JP2009164539A - Electret structure, its forming method and electret type capacitance sensor - Google Patents

Electret structure, its forming method and electret type capacitance sensor Download PDF

Info

Publication number
JP2009164539A
JP2009164539A JP2008003314A JP2008003314A JP2009164539A JP 2009164539 A JP2009164539 A JP 2009164539A JP 2008003314 A JP2008003314 A JP 2008003314A JP 2008003314 A JP2008003314 A JP 2008003314A JP 2009164539 A JP2009164539 A JP 2009164539A
Authority
JP
Japan
Prior art keywords
electret
silicon
substrate
inorganic
recess
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2008003314A
Other languages
Japanese (ja)
Other versions
JP5240900B2 (en
Inventor
Yoshinori Iguchi
義則 井口
Toshifumi Tajima
利文 田島
Masahide Goto
正英 後藤
Isanaga Yasuno
功修 安野
Kenichi Kidokoro
賢一 樹所
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rion Co Ltd
Kobayashi Institute of Physical Research
Japan Broadcasting Corp
Original Assignee
Nippon Hoso Kyokai NHK
Rion Co Ltd
Kobayashi Institute of Physical Research
Japan Broadcasting Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Hoso Kyokai NHK, Rion Co Ltd, Kobayashi Institute of Physical Research, Japan Broadcasting Corp filed Critical Nippon Hoso Kyokai NHK
Priority to JP2008003314A priority Critical patent/JP5240900B2/en
Publication of JP2009164539A publication Critical patent/JP2009164539A/en
Application granted granted Critical
Publication of JP5240900B2 publication Critical patent/JP5240900B2/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To provide an electret structure surely securing the moisture resistance regardless of the thickness of an inorganic electret member, and also to provide its forming method, and an electret type capacitance sensor. <P>SOLUTION: A silicon microphone 100 has a back surface electrode substrate 200, a movable electrode substrate 300 disposed facing the back surface electrode substrate 200, and an insulator 400 provided between the back surface electrode substrate 200 and the movable electrode substrate 300. The back surface electrode substrate 200 has: a silicon substrate 201; a through-hole 204 formed on the silicon substrate 201; a silicon oxide film 202 embedded in a recessed part patterned and formed so as to evade the through-hole 204; a silicon nitride film 203 formed so as to cover the surface of the silicon substrate 201 and the silicon oxide film 202; and an electrode 205. <P>COPYRIGHT: (C)2009,JPO&INPIT

Description

本発明は、半導体を用いて形成されるエレクトレット構造及びその形成方法並びにエレクトレット型静電容量センサに関する。   The present invention relates to an electret structure formed using a semiconductor, a method for forming the same, and an electret capacitive sensor.

従来、シリコン等の無機材料を用いて半導体微細加工技術によって製作されるシリコンマイクロホン、圧力センサ、加速度センサ等の半導体静電容量型センサが実用化されている。これらのセンサは、圧力や加速度等の物理量を受けて変位する可動電極と対向電極とを含み、両電極間に一定の電荷を蓄積させた状態で動作する。圧力等の物理量を受けて可動電極が変位すると、可動電極と対向電極との距離が変わることで、両電極間の静電容量が変化する。両電極間に蓄積された電荷は一定に保たれているため、静電容量変化は両電極間の電圧変化として検出される。   Conventionally, semiconductor capacitive sensors such as silicon microphones, pressure sensors, and acceleration sensors manufactured by semiconductor microfabrication technology using inorganic materials such as silicon have been put into practical use. These sensors include a movable electrode and a counter electrode that are displaced by receiving physical quantities such as pressure and acceleration, and operate in a state in which a constant charge is accumulated between both electrodes. When the movable electrode is displaced in response to a physical quantity such as pressure, the capacitance between the two electrodes is changed by changing the distance between the movable electrode and the counter electrode. Since the electric charge accumulated between both electrodes is kept constant, a change in capacitance is detected as a voltage change between both electrodes.

このような半導体静電容量型センサでは、従来、電荷を蓄積させるために両電極間に外部からバイアス電圧を印加する方式が主流であったが、近年では酸化シリコン等、半導体微細加工技術で加工可能な無機エレクトレット部材を組み込み、これに電荷を蓄積させる構造のセンサが発表されている。これらエレクトレット型のセンサは外部からのバイアス電圧が不要であるため、センサ全体の小型化や簡素化が可能となる等の利点を有する。   Conventionally, in such a semiconductor capacitance type sensor, a method of applying a bias voltage from the outside between both electrodes in order to accumulate electric charge has been the mainstream, but in recent years, it has been processed by semiconductor fine processing technology such as silicon oxide. A sensor having a structure in which a chargeable inorganic electret member is incorporated and electric charge is accumulated therein has been announced. Since these electret type sensors do not require an external bias voltage, they have advantages such as miniaturization and simplification of the entire sensor.

ところで、酸化シリコン等の半導体微細加工技術で加工可能な無機エレクトレット部材には、湿度の影響により蓄積された電荷が放電してしまうという問題がある。このため、無機エレクトレット部材(例えばシリコン酸化膜)が直接外気(湿気)に触れないように、窒化シリコン等の保護膜で覆うことが一般的である。その際、無機エレクトレット部材の側面を保護膜で覆いやすくする、すなわち、ステップカバレッジ(Step Coverage:段差被覆性)を改善するために、無機エレクトレット部材の上端部を丸く形成することが提案されている(例えば、特許文献1参照)。   By the way, an inorganic electret member that can be processed by a semiconductor microfabrication technique such as silicon oxide has a problem that the accumulated charges are discharged due to the influence of humidity. For this reason, it is common to cover an inorganic electret member (for example, a silicon oxide film) with a protective film such as silicon nitride so as not to directly touch the outside air (humidity). At that time, in order to easily cover the side surface of the inorganic electret member with a protective film, that is, in order to improve step coverage (step coverage), it is proposed to form the upper end portion of the inorganic electret member in a round shape. (For example, refer to Patent Document 1).

特許文献1に開示された従来のエレクトレット構造を図7に示す。図7に示すように、従来のものは、絶縁膜1上に無機エレクトレット部材であるシリコン酸化膜2が形成されている。また、このシリコン酸化膜2を覆うように絶縁膜3が形成されている。特許文献1によれば、シリコン酸化膜2の上端部2aを図示のように丸く形成することで絶縁膜3のステップカバレッジを改善し、シリコン酸化膜2に対する耐湿性を高くすることができるとしている。   A conventional electret structure disclosed in Patent Document 1 is shown in FIG. As shown in FIG. 7, in the conventional one, a silicon oxide film 2 that is an inorganic electret member is formed on an insulating film 1. An insulating film 3 is formed so as to cover the silicon oxide film 2. According to Patent Document 1, the step coverage of the insulating film 3 is improved by forming the upper end portion 2a of the silicon oxide film 2 in a round shape as shown in the figure, and the moisture resistance against the silicon oxide film 2 can be increased. .

ところで、シリコン酸化膜の厚さを厚くすることによりシリコン酸化膜に蓄積される電荷による蓄積電圧を大きくすることが可能であることが知られている(例えば、非特許文献1参照)。非特許文献1には、シリコン酸化膜を保護するシリコン窒化膜の厚さ100nmに対して、シリコン酸化膜の厚さを500nmから600nmに厚くするに従い、蓄積電圧が高くなることが記載されている。そこで、蓄積電圧を高めるため、実用上はシリコン窒化膜の数倍の厚さのシリコン酸化膜が用いられることがある。
特開2006−245398号公報 V. Leonov 他, "Stabilization of positive charge in SiO2/Si3N4 electrets", IEEE Transactions on Dielectric and Electrical Insulation誌, vol.13, No.5, pp.1049-1056, October 2006.
By the way, it is known that by increasing the thickness of the silicon oxide film, it is possible to increase the accumulated voltage due to the charges accumulated in the silicon oxide film (see, for example, Non-Patent Document 1). Non-Patent Document 1 describes that the storage voltage increases as the thickness of the silicon oxide film is increased from 500 nm to 600 nm with respect to the thickness of the silicon nitride film protecting the silicon oxide film of 100 nm. . Therefore, in order to increase the storage voltage, a silicon oxide film several times thicker than the silicon nitride film may be used in practice.
JP 2006-245398 A V. Leonov et al., "Stabilization of positive charge in SiO2 / Si3N4 electrets", IEEE Transactions on Dielectric and Electrical Insulation, vol.13, No.5, pp.1049-1056, October 2006.

しかしながら、特許文献1に示された従来のエレクトレット構造では、図7に示すように、無機エレクトレット部材であるシリコン酸化膜2の側面2bが絶縁膜1に対して垂直となっているので、ステップカバレッジの改善が限定的であり、特に、蓄積電圧を高めるためにシリコン酸化膜の厚さを厚くしようとするとステップカバレッジの改善効果が期待できず、シリコン酸化膜に対する耐湿性が確保できないという課題があった。   However, in the conventional electret structure shown in Patent Document 1, the side surface 2b of the silicon oxide film 2 that is an inorganic electret member is perpendicular to the insulating film 1 as shown in FIG. In particular, there is a problem that if the thickness of the silicon oxide film is increased in order to increase the storage voltage, the effect of improving the step coverage cannot be expected and the moisture resistance against the silicon oxide film cannot be ensured. It was.

本発明は、従来の課題を解決するためになされたものであり、無機エレクトレット部材の厚さに関わらず、その耐湿性を確実に確保することができるエレクトレット構造及びその形成方法並びにエレクトレット型静電容量センサを提供することを目的とする。   The present invention has been made in order to solve the conventional problems, and an electret structure that can reliably ensure moisture resistance regardless of the thickness of the inorganic electret member, a method for forming the same, and an electret electrostatic An object is to provide a capacitive sensor.

本発明のエレクトレット構造は、凹部が形成された第1の面及び該第1の面とは反対側の第2の面を有するシリコン基板と、前記凹部の底面から前記第1の面の位置までの前記凹部内に埋め込まれた無機エレクトレット部材と、前記第1の面及び前記無機エレクトレット部材の表面を保護する保護膜と、前記第2の面上に形成された電極とを備えた構成を有している。   The electret structure of the present invention includes a silicon substrate having a first surface on which a recess is formed and a second surface opposite to the first surface, and from the bottom surface of the recess to the position of the first surface. And an inorganic electret member embedded in the recess, a protective film for protecting the first surface and the surface of the inorganic electret member, and an electrode formed on the second surface. is doing.

この構成により、本発明のエレクトレット構造は、無機エレクトレット部材が、保護膜によって外気に触れないよう保護されるので、無機エレクトレット部材の厚さに関わらず、その耐湿性を確実に確保することができる。   With this configuration, the electret structure of the present invention is protected so that the inorganic electret member is not exposed to the outside air by the protective film, so that the moisture resistance can be reliably ensured regardless of the thickness of the inorganic electret member. .

また、本発明のエレクトレット構造は、凹部が形成された第1の面及び該第1の面とは反対側の第2の面を有するシリコン基板と、前記凹部の底面から前記第1の面の位置を超える予め定めた位置まで埋め込まれた無機エレクトレット部材と、前記第1の面及び前記無機エレクトレット部材の表面を保護する保護膜と、前記第2の面上に形成された電極とを備え、前記無機エレクトレット部材は、前記シリコン基板の厚さ方向において前記凹部の開口の中央から端に向かって次第に薄くなるようバーズビーク状に形成されている構成を有している。   Further, the electret structure of the present invention includes a silicon substrate having a first surface on which a recess is formed and a second surface opposite to the first surface, and a bottom surface of the recess from the first surface. An inorganic electret member embedded up to a predetermined position exceeding the position, a protective film protecting the surface of the first surface and the inorganic electret member, and an electrode formed on the second surface, The inorganic electret member has a configuration in which it is formed in a bird's beak shape so as to gradually become thinner from the center to the end of the opening of the recess in the thickness direction of the silicon substrate.

この構成により、本発明のエレクトレット構造は、無機エレクトレット部材が、バーズビーク状の形状を含む保護膜によって外気に触れないよう保護されるので、無機エレクトレット部材の厚さに関わらず、その耐湿性を確実に確保することができる。   With this configuration, the electret structure of the present invention protects the inorganic electret member from being exposed to the outside air by a protective film including a bird's beak-like shape, thus ensuring its moisture resistance regardless of the thickness of the inorganic electret member. Can be secured.

また、このバーズビーク状のエレクトレット構造の場合には、従来からあるバーズビーク状半導体部品の製造ラインを利用することができる。   Further, in the case of this bird's beak-like electret structure, a conventional production line for bird's beak-like semiconductor components can be used.

さらに、本発明のエレクトレット構造は、前記凹部の開口が設けられた前記第1の面上の領域とは異なる領域から前記第2の面に貫通する少なくとも1つの貫通孔を備えた構成を有している。   Furthermore, the electret structure of the present invention has a configuration including at least one through-hole penetrating from the region different from the region on the first surface where the opening of the concave portion is provided to the second surface. ing.

この構成により、本発明のエレクトレット構造は、無機エレクトレット部材の耐湿性を確実に確保するとともに、第1の面側から印加圧力(空気の振動)が加わった場合でも、貫通孔を通して空気を逃がすことができ、エレクトレット構造が変位しないようにできる。   With this configuration, the electret structure of the present invention reliably ensures the moisture resistance of the inorganic electret member and allows air to escape through the through-hole even when applied pressure (air vibration) is applied from the first surface side. It is possible to prevent the electret structure from being displaced.

本発明のエレクトレット型静電容量センサは、エレクトレット構造を有する背面電極基板と、該背面電極基板に対向配置され印加圧力に応じて変位する可動電極基板とを備えた構成を有している。   The electret capacitive sensor of the present invention has a configuration including a back electrode substrate having an electret structure and a movable electrode substrate that is disposed opposite to the back electrode substrate and is displaced according to an applied pressure.

この構成により、本発明のエレクトレット型静電容量センサは、背面電極基板の無機エレクトレット部材が、保護膜によって外気に触れないよう保護されるので、無機エレクトレット部材の厚さに関わらず、その耐湿性を確実に確保することができる。   With this configuration, the electret capacitive sensor of the present invention protects the inorganic electret member of the back electrode substrate from being exposed to the outside air by the protective film. Can be ensured.

本発明のエレクトレット構造の形成方法は、第1の面及び該第1の面とは反対側の第2の面を有するシリコン基板に無機エレクトレット部材を形成するエレクトレット構造の形成方法であって、前記シリコン基板の前記第1の面に凹部を形成する工程と、前記無機エレクトレット部材を前記凹部に形成する工程と、前記第1の面と前記無機エレクトレット部材の表面とを平坦化する工程と、平坦化した第1の面及び無機エレクトレット部材の表面に保護膜を形成する工程と、前記第2の面上に電極を形成する工程とを含む構成を有している。   The electret structure forming method of the present invention is an electret structure forming method of forming an inorganic electret member on a silicon substrate having a first surface and a second surface opposite to the first surface, Forming a recess in the first surface of the silicon substrate, forming the inorganic electret member in the recess, flattening the first surface and the surface of the inorganic electret member, and flattening The method includes a step of forming a protective film on the first surface and the surface of the inorganic electret member, and a step of forming an electrode on the second surface.

この構成により、本発明のエレクトレット構造の形成方法は、無機エレクトレット部材が、保護膜によって外気に触れないよう保護されるので、無機エレクトレット部材の厚さに関わらず、その耐湿性を確実に確保することができる。   With this configuration, the method of forming the electret structure of the present invention protects the inorganic electret member from being exposed to the outside air by the protective film, so that the moisture resistance is surely ensured regardless of the thickness of the inorganic electret member. be able to.

本発明は、無機エレクトレット部材の厚さに関わらず、その耐湿性を確実に確保することができるという効果を有するエレクトレット構造及びその形成方法並びにエレクトレット型静電容量センサを提供することができるものである。   The present invention can provide an electret structure having an effect that the moisture resistance can be reliably ensured regardless of the thickness of the inorganic electret member, a method of forming the electret structure, and an electret-type capacitance sensor. is there.

以下、本発明の実施の形態について図面を用いて説明する。なお、本発明のエレクトレット型静電容量センサをシリコンマイクロホンに適用する例を挙げて説明する。   Hereinafter, embodiments of the present invention will be described with reference to the drawings. An example in which the electret capacitive sensor of the present invention is applied to a silicon microphone will be described.

(第1の実施の形態)
まず、本実施の形態におけるシリコンマイクロホンの構成について図1を用いて説明する。図1は、本実施の形態におけるシリコンマイクロホンの構成を概念的に示す断面概念図である。
(First embodiment)
First, the structure of the silicon microphone in this embodiment will be described with reference to FIG. FIG. 1 is a conceptual cross-sectional view conceptually showing the configuration of the silicon microphone in the present embodiment.

図1に示すように、本実施の形態におけるシリコンマイクロホン100は、無機エレクトレット部材を含む背面電極基板200と、背面電極基板200と対向配置された可動電極基板300と、背面電極基板200と可動電極基板300との間に設けられた絶縁体400とを備えている。   As shown in FIG. 1, a silicon microphone 100 according to the present embodiment includes a back electrode substrate 200 including an inorganic electret member, a movable electrode substrate 300 disposed opposite to the back electrode substrate 200, the back electrode substrate 200, and the movable electrode. And an insulator 400 provided between the substrate 300 and the substrate 300.

背面電極基板200は、シリコン基板201と、シリコン酸化膜202と、シリコン窒化膜203と、貫通孔204と、外部回路(図示省略)に接続される電極205とを備えている。なお、背面電極基板200の詳細な構成については後述する。また、以下の説明において、シリコン窒化膜203がある側を「表面」、電極205がある側を「裏面」という。   The back electrode substrate 200 includes a silicon substrate 201, a silicon oxide film 202, a silicon nitride film 203, a through hole 204, and an electrode 205 connected to an external circuit (not shown). The detailed configuration of the back electrode substrate 200 will be described later. In the following description, the side having the silicon nitride film 203 is referred to as “front surface”, and the side having the electrode 205 is referred to as “back surface”.

可動電極基板300は、シリコン基板301と、シリコン基板301に形成された可動電極膜302と、可動電極膜302上に形成された接続用端子303とを備えている。   The movable electrode substrate 300 includes a silicon substrate 301, a movable electrode film 302 formed on the silicon substrate 301, and a connection terminal 303 formed on the movable electrode film 302.

可動電極膜302は、例えば不純物をドープしたシリコンからなる導電性の薄膜で構成され、音波による音圧変化に応じて変位するようになっている。   The movable electrode film 302 is made of a conductive thin film made of silicon doped with impurities, for example, and is displaced according to a change in sound pressure due to sound waves.

接続用端子303は、例えばアルミニウム膜で構成され、電極205と同様に外部回路に接続されるものである。   The connection terminal 303 is made of, for example, an aluminum film, and is connected to an external circuit like the electrode 205.

絶縁体400は、例えばガラスやセラミックスで構成され、背面電極基板200と可動電極基板300との間隔を所定の寸法に保持するようになっている。   The insulator 400 is made of, for example, glass or ceramics, and holds the gap between the back electrode substrate 200 and the movable electrode substrate 300 at a predetermined dimension.

前述のように構成されたシリコンマイクロホン100は、音波に応じて可動電極膜302が変位することにより背面電極基板200と可動電極基板300との間の静電容量が変化し、電荷が一定であることから電極205及び303に接続された外部回路においてこの静電容量の変化が電圧の変化として検出され、音波が電気信号に変換されるようになっている。   In the silicon microphone 100 configured as described above, the capacitance between the back electrode substrate 200 and the movable electrode substrate 300 changes due to the displacement of the movable electrode film 302 according to the sound wave, and the charge is constant. Therefore, in the external circuit connected to the electrodes 205 and 303, this change in capacitance is detected as a change in voltage, and sound waves are converted into electric signals.

次に、背面電極基板200の詳細な構成について図2を用いて説明する。図2(a)は、本実施の形態における背面電極基板200の断面概念図、図2(b)は、背面電極基板200の平面概念図である。なお、図2(a)は、図2(b)に示すA−A断面における断面概念図であり、図2(b)は、図2(a)に示すB方向から見た平面概念図である。   Next, a detailed configuration of the back electrode substrate 200 will be described with reference to FIG. 2A is a conceptual cross-sectional view of the back electrode substrate 200 in the present embodiment, and FIG. 2B is a conceptual plan view of the back electrode substrate 200. 2A is a conceptual cross-sectional view taken along the line AA shown in FIG. 2B, and FIG. 2B is a conceptual plan view seen from the direction B shown in FIG. 2A. is there.

図2に示すように、本実施の形態における背面電極基板200は、シリコン基板201と、無機エレクトレット部材であるシリコン酸化膜202と、保護膜としてのシリコン窒化膜203と、貫通孔204と、電極205とを備えている。   As shown in FIG. 2, the back electrode substrate 200 in this embodiment includes a silicon substrate 201, a silicon oxide film 202 that is an inorganic electret member, a silicon nitride film 203 as a protective film, a through hole 204, an electrode 205.

シリコン基板201には、貫通孔204を避けるようパターニングされて形成された凹部201aが設けられ、凹部201aには側面201bが形成されている。無機エレクトレット部材であるシリコン酸化膜202は、この凹部201aに埋め込まれて形成されている。   The silicon substrate 201 is provided with a recess 201a formed by patterning so as to avoid the through hole 204, and a side surface 201b is formed in the recess 201a. A silicon oxide film 202, which is an inorganic electret member, is formed by being embedded in the recess 201a.

シリコン窒化膜203は、段差無く形成された、シリコン基板201の表面201cとシリコン酸化膜202の表面202aとを覆うように形成されている。なお、シリコン窒化膜203に代わる保護膜として、例えばアルミニウム酸化膜やフッ素樹脂膜等を用いてもよい。   The silicon nitride film 203 is formed so as to cover the surface 201c of the silicon substrate 201 and the surface 202a of the silicon oxide film 202 formed without any step. For example, an aluminum oxide film or a fluororesin film may be used as a protective film in place of the silicon nitride film 203.

前述の構成により、シリコン酸化膜202の側面は、シリコン基板201に設けられた凹部201aの側面201bに保護される。また、シリコン基板201の表面201cと、シリコン酸化膜202の表面202aとには段差がないので、シリコン窒化膜203によってシリコン酸化膜202の表面202aを確実に保護することができる。   With the above-described configuration, the side surface of the silicon oxide film 202 is protected by the side surface 201b of the recess 201a provided in the silicon substrate 201. Further, since there is no step between the surface 201 c of the silicon substrate 201 and the surface 202 a of the silicon oxide film 202, the surface 202 a of the silicon oxide film 202 can be reliably protected by the silicon nitride film 203.

すなわち、本実施の形態における背面電極基板200は、従来のものとは異なり、シリコン酸化膜202を厚くしてもステップカバレッジの問題が発生せず、耐湿性の高いエレクトレット構造を有するものである。   That is, unlike the conventional substrate, the back electrode substrate 200 in the present embodiment does not cause a step coverage problem even if the silicon oxide film 202 is thick, and has an electret structure with high moisture resistance.

次に、本実施の形態における背面電極基板200の製造方法について図3〜図5を用いて説明する。   Next, a method for manufacturing back electrode substrate 200 in the present embodiment will be described with reference to FIGS.

まず、シリコン基板201の表面及び裏面にそれぞれ例えば熱酸化法によってシリコン酸化膜11を形成する(図3(a))。このシリコン酸化膜11は、後工程においてシリコン基板201に凹部201aを形成するためのマスク膜である。   First, the silicon oxide film 11 is formed on the front surface and the back surface of the silicon substrate 201 by, eg, thermal oxidation (FIG. 3A). This silicon oxide film 11 is a mask film for forming a recess 201a in the silicon substrate 201 in a later step.

続いて、シリコン基板201の表面及び裏面にそれぞれフォトレジスト12を塗布し、フォトリソグラフィ法により、シリコン基板201の表面に開口部12aを形成する(図3(b))。   Subsequently, a photoresist 12 is applied to each of the front and back surfaces of the silicon substrate 201, and an opening 12a is formed on the front surface of the silicon substrate 201 by photolithography (FIG. 3B).

さらに、開口部12aからシリコン酸化膜11をエッチングした後、フォトレジスト12を除去する。これによりシリコン基板201の表面201cに開口部11aが形成される(図3(c))。   Further, after etching the silicon oxide film 11 from the opening 12a, the photoresist 12 is removed. As a result, an opening 11a is formed in the surface 201c of the silicon substrate 201 (FIG. 3C).

次に、開口部11aからシリコン基板201をエッチングし、凹部201aを形成する。例えば、シリコン基板201が単結晶シリコンである場合、テトラメチルアンモニウムハイドロオキサイド等のエッチング液を使ってエッチングすると、凹部201aの側面201bは斜めに形成される(図3(d))。   Next, the silicon substrate 201 is etched from the opening 11a to form a recess 201a. For example, when the silicon substrate 201 is single crystal silicon, the side surface 201b of the recess 201a is formed obliquely when etched using an etchant such as tetramethylammonium hydroxide (FIG. 3D).

引き続き、エッチングによりシリコン基板201の表面及び裏面にそれぞれに形成したシリコン酸化膜11を除去する(図4(e))。   Subsequently, the silicon oxide film 11 formed on each of the front and back surfaces of the silicon substrate 201 is removed by etching (FIG. 4E).

次に、熱酸化法等を用いて、無機エレクトレット部材であるシリコン酸化膜202を形成する。シリコン酸化膜202の厚さは、凹部201aの深さより厚くしておくことが望ましい。なお、熱酸化法でシリコン酸化膜202を形成する場合、シリコン基板201の裏面にもシリコン酸化膜13が形成される(図4(f))。   Next, a silicon oxide film 202 which is an inorganic electret member is formed using a thermal oxidation method or the like. The thickness of the silicon oxide film 202 is desirably thicker than the depth of the recess 201a. When the silicon oxide film 202 is formed by the thermal oxidation method, the silicon oxide film 13 is also formed on the back surface of the silicon substrate 201 (FIG. 4F).

続いて、シリコン酸化膜202とシリコン基板201の表面201cとの段差が無くなるように、シリコン基板201の表面側を研磨する(図4(g))。   Subsequently, the surface side of the silicon substrate 201 is polished so that there is no step between the silicon oxide film 202 and the surface 201c of the silicon substrate 201 (FIG. 4G).

さらに、シリコン基板201の表面201cをフォトレジスト(図示せず)で保護して、シリコン基板201の裏面に形成されたシリコン酸化膜13をエッチングして除去する。フォトレジストはシリコン酸化膜13をエッチングした後に除去する(図4(h))。   Further, the surface 201c of the silicon substrate 201 is protected with a photoresist (not shown), and the silicon oxide film 13 formed on the back surface of the silicon substrate 201 is removed by etching. The photoresist is removed after etching the silicon oxide film 13 (FIG. 4H).

また、シリコン基板201の両面に化学気相成長法等でシリコン窒化膜203及び14を形成する(図4(i))。   Further, silicon nitride films 203 and 14 are formed on both surfaces of the silicon substrate 201 by chemical vapor deposition or the like (FIG. 4I).

次に、シリコン基板201の表面及び裏面にそれぞれフォトレジスト15を塗布し、フォトリソグラフィ法により、シリコン基板201の裏面に開口部15aを形成する(図5(j))。   Next, a photoresist 15 is applied to each of the front and back surfaces of the silicon substrate 201, and an opening 15a is formed on the back surface of the silicon substrate 201 by photolithography (FIG. 5J).

さらに、開口部15aからシリコン窒化膜203をエッチングし、続いて、フォトレジスト15を除去する。これによりシリコン基板201の裏面に開口部14aが形成される(図5(k))。   Further, the silicon nitride film 203 is etched from the opening 15a, and then the photoresist 15 is removed. As a result, an opening 14a is formed on the back surface of the silicon substrate 201 (FIG. 5K).

また、開口部14aからシリコン基板201をエッチングし、開口部201dを形成する。例えば、シリコン基板201が単結晶シリコンの場合、テトラメチルアンモニウムハイドロオキサイド等のエッチング液を使ってエッチングすると、開口部201dの側面201eは図示のように斜めに形成される(図5(l))。   Further, the silicon substrate 201 is etched from the opening 14a to form an opening 201d. For example, when the silicon substrate 201 is single crystal silicon, the side surface 201e of the opening 201d is formed obliquely as shown in FIG. 5 (l) when etched using an etching solution such as tetramethylammonium hydroxide. .

次に、例えばドライエッチング法を用いて、シリコン基板201の裏面からシリコン窒化膜14を除去する。このとき、開口部201dの底のシリコン窒化膜203(図5(l)参照)も同時にエッチングされ貫通孔204が形成される(図5(m))。   Next, the silicon nitride film 14 is removed from the back surface of the silicon substrate 201 using, for example, a dry etching method. At this time, the silicon nitride film 203 (see FIG. 5 (l)) at the bottom of the opening 201d is simultaneously etched to form a through hole 204 (FIG. 5 (m)).

そして、シリコン基板201の裏面にスパッタ法等で電極205を形成することで、本発明のエレクトレット構造を有する背面電極基板200が得られる(図5(n))。   Then, by forming the electrode 205 on the back surface of the silicon substrate 201 by sputtering or the like, the back electrode substrate 200 having the electret structure of the present invention is obtained (FIG. 5 (n)).

この後、背面電極基板200のシリコン窒化膜203側から、図示しないメッシュを通して針電極よりコロナ放電を行い、電荷を蓄積して背面電極基板200が完成する。   Thereafter, corona discharge is performed from the needle electrode through a mesh (not shown) from the side of the silicon nitride film 203 of the back electrode substrate 200, and charges are accumulated to complete the back electrode substrate 200.

次に、本実施の形態に係るシリコンマイクロホン100の可動電極基板300は公知の製造方法で製作することができる。この後、背面電極基板200と可動電極基板300との間に絶縁体400を設けて接合することによってシリコンマイクロホン100が得られる。   Next, the movable electrode substrate 300 of the silicon microphone 100 according to the present embodiment can be manufactured by a known manufacturing method. Thereafter, the silicon microphone 100 is obtained by providing and bonding the insulator 400 between the back electrode substrate 200 and the movable electrode substrate 300.

以上のように、本実施の形態におけるシリコンマイクロホン100によれば、シリコン基板201の表面201cと、無機エレクトレット部材であるシリコン酸化膜202の表面202aとを段差無くシリコン窒化膜203で保護するとともに、シリコン酸化膜202が形成されていない領域に貫通孔204を形成する構成としたので、シリコン酸化膜202は外気に触れないこととなる。したがって、本実施の形態におけるシリコンマイクロホン100は、無機エレクトレット部材の厚さに関わらず、その耐湿性を確実に確保することができる。   As described above, according to the silicon microphone 100 in the present embodiment, the surface 201c of the silicon substrate 201 and the surface 202a of the silicon oxide film 202 that is an inorganic electret member are protected by the silicon nitride film 203 without any step, Since the through hole 204 is formed in a region where the silicon oxide film 202 is not formed, the silicon oxide film 202 is not exposed to the outside air. Therefore, the silicon microphone 100 according to the present embodiment can reliably ensure the moisture resistance regardless of the thickness of the inorganic electret member.

なお、前述の実施の形態において、本発明のエレクトレット型静電容量センサをシリコンマイクロホン100に適用する例を挙げて説明したが、本発明はこれに限定されるものではなく、音波以外の圧力や加速度等に応じて可動電極が変位するものに適用することができる。   In the above-described embodiment, the example in which the electret capacitive sensor of the present invention is applied to the silicon microphone 100 has been described. However, the present invention is not limited to this, and pressures other than sound waves, The present invention can be applied to a case where the movable electrode is displaced according to acceleration or the like.

(第2の実施の形態)
本実施の形態におけるシリコンマイクロホンの背面基板を図6に示す。図6(a)は、図6(b)に示すA−A断面における断面概念図であり、図6(b)は、図6(a)に示すB方向から見た平面概念図である。また、図6(c)は、図6(a)におけるC部を拡大した断面概念図である。
(Second Embodiment)
FIG. 6 shows a back substrate of the silicon microphone according to the present embodiment. 6A is a conceptual cross-sectional view taken along the line AA shown in FIG. 6B, and FIG. 6B is a conceptual plan view seen from the direction B shown in FIG. 6A. Moreover, FIG.6 (c) is the cross-sectional conceptual diagram which expanded the C section in Fig.6 (a).

図6に示すように、本実施の形態における背面電極基板500は、第1の実施の形態における背面電極基板200(図2参照)に対し、C部の構成が異なっている。なお、第1の実施の形態における背面電極基板200と同様な構成には同一の符号を付し、説明を省略する。   As shown in FIG. 6, the back electrode substrate 500 in the present embodiment is different from the back electrode substrate 200 (see FIG. 2) in the first embodiment in the configuration of the C part. In addition, the same code | symbol is attached | subjected to the structure similar to the back electrode substrate 200 in 1st Embodiment, and description is abbreviate | omitted.

本実施の形態におけるシリコン酸化膜202は、その一部がシリコン基板201の凹部201aに埋め込まれ、シリコン基板201の表面201cから予め定めた位置まで盛り上がった形状で形成されている。そして、シリコン酸化膜202の端部202cはバーズビーク(鳥のくちばし)状に形成されている。また、シリコン窒化膜203は、シリコン基板201の表面201cと、シリコン酸化膜202の表面202aとを覆うように形成されている。   Part of the silicon oxide film 202 in this embodiment is embedded in the recess 201a of the silicon substrate 201, and is formed in a shape rising from the surface 201c of the silicon substrate 201 to a predetermined position. The end portion 202c of the silicon oxide film 202 is formed in a bird's beak (bird's beak) shape. The silicon nitride film 203 is formed so as to cover the surface 201 c of the silicon substrate 201 and the surface 202 a of the silicon oxide film 202.

本実施の形態における背面電極基板500は、前述のように構成されているので、シリコン酸化膜202の表面202aとシリコン基板201の表面201cとが、段差無く、緩やかに接続されるため、シリコン酸化膜202の厚さに関わらず、シリコン酸化膜202の表面202aをシリコン窒化膜203で確実に保護することができ、耐湿性の高いエレクトレット構造を有するものとなる。   Since the back electrode substrate 500 in the present embodiment is configured as described above, the surface 202a of the silicon oxide film 202 and the surface 201c of the silicon substrate 201 are gently connected without any step. Regardless of the thickness of the film 202, the surface 202a of the silicon oxide film 202 can be reliably protected by the silicon nitride film 203, and has an electret structure with high moisture resistance.

なお、バーズビーク形状の断面をもつシリコン酸化膜202をシリコン基板201に一部埋め込んで形成するには、例えば既に確立している半導体製造技術であるLOCOS(LOCal Oxidation of Silicon:選択酸化法)プロセスを用いることができる。このLOCOSプロセスは公知であるので、背面電極基板500の製造方法の説明を省略する。   In order to form the silicon oxide film 202 having a bird's beak-shaped cross-section partially embedded in the silicon substrate 201, for example, a LOCOS (LOCal Oxidation of Silicon) process, which is an already established semiconductor manufacturing technology, is used. Can be used. Since this LOCOS process is known, the description of the manufacturing method of the back electrode substrate 500 is omitted.

以上のように、本実施の形態におけるシリコンマイクロホンによれば、無機エレクトレット部材であるシリコン酸化膜202を、バーズビーク状の形状を有するシリコン窒化膜203で保護する構成としたので、無機エレクトレット部材の厚さに関わらず、その耐湿性を確実に確保することができる。   As described above, according to the silicon microphone of the present embodiment, since the silicon oxide film 202 that is an inorganic electret member is protected by the silicon nitride film 203 having a bird's beak shape, the thickness of the inorganic electret member Regardless of this, the moisture resistance can be reliably ensured.

以上のように、本発明に係るエレクトレット構造及びその形成方法並びにエレクトレット型静電容量センサは、無機エレクトレット部材の厚さに関わらず、その耐湿性を確実に確保することができるという効果を有し、シリコンマイクロホン、圧力センサ、加速度センサ等として有用である。   As described above, the electret structure according to the present invention, the method for forming the electret structure, and the electret-type capacitance sensor have an effect that the moisture resistance can be reliably ensured regardless of the thickness of the inorganic electret member. It is useful as a silicon microphone, pressure sensor, acceleration sensor and the like.

本発明の第1の実施の形態におけるシリコンマイクロホンの構成を示す断面概念図Sectional conceptual diagram which shows the structure of the silicon microphone in the 1st Embodiment of this invention. 本発明の第1の実施の形態におけるシリコンマイクロホンの背面電極基板の構成を示す概念図 (a)背面電極基板の断面概念図 (b)背面電極基板の平面概念図The conceptual diagram which shows the structure of the back electrode substrate of the silicon microphone in the 1st Embodiment of this invention (a) The cross-sectional conceptual diagram of a back electrode substrate (b) The plane conceptual diagram of a back electrode substrate 本発明の第1の実施の形態におけるシリコンマイクロホンの背面電極基板の製造工程を示す図The figure which shows the manufacturing process of the back electrode board | substrate of the silicon microphone in the 1st Embodiment of this invention. 本発明の第1の実施の形態におけるシリコンマイクロホンの背面電極基板の製造工程を示す図The figure which shows the manufacturing process of the back electrode board | substrate of the silicon microphone in the 1st Embodiment of this invention. 本発明の第1の実施の形態におけるシリコンマイクロホンの背面電極基板の製造工程を示す図The figure which shows the manufacturing process of the back electrode board | substrate of the silicon microphone in the 1st Embodiment of this invention. 本発明の第2の実施の形態におけるシリコンマイクロホンの背面電極基板の構成を示す概念図 (a)背面電極基板の断面概念図 (b)背面電極基板の平面概念図The conceptual diagram which shows the structure of the back electrode substrate of the silicon microphone in the 2nd Embodiment of this invention (a) The cross-sectional conceptual diagram of a back electrode substrate (b) The plane conceptual diagram of a back electrode substrate 従来のエレクトレット構造を示す断面図Sectional view showing a conventional electret structure

符号の説明Explanation of symbols

11 シリコン酸化膜
11a シリコン酸化膜の開口部
12 フォトレジスト
12a フォトレジストの開口部
13 シリコン酸化膜
14 シリコン窒化膜
14a シリコン窒化膜の開口部
15 フォトレジスト
15a フォトレジストの開口部
100 シリコンマイクロホン
200 背面電極基板
201 シリコン基板
201a シリコン基板の凹部
201b 凹部の側面
201c シリコン基板の表面
201d シリコン基板の開口部
201e 開口部の側面
202 シリコン酸化膜(無機エレクトレット部材)
202a シリコン酸化膜の表面
202b シリコン酸化膜の側面
202c シリコン酸化膜の端部
203 シリコン窒化膜(保護膜)
204 貫通孔
205 電極
300 可動電極基板
301 シリコン基板
302 可動電極膜
303 接続用端子
400 絶縁体
500 背面電極基板
DESCRIPTION OF SYMBOLS 11 Silicon oxide film 11a Silicon oxide film opening 12 Photoresist 12a Photoresist opening 13 Silicon oxide film 14 Silicon nitride film 14a Silicon nitride film opening 15 Photoresist 15a Photoresist opening 100 Silicon microphone 200 Back electrode Substrate 201 Silicon substrate 201a Recessed portion of silicon substrate 201b Side surface of recessed portion 201c Surface of silicon substrate 201d Opening portion of silicon substrate 201e Side surface of opening portion 202 Silicon oxide film (inorganic electret member)
202a Surface of silicon oxide film 202b Side surface of silicon oxide film 202c End portion of silicon oxide film 203 Silicon nitride film (protective film)
204 Through-hole 205 Electrode 300 Movable electrode substrate 301 Silicon substrate 302 Movable electrode film 303 Connection terminal 400 Insulator 500 Back electrode substrate

Claims (5)

凹部が形成された第1の面及び該第1の面とは反対側の第2の面を有するシリコン基板と、前記凹部の底面から前記第1の面の位置までの前記凹部内に埋め込まれた無機エレクトレット部材と、前記第1の面及び前記無機エレクトレット部材の表面を保護する保護膜と、前記第2の面上に形成された電極とを備えたことを特徴とするエレクトレット構造。 A silicon substrate having a first surface in which a recess is formed and a second surface opposite to the first surface; and embedded in the recess from the bottom surface of the recess to the position of the first surface. An electret structure comprising: an inorganic electret member; a protective film that protects the first surface and the surface of the inorganic electret member; and an electrode formed on the second surface. 凹部が形成された第1の面及び該第1の面とは反対側の第2の面を有するシリコン基板と、前記凹部の底面から前記第1の面の位置を超える予め定めた位置まで埋め込まれた無機エレクトレット部材と、前記第1の面及び前記無機エレクトレット部材の表面を保護する保護膜と、前記第2の面上に形成された電極とを備え、
前記無機エレクトレット部材は、前記シリコン基板の厚さ方向において前記凹部の開口の中央から端に向かって次第に薄くなるようバーズビーク状に形成されていることを特徴とするエレクトレット構造。
A silicon substrate having a first surface in which a recess is formed and a second surface opposite to the first surface, and embedded from the bottom surface of the recess to a predetermined position exceeding the position of the first surface An inorganic electret member formed, a protective film for protecting the first surface and the surface of the inorganic electret member, and an electrode formed on the second surface,
The electret structure is characterized in that the inorganic electret member is formed in a bird's beak shape so as to gradually become thinner from the center to the end of the opening of the recess in the thickness direction of the silicon substrate.
前記凹部の開口が設けられた前記第1の面上の領域とは異なる領域から前記第2の面に貫通する少なくとも1つの貫通孔を備えたことを特徴とする請求項1又は請求項2に記載のエレクトレット構造。 3. The method according to claim 1, further comprising at least one through-hole penetrating from the region different from the region on the first surface where the opening of the concave portion is provided to the second surface. The electret structure described. 請求項1から請求項3までのいずれか1項に記載のエレクトレット構造を有する背面電極基板と、該背面電極基板に対向配置され印加圧力に応じて変位する可動電極基板とを備えたことを特徴とするエレクトレット型静電容量センサ。 A back electrode substrate having the electret structure according to any one of claims 1 to 3, and a movable electrode substrate disposed opposite to the back electrode substrate and displaced in accordance with an applied pressure. Electret type capacitive sensor. 第1の面及び該第1の面とは反対側の第2の面を有するシリコン基板に無機エレクトレット部材を形成するエレクトレット構造の形成方法であって、
前記シリコン基板の前記第1の面に凹部を形成する工程と、前記無機エレクトレット部材を前記凹部に形成する工程と、前記第1の面と前記無機エレクトレット部材の表面とを平坦化する工程と、平坦化した第1の面及び無機エレクトレット部材の表面に保護膜を形成する工程と、前記第2の面上に電極を形成する工程とを含むエレクトレット構造の形成方法。
A method for forming an electret structure in which an inorganic electret member is formed on a silicon substrate having a first surface and a second surface opposite to the first surface,
Forming a recess in the first surface of the silicon substrate, forming the inorganic electret member in the recess, flattening the first surface and the surface of the inorganic electret member, A method of forming an electret structure, comprising: forming a protective film on the planarized first surface and the surface of the inorganic electret member; and forming an electrode on the second surface.
JP2008003314A 2008-01-10 2008-01-10 Electret structure, method of forming the same, and electret-type capacitance sensor Expired - Fee Related JP5240900B2 (en)