CN107604698A - A kind of manufacture craft of concentrator, fabric and fabric - Google Patents
A kind of manufacture craft of concentrator, fabric and fabric Download PDFInfo
- Publication number
- CN107604698A CN107604698A CN201710881364.9A CN201710881364A CN107604698A CN 107604698 A CN107604698 A CN 107604698A CN 201710881364 A CN201710881364 A CN 201710881364A CN 107604698 A CN107604698 A CN 107604698A
- Authority
- CN
- China
- Prior art keywords
- fabric
- concentrator
- water
- parts
- value
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This application discloses the manufacture craft of a kind of concentrator, fabric and fabric, the concentrator, in parts by weight, including：5~10 parts of anthocyanidin, 20~30 parts of printing adhesive, 1~2 part of printing thickening agent, 0.5~3 part of bleeding agent, 55~75 parts of deionized water；The concentrator absorbs water, and detects the pH value of water, and different colors is shown according to the difference of pH value.The manufacture craft of a kind of concentrator, fabric and fabric that the application provides, fabric is made using the concentrator containing anthocyanidin, after the fabric touches water, can be according to the pH value of the water touched, the conversion color corresponding with the pH value, to prompt the water of the user of the fabric now whether can be caused to human body dangerous or whether can be polluted to environment；And the fabric outer layer is handled using waterproof technology so that the fabric can also play the function of waterproof while can detect the pH value of water；PU or TPU membrane, which can also be pasted, in fabric internal layer increases the water resistance of the fabric.
Description
Technical field
The present invention relates to fabric manufacture technology field, the making work of more particularly to a kind of concentrator, fabric and fabric
Skill.
Background technology
At present, with the development of industrialization society, the pollutant increase to environment is launched, air quality declines, aerial
Rainwater contains various inorganic salts, organic matter, sand and dust or microorganism etc., impermeable because washing away roof, road etc. after rainwater falls earthward
Water surface, contain the pollutant such as ammonia nitrogen, oil, heavy metal in the rainwash that rainwater is formed.In addition the row of pollutant in living
Put, pollution is caused to the water in living environment.
The acid-base value of water is not only an important physical feature index, or important water quality operational factor.Rainwater
Main component is water (chemical formula H2O), there is a small amount of sulfur dioxide (chemical formula SO2), nitrogen dioxide (chemical formula NO2), usual rainwater
PH value be about 5.6 be normal value, be acid rain when the pH value in rainwater is less than 5.6.Water in living environment, if pH value is too low
With it is too high when, harm can be all brought to environment, and pH value is too high or too low, not only will injure human body flesh when contacting human body
Skin, also result in the death of organism in water.
People such as runs into rainfall in trip or outdoor exercises, would generally select to continue on when rainfall is smaller, at this moment need
The clothes of waterproof is wanted to make human body from the injury of rainwater.Approach is also required to know rainwater pollution degree, to determine simultaneously
Whether need to take shelter from rain.When needing to contact the water source in unknown source out of doors, it is also desirable to which approach knows the water source to human body skin
Whether there is injury, protect health.
Waterproof fabrics of the prior art has different degrees of water-proof function, but without the function of water pollution degree detection.
And spill resistant in main product on the market still based on fluorochemical, its produce and using process to human body and environment meeting
Produce harmful influence.
The content of the invention
In view of this, a kind of manufacture craft of the application offer is simple and environmentally-friendly, and can detect the printing paste of the pH value of water
The manufacture craft of material, fabric and fabric.
What the technical scheme of the application was realized in：
On the one hand, the application provides a kind of concentrator, in parts by weight, including：5~10 parts of anthocyanidin, printed adhesive
20~30 parts of agent, 1~2 part of printing thickening agent, 0.5~3 part of bleeding agent, 55~75 parts of deionized water；The concentrator absorbs
Water, and the pH value of water is detected, different colors is shown according to the difference of pH value.
Alternatively, the anthocyanidin includes purple cabbage pigment, pelargonidin, swears this asterin, lotus anthocyanidin, delphinium grandiflorum
Element, delphinidin, paeonidin, morning glory pigment and/or malvidin.
Alternatively, the printing adhesive includes self-cross linking type polyacrylate adhesive, in parts by weight, including：
10~15 parts of hard monomer, 10~15 parts of soft monomer, 1~2 part of cross-linking monomer, 0.1~0.3 part of emulsifying agent, deionized water 25~35
Part.
Alternatively, the hard monomer includes acrylonitrile, vinyl acetate, tertiary ethylene carbonate, one kind in styrene or several
Kind and the mixture of methyl methacrylate；Wherein, the methyl methacrylate account for the hard monomer gross mass 50%~
90%.
Alternatively, the soft monomer includes ethyl acrylate, Isooctyl acrylate monomer and/or butyl acrylate；Wherein, it is described
Butyl acrylate accounts for the 70%~100% of the soft monomer gross mass.
Alternatively, the emulsifying agent includes anion surfactant and nonionic surfactant.
Alternatively, the anion surfactant includes neopelex, lauryl sodium sulfate, succinic acid
Dihexyl sodium sulfonate and/or sulfosuccinate surfactant.
Alternatively, the nonionic surfactant includes isomerous tridecanol polyoxyethylene ether 3, isomerous tridecanol polyoxy second
Alkene ether 5, isomerous tridecanol polyoxyethylene ether 7 and/or isomerous tridecanol polyoxyethylene ether 9.
Alternatively, the cross-linking monomer includes GDMA and/or methylene-bisacrylamide.
On the other hand, the application provides a kind of fabric, including fabric body and the function that is arranged in the fabric body
Layer, the functional layer are made by concentrator, anthocyanidin are contained in the concentrator, the concentrator absorbs water, and examines
The pH value of water is surveyed, different colors is shown according to the difference of pH value.
Alternatively, the concentrator is above-mentioned concentrator.
Alternatively, the fabric also includes：Film layer, the film layer are bonded in the fabric body.
Alternatively, the film layer is the waterproof ventilated membrane that polyurethane material or TPUE make.
Alternatively, the fabric body includes one or more of fiber blends in cotton, viscose, terylene, polyamide fibre and spandex
Fabric, the cotton, viscose, terylene, polyamide fibre and spandex are true qualities, bleach, brighten or dye.
Alternatively, the fiber blended fabric is knitting or tatting.
Alternatively, it is characterised in that the fiber blended fabric is plain.
On the other hand, the application provides a kind of manufacture craft of fabric, including：
Choose fabric body；
Configure concentrator；
The concentrator configured is coated in the fabric body of selection and printing pattern, stamp after 80~
100 DEG C of drying, 140~160 DEG C bake, and form functional layer.
Alternatively, the manufacture craft of the fabric also includes：Water-proofing treatment, the water-proofing treatment include：Fabric is put into
Bath raio is 1：In 8~15 solution, after room temperature immersion, padding machine is crossed, 100 DEG C dry 3~5 minutes, then 140~160 DEG C bake 40
~90 seconds.
Alternatively, the solution composition is 8~12%owf waterproofing agent, 6~8%owf crosslinking agent, remaining for go from
Sub- water.
Alternatively, the concentrator is above-mentioned concentrator.
The beneficial effect of the application is：The manufacture craft of a kind of concentrator, fabric and fabric that the application provides, is adopted
Fabric is made with the concentrator containing anthocyanidin, after the fabric touches water, can be become according to the pH value for touching water
The color corresponding with pH value is changed, to prompt the water of the user of the fabric now whether can be caused to human body dangerous or whether can
Environment is polluted；And the fabric outer layer is handled using waterproof technology so that the fabric can detect water ph value
The function of waterproof can also be played simultaneously；PU or TPU membrane, which can also be pasted, in fabric internal layer increases the water resistance of the fabric.
Embodiment
Many details are elaborated in the following description in order to fully understand the application.But the application can be with
Much it is different from other manner described here to implement, those skilled in the art can be in the situation without prejudice to the application intension
Under do similar popularization, therefore the application is not limited by following public specific implementation.
The embodiment of the application one provides a kind of concentrator, in parts by weight, including：5~10 parts of anthocyanidin, printed adhesive
20~30 parts of agent, 1~2 part of printing thickening agent, 0.5~3 part of bleeding agent, 55~75 parts of deionized water；The concentrator absorbs
Water, and the pH value of water is detected, different colors is shown according to the difference of pH value.
In the embodiment of the present application, the anthocyanidin includes purple cabbage pigment, pelargonidin, swears this asterin, Flos Hibisci Mutabilis
Pigment, delphinidin, delphinidin, paeonidin, morning glory pigment and/or malvidin；Anthocyanidin is that nature is a kind of wide
The general water-soluble natural pigment being present in plant, belongs to flavone compound, and color be able to can be sent out because of the difference of the pH value touched
Changing, color is partially red if the water touched is in acidity, and color is partially blue if the water touched is in alkalescence.
Color change is specific as follows：
PH value is red less than 3, and pH value is lower, and color is deeper；PH value is in purple pink colour between 4~5；PH value 5~7 it
Between be in purple；PH value is between 7~10 in blueness；PH value color between 10~11 changes to black；When pH value is more than 12.5,
Yellow occurs.
In the embodiment of the present application, the printing adhesive includes self-cross linking type polyacrylate adhesive, with parts by weight
Meter, including：10~15 parts of hard monomer, 10~15 parts of soft monomer, 1~2 part of cross-linking monomer, 0.1~0.3 part of emulsifying agent, deionization
25~35 parts of water；Above-mentioned material is well mixed, pre-emulsification 30 minutes, then the water after pre-emulsification is positioned in reactor
Heated up, when coolant-temperature gage is warming up to 68 DEG C, 0.04~0.08 part of initiator potassium persulfate is added dropwise and is dissolved in 6~9 parts of deionizations
The solution of water, reaction terminate to obtain the self-cross linking type polyacrylate adhesive after 3~4 hours.
The hard monomer is acrylonitrile, vinyl acetate, tertiary ethylene carbonate, one or more and methyl-prop in styrene
The mixture of e pioic acid methyl ester；Wherein, the methyl methacrylate accounts for the 50%~90% of the hard monomer gross mass.
Wherein, the soft monomer is ethyl acrylate, Isooctyl acrylate monomer and/or butyl acrylate；Wherein, the propylene
Acid butyl ester accounts for the 70%~100% of the soft monomer gross mass.
The emulsifying agent is compounded by anion surfactant and nonionic surfactant and is made；The anionic surface
Activating agent is neopelex, lauryl sodium sulfate, succinic acid dihexyl sodium sulfonate and/or sulfosuccinate table
Face activating agent, the nonionic surfactant include isomerous tridecanol polyoxyethylene ether 3, isomerous tridecanol polyoxyethylene ether 5,
Isomerous tridecanol polyoxyethylene ether 7 and/or isomerous tridecanol polyoxyethylene ether 9.
The cross-linking monomer is GDMA and/or methylene-bisacrylamide.
A kind of concentrator that the application provides, adds anthocyanidin so that the concentrator is connecing in concentrator
The pH value of water can be detected by contacting during water, then the color according to corresponding to the pH value conversion detected, to prompt making for the fabric
Whether whether the water touched of user now can be harmful to body or environment can be polluted, and user can be according to detection
To situation make corresponding solution, avoid causing personal injury, and the fabric material is more environmentally friendly.
A kind of fabric that the embodiment of the application one provides, including fabric body and the function that is arranged in the fabric body
Layer, the functional layer are made by concentrator, anthocyanidin are contained in the concentrator, the concentrator absorbs water, and examines
The pH value of water is surveyed, different colors is shown according to the difference of pH value.
In the embodiment of the present application, the concentrator uses the concentrator in above-described embodiment, and the fabric is also
Including the film layer by polyurethane material PU or thermoplastic polyurethane elastomer making, the film layer is with scribbling glue
The fabric body overlapping, then again through pressing bundle the film layer is bonded into one with the fabric body, the glue can
To use PU PURs.
In the embodiment of the present application, the fabric body includes the one or more in cotton, viscose, terylene, polyamide fibre and spandex
Fiber blended fabric, the cotton, viscose, terylene, polyamide fibre and spandex are true qualities, bleach, brighten or dye, the fiber blend face
Material is using knitting or tatting, preferably plain.
A kind of fabric in the embodiment of the present application, the fabric is made using the concentrator containing anthocyanidin, in the fabric
After touching water, the color corresponding with pH value can be converted, to prompt the use of the fabric according to the pH value for touching water
Whether whether the water of person now can cause dangerous to human body or environment can be polluted；And waterproof and breathable is added in fabric
Layer so that the function of waterproof can also be played while the fabric can detect the pH value of water.
The application one implements to provide a kind of manufacture craft of fabric, including：
Choose fabric body；
Configure concentrator；
The concentrator configured is coated in the fabric body of selection and printing pattern, stamp after 80~
100 DEG C of drying, 140~160 DEG C bake, and form functional layer.
In the embodiment of the present application, the fabric body is from the fabric body in above-described embodiment, the concentrator choosing
With the concentrator in above-described embodiment.
In the embodiment of the present application, the manufacture craft of the fabric can also include：Water-proofing treatment, the water-proofing treatment bag
Include：It is 1 by fabric input bath raio：In 8~15 solution, after room temperature immersion, padding machine is crossed, 100 DEG C dry 3~5 minutes, then 140
~160 DEG C bake 40~90 seconds；The solution composition is 8~12%owf waterproofing agent, and 6~8%owf crosslinking agent, remaining is
Deionized water.
In the embodiment of the present application, the waterproofing agent is Ke Mu companies without fluoro water proofing agent Teflon EcoElite (abbreviations
R3) or Hensel is stepped without one kind in fluoro water proofing agent PHOBOL RSH, and the crosslinking agent is the waterproof crosslinking agent of Huntsman Corporation
PHOBOL XAN。
A kind of manufacture craft of fabric of the embodiment of the present application, fabric is made using the concentrator containing anthocyanidin,
After the functional layer touches water, the color corresponding with pH value can be converted, to prompt the face according to the pH value for touching water
Whether whether the water of the user of material now can cause dangerous to human body or environment can be polluted；And make in fabric outer layer
Handled with waterproof technology so that the function of waterproof can also be played while the fabric can detect water ph value.
In the embodiment of the application one, bleaching cotton plain is chosen as fabric body, is then printed in fabric body outer layer
System can detect the stamp functional layer of water pollution degree, and the functional layer is made by concentrator, wherein, the concentrator is
5 parts of purple cabbage pigment, 20 parts of printing adhesive, 1 part of printing thickening agent, 0.5 part of bleeding agent, the bleeding agent are isobutyl-benzene oxygen
Base polyoxyethylene ethanol, 70 parts of deionized water.
In the embodiment of the present application, the printing adhesive is self-cross linking type polyacrylate adhesive, the self-crosslinking
Type polyacrylate adhesive is 12 parts of hard monomer, and the hard monomer is 10 parts of 2 parts of styrene and methyl methacrylate
Mixture；15 parts of soft monomer, the soft monomer are butyl acrylate；1 part of cross-linking monomer, the cross-linking monomer are dimethyl allene
Sour glycol ester；0.15 part of emulsifying agent, wherein, the emulsifying agent is anion surfactant and nonionic surfactant
Compounding, the anion surfactant are 0.05 part of neopelex, and the nonionic surfactant is 0.1 part
Isomerous tridecanol polyoxyethylene ether 5；35 parts of deionized water.Then above-mentioned material is well mixed, pre-emulsification 30 minutes, then
Water after pre-emulsification is positioned in reactor and heated up, when water is warming up to 68 DEG C, initiator potassium persulfate is added dropwise in water
0.04 part is dissolved in the solution of 6 parts of deionized waters, and reaction can obtain the printing adhesive after 3 hours.
In the embodiment of the present application, the good concentrator of above-mentioned configuration is coated in the fabric body of selection and prints print
Floral pattern, after 80 DEG C of drying, 140 DEG C bake stamp, form functional layer.
In the embodiment of the present application, the fabric after stamp is subjected to water-proofing treatment, is 1 first by fabric input bath raio：8
In solution, after room temperature immersion, padding machine is crossed, 100 DEG C dry 3 minutes, then 140 DEG C bake 90 seconds；Wherein, solution composition is 8%owf
Waterproofing agent R3,6%owf crosslinking agent XAN, remaining as deionized water.
In the embodiment of the present application, it can also use and set the compound PU waterproof ventilated membranes of internal layer to cause fabric in fabric body
Possess water-proof function, PU waterproof ventilated membranes and the fabric body for scribbling glue are overlapped, make PU waterproof ventilated membranes and face through pressure rolling
Expect that bulk adhesive is integral, the function of waterproof and breathable can also be played；Wherein described glue can be PU PURs.
Gained fabric performance is shown in Table 1.
Table 1
Properties detection method is as follows in table 1：
(1) fastness to washing is tested according to GB/T420-1990.
(2) hydrostatic pressing is tested according to GB/T 4744-2013.
(3) rate of perviousness is tested according to GB/T 12704.1-2009:Using A group test conditions, sample is just facing anhydrous chlorination
Calcium.
(4) spray rating is tested according to GB/T 4745-2012.
It can be seen that from above-mentioned test, the fabric that the technique and concentrator provided by the application is obtained is not only floride-free
Environmental protection, also with good water resistance, and water pollution degree can be detected.
In the embodiment of the application one, 70% terylene of selection, the polyester-cotton blend plain weave light blue cloth of 30% cotton are fabric body, then
The stamp functional layer of water pollution degree can be detected in the printing of fabric body outer layer, the functional layer is made by concentrator, its
In, the concentrator is 8 parts of morning glory pigment, 30 parts of printing adhesive, 1.5 parts of printing thickening agent, 0.5 part of bleeding agent, institute
It is isobutyl-benzene epoxide polyoxyethylene ethanol JFC to state bleeding agent, 60 parts of deionized water.
In the embodiment of the present application, the printing adhesive is self-cross linking type polyacrylate adhesive, the self-crosslinking
Type polyacrylate adhesive is 13 parts of hard monomer, wherein, the hard monomer is 2 parts of acrylonitrile and 3 parts of styrene and methyl
The mixture that 8 parts of methyl acrylate；14 parts of soft monomer, wherein, the soft monomer is 2 parts of ethyl acrylate, Isooctyl acrylate monomer 2
Part and the mixture of 10 parts of butyl acrylate；1.3 parts of cross-linking monomer, the cross-linking monomer are GDMA
0.5 part and the mixture of 0.8 part of methylene-bisacrylamide；0.22 part of emulsifying agent, wherein, the emulsifying agent includes anion table
Face activating agent and nonionic surfactant, the anion surfactant are 0.05 part of neopelex and 12
The mixture that 0.02 part of sodium alkyl sulfate, the nonionic surfactant are 0.07 part of isomerous tridecanol polyoxyethylene ether 7
With the mixture of 0.08 part of isomerous tridecanol polyoxyethylene ether 9；35 parts of deionized water.Then above-mentioned material is well mixed,
Pre-emulsification 30 minutes, then the water after pre-emulsification is positioned in reactor and heated up, when water is warming up to 68 DEG C, dripped in water
0.05 part of initiator potassium persulfate is added to be dissolved in the solution of 8 parts of deionized waters, reaction can obtain the printed adhesive after 4 hours
Agent.
In the embodiment of the present application, the good concentrator of above-mentioned configuration is coated in the fabric body of selection and prints print
Floral pattern, after 100 DEG C of drying, 150 DEG C bake stamp, form functional layer.
In the embodiment of the present application, the fabric after stamp is subjected to water-proofing treatment, is 1 first by fabric input bath raio：8
In solution, after room temperature immersion, padding machine is crossed, 100 DEG C dry 3 minutes, then 150 DEG C bake 80 seconds；Wherein, solution composition is 10%
Owf waterproofing agent RSH, 6%owf crosslinking agent XAN, remaining as deionized water.
In the embodiment of the present application, it can also use and set the compound PU waterproof ventilated membranes of internal layer to cause fabric in fabric body
Possess water-proof function, PU waterproof ventilated membranes and the fabric body for scribbling glue are overlapped, make PU waterproof ventilated membranes and face through pressure rolling
Expect that bulk adhesive is integral, the function of waterproof and breathable can also be played；Wherein described glue can be PU PURs.
Gained fabric performance is shown in Table 2.
Table 2
Properties detection method is as follows in table 2：
(5) fastness to washing is tested according to GB/T420-1990.
(6) hydrostatic pressing is tested according to GB/T 4744-2013.
(7) rate of perviousness is tested according to GB/T 12704.1-2009:Using A group test conditions, sample is just facing anhydrous chlorination
Calcium.
(8) spray rating is tested according to GB/T 4745-2012.
It can be seen that from above-mentioned test, the fabric that the technique and concentrator provided by the application is obtained is not only floride-free
Environmental protection, also with good water resistance, and water pollution degree can be detected.
Present invention disclosed above preferred embodiment is only intended to help and illustrates the present invention.Alternative embodiment is not detailed
All details are described, it is only described embodiment also not limit the invention.Obviously, according to the content of this specification,
It can make many modifications and variations.This specification is chosen and specifically describes these embodiments, is to preferably explain the present invention
Principle and practical application so that skilled artisan can be best understood by and utilize the present invention.The present invention is only
Limited by claims and its four corner and equivalent.
Claims (20)
- A kind of 1. concentrator, it is characterised in that in parts by weight, including：5~10 parts of anthocyanidin, printing adhesive 20~30 Part, 1~2 part of printing thickening agent, 0.5~3 part of bleeding agent, 55~75 parts of deionized water；The concentrator absorbs water, and detects The pH value of water, different colors is shown according to the difference of pH value.
- 2. a kind of concentrator according to claim 1, it is characterised in that the anthocyanidin includes purple cabbage pigment, day Zhu Kui pigments, swear this asterin, lotus anthocyanidin, delphinidin, delphinidin, paeonidin, morning glory pigment and/or high mallow Pigment.
- 3. a kind of concentrator according to claim 1, it is characterised in that the printing adhesive gathers including self-cross linking type Acrylate adhesive, in parts by weight, including：10~15 parts of hard monomer, 10~15 parts of soft monomer, cross-linking monomer 1~2 Part, 0.1~0.3 part of emulsifying agent, 25~35 parts of deionized water.
- 4. a kind of concentrator according to claim 3, it is characterised in that the hard monomer includes acrylonitrile, acetic acid second One or more and the mixture of methyl methacrylate in alkene, tertiary ethylene carbonate, styrene；Wherein, the methyl-prop E pioic acid methyl ester accounts for the 50%~90% of the hard monomer gross mass.
- 5. a kind of concentrator according to claim 3, it is characterised in that the soft monomer includes ethyl acrylate, third The different monooctyl ester of olefin(e) acid and/or butyl acrylate；Wherein, the butyl acrylate accounts for the 70%~100% of the soft monomer gross mass.
- 6. a kind of concentrator according to claim 3, it is characterised in that the emulsifying agent includes anion surface active Agent and nonionic surfactant.
- 7. a kind of concentrator according to claim 6, it is characterised in that the anion surfactant includes 12 Sodium alkyl benzene sulfonate, lauryl sodium sulfate, succinic acid dihexyl sodium sulfonate and/or sulfosuccinate surfactant.
- 8. a kind of concentrator according to claim 6, it is characterised in that the nonionic surfactant includes isomery Tridecanol polyoxyethylene ether 3, isomerous tridecanol polyoxyethylene ether 5, isomerous tridecanol polyoxyethylene ether 7 and/or isomerous tridecanol APEO 9.
- 9. a kind of concentrator according to claim 3, it is characterised in that the cross-linking monomer includes dimethacrylate Glycol ester and/or methylene-bisacrylamide.
- 10. a kind of fabric, it is characterised in that including fabric body and the functional layer being arranged in the fabric body, the work( Ergosphere is made by concentrator, anthocyanidin is contained in the concentrator, the concentrator absorbs water, and detects the PH of water Value, different colors is shown according to the difference of pH value.
- 11. a kind of fabric according to claim 10, it is characterised in that the concentrator is that claim 1-9 is any Concentrator described in one.
- 12. a kind of fabric according to claim 10, it is characterised in that also include：Film layer, the film layer are bonded in In the fabric body.
- 13. a kind of fabric according to claim 12, it is characterised in that the film layer is polyurethane material or thermoplasticity The waterproof ventilated membrane that polyurethane elastomer makes.
- A kind of 14. fabric according to claim 10, it is characterised in that the fabric body include cotton, viscose, terylene, One or more of fiber blended fabrics in polyamide fibre and spandex, the cotton, viscose, terylene, polyamide fibre and spandex be true qualities, bleaching, Brighten or dye.
- 15. a kind of fabric according to claim 14, it is characterised in that the fiber blended fabric is knitting or tatting.
- 16. a kind of fabric according to claim 15, it is characterised in that the fiber blended fabric is plain.
- A kind of 17. manufacture craft of fabric, it is characterised in that including：Choose fabric body；Configure concentrator；The concentrator configured is coated in the fabric body of selection and printing pattern, stamp is after 80~100 DEG C drying, 140~160 DEG C bake, formed functional layer.
- 18. the manufacture craft of a kind of fabric according to claim 17, it is characterised in that also include：Water-proofing treatment, it is described Water-proofing treatment includes：It is 1 by fabric input bath raio：In 8~15 solution, after room temperature immersion, padding machine, 100 DEG C of drying 3~5 are crossed Minute, then 140~160 DEG C bake 40~90 seconds.
- A kind of 19. manufacture craft of fabric according to claim 18, it is characterised in that the solution composition is 8~ 12%owf waterproofing agent, 6~8%owf crosslinking agent, remaining is deionized water.
- 20. the manufacture craft of a kind of fabric according to claim 17, it is characterised in that the concentrator will for right Seek the concentrator described in 1-9 any one.