CN1087763C - 双组分聚氨酯建筑密封膏及生产工艺 - Google Patents

双组分聚氨酯建筑密封膏及生产工艺 Download PDF

Info

Publication number
CN1087763C
CN1087763C CN 98113700 CN98113700A CN1087763C CN 1087763 C CN1087763 C CN 1087763C CN 98113700 CN98113700 CN 98113700 CN 98113700 A CN98113700 A CN 98113700A CN 1087763 C CN1087763 C CN 1087763C
Authority
CN
China
Prior art keywords
component
parts
stir
oil
dibutyl phthalate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 98113700
Other languages
English (en)
Other versions
CN1247882A (zh
Inventor
黄万东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 98113700 priority Critical patent/CN1087763C/zh
Publication of CN1247882A publication Critical patent/CN1247882A/zh
Application granted granted Critical
Publication of CN1087763C publication Critical patent/CN1087763C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明提供一种双组分聚氨酯建筑密封膏,由A、B两种组分混合使用,A组分配比为聚醚5613:189~191、邻苯二甲酸二丁酯:36~38,异氰酸酯6~8;B组为精蓖麻油18.5~20、二甲酸二丁酯15~17,硅油和偶联剂各0.5~1.5,洗油20~30、双飞粉、滑石粉、轻质碳酸钙35~45、钛白粉16~20、辛酸亚锡0.5~1.5。工艺中主要区别是无中间烘干等工艺,填料与交联剂,助剂一起脱水。该密封膏粘接性能好,寿命可达30年以上。

Description

双组分聚氨酯建筑密封膏及生产工艺
本发明涉及一种建筑密封膏及生产工艺,属于化学建材类。
目前,建筑物所用密封材料多为PVC塑料油膏等低档油性材料,这种材料性能差,使用不久即会造成建筑物漏水。现有生产B组分类似产品需烘干机后加偶联剂、助剂、设备投资大,能耗高,生产周期长,因此成本高。
本发明的目的是选出合理配方,采用简单工艺生产出粘接力高,耐老化,有弹性,使用寿命长的建筑密封膏。
本发明的技术方案是这样实现的。分A、B两种组合配方,采用不同的工艺分别加工包装使用时混合在一起,两组成分及配比如下:A组分:聚氧乙烯醚-5613:189~191
邻苯二甲酸二丁酯:   36~38
异氰酸酯:            6~8B组分:精制麻油:      18.5~20
邻苯二甲酸二丁酯:   15~17
甲基硅油:          0.5~1.5
氨丙基三乙氧基硅烷:0.5~1.5  商品名:硅烷偶联剂(WD-50)
洗油:               20~30
重质碳酸钙:         35~45   商品名:双飞粉
滑石粉:             35~45
轻质碳酸钙:         35~45
钛白粉:             16~20
辛酸亚锡:          0.5~1.5
上述建筑密封膏的生产工艺,A组分为:在反应釜中按上述配比加入各组分搅拌,升温至90°±2℃进行合成,反应时间1.5~2小时,降温在50℃以下即可出料包装,包装前取样分析异氰酸根(NCO)含量3.5~4.5%,B组分为:先在反应釜中(按上述配比)中入精制麻油,升温搅拌,逐步加入双飞粉即重质碳酸钙,滑石粉,轻质碳酸钙,钛白粉及邻苯二甲酸二丁酯,升温到95°±5℃开真空泵脱水,维持真空在500mm水银柱以上,搅拌脱水1.5小时以上,降温至80℃,再依次加入硅油、洗油、辛酸亚锡、硅烷偶联剂,如氨丙基三乙氧基硅烷继续搅拌1小时,自然冷却至50℃出料包装。
本发明的优点是配方合理,性能指标可达到:表干≤4小时,实干≤12、小时挤出速率<30秒,伸长率≥300%,粘接力>1.5KN/M,硬度(邵氏)25~30,耐疲劳性±12.5%,寿命可达30年以上,而且施工简单容易。一般生产工艺,特别是B组,脱水后要烘干,这样设备投资大,能耗高,需再冷却,冷却和分装过程中易造成填料吸潮。本工艺采取填料与交联剂,助剂一起混匀脱水,一次即成产品,省去了中间烘干等工艺过程既保证了质量又大大缩短了生产周期,降低了能耗和成本。
本发明的实施例如上述技术方案给出。使用时将A、B两种组分按A∶B=1∶2混合均匀即可施工。可广泛用于高层建筑,高速公路,桥梁,机场等一切混凝土,砖施工场合。

Claims (2)

1、一种双组分聚氨酯建筑密封膏,由A、B两种组分的产品混合使用,各组分的成分及配比如下:A组分:聚氧乙烯醚-5613:189~191
邻苯二甲酸二丁酯:     36~38
异氰酸酯:             6~8B组分:精制麻油:       18.5~20
邻苯二甲酸二丁酯:    15~17
甲基硅油:           0.5~1.5
氨丙基三乙氧基硅烷: 0.5~1.5
洗油:                20~30
重质碳酸钙:          35~45
滑石粉:              35~45
轻质碳酸钙:          35~45
钛白粉:              16~20
辛酸亚锡:           0.5~1.5A组分子与B组分的用量比为A∶B=1∶2。
2、一种按权利要求1的建筑密封膏的生产工艺,A组分为:在反应釜中按所述的配比加入各组分搅拌,升温至90°±2°进行合成,反应时间1.5~2小时,降温在50°以下即可出料包装,包装前取样分析异氰酸根的含量3.5~4.5%,B组分为:也按给出的配比先在反应釜中加入精制麻油,升温搅拌,逐步加入重质碳酸钙,滑石粉,轻质碳酸钙,钛白粉及邻苯二甲酸二丁酯,升温到95°±5°开真空泵脱水,维持真空在500mm水银柱以上,搅拌脱水1.5小时以上,降温至80℃,依次加入硅油,洗油,辛酸亚锡,硅烷偶联剂 氨丙基三乙氧基硅烷,继续搅拌1小时,自然冷却至50℃出料包装,使用时A组分∶B组分=1∶2。
CN 98113700 1998-09-11 1998-09-11 双组分聚氨酯建筑密封膏及生产工艺 Expired - Fee Related CN1087763C (zh)