CN101748881B - Floor and preparation method thereof - Google Patents
Floor and preparation method thereof Download PDFInfo
- Publication number
- CN101748881B CN101748881B CN2009102564031A CN200910256403A CN101748881B CN 101748881 B CN101748881 B CN 101748881B CN 2009102564031 A CN2009102564031 A CN 2009102564031A CN 200910256403 A CN200910256403 A CN 200910256403A CN 101748881 B CN101748881 B CN 101748881B
- Authority
- CN
- China
- Prior art keywords
- parts
- floor
- kilograms
- shell
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a floor and a preparation method thereof. The floor is prepared from the following raw materials in part by weight: 30 to 40 parts of waste paper, 30 to 40 parts of peanut skin, 30 to 40 parts of walnut shell, 30 to 40 parts of filbert shell, 20 to 30 parts of pine nut shell, 10 to 20 parts of glutinous rice, 3 to 5 parts of charcoal, 20 to 30 parts of cement and 100 to 120 parts of phenolic resin cement. The floor has the advantages of having simple structure, low manufacturing cost, enhancing the utilization of wastes, reducing resource loss, avoiding using the resources such as wood, bamboo and the like, and facilitating the popularization and use of the floor.
Description
(1) technical field
The invention belongs to building materials, particularly a kind of floor and preparation method thereof.
(2) background technology
Existing wood flooring kind is a lot.Wood flooring is broadly divided into three major types: wooden floor, solid wooden compound floor, anion wood flooring and laminated flooring.The base material of laminated flooring is middle density or high density fiberboard and shaving board, and dimensional stability is good, and surface layer is the dipping decorative paper that contains high-abrasive material, has guaranteed the anti-wear performance of surface layer, anti-cigarette calcination, and is mar-proof good with anti-fouling performance.Just because of these plurality of advantages are arranged, laminated flooring all can use in the ground surface finishing of family room and public place.Because the forest reserves is deficient day by day, new trees will grow into useful timber needs the growth year of several years, therefore will reduce the use of timber, to respond the call of national energy-saving consumption-reducing as far as possible.
(3) summary of the invention
The present invention is in order to remedy the deficiencies in the prior art, provide a kind of simple in structure, cost is low, strengthen twice laid, reduce floor of resource loss and preparation method thereof.
The present invention is achieved through the following technical solutions:
Floor of the present invention, its special character is: the raw material by following parts by weight is made: waste paper 30-40 part, peanut skin 30-40 part, walnut shell 30-40 part, hazelnut shell 30-40 part, pine nut shell 20-30 part, glutinous rice 10-20 part, charcoal 3-5 part, cement 20-30 part, phenolic resin glue 100-120 part.
The manufacture method on floor of the present invention, its special character is: carry out successively according to the following steps:
A. preceding 7 kinds of raw material mixed powders are broken into 80～120 purpose fineves;
B. fines and cement, phenolic resin glue are mixed form slurry;
C. slurry is inserted in the pressing machine hot pressing and make substrate;
D. elevated temperature heat on the substrate is pressed top layer, wearing layer and balance layer;
E. press the specification of laminated flooring, process tongue and groove.
The invention has the beneficial effects as follows, simple in structure, cost is low, strengthen twice laid, reduce resource loss, do not use resources such as timber, bamboo wood, be convenient to this product promotion and use.
(4) specific embodiment
Embodiment 1
Floor of the present invention is made by the raw material of following weight: 35 kilograms in waste paper, 35 kilograms of peanut skins, 35 kilograms of walnut shells, 35 kilograms of hazelnut shell, 25 kilograms on pine nut shell, 15 kilograms in glutinous rice, 4 kilograms in charcoal, 25 kilograms of cement, 110 kilograms of phenolic resin glues.
The manufacture method on floor of the present invention, carry out successively according to the following steps:
A. preceding 7 kinds of raw material mixed powders are broken into 80～120 purpose fineves;
B. fines and cement, phenolic resin glue are mixed form slurry;
C. slurry is inserted in the pressing machine hot pressing and make substrate;
Press time 30min, pressure are 1Mpa/cm
2, temperature remains on 100 ℃-110 ℃;
D. elevated temperature heat on the substrate is pressed top layer, wearing layer and balance layer
Upper surface is suppressed top layer, wearing layer successively, soffit compacting balance layer; Its pressure is 1.2Mpa/cm
2, time 60s～70s, temperature is 195 ℃-200 ℃, the wearing layer material is Al
2O
3
E. press the specification of laminated flooring, process tongue and groove.
Embodiment 2
Floor of the present invention is made by the raw material of following weight: 30 kilograms in waste paper, 30 kilograms of peanut skins, 30 kilograms of walnut shells, 30 kilograms of hazelnut shell, 20 kilograms on pine nut shell, 10 kilograms in glutinous rice, 3 kilograms in charcoal, 20 kilograms of cement, 100 kilograms of phenolic resin glues.
All the other are identical with embodiment 1.
Embodiment 3
Floor of the present invention is made by the raw material of following weight: 40 kilograms in waste paper, 40 kilograms of peanut skins, 40 kilograms of walnut shells, 40 kilograms of hazelnut shell, 30 kilograms on pine nut shell, 20 kilograms in glutinous rice, 5 kilograms in charcoal, 30 kilograms of cement, phenolic resin glue 120 kg.
All the other are identical with embodiment 1.
Claims (1)
1. the manufacture method on a floor is characterized in that: the raw material that uses following parts by weight: waste paper 30-40 part, peanut skin 30-40 part, walnut shell 30-40 part, hazelnut shell 30-40 part, pine nut shell 20-30 part, glutinous rice 10-20 part, charcoal 3-5 part, cement 20-30 part, phenolic resin glue 100-120 part;
Manufacture method is carried out according to the following steps successively:
A. preceding 7 kinds of raw material mixed powders are broken into 80～120 purpose fineves;
B. fines and cement, phenolic resin glue are mixed form slurry;
C. slurry is inserted in the pressing machine hot pressing and make substrate;
D. elevated temperature heat on the substrate is pressed top layer, wearing layer and balance layer;
E. press the specification of laminated flooring, process tongue and groove.