CN104592829A - Water-based wood rib-expansion-resistant varnish primer and preparation method thereof - Google Patents
Water-based wood rib-expansion-resistant varnish primer and preparation method thereof Download PDFInfo
- Publication number
- CN104592829A CN104592829A CN201410840394.1A CN201410840394A CN104592829A CN 104592829 A CN104592829 A CN 104592829A CN 201410840394 A CN201410840394 A CN 201410840394A CN 104592829 A CN104592829 A CN 104592829A
- Authority
- CN
- China
- Prior art keywords
- water
- priming paint
- dispersion
- bulging tendons
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a water-based wood rib-expansion-resistant varnish primer and a preparation method thereof, particularly a water-based wood varnish primer, belonging to the field of architectural decoration paints. The primer is characterized by using a film forming matter as a single-component acrylic resin dispersion, and has the advantages of high drying speed, favorable sanding performance and rib expansion resistance. The water-based wood rib-expansion-resistant varnish primer comprises 80-90 parts of water-based acrylic resin dispersion, 0.1-0.2 part of pH regulator, 3-6 parts of film forming assistant, 0.5-1.5 parts of antifreezing agent, 0.1-0.3 part of defoaming agent, 0.1-0.2 part of anticorrosive bactericide, 0.4-1.2 parts of wetting and leveling agent, 0.3-0.8 part of thickener and 4-10 parts of water. The water-based wood varnish primer is used as a wood coating sealing primer, has the advantages of excellent rib-expansion-resistant effect, high sanding performance, high drying speed and favorable adhesion with the substrate, and can protect the substrate from being destroyed.
Description
Technical field
The present invention relates to architectural decoration paint field, be specifically related to clear priming paint of the anti-bulging tendons of a kind of aqueous wooden ware and preparation method thereof.
Background technology
Along with the propelling of China's process of industrialization, environmental problem highlights day by day, and haze and photochemical pollution etc. have had a strong impact on the health of people.Since entering 21 century, environmental regulation improves further, to alleviate the research of the new coating of low VOC or the Diamond Search discharge launched for the purpose of earth load, just increasingly becomes the focus of research and development.Aqueous woodware paint is because of its low-carbon (LC), environmental protection and attention.But current aqueous woodware paint is owing to having many technological difficulties, and as bulging tendons, the saturating Huang of bleeding etc., these technological difficulties hinder the application and development of aqueous woodware paint to a great extent.After water by timber, water infiltrates along the microgap in xylon pipe and wood grain, makes it expand and becomes large, and outstanding wood surface, can not restore after drying, so there will be wood grain projection, phenomenon and the bulging tendons such as particle, setation thorn after wood finishing water-miscible paint.As effectively do not prevented the appearance of wood surface bulging tendons, can affect next step application, make overall painting effect poor, this is seriously constraining the development of aqueous woodware paint.
Summary of the invention
In order to solve incident bulging tendons technological difficulties in aqueous wooden ware primer painting process, the invention provides clear priming paint of the anti-bulging tendons of a kind of aqueous wooden ware and preparation method thereof.The clear priming paint of the anti-bulging tendons of aqueous wooden ware prepared by the present invention is used for solid wood application seal coat and has excellent anti-bulging tendons effect and easy grinability, fast drying and good with substrate adhesion, and ground can be protected not to be damaged.
Technical scheme of the present invention provides the clear priming paint of the anti-bulging tendons of a kind of aqueous wooden ware, formulated by following weight proportion primarily of following raw material:
Water-borne acrylic resin dispersion 80-90 part,
PH adjusting agent 0.1-0.2 part,
Film coalescence aid 3-6 part,
Frostproofer 0.5-1.5 part,
Defoamer 0.1-0.3 part,
Anticorrosion and bactericidal agent 0.1-0.2 part,
Moistening flatting agent 0.4-1.2 part,
Thickening material 0.3-0.8 part,
Water 4-10 part.
In said components, water-borne acrylic resin dispersion, film coalescence aid and moistening flatting agent are the components of necessity of the clear priming paint of the preparation anti-bulging tendons of aqueous wooden ware of the present invention;
Described filmogen adopts water-borne acrylic resin dispersion; refer to that outward appearance is that oyster white is translucent; admittedly containing 46 ± 1%; minimum film-forming temperature (MFFT) is styrenated acrylic's dispersion with nucleocapsid structure of 20-30 DEG C; base material can be protected not to be damaged and to have good cohesive force with substrate surface; can effectively prevent timber bulging tendons, rate of drying is fast, easily polishes.
Described film coalescence aid is one or both arbitrary combination in dipropylene glycol monomethyl ether, Dipropylene glycol mono-n-butyl Ether, is conducive to paint liquid homogeneous film formation at low temperatures;
Described pH adjusting agent is DOW Chemical AMP-95, makes system pH keep slight alkalinity;
Described frostproofer is propylene glycol, plays the effect reducing paint liquid freezing point and prevent paint liquid low temperature freezing;
Described anticorrosion and bactericidal agent is isothiazolinone disinfecting agent, plays antisepsis and sterilization effect;
Described defoamer is the polydimethylsiloxane defoamer of special modification, contributes to suppressing and eliminating bubble, prevents from producing bubble in production and construction process;
Described moistening flatting agent is hydrophobically modified urethane rheology modifier and Siloxane-Oxyalkylene Copolymers solution, hydrophobically modified urethane rheology modifier has splendid flowing and levelling property, and it is good to the thickening effectiveness of ACRYLIC EMULSION, Siloxane-Oxyalkylene Copolymers solution strongly can reduce surface tension thus promote the wetting of ground, also promotes flowing and levelling simultaneously;
Described thickening material is non-ionic polyurethane associative thickener, for regulation system viscosity, improves the effect of anti-splashing and increase paint film fullness ratio;
Described water is general tap water, for regulation system viscosity and promotion dispersion.
The collocation of said components and the weight proportion of each component are determined by great many of experiments; aforesaid combination and weight proportion make the clear priming paint of the anti-bulging tendons of the aqueous wooden ware prepared by the present invention have excellent anti-bulging tendons effect and easy grinability for solid wood application seal coat; fast drying and good with substrate adhesion, can protect ground not to be damaged.
The concrete steps of the anti-bulging tendons of a kind of aqueous wooden ware of the present invention clear priming paint preparation method are as follows:
(1) select suitable dispersion cylinder, first add water-borne acrylic resin dispersion 80-90 part, starting dispersion machine adjustment rotating speed is 300-500 rev/min, disperses 1 minute;
(2) improving rotating speed is 500-800 rev/min, adds pH adjusting agent 0.1-0.2 part, frostproofer 0.5-1.5 part, dispersion 3-5 minute;
(3) container is separately got, add film coalescence aid 3-6 part, anticorrosion and bactericidal agent 0.1-0.2 part and water 4-10 part, mix, slowly add under rotating speed is 500-800 rev/min in above-mentioned dispersion cylinder, then defoamer 0.1-0.3 part, flow agent 0.4-1.2 part and thickening material 0.3-0.8 part is added successively, dispersion 10-20 minute, crosses 300 mesh filter screens.
Compared with prior art, advantage of the present invention is: (1) price is relatively cheap: filmogen is a kind of styrenated acrylic's dispersion of nucleocapsid structure, price be 12-16 unit/kilogram, other filmogen prices have larger advantage relatively; (2) rate of drying is fast, anti-bulging tendons is excellent: what the present invention adopted is styrenated acrylic's dispersion with nucleocapsid structure that particle diameter is little, filmogen to penetrate into faster in the fibre pipe of timber and the microgap of wood grain than water and can fast filming, avoids timber to absorb water bulging tendons.(3) excellent grinability: filmogen of the present invention is styrenated acrylic's dispersion with stone soft shell construction, shows higher hardness after film forming, ensure that paint film has good sanding property, 600 order sand papering not scab paper.(4) with ground, there is excellent sticking power: good with the sticking power of ground, ground can be protected not to be damaged.
Embodiment
Below by embodiment, the present invention will be further described:
In following embodiment, all according to each embodiment experimental result of national standard (GB/T23999-2009) category-B product test:
Embodiment one:
The clear priming paint of a kind of anti-bulging tendons of aqueous wooden ware, formulated by following weight proportion primarily of following raw material:
Water-borne acrylic resin dispersion 80-90 part, pH adjusting agent 0.1-0.2 part, film coalescence aid 3-6 part, frostproofer 0.5-1.5 part, defoamer 0.1-0.3 part, anticorrosion and bactericidal agent 0.1-0.2 part, moistening flatting agent 0.4-1.2 part, thickening material 0.3-0.8 part, water 4-10 part.
Concrete steps prepared by the clear priming paint of the anti-bulging tendons of this aqueous wooden ware are as follows:
(1) select suitable dispersion cylinder, first add water-borne acrylic resin dispersion 90 parts, starting dispersion machine adjustment rotating speed is 300-500 rev/min, disperses 1 minute;
(2) improving rotating speed is 500-800 rev/min, adds pH adjusting agent 0.2 part, frostproofer 1 part, dispersion 3-5 minute;
(3) container is separately got, add film coalescence aid 5 parts, anticorrosion and bactericidal agent 0.1 part and 4 parts, water, mix, slowly add under rotating speed is 500-800 rev/min in above-mentioned dispersion cylinder, then defoamer 0.1 part, moistening flatting agent 10.4 parts and thickening material 0.5 part is added successively, dispersion 10-20 minute, crosses 300 mesh filter screens.
Embodiment two:
The clear priming paint of a kind of anti-bulging tendons of aqueous wooden ware, formulated by following weight proportion primarily of following raw material:
Water-borne acrylic resin dispersion 80-90 part, pH adjusting agent 0.1-0.2 part, film coalescence aid 3-6 part, frostproofer 0.5-1.5 part, defoamer 0.1-0.3 part, anticorrosion and bactericidal agent 0.1-0.2 part, moistening flatting agent 0.4-1.2 part, thickening material 0.3-0.8 part, water 4-10 part.
Concrete steps prepared by the clear priming paint of the anti-bulging tendons of this aqueous wooden ware are as follows:
(1) select suitable dispersion cylinder, first add water-borne acrylic resin dispersion 84.8 parts, starting dispersion machine adjustment rotating speed is 300-500 rev/min, disperses 1 minute;
(2) improving rotating speed is 500-800 rev/min, adds pH adjusting agent 0.1 part, frostproofer 1 part, dispersion 3-5 minute;
(3) container is separately got, add film coalescence aid 5.5 parts, anticorrosion and bactericidal agent 0.1 part and 6.5 parts, water, mix, slowly add under rotating speed is 500-800 rev/min in above-mentioned dispersion cylinder, then defoamer 0.2 part, moistening flatting agent 1 part and thickening material 0.3 part is added successively, dispersion 10-20 minute, crosses 300 mesh filter screens.
Embodiment three:
The clear priming paint of a kind of anti-bulging tendons of aqueous wooden ware, formulated by following weight proportion primarily of following raw material:
Water-borne acrylic resin dispersion 80-90 part, pH adjusting agent 0.1-0.2 part, film coalescence aid 3-6 part, frostproofer 0.5-1.5 part, defoamer 0.1-0.3 part, anticorrosion and bactericidal agent 0.1-0.2 part, moistening flatting agent 0.4-1.2 part, thickening material 0.3-0.8 part, water 4-10 part.
Concrete steps prepared by the clear priming paint of the anti-bulging tendons of this aqueous wooden ware are as follows:
(1) select suitable dispersion cylinder, first add water-borne acrylic resin dispersion 86.2 parts, starting dispersion machine adjustment rotating speed is 300-500 rev/min, disperses 1 minute;
(2) improving rotating speed is 500-800 rev/min, adds pH adjusting agent 0.15 part, frostproofer 1.5 parts, dispersion 3-5 minute;
(3) container is separately got, add film coalescence aid 4.5 parts, anticorrosion and bactericidal agent 0.15 part and 6 parts, water, mix, slowly add under rotating speed is 500-800 rev/min in above-mentioned dispersion cylinder, then defoamer 0.2 part, moistening flatting agent 0.8 part and thickening material 0.6 part is added successively, dispersion 10-20 minute, crosses 300 mesh filter screens.
Embodiment four:
The clear priming paint of a kind of anti-bulging tendons of aqueous wooden ware, formulated by following weight proportion primarily of following raw material:
Water-borne acrylic resin dispersion 80-90 part, pH adjusting agent 0.1-0.2 part, film coalescence aid 3-6 part, frostproofer 0.5-1.5 part, defoamer 0.1-0.3 part, anticorrosion and bactericidal agent 0.1-0.2 part, moistening flatting agent 0.4-1.2 part, thickening material 0.3-0.8 part, water 4-10 part.
Concrete steps prepared by the clear priming paint of the anti-bulging tendons of this aqueous wooden ware are as follows:
(1) select suitable dispersion cylinder, first add water-borne acrylic resin dispersion 83 parts, starting dispersion machine adjustment rotating speed is 300-500 rev/min, disperses 1 minute;
(2) improving rotating speed is 500-800 rev/min, adds pH adjusting agent 0.1 part, frostproofer 1.5 parts, dispersion 3-5 minute;
(3) container is separately got, add film coalescence aid 6 parts, anticorrosion and bactericidal agent 0.15 part and 7.3 parts, water, mix, slowly add under rotating speed is 500-800 rev/min in above-mentioned dispersion cylinder, then defoamer 0.2 part, moistening flatting agent 1 part and thickening material 0.8 part is added successively, dispersion 10-20 minute, crosses 300 mesh filter screens.
Embodiment five:
The clear priming paint of a kind of anti-bulging tendons of aqueous wooden ware, formulated by following weight proportion primarily of following raw material:
Water-borne acrylic resin dispersion 80-90 part, pH adjusting agent 0.1-0.2 part, film coalescence aid 3-6 part, frostproofer 0.5-1.5 part, defoamer 0.1-0.3 part, anticorrosion and bactericidal agent 0.1-0.2 part, moistening flatting agent 0.4-1.2 part, thickening material 0.3-0.8 part, water 4-10 part.
Concrete steps prepared by the clear priming paint of the anti-bulging tendons of this aqueous wooden ware are as follows:
(1) select suitable dispersion cylinder, first add water-borne acrylic resin dispersion 80 parts, starting dispersion machine adjustment rotating speed is 300-500 rev/min, disperses 1 minute;
(2) improving rotating speed is 500-800 rev/min, adds pH adjusting agent 0.1 part, frostproofer 0.5 part, dispersion 3-5 minute;
(3) container is separately got, add film coalescence aid 3 parts, anticorrosion and bactericidal agent 0.2 part and 10 parts, water, mix, slowly add under rotating speed is 500-800 rev/min in above-mentioned dispersion cylinder, then defoamer 0.3 part, moistening flatting agent 1.2 parts and thickening material 0.8 part is added successively, dispersion 10-20 minute, crosses 300 mesh filter screens.
In above each embodiment:
Water-borne acrylic resin dispersion is preferably good rich JF2025;
Water-soluble multifunctional auxiliary agent is preferably the AMP-95 multifunctional assistant of Tao Shi;
1293 of water-based defoamer preferred extra large river chemical industry;
Film coalescence aid is preferably DPNB or DPM of Eastman Chemical;
Water-based moistening flatting agent is preferably BYK346 and the ROHM AND HAAS RM2020 of BYK;
Water-borne preservative is preferably the RS of THOR;
Water-based thickener is preferably the RM8W of ROHM AND HAAS.
In above each embodiment, all detect product performance according to GB/T23999-2009 standard, detected result is as shown in the table:
Each embodiment time of drying (surface drying) of the table anti-bulging tendons of this aqueous wooden ware of 1.1-clear priming paint, grinability with spraying solid wood board plate effect and the sticking power experimental data with solid wood board
Can as apparent from table 1.1, time of drying (surface drying) < of each embodiment of the clear priming paint of the anti-bulging tendons of aqueous wooden ware of the present invention 15 minutes, the paint film 600 object sand papering not scab paper of the prepared clear priming paint of the anti-bulging tendons of aqueous wooden ware, to construct on solid wood board not bulging tendons and sticking power is good with the clear basecoat paint of the anti-bulging tendons of aqueous wooden ware of preparation.Therefore, the clear priming paint of aqueous wooden ware of the present invention is used for solid wood application seal coat and has excellent anti-bulging tendons effect and easy grinability, fast drying and good with substrate adhesion, and ground can be protected not to be damaged.
Above-mentioned embodiment is just explained in detail technical scheme of the present invention; the present invention has more than and is only confined to above-described embodiment; those skilled in the art should be understood that; every improvement on basis of the present invention according to above-mentioned principle and spirit, substitute, all should within protection scope of the present invention.
Claims (10)
1. the clear priming paint of the anti-bulging tendons of aqueous wooden ware, is characterized in that: formulated by following weight proportion primarily of following raw material:
Water-borne acrylic resin dispersion 80-90 part,
PH adjusting agent 0.1-0.2 part,
Film coalescence aid 3-6 part,
Frostproofer 0.5-1.5 part,
Defoamer 0.1-0.3 part,
Anticorrosion and bactericidal agent 0.1-0.2 part,
Moistening flatting agent 0.4-1.2 part,
Thickening material 0.3-0.8 part,
Water 4-10 part.
2. the clear priming paint of the anti-bulging tendons of aqueous wooden ware according to claim 1, it is characterized in that: described filmogen adopts water-borne acrylic resin dispersion, be outward appearance be that oyster white is translucent, admittedly containing 46 ± 1%, minimum film-forming temperature (MFFT) is styrenated acrylic's dispersion with nucleocapsid structure of 20-30 DEG C.
3. the clear priming paint of the anti-bulging tendons of aqueous wooden ware according to claim 1, is characterized in that: described film coalescence aid is one or both arbitrary combination in dipropylene glycol monomethyl ether, Dipropylene glycol mono-n-butyl Ether.
4. the clear priming paint of the anti-bulging tendons of aqueous wooden ware according to claim 1, is characterized in that: described pH adjusting agent is DOW Chemical AMP-95.
5. the clear priming paint of the anti-bulging tendons of aqueous wooden ware according to claim 1, is characterized in that: described frostproofer is propylene glycol.
6. the clear priming paint of the anti-bulging tendons of aqueous wooden ware according to claim 1, is characterized in that: described anticorrosion and bactericidal agent is isothiazolinone disinfecting agent.
7. the clear priming paint of the anti-bulging tendons of aqueous wooden ware according to claim 1, is characterized in that: described defoamer is the polydimethylsiloxane defoamer of special modification.
8. the clear priming paint of the anti-bulging tendons of aqueous wooden ware according to claim 1, is characterized in that: described moistening flatting agent is hydrophobically modified urethane rheology modifier and Siloxane-Oxyalkylene Copolymers solution.
9. the clear priming paint of the anti-bulging tendons of aqueous wooden ware according to claim 1, is characterized in that: described thickening material is non-ionic polyurethane associative thickener.
10. a preparation method for the clear priming paint of the anti-bulging tendons of aqueous wooden ware according to claim 1, is characterized in that: concrete steps are as follows:
(1) select suitable dispersion cylinder, first add water-borne acrylic resin dispersion 80-90 part, starting dispersion machine adjustment rotating speed is 300-500 rev/min, disperses 1 minute;
(2) improving rotating speed is 500-800 rev/min, adds pH adjusting agent 0.1-0.2 part, frostproofer 0.5-1.5 part, dispersion 3-5 minute;
(3) container is separately got, add film coalescence aid 3-6 part, anticorrosion and bactericidal agent 0.1-0.2 part and water 4-10 part, mix, slowly add under rotating speed is 500-800 rev/min in above-mentioned dispersion cylinder, then defoamer 0.1-0.3 part, flow agent 0.4-1.2 part and thickening material 0.3-0.8 part is added successively, dispersion 10-20 minute, crosses 300 mesh filter screens.