CN107388733A - A kind of Ardealite block brick microwave drying process - Google Patents
A kind of Ardealite block brick microwave drying process Download PDFInfo
- Publication number
- CN107388733A CN107388733A CN201710549666.6A CN201710549666A CN107388733A CN 107388733 A CN107388733 A CN 107388733A CN 201710549666 A CN201710549666 A CN 201710549666A CN 107388733 A CN107388733 A CN 107388733A
- Authority
- CN
- China
- Prior art keywords
- microwave
- drying
- time
- ardealite
- dried
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of Ardealite block brick microwave drying process, it includes step：Drying, microwave operation three times is carried out to the Ardealite block brick after shaping, is most dried after under natural conditions.It is an advantage of the invention that：Realize and higher drying effect is can be achieved with shorter tunnel, so as to cost of saving the area；And the microwave generation system described in this technique belongs to green energy resource based on electric energy, it is possible to reduce the discharge capacity of carbon dioxide in production process, reduces pollution.
Description
Technical field
The present invention relates to building material field, and in particular to a kind of Ardealite block brick microwave drying process.
Background technology
Ardealite is a kind of solid waste, is mainly derived from phophatic fertilizer production process.At present, ardealite utilization rate is relatively low,
It is larger to ambient contamination mainly based on stacking.Ardealite is used to make building block brick, can both realize solid waste
Recycling, and can are beautified the environment.Ardealite is chronically at dampness, has harmful effect, main table to Ardealite block brick
It is now：Intensity decreases, the raw bacterium in surface, return frost etc..Thus Ardealite block needs to dry in a short time after shaping.And in reality
In production process, Ardealite block yield is limited by drying time is long, and Ardealite block brick stoving process is still immature.
The more difficult drying of Ardealite block, filled main reason is that the multi-pore structure of ardealite causes Ardealite block to contain large quantity of moisture
Reprimand is in pore.Gypsum block drying technology scheme application at present at present it is most be mainly tunnel type drying technique.Tunnel
Road formula stoving process can realize batch production.Existing tunnel formula stoving process exist floor space is larger, drying effect by
The problems such as being restricted to length of tunnel.Problem be present for existing stoving process, the present invention proposes microwave drying process being incorporated into
In ardealite drying course, to improve drying efficiency.How microwave drying process is incorporated into ardealite drying course, simultaneous
While caring for economic benefit, make drying course more efficient, be that the present invention needs to solve the problems, such as.
The content of the invention
The present invention provides a kind of Ardealite block brick microwave drying process, mainly solves existing tunnel formula stoving process, dries
Do the problems such as inefficient and drying effect is restricted by length of tunnel.The present invention can be realized under shorter length of tunnel, i.e.,
Excellent drying effect can be obtained, saves space, reduces land used cost.
The technical solution adopted by the present invention is：
A kind of Ardealite block brick microwave drying process, comprises the following steps：
Step 1：Ardealite block brick after shaping is being dried, first time microwave is carried out after drying；
Step 2：Ardealite block after first time microwave is dried, second of microwave is carried out after drying；
Step 3：Ardealite block after second of microwave is dried, third time microwave is carried out after drying；
Step 4：Ardealite block after third time microwave is dried；
Step 5：Gypsum block after drying is placed under natural conditions and dried.
Preferably Step 1: the drying temperature described in two and three is 60 DEG C -90 DEG C, drying time 30min-60min.
Preferably Step 1: the microwave time described in two and three is 1min-10min, microwave frequency 2400Hz-
2500Hz。
Compared with prior art, it is an advantage of the invention that：1st, the present invention solves tunnel type drying kiln drying effect by its length
The problem of restriction, realize and higher drying effect is can be achieved with shorter tunnel, so as to cost of saving the area；2nd, this technique
Described microwave generation system belongs to green energy resource based on electric energy, it is possible to reduce the discharge capacity of carbon dioxide in production process,
Reduce pollution.
Embodiment：
Embodiment 1
Take experiment use the Ardealite block brick 32kg being just molded, size for length be respectively 666mm, 333mm, 500mm.
Step 1：Ardealite block brick after shaping is being dried, drying temperature is 60 DEG C, drying time 30min, is dried
First time microwave is carried out after dry, the microwave time is 5min, microwave frequency 2400Hz；
Step 2：Ardealite block after first time microwave is dried, drying temperature is 60 DEG C, drying time 30min, drying
After carry out second of microwave, the microwave time is 5min, microwave frequency 2400Hz；
Step 3：Ardealite block after second of microwave is dried, drying temperature is 60 DEG C, drying time 30min, drying
Third time microwave is carried out afterwards, and the microwave time is 5min, microwave frequency 2400Hz；
Step 4：Ardealite block after third time microwave is dried；
Step 5：Gypsum block after drying is placed under natural conditions and dried.
Embodiment 2
Take experiment use the Ardealite block brick 32kg being just molded, size for length be respectively 666mm, 333mm, 500mm.
Step 1：Ardealite block brick after shaping is being dried, drying temperature is 80 DEG C, drying time 40min, is dried
First time microwave is carried out after dry, the microwave time is 7min, microwave frequency 2450Hz；
Step 2：Ardealite block after first time microwave is dried, drying temperature is 80 DEG C, drying time 40min, drying
After carry out second of microwave, the microwave time is 7min, microwave frequency 2450Hz；
Step 3：Ardealite block after second of microwave is dried, drying temperature is 80 DEG C, drying time 40min, drying
Third time microwave is carried out afterwards, and the microwave time is 7min, microwave frequency 2450Hz；
Step 4：Ardealite block after third time microwave is dried；
Step 5：Gypsum block after drying is placed under natural conditions and dried.
Embodiment 3
Take experiment use the Ardealite block brick 32kg being just molded, size for length be respectively 666mm, 333mm, 500mm.
Step 1：Ardealite block brick after shaping is being dried, drying temperature is 90 DEG C, drying time 60min, is dried
First time microwave is carried out after dry, the microwave time is 10min, microwave frequency 2500Hz；
Step 2：Ardealite block after first time microwave is dried, drying temperature is 90 DEG C, drying time 60min, drying
After carry out second of microwave, the microwave time is 10min, microwave frequency 2500Hz；
Step 3：Ardealite block after second of microwave is dried, drying temperature is 90 DEG C, drying time 60min, drying
Third time microwave is carried out afterwards, and the microwave time is 10min, microwave frequency 2500Hz；
Step 4：Ardealite block after third time microwave is dried；
Step 5：Gypsum block after drying is placed under natural conditions and dried.
Detection, wherein 1 each step stage of embodiment are sampled to the gypsum block in each step in embodiment 1-3 respectively
Sampling result be shown in Table 1：
Table 1
The sampling result of 2 each step stage of embodiment is shown in Table 2：
Table 2
The sampling result of 3 each step stage of embodiment is shown in Table 3：
Table 3
As seen from the above table, the present invention, which realizes, can be achieved with higher drying effect in shorter tunnel, so as to save the area into
This；And the microwave generation system described in this technique belongs to green energy resource based on electric energy, it is possible to reduce titanium dioxide in production process
The discharge capacity of carbon, reduce pollution.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, for the skill of this area
For art personnel, the present invention can have various modifications and variations.Within the spirit and principles of the invention, that is made any repaiies
Change, equivalent substitution, improvement etc., should be included in the scope of the protection.
Claims (3)
1. a kind of Ardealite block brick microwave drying process, it is characterised in that comprise the following steps：
Step 1：Ardealite block brick after shaping is being dried, first time microwave is carried out after drying；
Step 2：Ardealite block after first time microwave is dried, second of microwave is carried out after drying；
Step 3：Ardealite block after second of microwave is dried, third time microwave is carried out after drying；
Step 4：Ardealite block after third time microwave is dried；
Step 5：Gypsum block after drying is placed under natural conditions and dried.
2. Ardealite block brick microwave drying process according to claim 1, it is characterised in that：Step 1: in two and three
Described drying temperature is 60 DEG C -90 DEG C, drying time 30min-60min.
3. Ardealite block brick microwave drying process according to claim 1, it is characterised in that：Step 1: in two and three
The described microwave time is 1min-10min, microwave frequency 2400Hz-2500Hz.