DE3021377C2 - Perlite-based adsorbent, process for its production and its use - Google Patents
Perlite-based adsorbent, process for its production and its useInfo
- Publication number
- DE3021377C2 DE3021377C2 DE19803021377 DE3021377A DE3021377C2 DE 3021377 C2 DE3021377 C2 DE 3021377C2 DE 19803021377 DE19803021377 DE 19803021377 DE 3021377 A DE3021377 A DE 3021377A DE 3021377 C2 DE3021377 C2 DE 3021377C2
- Authority
- DE
- Germany
- Prior art keywords
- water
- perlite
- adsorbent
- granulate
- binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Die Erfindung betrifft ein Adsorptionsmittel aus körnigem, geblähten und mit einem Überzug versehenen Perlit. Sie betrifft auch ein Verfahren zur Herstellung des Adsorptionsmittels und dessen Verwendung.The invention relates to an adsorbent made of granular, expanded and coated Perlite. It also relates to a method for producing the adsorbent and its use.
Kieselerden, d. h. Diatomeenerden, Bleicherden besitzen hohes Adsorptionsvermögen für färbende Verunreinigungen und Geruchsstoffe, besonders wenn diese Produkte vorher mit Salzsäure ausgekocht, d. h. aktiviert werden. Kieselerden werden als Adsorptionsmittel für Ausscheidungen von Kleintieren verwendet. Außerdem können diese Produkte, wenn sie getrocknet sind, große Mengen von Wasser binden. Chemisch gesehen stellen diese Produkte Magnesium- und Aluminiumsilikate dar. So besteht ein als Katzenstreu verbreitetes Handelsprodukt ausschließlich aus gekörntem Magnesiumsilikat. Magnesiumsilikat Ist im feuchten Zustand eine sehr schwere Masse, die zum Zusammenbacken neigt. Laut Anwendungsvorschrift sollen diese Massen bei der Anwendung in der Kleintiertoilette öfters umgewälzt werden. Dieses Umwälzen mit einem Plastikrechen ist bei teilweise verbrauchtem bzw. wassergesättigtem Magnesiumsilikat sehr schwer durchführbar. Auch bleiben die Käfigböden nicht trocken und sauber.Silica, d. H. Diatomaceous earth and bleaching earth have a high adsorption capacity for coloring impurities and odorous substances, especially if these products are previously boiled with hydrochloric acid, d. H. activated will. Silica is used as an adsorbent for excretions from small animals. aside from that these products can bind large amounts of water once they have dried. Put chemically these products are magnesium and aluminum silicates. There is a common commercial product as cat litter made exclusively from granular magnesium silicate. Magnesium silicate is a very when moist heavy mass that tends to stick together. According to the instructions for use, these masses should be used in the When used in the small animal toilet, it must be turned over frequently. This tumbling with a plastic rake is at partially used or water-saturated magnesium silicate is very difficult to carry out. They stay too Cage floors are not dry and clean.
Bei einem bekannten (DE-AS 15 19 800) Adsorptionsmittel der eingangs genannten Art ist der Überzug eine
dünne, auf den geblähten Perllten aufgesprühte Schicht aus Silikon-Emulsion, die den Eintritt von Wasser in
den Perlltkern verhindern soll. Dieses Adsorptionsmittel dient zur Beseitigung von Ölen und Fetten. Es ist auch
bekannt (DE-AS 19 29 828), Körner aus Perlit mit Kunststoff zu überziehen, um den Wasserfaktor zu verringern,
damit das Granulat in verbesserter Weise als Leichtbaustoff verwendbar ist. Es gibt auch ein Adsorptionsmittel
(DE-AS 12 54 591), bei dem aufgelöstes und wiedergetrocknetes faserartiges Silikat mit Kalk überzogen
ist.
Aufgabe der Erfindung ist es nun, ein Adsorptionsmittel der eingangs genannten Art zu schaffen, das einerselts
ebenso wie das bekannte Magnesiumsilikat ein hohes Adsorptionsvermögen für färbende Verunreinigungen,
Geruchsstoffe und Wasser hat und andererseits auch Im wassergesättigten Zustand eine lockere, nicht
klebende Masse 1st. Die Erfindung löst diese Aufgabe durch ein Adsorptionsmittel der eingangs genannten Art,
das dadurch gekennzeichnet ist, daß der Überzug ein als Bindemittel wirkendes Silikat oder Sulfat ist.
Erfindungsgemäß umhüllte Perlite sind auch im wassergesättigten Zustand noch leicht umwälzbar und als f
lockere, nicht klebende Masse leicht aus Tierställen zu entfernen. Sie sind als Aufsaugmittel für Ausscheidungen
von Kleintieren anwendbar. Käfigböden bleiben im Gegensatz zu Magnesiumsilikat trocken und sauber.
Erfindungsgemäß umhüllte Perlite verhalten sich neutral, führen beim Tier zu keinerlei Reizerscheinungen und
werden vom Versuchstier als Toilette sofort angenommen.
Geblähte und ummantelte Perlite besitzen den Magnesium- und Magnesium-Aluminiumsilikaten entsprechende
Eigenschaften, insbesondere ähnlich gute Adsorptionseigenschaften gegenüber Geruchsstoffen und
Wasser bzw. Abwasser. Gewichtsmäßig miteinander verglichen sind gipsumhüllte Perlite In bezug auf Aufnahmefähigkeit
von tierischen Ausscheidungen und Geruchsblndung genauso wirksam und gebrauchsfähig wie das
bereits verwendete gekörnte Magnesiumsilikat. Da das erfindungsgemäße Granulat voluminöser als gekörntes
Magnesiumsilikat ist, können vorgegebene Räume mit gewichtsmäßig weniger Material gefüllt werden.In a known (DE-AS 15 19 800) adsorbent of the type mentioned, the coating is a thin layer of silicone emulsion which is sprayed onto the puffed pearls and is intended to prevent water from entering the pearl core. This adsorbent is used to remove oils and fats. It is also known (DE-AS 19 29 828) to coat grains of perlite with plastic in order to reduce the water factor so that the granulate can be used in an improved manner as a lightweight building material. There is also an adsorbent (DE-AS 12 54 591) in which dissolved and redried fibrous silicate is coated with lime.
The object of the invention is to create an adsorbent of the type mentioned at the outset which, like the well-known magnesium silicate, has a high adsorption capacity for coloring impurities, odorous substances and water and, on the other hand, is a loose, non-sticky mass even when saturated with water. The invention solves this problem by means of an adsorbent of the type mentioned at the beginning, which is characterized in that the coating is a silicate or sulfate which acts as a binding agent.
Perlites encased according to the invention can still be easily circulated even in the water-saturated state and, as a loose, non-sticky mass, can be easily removed from animal stalls. They can be used as absorbents for excretions from small animals. In contrast to magnesium silicate, cage floors stay dry and clean. Perlites coated according to the invention behave neutrally, do not cause any irritation in the animal and are immediately accepted as a toilet by the test animal.
Expanded and coated perlites have properties corresponding to those of magnesium and magnesium aluminum silicates, in particular similar good adsorption properties with regard to odorous substances and water or waste water. In terms of weight, gypsum-coated perlites are just as effective and usable as the granular magnesium silicate that has already been used in terms of their ability to absorb animal excretions and unpleasant odors. Since the granulate according to the invention is more voluminous than granular magnesium silicate, predetermined spaces can be filled with less material in terms of weight.
Perlite, auch Perlit genannt, sind die Llparit- oder Quarzporphyrgläser mit vielen kleinen Wassereinschlüssen. Dieser wasserhaltige Rohperlit wird auf 1 100-1 3000C erhitzt und expandiert zu aufgeblähtem Perlit mit zwanzigfachem Volumen. Dieser Gesteinsschaum ist für den vorliegenden Verwendungszweck seiner Leichtigkeit wegen an sich unbrauchbar und wird durch die erfindungsgemäß vorgesehene Ummantelung schwer gemacht, so daß ein ausreichend schweres Granulat vorliegt. Bei dem Granulat weist vorzugsweise jede Granalie einen Perlitkern auf, der vom Mantel umgeben Ist, oder es sind sehr feinkörnige geblähte Perlite mit dem Ummantelungsmaterial zu stückigen Granulaten aufgearbeitet.Perlite, also known as perlite, are the parite or quartz porphyry glasses with many small water inclusions. This water-containing raw perlite is heated to 1100-1300 0 C and expanded to an inflated perlite twenty times volume. This rock foam is per se unusable for the present purpose because of its lightness and is made heavy by the casing provided according to the invention, so that a sufficiently heavy granulate is present. In the case of the granules, each granule preferably has a perlite core which is surrounded by the jacket, or very fine-grained expanded perlites are worked up with the jacket material to form lumpy granules.
Die Umhüllung bzw. der Mantel erhöht noch die Aufnahmefähigkeit des Granulates, wenn das Bindemittel
des Mantels noch unabgebundene Reste enthält, also ebenfalls noch Wasser aufnehmen kann. Wenft der Mantel
aus Calciumsulfat-Halbhydrat hergestellt wird, dann Ist er In der Regel fast vollständig, z. B. zu 95% abgebunden;
wenn der Mantel aber aus Anhydrit hergestellt wird, dann kann der Mantel von 5 bis 9596 Anhydrit enthalten.
Durch nicht abgebundene Bestandteile des Mantels wird die Saugfähigkeit des Mantels erhöht. Der Mantel
macht das Material aus geblähtem Perlit schwerer und bindet feinen Perlitstaub.
Für die Erfindung sind die Eigenschaften des Perlitkornes wichtig. Dieses Korn läßt sich, wenn es feucht ist,The covering or the jacket increases the absorption capacity of the granulate if the binding agent of the jacket still contains unbound residues, that is to say it can also absorb water. If the coat is made from calcium sulfate hemihydrate, then it is usually almost completely, e.g. B. 95% set; but if the jacket is made of anhydrite, then the jacket can contain from 5 to 9596 anhydrite. The absorbency of the jacket is increased by components of the jacket that have not set. The jacket makes the expanded perlite material heavier and binds fine perlite dust.
The properties of the pearlite grain are important for the invention. This grain can, when it is damp,
nicht zerdrücken, d. h. es bleibt fest, wenn es vollgesaugt 1st. Das Mantelmaterial, insbesondere Gips, haftet am Perlitkorn sehr gut. Es liegen zumeist regelrechte Teilchen mit guter Stabilität vor. Die Ummantelung der Körner läßt sich erleichtert durchführen. Die geblähten Perlite besitzen eine Hohlstruktur und bilden ein ausreichend grobes Korn, d. h. sie sind nicht durchweg pulverig. Die Körner aus geblähtem Perlit bilden jeweils Hohlräume, die von dem Manie! nicht ausgefüllt sondern überdeckt sind.do not crush, d. H. it sticks when it's soaked. The jacket material, especially plaster of paris, adheres to the Pearlite grain very good. There are mostly regular particles with good stability. The sheathing of the Körner can be carried out more easily. The expanded perlites have a hollow structure and form a sufficient amount coarse grain, d. H. they are not all powdery. The grains of expanded perlite each form cavities, the mania! are not filled in but covered.
Das Bindemittel ist z. B. silikatisch, d. h. abgebundener Zement, da Zement ausreichend schnell bei Ummanteln abbindet. Jedoch könnte Zement infolge Alkalitat gegebenenfalls zu Reizerscheinungen am Tier führen. Deshalb ist ein sulphatisches Bindemittel bevorzugt, das praktisch neutral reagiert. Dabei ist es für die Aufnahmefähigkeit von Wasser von Vorteil, wenn der Mantel zu einem Teil aus abgebundenem Gips und etwas Kalziumsulphat-Haibhydrat oder Anhydrit besteht. ΌThe binder is e.g. B. silicate, d. H. Cement that has set, as cement is sufficiently quick to coat sets. However, due to the alkalinity, cement could cause irritation to the animal. A sulphate binder is therefore preferred, which reacts practically neutrally. Thereby it is for the receptivity Water is an advantage if the coat is partly made up of hardened plaster of paris and some calcium sulphate shark hydrate or anhydrite. Ό
Bei dem erfindungsgemäßen Granulat sind feinkörnige Perlitteile weitgehend gebunden. Daher ist es eine besondere vorteilhafte und zweckmäßige Eigenschaft des erfindungsgemäßen Adsorptionsgranulates, wenn mindestens 6596, vorzugsweise mindestens 70% der Granallen eine Körnung größer 1,25 mm besitzen. Eine solche Körnung ist auch für den erfindungsgemäßen Verwendungszweck besonders geeignet.In the case of the granulate according to the invention, fine-grained pearlite parts are largely bound. Hence it is one particularly advantageous and expedient property of the adsorption granules according to the invention, if at least 6596, preferably at least 70% of the granules have a grain size greater than 1.25 mm. One such grain size is also particularly suitable for the purpose according to the invention.
Die pro Gewichtseinheit Perlit vorgesehene Menge an Bindemittel richtet sich primär danach, wie schwer das Granulat letztlich sein soll. Besonders zweckmäßig und vorteilhaft ist es, wenn das Gewichtsverhältnis von Perlit: Mantel-Bindemittel von 1 : 1,9 bis 1 :5,0 und vorzugsweise ca. 1 :3,8 beträgt. Hierbei ist das Granulat ausreichend schwer und die Dicke de: Ummantelung derart, daß die Adsorptionsfähigkeit der Granalien nicht allzu stark beeinträchtigt ist. Die Manteldicke beträgt bei einem in der Praxis brauchbaren Granulat von 0,5 mm bis 1,5 mm, vorzugsweise ca. 1 mm.The amount of binding agent per unit weight of perlite depends primarily on how difficult it is Granulate should ultimately be. It is particularly useful and advantageous if the weight ratio of Perlite: cladding binder is from 1: 1.9 to 1: 5.0 and preferably about 1: 3.8. Here is the granulate sufficiently heavy and the thickness de: coating such that the adsorption capacity of the granules is not is too badly affected. In the case of granules which can be used in practice, the jacket thickness is 0.5 mm up to 1.5 mm, preferably approx. 1 mm.
Es ist bekannt (DE-AS 12 54 591), zwecks Herstellung eines Adsorptionsgranulates Silikatteilchen in eine Kalksuspension zu tauchen und anschließend zu brennen, um eine Oberflächenschicht aus Kalk zu erreichen. Diese Verfahrensweise ist wegen des Brennens recht umständlich und zeitaufwendig. Auch ergibt die Anwendung dieser Verfahrensweise auf die Herstellung des erfindungsgemäßen Granulates kein befriedigendes Produkt. 2S It is known (DE-AS 12 54 591) to immerse silicate particles in a lime suspension for the purpose of producing adsorption granules and then to burn them in order to achieve a surface layer of lime. This procedure is quite cumbersome and time-consuming because of the firing. The application of this procedure to the production of the granulate according to the invention also does not result in a satisfactory product. 2S
Die Erfindung sieht daher ein Verfahren der eingangs genannten Art vor, das dadurch gekennzeichnet ist, daß die Perlitkörner unter Mischen zunächst mit Wasser besprüht werden und dann gleichmäßig mit dem Bindemittel bestreut werden. Dieses Verfahren ist einfach und zeltsparend durchzuführen. Dabei ist sichergestellt, daß jedes Perlitkorn von dem Bindemittel vollständig ummantelt wird. Durch die richtige Dosierung des Wassers läßt sich erreichen, daß nur der erwünschte Anteil des Bindemittels abbilndet.The invention therefore provides a method of the type mentioned at the outset, which is characterized in that that the pearlite grains are first sprayed with water while mixing and then evenly with the Binders are sprinkled. This procedure is simple and time-saving to carry out. It is ensured that that each pearlite grain is completely covered by the binder. With the correct dosage of the Water can ensure that only the desired proportion of the binder is formed.
! Z. B. wird auf eine Menge von Körnern aus geblähtem Perlit, die ständig gerührt wird, eine wäßrige Lösung! For example, an aqueous solution is applied to a quantity of expanded perlite grains which are kept being stirred
von Eisenkallumsulfat in der erforderlichen Menge aufgesprüht. Sofort danach wird in der erforderlichen Menge
Anhydrit (CaSO4) darüber gepudert. Die Mengen richten sich danach, daß ein Mantel mit einem ausreichenden
Gehalt an Dihydrat entsteht, der dem Mantel die erforderliche Festigkeit gibt.
\ Besonders zweckmäßig und vorteilhaft ist es, wenn nach dem Bestreuen mit Bindemittel unter weiteremsprayed with iron kallum sulfate in the required amount. Immediately afterwards, the required amount of anhydrite (CaSO 4 ) is powdered over it. The amounts depend on the fact that a jacket is formed with a sufficient content of dihydrate to give the jacket the required strength.
\ It is particularly useful and advantageous if, after sprinkling with binding agent, among other things
Mischen nochmals mit Wasser besprüht wird. Durch das zuerst aufgesprühte Wasser wird ein Haften des Bindemittel-Puders an den Perlitkörnem erreicht. Das zweite Aufsprühen von Wasser erfolgt in dem Maß, in dem das aufgestreute Bindemittel schließlich abgebunden sein soll.Mix again is sprayed with water. The first sprayed water causes the binder powder to adhere reached on the pearlite grains. The second spray of water is done to the extent that the scattered binding agent should finally be set.
Beispielhafte Herstellung eines erfindungsgemäßen Adsorptionsgranulates unter Verwendung von Gips. 40 1 (3,2 kg) geblähte Perlite der Körnung 0-6 mm und dem Schüttgewicht 80 g/l werden in einer rotierenden Granuliertrommel mit 375-750 ml Wasser besprüht. Das Wasser wird in feinen Tröpfchen aufgesprüht. Danach werden auf die vorbefeuchtete, rotierende Perlitmasse 6-12 kg Stuckgips (Kalziumsulfat-Halbhydrat) gleichmäßig aufgestreut.Exemplary production of adsorption granules according to the invention using plaster of paris. 40 1 (3.2 kg) expanded perlite with a grain size of 0-6 mm and a bulk density of 80 g / l are in a rotating Granulating drum sprayed with 375-750 ml of water. The water is sprayed on in fine droplets. Thereafter Apply 6-12 kg of stucco (calcium sulfate hemihydrate) evenly to the pre-moistened, rotating perlite mass scattered.
Nach dem vollständigen Aufstreuen des Stuckgipses werden nochmals 1125-2250ml Wasser zwecks Abbindung des Stuckgipses auf die schon gebildeten Perlitgranallen fein aufgesprüht. Man erhält ein festes, trockenes, nur gering staubendes gipsumhülltes Perlltgranulat mit einem SchtUtgewicht von ca. 200-300 g/l. Falls vollständig Staubfreiheit gewünscht wird, setzt man dem zugesprühten Wasser etwas Glyzerin oder einen anderen Polyalkohol zu.After the stucco has been completely sprinkled on, 1125-2250ml of water are used again for the purpose of setting of the plaster of paris finely sprayed onto the already formed perlite granules. A firm, dry, Gypsum-coated pearl granulate with a bulk weight of approx. 200-300 g / l only generates a low level of dust. If complete If you want to be free of dust, add a little glycerine or something else to the sprayed water Polyalcohol too.
Es wird soviel Stuckgips angewendet, daß das Perlitkorn von dem Gips vollständig umhüllt und das gewünschte Schüttgewicht erreicht wird. Außerdem 1st ein Überschuß an eingesprühtem Wasser zu vermeiden, da der Überschuß sonst dann bei 45-55° wieder durch Trocknung entfernt werden müßte. Es hat sich in bezug auf die Aufnahmefähigkeit von Wasser als vorteilhaft erwiesen, daß mit einem Wasser-Gips-Verhältnis von 0,25 gearbeitet wird, wobei z. B. auf 100 kg Gips 25 kg Wasser verarbeitet werden.So much plaster of paris is used that the perlite grain is completely covered by the plaster and that desired bulk density is achieved. In addition, an excess of sprayed water is to be avoided, otherwise the excess would have to be removed again by drying at 45-55 °. It has to be related on the absorption capacity of water proved to be advantageous that with a water-gypsum ratio of 0.25 is worked, with z. B. 25 kg of water can be processed for 100 kg of plaster of paris.
Vergleich eines erfindungsgemäßen Perlitgranulates mit bekannten körnigem MagnesiumsilikatComparison of a perlite granulate according to the invention with known granular magnesium silicate
1S1S
Fortsetzungcontinuation
Perlitgranulat Magnesiumsilikat
gekörntPerlite granulate magnesium silicate
grained
Wasseraufnahmefähigkeit*) (gH20) 119,6 119,6Water absorbency *) (gH 2 0) 119.6 119.6
bei Volumenat volume
AdsorptionsmittelAdsorbent
(ml) 400 211(ml) 400 211
und Gewicht
Adsorptionsmitteland weight
Adsorbent
(g) no no(g) no no
Vergleich von granuliertem Perlite mit gekörntem
-,ο ' MagnesiumsilikatComparison of granulated perlite with granular
-, ο 'magnesium silicate
*) Bestimmung der Wasseraufnahmefähigkeit: HOg zu*) Determination of the water absorption capacity: HOg to
' prüfende Substanz werden in einen Zylinder gefüllt'Test substance are filled into a cylinder
Dieser Zylinder ist am Boden mit einem Sieb verschlossen. Von oben wird die zu prüfende Substanz mitThis cylinder is closed with a sieve at the bottom. The substance to be tested is shown from above
250 ml Wasser übergössen. Gemessen wird die auslauPour over 250 ml of water. The endurance is measured
fende Wassermenge in ml.amount of water in ml.
Nachfolgend eine Durchschnittsanalyse von Perlite und MagnesiumsilikatBelow is an average analysis of perlite and magnesium silicate
3030th
Es wird nun das Adsorptionsmittel der DE-AS 12 54 591 mit dem erfindungsgemäßen Adsorptionsmittel verglichen. Dazu wird gemahlene Steinwolle, wie In der DE-AS 12 54 591 beschrieben, in Wasserglas gelöst. Es wird eine homogene, glasklare Lösung bzw. Schmelze erhalten. Die auf Restwassergehalte von 5 bis 2096 getrocknete Schmelze wird gemahlen und die Korngröße 0,5-2,0 mm ausgesiebt. Das ausgesiebte Vorprodukt mit der Körnung 0,5-2,0 mm wird nach Vorschrift in eine Kalksuspension getaucht, wobei die einzelnen Körnchen rasch stark angelöst werden und zum Verkleben neigen. Das Expandieren der mit Kalkmilch behandelten so Silikatteilchen geschieht in einem Ofen bei 600-900° C. Auch beim Aufblähen kommt es wieder zu starken Verklebungen und Verbackungen. Am besten kann aufgebläht werden, wenn nur einzelne Teilchen, die sich nicht berühren, der Hitze ausgesetzt werden.It is now the adsorbent of DE-AS 12 54 591 with the adsorbent according to the invention compared. For this purpose, ground rock wool, as described in DE-AS 12 54 591, is dissolved in water glass. It a homogeneous, crystal-clear solution or melt is obtained. The residual water content from 5 to 2096 The dried melt is ground and the grain size 0.5-2.0 mm is sieved out. The pre-screened product with a grain size of 0.5-2.0 mm is dipped into a lime suspension according to the instructions, with the individual grains are quickly dissolved and tend to stick together. Expanding those treated with milk of lime so silicate particles happens in an oven at 600-900 ° C. Even when puffing it comes back to strong Bonding and caking. It can be best bloated when only individual particles are in place do not touch, be exposed to heat.
Der Blähvorgang gestaltet sich sehr aufwendig und kann mit der rationellen Fertigung des anmeldungsgemäßen
Adsorptionsmittels in keiner Weise konkurrieren. Die erhaltenen Granalien sind außerdem sehr instabil,
mehlen stark ab und lassen sich trotz Kalkhaut sehr leicht zerdrücken. Werden die Granallen nach der Kalkbehandlung
und nach dem Blähen mit Wasser benetzt, so kommt es rasch zu einem Ablösen der Kalkummantelung.
Ein Effekt, der bei dem nach dem erfindungsgemäßen Verfahren hergestellten Adsorptionsmittel nicht
eintritt.
Über die erhaltenen Ergebnisse gibt nachstehende Tabelle Auskunft:The expansion process is very complex and can in no way compete with the efficient production of the adsorbent according to the application. The granules obtained are also very unstable, flour heavily and can be crushed very easily despite the calcareous skin. If the granules are wetted with water after the lime treatment and after the expansion, the lime coating will quickly peel off. An effect which does not occur with the adsorbent produced by the process according to the invention.
The table below provides information about the results obtained:
MlMl
Versuch-Nr. Schüttgewicht WasseraufnahmefähigkeitExperiment no. Bulk density water absorption capacity
Ij (g/l) (g Wasser pro (g Wasser proIj (g / l) (g water per (g water per
f ! I Produkt) 1 kg Produkt)f! I product) 1 kg product)
(,5 : (, 5:
u 1 42 235 3700 u 1 42 235 3700
% 2 53 240 4500 % 2 53 240 4500
*) Die Angaben der Durchschnitlsanalyse betreffenden Tabelle sind jeweils auf die BezugsgröBe 11 bzw. 1 kg absorbierende Substanz umgerechnet.*) The information in the table relating to the average analysis is based on the reference size 11 or 1 kg converted to absorbent substance.
Interpretation der TabelleInterpretation of the table
Es ist verständlich, daß das Aufnahmevermögen des Granulates gemäß DE-AS 12 54 591 für Flüssigkeiten, gewichtsmäßig verglichen, höher ist, da die Schüttgewichte enorm niedrig liegen, d. h. 1 kg Produkt ein Volumen von ca. 16-24 Liter hat und dadurch eine entsprechend hohe Oberfläche für die Adsorption von Flüssigkeiten bietet.It is understandable that the absorption capacity of the granules according to DE-AS 12 54 591 for liquids, compared by weight, is higher because the bulk weights are extremely low, i.e. H. 1 kg of product one volume of approx. 16-24 liters and therefore a correspondingly high surface area for the adsorption of liquids offers.
Vergleicht man aber die Volumina des erfindungsgemäßen Adsorptionsmittels und des Produktes gemäß DE-AS 12 54 591, so schneidet das nach dem erfindungsgemäßen Verfahren hergestellte Adsorptionsgranulat gut ab. Ein Liter erfindungsgemäßes Adsorptionsgranulat bindet 299 g Flüssigkeit, während 1 Liter Granulat gemäß DE-AS 12 54 591 nur 195-24Og Flüssigkeit aufnimmt. In der Praxis kommt es schließlich auf die Wasseraufnahmefähigkeit nach Volumen an. Keine handelsübliche Kleintiertoilette faßt 24 Liter Granulat. Es kommt darauf an, daß ein bestimmtes Volumen eines Adsorptionsgranulates, in der Praxis meist 5 Liter, eine maximale Menge an Flüssigkeit aufnimmt. Kleintiertoiletten werden nach Volumen gefüllt und nicht nach Gewicht.But if one compares the volumes of the adsorbent according to the invention and the product according to DE-AS 12 54 591 cuts the adsorption granules produced by the process according to the invention good. One liter of adsorption granules according to the invention binds 299 g of liquid, while 1 liter of granules according to DE-AS 12 54 591 only absorbs 195-24Og of liquid. In practice, it ultimately comes down to that Water absorbency according to volume. No commercially available small animal toilet holds 24 liters of granulate. It depends on the fact that a certain volume of an adsorption granulate, in practice usually 5 liters, a absorbs maximum amount of fluid. Small animal toilets are filled by volume, not by volume Weight.
Der Verwendung eines Granulates gemäß DE-AS 12 54 591 in Kleintiertoiletten stehen folgende Gründe entgegen:The use of a granulate according to DE-AS 12 54 591 in small animal toilets is due to the following reasons opposite:
1. Das Granulat 1st viel zu leicht, das Schüttgewichl zu gering. Es fliegt beim Scharren des Tieres aus der Toilette und verunreinigt die Wohnung.1. The granulate is much too light, the bulk weight too low. It flies out when the animal scratches Toilet and pollutes the apartment.
2. Das Granulat ist instabil und leicht zerdrückbar. Das Tier sinkt in der Toilette ein.2. The granulate is unstable and easy to crush. The animal sinks into the toilet.
3. Das Granulat ist stark abmehlend. Das Tier bekommt weiße Pfoten und verunreinigt die Wohnung.3. The granulate is very powdery. The animal gets white paws and contaminates the apartment.
4. Der Kalkmantel löst sich beim Anfeuchten ab. Das Granulat zerfällt dann leicht. Es bildet sich ein »Brei« in der Toilette.4. The lime coat comes off when moistened. The granulate then disintegrates easily. A "pulp" forms in the toilet.
Claims (6)