CN102051117A - High temperature resistant anticorrosive paint and preparation method thereof - Google Patents
High temperature resistant anticorrosive paint and preparation method thereof Download PDFInfo
- Publication number
- CN102051117A CN102051117A CN2009101883701A CN200910188370A CN102051117A CN 102051117 A CN102051117 A CN 102051117A CN 2009101883701 A CN2009101883701 A CN 2009101883701A CN 200910188370 A CN200910188370 A CN 200910188370A CN 102051117 A CN102051117 A CN 102051117A
- Authority
- CN
- China
- Prior art keywords
- component
- preparation
- high temperature
- black
- silicone resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of light industry, in particular to a high temperature resistant anticorrosive paint and a preparation method thereof. The invention provides a high temperature resistant anticorrosive paint which is efficient and stable and a preparation method thereof. The paint contains a component A, a component B and a component C. The component A comprises the following components by weight percent: 1.0-2.0% of bentonite and 3.0-6.0% of butyl acetate. The component B comprises the following components by weight percent: 6.0-10.0% of epoxy resin and 4.0-6.0% of amino resin. The component C comprises the following components by weight percent: 28.0-32.0% of organosilicon resin A, 3.0-7.0% of organosilicon resin B, 1.0-3.0% of organic inhibitor, 1.0-2.0% of color black, 1.0-2.0% of titanium dioxide powder, 10.0-15.0% of graphite black, 2.0-6.0% of high temperature iron black, 10.0-17.0% of talcum powder, 3.0-7.0% of aluminum tripolyphosphate and 3.0-6.0% of isobutanol.
Description
Technical field:
The invention belongs to the light industry technical field, more particularly, relate to a kind of fire-resistant anticorrosion paint and preparation method thereof.
Background technology:
High-temperature resistant coating as its name suggests, is exactly can be in a specified time; in the certain temperature section; stand the coating of oxidation corrosion and other dielectric corrosion under the hot environment, can generally divide organosilicon series and inorganic silicon series in the purpose of works better under the hot environment thereby reach the protection coated article.Accordingly, (between 100-1500 ℃) can reach anti-oxidant, corrosion-resistant and anti-thermal shock, can bear certain performance coating such as mechanical load under hot environment, and we are referred to as high-temperature resistant coating.
Being used for resistant to elevated temperatures heat stable resin has tetrafluoroethylene, polyarylsulphone (ether), polyimide, organosilicon etc., and silicone resin is a class that is most widely used in the heat resisting coating.The resistance toheat of coating is not only relevant with resin (base-material) with antiseptic property, simultaneously confidential relation is also arranged with pigment, stopping composition etc., pure silicone resin can use 300 ℃ of short-terms at 200～250 ℃ of life-time service, and heatproof can be up to 700～800 ℃ behind the adding thermotolerance color stuffing.But with the coating that common silicone resin is made, sticking power, shock-resistance, chemically-resistant and physical strength are not good.
Summary of the invention:
The present invention is exactly at the problems referred to above, and a kind of efficient, stable fire-resistant anticorrosion paint and preparation method thereof is provided.
In order to realize above-mentioned purpose of the present invention, proportioning of the present invention is: the A component: wilkinite is 1.0～2.0%, and N-BUTYL ACETATE is 3.0～6.0%; The B component: Resins, epoxy is 6.0～10.0%, and aminoresin is 4.0～6.0%; The C component: silicone resin A is 28.0～32.0%, silicone resin B is 3.0～7.0%, organic inhibitor is 1.0～3.0%, colour carbon black is 1.0～2.0%, and titanium dioxide is 1.0～2.0%, and graphite is black to be 10.0～15.0%, the high temperature iron oxide black is 2.0～6.0%, talcum powder is 10.0～17.0%, and aluminium triphosphate is 3.0～7.0%, and isopropylcarbinol is 3.0～6.0%.
Preparation method of the present invention is:
The preparation of A component: it is complete that organobentonite is diluted to volumetric expansion with N-BUTYL ACETATE;
The preparation of B component: Resins, epoxy is mixed fully with aminoresin;
The preparation of C component: silicone resin, color stuffing, auxiliary agent, solvent are measured in the adding shredder in accordance with regulations, be ground to fineness less than 30 μ m;
A, B are added among the C, continue to grind dispersion 5～10min, filtration, sealing, packing.
Beneficial effect of the present invention:
1. the present invention has good sticking power, impact resistance, chemical resistant properties and physical strength, and the resistance to elevated temperatures of having a mind to;
2. easy construction of the present invention can be widely used in the various high temperature resistant equipment;
Embodiment:
The present invention is to be base-material with the modified organic silicone resin, adding thermostable rustproof color stuffing, auxiliary agent and solvent composition.
Proportioning of the present invention is: the A component: wilkinite is 1.0～2.0%, and N-BUTYL ACETATE is 3.0～6.0%; The B component: Resins, epoxy is 6.0～10.0%, and aminoresin is 4.0～6.0%; The C component: silicone resin A is 28.0～32.0%, silicone resin B is 3.0～7.0%, organic inhibitor is 1.0～3.0%, colour carbon black is 1.0～2.0%, and titanium dioxide is 1.0～2.0%, and graphite is black to be 10.0～15.0%, the high temperature iron oxide black is 2.0～6.0%, talcum powder is 10.0～17.0%, and aluminium triphosphate is 3.0～7.0%, and isopropylcarbinol is 3.0～6.0%.
Graphite is black, high temperature is iron black, talcum powder, aluminium triphosphate be as main filler, and its effect is thermotolerance, the physical strength that improves coating.
Talcum powder, chemical formula are 3MgO4SiO
2H
2O is silicon-dioxide and magnesian combined type silicate, and stability is fine, high temperature resistantly reaches 900 ℃, water insoluble, organic solvent, cold acid and cold alkali, and density is suitable, is easy to disperse the most suitable high-temperature resistant anti-corrosive priming paint of doing.
Aluminium triphosphate, it can discharge the very strong tripolyphosphate radical ion (P3O10) of complex ability
5-, have very strong complex ability with Fe3+, form MxFey (PO at steel surface
4)
zBe neoplastic passivation protection film, its host molecule AlH
2P
3O
102H
2Hydrogen atom among the O makes it be slightly acidic, and similar diprotic acid and metal reaction generate the stable weak acid and weak base salt that is insoluble in water of chemical property, thereby form the second road barrier in the metallic surface, protect metal not to be etched effectively.Its rustless property excellence, weather resistance is also fine.
High temperature resistant iron oxide black has characteristics such as high brightness, even particle size distribution, good dispersity, proportion be little; its alkali resistance excellence, be slightly soluble in diluted acid, heat-resistingly reach about 600 ℃, not spontaneous combustion, water insoluble, nontoxic itself; have high tinting strength and opacifying power; stable to light and atmospheric effect; itself and the black high-temperature resistant anti-corrosive priming paint that is suitable for of inert graphite; be widely used in petrochemical complex, the heatproof protection of metallurgical workpiece, chimney breast, boiler storage tank, power equipment and steel and iron member.
Anti-settling agent is selected wilkinite for use, add a small amount of wilkinite in the prescription and can make coating thickening in storage process, prevent dispersive pigment sedimentation and can make coating produce thixotropy viscosity, under execution conditions, dope viscosity is diminished be easy to levelling, and film reach levelling after, can return to original viscosity again, prevent sagging.
Inhibiter is selected organic nitrogen(ous) base and its esters rust-preventive agent for use, and they have an important effect to the stable of rust, are usually used in protection against corrosion priming paint, thereby reaches stable with heteropolyacid complex compound that active iron rust forms indissoluble
The effect of corrosion, protection iron and steel, its consumption is 1%～3%, can obviously improve the corrosion resistance of coating.
Preparation method of the present invention is:
The preparation of A component: it is complete that organobentonite is diluted to volumetric expansion with N-BUTYL ACETATE;
The preparation of B component: Resins, epoxy is mixed fully with aminoresin;
The preparation of C component: silicone resin, color stuffing, auxiliary agent, solvent are measured in the adding shredder in accordance with regulations, be ground to fineness less than 30 μ m;
A, B are added among the C, continue to grind dispersion 5～10min, filtration, sealing, packing.
Claims (2)
1. a fire-resistant anticorrosion paint is characterized in that, proportioning of the present invention is: the A component: wilkinite is 1.0～2.0%, and N-BUTYL ACETATE is 3.0～6.0%; The B component: Resins, epoxy is 6.0～10.0%, and aminoresin is 4.0～6.0%; The C component: silicone resin A is 28.0～32.0%, silicone resin B is 3.0～7.0%, organic inhibitor is 1.0～3.0%, colour carbon black is 1.0～2.0%, and titanium dioxide is 1.0～2.0%, and graphite is black to be 10.0～15.0%, the high temperature iron oxide black is 2.0～6.0%, talcum powder is 10.0～17.0%, and aluminium triphosphate is 3.0～7.0%, and isopropylcarbinol is 3.0～6.0%.
2. the preparation method of a fire-resistant anticorrosion paint is characterized in that, preparation method of the present invention is:
The preparation of A component: it is complete that organobentonite is diluted to volumetric expansion with N-BUTYL ACETATE;
The preparation of B component: Resins, epoxy is mixed fully with aminoresin;
The preparation of C component: silicone resin, color stuffing, auxiliary agent, solvent are measured in the adding shredder in accordance with regulations, be ground to fineness less than 30 μ m;
A, B are added among the C, continue to grind dispersion 5～10min, filtration, sealing, packing.