JP2002254546A - Latent image recording medium - Google Patents

Latent image recording medium

Info

Publication number
JP2002254546A
JP2002254546A JP2001054913A JP2001054913A JP2002254546A JP 2002254546 A JP2002254546 A JP 2002254546A JP 2001054913 A JP2001054913 A JP 2001054913A JP 2001054913 A JP2001054913 A JP 2001054913A JP 2002254546 A JP2002254546 A JP 2002254546A
Authority
JP
Japan
Prior art keywords
latent image
layer
diffraction
forming structure
recording medium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
JP2001054913A
Other languages
Japanese (ja)
Inventor
Harumi Ota
陽美 太田
Satoshi Gocho
智 牛腸
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toppan Inc
Original Assignee
Toppan Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toppan Printing Co Ltd filed Critical Toppan Printing Co Ltd
Priority to JP2001054913A priority Critical patent/JP2002254546A/en
Publication of JP2002254546A publication Critical patent/JP2002254546A/en
Withdrawn legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide a latent image recording medium such as a lottery ticket, passbooks, a show ticket, a membership certificate, a passport, a picture book, a game, a cash card, a telephone card or an IC card, of such a construction that a latent image in a latent image forming structural layer can be visually determined when viewed through a dedicated verifying medium, contrary to a normal state that an image such as a hologram image or a diffraction grating image played back through the mutual interference of a reflected and a diffracted light is only viewed. SOLUTION: At least the latent image forming structural layer and a diffraction forming structural layer with light transmission properties are laminated in that order on a base material. Further, the latent image forming structural layer is at least a reflective layer and a polymer material layer showing thermotropic properties.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【発明の属する技術分野】本発明は、通常の状態では反
射・回折光が互いに干渉して再生されるホログラム画像
や回折格子画像等の画像が観察されるのみであるが、専
用の検証媒体を介して観察したときには潜像形成構造層
中の潜像が認識できるようにした、抽選券、通帳類、鑑
賞券、会員証、パスポート、絵本、ゲーム、キャッシュ
カード、テレホンカード、ICカード等の潜像記録媒体
である。
BACKGROUND OF THE INVENTION The present invention relates to a method for observing an image such as a hologram image or a diffraction grating image which is reproduced by interference of reflected and diffracted light under normal conditions. The latent image in the latent image forming structure layer can be recognized when observed through a device, such as a lottery ticket, passbook, appreciation ticket, membership card, passport, picture book, game, cash card, telephone card, IC card, etc. An image recording medium.

【0002】[0002]

【従来の技術】従来から所望の部分に潜像を設けた潜像
記録媒体は種々ある。例えば万線のピッチの間隙を利用
して潜像(隠し文字等)を入れ、万線部分を検証部材で
隠蔽することで潜像化していた像が現れるようにした万
線画や、フィラーを入れた透明インキで潜像を印刷し、
鉛筆で潜像部分を擦ると鉛筆の粉が印刷部分に付着して
隠しパターン等が現れるようにした鉛筆出し印刷物(デ
コマット)等である。これらの潜像記録媒体は隠されて
いる潜像はよく見ると分かってしまうため、本格的な潜
像記録媒体というよりは、遊び用として使用されてい
る。
2. Description of the Related Art There are various types of latent image recording media in which a latent image is provided at a desired portion. For example, a latent image (hidden characters, etc.) is inserted by using a line pitch of a line, and a line drawing or a filler is used in which a latent image is displayed by concealing the line portion with a verification member. Prints the latent image with transparent ink
A pencil-out printed matter (deco mat) or the like in which a pencil pattern adheres to a printed part when a latent image portion is rubbed with a pencil to display a hidden pattern or the like. These latent image recording media are used for play rather than full-scale latent image recording media because hidden latent images can be seen by observing them well.

【0003】これらを含む種々の潜像を記録するための
画像記録用材料としては、不可逆性感熱発色インキ、フ
ィラー含有の白色インキ、可逆性感熱発色インキ、フォ
トクロミックインキ、蛍光インキ、磁性インキ、赤外線
吸収インキ等があり、種々の形態で使用されている。
Image recording materials for recording various latent images including these include irreversible thermosensitive coloring ink, filler-containing white ink, reversible thermosensitive coloring ink, photochromic ink, fluorescent ink, magnetic ink, and infrared ink. There are absorption inks and the like, which are used in various forms.

【0004】不可逆性感熱発色インキは熱を加えること
によって不可逆的に発色するインキであり、このインキ
の白色もしくは無色透明タイプのものにより基材上に潜
像を形成して潜像記録媒体とする。しかし、このような
構成の画像記録媒体は、潜像を表示させるためには熱源
装置が必要であり、しかも一回発色表示させた画像は消
色することができないため、用途が限定される。
An irreversible thermosensitive ink is an ink which irreversibly develops color when heated, and forms a latent image on a substrate by using a white or colorless and transparent type of this ink to form a latent image recording medium. . However, the image recording medium having such a configuration requires a heat source device to display a latent image, and furthermore, an image displayed once by color cannot be erased, so that its use is limited.

【0005】また、フィラー含有の白色インキは、例え
ば酸化チタン等の金属よりも硬いフィラーを含有させた
白色インキで、このインキにより白色の紙に潜像を印刷
し、必要であればマット調のニスでオーバーコートして
潜像記録媒体とする。このような構成の潜像記録媒体は
潜像の部分をコイン等で擦ることにより所期の像を表示
させることができるが、表示できるのは一回限りであり
用途が限定される。
[0005] The filler-containing white ink is a white ink containing a filler harder than a metal such as titanium oxide. A latent image is printed on white paper by using this ink. The latent image recording medium is overcoated with varnish. The latent image recording medium having such a configuration can display the intended image by rubbing the latent image portion with a coin or the like, but the display can be performed only once and the use is limited.

【0006】さらにまた、可逆性感熱発色インキ(サー
モクロミックインキ)は、熱をかけることにより可逆的
に発色もしくは消色するインキであり、加熱をやめて暫
く放置すると元の状態に戻るという特性を利用し、潜像
記録媒体の潜像や画像を一時的に隠蔽して潜像化するた
めの隠蔽層等の形成用材料として使用されている。しか
しこのインキならびにこのインキにより潜像を記録した
潜像記録媒体は、耐性、特に耐熱性が弱く、用途が限定
される。
Further, a reversible thermosensitive coloring ink (thermochromic ink) is an ink which reversibly develops or decolors by applying heat, and utilizes the property of returning to the original state when the heating is stopped and left for a while. However, it is used as a material for forming a concealing layer or the like for temporarily concealing a latent image or image of a latent image recording medium to form a latent image. However, this ink and a latent image recording medium on which a latent image has been recorded with this ink have low durability, especially low heat resistance, and their applications are limited.

【0007】さらにまた、フォトクロミックインキは、
光を照射することにより発色するインキで、白色もしく
は無色透明のタイプのものが潜像記録媒体の潜像の形成
用材料として使用されている。しかし、このインキなら
びにこのインキにより潜像を記録した潜像記録媒体は、
耐性、特に耐光性が弱く、用途が限定されている。
Furthermore, photochromic inks are
Ink that develops color when irradiated with light and is white or colorless and transparent is used as a material for forming a latent image on a latent image recording medium. However, this ink and a latent image recording medium on which a latent image is recorded with this ink are:
Poor resistance, especially light resistance, limits its use.

【0008】さらにまた、蛍光インキは紫外線等の活性
光線を照射することにより蛍光を発光するインキで、白
色または無色透明タイプのもので潜像を形成することが
ある。蛍光インキには有機タイプと無機タイプのものが
あるが、有機タイプのものはインキ中にごく少量の有機
系蛍光物質を含有するだけで発光が確認されるが、耐光
性が弱いために用途が限定される。また、無機タイプの
ものはインキ中に無機系蛍光物質を多く入れる必要があ
り(10〜20%程度)、これにより形成された潜像は
それ単独では目視で分かってしまうため、デザイン等に
工夫が必要である。
Further, a fluorescent ink is an ink which emits fluorescence when irradiated with actinic rays such as ultraviolet rays, and may form a latent image of a white or colorless transparent type. There are two types of fluorescent inks: organic and inorganic types. The organic type can be confirmed to emit light only by containing a very small amount of organic fluorescent substance in the ink. Limited. In addition, the inorganic type requires a large amount of an inorganic fluorescent substance to be contained in the ink (about 10 to 20%), and the latent image formed thereby can be visually recognized by itself. is necessary.

【0009】さらにまた、磁性インキは磁性微粒子をイ
ンキ中に分散したものであり、これを利用して潜像を形
成するには、まず磁気記録可能な保持力(約300Oe
以上)のある磁性層を形成し、しかる後にこの磁性層の
一部をパターン状に磁化させればよい。そして、潜像の
可視化は、磁性層上に鉄粉を振りかけ、磁化させた潜像
部分のみに選択的に吸着させてやればよい。しかし、こ
の方式では潜像を表示させる工程が煩雑であり、また画
像の書き換えが可能であり、用途が限定される。
Further, the magnetic ink is obtained by dispersing magnetic fine particles in the ink. In order to form a latent image using the magnetic ink, first, a coercive force (about 300 Oe) capable of magnetic recording is used.
Above), a portion of this magnetic layer may be magnetized in a pattern thereafter. The latent image can be visualized by sprinkling iron powder on the magnetic layer and selectively adsorbing only the magnetized latent image portion. However, in this method, the process of displaying the latent image is complicated, and the image can be rewritten, and the application is limited.

【0010】さらにまた、赤外線を吸収するインキにて
画像を形成し、この上に赤外線は透過し前記画像を隠蔽
して潜像化(目視できないようにする)するための層を
設けた潜像記録媒体があるが、この隠蔽されている潜像
化画像を現出させ、表示させるためには赤外線照射装置
や赤外線カメラ等が必要であり、装置的に大がかりとな
る。また、可視光域では白色もしくは無色であるが、赤
外線域に吸収のあるインキ(IVインキ)があり、これ
により潜像を形成した潜像記録媒体もあるが、これも前
記同様、潜像を可視化するためには赤外線カメラ等が必
要である。
[0010] Furthermore, a latent image is formed by forming an image with an ink that absorbs infrared rays, on which an infrared ray is transmitted to conceal the image to form a latent image (to make it invisible). Although there is a recording medium, an infrared irradiation device, an infrared camera, and the like are required to display and display the hidden latent image, and the device becomes large. Further, there is an ink (IV ink) which is white or colorless in the visible light region, but absorbs in the infrared region, and there is also a latent image recording medium on which a latent image is formed by using this ink. An infrared camera or the like is required for visualization.

【0011】一方、ピッチもしくは角度を部分的に変え
た網点や万線で構成される潜像を通常の印刷インキによ
り形成することもある。このような構成の潜像の可視化
は、整然と並んだ網点もしくは万線を設けた透明フィル
ムをこの潜像上にモアレを発生するように重ね合わせた
り、あるいは潜像以外の万線部分を前記した透明フィル
ムの万線部分で隠蔽するように重ね合わせて行ってい
た。この場合、潜像ならびに潜像記録媒体の構成が簡単
で、しかも潜像の現出、消去が繰り返し行えるが、複雑
な形状の潜像パターンを形成できないという問題があ
る。
On the other hand, a latent image composed of halftone dots or lines in which the pitch or angle is partially changed may be formed with ordinary printing ink. Visualization of the latent image having such a configuration is performed by superimposing a transparent film provided with neatly arranged halftone dots or lines so as to generate moire on the latent image, or the line portion other than the latent image is formed by the above-described method. It was superimposed so as to be concealed by the lines of the transparent film. In this case, the construction of the latent image and the latent image recording medium is simple, and the appearance and erasure of the latent image can be repeated. However, there is a problem that a latent image pattern having a complicated shape cannot be formed.

【0012】他方、従来から、ホログラムや回折格子画
像等は光の回折・干渉効果を用いて立体画像や特殊な装
飾画像を表現でき、その製造方法は高度な製造技術を要
するため、偽造防止手段として、クレジットカード、有
価証券、証明書類等の一部あるいは全面に使用されてい
る。
On the other hand, holograms and diffraction grating images have conventionally been able to express stereoscopic images and special decorative images by using the light diffraction / interference effect, and their manufacturing methods require advanced manufacturing techniques. Is used for some or all of credit cards, securities, certificates, and the like.

【0013】ホログラムは製造方法により、レリーフ型
ホログラム及び体積型ホログラムに分けられる。レリー
フ型ホログラムは、光学的撮影方法により微細な凹凸パ
ターンからなるレリーフ型のマスターホログラムを作製
し、さらにこれから電気メッキ法により凹凸パターンを
複製してニッケル製のプレス版を作製し、しかる後この
プレス版をホログラム形成層上に加熱押圧して製造する
ものである。一方、体積型ホログラムは、感光性樹脂等
の記録材料を用いて、体積方向に干渉縞を記録したもの
である。この型のホログラムでは、リップマンホログラ
ムと呼ばれるものが一般に使用されており、感光性樹脂
の屈折率を体積方向に変化させ、反射型ホログラムとし
たものである。
Holograms are classified into relief holograms and volume holograms according to the manufacturing method. For the relief hologram, a relief-type master hologram consisting of a fine uneven pattern is produced by an optical photographing method, and then the uneven pattern is duplicated by an electroplating method to produce a nickel press plate. The plate is manufactured by heating and pressing the plate on the hologram forming layer. On the other hand, a volume hologram is obtained by recording interference fringes in a volume direction using a recording material such as a photosensitive resin. In this type of hologram, a so-called Lippmann hologram is generally used, and the refractive index of the photosensitive resin is changed in the volume direction to form a reflection hologram.

【0014】また、回折格子画像は回折格子からなる微
少セルが回折形成層表面に複数配置されて形成され、回
折格子の空間周波数、回折格子の方向、各セルの並び方
の少なくとも何れかを変化させてなる画像であり、前述
したホログラム同様、偽造防止の有効な手段としてカー
ドや印刷物等の分野で採用されている。
Further, the diffraction grating image is formed by arranging a plurality of micro cells made of a diffraction grating on the surface of the diffraction forming layer, and changing at least one of the spatial frequency of the diffraction grating, the direction of the diffraction grating, and the arrangement of the cells. Like the hologram described above, it is used in the field of cards and printed matter as an effective means for preventing forgery.

【0015】しかし、これらのホログラムや回折格子画
像は、上述したように偽造防止のための手段としては有
効なものであるが、最近の複製技術の進歩により、ホロ
グラムや回折格子画像を有する画像記録媒体の真正品に
近似する複製物も得られるようになっている。
However, these holograms and diffraction grating images are effective as a means for preventing forgery as described above, but with the recent progress in duplication technology, image recording having holograms and diffraction grating images has been carried out. Reproductions that are close to authentic media can also be obtained.

【0016】[0016]

【発明が解決しようとする課題】本発明は以上のような
状況に鑑みなされたものであり、通常の状態では反射・
回折光が互いに干渉して再生されるホログラム画像や回
折格子画像等の画像が観察されるのみであるが、専用の
検証媒体を介して観察したときのみにその内容の確認が
可能な潜像を有し、しかもその偽造防止効果をより高め
た潜像記録媒体の提供を目的とする。
DISCLOSURE OF THE INVENTION The present invention has been made in view of the above-described situation, and it is difficult to reflect and reflect light in a normal state.
Only images such as hologram images and diffraction grating images, which are reproduced by diffracted light interfering with each other, are observed, but a latent image whose contents can be confirmed only when observed through a dedicated verification medium. It is another object of the present invention to provide a latent image recording medium having a forgery prevention effect.

【0017】[0017]

【課題を解決するための手段】本発明は上記目的を達成
するためになされたもので、請求項1に記載の発明は、
基材上に、少なくとも潜像形成構造層ならびに光透過性
を有する回折形成構造層がこの順序で積層されてなり、
該潜像形成構造層は少なくとも反射層とサーモトロピッ
ク性を示す高分子材料層からなることを特徴とする。
Means for Solving the Problems The present invention has been made to achieve the above object, and the invention according to claim 1 has the following features.
On the substrate, at least a latent image forming structure layer and a diffraction forming structure layer having optical transparency are laminated in this order,
The latent image forming structure layer comprises at least a reflective layer and a thermotropic polymer material layer.

【0018】また、請求項2に記載の発明は、請求項1
に記載の潜像記録媒体において、光透過性を有する回折
形成構造層は、少なくとも画像再生効果層と回折形成層
からなり、かつ回折形成層の構成材料よりも高い屈折率
で、しかも下部の潜像形成構造層の存在が認識できる程
度の透明性は少なくとも有する構成材料からなることを
特徴とする。
The invention described in claim 2 is the same as the invention described in claim 1.
In the latent image recording medium described in the above, the diffraction forming structure layer having optical transparency comprises at least an image reproduction effect layer and a diffraction forming layer, has a higher refractive index than the constituent material of the diffraction forming layer, and has a lower latent formation layer. It is characterized by being composed of a constituent material having at least transparency enough to recognize the existence of the image forming structure layer.

【0019】さらにまた、請求項3に記載の発明は、請
求項1または請求項2に記載の潜像記録媒体において、
潜像形成構造層を構成する反射層は潜像形成構造層の全
面あるいは一部分に設けられ、かつ金属材料からなるこ
とを特徴とする。
Further, according to a third aspect of the present invention, in the latent image recording medium according to the first or second aspect,
The reflection layer constituting the latent image forming structure layer is provided on the entire surface or a part of the latent image forming structure layer, and is made of a metal material.

【0020】さらにまた、請求項4に記載の発明は、請
求項1ないし請求項3のいずれか1項に記載の潜像記録
媒体において、サーモトロピック性を示す高分子材料層
には所望の部分を配向せしめてなる潜像が形成されてい
ることを特徴とする。
According to a fourth aspect of the present invention, there is provided the latent image recording medium according to any one of the first to third aspects, wherein the polymer material layer exhibiting the thermotropic property has a desired portion. Are formed, and a latent image is formed by orienting the latent images.

【0021】さらにまた、請求項5に記載の発明は、請
求項1ないし請求項4のいずれか1項に記載の潜像記録
媒体において、基材の潜像形成構造層ならびに光透過性
を有する回折形成構造層が積層されていない側には接着
層が形成されていることを特徴とする。
According to a fifth aspect of the present invention, there is provided the latent image recording medium according to any one of the first to fourth aspects, wherein the latent image recording medium has a latent image forming structure layer of a substrate and a light transmitting property. An adhesive layer is formed on the side where the diffraction forming structure layer is not laminated.

【0022】[0022]

【発明の実施の形態】以下、本発明を図面に示す実施の
形態によって詳細に説明する。図1は本発明の実施の形
態の一例を示す潜像記録媒体の概略断面説明図である。
この潜像記録媒体1は、基本的には、基材2と潜像形成
構造層5ならびに光透過性を有する回折形成構造層8が
この順序で積層されてなるものである。図1に示す潜像
記録媒体1においては、光透過性を有する回折形成構造
層8上にさらに保護層9が形成されている。
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, the present invention will be described in detail with reference to embodiments shown in the drawings. FIG. 1 is a schematic sectional explanatory view of a latent image recording medium showing an example of an embodiment of the present invention.
The latent image recording medium 1 basically includes a substrate 2, a latent image forming structure layer 5, and a light-transmitting diffraction forming structure layer 8 laminated in this order. In the latent image recording medium 1 shown in FIG. 1, a protective layer 9 is further formed on a light-transmitting diffraction forming structure layer 8.

【0023】ここで、基材2の構成材料としては、ポリ
エチレンテレフタレート、ポリ塩化ビニル、ポリエステ
ル、ポリカーボネート、ポリメタクリル酸メチル、ポリ
スチレン等の合成樹脂、天然樹脂等のフィルム、合成
紙、紙、薄膜ガラスあるいはこれらの材料から選択され
たものを適宜組み合わせた複合体等が使用可能である。
Here, the constituent materials of the substrate 2 include synthetic resin such as polyethylene terephthalate, polyvinyl chloride, polyester, polycarbonate, polymethyl methacrylate, polystyrene, etc., films such as natural resin, synthetic paper, paper, and thin film glass. Alternatively, a composite or the like in which one selected from these materials is appropriately combined can be used.

【0024】一方、この基材2上に形成されている潜像
形成構造層5はそこに潜像を記録、形成できるようにな
っており、専用の検証媒体を介して観察したときのみに
その潜像化されていた画像が認識できるようにした層で
あり、少なくとも反射層3とその上のサーモトロピック
性を示す高分子材料層4からなっている。
On the other hand, the latent image forming structure layer 5 formed on the substrate 2 can record and form a latent image thereon, and the latent image is formed only when observed through a dedicated verification medium. This is a layer that allows the latent image to be recognized, and includes at least a reflective layer 3 and a polymer layer 4 having thermotropic properties thereon.

【0025】反射層3は、反射性を有していればよく、
構成する材料も特に限定されるものではない。例えばA
l、Cr、Ni、Cu、Ag等の各種金属、あるいはP
t−Rh、Ni−Cr等の各種合金等から適宜のものを
選択し、蒸着やスパッタリング等により設ければよい。
The reflecting layer 3 only needs to have reflectivity.
The constituent materials are not particularly limited. For example, A
l, various metals such as Cr, Ni, Cu, Ag, or P
An appropriate alloy may be selected from various alloys such as t-Rh and Ni-Cr, and may be provided by vapor deposition or sputtering.

【0026】一方、サーモトロピック性を示す高分子材
料層4は、80〜200℃程度の融点を有し、サーモト
ロピック性を示し、例えばポリエステル共重合体、ポリ
エーテル、ポリカーボネイト、ポリイソシアネート、ポ
リグルタミン酸エステル等のサーモトロピック性高分子
材料からなるものであり、例えばグラビア印刷法、スク
リーン印刷法等の印刷手段やノズルコーター法等の塗布
手段等の既知の層形成手段により形成すればよい。
On the other hand, the polymer material layer 4 having a thermotropic property has a melting point of about 80 to 200 ° C. and has a thermotropic property, and is, for example, a polyester copolymer, a polyether, a polycarbonate, a polyisocyanate, or a polyglutamic acid. It is made of a thermotropic polymer material such as an ester, and may be formed by a known layer forming means such as a printing means such as a gravure printing method or a screen printing method or a coating means such as a nozzle coater method.

【0027】このサーモトロピック性を示す高分子材料
層4は通常に形成した状態では、特定の結晶構造を有し
てないランダムな分子配列状態になっている。このよう
な分子配列状態にて形成されているサーモトロピック性
を示す高分子材料層4に対してサーマルヘッド、レーザ
ービーム、ホットスタンパー等により部分的に熱を加
え、その部分を溶融すると、その部分に一定方向の配向
が生じ、加熱部分に対応した潜像が形成されることにな
る。この潜像はそのままではその存在が確認されない
が、偏光フィルムや偏光フィルター等の検証媒体を介し
て観察すると、認識されるようになる。
When the polymer material layer 4 having the thermotropic property is formed normally, the polymer material layer 4 has a random molecular arrangement state having no specific crystal structure. When heat is partially applied to the thermotropic polymer material layer 4 formed in such a molecular arrangement state by a thermal head, a laser beam, a hot stamper or the like, and the portion is melted, the portion is melted. Is oriented in a certain direction, and a latent image corresponding to the heated portion is formed. Although the existence of this latent image is not confirmed as it is, it is recognized when observed through a verification medium such as a polarizing film or a polarizing filter.

【0028】この時の状況が図2に示してある。図2の
aに示す潜像記録媒体1は、単に目視しただけでは潜像
が確認できず、ホログラム画像や回折格子画像等の再生
画像22が認識されるだけの単なる画像形成体にしか見
えない。しかしながら、図2のbに示すようにこの潜像
を有する潜像記録媒体1の上に偏光フィルム23を重ね
合わせて観察すると潜像化されていた画像24が出現す
る。潜像はサーモトロピック性を示す高分子材料層4の
一部を熱、電気、磁気エネルギー等で選択的に配向した
部分である。
The situation at this time is shown in FIG. The latent image recording medium 1 shown in FIG. 2A cannot be recognized simply by visual observation, but can be seen only as a mere image forming body in which a reproduced image 22 such as a hologram image or a diffraction grating image is recognized. . However, as shown in FIG. 2B, when the polarizing film 23 is superimposed on the latent image recording medium 1 having the latent image and observed, an image 24 that has been turned into a latent image appears. The latent image is a portion where a part of the polymer material layer 4 exhibiting thermotropic property is selectively oriented by heat, electricity, magnetic energy, or the like.

【0029】潜像の可視化の際に使用される検証媒体と
は、具体的には偏光フィルムや偏光フィルター等であ
る。偏光フィルムや偏光フィルターのタイプには、PV
A延伸フィルムにヨードを吸収させたPVA−ヨウ素
型、二色性染料型、金属または金属化合物含有型、ポリ
エン型などの高分子多結晶型等種々のものがあるが、こ
れらの中から適宜のものを選択して図2のbに示すよう
に潜像記録媒体1に重ね合わせて使用すればよい。偏光
フィルムには、前記偏光フィルムに1/4波長フィルム
を重ねた円偏光フィルムもあるが、この円偏光フィルム
を用いることで観察角度に依存することなく、潜像を容
易に現出させることが可能となる。
The verification medium used for visualizing the latent image is, specifically, a polarizing film or a polarizing filter. For types of polarizing film and polarizing filter, PV
There are various types such as PVA-iodine type, iodine-absorbed PVA-iodine type, dichroic dye type, metal or metal compound-containing type, polyene type and other high molecular polycrystalline types. What is necessary is just to select one and use it by superimposing it on the latent image recording medium 1 as shown in FIG. In the polarizing film, there is also a circular polarizing film in which a quarter-wave film is superimposed on the polarizing film, but by using the circular polarizing film, a latent image can be easily made to appear without depending on an observation angle. It becomes possible.

【0030】一方、叙述した潜像形成構造層5の上方に
形成されているのが回折形成構造層8である。この回折
形成構造層5はここに照射されて反射されたり、回折さ
れる光が互いに干渉して再生される画像、すなわちホロ
グラム画像や回折格子画像が観察されるようにした構造
層である。
On the other hand, the diffraction forming structure layer 8 is formed above the latent image forming structure layer 5 described above. The diffraction-forming structure layer 5 is a structure layer in which an image reproduced and irradiated with reflected or diffracted light interferes with each other, that is, a hologram image or a diffraction grating image is observed.

【0031】ここで、回折格子画像とは、回折格子から
なる微少セルが複数配置されて構成され、回折格子の空
間周波数、回折格子の方向、各セルの並べ方の少なくと
も何れかを変化させてなる画像構成部分に光を照射した
ときの反射・回折光が互いに干渉して再生される画像で
ある。
Here, the diffraction grating image is constituted by arranging a plurality of minute cells each composed of a diffraction grating, and changing at least one of the spatial frequency of the diffraction grating, the direction of the diffraction grating, and the arrangement of each cell. This is an image reproduced when reflected and diffracted light when the image constituent part is irradiated with light interferes with each other.

【0032】回折形成層7は上述したようにこれらの回
折格子画像やホログラム画像が再生するようにした層
で、ホログラム画像や回折格子画像等を再生させるため
の干渉縞や微少凹凸が安定的に成形可能な材料であれば
使用可能であり、熱プレスによる成形性が良好で、プレ
スムラが生じ難く、明るい再生像が得られるような材料
からなる。例えば、ポリカーボネート樹脂、ポリスチレ
ン樹脂、ポリ塩化ビニル樹脂等の熱可塑性樹脂、不飽和
ポリエステル樹脂、メラミン樹脂、エポキシ樹脂等の熱
硬化性樹脂、あるいはラジカル重合性不飽和基を有する
紫外線や電子線硬化性樹脂の単独或いはこれらの複合材
料により形成すればよい。
As described above, the diffraction forming layer 7 is a layer for reproducing these diffraction grating images and hologram images. The interference fringes and minute unevenness for reproducing the hologram images and diffraction grating images are stably formed. Any material that can be molded can be used, and it is made of a material that has good moldability by hot pressing, hardly causes press unevenness, and can provide a bright reproduced image. For example, thermoplastic resins such as polycarbonate resin, polystyrene resin and polyvinyl chloride resin, thermosetting resins such as unsaturated polyester resin, melamine resin and epoxy resin, or ultraviolet or electron beam curable having radical polymerizable unsaturated groups What is necessary is just to form with resin alone or these composite materials.

【0033】この回折形成層7の下側には必要に応じて
画像再生効果層6が設けてある。この画像再生効果層6
はホログラム画像や回折格子画像の再生時における回折
効率を高め、より鮮明な画像の再生や色の変化が得られ
るようにするために設けるものである。
An image reproducing effect layer 6 is provided below the diffraction forming layer 7 as required. This image reproduction effect layer 6
Is provided to increase the diffraction efficiency during reproduction of a hologram image or diffraction grating image, and to reproduce a clearer image and obtain a change in color.

【0034】この画像再生効果層6はホログラム画像や
回折格子画像等を再生させるための干渉縞や微少凹凸が
形成されている回折形成層7の構成材料よりも屈折率や
反射効果が高く、しかも下部の潜像形成構造層5の存在
が認識できる程度の透明性は少なくとも有する材料で構
成される。
This image reproducing effect layer 6 has a higher refractive index and a higher reflection effect than the constituent material of the diffraction forming layer 7 in which interference fringes for reproducing a hologram image or a diffraction grating image or the like are formed. It is made of a material having at least transparency enough to recognize the existence of the lower latent image forming structure layer 5.

【0035】具体的には、屈折率の異なるTiO2、S
23、SiO、Fe23、ZnS等の高屈折率材料や
より反射効果の高いAl、Sn、Cr、Ni、Cu、A
u等の金属材料が挙げられ、これら材料を単独あるいは
積層して使用できる。この層は真空蒸着法、スパッタリ
ング等の公知の薄膜形成技術にて形成され、その膜厚は
用途によって異なるが、5〜1000nm程度であれば
よい。上記以外でも、画像再生効果層を構成する材料と
しては、その屈折率が、回折形成層7で使用する高分子
材料(屈折率n=1.3〜1.5)よりも高い材料であ
れば、上記の無機材料以外の有機系、有機無機複合体、
有機系材料に無機系フィラーを分散したものであっても
使用可能である。これらの材料によりグラビアコート、
ダイコート、スクリーン印刷等の公知のコーティング
法、や印刷法にて0.1μm〜10μm程度の層厚にて
形成すればよい。さらに、上記以外の材料であっても反
射性と潜像形成構造層中の潜像を確認する際に支障のな
い程度の透明性をを有した材料であれば、適宜使用する
ことが可能である。
Specifically, TiO 2 , S having different refractive indexes
High refractive index materials such as i 2 O 3 , SiO, Fe 2 O 3 , ZnS, and Al, Sn, Cr, Ni, Cu, A
and metal materials such as u, and these materials can be used alone or in a laminated form. This layer is formed by a known thin film forming technique such as a vacuum evaporation method and sputtering, and its thickness varies depending on the application, but may be about 5 to 1000 nm. In addition to the above, as a material constituting the image reproduction effect layer, a material whose refractive index is higher than the polymer material (refractive index n = 1.3 to 1.5) used in the diffraction forming layer 7 is used. , An organic material other than the above inorganic materials, an organic-inorganic composite,
Even a material in which an inorganic filler is dispersed in an organic material can be used. Gravure coat,
It may be formed with a layer thickness of about 0.1 μm to 10 μm by a known coating method such as die coating or screen printing, or a printing method. Further, any material other than the above may be used as long as the material has reflectivity and transparency to the extent that it does not hinder the confirmation of the latent image in the latent image forming structure layer. is there.

【0036】一方、回折形成構造層8上に形成されてい
る保護層9は、潜像記録媒体1を外傷から保護し、また
潜像形成時の熱圧から潜像形成痕による潜像の視認を防
ぐ役割を持つもので、使用される樹脂としては、例え
ば、アクリル系樹脂、ウレタン系樹脂、塩化ビニル樹脂
−酢酸ビニル共重合樹脂、ポリエステル系樹脂、メラミ
ン系樹脂、エポキシ系樹脂、ポリスチレン系樹脂、ポリ
イミド樹脂等の従来公知の熱可塑性樹脂、熱硬化性樹
脂、紫外線または電子線硬化樹脂を単独あるいは、混合
して用いる。
On the other hand, the protective layer 9 formed on the diffraction forming structure layer 8 protects the latent image recording medium 1 from external damage, and visually recognizes the latent image by the latent image forming trace from the heat pressure at the time of forming the latent image. The resin used has the role of preventing, for example, acrylic resin, urethane resin, vinyl chloride resin-vinyl acetate copolymer resin, polyester resin, melamine resin, epoxy resin, polystyrene resin A conventionally known thermoplastic resin such as a polyimide resin, a thermosetting resin, an ultraviolet or electron beam curable resin is used alone or in combination.

【0037】この層には、さらにサーマルヘッド等によ
る潜像形成時の印字痕を残さないようにするための効果
をより高めるために、樹脂を架橋する硬化剤、ポリエチ
レンワッス、カルナバワックス、シリコンワックス等の
ワックス類、あるいは炭酸カルシウム、ステアリン酸亜
鉛、シリカ、アルミナ、タルク等の体質顔料、シリコ−
ン油脂等の油脂類を透明性を損なわない範囲で添加する
ことができる。この保護層9は、例えばグラビア印刷
法、スクリーン印刷法、ノズルコーター法等の既知の塗
布手段やオフセット印刷法、フレキソ印刷法等の印刷手
段等により形成する。
This layer is further provided with a curing agent for cross-linking the resin, polyethylene washes, carnauba wax, silicone, in order to further enhance the effect of not leaving a print mark when a latent image is formed by a thermal head or the like. Waxes such as waxes, extenders such as calcium carbonate, zinc stearate, silica, alumina and talc;
Fats and oils such as oils and fats can be added within a range that does not impair transparency. The protective layer 9 is formed by a known coating means such as a gravure printing method, a screen printing method, a nozzle coater method, or a printing means such as an offset printing method or a flexographic printing method.

【0038】一方、図3は本発明の他の実施の形態に係
る潜像記録媒体30とその使用例を示す説明図である。
この潜像記録媒体30は、図1に示す潜像記録媒体1と
同じように、基材2上に潜像形成構造層5、光透過性を
有する回折形成構造層8ならびに保護層9がこの順序で
積層されている。両者において異なるのは、潜像形成構
造層5を構成する反射層3とサーモトロピック性を示す
高分子材料層4との間、さらには潜像形成構造層5と光
透過性を有する回折形成構造層8との間にアンカー層3
2,33がそれぞれ形成されていると共に、上記した各
層が形成されていない基材面に接着層35が形成されて
いる点である。
FIG. 3 is an explanatory view showing a latent image recording medium 30 according to another embodiment of the present invention and an example of its use.
The latent image recording medium 30 has a latent image forming structure layer 5, a light-transmitting diffraction forming structure layer 8 and a protective layer 9 formed on a base material 2 in the same manner as the latent image recording medium 1 shown in FIG. They are stacked in order. The difference between the two is that the reflective layer 3 constituting the latent image forming structure layer 5 and the polymer material layer 4 exhibiting thermotropic property, and further, the latent image forming structure layer 5 and the diffractive forming structure having optical transparency. Anchor layer 3 between layer 8
2 and 33 are formed, and the adhesive layer 35 is formed on the base material surface on which the above-described layers are not formed.

【0039】アンカー層32、33は、反射層3とサー
モトロピック性を示す高分子材料層4、潜像形成構造層
5と光透過性を有する回折形成構造層8をしっかりと接
着させるために必要に応じて設けるものである。その構
成材料としては熱可塑性樹脂が好ましく、アクリル系樹
脂、ウレタン系樹脂、エポキシ系樹脂、ポリエステル系
樹脂、ビニル系樹脂等の単体或いは共重合体を、単独も
しくは複合して使用可能であるが、必ずしもこれに限定
されるものではない。これらのアンカー材料は、例えば
グラビア印刷法、スクリーン印刷法、ノズルコーター法
等の既知の塗布手段等により塗布する。
The anchor layers 32 and 33 are necessary for firmly adhering the reflective layer 3, the polymer layer 4 exhibiting thermotropic property, the latent image forming structural layer 5 and the diffraction forming structural layer 8 having light transmittance. Are provided according to the conditions. As a constituent material thereof, a thermoplastic resin is preferable, and an acrylic resin, a urethane resin, an epoxy resin, a polyester resin, a vinyl resin or the like can be used alone or in combination. It is not necessarily limited to this. These anchor materials are applied by a known application means such as a gravure printing method, a screen printing method, and a nozzle coater method.

【0040】一方、接着層35は、抽選券、通帳類、鑑
賞券、会員証、パスポート、絵本、ゲーム、キャッシュ
カード、テレホンカード、ICカード等の媒体に貼り付
け、一体化するために形成した層である。図3は媒体3
4にこの接着層35で接着、一体化させたときの状態を
示している。こうすることにより貼り付けた媒体34の
偽造防止効果やコピー防止効果等を更に向上させること
ができる。また、図4のaは図3に示す本発明の潜像記
録媒体30を貼り付けた媒体34の平面図を示してお
り、図4のbはこれを偏光フィルター38を介して観察
しているときの状態を示している。偏光フィルター38
を介して観察すると潜像記録媒体30中に潜像化してあ
った像が現出する。
On the other hand, the adhesive layer 35 is formed so as to be attached to and integrated with a medium such as a lottery ticket, passbooks, appreciation ticket, membership card, passport, picture book, game, cash card, telephone card, IC card and the like. Layer. FIG. 3 shows medium 3
FIG. 4 shows a state when the adhesive layer 35 is bonded and integrated. By doing so, the forgery prevention effect, the copy prevention effect, and the like, of the attached medium 34 can be further improved. 4A shows a plan view of the medium 34 to which the latent image recording medium 30 of the present invention shown in FIG. 3 is attached, and FIG. 4B shows the medium 34 observed through the polarizing filter 38. The state at the time is shown. Polarizing filter 38
Observed through the CPU, the latent image appears in the latent image recording medium 30.

【0041】図5は本発明の潜像記録媒体に偏光フィル
ム43を重ね合わせて潜像形成構造層中の潜像を観察し
ているときの、偏光フィルム43、透明性を有する高分
子材料層41及び反射層42の3層間の光路状態を概念
的に説明した図である。光源46から照射された白色照
射光44は偏光フィルム43を透過して直線偏光とな
り、さらに部分的に分子配向に異方性をもたせた透明性
を有する高分子材料層41を透過していくと楕円偏光に
変わり、蒸着層42により反射される。反射された楕円
偏光は再度偏光フィルム43を透過して透過反射光45
として戻ってくる。この透過反射光45は波長によって
光の強さが異なるため、多彩な色相を有する画像が得ら
れるようになる。また、偏光フィルムの配向方向と分子
配向された高分子材料層との角度によっても見える色相
が異なってくる。
FIG. 5 shows the polarizing film 43 and the transparent polymer material layer when the polarizing film 43 is superimposed on the latent image recording medium of the present invention and the latent image in the latent image forming structure layer is observed. FIG. 4 is a diagram conceptually illustrating an optical path state between three layers 41 and a reflection layer 42. When the white irradiation light 44 emitted from the light source 46 passes through the polarizing film 43 to become linearly polarized light, and further passes through the partially transparent polymer material layer 41 having anisotropy in molecular orientation. The light changes to elliptically polarized light and is reflected by the deposition layer 42. The reflected elliptically polarized light passes through the polarizing film 43 again, and is transmitted and reflected light 45.
Come back as. Since the transmitted and reflected light 45 has different light intensity depending on the wavelength, an image having various hues can be obtained. Further, the visible hue varies depending on the angle between the orientation direction of the polarizing film and the polymer material layer having the molecular orientation.

【0042】[0042]

【実施例】以下、本発明を、具体的な実施例を挙げて詳
細に説明する。 <実施例1>厚さ50μmのポリエチレンテレフタレー
ト(PET)基材の一方の面上に真空蒸着法にて膜厚が
約60nmのAl膜を成膜して金属反射層を形成した。
その上に下記[高分子材料層の組成]からなるサーモト
ロピック性高分子材料インキをグラビア印刷法にて、乾
燥温度60℃、塗布厚0.5μmの条件で塗布し、サー
モトロピック性を示す高分子材料層を形成した。また、
前記基材の他方の面には下記[接着層1の組成]からな
る接着材料インキをグラビア印刷法にて、乾燥温度80
℃、膜厚2.0μmの条件で塗布して接着層とし、高分
子材料媒体を得た。
DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below in detail with reference to specific embodiments. <Example 1> An Al film having a thickness of about 60 nm was formed on one surface of a polyethylene terephthalate (PET) substrate having a thickness of 50 µm by a vacuum evaporation method to form a metal reflection layer.
A thermotropic polymer material ink composed of the following [composition of the polymer material layer] is applied thereon by a gravure printing method under the conditions of a drying temperature of 60 ° C. and a coating thickness of 0.5 μm. A molecular material layer was formed. Also,
On the other surface of the base material, an adhesive material ink composed of the following [composition of the adhesive layer 1] was dried at a drying temperature of 80 by a gravure printing method.
An adhesive layer was formed by coating at a temperature of 2.0 ° C. and a thickness of 2.0 μm to obtain a polymer material medium.

【0043】一方、厚さ25μmの透明PETフィルム
からなる支持体上に、下記[保護層の組成]からなる保
護層材料インキをグラビア印刷法で乾燥温度60℃、膜
厚0.4μmの条件で塗布し、保護層とした。次に、こ
の保護層上に下記[回折形成層の組成]からなる回折形
成層材料インキをグラビア印刷法にて、乾燥温度80
℃、膜厚1.0μmの条件で塗布し、回折形成層を形成
し、回折形成構造層転写箔原反を得た。
On the other hand, on a support made of a transparent PET film having a thickness of 25 μm, a protective layer material ink comprising the following [protective layer composition] was applied by gravure printing at a drying temperature of 60 ° C. and a film thickness of 0.4 μm. It was applied to form a protective layer. Next, on the protective layer, a diffraction forming layer material ink consisting of the following [composition of the diffraction forming layer] is dried at a drying temperature of 80 by a gravure printing method.
The resultant was applied under the conditions of a temperature of 1.0 ° C. and a film thickness of 1.0 μm to form a diffraction-forming layer, thereby obtaining an original transfer foil of a diffraction-forming structure layer.

【0044】次いで、ホログラムレリーフパターンを有
するニッケル製の画像金型を100℃に加熱し、公知の
ロールエンボス法により、回折形成層上に押圧すること
で、ホログラム形成層上にレリーフパターンを形成し
た。上記方法でレリーフパターンを形成した回折形成層
上に、真空蒸着法を用いて膜厚0.05μmのZnSか
らなる蒸着薄膜層を形成して、回折効果層を設けた。次
に、この回折効果層の上に下記[接着層2の組成]から
なる接着層材料インキをグラビア印刷法にて、乾燥温度
80℃、塗布厚2.0μmの条件で塗布して接着層と
し、回折形成構造層転写箔を得た。
Next, a nickel image mold having a hologram relief pattern was heated to 100 ° C. and pressed onto the diffraction layer by a known roll embossing method to form a relief pattern on the hologram layer. . On the diffraction forming layer on which the relief pattern was formed by the above method, a 0.05 μm-thick deposited thin film layer made of ZnS was formed by a vacuum deposition method to provide a diffraction effect layer. Next, an adhesive layer material ink composed of the following [composition of the adhesive layer 2] is applied onto the diffraction effect layer by a gravure printing method at a drying temperature of 80 ° C. and a coating thickness of 2.0 μm to form an adhesive layer. Thus, a transfer foil for a diffraction-formed structure layer was obtained.

【0045】さらに、上記各工程で得られた高分子液晶
媒体と回折形成構造層転写箔をサーモトロピック性を示
す高分子材料層と接着層が接するように重ね、ロール転
写法にて両者を融着させ、次いで回折形成構造層転写箔
の支持体を剥がすことで、本発明の潜像記録媒体を得
た。
Further, the polymer liquid crystal medium obtained in each of the above steps and the diffraction-forming structure layer transfer foil are overlapped so that the polymer layer exhibiting thermotropic property and the adhesive layer are in contact with each other. The latent image recording medium of the present invention was obtained by peeling off the support of the transfer foil for the diffraction forming structure layer.

【0046】この潜像記録媒体のサーモトロピック性を
示す高分子材料層に、120℃、0.2秒間の条件でホ
ットスタンパーにて熱圧をかけて部分的な配向を行い、
潜像を有する本発明の潜像記録媒体を得た。
The polymer layer exhibiting thermotropic property of the latent image recording medium is partially oriented by applying a heat pressure with a hot stamper at 120 ° C. for 0.2 seconds.
A latent image recording medium of the present invention having a latent image was obtained.

【0047】 [高分子液晶層の組成] 高分子液晶(キラコールPLC−7003:旭電化工業(株)製) 20重量部 メチルエチルケトン 80重量部 [接着層1の組成] ポリエステル樹脂 10重量部 アクリル樹脂 10重量部 メチルエチルケトン 40重量部 トルエン 40重量部 [保護層の組成] アクリル樹脂 10重量部 メチルエチルケトン 45重量部 トルエン 45重量部 [回折形成層の組成] 塩化ビニル−酢酸ビニル共重合体 15重量部 ウレタン樹脂 10重量部 メチルエチルケトン 50重量部 トルエン 25重量部 [接着層2の組成] アクリル樹脂 10重量部 ポリエステル樹脂 10重量部 メチルエチルケトン 30重量部 トルエン 50重量部[Composition of polymer liquid crystal layer] Polymer liquid crystal (Kiracol PLC-7003: manufactured by Asahi Denka Kogyo KK) 20 parts by weight Methyl ethyl ketone 80 parts by weight [Composition of adhesive layer 1] Polyester resin 10 parts by weight Acrylic resin 10 Parts by weight methyl ethyl ketone 40 parts by weight toluene 40 parts by weight [composition of protective layer] acrylic resin 10 parts by weight methyl ethyl ketone 45 parts by weight toluene 45 parts by weight [composition of diffraction forming layer] vinyl chloride-vinyl acetate copolymer 15 parts by weight urethane resin 10 Parts by weight methyl ethyl ketone 50 parts by weight toluene 25 parts by weight [composition of adhesive layer 2] acrylic resin 10 parts by weight polyester resin 10 parts by weight methyl ethyl ketone 30 parts by weight toluene 50 parts by weight

【0048】得られた潜像を有する潜像記録媒体は目視
では潜像が全く視認できず、ホログラム画像が観察され
る単なるホログラムフィルムに見えたが、偏光フィルム
を重ねることで潜像化されていたパターンが鮮明に出現
した。
Although the latent image recording medium having the obtained latent image could not be visually recognized at all and the hologram image could be observed as a mere hologram film, the latent image was formed by superimposing a polarizing film. Pattern appeared clearly.

【0049】<実施例2>厚さ50μmのPET基材の
一方の面上に真空蒸着法にて膜厚約60nmのAl膜を
成膜して金属反射層を形成した。その上に下記[アンカ
ー層の組成]からなるアンカー層材料インキをグラビア
印刷法にて、乾燥温度80℃、塗布厚1.0μmの条件
で塗布し、アンカー層を形成した。次に、このアンカー
層上に下記[高分子材料層の組成]からなるサーモトロ
ピック性高分子材料インキをグラビア印刷法にて、乾燥
温度60℃、塗布厚0.5μmの条件で塗布し、サーモ
トロピック性を示す高分子材料層を形成した。また、前
記基材の他方の面には下記[接着層3の組成]からなる
接着材料インキをグラビア印刷法にて、乾燥温度80
℃、膜厚2.0μmの条件で塗布し、接着層を形成し、
高分子材料媒体を得た。
Example 2 An Al film having a thickness of about 60 nm was formed on one surface of a PET base material having a thickness of 50 μm by a vacuum evaporation method to form a metal reflection layer. An anchor layer material ink consisting of the following [composition of anchor layer] was applied thereon by a gravure printing method at a drying temperature of 80 ° C. and a coating thickness of 1.0 μm to form an anchor layer. Next, a thermotropic polymer material ink composed of the following [composition of the polymer material layer] is applied onto the anchor layer by a gravure printing method at a drying temperature of 60 ° C. and a coating thickness of 0.5 μm. A polymer material layer exhibiting tropic properties was formed. On the other surface of the base material, an adhesive material ink composed of the following [composition of the adhesive layer 3] was dried at a drying temperature of 80 by a gravure printing method.
C, applied under the condition of a film thickness of 2.0 μm to form an adhesive layer,
A polymer material medium was obtained.

【0050】一方、厚さ25μmの透明PETフィルム
からなる支持体上に、下記[保護層の組成]からなる保
護層材料インキをグラビア印刷法で乾燥温度80℃、厚
さ1.0μmの条件で塗布し、保護層を形成した。次
に、この保護層上に下記[回折形成層の組成]からなる
回折形成層材料インキをグラビア印刷法にて、乾燥温度
80℃、厚さ2.0μmの条件で塗布し、回折形成層と
し、回折形成構造層転写箔原反を得た。
On the other hand, on a support made of a transparent PET film having a thickness of 25 μm, a protective layer material ink consisting of the following [protective layer composition] was applied by gravure printing at a drying temperature of 80 ° C. and a thickness of 1.0 μm. It was applied to form a protective layer. Next, on the protective layer, a diffraction forming layer material ink composed of the following [Diffraction forming layer composition] is applied by a gravure printing method at a drying temperature of 80 ° C. and a thickness of 2.0 μm to form a diffraction forming layer. Thus, an original transfer foil of the diffraction forming structure layer was obtained.

【0051】次いで、ホログラムレリーフパターンを有
するニッケル製の画像金型を100℃に加熱し、公知の
ロールエンボス法により、回折形成構造層転写箔減反の
回折形成層上に押圧することで、回折形成層上にレリー
フパターンを形成した。上記方法でレリーフパターンを
形成した回折形成層上に、真空蒸着法を用いて膜厚0.
05μmのSi23からなる蒸着薄膜層を形成して回折
効果層(再生画像効果層)を設けた。次に、このホログ
ラム効果層上に下記[接着層4の組成]からなる接着層
材料インキをグラビア印刷法にて、乾燥温度80℃、塗
布厚2.0μmの条件で塗布して接着層とし、回折形成
構造層転写箔を得た。
Next, a nickel image mold having a hologram relief pattern is heated to 100 ° C. and pressed by a known roll embossing method on the diffraction forming layer of the transfer foil of the diffraction forming structure layer, thereby forming a diffraction pattern. A relief pattern was formed on the layer. On the diffraction forming layer on which the relief pattern has been formed by the above method, a film thickness of 0.
It provided a diffraction effect layer (reproduced image effect layer) to form a vapor deposited thin film layer made of Si 2 O 3 of 05Myuemu. Next, on the hologram effect layer, an adhesive layer material ink composed of the following [composition of the adhesive layer 4] is applied by a gravure printing method at a drying temperature of 80 ° C. and a coating thickness of 2.0 μm to form an adhesive layer. A diffraction forming structure layer transfer foil was obtained.

【0052】上記各工程により得られた高分子液晶媒体
と回折形成構造層転写箔をサーモトロピック性を示す高
分子材料層と接着層が互いに接するように重ね、ロール
転写法にて両者を融着させ、しかる後回折形成構造層転
写箔の支持体を剥がすことで、本発明の潜像記録媒体を
得た。
The polymer liquid crystal medium obtained in each of the above steps and the transfer foil for the diffraction-forming structure layer are overlapped with each other so that the polymer material layer having thermotropic property and the adhesive layer are in contact with each other, and they are fused by a roll transfer method. Thereafter, the support of the transfer foil for the diffraction-forming structure layer was peeled off to obtain a latent image recording medium of the present invention.

【0053】この潜像記録媒体媒体のサーモトロピック
を示す高分子材料層に、120℃、0.2秒間の条件で
ホットスタンパーにて熱圧をかけて部分的な配向を行
い、潜像を有する本発明の潜像記録媒体を得た。
The latent image recording medium is partially orientated by applying heat and pressure with a hot stamper at 120 ° C. for 0.2 seconds on the polymer material layer showing the thermotropic property to have a latent image. A latent image recording medium of the present invention was obtained.

【0054】 [高分子液晶層の組成] 高分子液晶(キラコールPLC−7003:旭電化工業(株)製) 20重量部 メチルエチルケトン 80重量部 [接着層3の組成] ポリエステル樹脂 5重量部 アクリル樹脂 15重量部 メチルエチルケトン 40重量部 トルエン 40重量部 [保護層の組成] アクリル樹脂 10重量部 メチルエチルケトン 45重量部 トルエン 45重量部 [回折形成層の組成] アクリルポリオール樹脂 20重量部 ヘキサメチレンジイソシアネート 3重量部 メチルエチルケトン 50重量部 トルエン 27重量部 [接着層4の組成] アクリル樹脂 10重量部 ポリエステル樹脂 10重量部 メチルエチルケトン 30重量部 トルエン 50重量部[Composition of Polymer Liquid Crystal Layer] Polymer liquid crystal (Kiracol PLC-7003: manufactured by Asahi Denka Kogyo KK) 20 parts by weight Methyl ethyl ketone 80 parts by weight [Composition of adhesive layer 3] Polyester resin 5 parts by weight Acrylic resin 15 Parts by weight methyl ethyl ketone 40 parts by weight toluene 40 parts by weight [composition of protective layer] acrylic resin 10 parts by weight methyl ethyl ketone 45 parts by weight toluene 45 parts by weight [composition of diffraction forming layer] acrylic polyol resin 20 parts by weight hexamethylene diisocyanate 3 parts by weight methyl ethyl ketone 50 Parts by weight toluene 27 parts by weight [Composition of adhesive layer 4] acrylic resin 10 parts by weight polyester resin 10 parts by weight methyl ethyl ketone 30 parts by weight toluene 50 parts by weight

【0055】得られた潜像を有する潜像記録媒体は目視
ではそこに内在する潜像が全く視認できず、ホログラム
画像が観察されるだけの単なる回折形成構造フィルムの
ように見えたが、円偏光フィルムを重ねることで角度に
依存しないで所望の画像を鮮明に出現することができ
た。また潜像記録時の痕跡は認めることができなかっ
た。
Although the latent image recording medium having the obtained latent image was visually invisible, the latent image contained therein could not be visually recognized at all, and it looked like a mere diffraction-formed structure film in which only a hologram image was observed. By overlapping the polarizing films, a desired image could be clearly displayed without depending on the angle. Also, no trace at the time of recording the latent image could be recognized.

【0056】[0056]

【発明の効果】以上述べたように、本発明はそのサーモ
トロピックを示す高分子材料層を部分的に配向して潜像
を形成することができ、しかもそれを直接見ただけでは
その所在、内容が全くわからず、しかも潜像化されてい
た画像は偏光フィルム等の使用により簡単に出現させる
ことができる。また、潜像の形成はサーマルヘッドやレ
ーザービーム等により、記録時の痕跡を残すこともな
く、簡単に形成することができる。
As described above, according to the present invention, a latent image can be formed by partially orienting the polymer material layer exhibiting the thermotropic property, and its location can be obtained by directly looking at the latent image. The image whose content is not known at all and which has been turned into a latent image can be easily displayed by using a polarizing film or the like. Further, the latent image can be easily formed by a thermal head or a laser beam without leaving any trace at the time of recording.

【図面の簡単な説明】[Brief description of the drawings]

【図1】本発明の潜像記録媒体の実施の形態を示す概略
断面説明図である。
FIG. 1 is a schematic sectional explanatory view showing an embodiment of a latent image recording medium of the present invention.

【図2】図1に示す潜像記録媒体とその媒体上に偏光フ
ィルムを重ね合わせて潜像化画像を現出させているとき
の状態の説明図である。
FIG. 2 is an explanatory diagram of a state in which a latent image is displayed by superposing a polarizing film on the latent image recording medium shown in FIG. 1 and the medium;

【図3】本発明の他の実施の形態に係る潜像記録媒体と
その使用状態を示す概略断面説明図である。
FIG. 3 is a schematic sectional explanatory view showing a latent image recording medium according to another embodiment of the present invention and a use state thereof.

【図4】図3に示す本発明の潜像記録媒体を貼り付けた
媒体34と、この媒体を偏光フィルターを介して観察し
ているときの状態を示す平面説明図である。
4 is an explanatory plan view showing a medium 34 to which the latent image recording medium of the present invention shown in FIG. 3 is attached, and a state when the medium is observed through a polarizing filter.

【図5】本発明の潜像記録媒体に偏光フィルムを重ね合
わせて潜像形成構造層中の潜像を観察しているときの、
偏光フィルム、透明性を有する高分子材料層及び反射層
の3層間の光路状態を概念的に説明した説明図である。
FIG. 5 shows a state in which a polarizing film is superimposed on the latent image recording medium of the present invention and a latent image in the latent image forming structure layer is observed.
FIG. 3 is an explanatory view conceptually illustrating an optical path state between three layers of a polarizing film, a polymer material layer having transparency, and a reflective layer.

【符号の説明】[Explanation of symbols]

1、30 潜像記録媒体 2 基材 3、42 反射層 4 サーモトロピック性を示す高分子材料
層 5 潜像形成構造層 6 画像再生効果層 7 回折形成層 8 回折形成構造層 9 保護層 22 再生画像 23 偏光フィルム 24 画像 32、33 アンカー層 34 媒体 35 接着層 38 偏光フィルター 43 偏光フィルム 31 円偏光フィルム 44 白色照射光 45 透過反射光 46 光源
DESCRIPTION OF SYMBOLS 1, 30 Latent image recording medium 2 Substrate 3, 42 Reflective layer 4 Polymer material layer showing thermotropic property 5 Latent image forming structure layer 6 Image reproducing effect layer 7 Diffraction forming layer 8 Diffraction forming structure layer 9 Protective layer 22 Reproduction Image 23 Polarizing film 24 Image 32, 33 Anchor layer 34 Medium 35 Adhesive layer 38 Polarizing filter 43 Polarizing film 31 Circular polarizing film 44 White irradiation light 45 Transmitted reflected light 46 Light source

フロントページの続き (51)Int.Cl.7 識別記号 FI テーマコート゛(参考) G02B 5/30 G02B 5/30 G03H 1/18 G03H 1/18 G06K 19/06 G06K 19/00 D 19/077 K Fターム(参考) 2C005 HB02 HB05 HB09 HB12 JB08 JB09 KA37 KA48 LA20 LA30 LB22 2H049 AA02 AA03 AA06 AA12 AA13 AA40 AA43 AA60 AA64 AA66 AA68 BA02 BA03 BA07 BC22 2K008 AA13 CC03 EE04 HH11 HH12 HH18 4F100 AA11 AB01C AB10 AK01C AK15C AK15J AK22C AK22J AK25G AK41G AK42 AL01C AR00B AR00C AR00D AT00A BA03 BA04 BA07 BA10C BA10D BA44C CB00D EC04 EH46 EH66 GB71 GB90 HB08 HB31 JJ10C JL00B JL00C JL11D JN01B JN06C JN18B 5B035 BA03 BB03 BB05 BB09 CA01Of the front page Continued (51) Int.Cl. 7 identification mark FI theme Court Bu (Reference) G02B 5/30 G02B 5/30 G03H 1/18 G03H 1/18 G06K 19/06 G06K 19/00 D 19/077 K F Terms (reference) 2C005 HB02 HB05 HB09 HB12 JB08 JB09 KA37 KA48 LA20 LA30 LB22 2H049 AA02 AA03 AA06 AA12 AA13 AA40 AA43 AA60 AA64 AA66 AA68 BA02 BA03 BA07 BC22 2K008 AA13 H03 H01A01 CCH AK42 AL01C AR00B AR00C AR00D AT00A BA03 BA04 BA07 BA10C BA10D BA44C CB00D EC04 EH46 EH66 GB71 GB90 HB08 HB31 JJ10C JL00B JL00C JL11D JN01B JN06C JN18B 5B035 BA03 BB03 BB05 BB05

Claims (5)

【特許請求の範囲】[Claims] 【請求項1】基材上に、少なくとも潜像形成構造層なら
びに光透過性を有する回折形成構造層がこの順序で積層
されてなり、該潜像形成構造層は少なくとも反射層とサ
ーモトロピック性を示す高分子材料層からなることを特
徴とする潜像記録媒体。
1. A latent image forming structure layer and a light-transmitting diffraction forming structure layer are laminated on a substrate in this order, and the latent image forming structure layer has at least a thermotropic property with a reflective layer. A latent image recording medium comprising a polymer material layer as shown in the following.
【請求項2】光透過性を有する回折形成構造層は、少な
くとも画像再生効果層と回折形成層からなり、かつ回折
形成層の構成材料よりも高い屈折率で、しかも下部の潜
像形成構造層の存在が認識できる程度の透明性は少なく
とも有する構成材料からなることを特徴とする請求項1
に記載の潜像記録材料。
2. The light-transmitting diffraction-forming structure layer comprises at least an image reproduction effect layer and a diffraction-forming layer, has a higher refractive index than the constituent material of the diffraction-forming layer, and has a lower latent image-forming structure layer. 2. A material comprising at least a material having at least transparency enough to recognize the presence of the material.
2. The latent image recording material according to item 1.
【請求項3】潜像形成構造層を構成する反射層は潜像形
成構造層の全面あるいは一部分に設けられ、かつ金属材
料からなることを特徴とする請求項1または請求項2に
記載の潜像記録媒体。
3. The latent image forming structure according to claim 1, wherein the reflective layer constituting the latent image forming structure layer is provided on the entire surface or a part of the latent image forming structure layer, and is made of a metal material. Image recording medium.
【請求項4】サーモトロピック性を示す高分子材料層に
は所望の部分を配向せしめてなる潜像が形成されている
ことを特徴とする請求項1ないし請求項3のいずれか1
項に記載の潜像形成材料。
4. The method according to claim 1, wherein a latent image formed by orienting a desired portion is formed on the polymer material layer exhibiting thermotropic property.
Item. The latent image forming material according to item 1.
【請求項5】基材の潜像形成構造層ならびに光透過性を
有する回折形成構造層が積層されていない側には接着層
が形成されていることを特徴とする請求項1ないし請求
項4のいずれか1項に記載の潜像形成体。
5. An adhesive layer is formed on the side of the substrate on which the latent image forming structure layer and the light transmitting diffraction forming structure layer are not laminated. The latent image forming body according to any one of the above.
JP2001054913A 2001-02-28 2001-02-28 Latent image recording medium Withdrawn JP2002254546A (en)