JP2009265425A - Toner seal member - Google Patents
Toner seal member Download PDFInfo
- Publication number
- JP2009265425A JP2009265425A JP2008116130A JP2008116130A JP2009265425A JP 2009265425 A JP2009265425 A JP 2009265425A JP 2008116130 A JP2008116130 A JP 2008116130A JP 2008116130 A JP2008116130 A JP 2008116130A JP 2009265425 A JP2009265425 A JP 2009265425A
- Authority
- JP
- Japan
- Prior art keywords
- seal member
- urethane
- toner
- toner seal
- urethane foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、トナーシール部材に関する。更に詳しくは、本発明は、特定のウレタンフォーム層及びウレタンフィルム層の積層体からなり、フォーム層とフィルム層の界面剥離強度が高く、長期に渡ってトナーシール性及び摺動性に優れるトナーシール部材に関する。 The present invention relates to a toner seal member. More specifically, the present invention is a toner seal comprising a laminate of a specific urethane foam layer and a urethane film layer, having high interfacial peel strength between the foam layer and the film layer, and excellent in toner sealability and slidability over a long period of time. It relates to members.
各種プリンタ、コピー機、ファクシミリ等に代表される事務機器では、静電記録された静電潜像を現像して可視画像とし、これを熱定着させるトナーが使用されている。このトナーは、微細な粉体であり、事務機器の使用に伴って順次消費される消耗材である。
前記トナーの補給は、例えば、補給用トナーが充填されており、スライド可能な蓋部材を備えるトナーボトル等のトナー容器を、事務機器のトナーホッパー上に装着することにより行われる。
前記蓋部材には、通常、容器に充填されているトナーが漏れないようにするため、トナーシール部材が配設されている。そして、このトナーシール部材には、トナーの外部への漏出を防止する高いシール性が要求されていると共に、トナーを供給する際における前記蓋部材の開閉を容易にし得る摺動性も必要とされており、相反する要素が求められている。更には、これらの特性を長期に渡って維持する耐久性も求められている。
このようなシール部材としては、従来より、ウレタンフォーム等の各種フォームや、ウレタンフォームの一面側にＰＥＴフィルム等が接着された積層体等が開示されている（特許文献１〜３等参照）。
In office equipment typified by various printers, copiers, facsimiles, and the like, toner is used that develops an electrostatically recorded electrostatic latent image into a visible image and thermally fixes it. This toner is a fine powder and is a consumable material that is sequentially consumed as office equipment is used.
The replenishment of the toner is performed, for example, by mounting a toner container such as a toner bottle filled with a replenishing toner and having a slidable lid member on a toner hopper of an office machine.
The lid member is usually provided with a toner seal member so that the toner filled in the container does not leak. The toner seal member is required to have a high sealing property to prevent the toner from leaking to the outside, and also has a sliding property that can easily open and close the lid member when supplying the toner. And conflicting elements are required. Furthermore, the durability which maintains these characteristics over a long period is also calculated | required.
As such a sealing member, conventionally, various foams such as urethane foam, and a laminated body in which a PET film or the like is bonded to one surface side of the urethane foam have been disclosed (see
しかしながら、最近のトナーは粒径が細かくなり（４〜６μｍ）、且つその形状が丸みを帯びていることから流動性が高く、上述の従来のシール部材等では、十分なシール特性が得られない場合が発生している。
具体的には、従来の圧縮性に優れた低密度ウレタンフォーム等からなるシール部材では、フォームの連続気泡に起因する通気性やセル径（通常、４００μｍ以上）により、十分なシール特性が得られない場合がある。
また、ＰＥＴフィルムを摺動面側に備えるウレタンフォームからなるシール部材では、ＰＥＴフィルムが形成されている分、ウレタンフォーム単体からなるシール部材よりも摺動性及びシール特性に優れる。しかしながら、ＰＥＴフィルムはその剛性により柔軟性が乏しいため、シワや折れ等の変形が生じ易く、凹凸形状に対する追従性が低い。そのため、これらの欠点に起因するトナー漏れが生じ、十分なシール特性が得られない場合がある。更には、ＰＥＴフィルムは接着剤等によりフォームに接合されているため、摺動時の圧力や接着層の経時的劣化等によりフィルムの剥離が生じ、長期に渡ってシール特性及び摺動性を維持できないこともある。
そのため、シール性及び摺動性により優れており、且つそれらの特性を長期に渡って維持できるトナーシール部材が求められているのが現状である。
However, recent toners have a small particle size (4 to 6 μm) and are rounded in shape, so that they have high fluidity, and the above-described conventional sealing members cannot provide sufficient sealing characteristics. A case has occurred.
Specifically, with a conventional sealing member made of low-density urethane foam or the like having excellent compressibility, sufficient sealing characteristics can be obtained depending on the air permeability and cell diameter (usually 400 μm or more) due to the open cells of the foam. There may not be.
In addition, a seal member made of urethane foam having a PET film on the sliding surface side is more excellent in slidability and seal characteristics than a seal member made of urethane foam alone because the PET film is formed. However, since the PET film lacks flexibility due to its rigidity, it is likely to be deformed such as wrinkles and folds, and has low followability to the uneven shape. Therefore, toner leakage due to these defects may occur, and sufficient sealing characteristics may not be obtained. Furthermore, since PET film is bonded to the foam with an adhesive or the like, peeling of the film occurs due to pressure during sliding, deterioration of the adhesive layer over time, etc., and the sealing characteristics and slidability are maintained over a long period of time. There are things you can't do.
For this reason, there is a need for a toner seal member that is superior in sealing properties and sliding properties and can maintain these characteristics over a long period of time.
本発明は、前記実情に鑑みてなされたものであり、特定のウレタンフォーム層及びウレタンフィルム層の積層体からなり、フォーム層とフィルム層の界面剥離強度が高く、長期に渡ってトナーシール性及び摺動性に優れるトナーシール部材を提供することを目的とする。 The present invention has been made in view of the above circumstances, and is composed of a laminate of a specific urethane foam layer and a urethane film layer, has a high interfacial peel strength between the foam layer and the film layer, An object of the present invention is to provide a toner seal member having excellent slidability.
本発明は以下の通りである。
［１］ウレタンフォーム層及びウレタンフィルム層の積層体からなるトナーシール部材であって、前記積層体はウレタンフォーム原料をウレタンフィルム上で発泡させることによって形成されており、該積層体の摺動強度は６０Ｎ以下であり、前記ウレタンフォーム層の密度は２００〜４８０ｋｇ／ｍ３であり、セル径は３００μｍ以下であり、厚みは０．５ｍｍ以上であることを特徴とするトナーシール部材。
［２］前記ウレタンフィルム層の伸びが１５０％以上である前記［１］に記載のトナーシール部材。
［３］前記ウレタンフィルム層の厚みが３〜３０μｍである前記［１］又は［２］に記載のトナーシール部材。
［４］前記ウレタンフォーム層の厚みが０．５〜６ｍｍである前記［１］乃至［３］のいずれかに記載のトナーシール部材。
［５］前記ウレタンフォーム層の２５％ＣＬＤ硬度が０．１ＭＰａ以下である前記［１］乃至［４］のいずれかに記載のトナーシール部材。
The present invention is as follows.
[1] A toner seal member comprising a laminate of a urethane foam layer and a urethane film layer, wherein the laminate is formed by foaming a urethane foam raw material on a urethane film, and the sliding strength of the laminate Is a toner seal member, wherein the urethane foam layer has a density of 200 to 480 kg / m 3 , a cell diameter of 300 μm or less, and a thickness of 0.5 mm or more.
[2] The toner seal member according to [1], wherein the urethane film layer has an elongation of 150% or more.
[3] The toner seal member according to [1] or [2], wherein the urethane film layer has a thickness of 3 to 30 μm.
[4] The toner seal member according to any one of [1] to [3], wherein the urethane foam layer has a thickness of 0.5 to 6 mm.
[5] The toner seal member according to any one of [1] to [4], wherein the urethane foam layer has a 25% CLD hardness of 0.1 MPa or less.
本発明のトナーシール部材は、特定のウレタンフォーム層及びウレタンフィルム層の積層体により形成されており、フォーム層とフィルム層との界面剥離強度が高く、十分な摺動性を有しており、且つ長期に渡ってトナーシール特性に優れる。そのため、電子写真画像形成装置、例えば、各種プリンタ、ファクシミリ、複写機等に利用されるトナーボトル、プロセスカートリッジ等におけるトナーシール部材として好適に用いることができる。
また、ウレタンフィルム層の伸びや厚みが特定の範囲である場合には、柔軟性に優れたトナーシール部材となり、トナーシール部材が配設される部材の形状等に対する追随性に優れ、シール特性により優れたトナーシール部材となる。
更に、ウレタンフォーム層の厚みや２５％ＣＬＤ硬度が特定の範囲である場合には、柔軟性に優れたトナーシール部材となり、トナーシール部材が配設される部材の形状等に対する追随性に優れ、シール特性により優れたトナーシール部材となる。
The toner seal member of the present invention is formed by a laminate of a specific urethane foam layer and a urethane film layer, has high interfacial peel strength between the foam layer and the film layer, and has sufficient slidability. In addition, the toner seal characteristics are excellent over a long period of time. Therefore, it can be suitably used as a toner seal member in an electrophotographic image forming apparatus, for example, a toner bottle or a process cartridge used in various printers, facsimiles, copiers and the like.
In addition, when the elongation and thickness of the urethane film layer are within a specific range, the toner seal member is excellent in flexibility, and is excellent in followability to the shape of the member on which the toner seal member is disposed. It becomes an excellent toner seal member.
Furthermore, when the thickness of the urethane foam layer and the 25% CLD hardness are in a specific range, the toner seal member is excellent in flexibility, and has excellent followability to the shape of the member on which the toner seal member is disposed, An excellent toner seal member due to the sealing properties.
以下、本発明を詳細に説明する。
本発明のトナーシール部材は、ウレタンフォーム層及びウレタンフィルム層の積層体からなる。
前記「ウレタンフォーム層」の密度は、２００〜４８０ｋｇ／ｍ３であり、好ましくは２００〜４００ｋｇ／ｍ３、より好ましくは３２０〜４００ｋｇ／ｍ３である。この密度が２００〜４８０ｋｇ／ｍ３である場合には、シール特性及び摺動性に優れるトナーシール部材とすることができる。また、この密度が２００ｋｇ／ｍ３未満の場合には、十分なシール特性が得られないおそれがある。一方、４８０ｋｇ／ｍ３を超える場合には、ウレタンフォーム層の柔軟性が低下して硬くなり、十分な摺動性が得られないおそれがある。
尚、この密度は、ＪＩＳ Ｋ ６４０１に準拠して測定される値である。
Hereinafter, the present invention will be described in detail.
The toner seal member of the present invention comprises a laminate of a urethane foam layer and a urethane film layer.
The density of the “urethane foam layer” is 200 to 480 kg / m 3 , preferably 200 to 400 kg / m 3 , more preferably 320 to 400 kg / m 3 . When the density is 200 to 480 kg / m 3 , a toner seal member having excellent sealing characteristics and slidability can be obtained. Moreover, when this density is less than 200 kg / m 3 , there is a possibility that sufficient sealing characteristics cannot be obtained. On the other hand, when it exceeds 480 kg / m 3 , the flexibility of the urethane foam layer is lowered and hardened, and sufficient slidability may not be obtained.
This density is a value measured in accordance with JIS K 6401.
ウレタンフォーム層のセル径は、３００μｍ以下であり、好ましくは５０〜３００μｍ、より好ましくは５０〜２００μｍ、更に好ましくは５０〜１００μｍである。このセル径が３００μｍ以下である場合には、十分なシール特性を有するトナーシール部材とすることができる。また、このセル径が３００μｍを超える場合には、トナー漏れが生じるおそれがある。
尚、このセル径は、ＳＥＭ写真（電子顕微鏡写真）を用いて測定される値である。
The cell diameter of the urethane foam layer is 300 μm or less, preferably 50 to 300 μm, more preferably 50 to 200 μm, and still more preferably 50 to 100 μm. When the cell diameter is 300 μm or less, a toner seal member having sufficient sealing characteristics can be obtained. If the cell diameter exceeds 300 μm, toner leakage may occur.
In addition, this cell diameter is a value measured using a SEM photograph (electron micrograph).
また、ウレタンフォーム層の厚みは、０．５ｍｍ以上であり、好ましくは０．５〜６ｍｍ、より好ましくは１〜３ｍｍ、更に好ましくは１〜２ｍｍである。この厚みが０．５ｍｍ以上である場合には、十分なシール特性を有するトナーシール部材とすることができる。特に、この厚みが０．５〜６ｍｍである場合には、十分なシール特性を有すると共に、トナーシール部材が配設される部材（被摺動体）の形状等に対する十分な追随性が得られる。尚、この厚みが厚過ぎると、シール部材としての使用時におけるフォーム層の反発力が過度に大きくなり、シール部材が配設される樹脂成形品（トナー容器等）が変形したり、亀裂が生じたりするおそれがある。一方、この厚みが０．５ｍｍ未満の場合には、トナー漏れが生じるおそれがある。 Moreover, the thickness of a urethane foam layer is 0.5 mm or more, Preferably it is 0.5-6 mm, More preferably, it is 1-3 mm, More preferably, it is 1-2 mm. When the thickness is 0.5 mm or more, a toner seal member having sufficient sealing characteristics can be obtained. In particular, when the thickness is 0.5 to 6 mm, it has sufficient sealing characteristics and sufficient followability with respect to the shape of the member (slider) on which the toner seal member is disposed. If this thickness is too thick, the repulsive force of the foam layer when used as a seal member will be excessively large, and the resin molded product (toner container, etc.) on which the seal member is disposed will be deformed or cracked. There is a risk of On the other hand, if this thickness is less than 0.5 mm, toner leakage may occur.
更に、ウレタンフォーム層の２５％ＣＬＤ硬度は、０．１ＭＰａ以下であることが好ましく、より好ましくは０．０１〜０．１ＭＰａ、更に好ましくは０．０１〜０．０５ＭＰａである。この２５％ＣＬＤ硬度が０．１ＭＰａ以下である場合には、シール特性及び摺動性に優れるトナーシール部材とすることができる。
尚、この２５％ＣＬＤ硬度は、ＪＩＳ Ｋ ６２５４に準拠して測定される値である。
Furthermore, the 25% CLD hardness of the urethane foam layer is preferably 0.1 MPa or less, more preferably 0.01 to 0.1 MPa, and still more preferably 0.01 to 0.05 MPa. When the 25% CLD hardness is 0.1 MPa or less, a toner seal member having excellent sealing properties and slidability can be obtained.
The 25% CLD hardness is a value measured according to JIS K 6254.
更に、ウレタンフォーム層の圧縮残留歪は、１０％以下であることが好ましく、より好ましくは０〜５％、更に好ましくは０〜３％である。この圧縮残留歪が１０％以下である場合には、長期に渡ってシール特性に優れるトナーシール部材とすることができる。
尚、この圧縮残留歪は、ＪＩＳ Ｋ ６４０１に準拠して測定される値である。
Furthermore, the compressive residual strain of the urethane foam layer is preferably 10% or less, more preferably 0 to 5%, and still more preferably 0 to 3%. When the compression residual strain is 10% or less, a toner seal member having excellent sealing characteristics over a long period can be obtained.
The compression residual strain is a value measured according to JIS K 6401.
前記「ウレタンフィルム層」の伸びは、１５０％以上であることが好ましく、より好ましくは１５０〜５００％、更に好ましくは２００〜５００％である。この伸びが１５０％以上である場合には、従来の発泡体の一面側にＰＥＴフィルムを備えるシール部材よりも、追随性に優れるトナーシール部材とすることができる。
尚、この伸びは、ＪＩＳ Ｋ ６２５１に準拠して測定される値である。
The elongation of the “urethane film layer” is preferably 150% or more, more preferably 150 to 500%, and still more preferably 200 to 500%. When this elongation is 150% or more, it can be a toner seal member having better followability than a seal member having a PET film on one side of a conventional foam.
This elongation is a value measured according to JIS K 6251.
また、ウレタンフィルム層の厚みは、３μｍ以上であることが好ましく、より好ましくは３〜３０μｍ、更に好ましくは１５〜３０μｍである。この厚みが３μｍ以上である場合には、十分なシール特性、及び十分な追随性を有するトナーシール部材とすることができる。また、この厚みが３０μｍを超える場合には、シール特性の更なる向上が望めず、コスト高となる。 Moreover, it is preferable that the thickness of a urethane film layer is 3 micrometers or more, More preferably, it is 3-30 micrometers, More preferably, it is 15-30 micrometers. When the thickness is 3 μm or more, a toner seal member having sufficient sealing characteristics and sufficient followability can be obtained. On the other hand, if the thickness exceeds 30 μm, further improvement of the sealing characteristics cannot be expected, resulting in high costs.
前記ウレタンフィルム層を構成するウレタンフィルムとしては、市販品等の公知のものを用いることができる。また、このウレタンフィルムは、熱硬化フィルムであってもよいし、熱可塑性フィルムであってもよいが、熱可塑性フィルムである場合には、その融点が１５０℃以上であることが好ましい。 As a urethane film which comprises the said urethane film layer, well-known things, such as a commercial item, can be used. Further, the urethane film may be a thermosetting film or a thermoplastic film, but in the case of a thermoplastic film, the melting point is preferably 150 ° C. or higher.
また、前記ウレタンフォーム層及び前記ウレタンフィルム層からなる前記「積層体」の摺動強度は、６０Ｎ以下であり、好ましくは３０Ｎ以下、より好ましくは１５Ｎ以下である。この摺動強度が６０Ｎ以下である場合には、十分な追随性を有し、摺動性に優れるトナーシール部材とすることができる。
尚、この摺動強度は、後述する実施例に記載の方法により測定される値である。
The sliding strength of the “laminate” composed of the urethane foam layer and the urethane film layer is 60 N or less, preferably 30 N or less, more preferably 15 N or less. When the sliding strength is 60 N or less, a toner seal member having sufficient followability and excellent slidability can be obtained.
In addition, this sliding strength is a value measured by the method as described in the Example mentioned later.
また、本発明のトナーシール部材が、トナー容器の蓋部材等の樹脂成形品におけるトナーシール部材として使用される際には、ウレタンフィルム層側が被摺動体側となり、ウレタンフォーム層側が蓋部材等の基材側となるように配設される。配設の際には、通常、積層体におけるウレタンフォーム層が圧縮されて配設される。その圧縮率は、５０％以下であることが好ましく、より好ましくは２０〜４０％、更に好ましくは２０〜３０％である。この圧縮率が５０％以下である場合には、十分な柔軟性が保たれるため、被摺動体の形状に対する追随性に優れており、且つ圧縮による適度な反発弾性が得られるため、優れたシール性が発揮される。 In addition, when the toner seal member of the present invention is used as a toner seal member in a resin molded product such as a lid member of a toner container, the urethane film layer side is a sliding member side, and the urethane foam layer side is a lid member or the like. It arrange | positions so that it may become a base material side. At the time of arrangement, the urethane foam layer in the laminate is usually compressed and arranged. The compression ratio is preferably 50% or less, more preferably 20 to 40%, and still more preferably 20 to 30%. When the compression ratio is 50% or less, sufficient flexibility is maintained, so that the followability with respect to the shape of the sliding object is excellent, and an appropriate rebound resilience due to compression is obtained. Sealing performance is demonstrated.
また、本発明のトナーシール部材を構成する積層体は、ウレタンフォーム原料をウレタンフィルム上で発泡させることによって一体形成されたものであり、同系成分であるウレタンフォーム層とウレタンフィルム層との界面は強固に接合されている。そのため、発泡体の表面にＰＥＴフィルム等のフィルムを接着剤等により接着して得られる従来のトナーシール部材よりも、表面が平滑であり、界面における剥離強度に優れると共に、接着層の経時的な劣化を懸念する必要がないため、優れたシール性が長期に渡って維持される。更には、粘着剤や接着剤等の使用が不要となるため、加熱の際における希釈溶剤のＶＯＣ（揮発性有機化合物）の発生も懸念する必要がない。 Further, the laminate constituting the toner seal member of the present invention is integrally formed by foaming a urethane foam raw material on a urethane film, and the interface between the urethane foam layer and the urethane film layer, which are similar components, is It is firmly joined. Therefore, the surface is smoother than the conventional toner seal member obtained by adhering a film such as a PET film to the surface of the foam with an adhesive or the like, and has excellent peel strength at the interface. Since there is no need to worry about deterioration, excellent sealing performance is maintained for a long time. Furthermore, since it is not necessary to use a pressure-sensitive adhesive or an adhesive, there is no need to worry about the occurrence of VOC (volatile organic compound) as a diluting solvent during heating.
前記積層体は、例えば、ウレタンフィルム上にウレタンフォーム原料を供給し、発泡させて形成することができる。この際、メカニカルフロス法を用いてウレタンフォーム層を形成することが好ましい。尚、メカニカルフロス法とは、原則として水や発泡剤をフォーム原料に配合せず、フォーム原料に予め、乾燥空気や不活性ガス等の気体を混入させ、機械的に攪拌することにより気液混合されたフォーム原料を用いて発泡層を形成する公知の成形法である。 The laminate can be formed, for example, by supplying a urethane foam raw material onto a urethane film and causing it to foam. At this time, it is preferable to form the urethane foam layer using a mechanical floss method. The mechanical frothing method is basically a method of mixing gas and liquid by not mixing water or foaming agent in the foam raw material, but mixing gas such as dry air or inert gas in the foam raw material in advance and mechanically stirring. This is a known molding method in which a foam layer is formed using the foam raw material.
前記「ウレタンフォーム原料」としては、ポリオール及びイソシアネートを含むものが用いられる。
前記ポリオールとしては、例えば、エーテル系ポリオール、エステル系ポリオール等を用いることができる。
前記エーテル系ポリオールとしては、例えば、エチレングリコール、ジエチレングリコール、プロピレングリコール、ジプロピレングリコール、ブチレングリコール、ネオペンチルグリコール、グリセリン、ペンタエリスリトール、トリメチロールプロパン、ソルビトール、シュークロース等の多価アルコール、又はその多価アルコールにエチレンオキサイド、プロピレンオキサイド等のアルキレンオキサイドを付加したポリエーテルポリオールが挙げられる。
また、前記エステル系ポリオールとしては、例えば、マロン酸、コハク酸、アジピン酸等の脂肪族カルボン酸やフタル酸等の芳香族カルボン酸と、エチレングリコール、ジエチレングリコール、プロピレングリコール等の脂肪族グリコール等とから重縮合して得られるポリエステルポリオールが挙げられる。更には、ε-カプロラクタムの開環重合によって得られるラクトン系ポリエステルポリオールが挙げられる。
これらのポリオールのなかでも、エーテル系ポリオールが好ましい。
尚、これらのポリオールは、１種単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
As the “urethane foam raw material”, those containing polyol and isocyanate are used.
As said polyol, ether type polyol, ester type polyol etc. can be used, for example.
Examples of the ether polyol include polyhydric alcohols such as ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, butylene glycol, neopentyl glycol, glycerin, pentaerythritol, trimethylolpropane, sorbitol, and sucrose, or many of them. Examples include polyether polyols in which alkylene oxides such as ethylene oxide and propylene oxide are added to a monohydric alcohol.
Examples of the ester polyol include aliphatic carboxylic acids such as malonic acid, succinic acid, and adipic acid, aromatic carboxylic acids such as phthalic acid, and aliphatic glycols such as ethylene glycol, diethylene glycol, and propylene glycol. Polyester polyols obtained by polycondensation from Furthermore, a lactone polyester polyol obtained by ring-opening polymerization of ε-caprolactam can be mentioned.
Of these polyols, ether-based polyols are preferable.
In addition, these polyols may be used individually by 1 type, and may be used in combination of 2 or more type.
前記イソシアネートとしては、例えば、トルエンジイソシアネート（ＴＤＩ）、粗ＴＤＩ、４，４’−ジフェニルメタンジイソシアネート（ＭＤＩ）、粗ＭＤＩ、１，６−ヘキサメチレンジイソシアネート（ＨＤＩ）、粗ＨＤＩ、１，５−ナフタレンジイソシアネート、パラフェニレンジイソシアネート、２，２，４−トリメチルヘキサメチレンジイソシアネート、２，４，４−トリメチルヘキサメチレンジイソシアネート、４，４’−ジシクロヘキシルメタンジイソシアネート、ｍ−キシレンジイソシアネート、ヘキサメチレンジイソシアネート、水添ＭＤＩ、イソホロンジイソシアネート等が挙げられる。これらのなかでも、ＭＤＩ、粗ＭＤＩが好ましい。
尚、これらのイソシアネートは１種単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
Examples of the isocyanate include toluene diisocyanate (TDI), crude TDI, 4,4′-diphenylmethane diisocyanate (MDI), crude MDI, 1,6-hexamethylene diisocyanate (HDI), crude HDI, and 1,5-naphthalene diisocyanate. , Paraphenylene diisocyanate, 2,2,4-trimethylhexamethylene diisocyanate, 2,4,4-trimethylhexamethylene diisocyanate, 4,4'-dicyclohexylmethane diisocyanate, m-xylene diisocyanate, hexamethylene diisocyanate, hydrogenated MDI, isophorone Diisocyanate etc. are mentioned. Among these, MDI and crude MDI are preferable.
In addition, these isocyanates may be used individually by 1 type, and may be used in combination of 2 or more type.
イソシアネートの配合量は、ウレタンフォーム層に必要とされる物性等により設定することが好ましい。この配合量はイソシアネートインデックスにより調整され、このイソシアネートインデックスは、８０〜１２０であることが好ましく、より好ましくは９０〜１１０である。イソシアネートインデックスが８０〜１２０である場合には、得られるウレタンフォーム層の圧縮残留歪を十分に低くすること（具体的には、１０％以下にすること）ができるため好ましい。 The blending amount of isocyanate is preferably set according to physical properties required for the urethane foam layer. The blending amount is adjusted by the isocyanate index, and the isocyanate index is preferably 80 to 120, more preferably 90 to 110. When the isocyanate index is 80 to 120, it is preferable because the compression residual strain of the obtained urethane foam layer can be sufficiently lowered (specifically, 10% or less).
前記フォーム原料には、ポリオール及びポリイソシアネートの他、触媒、整泡剤、鎖延長剤等を配合することができる。
前記触媒としては、例えば、金属触媒、アミン系触媒等が挙げられる。
前記金属触媒としては、スタナスオクトエート、ジブチルチンジアセテート、ジブチルチンジラウレート等の有機錫化合物、オクチル酸亜鉛等の有機亜鉛化合物、ニッケルアセチルアセトエート、ニッケルジアセチルアセトエート等の有機ニッケル化合物、鉄アセチルアセトエート等の有機鉄化合物、酢酸ナトリウム等のアルカリ金属又はアルカリ土類金属のアルコキシドやフェノキシド等が挙げられる。
前記アミン系触媒としては、トリエチレンジアミン、テトラメチルグアニジン、Ｎ，Ｎ，Ｎ’Ｎ’−テトラメチルヘキサン−１，６ジアミン等が挙げられる。
これらの触媒は、１種単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
また、触媒の配合量は特に限定されないが、前記ポリオールの全量を１００質量部とした場合に、１〜８質量部であることが好ましく、より好ましくは３〜６質量部である。
In addition to polyol and polyisocyanate, the foam raw material may contain a catalyst, a foam stabilizer, a chain extender and the like.
Examples of the catalyst include a metal catalyst and an amine catalyst.
Examples of the metal catalyst include organic tin compounds such as stannous octoate, dibutyltin diacetate and dibutyltin dilaurate, organic zinc compounds such as zinc octylate, organic nickel compounds such as nickel acetylacetoate and nickel diacetylacetoate, iron acetyl Examples thereof include organic iron compounds such as acetoate, alkali metal or alkaline earth metal alkoxides such as sodium acetate, and phenoxides.
Examples of the amine catalyst include triethylenediamine, tetramethylguanidine, N, N, N′N′-tetramethylhexane-1,6diamine, and the like.
These catalysts may be used individually by 1 type, and may be used in combination of 2 or more type.
Moreover, the compounding quantity of a catalyst is although it does not specifically limit, When the whole quantity of the said polyol is 100 mass parts, it is preferable that it is 1-8 mass parts, More preferably, it is 3-6 mass parts.
前記整泡剤は、均一に分散した微細な気泡を安定化させるために配合されるものである。この整泡剤は特に限定されないが、ジメチルポリシロキサンとポリエーテルのブロック共重合体を使用することができる。また、ポリシロキサンに有機官能基を付加した特殊な整泡剤を用いることもできる。このように、整泡剤としてはシリコーン系整泡剤が用いられることが多い。
この整泡剤は１種単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
また、整泡剤の配合量は特に限定されないが、前記ポリオールの全量を１００質量部とした場合に、２〜８質量部であることが好ましく、より好ましくは３〜５質量部である。
The foam stabilizer is blended to stabilize uniformly dispersed fine bubbles. The foam stabilizer is not particularly limited, but a block copolymer of dimethylpolysiloxane and polyether can be used. A special foam stabilizer in which an organic functional group is added to polysiloxane can also be used. Thus, a silicone type foam stabilizer is often used as the foam stabilizer.
This foam stabilizer may be used individually by 1 type, and may be used in combination of 2 or more type.
Moreover, the compounding quantity of a foam stabilizer is although it does not specifically limit, When the whole quantity of the said polyol is 100 mass parts, it is preferable that it is 2-8 mass parts, More preferably, it is 3-5 mass parts.
前記鎖延長剤としては、例えば、エチレングリコール、ジエチレングリコール、プロピレングリコール、ジプロピレングリコール、１，４−ブタンジオール等の短鎖ジオール系のもの、グリセリン、トリメチロールプロパン等のトリオール系のもの等が挙げられる。
この鎖延長剤は１種単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
また、鎖延長剤の配合量は特に限定されないが、前記ポリオールの全量を１００質量部とした場合に、１〜６質量部であることが好ましく、より好ましくは２〜４質量部である。
Examples of the chain extender include short-chain diols such as ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, and 1,4-butanediol, and triols such as glycerin and trimethylolpropane. It is done.
This chain extender may be used individually by 1 type, and may be used in combination of 2 or more type.
Moreover, the compounding quantity of a chain extension agent is although it does not specifically limit, When the whole quantity of the said polyol is 100 mass parts, it is preferable that it is 1-6 mass parts, More preferably, it is 2-4 mass parts.
尚、フォーム原料には、紫外線吸収剤、酸化防止剤、有機及び無機充填剤、着色剤、顔料、発泡剤、脱水剤、難燃剤等のウレタン配合に一般に使用される各種添加剤を適宜使用することもできる。 For the foam raw material, various additives generally used for urethane blending such as ultraviolet absorbers, antioxidants, organic and inorganic fillers, colorants, pigments, foaming agents, dehydrating agents, flame retardants, etc. are appropriately used. You can also.
以下、実施例を挙げて、本発明の実施の形態を更に具体的に説明する。但し、本発明は、これらの実施例に何ら制約されるものではない。ここで、「部」及び「％」は、特記しない限り質量基準である。 Hereinafter, the embodiment of the present invention will be described more specifically with reference to examples. However, the present invention is not limited to these examples. Here, “part” and “%” are based on mass unless otherwise specified.
［１］使用原料
（１）ポリオール；ポリエーテル系ポリオール（三洋化成社製、商品名「ＧＰ−３０００」、数平均分子量：３０００、官能基数：３、水酸基価：５６ｍｇＫＯＨ／ｍｇ）
（２）イソシアネート；クルードＭＤＩ（日本ポリウレタン社製、商品名「コロネート １１３０」、ＮＣＯ％；３１％）
（３）鎖延長剤；１，４−ブタンジオール
（４）触媒；スタナスオクトエート（城北化学社製）
（５）整泡剤；シリコーン系整泡剤（モメンティブ製、商品名「Ｌ−５６１４」）
（６）増粘剤；水酸化アルミニウム（昭和電工社製、商品名「ハイジライト Ｈ−１０」）
[1] Raw materials used (1) Polyol: Polyether-based polyol (manufactured by Sanyo Chemical Co., Ltd., trade name “GP-3000”, number average molecular weight: 3000, number of functional groups: 3, hydroxyl value: 56 mgKOH / mg)
(2) Isocyanate; Crude MDI (manufactured by Nippon Polyurethane Co., Ltd., trade name “Coronate 1130”, NCO%; 31%)
(3) Chain extender; 1,4-butanediol (4) Catalyst; Stanas octoate (manufactured by Johoku Chemical Co., Ltd.)
(5) Foam stabilizer: Silicone foam stabilizer (product name “L-5614” manufactured by Momentive)
(6) Thickener: Aluminum hydroxide (made by Showa Denko KK, trade name “Hijilite H-10”)
［２］トナーシール部材の製造
（１）実施例１〜１０
ポリオール１００部、鎖延長剤４部、増粘剤２０部、触媒０．１部、及び整泡剤４部の混合物に、イソシアネート及び造泡用気体（窒素ガス、供給量：０．１ｍ３Ｎ／ｍｉｎ）を供給し、混合・剪断することによりウレタンフォーム原料を調製した。尚、前記イソシアネートは、インデックスが９０〜１１０となるように配合した。
次いで、表１に示すウレタンフィルム（厚み：３〜３０μｍ、伸び：２００〜３００％）上に、前記ウレタンフォーム原料を吐出ノズルより供給し、１５０℃に加熱し、フォーム原料を反応、硬化させることにより、表１に示すウレタンフォーム層（厚み：０．５〜７ｍｍ、密度：２００〜４８０ｋｇ／ｍ３、セル径：５０〜３００μｍ、２５％ＣＬＤ硬度：０．０１〜０．１Ｎ、圧縮残留歪：１〜３．５％）と、ウレタンフィルム層とからなる積層体を製造した。その後、所定の寸法（縦５０ｍｍ×横５０ｍｍ）に裁断し、図１に示すように、ウレタンフォーム層２１及びウレタンフィルム層２２の積層体２からなるトナーシール部材１を得た。
尚、このトナーシール部材１においては、ウレタンフィルム層２２側が摺動面側となり、ウレタンフォーム層２１側がトナーボトル等の蓋部材に配設されることになる。
[2] Production of toner seal member (1) Examples 1 to 10
In a mixture of 100 parts polyol, 4 parts chain extender, 20 parts thickener, 0.1 part catalyst, and 4 parts foam stabilizer, isocyanate and foaming gas (nitrogen gas, feed rate: 0.1 m 3 N) / Min) to prepare a urethane foam raw material by mixing and shearing. In addition, the said isocyanate was mix | blended so that an index might be set to 90-110.
Next, the urethane foam raw material is supplied from a discharge nozzle onto a urethane film (thickness: 3 to 30 μm, elongation: 200 to 300%) shown in Table 1 and heated to 150 ° C. to react and cure the foam raw material. The urethane foam layer shown in Table 1 (thickness: 0.5 to 7 mm, density: 200 to 480 kg / m 3 , cell diameter: 50 to 300 μm, 25% CLD hardness: 0.01 to 0.1 N, compression residual strain : 1 to 3.5%) and a laminate comprising a urethane film layer was produced. Then, it cut | judged to the predetermined dimension (50 mm long x 50 mm wide), and obtained the
In the
（２）比較例１、２
実施例１と同様のウレタンフォーム原料を支持体上に吐出ノズルより供給し、１５０℃に加熱してフォーム原料を反応、硬化させることにより、表２に示すウレタンフォーム（厚み：１〜２ｍｍ、密度：２００〜３２０ｋｇ／ｍ３、セル径：１００〜３００μｍ、２５％ＣＬＤ硬度：０．０１〜０．０５Ｎ、圧縮残留歪：１．５〜３％）を製造し、所定の寸法（縦５０ｍｍ×横５０ｍｍ）に裁断して、比較例１及び２の各トナーシール部材を製造した。
(2) Comparative Examples 1 and 2
The same urethane foam raw material as in Example 1 was supplied onto the support from the discharge nozzle and heated to 150 ° C. to react and cure the foam raw material, whereby the urethane foam shown in Table 2 (thickness: 1 to 2 mm, density) : 200 to 320 kg / m 3 , cell diameter: 100 to 300 μm, 25% CLD hardness: 0.01 to 0.05 N, compression residual strain: 1.5 to 3%) are manufactured, and predetermined dimensions (length 50 mm × Each toner seal member of Comparative Examples 1 and 2 was manufactured by cutting into 50 mm in width.
（３）比較例３〜７
実施例１と同様のウレタンフォーム原料を支持体上に吐出ノズルより供給し、１５０℃に加熱してフォーム原料を反応、硬化させることにより、表２に示すウレタンフォーム（厚み：０．４〜２ｍｍ、密度：１５０〜５００ｋｇ／ｍ３、セル径：５０〜４００μｍ、２５％ＣＬＤ硬度：０．０１〜０．１１Ｎ、圧縮残留歪：１〜４％）を製造した。
次いで、得られたウレタンフォーム層の一表面に、表２に示すフィルム（種類：ウレタン又はＰＥＴ、厚み：３〜２５μｍ、伸び：１４０〜３００％）を、アクリル系粘着剤により接着し、ウレタンフォーム層とウレタンフィルム層とからなる積層体を製造し、所定の寸法（縦５０ｍｍ×横５０ｍｍ）に裁断して、比較例３〜７の各トナーシール部材を得た。
(3) Comparative Examples 3-7
The same urethane foam raw material as in Example 1 was supplied onto the support from the discharge nozzle and heated to 150 ° C. to react and cure the foam raw material, whereby the urethane foam shown in Table 2 (thickness: 0.4 to 2 mm) , Density: 150 to 500 kg / m 3 , cell diameter: 50 to 400 μm, 25% CLD hardness: 0.01 to 0.11 N, compression residual strain: 1 to 4%).
Next, a film (type: urethane or PET, thickness: 3 to 25 μm, elongation: 140 to 300%) shown in Table 2 was adhered to one surface of the obtained urethane foam layer with an acrylic pressure-sensitive adhesive. A laminate composed of a layer and a urethane film layer was manufactured and cut into a predetermined size (50 mm long × 50 mm wide) to obtain toner seal members of Comparative Examples 3 to 7.
［３］評価
下記に示す方法により各種評価試験を行った。その結果を表３及び表４に示す。
（１）摺動強度
まず、実施例及び比較例の各トナーシール部材から、縦３０ｍｍ×横３０ｍｍの試験片を作製した。次いで、図２及び図３に示す摺動強度測定器３において、スライド可能なガイド３５上に固定された被摺動体（ＡＢＳ樹脂板）３１とブリッジ部３２との間に、試験片１０が初期厚みに対し４０％の圧縮率（スペーサ３３及び締付部材３４にて調節可能）となり且つ両面テープによりブリッジ部３２側に固定されるように配置した（図２参照）。尚、この際、試験片１０は、ウレタンフィルム側が被摺動体３１側となり、ウレタンフォーム側がブリッジ部３２側となるように配置した。
そして、３分間放置した後、ガイド３５の先端に配設されたワイヤー３６を引張試験機にて、前記被摺動体３１をガイド３５ごと、引張速度２００ｍｍ／ｍｉｎで動かし（図３参照）、ガイド３５が移動し始める際に必要な力から引張強度を求め、この引張強度を摺動強度（Ｎ）とした。
[3] Evaluation Various evaluation tests were performed by the following methods. The results are shown in Tables 3 and 4.
(1) Sliding Strength First, a test piece of 30 mm length × 30 mm width was prepared from the toner seal members of Examples and Comparative Examples. Next, in the sliding
Then, after being left for 3 minutes, the wire 36 arranged at the tip of the
（２）トナーシール性
まず、図４に示すように、支持体４（厚み：２ｍｍ）上に、実施例及び比較例の各トナーシール部材を接合し、縦５０ｍｍ×横５０ｍｍの試験片１００を作製した。尚、実施例及び比較例３〜７においては、トナーシール部材を構成する積層体２のウレタンフォーム層２１側に支持体４を形成し、ウレタンフォーム層のみから構成される比較例１及び２においては、いずれか一方の面に支持体４を形成した。
次いで、図４及び５に示すように、トナーボトル５における凹凸のある開口部５１（被摺動面）に対して、試験片１００における支持体４が形成されていない側を押しつけた状態で固定した。この際、ウレタンフォーム層の圧縮率が約２５％となるように固定した。尚、前記開口部５１の凹凸部における最頂部と最底部との最大差は、１００μｍ程度である。
その後、トナーシール部材が固定された状態で、周波数１００Ｈｚにて１００回上下に震動させて、トナー漏れの有無を確認し、トナーシール性を評価した。尚、評価基準は以下の通りである。
良好：トナー漏れ無し
不良：トナー漏れ有り
(2) Toner Sealing Property First, as shown in FIG. 4, the toner seal members of Examples and Comparative Examples are joined on a support 4 (thickness: 2 mm), and a
Next, as shown in FIGS. 4 and 5, the
Thereafter, the toner seal member was fixed, and was shaken up and down 100 times at a frequency of 100 Hz to check for toner leakage and to evaluate toner sealability. The evaluation criteria are as follows.
Good: No toner leakage Bad: Toner leakage
（３）追随性
前記（２）と同様の評価試験を行い、試験片１００と凹凸のある開口部５１（被摺動面）の界面からのトナー漏れの有無を確認し、追随性を評価した。尚、評価基準は以下の通りである。
良好：試験片１００が開口部５１の凹凸に対して十分に追従し、界面からのトナー漏れが無かった場合
不良：試験片１００が開口部５１の凹凸に対して十分に追従せず、界面からのトナー漏れが有った場合
(3) Followability The same evaluation test as in (2) above was performed, and the presence or absence of toner leakage from the interface between the
Good: When the
（４）界面剥離強度
ＪＩＳ Ｚ ０２３７における１８０°剥離試験に準拠して界面剥離強度を評価した。尚、評価基準は以下の通りである。
良好：フォーム層からフィルム層が剥離せず、フォーム層が破壊された場合
不良：フォーム層からフィルム層が剥離した場合
(4) Interfacial peel strength Interfacial peel strength was evaluated based on a 180 ° peel test in JIS Z 0237. The evaluation criteria are as follows.
Good: When the film layer does not peel off from the foam layer and the foam layer is destroyed. Bad: When the film layer peels off from the foam layer
（５）総合評価
前記（１）〜（４）の結果、及び、積層体を構成するウレタンフォーム層やウレタンフィルム層等の物性を考慮し、トナーシール部材としての使用感が非常に良好な場合を「◎」とし、使用感が良好な場合を「○」とし、使用に問題がある場合を「×」とした。
(5) Comprehensive evaluation In consideration of the results of (1) to (4) and the physical properties of the urethane foam layer and the urethane film layer constituting the laminate, the usability as a toner seal member is very good. Was marked with “◎”, when the feeling of use was good, “◯”, and when there was a problem in use, “x”.
表３に示すように、特定のウレタンフォーム層とウレタンフィルム層の積層体からなる実施例１〜１０の各トナーシール部材においては、摺動強度が１５〜６０Ｎと十分な摺動性を有しており、且つトナーシール性、追随性及び界面剥離強度が全て良好であり、総合評価は、全て「◎」及び「○」であった。
尚、実施例９の総合評価が「○」である理由は、ウレタンフォーム層の厚みが７ｍｍと少し厚く、トナーシール部材として使用する際のウレタンフォーム層の圧縮率によっては、反発弾性が大きくなりすぎる場合があるからである。
As shown in Table 3, each of the toner seal members of Examples 1 to 10 composed of a laminate of a specific urethane foam layer and a urethane film layer has a sufficient sliding property with a sliding strength of 15 to 60 N. In addition, the toner sealability, followability and interfacial peel strength were all good, and the overall evaluations were all “及 び” and “○”.
The reason why the overall evaluation of Example 9 is “◯” is that the thickness of the urethane foam layer is 7 mm, which is a little thick, and depending on the compressibility of the urethane foam layer when used as a toner seal member, the resilience becomes large. This is because it may be too much.
一方、表４に示すように、比較例１及び２のフィルム層が形成されていないウレタンフォーム層のみからなるトナーシール部材においては、摺動強度が４０Ｎであり且つ追随性は良好であったが、トナーシール性が不良であり、総合評価は共に「×」であった。
また、比較例３及び４のウレタンフォーム層にＰＥＴフィルム層が接合されたトナーシール部材においては、摺動強度が１５〜３０Ｎと十分な摺動性を有していたが、追随性が不良であり、その結果としてトナー漏れが生じるためトナーシール性も不良であり、総合評価は共に「×」であった。
更に、比較例５のウレタンフォーム層にウレタンフィルム層が接合されたトナーシール部材においては、トナーシール性及び追随性は良好であったが、摺動強度が６５Ｎと高いため摺動性が悪く、総合評価は「×」であった。
また、比較例６及び７のウレタンフォーム層にウレタンフィルム層が接合されたトナーシール部材においては、追随性は良好であったが、トナーシール性が不良であり、総合評価は共に「×」であった。
更に、比較例３〜７においては、フィルム層がウレタンフォーム層に粘着剤により接合されているため、ウレタンフィルム上でフォーム原料を発泡させることによってウレタンフォーム層が形成されている実施例よりも界面剥離強度が劣っていた。
On the other hand, as shown in Table 4, in the toner seal member consisting only of the urethane foam layer in which the film layers of Comparative Examples 1 and 2 were not formed, the sliding strength was 40 N and the followability was good. The toner sealability was poor, and the overall evaluation was “x”.
Further, the toner seal member in which the PET film layer was bonded to the urethane foam layers of Comparative Examples 3 and 4 had sufficient sliding properties with a sliding strength of 15 to 30 N, but the followability was poor. As a result, toner leakage occurs, resulting in poor toner sealability. The overall evaluation was “x”.
Furthermore, in the toner seal member in which the urethane film layer was bonded to the urethane foam layer of Comparative Example 5, the toner sealability and followability were good, but the slide strength was as high as 65 N, so the slidability was bad. The overall evaluation was “x”.
Further, in the toner seal member in which the urethane film layer was bonded to the urethane foam layer of Comparative Examples 6 and 7, the followability was good, but the toner sealability was poor, and the overall evaluation was “x”. there were.
Furthermore, in Comparative Examples 3 to 7, since the film layer is bonded to the urethane foam layer with an adhesive, the interface is more than the example in which the urethane foam layer is formed by foaming the foam raw material on the urethane film. The peel strength was inferior.
以上のように、本実施例の各トナーシール部材は、フォーム層とフィルム層の界面剥離強度が高く、長期に渡ってトナーシール性及び摺動性に優れることが分かった。 As described above, it was found that each toner seal member of this example has a high interfacial peel strength between the foam layer and the film layer and is excellent in toner sealability and slidability over a long period of time.
１；トナーシール部材、２；積層体、２１；ウレタンフォーム層、２２；ウレタンフィルム層、３；摺動強度測定装置、３１；被摺動体、３２；ブリッジ部、３３；スペーサ、３４；締付部材、３５；ガイド、３６；ワイヤー、４；支持体、５；トナーボトル、５１；開口部、１０、１００；試験片。
DESCRIPTION OF
Claims (5)
前記積層体はウレタンフォーム原料をウレタンフィルム上で発泡させることによって形成されており、該積層体の摺動強度は６０Ｎ以下であり、
前記ウレタンフォーム層の密度は２００〜４８０ｋｇ／ｍ３であり、セル径は３００μｍ以下であり、厚みは０．５ｍｍ以上であることを特徴とするトナーシール部材。 A toner seal member comprising a laminate of a urethane foam layer and a urethane film layer,
The laminate is formed by foaming a urethane foam raw material on a urethane film, and the sliding strength of the laminate is 60 N or less,
A density of the urethane foam layer is 200 to 480 kg / m 3 , a cell diameter is 300 μm or less, and a thickness is 0.5 mm or more.