CN109401412A - A kind of aqueous static conductive putty and preparation method thereof - Google Patents
A kind of aqueous static conductive putty and preparation method thereof Download PDFInfo
- Publication number
- CN109401412A CN109401412A CN201811232925.3A CN201811232925A CN109401412A CN 109401412 A CN109401412 A CN 109401412A CN 201811232925 A CN201811232925 A CN 201811232925A CN 109401412 A CN109401412 A CN 109401412A
- Authority
- CN
- China
- Prior art keywords
- component
- conductive
- parts
- putty
- auxiliary agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of aqueous static conductive putty, be made of component A and B component: component A includes 0.2~0.5 part of Carbon fibe, 1.0~1.5 parts of carbon black, 0.3~0.6 part of Conductive mica, 0.1~0.3 part of conductive titanium dioxide, 10~15 parts of polyvinyl alcohol Emulgating polymers, 130~135 parts of methylcellulose, 0.01~0.05 part of auxiliary agent；B component includes 0.8~1.5 part of white cement, 0.6~0.8 part of coarse whiting, 0.3~0.5 part of sierozem power, 0.05~0.09 part of dry powder glue；When preparing component A, first takes Carbon fibe, carbon black, Conductive mica and conductive titanium dioxide to be put into powder stirrer and pour into dispersion cylinder after mixing evenly, be subsequently added into polyvinyl alcohol polymer, methylcellulose and auxiliary agent and dispersed, then ground on three-roller；When preparing B component, white cement, coarse whiting, sierozem power and dry powder glue are put into powder stirrer and are stirred evenly, is then packed.By utilizing mentioned component, so that putty has the characteristics that environmental protection, use scope are wide；Resistance value is adjustable, and compression strength is high, can be widely applied to the levelling and antistatic inner wall of building field of antistatic floor.
Description
Technical field
The present invention relates to the levelling and antistatic inner wall of building technical field of antistatic floor, in particular to a kind of aqueous lead
Electrostatic putty and preparation method thereof.
Background technique
Existing antistatic putty only has epoxy group anti-electrostatic solvent terrace putty, is only used for antistatic floor construction,
It can not be used on inner wall of building and not environmentally, belong to and eliminate object.And existing Formula of putty only imparts filling up, looking for for putty
Gentle decoration functions (such as inner-outer wall building putties), there are the shortcomings that include: that (1) compression strength is low, it is impossible to be used in ground；
(2) there is no electrostatic conductive performance, it is impossible to be used in the industries such as chemical industry, electronics need the workplace of antistatic.
Therefore, a kind of environmental protection, the aqueous static conductive putty that resistance value is low and compression strength is high require study.
Summary of the invention
In order to solve the above technical problems, technical solution provided by the invention are as follows:
A kind of aqueous static conductive putty, be made of the component A and B component of following parts by weight: component A includes Carbon fibe
0.2~0.5 part, 1.0~1.5 parts of carbon black, 0.3~0.6 part of Conductive mica, 0.1~0.3 part of conductive titanium dioxide, polyvinyl alcohol cream
10~15 parts of fluidized polymer, 130~135 parts of methylcellulose, 0.01~0.05 part of auxiliary agent；B component include white cement 0.8~
1.5 parts, 0.6~0.8 part of coarse whiting, 0.3~0.5 part of sierozem power, 0.05~0.09 part of dry powder glue.
Preferably, be made of the component A and B component of following parts by weight: component A includes 0.3 part of Carbon fibe, conductive black
It 1.3 parts, 0.5 part of Conductive mica, 0.2 part of conductive titanium dioxide, 13 parts of polyvinyl alcohol Emulgating polymers, 133 parts of methylcellulose, helps
0.04 part of agent；B component includes 1.2 parts of white cement, 0.7 part of coarse whiting, 0.4 part of sierozem power, 0.07 part of dry powder glue.
Preferably, the auxiliary agent is non-film auxiliary agent.
The present invention also provides a kind of technical solutions:
A kind of preparation method of aqueous static conductive putty, the aqueous static conductive putty are that static conductive described above is greasy
Son first respectively takes a certain amount of Carbon fibe, carbon black, Conductive mica and conductive titanium dioxide to be put into powder stirrer when preparing component A
In pour into dispersion cylinder after mixing evenly, a certain amount of polyvinyl alcohol polymer, Methyl cellulose are then added under stirring
Element and auxiliary agent are dispersed, and are then ground on three-roller, are packed after being fabricated to conductive paste with closed container；In preparation B component
When, it takes a certain amount of white cement, coarse whiting, sierozem power and dry powder glue to be put into powder stirrer and stir evenly, is then put into moisture-proof
It is packed in paper bag；When in use, component A and B group are mixed according to a certain percentage, can be made after adding water and stirring uniformly
With.
Preferably, when carrying out decentralized processing to component A, the time of dispersion is 40min.
Preferably, it when being ground component A, needs to grind it twice on three-roller.
After the above ingredient and preparation method, the present invention has the advantage that
(1) have the characteristics that environmental protection, make its can be widely applied to Aeronautics and Astronautics, electronics, explosive industry field etc. need to lead it is quiet
In the industrial premises interior wall and antistatic floor of electricity or antistatic；
(2) volume resistance: codomain is wide by 103Ω~109Ω, and resistance can be adjusted by increase and decrease component A according to requirements
Value, resistance value is stable and is not influenced by ambient temperature and humidity；
(3) compression strength >=30N/mm2, compression strength is higher, and cracking resistance and adhesive force are excellent, can be widely applied to prevent
Electrostatic terrace engineering field.
Specific embodiment
The present invention is described in further detail below.
Embodiment one
A kind of aqueous static conductive putty, be made of the component A and B component of following mass fraction: component A includes Carbon fibe
0.3 part, 1.3 parts of carbon black, 0.5 part of Conductive mica, 0.2 part of conductive titanium dioxide, 13 parts of polyvinyl alcohol Emulgating polymers, Methyl cellulose
133 parts, 0.04 part of auxiliary agent of element；B component includes 1.2 parts of white cement, 0.7 part of coarse whiting, 0.4 part of sierozem power, 0.07 part of dry powder glue.
Wherein: auxiliary agent is non-film auxiliary agent.
When preparing the present invention, when preparing component A, a certain amount of Carbon fibe, carbon black, Conductive mica and conductive titanium are first respectively taken
White powder is put into powder stirrer and pours into dispersion cylinder after mixing evenly, and a certain amount of polyethylene is then added under stirring
Alkoxide polymer, methylcellulose and auxiliary agent are dispersed, and are then ground on three-roller, use closed container after being fabricated to conductive paste
Packaging；When preparing B component, takes a certain amount of white cement, coarse whiting, sierozem power and dry powder glue to be put into powder stirrer and stir
It is even, it is then put into Moisture Proof Pager Bag and is packed；When in use, at the construction field (site) by component A and B component according to one barrel of one bag of ratio
Ratio mixing, it is i.e. usable after adding water and stirring uniformly；The resistance value of putty is adjustable according to the amount that product description increases and decreases component A
Section, adjustable range；103Ω~109Ω。
Wherein: when carrying out decentralized processing to component A, the time of dispersion is 40min；It is ground to component A
When, it needs to grind it twice on three-roller.
Embodiment two
A kind of aqueous static conductive putty, which is characterized in that be made of the component A and B component of following parts by weight: component A
Including 0.2 part of Carbon fibe, 1.0 parts of carbon black, 0.3 part of Conductive mica, 0.1 part of conductive titanium dioxide, polyvinyl alcohol Emulgating polymers 10
Part, 132 parts of methylcellulose, 0.01 part of auxiliary agent；B component includes 0.8 part of white cement, and 0.6 part of coarse whiting, 0.3 part of sierozem power, dry powder
0.05 part of glue.
Other technologies scheme is the same as example 1.
Embodiment three
A kind of aqueous static conductive putty, which is characterized in that be made of the component A and B component of following parts by weight: component A
Including 0.5 part of Carbon fibe, 1.5 parts of carbon black, 0.6 part of Conductive mica, 0.3 part of conductive titanium dioxide, polyvinyl alcohol Emulgating polymers 15
Part, 135 parts of methylcellulose, 0.05 part of auxiliary agent；B component includes 1.5 parts of white cement, and 0.8 part of coarse whiting, 0.5 part of sierozem power, dry powder
0.09 part of glue.
Other technologies scheme is the same as example 1.
Claims (6)
1. a kind of aqueous static conductive putty, which is characterized in that be made of the component A and B component of following parts by weight: component A packet
0.2~0.5 part of Carbon fibe is included, 1.0~1.5 parts of carbon black, 0.3~0.6 part of Conductive mica, 0.1~0.3 part of conductive titanium dioxide, is gathered
10~15 parts of vinyl alcohol Emulgating polymers, 130~135 parts of methylcellulose, 0.01~0.05 part of auxiliary agent；B component includes plain boiled water
0.8~1.5 part of mud, 0.6~0.8 part of coarse whiting, 0.3~0.5 part of sierozem power, 0.05~0.09 part of dry powder glue.
2. a kind of aqueous static conductive putty according to claim 1, which is characterized in that by the component A of following parts by weight
Form with B component: component A includes 0.3 part of Carbon fibe, and 1.3 parts of conductive black, 0.5 part of Conductive mica, 0.2 part of conductive titanium dioxide,
13 parts of polyvinyl alcohol Emulgating polymers, 133 parts of methylcellulose, 0.04 part of auxiliary agent；B component includes 1.2 parts of white cement, coarse whiting
0.7 part, 0.4 part of sierozem power, 0.07 part of dry powder glue.
3. a kind of aqueous static conductive putty according to claim 2, which is characterized in that the auxiliary agent is non-film auxiliary agent.
4. a kind of preparation method of aqueous static conductive putty, which is characterized in that the aqueous static conductive putty is wanted for aforesaid right
Static conductive putty described in asking 1 first respectively takes a certain amount of Carbon fibe, carbon black, Conductive mica and conductive titanium when preparing component A
White powder is put into powder stirrer and pours into dispersion cylinder after mixing evenly, and a certain amount of polyethylene is then added under stirring
Alkoxide polymer, methylcellulose and auxiliary agent are dispersed, and are then ground on three-roller, use closed container after being fabricated to conductive paste
Packaging；When preparing B component, takes a certain amount of white cement, coarse whiting, sierozem power and dry powder glue to be put into powder stirrer and stir
It is even, it is then put into Moisture Proof Pager Bag and is packed；When in use, when in use, according to a certain percentage by component A and B component
Mixing can be used after adding water and stirring uniformly.
5. a kind of preparation method of aqueous static conductive putty according to claim 4, which is characterized in that component A into
When row decentralized processing, the time of dispersion is 40min.
6. a kind of preparation method of aqueous static conductive putty according to claim 4, which is characterized in that component A into
When row milled processed, need to grind it twice on three-roller.