CN1831064A - Two-component acid-cured termide-proof and insect-proof putty and its application - Google Patents

Two-component acid-cured termide-proof and insect-proof putty and its application Download PDF

Info

Publication number
CN1831064A
CN1831064A CN 200510024316 CN200510024316A CN1831064A CN 1831064 A CN1831064 A CN 1831064A CN 200510024316 CN200510024316 CN 200510024316 CN 200510024316 A CN200510024316 A CN 200510024316A CN 1831064 A CN1831064 A CN 1831064A
Authority
CN
China
Prior art keywords
proof
insect
termide
parts
putty
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200510024316
Other languages
Chinese (zh)
Other versions
CN100547043C (en
Inventor
陈寿生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Zhanchen Paint Co ltd
Zhuhai Zhanchen New Material Co Ltd
Original Assignee
SHENZHEN ZHANCHENDA CHEMICAL INDUSTRY Co Ltd
Shanghai Fuchen Chemical Co Ltd
Beijing Zhanchen Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHENZHEN ZHANCHENDA CHEMICAL INDUSTRY Co Ltd, Shanghai Fuchen Chemical Co Ltd, Beijing Zhanchen Chemical Co Ltd filed Critical SHENZHEN ZHANCHENDA CHEMICAL INDUSTRY Co Ltd
Priority to CNB2005100243165A priority Critical patent/CN100547043C/en
Publication of CN1831064A publication Critical patent/CN1831064A/en
Application granted granted Critical
Publication of CN100547043C publication Critical patent/CN100547043C/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

This invention discloses a two-group acid solidifying termite-proof and bug-proof putty and its application. The filming matter(alkyd resin and aminoresin, etc.), special bug-proof agent, solution, gas phase silicon dioxide, talcum powder, disintagrated chalk, curing agent in the receipt are used in painting dressing process of furniture and plank floor to form termite and bug proof putty film to prevent termite and other bristletail to erode carpentry. The advantages are high efficiency, good decoration effect.Its termite and bug-proof efficiency is 1 level.

Description

Two component acid cure termide-proof and insect-proof putty and application thereof
Technical field
The present invention relates to a kind of solvent-borne type woodwork coating, relate in particular to two component acid cure putty.
Background technology
At present, the timber termide-proof and insect-proof is handled mainly based on infusion method and squeegee process, being about to timber is immersed in the solution that contains medicine, the solution brushing that maybe will contain medicine is on wood surface, as patent low temperature normal temperature quick-drying putty, 93107061.9 and document MA transparent woodenware priming paint of series and putty (" New Building Materials ", 2002,2); The technology of report, its shortcoming is that medicine easily runs off, duration of efficacy is short; Medicine is harmful, environmental pollution; Behind the solution of wood surface brushing medicine, influenced lacquer decorations effect to wood surface.Therefore, the termide-proof and insect-proof pesticide application technology of present timber or plank can not be applicable to the application and the decoration design for residence of modern wooden furniture.
Summary of the invention
The technical issues that need to address of the present invention are to disclose a kind of pair of component acid cure termide-proof and insect-proof putty and application thereof, to overcome above-mentioned the deficiencies in the prior art.
Of the present invention pair of component acid cure termide-proof and insect-proof putty is made up of host and solidifying agent, and the weight ratio of host and solidifying agent is:
Host: solidifying agent=1: 0.3～0.7.
The component and the parts by weight of host comprise:
25～35 parts of Synolac
0.1～0.5 part of wetting agent
8～16 parts of solvents
0.5～2.5 part of anti-settling agent
16～26 parts in aminoresin
28～38 parts of talcum powder
0.5～4.5 part of insect-proof agent
It is the product of DA2272-70 that said Synolac can adopt the turtle power trade Co., Ltd trade mark;
Said wetting agent is unsaturated polycarboxylic acid polymkeric substance of lower molecular weight and polysiloxane interpolymer solution, and can adopt German Bi Ke (BYK) the company trade mark is the product of BYK P104S;
Said solvent is selected from conventional organic solvent such as toluene, dimethylbenzene;
Said anti-settling agent is an aerosil, and optional is the product of M-5 with the Shanghai Cabot chemical industry company limited trade mark;
The said aminoresin preferably Guangzhou Ya Xin trade Co., Ltd trade mark is the product of 107AM-65;
Said talcous fineness is 800～1200;
Said insect-proof agent is selected from a kind of or its mixture in the white spirit of pyrethroid, stuck gram missible oil or silicon (chemical name is 4-phenelyl [3-(4-fluoro-3-phenoxy phenyl) propyl group] dimethylsilane), can select the Guangdong Province Insects Research Institute for use, Britain Shell Co. Ltd, the product of Japan Pyrethrum Co., Ltd;
The component and the parts by weight of solidifying agent comprise:
18～30 parts of tosic acid, 40～50 parts of propyl carbinols, 25～35 parts of toluene.
The preparation method of of the present invention pair of component acid cure termide-proof and insect-proof putty is foolproof, each component of host is proportionally mixed, obtain host, each component of solidifying agent is proportionally mixed, obtain solidifying agent, with host and solidifying agent according to above-mentioned mixed, acquisition putty, with brush and the method for blade coating with woodwork closed allround such as wooden furniture, timber floors, get final product.
Of the present invention pair of component acid cure termide-proof and insect-proof putty can be used for the woodenware pre-treatment of modern wooden furniture application and the woodenware pre-treatment of decoration design for residence.
The present invention mainly utilizes filmogen (Synolac, aminoresin etc.) in the prescription, special efficacy insect-proof agent (pyrethroid or other insect-proof agent), solvent, aerosil, talcum powder, coatings additive(s), solidifying agent etc., in the coating process of woodworks such as furniture, timber floor, form the termide-proof and insect-proof putty membrane, thereby stop termite and of the moth erosion of other moth woodenware.Have advantages such as termide-proof and insect-proof efficient height, decorative effect are good, easy construction, can be used for the woodenware pre-treatment of modern wooden furniture application and the woodenware pre-treatment of decoration design for residence.Adopt GB/T 18260-2000 " wood preservative is to termite toxic effect test method " to detect, termide-proof and insect-proof efficient is 1 grade.
Embodiment
Embodiment 1
Host
Sequence number Title Weight, kilogram
1 Synolac (DA2272-70) 30
2 Wetting agent (BYK P104S, unsaturated polycarboxylic acid polymkeric substance of lower molecular weight and polysiloxane interpolymer solution) 0.2
3 Solvent (toluene) 7
4 Anti-settling agent (M-5, aerosil) 2
5 Aminoresin (107AM-65) 24
6 1000 order talcum powder 34.8
7 Pyrethroid (effective cypermethrin) 2
Add up to 100
Solidifying agent
Sequence number Title Weight, kilogram
1 Tosic acid 22
2 Propyl carbinol 47
3 Toluene 31
Add up to 100
Each component of host is proportionally mixed, obtain host, each component of solidifying agent is proportionally mixed, obtain solidifying agent, host is mixed with the part by weight of solidifying agent according to 1: 0.5, obtain putty, the method for using brushing and blade coating gets final product woodwork closed allround such as wooden furniture, timber floor.
Adopt GB/T 18260-2000 " wood preservative is to termite toxic effect test method " to detect, termide-proof and insect-proof efficient is 1 grade.
Quality and technical index and harmful substance contents are as follows:
Sequence number Interventions Requested Assay The method of inspection
1 Outward appearance There is not mechanical impurity, no skinning
2 Appearance of film Surfacing, smooth Range estimation
3 The host denseness 8～14cm GB/T1749
4 Time of drying (25 ℃) Surface drying 8min GB/T1728-89 (second method)
Do solid work ≤1h GB/T1728-89 (first method)
5 Sticking power (cross-hatching) ≤ 2 grades GB/T9286-1998
6 Snappiness ≤100mm GB/T1748
7 Thermotolerance (60 ℃, 2h) No change GB/T1735-79
Embodiment 2
Host
Sequence number Title Weight, kilogram
1 Synolac (DA2272-70) 27
2 Wetting agent (BYK P104S, unsaturated polycarboxylic acid polymkeric substance of lower molecular weight and polysiloxane interpolymer solution) 0.2
3 Solvent (toluene) 7.5
4 Anti-settling agent (M-5, aerosil) 2.5
5 Aminoresin (107AM-65) 24.5
6 1000 order talcum powder 35.8
7 Silicon is spirit in vain 2.5
Add up to 100
Solidifying agent
Sequence number Title Weight, kilogram
1 Tosic acid 24
2 Propyl carbinol 42
3 Toluene 34
Add up to 100
Each component of host is proportionally mixed, obtain host, each component of solidifying agent is proportionally mixed, obtain solidifying agent, host is mixed with the part by weight of solidifying agent according to 1: 0.3, obtain putty, the method for using brushing and blade coating gets final product woodwork closed allround such as wooden furniture, timber floor.
Adopt GB/T18260-2000 " wood preservative is to termite toxic effect test method " to detect, termide-proof and insect-proof efficient is 1 grade.
Quality and technical index and harmful substance contents are as follows:
Sequence number Interventions Requested Assay The method of inspection
1 Outward appearance There is not mechanical impurity, no skinning
2 Appearance of film Surfacing, smooth Range estimation
3 The host denseness 8～14cm GB/T1749
4 Time of drying (25 ℃) Surface drying 8min GB/T1728-89 (second method)
Do solid work ≤1h GB/T1728-89 (first method)
5 Sticking power (cross-hatching) ≤ 2 grades GB/T9286-1998
6 Snappiness ≤100mm GB/T1748
7 Thermotolerance (60 ℃, 2h) No change GB/T1735-79

Claims (8)

1. two component acid cure termide-proof and insect-proof putty is characterized in that, is made up of host and solidifying agent;
The component and the parts by weight of host comprise:
25～35 parts of Synolac
0.1～0.5 part of wetting agent
8～16 parts of solvents
0.5～2.5 part of anti-settling agent
16～26 parts in aminoresin
28～38 parts of talcum powder
0.5～4.5 part of insect-proof agent
Said anti-settling agent is a silicon-dioxide;
The component and the parts by weight of solidifying agent comprise:
18～30 parts of tosic acid, 40～50 parts of propyl carbinols, 25～35 parts of toluene.
2. according to claim 1 pair of component acid cure termide-proof and insect-proof putty is characterized in that, said wetting agent is unsaturated polycarboxylic acid polymkeric substance of lower molecular weight and polysiloxane interpolymer solution.
3. according to claim 1 pair of component acid cure termide-proof and insect-proof putty is characterized in that said solvent is selected from toluene or dimethylbenzene.
4. according to claim 1 pair of component acid cure termide-proof and insect-proof putty is characterized in that said anti-settling agent is an aerosil.
5. according to claim 1 pair of component acid cure termide-proof and insect-proof putty is characterized in that said talcous fineness is 800～1200.
6. according to claim 1 pair of component acid cure termide-proof and insect-proof putty is characterized in that said insect-proof agent is selected from a kind of or its mixture of pyrethroid, stuck gram missible oil or silicon Bai Lingzhong.
7. according to each described pair of component acid cure termide-proof and insect-proof putty of claim 1～6, it is characterized in that the weight ratio of host and solidifying agent is: host: solidifying agent=1: 0.3～0.7.
8. according to the application of each described pair of component acid cure termide-proof and insect-proof putty of claim 1～6, it is characterized in that, be used for the woodenware pre-treatment of modern wooden furniture application and the woodenware pre-treatment of decoration design for residence.
CNB2005100243165A 2005-03-10 2005-03-10 Two component acid cure termide-proof and insect-proof putty and application thereof Active CN100547043C (en)