is suitable for use in a case where construction is performed on a ridge portion of a building using the waterproof sheet for a building. The third invention aims to provide a building construction unit using a building waterproof sheet, which is suitable for use in a building ridge.

上記課題を解決する第一の発明の棟用防水シートは、例えば図5に示すように、棟用防水シート20の長手方向の両裾部を、棟木31に対して屋根材35に下ろした場所が、棟包36の両裾を垂直に下ろした線又はその内側に納まるように、構成されたことを特徴とする。このように構成された棟用防水シート20によれば、一般的に、棟包36の横手寸法は180〜240mmであるが、本発明の棟用防水シート20は、例えば図5(b)に示すように、棟木31に対し、両裾部を下方へ押し下げることで、裾部が同棟包16の内側の墨打ち位置に相当する線か、その線の内側に納まる。 The ridge waterproof sheet of the first invention that solves the above problem is a place where both hems in the longitudinal direction of the ridge waterproof sheet 20 are lowered to the roof material 35 with respect to the purlin 31 as shown in FIG. However, it is characterized in that it is configured so that both hems of the ridge wrap 36 are accommodated in a vertically lowered line or inside thereof. According to the ridge waterproof sheet 20 configured as described above, the transverse dimension of the ridge wrap 36 is generally 180 to 240 mm, but the ridge waterproof sheet 20 of the present invention is shown in FIG. As shown in the figure, by pushing down both skirts downward with respect to the purlin 31, the skirts fit within the line corresponding to the inking position inside the wing 16 or inside the line.

好ましくは、前記棟用防水シートは、耐引き裂き性と熱収縮性を有するエラストマーシートを、粘着剤を用いてアルミ箔の表面側に貼り合わせ、該アルミ箔の裏面側に、樹脂系塗料をコーティングした多層防水シートであって、当該多層防水シートの長手方向の途中に該長手方向と直交する横手方向にわたって横手方向折返し重合せ部を形成し、該長手方向にわたって長手方向折返し重合せ部を形成した屋根用防水シートを用いることを特徴とするとよい。ここで、当該多層防水シートは、例えば図1に示すように、耐引き裂き性と熱収縮性を有するエラストマーシート1を、粘着剤2を用いてアルミ箔3の表面側に貼り合わせ、該アルミ箔3の裏面側に、樹脂系塗料4をコーティングしたことを特徴とするものである。 Preferably, the waterproof sheet for ridges is formed by bonding an elastomer sheet having tear resistance and heat shrinkability to the front side of the aluminum foil using an adhesive, and coating the resin-based paint on the back side of the aluminum foil. In the multilayer waterproof sheet, a transverse folded portion was formed over the transverse direction perpendicular to the longitudinal direction in the middle of the longitudinal direction of the multilayer waterproof sheet, and a longitudinal folded portion was formed over the longitudinal direction. It is good to use the waterproof sheet for roofs. Here , for example, as shown in FIG. 1, the multilayer waterproof sheet is formed by bonding an elastomer sheet 1 having tear resistance and heat shrinkability to the surface side of the aluminum foil 3 using an adhesive 2. 3 is coated with a resin-based paint 4 on the back side.

当該多層防水シートによれば、エラストマーシート1が可塑性を有すると共に耐久性を有しているので、屋根用の防水シートとしての用途に適する。アルミ箔3は、エラストマーシート1を貼り合せて積層させることで、保形性・断熱性・防火性を多層防水シートに付与すると共に、エラストマーシート1が熱収縮性である場合の、熱収縮防止ができる。粘着剤2は、エラストマーシート1とアルミ箔3との二層間の接着をするもので、併せて折り曲げ加工の際に生じる当該二層間に起こる応力を緩和して、折り曲げ加工を容易にする。樹脂系塗料4をコーティングしているので、耐久性や耐食性を向上させるという通常の目的を達成すると共に、仮に多層防水シート5の被覆対象となる屋根形状や壁際形状が突端のような曲率の大きな形状であるため、多層防水シート5を極端に変形させて被覆する必要がある場合でも、アルミ箔3が破れてしまうことを防止でき、防水性が高まる。According to the multilayer waterproof sheet, since the elastomer sheet 1 has plasticity and durability, it is suitable for use as a waterproof sheet for roofs. The aluminum foil 3 is formed by laminating and laminating the elastomer sheet 1, thereby imparting shape retention, heat insulation, and fire resistance to the multilayer waterproof sheet, and preventing thermal shrinkage when the elastomer sheet 1 is heat shrinkable. Can do. The pressure-sensitive adhesive 2 adheres between the two layers of the elastomer sheet 1 and the aluminum foil 3, and relaxes the stress generated between the two layers generated during the bending process, thereby facilitating the bending process. Since the resin-based paint 4 is coated, the usual purpose of improving durability and corrosion resistance is achieved, and the roof shape and the wall-side shape to be covered with the multilayer waterproof sheet 5 have a large curvature like a tip. Since it is a shape, even when the multilayer waterproof sheet 5 needs to be extremely deformed and covered, the aluminum foil 3 can be prevented from being torn and the waterproof property is improved.

また、当該屋根用防水シートは、例えば図2(b)に示すように、多層防水シート5の長手方向の途中に該長手方向と直交する横手方向にわたって横手方向折返し重合せ部Tを形成し、該長手方向にわたって長手方向折返し重合せ部Lを形成した二方向折り重ね状態とする。そして、例えば当該二方向折り重ね状態の屋根用防水シート10を、例えば図3に示すように構成することで、長手方向に加えて横手方向にも延伸性を有する棟用防水シート20を形成するための部材として利用できる。 In addition, the roof waterproof sheet, for example, as shown in FIG. 2 (b), in the middle of the multilayer waterproof sheet 5, in the middle of the longitudinal direction, a transverse direction folded overlap portion T is formed over the transverse direction perpendicular to the longitudinal direction, It is set as the two-way folding state which formed the longitudinal direction folding superposition part L over this longitudinal direction. For example, the roof waterproof sheet 10 in the two-way folded state is configured as shown in FIG. 3, for example, thereby forming the ridge waterproof sheet 20 having extensibility in the lateral direction in addition to the longitudinal direction. It can be used as a member for

当該屋根用防水シートによれば、当該二方向折り重ね状態の屋根用防水シート10としているので、横手方向折返し重合せ部Tを延伸することで、屋根材の凹凸に対応し、長手方向折返し重合せ部Lを延伸することで、棟木の高さの差異への対応だけでなく、水返しの役目も果たす。また、作業者にとっても、横手方向への薄手のエラストマーシート1の弾性とアルミ箔3の保形性を有するシートのため、手に馴染みやすいため、施工不良が起き難く、施工時間の短縮につながる。 According to the waterproof sheet for the roof, since with the two-way folding roof tarpaulin 10 states, by stretching the transverse folding the superimposed portions T, corresponding to the unevenness of the roofing material, longitudinally folded Weight By extending the mating portion L, it not only handles the difference in the height of the purlin but also serves as a water return. Moreover, since it is a sheet having the elasticity of the thin elastomer sheet 1 in the transverse direction and the shape retaining property of the aluminum foil 3 for the operator, it is easy to be familiar with the hand, so that it is difficult for construction failure to occur and the construction time is reduced .

好ましくは、第一の発明の棟用防水シートにおいて、当該棟用防水シートは、例えば図3に示すように、長手方向の延伸性が125%〜175%であり、横手方向の延伸長さが40mm〜200mmであることを特徴とする。 Preferably, in the ridge waterproof sheet of the first invention, the ridge waterproof sheet has a longitudinal stretchability of 125% to 175% , for example, as shown in FIG. It is 40 mm to 200 mm.

このように構成された棟用防水シート20によれば、例えば図3・図5に示すように、長手方向への延伸について、屋根の棟木31の長さを100%とすると、瓦などの代表的な屋根材35の凹凸を考慮した表面長さは145%であるため、これ以上の延伸率を確保すれば施工できるのだが、凹凸の少ない屋根材35は、125%でもよい。これにより、無駄な材料コストを抑えることができる。また、横方向への延伸について、一般的な施工では、棟木31の高さが屋根の棟頂から、20mm〜80mmの間であり、これを大幅に上回る延伸は必要がないため、無駄な材料コストを抑えることができる。   According to the waterproof sheet 20 for a ridge thus configured, for example, as shown in FIGS. 3 and 5, when the length of the roof purlin 31 is 100%, the roof tile 31 is representative of tiles and the like. Since the surface length in consideration of the unevenness of the typical roofing material 35 is 145%, the roofing material 35 with less unevenness may be 125%, although it can be constructed if a higher stretch ratio is secured. Thereby, useless material cost can be suppressed. In addition, with respect to stretching in the lateral direction, in general construction, the height of the purlin 31 is between 20 mm and 80 mm from the top of the roof, and it is not necessary to stretch much above this, so wasted material Cost can be reduced.

好ましくは、第一の発明の棟用防水シートにおいて、当該棟用防水シートは、例えば図3に示すように、横手方向に延伸する前の横手方向の長さが、130mm〜260mmであることを特徴とする。このように構成された棟用防水シート20によれば、一般的に、棟包36の横手寸法は180〜240mmであるが、本発明の棟用防水シート20は、例えば図5(b)に示すように、棟木31に対し、両裾部を下方へ押し下げることで、裾部が同棟包16の内側の墨打ち位置か、その位置の内側に納まる。 Preferably, in the ridge waterproof sheet of the first invention, the ridge waterproof sheet has a length in the lateral direction before extending in the lateral direction , for example, as shown in FIG. Features. According to the ridge waterproof sheet 20 configured as described above, the transverse dimension of the ridge wrap 36 is generally 180 to 240 mm, but the ridge waterproof sheet 20 of the present invention is shown in FIG. As shown in the figure, by pushing down both skirts downward with respect to the purlin 31, the skirts fit in the ink marking position inside the ward 16 or inside the position.

好ましくは、第一の発明の棟用防水シートにおいて、当該棟用防水シートは、例えば図3に示すように、エラストマーシートの表面の少なくとも一部に、長手方向にわたって釘穴シール性を有するシートを装着したことを特徴とする。このように構成された棟用防水シート20によれば、棟木31の上側面に対応する屋根用防水シートのエラストマーシート1の表面に、釘穴シール性を有するシート27を装着することで、屋根用防水シート20を棟木31の上にステープル、釘、ビスなどで仮止めした穴からの漏水の問題を解決することができる。 Preferably, in the ridge waterproof sheet according to the first invention, the ridge waterproof sheet includes a sheet having a nail hole sealing property in the longitudinal direction on at least a part of the surface of the elastomer sheet , for example, as shown in FIG. It is characterized by wearing. According to the ridge waterproof sheet 20 configured as described above, by attaching the sheet 27 having the nail hole sealing property to the surface of the elastomer sheet 1 of the roof waterproof sheet corresponding to the upper side surface of the purlin 31, the roof It is possible to solve the problem of water leakage from a hole in which the waterproof sheet 20 is temporarily fixed on the purlin 31 with staples, nails, screws or the like.

好ましくは、第一の発明の棟用防水シートにおいて、当該棟用防水シートは、例えば図5(a)、(b)に示すように、長手方向折返し重合せ部Lは、各建築物によって相違する棟木31の高さに対して、長手方向折返し重合せ部Lの展開状態を調整することで対処できるように構成されるとよい。 Preferably, in the building waterproof sheet according to the first invention, the waterproof sheet for the building is different in each longitudinally folded portion L as shown in FIGS. 5A and 5B, for example. It is good to be comprised so that it can cope with the height of the purlin 31 to adjust by adjusting the expansion | deployment state of the longitudinal direction folding overlap part L. FIG.

好ましくは、第一の発明の棟用防水シートにおいて、当該棟用防水シートは、例えば図5(c)に示すように、長手方向折返し重合せ部Lは、水返しとして機能するように、長手方向折返し重合せ部Lの展開状態を調整できるように構成されるとよい。 Preferably, in the ridge waterproof sheet according to the first aspect of the present invention, the ridge waterproof sheet has a longitudinal direction so that the folded portion L in the longitudinal direction functions as a water return , for example, as shown in FIG. It is good to be comprised so that the expansion | deployment state of the direction folding overlapping part L can be adjusted.

好ましくは、第一の発明の棟用防水シートにおいて、当該棟用防水シートは、例えば図4に示すように、屋根用防水シート10に通気性手段28,29を備えたことを特徴とする。このように構成された棟用防水シート20によれば、通気性手段を設けることで、通気性を備え、風を伴う雨であっても、雨水が撥ね返される。さらに好ましくは、通気性手段に撥水作用を附帯させると、通気性手段に水分が付着しても、通気性手段から内側への雨水侵入を防止できる。 Preferably, in the ridge waterproof sheet according to the first aspect of the invention, the ridge waterproof sheet is provided with breathable means 28 and 29 in the roof waterproof sheet 10 as shown in FIG. 4, for example . According to the building waterproof sheet 20 configured as described above, by providing the air permeability means, the air waterproofness is provided, and rainwater is repelled even in rain with wind. More preferably, when a water repellent effect is attached to the air permeable means, rainwater can be prevented from entering from the air permeable means to the inside even if moisture adheres to the air permeable means.

好ましくは、当該棟用防水シートにおいて、通気性手段は通気孔29を長手方向に向けて複数設け、通気孔29を覆う通気撥水繊維28をエラストマーシート1の表面に装着してなるように構成するとよい。このように構成された棟用防水シート20によれば、エラストマーシート1の表面に通気撥水繊維28と通気孔29を設けることで、通気性を備え、風を伴う雨であっても、雨水が撥ね返され、さらに通気撥水繊維28に水分が付着しても、撥水作用により、通気孔29から内側への雨水の侵入を防止できる。さらに好ましくは、水返し機能を営む長手方向折返し重合せ部Lの棟設置方向の上側に位置する部位に、通気撥水繊維28と通気孔29を設けると、水返し機能により雨水が撥ね返されると共に、水返し機能の上部の通気撥水繊維28に水分が付着しても、撥水作用により、通気孔29から内側への雨水の侵入を防止できる。 Preferably, the waterproof sheet for the building, the ventilation means is provided more toward the vent hole 29 in the longitudinal direction, configured so as to ventilation repellent fibers 28 for covering the vent hole 29 is attached to the surface of the elastomeric sheet 1 Good. According to the waterproof sheet 20 for a ridge configured as described above, the ventilation sheet 29 is provided with the ventilation water-repellent fibers 28 and the ventilation holes 29 on the surface of the elastomer sheet 1. Even if water is repelled and moisture adheres to the ventilated water-repellent fibers 28, rainwater can be prevented from entering into the inside through the vent holes 29 due to the water-repellent action. More preferably, when the ventilated water repellent fiber 28 and the vent hole 29 are provided in a portion located on the upper side in the building installation direction of the longitudinal folding portion L that performs the water return function, rainwater is repelled by the water return function. At the same time, even if moisture adheres to the air repellent fiber 28 at the upper part of the water return function, rainwater can be prevented from entering from the air vent 29 to the inside due to the water repellent action.

さらに、好ましくは、第一の発明の棟用防水シートにおいて、当該棟用防水シートは、例えば図5に示すように、棟用防水シート20の長手方向の中央部が棟木31の上側面に長手方向に固定され、棟用防水シート20の長手方向の両裾部が棟包36の両裾を垂直に下ろした線の内側に納まるように、棟際1段目の屋根材35に粘着テープ25で接着され、棟包36が屋根用防水シートを覆う状態で施工されるように構成されるとよい。 Further, preferably, in the ridge waterproof sheet of the first invention, the ridge waterproof sheet has a longitudinal center portion of the ridge waterproof sheet 20 extending longitudinally on the upper surface of the purse 31 as shown in FIG. The adhesive tape 25 is attached to the roof material 35 at the first stage of the building so that the two hems in the longitudinal direction of the waterproof sheet 20 for the ridge are placed inside the line where the two hems of the wing 36 are vertically lowered. It is good to comprise so that it may be constructed | assembled in the state which adhere | attaches, and the ridge wrapper 36 covers the waterproof sheet for roofs .

好ましくは、第一の発明の多層防水シートにおいて、更に、エラストマーシートは、クロロスルフォン化ポリエチレンまたはEPDMであることを特徴とする。このように構成された多層防水シートによれば、クロロスルフォン化ポリエチレンまたはEPDMは、耐久性を有しているので、エラストマーシートの耐久性を高め、屋根用の防水シートとしての用途に適する。特に、クロロスルフォン化ポリエチレンは、優れた着色性を有するため、屋根材の色に自在に対応ができる。さらに、クロロスルフォン化ポリエチレンは、耐熱性、耐焔性、耐寒性、耐屈曲性、耐塩性等々に優れているため、寒冷地や熱帯地、防火地域、強風地、塩害地でも地域を問わず使用が可能で、屋根用の防水シートとしての用途に適する。Preferably, in the multilayer waterproof sheet of the first invention, the elastomer sheet is further characterized by being chlorosulfonated polyethylene or EPDM. According to the multilayer waterproof sheet configured as described above, since chlorosulfonated polyethylene or EPDM has durability, the durability of the elastomer sheet is enhanced and it is suitable for use as a waterproof sheet for roofs. In particular, since chlorosulfonated polyethylene has excellent colorability, it can freely correspond to the color of the roofing material. In addition, chlorosulfonated polyethylene is excellent in heat resistance, weather resistance, cold resistance, bending resistance, salt resistance, etc., so it can be used in cold, tropical, fireproof, strong wind and salt damage areas. It can be used and is suitable for use as a waterproof sheet for roofs.

上記課題を解決する第二の発明である棟用防水シートの設置方法は、例えば図5〜図7に示すように、請求項乃至請求項の何れか1項に記載の棟用防水シート20の長手方向の中央部を、棟木31の上側面に屋根の棟方向と並行に設置する工程と(ステップ100)、棟用防水シート20を棟木31にステープル等で仮止めする工程と(ステップ102)、棟用防水シート20の長手方向の裾部を棟木31に対して押し下げる工程と(ステップ104)、棟用防水シート20の裾部24が屋根材35に届かない場合に、長手方向折返し重合せ部Lを横手方向に延伸させて、裾部24が屋根材35に届く状態にする工程と(ステップ106)、屋根材35の山部352に対しては、棟用防水シート20の裾部24を長手方向に接着する工程と(ステップ108)、屋根材35の谷部354に対しては、当該谷部形状に沿うように、棟用防水シート20を長手方向に延伸させて接着する工程と(ステップ110)、とを有することを特徴とする。 Installation of the second ridge waterproof sheet is an invention for solving the above problems, for example, as shown in FIGS. 5 to 7, the waterproof sheet building according to any one of claims 1 to 3 A step of installing a central portion in the longitudinal direction of the ridge 20 on the upper side of the purlin 31 in parallel with the ridge direction of the roof (step 100), a step of temporarily fixing the ridge waterproof sheet 20 to the purlin 31 with staples, etc. 102) the step of pushing down the longitudinal skirt of the ridge waterproof sheet 20 against the purlin 31 (step 104), and the fold 24 when the skirt 24 of the ridge waterproof sheet 20 does not reach the roof material 35. The step of extending the overlapping portion L in the transverse direction so that the skirt portion 24 reaches the roof material 35 (step 106), and the skirt portion 352 of the roof material 35, the skirt of the waterproof sheet for buildings 20 Step of bonding the portion 24 in the longitudinal direction (Step 108), for the valley 354 of the roofing material 35, a step of extending the ridge waterproof sheet 20 in the longitudinal direction and adhering the ridge waterproof sheet 20 along the shape of the valley (Step 110). It is characterized by that.

ここで、棟用防水シート20として請求項10に記載の接着テープ25を用いている場合に、棟用防水シート20を屋根材35の山部352や谷部354と接着するために、粘着テープ25に設けられた剥離紙26を剥がすタイミングは、ステップ102とステップ104との間、ステップ104と同時、ステップ104とステップ106との間、ステップ106とステップ108との間、ステップ108とステップ1010との間、の何れでもよい。 Here, in the case where the adhesive tape 25 according to claim 10 is used as the ridge waterproof sheet 20, the adhesive tape is used to bond the ridge waterproof sheet 20 to the mountain portion 352 and the valley portion 354 of the roof material 35. The timing at which the release paper 26 provided on 25 is peeled off is between step 102 and step 104, at the same time as step 104, between step 104 and step 106, between step 106 and step 108, and between step 108 and step 1010. Or between the two.

上記課題を解決する第三の発明である棟用防水シートを用いた棟施工ユニットは、例えば図5に示すように、請求項乃至請求項の何れか1項に記載の棟用防水シート20を用いると共に、棟用防水シート20で被覆される棟木31の支持に樹脂製棟支持材32を用いたことを特徴とする。このように構成された棟用防水シートを用いた棟施工ユニットによれば、棟木31の支持に樹脂製棟支持材32を用いているので、堅牢性を確保して、長期間使用しても倒れることが防止できる。そこで、従来のように防錆加工された金属製の棟支持材について生じていた課題、即ち、剛性に乏しく、風や積雪などで揺れたり曲がってしまう課題が解決される。 The building construction unit using a waterproof sheet for building a third invention for solving the above problems, for example, as shown in FIG. 5, a waterproof sheet for building according to any one of claims 1 to 3 20 and a resin ridge support material 32 is used to support the purlin 31 covered with the ridge waterproof sheet 20. According to the building construction unit using the building waterproof sheet configured as described above, since the resin building support material 32 is used to support the purlin 31, even if it is used for a long period of time by securing robustness. It can be prevented from falling. Therefore, the problem that has arisen with respect to the conventional metal building support material that has been rust-proofed, that is, the problem that the rigidity is poor and the object is swayed or bent due to wind, snow or the like is solved.

第一の発明の棟用防水シートによれば、以下の効果がある。
(a) 棟用防水シートは、軽量であり作業者の熟練度や技術に依らずに使用できる。
(b) 棟用防水シートに用いられる屋根用防水シートに、クロロスルフォン化ポリエチレンシートを用いると、棟用防水シートの表面が耐摩耗性や耐引き裂き性に優れるクロロスルフォン化ポリエチレンシートで覆われているため、屋根用防水シートや棟用防水シートに対する鳥害の恐れがない。
According to the ridge waterproof sheet of the first invention , the following effects are obtained.
(A) The waterproof sheet for buildings is lightweight and can be used regardless of the skill level and skill of the operator.
(B) When a chlorosulfonated polyethylene sheet is used for a roof waterproof sheet used for a building waterproof sheet, the surface of the building waterproof sheet is covered with a chlorosulfonated polyethylene sheet having excellent wear resistance and tear resistance. Therefore, there is no fear of bird damage to the waterproof sheet for roofs or the waterproof sheet for buildings.

(c) 棟用防水シートには、請求項記載の長手方向折返し重合せ部Lを設けてあるため、棟用防水シートを棟等の屋根に設置する場合にも、幅手方向又は高さ方向にも延伸ができる。また、長手方向折返し重合せ部Lによって棟用防水シートが予め折り畳まれているため、棟包内に納めるための折り畳み作業が不要になると共に、長手方向折返し重合せ部Lは水返し効果を有すため、請求項記載のように通気部を設けている類型の棟用防水シートであっても漏水問題が生じない。 (C) Since the building waterproof sheet is provided with the folded portion L in the longitudinal direction according to claim 3 , the width direction or height of the building waterproof sheet is also provided when the building waterproof sheet is installed on the roof of the building. It can also be stretched in the direction. In addition, since the ridge waterproof sheet is pre-folded by the longitudinal folding overlap portion L, the folding work for storing in the ridge wrap becomes unnecessary, and the longitudinal folding overlap portion L has a water return effect. Therefore, even if it is a type of building waterproof sheet provided with a ventilation portion as described in claim 9, a water leakage problem does not occur.

(d) 棟用防水シートに、クロロスルフォン化ポリエチレンシート1を使用すると、従来の粘着テープの接着力とアルミ箔の保形性との協働関係に起因する、経年変化による屋根材からの剥離を抑えることができる。(D) When the chlorosulfonated polyethylene sheet 1 is used for the waterproof sheet for the building, peeling from the roofing material due to aging due to the cooperative relationship between the adhesive strength of the conventional adhesive tape and the shape retention of the aluminum foil Can be suppressed.

棟用防水シートに多層防水シートを用いると、耐引き裂き性と熱収縮性を有するエラストマーシートを、粘着剤を用いてアルミ箔の表面側に貼り合わせ、該アルミ箔の裏面側に、樹脂系塗料をコーティングので、エラストマーシート・アルミ箔・粘着剤・樹脂系塗料の四層構造により、折り曲げ加工性と耐久性も併せ持つ。従って、本発明の多層防水シートを屋根用防水シートとして使用する場合の効果として、様々な意匠の屋根材や屋根勾配が類型的に存在する建築物において、屋根の棟や壁際への防水シートの設置が現場設置形状に適合するように、容易に施工できる屋根用防水シートに用いて好適である。  When a multilayer waterproof sheet is used as the waterproof sheet for a building, an elastomer sheet having tear resistance and heat shrinkability is bonded to the front side of the aluminum foil using an adhesive, and a resin-based paint is applied to the back side of the aluminum foil. Because of the coating, the four-layer structure of elastomer sheet, aluminum foil, pressure-sensitive adhesive, and resin-based paint has both folding workability and durability. Therefore, as an effect when using the multilayer waterproof sheet of the present invention as a roof waterproof sheet, in a building where roof materials and roof gradients of various designs exist in a typical manner, It is suitable for use as a waterproof sheet for roofs that can be easily constructed so that the installation conforms to the on-site installation shape.

以下、図面によって本発明の実施の形態について説明する。まず、多層防水シートを説明する。 Hereinafter, embodiments of the present invention will be described with reference to the drawings. First, a multilayer waterproof sheet will be described.

図1は、本発明の棟用防水シートに用いられる多層防水シートを説明する構成図である。図において、多層防水シート5は、エラストマーシート1、粘着剤2、アルミ箔3、樹脂系塗料4の四層構造になっている。ここで、エラストマーシート1に用いられるエラストマーには、熱可塑性エラストマー、架橋ゴム、未架橋ゴムが含まれる。エラストマーは、JISK6418に用語の定義があり、弾性ポリマー(Elastic Polymer)の一種である。分子間を共有結合で結合し、三次元網目構造(Network Structure)を形成する高分子は、ガラス転移温度T以上ではゴム弾性という性質を示す。ゴムの弾性は、本来規則構造を持たない分子の配列が、外部からの力により規則性になり、これが元の不規則な配列に戻ろうとするときの力によるもので、熱力学的には応力によるエントロピーの低下(ギブス自由エネルギーの増加)が元に戻ろうとする力による弾性であるから、エントロピー弾性とも呼ばれる。 FIG. 1 is a configuration diagram illustrating a multilayer waterproof sheet used for a ridge waterproof sheet according to the present invention . In the figure, the multilayer waterproof sheet 5 has a four-layer structure of an elastomer sheet 1, an adhesive 2, an aluminum foil 3, and a resin-based paint 4. Here, the elastomer used for the elastomer sheet 1 includes a thermoplastic elastomer, a crosslinked rubber, and an uncrosslinked rubber. The term “elastomer” has a definition in JISK6418 and is a kind of elastic polymer. Covalently coupling between molecules, the polymer capable of forming a three-dimensional network (Network Structure) shows the property of rubber elasticity at the glass transition temperature T g or more. The elasticity of rubber is due to the force that occurs when an array of molecules that do not originally have a regular structure becomes regularity due to external forces, and this tries to return to the original irregular arrangement. This is also called entropy elasticity because the decrease in entropy due to (increase in Gibbs free energy) is the elasticity due to the force to return.

そして、多層防水シート5におけるエラストマーシート1には、自然架橋のクロロスルフォン化ポリエチレンを用いることが好ましい。特に、自然架橋タイプを用いることで、架橋工程を省くことができ、成形後、常温状態で形状を記憶するシートとなる。クロロスルフォン化ポリエチレンシート1は、0.15mm〜0.45mm、特に好ましくは、0.3mm、という薄手の状態であることが好ましい。ここで、クロロスルフォン化ポリエチレンとは、クロロスルホン化ポリエチレンを主成分とする配合物で、クロロスルホン化ポリエチレン以外に、タルク、炭カル、シリカ、カーボンなどの無機物、芳香族プロセスオイル、塩素化パラフィンなどの可塑剤、ポリエチレンワックスなどの加工助剤を必要に応じて添加することができる。   The elastomer sheet 1 in the multilayer waterproof sheet 5 is preferably made of naturally crosslinked chlorosulfonated polyethylene. In particular, by using a natural cross-linking type, the cross-linking step can be omitted, and the sheet can be memorized in a normal temperature state after molding. The chlorosulfonated polyethylene sheet 1 is preferably in a thin state of 0.15 mm to 0.45 mm, particularly preferably 0.3 mm. Here, chlorosulfonated polyethylene is a compound mainly composed of chlorosulfonated polyethylene. In addition to chlorosulfonated polyethylene, inorganic substances such as talc, charcoal cal, silica, carbon, aromatic process oil, chlorinated paraffin A processing aid such as a plasticizer and polyethylene wax can be added as necessary.

また、自然環境下での架橋状態を調整するために、酸化マグネシウム、リサージ、硫黄、エポキシなど、クロロスルホン化ポリエチレンの架橋に使用される一般的な架橋剤、もしくは架橋助剤を必要に応じて添加することもできる。さらに、ゴム成分として、主成分のクロロスルホン化ポリエチレン以外のゴム成分として、天然ゴム、スチレン・ブタジエンゴム、ブタジエンゴム、エチレン・プロピレン・ジエンゴム、クロロプレンゴム、ブチルゴム、二トリルゴム、ウレタンゴムなどを必要に応じて添加することができる。また、ゴム成分以外にも、ポリエチレン、ポリプロピレン、ポリエステル樹脂、ポリカーボネート、アクリロ二トリルスチレンブタジエン共重合体、アクリル、エチレン酢酸ビニル(EVA)などの樹脂成分、さらには、ナイロン、ポリエステルなどを主成分とする繊維を必要に応じて添加することもできる。   In addition, in order to adjust the crosslinking state in the natural environment, a general crosslinking agent or crosslinking aid used for crosslinking chlorosulfonated polyethylene, such as magnesium oxide, risurge, sulfur, epoxy, etc. It can also be added. Furthermore, as rubber components other than the main component chlorosulfonated polyethylene, natural rubber, styrene / butadiene rubber, butadiene rubber, ethylene / propylene / diene rubber, chloroprene rubber, butyl rubber, nitrile rubber, urethane rubber, etc. are required. Can be added accordingly. Besides rubber components, polyethylene, polypropylene, polyester resin, polycarbonate, acrylonitrile styrene butadiene copolymer, resin components such as acrylic, ethylene vinyl acetate (EVA), and nylon, polyester, etc. The fibers to be added can be added as necessary.

粘着剤2は、エラストマーシート1とアルミ箔3の二層間の接着に用いられる。粘着剤2により、二層間に起こる折り返した部位の応力を緩和でき、より折り曲げ加工性に富むシートが得られる。粘着剤2には、特にアクリル系粘着剤2が好ましい。これに対して、ブチルゴムやポリイソブチレンなどでは、加熱時に軟化してしまうため、エラストマーシート1が熱収縮した場合に、アルミ箔上3に固着しておくことができなくなるという不都合を生じる。   The pressure-sensitive adhesive 2 is used for adhesion between two layers of the elastomer sheet 1 and the aluminum foil 3. The pressure-sensitive adhesive 2 can relieve the stress at the folded portion that occurs between the two layers, and a sheet having a higher bending workability can be obtained. The adhesive 2 is particularly preferably an acrylic adhesive 2. On the other hand, butyl rubber, polyisobutylene, and the like are softened during heating, and therefore, when the elastomer sheet 1 is thermally contracted, there is a disadvantage that it cannot be fixed to the aluminum foil 3.

また、エラストマーシート1とアルミ箔3を積層させる工程についても、アクリル粘着剤2は、ブチルゴムやポリイソブチレンなどのゴム系粘着剤と比較すると、粘性が低いためラミネート加工装置が使用でき、加工速度も10[km/h]以上で貼り合わせ加工ができ、加工コストを低減できる。   Also, in the process of laminating the elastomer sheet 1 and the aluminum foil 3, the acrylic pressure-sensitive adhesive 2 has a lower viscosity than a rubber-based pressure-sensitive adhesive such as butyl rubber or polyisobutylene, so that a laminating apparatus can be used and the processing speed is also high. Bonding can be performed at 10 [km / h] or more, and processing costs can be reduced.

アルミ箔3は、作業者が手加工により成形するため、軟質アルミニウムであり、厚みが30μm〜90μm(好ましくは40μm)程度が好ましい。アルミ箔3の厚みは、貼り合せられるエラストマーシート1の厚さと熱収縮力、作業者が多層防水シートを屋根材の凹凸に対応できるように変形する場合の作業性、並びに多層防水シートを製造するために用いる織り機の能力により定まる。そして、アルミ箔3の厚みの下限側は、次の三要件により定まる。   The aluminum foil 3 is soft aluminum because the operator forms it manually, and the thickness is preferably about 30 μm to 90 μm (preferably 40 μm). The thickness of the aluminum foil 3 is the thickness and heat shrinkage of the elastomer sheet 1 to be bonded together, the workability when the worker deforms the multilayer waterproof sheet to correspond to the unevenness of the roof material, and the multilayer waterproof sheet is manufactured. It depends on the capacity of the weaving machine used for the purpose. And the lower limit side of the thickness of the aluminum foil 3 is determined by the following three requirements.

(i)エラストマーシート1とアルミ箔3の貼り合わせ工程における巻き巣の発生頻度
(ii)アルミ箔3がエラストマーシート1を積層固定する力に対し、列理方向への熱収縮力が大きくなり、エラストマーシート1がアルミ箔3から剥離してしまうこと、
(iii)アルミ箔3が形状を保持する力に対し、列理方向への熱収縮力が大きくなり、アルミ箔3が表面側に丸まってしまうこと。
(I) Occurrence frequency of the winding nest in the bonding step of the elastomer sheet 1 and the aluminum foil 3 (ii) The heat shrinkage force in the direction of preparation increases with respect to the force by which the aluminum foil 3 laminates and fixes the elastomer sheet 1, That the elastomer sheet 1 is peeled off from the aluminum foil 3,
(Iii) The heat-shrinking force in the line direction increases with respect to the force with which the aluminum foil 3 maintains its shape, and the aluminum foil 3 is rounded to the surface side.

他方、アルミ箔の厚さの上限は、作業者が多層防水シートを手加工で屋根材の凹凸に対応できるように変形できる程度の低剛性が必要である。さらに、エラストマーシート1とアルミ箔3の厚さは、多層防水シートを製造するために用いる織り機で織ることができる剛性である必要がある。これら三要件を充足するアルミ箔3の厚さとしては、30μm〜120μmが好ましい(表1、表2、表3参照)。   On the other hand, the upper limit of the thickness of the aluminum foil needs to be low enough to allow the operator to deform the multilayer waterproof sheet so as to cope with the unevenness of the roofing material by hand processing. Furthermore, the thickness of the elastomer sheet 1 and the aluminum foil 3 needs to be rigid enough to be woven by a weaving machine used to manufacture a multilayer waterproof sheet. As thickness of the aluminum foil 3 which satisfies these three requirements, 30 micrometers-120 micrometers are preferable (refer Table 1, Table 2, Table 3).

樹脂系塗料4は、耐引裂性を考慮し、エポキシ樹脂系塗料の塗布厚を0.5μm〜5μm、好ましくは1μm〜4μm、特に好ましくは3μm程度を焼付け加工するのがよい。樹脂系塗料4は、耐久性や耐食性を向上させることを目的としてコーティングされるが、更にアルミ箔3の裏面への加工ついて、耐引裂性を考慮して定められる。耐引裂性の点は、図2(b)を参照する関係で、該当箇所で詳細に説明する。   In consideration of tear resistance, the resin-based paint 4 is preferably baked to have an epoxy resin-based coating thickness of 0.5 μm to 5 μm, preferably 1 μm to 4 μm, and particularly preferably about 3 μm. The resin-based paint 4 is coated for the purpose of improving durability and corrosion resistance. Further, the processing of the back surface of the aluminum foil 3 is determined in consideration of tear resistance. The point of tear resistance will be described in detail in the relevant part with reference to FIG.

ここで、エラストマーシート1としてクロロスルフォン化ポリエチレンシートを用いた場合の、多層防水シート5の物性について説明する。まず、クロロスルフォン化ポリエチレンシートでは、熱可塑性を有する未架橋ゴムであるため、約70℃以上の温度が加わると、シートの列理方向に大きく収縮が発生してしまう(表1参照)。このため、保形成を有するアルミ箔3に積層固定することが必要となる。   Here, the physical properties of the multilayer waterproof sheet 5 when a chlorosulfonated polyethylene sheet is used as the elastomer sheet 1 will be described. First, since a chlorosulfonated polyethylene sheet is an uncrosslinked rubber having thermoplasticity, when a temperature of about 70 ° C. or higher is applied, a large shrinkage occurs in the direction of the sheet (see Table 1). For this reason, it is necessary to laminate and fix to the aluminum foil 3 having a preserving shape.

この際、より折り曲げ加工を容易にするため、粘着剤2がクロロスルフォン化ポリエチレンシート1とアルミ箔3との二層間の接着に用いられる。なお、粘着剤2は特にアクリル系粘着剤2が好ましい。これはブチルゴムやポリイソブチレンなどでは、クロロスルフォン化ポリエチレンと同様、熱により軟化してしまい、アルミ箔3上にクロロスルフォン化ポリエチレンシート1を固着させておくことができない場合があるだけでなく(表1参照)、ブチル等のゴム系粘着剤では粘性が高すぎて、二層の貼り合わせ工程に用いるラミネート加工装置が使用できず、貼り合わせコストが高くなる場合があるためである。   At this time, the pressure-sensitive adhesive 2 is used for adhesion between the two layers of the chlorosulfonated polyethylene sheet 1 and the aluminum foil 3 in order to facilitate the bending process. The pressure-sensitive adhesive 2 is particularly preferably an acrylic pressure-sensitive adhesive 2. This is because not only butyl rubber or polyisobutylene is softened by heat in the same manner as chlorosulfonated polyethylene, and not only the chlorosulfonated polyethylene sheet 1 cannot be fixed on the aluminum foil 3 (Table 1). 1), a rubber-based adhesive such as butyl has a viscosity that is too high to use a laminating apparatus used in the two-layer bonding process, which may increase the bonding cost.

なお、クロロスルフォン化ポリエチレンシート1を厚くすると、貼り合わせ工程における巻き巣が起こりやすくなるだけでなく、アルミ箔3がクロロスルフォン化ポリエチレンシート1を積層固定する力(β)に対し、列理方向への熱収縮力(α)が大きくなり、クロロスルフォン化ポリエチレンシート1がアルミ箔3から剥離してしまうことや(表2参照)、アルミ箔3が形状を保持する力(γ)に対し、列理方向への熱収縮力(α)が大きくなり、アルミ箔3が表面側に丸まってしまう(表3参照)ため、注意が必要である。   In addition, when the chlorosulfonated polyethylene sheet 1 is thickened, not only is the nest formed in the bonding process easy to occur, but also the aluminum foil 3 is laminated to the force (β) for laminating and fixing the chlorosulfonated polyethylene sheet 1. The heat shrinkage force (α) increases, and the chlorosulfonated polyethylene sheet 1 is peeled off from the aluminum foil 3 (see Table 2), and the force (γ) that the aluminum foil 3 maintains the shape, Care must be taken because the heat shrinkage force (α) in the direction of the line is increased and the aluminum foil 3 is rounded to the surface side (see Table 3).

クロロスルフォン化ポリエチレンシート1とアルミ箔3の厚さ決定は、熱収縮性の条件を満たし、且つ織り機で織ることができ、且つ作業者が手加工で屋根材の凹凸に対応できるアルミ箔3でなければならない。これらの熱収縮性に対する剛性、施工現場での作業性、製造効率の三要件を満たすアルミ箔3の厚さとしては、30μm〜120μmが好ましい。
Determination of the thickness of the chlorosulfonated polyethylene sheet 1 and the aluminum foil 3 is an aluminum foil 3 that satisfies the conditions of heat shrinkability, can be woven by a loom, and can be manually processed by the operator to cope with the unevenness of the roofing material. Must. The thickness of the aluminum foil 3 that satisfies these three requirements of rigidity against heat shrinkability, workability at the construction site, and production efficiency is preferably 30 μm to 120 μm.

続いて、本発明の棟用防水シートに用いられる屋根用防水シートを説明する。図2は屋根用防水シートの構成図で、図2(a)は屋根用防水シートについて図2(b)のA−A方向の断面図、図2(b)は屋根用防水シートの構成斜視図である。 Then, the waterproof sheet for roofs used for the waterproof sheet for buildings of the present invention is explained. FIG. 2 is a configuration diagram of the roof waterproof sheet, FIG. 2A is a cross-sectional view of the roof waterproof sheet in the AA direction of FIG. 2B, and FIG. 2B is a configuration perspective view of the roof waterproof sheet. FIG.

図において、屋根用防水シート10は、多層防水シート5を例えば図2(b)に示すように、この多層防水シート5の長手方向(Length
direction)の途中に該長手方向と直交する横手方向(Transverse direction)にわたって横手方向折返し重合せ部Tを形成し、該長手方向にわたって長手方向折返し重合せ部Lを形成した二方向折り重ね状態としている。
In the figure, the waterproof sheet 10 for roof is made of a multilayer waterproof sheet 5 as shown in FIG. 2B, for example.
The transverse direction folded overlap portion T is formed in the transverse direction perpendicular to the longitudinal direction (Transverse direction) and the longitudinal direction folded overlap portion L is formed in the longitudinal direction. .

図2(a)、(b)に示すように、横手方向折返し重合せ部Tの間隔Lpは、屋根形状の凸凹形状の複雑さに対応するため、適宜に定める。また、横手方向折返し重合せ部Tが存在するため、屋根用防水シート10は、上段屋根用防水シート部101、上段折曲げ部102、折返し屋根用防水シート部103、下段折曲げ部104、下段屋根用防水シート部105、連結屋根用防水シート部106を有している。そして、折返し屋根用防水シート部103を展開すると、上段屋根用防水シート部101と下段屋根用防水シート部105との間隔が、折返し屋根用防水シート部103の長手方向長さL103の二倍の範囲で調整できる。長手方向折返し重合せ部Lの間隔Lpに適合するように、長手側折返し屋根用防水シート部103の長手方向長さL103と長手側連結屋根用防水シート部106の長手方向長さL106が定められる。 As shown in FIGS. 2A and 2B, the interval Lp between the laterally folded portions T is determined as appropriate in order to correspond to the complexity of the uneven shape of the roof shape. Further, since there is a transverse direction folded overlap portion T, the roof waterproof sheet 10 includes an upper roof waterproof sheet portion 101, an upper folded portion 102, a folded roof waterproof sheet portion 103, a lower folded portion 104, and a lower step. It has a roof waterproof sheet portion 105 and a connected roof waterproof sheet portion 106. Then, when the folded roof waterproof sheet portion 103 is expanded, the distance between the upper roof waterproof sheet portion 101 and the lower roof waterproof sheet portion 105 is twice the longitudinal length L 103 of the folded roof waterproof sheet portion 103. Can be adjusted within the range. To match the spacing Lp longitudinal folding the superimposed portion L, the longitudinal length L 106 of the longitudinal length L 103 and the longitudinal side connecting roof tarpaulin portion 106 of the longitudinal side folded roof tarpaulin 103 Determined.

また、図2(b)に示すように、長手方向折返し重合せ部Lが存在するため、屋根用防水シート10は、長手延伸側上段屋根用防水シート部121、長手延伸側上段折曲げ部122、長手延伸側折返し屋根用防水シート部123、長手延伸側下段折曲げ部124、長手延伸側下段屋根用防水シート部125を有している。そして、長手延伸側折返し屋根用防水シート部123を展開すると、長手延伸側上段屋根用防水シート部121と長手延伸側下段屋根用防水シート部125との間隔が、長手延伸側折返し屋根用防水シート部123の横手方向長さT123の二倍の範囲で調整できる。 Further, as shown in FIG. 2B, since the longitudinal folded portion L exists, the roof waterproof sheet 10 includes a longitudinal stretch side upper roof waterproof sheet portion 121 and a longitudinal stretch side upper folded portion 122. , A longitudinally extending side folded roof waterproof sheet portion 123, a longitudinally extending side lower folded portion 124, and a longitudinally extending side lower roof waterproof sheet portion 125. When the longitudinally extending side folded roof waterproof sheet portion 123 is developed, the distance between the longitudinally extending side upper roof waterproof sheet portion 121 and the longitudinally extending side lower roof waterproof sheet portion 125 is set to the longitudinally extending side folded roof waterproof sheet. It can be adjusted in transverse direction length double the range of T 123 parts 123.

横手方向折返し重合せ部Tは、屋根材の凹凸に馴染ませるように貼り付けるため、横手方向折返し重合せ部Tを連続して設け、横手方向折返し重合せ部T同士の間隔Lpと延伸率Exptは、主に被覆対象となる屋根材の凹凸に応じた適宜の価とすることが好ましい。ここで、横手方向折返し重合せ部Tの延伸率Exptは、例えば次式で定義することができる。
Expt=(Lp+2L103)/Lp (1)
In order to attach the transverse direction folded overlap portion T so as to conform to the unevenness of the roofing material, the transverse direction folded overlap portion T is continuously provided, the interval Lp between the transverse direction folded overlap portions T and the stretch ratio Expt Is preferably set to an appropriate value according to the unevenness of the roofing material to be covered. Here, the stretching ratio Expt of the laterally folded portion T can be defined by the following equation, for example.
Expt = (Lp + 2L 103 ) / Lp (1)

長手方向折返し重合せ部Lは、主に被覆対象となる屋根材の段差のような凸凹形状に適合するように長手方向に延伸させるため、長手延伸側折返し屋根用防水シート部123を適宜の長さ確保することが好ましい。ここで、長手方向折返し重合せ部Lの延伸率Explは、例えば屋根用防水シート10の横手方向の長さTallを用いて次式で定義することができる。
Expl=(Tall+2T123)/Tall (2)
The longitudinally folded portion L is stretched in the longitudinal direction mainly so as to conform to the uneven shape such as the step of the roofing material to be covered, so that the longitudinally extending folded roof waterproof sheet portion 123 has an appropriate length. It is preferable to ensure the thickness. Here, the stretch ratio Expl of the overlapped portion L in the longitudinal direction can be defined by the following formula using, for example, the length T all in the transverse direction of the waterproof sheet 10 for roof.
Expl = (T all + 2T 123 ) / T all (2)

本発明の屋根用防水シートによれば、当該二方向折り重ね状態の多層防水シートを用いているので、横手方向折返し重合せ部Tを延伸することで、屋根材の凹凸に対応できると共に、長手方向折返し重合せ部Lを延伸することで、屋根材の段差への対応だけでなく、屋根材の段差による隙間に対して水返しの役目も果たす。また、作業者にとっても、横手方向への薄手のエラストマーシート1の弾性とアルミ箔3の保形性を有するシートのため、手に馴染みやすいため、施工不良が起き難く、施工時間の短縮につながる。   According to the roof waterproof sheet of the present invention, since the multilayer waterproof sheet in the two-way folded state is used, by extending the transverse direction folded overlapping portion T, it is possible to cope with the unevenness of the roof material, and the longitudinal direction. By extending the direction folding overlapping portion L, not only the response to the step difference of the roof material but also the function of returning water to the gap due to the step difference of the roof material is achieved. Moreover, since it is a sheet having the elasticity of the thin elastomer sheet 1 in the transverse direction and the shape retaining property of the aluminum foil 3 for the operator, it is easy to be familiar with the hand, so that it is difficult for construction failure to occur and the construction time is shortened. .

なお、本実施の形態においては、アルミ箔3の裏面への加工として樹脂系塗料4をコーティングする際に、特段の配慮をしている。即ち、図2(b)に示すように、多層防水シート5を長手方向と横手方向の二方向で折畳み加工する場合、アルミ箔3に屈折に伴う応力が掛かり、長手方向折返し重合せ部Lと横手方向折返し重合せ部Tの接点でアルミ箔3が破れやすくなる。そこで、樹脂系塗料4の塗布により当該接点での応力を緩和して、アルミ箔3を破れにくくして、製品の歩留まり率を向上させている。アルミ箔3の当該接点での応力を緩和するため、塗布厚が0.5μm〜5μmであることが望ましい。   In the present embodiment, special consideration is given when the resin-based paint 4 is coated as processing on the back surface of the aluminum foil 3. That is, as shown in FIG. 2 (b), when the multilayer waterproof sheet 5 is folded in two directions, the longitudinal direction and the transverse direction, the aluminum foil 3 is subjected to stress due to refraction, and the longitudinal folded portion L and The aluminum foil 3 is easily broken at the contact point of the overlapped portion T in the transverse direction. Therefore, the resin-based paint 4 is applied to relieve stress at the contact points, making the aluminum foil 3 difficult to break and improving the product yield rate. In order to relieve the stress at the contact point of the aluminum foil 3, it is desirable that the coating thickness is 0.5 μm to 5 μm.

また仮に、図2(b)に示すような、長手方向折返し重合せ部Lと横手方向折返し重合せ部Tとの接点を起点として、仮にアルミ箔3に破れが生じた場合であっても、耐引き裂性に優れるクロロスルフォン化ポリエチレンシート1によって破れる領域の拡大を防止でき、破断の急速な拡大を防止できる。   Further, even if the aluminum foil 3 is torn, starting from the contact point between the longitudinal folded portion L and the transverse folded portion T as shown in FIG. 2 (b), The chlorosulfonated polyethylene sheet 1 having excellent tear resistance can prevent the area to be broken from being expanded and can prevent rapid expansion of the break.

続いて、発明である棟用防水シートを説明する。図3は、棟用防水シートの一実施の形態を説明する構成図で、(a)は上面から見た平面図、(b)は図3(a)のb−b方向から見た横手方向断面図、(c)は下面から見た底面図、(d)は図3(a)d−d方向から見た側面図である。二方向折り重ね状態の屋根用防水シート10に用いる多層防水シート5には、横手方向折返し重合せ部Tと長手方向折返し重合せ部Lとを形成した二方向折り重ね状態のものを用いているので、棟用防水シート20は長手方向だけでなく横手方向にも延伸性を有する。 Subsequently, the ridge waterproof sheet according to the present invention will be described. FIGS. 3A and 3B are configuration diagrams illustrating an embodiment of a waterproof sheet for a building, in which FIG. 3A is a plan view seen from the top, and FIG. 3B is a transverse direction seen from the bb direction in FIG. Sectional drawing, (c) is a bottom view seen from the lower surface, and (d) is a side view seen from the direction of FIG. 3 (a) dd. As the multilayer waterproof sheet 5 used for the roof waterproof sheet 10 in the two-way folded state, the one in the two-way folded state in which the transverse direction folded overlap portion T and the longitudinal direction folded overlap portion L are formed is used. Therefore, the waterproof sheet 20 for ridges has a stretching property not only in the longitudinal direction but also in the lateral direction.

図において、棟用防水シート20は、屋根用防水シート10を棟部用に適宜の形状にして用いると共に、粘着テープ25、剥離紙26、釘穴シール性シート部27を有している。図3(a)に示すように、棟用防水シート20は、釘穴シール性シート部27を介して左右対称の形状を有している。棟用防水シート20には、長手方向折返し重合せ部Lが釘穴シール性シート部27に沿って左右に夫々二箇所設けられている。長手方向折返し重合せ部Lが存在するため、棟用防水シート20は、上段棟用防水シート部201、上段折曲げ部202、折返し棟用防水シート部203、下段折曲げ部204、下段棟用防水シート部205を左右対称に有している。また、図3(c)に示すように、折り目部206は、棟用防水シート20の下面に現れており、釘穴シール性シート部27と上段棟用防水シート部201との位置合わせ部位である。典型的な棟用防水シート20の形状は、横手方向に関しては、釘穴シール性シート部27の長さT27と、折返し棟用防水シート部203を折り重ねた状態での上段棟用防水シート部201と下段棟用防水シート部205との両端の間隔T,Tを用いて、(T+T27+T)となっている。他方、棟用防水シート20の長手方向の長さLallは、棟の長さや棟用防水シート20の全体重量と作業性の観点から、適宜に定める。 In the figure, the ridge waterproof sheet 20 uses the roof waterproof sheet 10 in an appropriate shape for the ridge, and has an adhesive tape 25, release paper 26, and a nail hole sealing sheet portion 27. As shown in FIG. 3A, the ridge waterproof sheet 20 has a symmetrical shape with a nail hole sealing sheet portion 27 interposed therebetween. The waterproof sheet 20 for ridges is provided with two folded portions L in the longitudinal direction along the nail hole sealing sheet portion 27 on the left and right. Since there is a folded portion L in the longitudinal direction, the waterproof sheet 20 for the ridge includes the waterproof sheet portion 201 for the upper ridge, the upper folded portion 202, the waterproof sheet portion 203 for the folded ridge, the lower folded portion 204, and the lower fold portion. The waterproof sheet portion 205 is symmetrically provided. Further, as shown in FIG. 3C, the fold portion 206 appears on the lower surface of the ridge waterproof sheet 20, and is an alignment portion between the nail hole sealing sheet portion 27 and the upper ridge waterproof sheet portion 201. is there. As for the typical shape of the waterproof sheet 20 for the ridge, with respect to the lateral direction, the length T 27 of the nail hole sealing sheet 27 and the waterproof sheet 203 for the upper ridge in a state where the folded waterproof sheet 203 is folded. Using the distances T r and T l between both ends of the portion 201 and the lower ridge waterproof sheet portion 205, (T r + T 27 + T l ) is obtained. On the other hand, the longitudinal length L all of the ridge waterproof sheet 20 is appropriately determined from the viewpoint of the ridge length, the overall weight of the ridge waterproof sheet 20 and workability.

粘着テープ25は、ブチルまたはEPDMが好ましい。壁際用簡便施工装置の長手方向の裾部Mに幅10mm〜50mm(好ましくは30mm)装着することが好ましい。釘穴シール性シート部27には、例えばポリプロピレンの不織布またはルーフィングと同質材を用いる。このように構成すると、上段棟用防水シート部201を構成する未架橋クロロスルフォン化ポリエチレンと、これを被覆する釘穴シール性シート部27によって、未架橋クロロスルフォン化ポリエチレンの可塑性が保持され、釘穴シール性を保持できる。   The adhesive tape 25 is preferably butyl or EPDM. It is preferable that a width of 10 mm to 50 mm (preferably 30 mm) is attached to the skirt M in the longitudinal direction of the simple construction apparatus for a wall. For the nail hole sealing sheet portion 27, for example, a polypropylene non-woven fabric or a material similar to roofing is used. If comprised in this way, the plasticity of uncrosslinked chlorosulfonated polyethylene is maintained by the uncrosslinked chlorosulfonated polyethylene constituting the upper ridge waterproof sheet portion 201 and the nail hole sealing sheet portion 27 covering this, and the nail The hole sealability can be maintained.

横手方向折返し重合せ部Tは、屋根材の凹凸に馴染ませるように貼り付けるため、折返し重合せ部Tを連続して設け、折返し重合せ部T同士の間隔Lpは6mm〜18mmであり、延伸率Exptが140%〜160%であることが好ましい。長手方向折返し重合せ部Lは、主に屋根材の谷部に沿うように長手方向に延伸させるため、折返し棟用防水シート部203の横手方向の長さT203を20mm〜40mm確保することが好ましい。 In order to attach the overlapped portion T in the transverse direction so as to conform to the unevenness of the roofing material, the overlapped portion T is continuously provided, the interval Lp between the folded overlapped portions T is 6 mm to 18 mm, The rate Expt is preferably 140% to 160%. The longitudinal folded portion L is stretched in the longitudinal direction mainly along the valley portion of the roofing material, so that the lateral length T 203 of the folded ridge waterproof sheet portion 203 can be ensured from 20 mm to 40 mm. preferable.

本発明の棟用防水シートによれば、屋根用防水シート10を棟部用に適宜の形状に裁断しているので、横手方向折返し重合せ部Tを延伸することで、屋根材の凹凸に対応できると共に、長手方向折返し重合せ部Lを延伸することで、屋根材の段差への対応だけでなく、水返しの役目も果たす。また、作業者にとっても、横手方向への薄手のエラストマーシート1の弾性とアルミ箔3の保形性を有するシートのため、手に馴染みやすいため、平坦な屋根瓦の葺かれている領域と比較して、棟瓦部のように屋根傾斜の異なる領域の境界において類型的に生じやすい施工不良の発生が防止でき、施工時間の短縮につながる。   According to the ridge waterproof sheet of the present invention, the roof waterproof sheet 10 is cut into an appropriate shape for the ridge portion, so that it can cope with the unevenness of the roof material by extending the laterally folded portion T. At the same time, by extending the overlapped portion L in the longitudinal direction, it not only responds to the steps of the roofing material but also serves as a water return. In addition, because it is a sheet that has the elasticity of the thin elastomer sheet 1 in the transverse direction and the shape retaining property of the aluminum foil 3 for the operator, it is easy to adjust to the hand, so it is compared with the area where flat roof tiles are sown. Thus, it is possible to prevent the occurrence of construction defects that tend to occur typi- cally at the boundary between regions with different roof slopes, such as a ridge tile, leading to a reduction in construction time.

図4は、棟用防水シートの他の実施の形態を説明する構成図で、(a)は上面から見た平面図、(b)は図4(a)のb−b方向から見た横手方向断面図、(c)は下面から見た底面図、(d)は図4(a)d−d方向から見た側面図である。図において、棟用防水シート20は、屋根用防水シート10を棟部用に適宜の形状に裁断すると共に、粘着テープ25、剥離紙26、釘穴シール性シート部27、通気撥水繊維部28、通気孔部29を有している。   4A and 4B are configuration diagrams for explaining another embodiment of the waterproof sheet for a building, in which FIG. 4A is a plan view seen from the upper surface, and FIG. 4B is a lateral view seen from the bb direction in FIG. Sectional drawing of a direction, (c) is the bottom view seen from the lower surface, (d) is the side view seen from Fig.4 (a) dd direction. In the figure, the ridge waterproof sheet 20 cuts the roof waterproof sheet 10 into an appropriate shape for the ridge, and also includes an adhesive tape 25, a release paper 26, a nail hole sealing sheet 27, and a ventilated water repellent fiber 28. The air hole portion 29 is provided.

通気撥水繊維部28は、例えば不織布に撥水処理をしたもので、上段棟用防水シート部201の上側に、上段棟用防水シート部201の両側に位置する上段折曲げ部202まで被覆する状態で設けられている。通気孔部29は、上段棟用防水シート部201の両側に位置する折り目部206と上段折曲げ部202との間に、長手方向に連続して設ける。通気孔部29の形状は、通気撥水繊維部28で被覆された状態で通気性が確保できるように定めるのがよい。ここでは、上段棟用防水シート部201の両側に位置する折り目部206の間隔T206と、折返し棟用防水シート部203を折り重ねた状態での上段棟用防水シート部201と下段棟用防水シート部205との両端の間隔T,Tを用いて、(T+T206+T)となっている。図4(c)に示すように、通気孔部29は長手方向に二列又は三列形成してある。 The ventilated water repellent fiber portion 28 is, for example, a non-woven fabric subjected to water repellency treatment and covers the upper fold waterproof sheet portion 201 up to the upper bent portion 202 located on both sides of the upper ridge waterproof sheet portion 201. It is provided in the state. The vent hole 29 is continuously provided in the longitudinal direction between the fold portion 206 and the upper bent portion 202 located on both sides of the upper ridge waterproof sheet portion 201. The shape of the vent hole 29 is preferably determined so that air permeability can be secured in a state where the vent hole 29 is covered with the vent water-repellent fiber portion 28. Here, the space T 206 between the folds 206 located on both sides of the upper ridge waterproof sheet 201 and the upper ridge waterproof sheet 201 and the lower ridge waterproof with the folded fold waterproof sheet 203 folded. The distances T r and T l between both ends of the sheet portion 205 are used, and (T r + T 206 + T l ). As shown in FIG. 4C, the vent holes 29 are formed in two or three rows in the longitudinal direction.

図5は、棟用防水シートの施工状態を説明する要部拡大断面図で、(a)は屋根の棟部近傍における棟用防水シートの納まり状態を説明する要部断面図、(b)は棟用防水シートの棟部近傍における作業態様を説明する要部断面図、(c)は棟用防水シートの効用を説明する要部断面図である。図5(b)に示すように、棟用防水シートの裾部を棟木の上辺を軸にして下ろすことで、棟包の内側に納まることを示した図である。図5(c)に示すように、棟用防水シートが雨水を遮断して、空気を通している状態を説明している。   FIG. 5: is a principal part expanded sectional view explaining the construction state of the waterproof sheet for ridges, (a) is principal part sectional drawing explaining the accommodation state of the waterproof sheet | seat for ridges in the vicinity of the ridge part of a roof, (b) The principal part sectional drawing explaining the operation | work aspect in the ridge part vicinity of the ridge waterproof sheet, (c) is principal part sectional drawing explaining the effect of the ridge waterproof sheet. As shown in FIG. 5 (b), it is a view showing that the bottom of the ridge waterproof sheet is placed inside the ridge parcel by lowering the ridge of the ridge tree around the upper side. As shown in FIG.5 (c), the state which the waterproof sheet | seat for buildings blocks | prevents rainwater and has let air pass is demonstrated.

図5(a)において、施工対象となる建造物の屋根の棟部30には、棟木31、棟木支持材32、ルーフィング33、桟木34、屋根材35、棟包36、ビス37、木ズリ38、野地板39が用いられている。ここで、棟木31は、屋根の最上部に、桁行(けたゆき)方向に取り付ける横木をいう。棟木支持材32は、例えば発泡ポリスチレンのような樹脂製が好ましく、棟木31を支持する棟木接触部321と、棟木31とルーフィング33までの間隙に設けられて支持する縦支持部322と、棟を境として両側に傾斜しているルーフィング33と接触する逆Y字形接触部323とを有している。ルーフィング33は、防水作用のあるシート状の部材で、屋根材35が瓦の場合にはアスファルト系シートが用いられる。   In FIG. 5A, the ridge 30 of the roof of the building to be constructed includes a purlin 31, a purlin support material 32, a roofing 33, a pier 34, a roof material 35, a parcel 36, a screw 37, and a wood slide 38. A field plate 39 is used. Here, the purlin 31 is a cross that is attached to the top of the roof in the girder direction. The purlin support material 32 is preferably made of a resin such as expanded polystyrene, for example, a purlin contact portion 321 that supports the purlin 31, a vertical support portion 322 that is provided and supported in a gap between the purlin 31 and the roofing 33, and a ridge As a boundary, it has an inverted Y-shaped contact portion 323 that contacts the roofing 33 that is inclined on both sides. The roofing 33 is a sheet-like member having a waterproof effect, and an asphalt-based sheet is used when the roofing material 35 is a tile.

桟木34は、屋根の瓦35をとめるときに使用する部材で、風通しをよくするため材に直交して間に挟む小角材である。屋根材35には、典型的には瓦やスレートを用いるが、瓦のような厚型の屋根材を用いるとよい。棟包36は、棟木31を被覆して防水を確実にするもので、耐久性の高い金属板や屋根材と同質素材が用いられる。ビス37は、棟包36を棟木31に固定するのに用いるもので、金属製の剛性が高く耐久性の高い材料が用いられる。木ズリ38は、桟木34の下に垂直に設置する幅20mm程度のテープ状のもので、桟木34に雨水が溜まらず、流れ落ちる。野地板39は、屋根瓦などを固定する屋根面の下地合板をいい、垂木の上に合板を張り、その上にルーフィング33を施工してある。   The pier 34 is a member used when the roof tiles 35 are stopped, and is a small square member sandwiched between the members in order to improve ventilation. The roof material 35 is typically a tile or a slate, but a thick roof material such as a tile may be used. The ridge wrap 36 covers the purlin 31 to ensure waterproofness, and is made of the same material as a highly durable metal plate or roof material. The screw 37 is used to fix the ridge 36 to the purlin 31 and is made of a metal material having high rigidity and durability. The wood slide 38 is a tape-like thing with a width of about 20 mm installed vertically below the pier 34, and rainwater does not collect on the pier 34 and flows down. The field board 39 is a base plywood on the roof surface for fixing roof tiles and the like, and a plywood is stretched on a rafter and a roofing 33 is constructed thereon.

このように構成された施工対象となる建造物の屋根の棟部近傍における、棟用防水シート20の設置手順を次に説明する。図6は、棟用防水シートの設置方法を説明する流れ図、図7は棟の長手方向に棟用防水シートを敷設する場合を説明する斜視図である。まず、図5(b)(i)に示すように、棟用防水シート20の長手方向の中央部を、棟木31の上側面に屋根の棟方向と並行に設置する(ステップ100)。次に、棟用防水シート20を棟木31にステープル等で仮止めする(ステップ102)。ステープル等を打つのは、釘穴シール性シート部27とするのがよい。次に、棟用防水シート20の長手方向の裾部を棟木31に対して押し下げると共に、粘着テープ25の剥離紙26を剥がす(ステップ104)。ここで、ステップ104の棟用防水シート20の長手方向の裾部を棟木31に対して押し下げと、粘着テープ25の剥離紙26を剥がすこととは、時間的に前者と後者を同時並行的に行ってよく、また後者の剥離を先に行ってから前者の押し下げを行っても良い。棟用防水シート20の長手方向の裾部を棟木31に対して押し下げる際に、粘着テープ25の剥離紙26を剥がしながら押し下げることで、同時並行的に作業でき、施工の手順を簡略化できる。   Next, the installation procedure of the waterproof sheet for buildings 20 in the vicinity of the ridge portion of the roof of the building to be constructed as described above will be described. FIG. 6 is a flowchart for explaining a method for installing the ridge waterproof sheet, and FIG. 7 is a perspective view for explaining a case where the ridge waterproof sheet is laid in the longitudinal direction of the ridge. First, as shown in FIGS. 5B and 5I, the longitudinal center of the ridge waterproof sheet 20 is installed on the upper side surface of the purlin 31 in parallel with the ridge direction of the roof (step 100). Next, the ridge waterproof sheet 20 is temporarily fixed to the purlin 31 with staples (step 102). The nail hole sealing sheet portion 27 is preferably used for hitting staples or the like. Next, the longitudinal skirt of the ridge waterproof sheet 20 is pushed down against the purlin 31 and the release paper 26 of the adhesive tape 25 is peeled off (step 104). Here, pressing down the longitudinal skirt of the ridge waterproof sheet 20 in step 104 against the purlin 31 and peeling off the release paper 26 of the adhesive tape 25 means that the former and the latter are simultaneously performed in parallel. Alternatively, the former may be peeled off first, and then the former may be pushed down. When the skirt portion in the longitudinal direction of the waterproof sheet for buildings 20 is pushed down against the purlin 31, it is possible to work in parallel by pushing down while peeling the release paper 26 of the adhesive tape 25, thereby simplifying the construction procedure.

なお、棟用防水シート20が接着テープ25を有している場合に、棟用防水シート20を屋根材35の山部352や谷部354と接着するために、粘着テープ25に設けられた剥離紙26を剥がすタイミングは、ステップ102とステップ104との間やステップ104と同時に限られるものではなく、後で述べるようなステップ104とステップ106との間、ステップ106とステップ108との間、ステップ108とステップ1010との間、の何れでもよい。   In addition, when the ridge waterproof sheet 20 has the adhesive tape 25, the peeling provided on the adhesive tape 25 in order to bond the ridge waterproof sheet 20 to the peak portion 352 and the valley portion 354 of the roof material 35. The timing at which the paper 26 is peeled off is not limited between step 102 and step 104 or at the same time as step 104, but between step 104 and step 106, between step 106 and step 108, as described later, Either of 108 and step 1010 may be used.

次に、図5(b)(ii)・(iii)に示すように、棟用防水シート20の裾部24が屋根材35に届かない場合に、長手方向折返し重合せ部Lを横手方向に延伸させて、裾部24が屋根材35に届く状態にする(ステップ106)。この場合、長手方向折返し重合せ部Lを横手方向に延伸させる程度としては、裾部24を棟包36の内側の墨打ち位置に納まる程度にするのがよい。続いて、屋根材35の山部352に対しては、棟用防水シート20を長手方向に接着する(ステップ108)。他方、屋根材35の谷部354に対しては、当該谷部形状に沿うように、棟用防水シート20を長手方向に延伸させて接着する(ステップ110)。棟用防水シート20と屋根材35の山部352や谷部354との接着には、粘着テープ25を用いるのがよい。屋根材35として日本瓦のように一枚の瓦に山部352と谷部354が存在するものを用いると、隣接する瓦相互の設置において山部352と谷部354の端部を旨く位置合わせすることで、雨水に対する耐性の高い、強固に一体構造の屋根が構成できる(ステップ112)。このとき、図7に示すように、棟用防水シート20は、屋根材35の山部352や谷部354の形状に適合させると共に、棟木31の形状に適合させる必要がある。そこで、棟用防水シート20の横手方向折返し重合せ部Tに関しては、棟木31のように平坦な場合では重ね合せた状態で装着し、屋根材35の山部352や谷部354のように凸凹形状の場合は重ね合せた状態から展開状態にして、装着する。   Next, as shown in FIGS. 5 (b), (ii) and (iii), when the skirt 24 of the waterproof sheet for buildings 20 does not reach the roofing material 35, the overlapped portion L in the longitudinal direction is set in the transverse direction. The skirt 24 is stretched to reach the roof material 35 (step 106). In this case, it is preferable that the longitudinal direction folded overlap portion L is extended in the lateral direction so that the skirt portion 24 is accommodated in the inking position inside the ridge 36. Subsequently, the ridge waterproof sheet 20 is bonded in the longitudinal direction to the mountain portion 352 of the roof material 35 (step 108). On the other hand, the ridge waterproof sheet 20 is stretched in the longitudinal direction and bonded to the valley 354 of the roof material 35 so as to follow the valley shape (step 110). Adhesive tape 25 may be used for bonding the ridge waterproof sheet 20 to the peak portions 352 and valley portions 354 of the roof material 35. If the roof material 35 is a single tile, such as a Japanese tile, with a peak 352 and a valley 354, the edges of the peaks 352 and the valley 354 are aligned well in the installation of adjacent tiles. By doing so, a strongly integrated roof having high resistance to rainwater can be formed (step 112). At this time, as shown in FIG. 7, the ridge waterproof sheet 20 needs to be adapted to the shape of the peak portion 352 and the valley portion 354 of the roof material 35 and to the shape of the purlin 31. Accordingly, the laterally folded overlapped portion T of the waterproof sheet 20 for the ridge is mounted in a superposed state when it is flat like the purlin 31 and is uneven like the mountain portion 352 or the valley portion 354 of the roofing material 35. In the case of a shape, it is mounted from the overlapped state to the expanded state.

図6に示す棟用防水シートの設置手順によれば、図5(b)に示すように、棟用防水シート20の長手方向の裾部を棟木31に対して押し下げた位置が、棟包36からはみ出ることはない。これにより、棟包内の墨打ちをした所定位置に納まり、裾部が所定位置に届かない場合は、長手方向折返し重合せ部Lを横手方向に伸ばして屋根材35に接着でき、従来の棟用防水シート20に長手方向折返し重合せ部Lが存在しない場合において、棟用防水シート20がはみ出た場合にも棟用防水シート20の折り曲げ作業をする必要がなくなる。   According to the installation procedure of the waterproof sheet for ridges shown in FIG. 6, as shown in FIG. It doesn't stick out. As a result, when the ink cartridge is placed in a predetermined position in the building wrapping and the skirt portion does not reach the predetermined position, the folded portion L in the longitudinal direction can be extended in the lateral direction and adhered to the roofing material 35. In the case where the longitudinal folding portion L does not exist in the waterproof sheet 20 for the building, even when the waterproof sheet 20 for the building protrudes, there is no need to bend the waterproof sheet 20 for the building.

長手方向折返し重合せ部Lは、折返し棟用防水シート部203を折り重ねた状態から横手方向に伸ばすことによって、棟木31の高さが各種の建築物によって相違する場合にも、単一の棟用防水シート20で対処できる範囲が広がる。また、長手方向折返し重合せ部Lは、建造物の屋根内部への浸水を防止する止面戸と同様の機能を発揮する水返し部としても使用できると共に、さらに粘着テープ25の装着幅を広げることにも使用できる。   Even if the height of the purlin 31 is different depending on various buildings by extending the folded folding waterproof sheet portion 203 from the folded state in the lateral direction, the longitudinal folding portion L is a single building. The range that can be dealt with by the waterproof sheet 20 is expanded. Moreover, while the longitudinal direction folding superimposition part L can be used also as a water return part which exhibits the function similar to the stop door which prevents the infiltration of the inside of the roof of a building, the mounting width of the adhesive tape 25 is further expanded. Can also be used.

図6(ステップ100)のように、棟用防水シート20の長手方向の中央部を、棟木31の上側面に長手方向に固定することで、作業者は両手を用いて、図5(a)に図示するように、棟用防水シート20の両裾部を屋根材35に隙間なく貼り付けることができる。また、棟包36部の外側に棟用防水シート20の裾部が出ることがなく、意匠性も良好である。   As shown in FIG. 6 (step 100), by fixing the longitudinal center portion of the ridge waterproof sheet 20 to the upper side surface of the purlin 31 in the longitudinal direction, the operator uses both hands, and FIG. As shown in the figure, both hem parts of the waterproof sheet 20 for ridges can be attached to the roof material 35 without a gap. Moreover, the skirt part of the waterproof sheet 20 for ridges does not come out on the outer side of 36 parts of the ridge package, and the design property is also favorable.

本発明の棟用防水シートの設置方法によれば、多層防水シートが折り曲げ加工性と耐久性も併せ持つので、棟用防水シート20を施工後、時間と共にエラストマーシート1が常温で形状記憶するため、裾部の下面に装着されている粘着テープ25の接着力とアルミ箔3の形保性に加え、エラストマーシート1も形状を記憶しているため、屋根材35への接着に大きく貢献する。例えば、仮に経年後に粘着テープ25の粘着力の低下があった場合でも、アルミ箔3の保形性だけでなく、多層防水シート5の効果によって、屋根材35から剥離する危険性が減るので、これに伴い漏水の危険性も減るため、結果的に建造物の高耐久化に寄与するものである。   According to the installation method of the waterproof sheet for ridges of the present invention, since the multilayer waterproof sheet has both foldability and durability, after the waterproof sheet 20 for ridges is constructed, the elastomer sheet 1 stores the shape at room temperature over time. In addition to the adhesive strength of the adhesive tape 25 attached to the lower surface of the hem and the shape-preserving property of the aluminum foil 3, the elastomer sheet 1 also stores the shape, which greatly contributes to adhesion to the roofing material 35. For example, even if there is a decrease in the adhesive strength of the adhesive tape 25 after aging, not only the shape retention of the aluminum foil 3 but also the risk of peeling from the roofing material 35 due to the effect of the multilayer waterproof sheet 5 is reduced. As a result, the risk of water leakage is reduced, resulting in higher durability of the building.

また、本発明の棟用防水シートを用いた棟施工ユニットによれば、次のような特徴がある。即ち、棟木支持材32は、従来のように防錆加工された金属製の場合には剛性に乏しく、風や積雪などで揺れたり曲がってしまう課題があった。しかし、棟木支持材として、棟木接触部321、縦支持部322、逆Y字形接触部323を有する樹脂製棟支持材32を用いることで、堅牢性を確保して、長期間使用しても倒れることが防止できる。   Moreover, according to the building construction unit using the waterproof sheet for buildings of this invention, there exist the following characteristics. That is, the purlin support material 32 has a problem that it is poor in rigidity when it is made of a rust-proof metal as in the prior art, and is swayed or bent due to wind or snow. However, as the purlin support material, the resin ridge support material 32 having the purlin contact portion 321, the vertical support portion 322, and the inverted Y-shaped contact portion 323 is used to ensure robustness and fall down even when used for a long time. Can be prevented.

以上、添付図面を参照して、この発明の実施形態を説明したが、この発明はかかる実施形態に限定されるものではなく、特許請求の範囲の記載から把握される技術的範囲において種々の形態に変更可能である。例えば、上記実施例においては、屋根用防水シートの用途として棟用防水シートを例示しているが、本発明はこれに限定されるものではなく、雨水が建築物に侵入しやすい箇所における雨止めシール材として利用できる。   As mentioned above, although embodiment of this invention was described with reference to an accompanying drawing, this invention is not limited to this embodiment, Various forms in the technical scope grasped | ascertained from description of a claim Can be changed. For example, in the above embodiment, the waterproof sheet for ridges is illustrated as an application of the waterproof sheet for roofs, but the present invention is not limited to this, and the rain stopper in a place where rainwater easily enters the building. It can be used as a sealing material.

本発明の棟用防水シートに用いられる多層防水シートの拡大断面図である。It is an expanded sectional view of the multilayer waterproof sheet used for the waterproof sheet for buildings of the present invention . 屋根用防水シートの構成図で、(a)は屋根用防水シートについて(b)のA−A方向の断面図、(b)は屋根用防水シートの構成斜視図である。It is a block diagram of the waterproof sheet for roofs, (a) is sectional drawing of the AA direction of (b) about the waterproof sheet for roofs, (b) is a structure perspective view of the waterproof sheet for roofs. 棟用防水シートの一実施の形態を説明する構成図で、(a)は上面から見た平面図、(b)は図3(a)のb−b方向から見た横手方向断面図、(c)は下面から見た底面図、(d)は図3(a)d−d方向から見た側面図である。BRIEF DESCRIPTION OF THE DRAWINGS It is a block diagram explaining one embodiment of the waterproof sheet | seat for ridges, (a) is the top view seen from the upper surface, (b) is a transverse direction sectional view seen from the bb direction of Fig.3 (a), ( FIG. 3C is a bottom view seen from the bottom surface, and FIG. 3D is a side view seen from the direction of FIG. 棟用防水シートの他の実施の形態を説明する構成図で、(a)は上面から見た平面図、(b)は図4(a)のb−b方向から見た横手方向断面図、(c)は下面から見た底面図、(d)は図4(a)d−d方向から見た側面図である。It is a block diagram explaining other embodiment of the waterproof sheet for wings, (a) is a top view seen from the upper surface, (b) is a transverse direction sectional view seen from the bb direction of FIG. 4 (a), (C) is the bottom view seen from the lower surface, (d) is the side view seen from Fig.4 (a) dd direction. 棟用防水シートの施工状態を説明する要部拡大断面図で、(a)は屋根の棟部近傍における棟用防水シートの納まり状態を説明する要部断面図、(b)は棟用防水シートの棟部近傍における作業態様を説明する要部断面図、(c)は棟用防水シートの効用を説明する要部断面図である。It is a principal part expanded sectional view explaining the construction state of the waterproof sheet | seat for buildings, (a) is principal part sectional drawing explaining the accommodation state of the waterproof sheet for buildings in the vicinity of the ridge part of a roof, (b) is a waterproof sheet for buildings. The principal part sectional drawing explaining the operation | work aspect in the vicinity of a ridge part of this is, (c) is principal part sectional drawing explaining the effect of the waterproof sheet | seat for ridges. 棟用防水シートの設置方法を説明する流れ図である。It is a flowchart explaining the installation method of the waterproof sheet for buildings. 棟の長手方向に棟用防水シートを敷設する場合を説明する斜視図である。It is a perspective view explaining the case where the waterproof sheet for ridges is laid in the longitudinal direction of a ridge.

1 エラストマーシート(クロロスルフォン化ポリエチレン)
2 粘着剤(アクリル樹脂系粘着剤)
3 アルミ箔
4 樹脂系塗料
5 多層防水シート
10 屋根用防水シート
20 棟用防水シート
25 粘着テープ(ブチルテープ)
26 剥離紙
27 釘穴シール性シート部
28 通気撥水繊維部
29 通気孔部
30 棟部
31 棟木
32 棟木支持材
33 ルーフィング
34 桟木
35 屋根材(瓦)
36 屋根材(棟包)
38 木ズリ
39 野地板(下地板)
L.長手方向折返し重合せ部(Length direction)
T.横手方向折返し重合せ部(Transverse direction)
1 Elastomer sheet (chlorosulfonated polyethylene)
2 Adhesive (acrylic resin adhesive)
3 Aluminum foil 4 Resin-based paint 5 Multi-layered waterproof sheet 10 Waterproof sheet for roof 20 Waterproof sheet for building 25 Adhesive tape (butyl tape)
26 Release paper 27 Nail hole sealing sheet portion 28 Ventilated water repellent fiber portion 29 Vent hole portion 30 Building portion 31 Purlin 32 Purlin support material 33 Roofing 34 Pier 35 Roof material (tile)
36 Roofing material (building wrap)
38 Wood shear 39 Field board (underlying board)
L. Longitudinal folding part (Length direction)
T.A. Transverse direction

Claims (5)

棟用防水シートの長手方向の両裾部を、棟木に対して屋根材に下ろした場所が、棟包の両裾を垂直に下ろした線又はその内側に納まるように、構成されたことを特徴とする、棟用防水シート。   It is constructed so that the place where both hems in the longitudinal direction of the waterproof sheet for the ridge are lowered to the roof material with respect to the purlin is placed in the line where the hems of the ridge parcel are vertically lowered or inside it. A waterproof sheet for the building. 前記棟包の横手寸法は180〜240mmであり、
前記棟用防水シートが、前記棟包の内側の墨打ち位置に相当する線か、その線の内側に納まるように、構成されたことを特徴とする請求項1に記載の棟用防水シート。
The lateral dimension of the ward package is 180-240 mm,
2. The ridge waterproof sheet according to claim 1, wherein the ridge waterproof sheet is configured such that the ridge waterproof sheet is placed in a line corresponding to an inking position on the inner side of the ridge parcel or on the inner side of the line.
前記棟用防水シートは、耐引き裂き性と熱収縮性を有するエラストマーシートを、粘着剤を用いてアルミ箔の表面側に貼り合わせ、該アルミ箔の裏面側に、樹脂系塗料をコーティングした多層防水シートであって、当該多層防水シートの長手方向の途中に該長手方向と直交する横手方向にわたって横手方向折返し重合せ部を形成し、該長手方向にわたって長手方向折返し重合せ部を形成した屋根用防水シートを用いることを特徴とする、請求項1又は請求項2に記載の棟用防水シート。The building waterproof sheet is a multi-layer waterproof sheet in which an tear-resistant and heat-shrinkable elastomer sheet is bonded to the front surface side of an aluminum foil using an adhesive, and the rear surface side of the aluminum foil is coated with a resin-based paint. Waterproofing for roofs, in which a transverse folded portion is formed in the transverse direction perpendicular to the longitudinal direction in the middle of the multilayer waterproof sheet, and a longitudinal folded portion is formed in the longitudinal direction. The ridge waterproof sheet according to claim 1 or 2, wherein a sheet is used. 請求項乃至請求項の何れか1項に記載の棟用防水シートの長手方向の中央部を、棟木の上側面に屋根の棟方向と並行に設置する工程と、
棟用防水シートを棟木にステープル等で仮止めする工程と、
棟用防水シートの長手方向の裾部を棟木に対して押し下げる工程と、
前記棟用防水シートの裾部が屋根材に届かない場合に、前記長手方向折返し重合せ部を横手方向に延伸させて、当該裾部が当該屋根材に届く状態にする工程と、
前記屋根材の山部に対しては、前記棟用防水シートの裾部を長手方向に接着する工程と、
前記屋根材の谷部に対しては、当該谷部形状に沿うように、前記棟用防水シートを長手方向に延伸させて接着する工程と、
を備えることを特徴とする棟用防水シートの設置方法。
A longitudinal central portion of the ridge waterproof sheet according to any one of claims 1 to 3, a step of placing the upper surface of the purlin parallel to the ridge direction of a roof,
A process of temporarily fixing the waterproof sheet for the ridge to the purlin with staples,
A process of pushing down the hem in the longitudinal direction of the waterproof sheet for building against the purlin;
When the skirt of the ridge waterproof sheet does not reach the roofing material, extending the longitudinal folding portion in the transverse direction, and making the skirt reach the roofing material; and
For the mountain part of the roofing material, the step of adhering the hem part of the waterproof sheet for ridges in the longitudinal direction;
For the troughs of the roof material, the step of extending and bonding the ridge waterproof sheet in the longitudinal direction so as to follow the trough shape,
The installation method of the waterproof sheet | seat for buildings characterized by comprising.
請求項乃至請求項の何れか1項に記載の棟用防水シートを用いると共に、
前記棟用防水シートで被覆される棟木の支持に樹脂製棟支持材を用いたことを特徴とする棟用防水シートを用いた棟施工ユニット。
With use of the waterproof sheet for building according to any one of claims 1 to 4,
A ridge construction unit using a ridge waterproof sheet, wherein a resin ridge support material is used to support a ridge that is covered with the ridge waterproof sheet.
JP2008270757A 2008-10-21 2008-10-21 Building waterproof sheet, installation method of building waterproof sheet, building construction unit using building waterproof sheet Active JP4925222B2 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2008270757A JP4925222B2 (en) 2008-10-21 2008-10-21 Building waterproof sheet, installation method of building waterproof sheet, building construction unit using building waterproof sheet

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP2008270757A JP4925222B2 (en) 2008-10-21 2008-10-21 Building waterproof sheet, installation method of building waterproof sheet, building construction unit using building waterproof sheet

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
JP2008198379A Division JP4384725B1 (en) 2008-07-31 2008-07-31 Roof waterproof sheet, building waterproof sheet, building waterproof sheet installation method, building construction unit using the building waterproof sheet

Publications (3)

Publication Number Publication Date
JP2010037930A JP2010037930A (en) 2010-02-18
JP2010037930A5 true JP2010037930A5 (en) 2011-09-15
JP4925222B2 JP4925222B2 (en) 2012-04-25

Family

ID=42010757

Family Applications (1)

Application Number Title Priority Date Filing Date
JP2008270757A Active JP4925222B2 (en) 2008-10-21 2008-10-21 Building waterproof sheet, installation method of building waterproof sheet, building construction unit using building waterproof sheet

Country Status (1)

Country Link
JP (1) JP4925222B2 (en)

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ES2916720T3 (en) 2010-02-23 2022-07-05 Asahi Chemical Ind Method for producing diaryl carbonate
JP5981061B1 (en) * 2016-03-28 2016-08-31 株式会社馬場商店 Wing support material having an opening and method of using the same
MX2021000697A (en) * 2018-08-27 2021-03-25 Sika Tech Ag A self-adhering sealing device with an adhesive layer arrangement.
JP2020051142A (en) * 2018-09-27 2020-04-02 日鉄日新製鋼株式会社 Metallic roofing material
PL445277A1 (en) * 2023-06-19 2024-01-03 Uniwersytet Jana Kochanowskiego W Kielcach Innovative, pro-ecological, self-vulcanizing chimney tape

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08284335A (en) * 1995-04-14 1996-10-29 Tajima Inc Sheet for flexible rising section
JP2000006309A (en) * 1998-06-18 2000-01-11 Nitto Denko Corp Waterproof sheet
JP3834497B2 (en) * 2001-09-28 2006-10-18 アサヒゴム株式会社 Waterproof sheet for roof and waterproof construction method using the same
JP3702277B2 (en) * 2003-03-28 2005-10-05 アサヒゴム株式会社 Waterproof sheet for roof and waterproof construction method using the same
JP2007146630A (en) * 2005-10-25 2007-06-14 Baba Shoten:Kk Ridge execution sheet, ridge execution method and ridge execution device

Similar Documents

Publication Publication Date Title
CA2530558C (en) Fastener-free composite roofing product
US8765251B2 (en) Slip resistant roof underlayment
US7765763B2 (en) Pleated roofing membrane and roofing shingle system
US8297020B1 (en) Top down trap lock two-ply shingle system for roofs
CA2587623C (en) Roof underlayment
CA2587995C (en) Pre-assembled hip, ridge or rake shingle
JP4384725B1 (en) Roof waterproof sheet, building waterproof sheet, building waterproof sheet installation method, building construction unit using the building waterproof sheet
US7810296B1 (en) Sheathing assembly and method of sheathing a roofing structure
KR101426881B1 (en) Waterproofing roof shingle structure and, repairing method for preventing the blowing of roof shingle
JP4925222B2 (en) Building waterproof sheet, installation method of building waterproof sheet, building construction unit using building waterproof sheet
EP2466032A1 (en) An insulating member comprising two elements of different material and a method for insulating a window in an inclined roof structure with this insulating member
JP2010037930A5 (en)
JP4925221B2 (en) Wall tarpaulin
US20110173908A1 (en) Method and Apparatus for Reducing Solar Radiation Absorption Through a Roof
US20110000159A1 (en) Hail-resistant roofing membrane and method for making same
JP5284682B2 (en) Shimoya waterproof gasket, seal structure of outer wall joint using the same, and sealing method of outer wall joint
JP6591032B1 (en) Expansion joint structure
US20110059303A1 (en) Roofing Material
CN107237456B (en) Ridge supporting member and its application method with opening portion
CN109779163A (en) A kind of light steel construction waterproof parapet and its construction method
ITVI20110339A1 (en) PHYSICAL-MECHANICAL DEVICE FOR THE ANCHORING OF BITUMINOUS OR SYNTHETIC WATERPROOF STRATIGRAPHS WITH BASIC SUPPORTS
GB2244297A (en) Roof lining system
JP4822827B2 (en) Waterproof wooden roof structure
CN106164391B (en) The small gradient roof structure of lightweight and watertight
US20090013637A1 (en) Roof and Shingle Protector