CN106146762A - A kind of method of rapeseed meal synthesis hydroscopic high-molecular resin - Google Patents
A kind of method of rapeseed meal synthesis hydroscopic high-molecular resin Download PDFInfo
- Publication number
- CN106146762A CN106146762A CN201510102447.4A CN201510102447A CN106146762A CN 106146762 A CN106146762 A CN 106146762A CN 201510102447 A CN201510102447 A CN 201510102447A CN 106146762 A CN106146762 A CN 106146762A
- Authority
- CN
- China
- Prior art keywords
- rapeseed meal
- water
- solution
- molecular resin
- hydroscopic high
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The method that the invention discloses a kind of rapeseed meal synthesis hydroscopic high-molecular resin, configures sodium acrylate solution；Rapeseed meal and water are inserted in reactor, at 80 DEG C of gelatinizing 1h, after cooling；Add the sodium acrylate solution containing cross-linking agent, under nitrogen atmosphere after stirring 30min, be replaced into oxygen, add initiator；It is warming up to 55 DEG C of reaction 1-5h；It is cooled to room temperature；It is dried, splits, dries, pulverizes, cross 150 mesh sieves, pack and get final product.Present invention can apply to large-scale production, opened up the value of Semen Allii Tuberosi, have the advantage that cost is low, produce and control simply, the performance of gained water-absorbing resin is good.Not only water absorption, water-retaining property are splendid, and as modifying agent and the water-retaining agent of soil, it can also improve the crumb structure of soil, increase breathability and the water penetration of soil, reduce the temperature difference in soil daytime and evening；The effect of fertilizer, pesticide can also be improved, strengthen drought-resistant ability.
Description
Technical field
The present invention relates to water-absorbing resins field, the method for a kind of rapeseed meal synthesis hydroscopic high-molecular resin.
Background technology
Rapeseed meal is the by-product of Semen Brassicae campestris, the crude protein content about 36% of rapeseed meal, and aminoacid composition relatively balances, sulfur-bearing
Amino acid content is high, and methionine, lysine content are the highest, but less than bean cake, and arginine content is low.The carbon of rapeseed meal
Mostly hydrate is stodgy pentose, containing 8% pentosan, crude fiber content 10-12%, therefore available energy water
Flat low, less than bean cake and the energy of Semen arachidis hypogaeae dregs, but higher than cottonseed meal.The nicotinic acid of rapeseed meal and content of choline are high, carotene,
Vitamin D equal size is low；Calcium, phosphorus, selenium, Fe content height in mineral, but the 60-70% of phosphorus content belongs to phytate phosphorus, utilizes
Rate is low.
High-molecular water-absorption water-retention resin is the novel high polymer functional material that development in recent years is got up, owing to water absorption is very strong, and tool
There are the ability absorbing the most thousands of times of moisture of own wt hundred times, and the moisture that release absorbs when arid, thus can be in work
The aspects such as industry, agricultural and daily life are applied.In rapeseed meal, introduce acrylic monomers carry out combined polymerization, dish can be made
The seed dregs of rice become a kind of material with super-strong moisture absorbing water conservation.Also do not have above materials application at present in preparing macromolecule water uptake guarantor
The report of water-resin.
Summary of the invention
The method that it is an object of the invention to provide the splendid rapeseed meal synthesis hydroscopic high-molecular resin of a kind of water absorption, water-retaining property,
With the problem solving to propose in above-mentioned background technology.
For achieving the above object, the present invention provides following technical scheme:
A kind of method of rapeseed meal synthesis hydroscopic high-molecular resin, concrete steps include:
1) configuration sodium acrylate solution；The acrylic acid of 120g is dissolved in 50ml deionized water, forms acrylic acid solution；
50g sodium hydroxide 150ml water dissolution is become sodium hydroxide solution, after being mixed with sodium hydroxide solution by acrylic acid solution
Prepare sodium acrylate solution；
2) 5-10g rapeseed meal and 50ml water are inserted in reactor, and at 80 DEG C of gelatinizing 1h, be cooled to 40 DEG C；To propylene
Acid sodium solution adds 0.2-0.3g cross-linking agent, and the sodium acrylate solution adding cross-linking agent is inserted in reactor, at nitrogen
Atmosphere encloses lower stirring 30min,
3) displacement nitrogen is to become oxygen atmosphere in oxygen makes reactor, adds 0.19-0.2g initiator；It is warming up to 55
DEG C reaction 1-5h；
4) it is cooled to room temperature；Being dried to biodiversity content is 5-15%, segmentation, 70 DEG C of drying, pulverizes, mistake 150 mesh sieves,
Pack and get final product.
As the further scheme of the present invention: described rapeseed meal can directly use or re-use after treatment；Wherein process
Process: after being soaked by rapeseed meal, squeezes into pressure filter the solution after immersion and carries out filter pressing, and the filtrate after filter pressing is dried
Dry standby i.e. obtain the rapeseed meal after process.
As the further scheme of the present invention: the degree of neutralization of described sodium acrylate solution is 75%.
As the further scheme of the present invention: described cross-linking agent uses N, N '-methylene-bisacrylamide solution.
As the further scheme of the present invention: described initiator uses potassium peroxydisulfate.
Compared with prior art, the invention has the beneficial effects as follows: a kind of Semen Allii Tuberosi product synthesis macromolecule provided by the present invention is inhaled
The method of water-resin, can be applicable to large-scale production, has opened up the value of Semen Allii Tuberosi, has the advantage that cost is low, produces control
System is simple, and the performance of gained water-absorbing resin is good.The soil that the super absorbent resin prepared in the process of the present invention is prepared as base material
Water-retaining agent, has good water absorbing properties.Water absorption >=450, moisture-holding capacity >=40, for soil have good water conservation,
Soil moisture conservation performance, and water retention property is sustainable for many years.Hydroscopic high-molecular resin not only water absorption, water-retaining property are splendid, as soil
Modifying agent and water-retaining agent, it can also improve the crumb structure of soil, increase breathability and the water penetration of soil, reduce soil
Earth daytime and the temperature difference in evening.Fertilizer, pesticide can also be absorbed simultaneously, prevent fertilizer, pesticide and soil erosion, and make fertilizer
Material, agricultural, water are slowly released, and improve fertilizer, the effect of pesticide, and are greatly enhanced drought-resistant ability.
The present invention is that the deep processing of Semen Allii Tuberosi product opens an approach with application.In terms of Tailings Dam, heavy metal is all extracted
Rear addition hydroscopic high-molecular resin, the arable land that can realize reclaiming, afforest, plant trees, sandy soilization transformation, reach heavy metal-polluted
Dye administers purpose, simultaneously can be used for the pollution control of flyash stack-up-yard, after improvement and can realize second ploughing, for enterprise's extra earning
Abundant profit.
Accompanying drawing explanation
Fig. 1 is the process chart of the present invention.
Detailed description of the invention
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, aobvious
So, described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under not making creative work premise, all
Belong to the scope of protection of the invention.
Embodiment 1
Refer to Fig. 1, in the embodiment of the present invention, the method for a kind of rapeseed meal synthesis hydroscopic high-molecular resin, concrete steps bag
Include:
1) acrylic acid of 120g is dissolved in 50ml deionized water, forms acrylic acid solution.
2) 50g sodium hydroxide 150ml water dissolution is become sodium hydroxide solution.
3) sodium hydroxide solution is added slowly in acrylic acid solution, is configured to the sodium acrylate solution that degree of neutralization is 75% standby.
4) 5g rapeseed meal and 50ml distilled water are added in 250ml there-necked flask at 80 DEG C of gelatinizing 1h, be cooled to 40 DEG C.
0.2g cross-linking agent N, N '-methylene-bisacrylamide solution, juxtaposition is added in the sodium acrylate solution that degree of neutralization is 75%
Entering in there-necked flask, stir 30min under nitrogen atmosphere, then displacement nitrogen is to become oxygen atmosphere in oxygen makes reactor,
Add initiator potassium persulfate 0.2g.It is warming up to 55 DEG C of reaction 1h, is cooled to room temperature.
5) it is dried to suitable degree, segmentation, 70 DEG C of drying, pulverizing, 150 mesh packagings of sieving.
Embodiment 2
Refer to Fig. 1, in the embodiment of the present invention, the method for a kind of rapeseed meal synthesis hydroscopic high-molecular resin, concrete steps bag
Include:
1), after rapeseed meal powder being soaked, the solution after immersion is squeezed into pressure filter and carries out filter pressing, the filtrate after filter pressing
Carry out dry for standby.
2) acrylic acid of 120g is dissolved in 50ml deionized water, forms acrylic acid solution.
3) 50g sodium hydroxide 150ml water dissolution is become sodium hydroxide solution.
4) sodium hydroxide solution is added slowly in acrylic acid solution, is configured to sodium acrylate solution standby.
5) 10g rapeseed meal after preparation and 50ml distilled water are added in 250ml there-necked flask at 80 DEG C of gelatinizing 1h,
It is cooled to 40 DEG C.
6) in the sodium acrylate solution that degree of neutralization is 75%, 0.3g cross-linking agent N is added, N '-methylene-bisacrylamide solution,
Being placed in there-necked flask, stir 30min under nitrogen atmosphere, then displacement nitrogen is to become oxygen in oxygen makes reactor
Environment, adds initiator potassium persulfate 0.19g.It is warming up to 55 DEG C of reaction 2h, is cooled to room temperature.
7) it is dried to suitable degree, segmentation, 70 DEG C of drying, pulverizing, 150 mesh packagings of sieving.
Embodiment 3
Refer to Fig. 1, in the embodiment of the present invention, the method for a kind of rapeseed meal synthesis hydroscopic high-molecular resin, concrete steps bag
Include:
1) acrylic acid of 120g is dissolved in 50ml deionized water, forms acrylic acid solution.
2) 60g sodium hydroxide 150ml water dissolution is become sodium hydroxide solution.
3) sodium hydroxide solution is added slowly in acrylic acid solution, is configured to sodium acrylate solution standby.
4) 8g rapeseed meal powder and 50ml distilled water are added in 250ml there-necked flask at 80 DEG C of gelatinizing 1h, be cooled to 40
℃。
5) adding 0.24g cross-linking agent N in the sodium acrylate solution that degree of neutralization is 75%, N '-methylene-bisacrylamide is molten
Liquid, is placed in there-necked flask, stirs 30min under nitrogen atmosphere, and then displacement nitrogen is to become in oxygen makes reactor
Oxygen atmosphere, adds initiator potassium persulfate 0.192g.It is warming up to 55 DEG C of reaction 5h, is cooled to room temperature.
6) it is dried to suitable degree, segmentation, 70 DEG C of drying, pulverizing, 150 mesh packagings of sieving.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, and do not carrying on the back
In the case of the spirit or essential attributes of the present invention, it is possible to realize the present invention in other specific forms.Therefore, no matter from
From the point of view of which point, all should regard embodiment as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all by fall in the implication of equivalency and scope of claim
Change is included in the present invention.
Although moreover, it will be appreciated that this specification is been described by according to embodiment, but the most each embodiment only comprises
One independent technical scheme, this narrating mode of description is only the most for clarity sake, and those skilled in the art should be by
Description is as an entirety, and the technical scheme in each embodiment can also be through appropriately combined, and forming those skilled in the art can
With other embodiment party understood.
Claims (5)
1. the method for a rapeseed meal synthesis hydroscopic high-molecular resin, it is characterised in that concrete steps include:
1) configuration sodium acrylate solution: be dissolved in 50ml deionized water by the acrylic acid of 120g, forms acrylic acid solution；
50g sodium hydroxide 150ml water dissolution is become sodium hydroxide solution, after being mixed with sodium hydroxide solution by acrylic acid solution
Prepare sodium acrylate solution；
2) 5-10g rapeseed meal and 50ml water are inserted in reactor, and at 80 DEG C of gelatinizing 1h, be cooled to 40 DEG C；To propylene
Acid sodium solution adds 0.2-0.3g cross-linking agent, and the sodium acrylate solution adding cross-linking agent is inserted in reactor, at nitrogen
Atmosphere encloses lower stirring 30min,
3) displacement nitrogen is to become oxygen atmosphere in oxygen makes reactor, adds 0.19-0.2g initiator；It is warming up to 55
DEG C reaction 1-5h；
4) it is cooled to room temperature；Being dried to biodiversity content is 5-15%, segmentation, 70 DEG C of drying, pulverizes, mistake 150 mesh sieves,
Pack and get final product.
The method of rapeseed meal the most according to claim 1 synthesis hydroscopic high-molecular resin, it is characterised in that described Semen Allii Tuberosi
The dregs of rice can directly use or re-use after treatment；The process wherein processed: after being soaked by rapeseed meal, after soaking
Solution is squeezed into pressure filter and is carried out filter pressing, and the filtrate after filter pressing carries out the rapeseed meal dried after being processed.
The method of rapeseed meal the most according to claim 1 synthesis hydroscopic high-molecular resin, it is characterised in that described propylene
The degree of neutralization of acid sodium solution is 75%.
The method of rapeseed meal the most according to claim 1 synthesis hydroscopic high-molecular resin, it is characterised in that described crosslinking
Agent uses N, N '-methylene-bisacrylamide solution.
The method of rapeseed meal the most according to claim 1 synthesis hydroscopic high-molecular resin, it is characterised in that described initiation
Agent uses potassium peroxydisulfate.