CN103668791A - Production method for non-woven fabric wet curtain - Google Patents

Abstract

The invention discloses a production method for a non-woven fabric wet curtain. The production method comprises the following steps of (1) mixing 0.2-0.3 part by mass of polyethylene glycol octylphenol ether, 0.3-0.4 part by mass of chlorine dioxide and 0.1 part by mass of carbon black, heating the mixture, uniformly mixing the mixture, adding 2-3 parts by mass of polypropylene in a molten state, 4-6 parts by mass of polyester, 5-6 parts by mass of viscose, 2-3 parts by mass of polyethylene and 7-8 parts by mass of acrylic fibers in the mixture, keeping the mixture molten and further uniformly mixing the mixture; and (2) spraying out the molten aggregates according to a basic technology of a melt-blown non-woven fabric via a spinneret plates to obtain a wet curtain material by using air flow or mechanical net formation. The non-woven fabric wet curtain produced by using the production method is high in water absorption effect and long in service life.

Description

The production method of wet nonwoven curtain

Technical field

The present invention relates to the production method of wet nonwoven curtain.

Background technology

Existing wet curtain material, when sharp draft and humidification, usually there will be airborne water-soluble peculiar smell, dust foreign material thoroughly not to filter out or lowers the temperature not obvious and the phenomenon such as drip, leak.Meanwhile, existing wet curtain material cannot meet the requirements such as client's height water suction, high air quantity, anti-mildew change, long service life in selection or technologic limitation.

Summary of the invention

The object of the present invention is to provide a kind of production method of wet nonwoven curtain, the wet nonwoven curtain that it is produced, its soaking effect is good, and the life-span is long.

For achieving the above object, technical scheme of the present invention is the production method of a kind of wet nonwoven curtain of design, comprises the steps:

1) 0.2-0.3 parts by mass Triton X-100,0.3-0.4 parts by mass chlorine dioxide, 0.1 parts by mass carbon black are mixed, intensification mixes, then join in the 2-3 parts by mass polypropylene, 4-6 parts by mass polyester, 5-6 parts by mass viscose, 2-3 parts by mass polyethylene, 7-8 parts by mass acrylic fibers of molten condition, keep molten condition and further mix;

2) by the basic technology of meltblown nonwoven fabric: by the pellet of above-mentioned melting, through spinnerets ejection, utilize air-flow or machinery to become net to obtain wet curtain material.

Advantage of the present invention and beneficial effect are: a kind of production method of wet nonwoven curtain is provided, and the wet nonwoven curtain that it is produced, its soaking effect is good, and the life-span is long.

The specific embodiment

Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples are only for technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.

The concrete technical scheme of implementing of the present invention is:

Embodiment 1

A production method for wet nonwoven curtain, comprises the steps:

1) 0.3 parts by mass Triton X-100,0.4 parts by mass chlorine dioxide, 0.1 parts by mass carbon black are mixed, intensification mixes, then join in the 3 parts by mass polypropylene, 6 parts by mass polyester, 6 parts by mass viscoses, 3 parts by mass polyethylene, 8 parts by mass acrylic fibers of molten condition, keep molten condition and further mix;

2) by the basic technology of meltblown nonwoven fabric: by the pellet of above-mentioned melting, through spinnerets ejection, utilize air-flow or machinery to become net to obtain wet curtain material.

Embodiment 2

A production method for wet nonwoven curtain, comprises the steps:

1) 0.2 parts by mass Triton X-100,0.3 parts by mass chlorine dioxide, 0.1 parts by mass carbon black are mixed, intensification mixes, then join in the 2 parts by mass polypropylene, 4 parts by mass polyester, 5 parts by mass viscoses, 2 parts by mass polyethylene, 7 parts by mass acrylic fibers of molten condition, keep molten condition and further mix;

2) by the basic technology of meltblown nonwoven fabric: by the pellet of above-mentioned melting, through spinnerets ejection, utilize air-flow or machinery to become net to obtain wet curtain material.

Embodiment 3

A production method for wet nonwoven curtain, comprises the steps:

1) 0.25 parts by mass Triton X-100,0.35 parts by mass chlorine dioxide, 0.1 parts by mass carbon black are mixed, intensification mixes, then join in the 2.3 parts by mass polypropylene, 4.6 parts by mass polyester, 5.6 parts by mass viscoses, 2.3 parts by mass polyethylene, 7.8 parts by mass acrylic fibers of molten condition, keep molten condition and further mix;

2) by the basic technology of meltblown nonwoven fabric: by the pellet of above-mentioned melting, through spinnerets ejection, utilize air-flow or machinery to become net to obtain wet curtain material.

The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (1)

1. the production method of wet nonwoven curtain, is characterized in that, comprises the steps:

1) 0.2-0.3 parts by mass Triton X-100,0.3-0.4 parts by mass chlorine dioxide, 0.1 parts by mass carbon black are mixed, intensification mixes, then join in the 2-3 parts by mass polypropylene, 4-6 parts by mass polyester, 5-6 parts by mass viscose, 2-3 parts by mass polyethylene, 7-8 parts by mass acrylic fibers of molten condition, keep molten condition and further mix;

2) by the basic technology of meltblown nonwoven fabric: by the pellet of above-mentioned melting, through spinnerets ejection, utilize air-flow or machinery to become net to obtain wet curtain material.