CN101225236B - 用作聚氯乙烯树脂增塑剂的组合物及其使用方法 - Google Patents

用作聚氯乙烯树脂增塑剂的组合物及其使用方法 Download PDF

Info

Publication number
CN101225236B
CN101225236B CN2007101922124A CN200710192212A CN101225236B CN 101225236 B CN101225236 B CN 101225236B CN 2007101922124 A CN2007101922124 A CN 2007101922124A CN 200710192212 A CN200710192212 A CN 200710192212A CN 101225236 B CN101225236 B CN 101225236B
Authority
CN
China
Prior art keywords
polyvinyl chloride
resins
pvc
compound
composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2007101922124A
Other languages
English (en)
Other versions
CN101225236A (zh
Inventor
黄德周
张海波
徐佩军
陈飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Feixiang Chemicals Co Ltd
Original Assignee
Jiangsu Feixiang Chemicals Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Feixiang Chemicals Co Ltd filed Critical Jiangsu Feixiang Chemicals Co Ltd
Priority to CN2007101922124A priority Critical patent/CN101225236B/zh
Publication of CN101225236A publication Critical patent/CN101225236A/zh
Application granted granted Critical
Publication of CN101225236B publication Critical patent/CN101225236B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种无毒、能降低聚氯乙烯树脂熔融温度、提高聚氯乙烯树脂柔软性的用作聚氯乙烯树脂增塑剂的组合物及其使用方法。所述组合物中含有质量百分比为10～90％的环氧大豆油，质量百分比为10～90％的C12-C18烷基吡咯烷酮。该组合物用作聚氯乙烯树脂的增塑剂时在聚氯乙烯树脂中的存在量为10～100phr。将本发明的组合物加入聚氯乙烯树脂后，会使聚氯乙烯树脂具有邵氏A硬度小于100的性能。这些聚氯乙烯树脂适合制造压延板材、增塑溶胶、薄膜、公称管或是管子件等。

Description

用作聚氯乙烯树脂增塑剂的组合物及其使用方法
技术领域
本发明涉及到一种用作聚氯乙烯树脂增塑剂的组合物，以及该组合物用作增塑剂时的具体使用方法。
背景技术
众所周知，一些常用的热塑性聚合物具有高于室温的玻璃化转变温度(Tg)，在此温度以下，聚合物表现为类似玻璃的脆性状态，在此温度以上，则呈现较大的回弹性、柔韧性和冲击强度。要使聚合物具有实用价值，就必须使其玻璃化转变温度降到使用温度以下。增塑剂就是为解决这个问题而引入聚合物中的一类助剂。
聚氯乙烯树脂中的增塑剂是通过降低聚合物链间的内聚能密度及聚氯乙烯树脂中的卤素原子间的极性吸引力而起到增塑作用的。
目前，大量的有机物已经被报道可以作为聚氯乙烯树脂的增塑剂。其中包括邻苯二甲酸酐与C4-C15脂肪醇(直链或支链的)反应得到的酯类、环氧大豆油、偏苯三酸酯、安息香酸酯和柠檬酸酯及卤代烃等。二元醇与己二酸或癸二酸反应得到的高分子量的聚酯也被用做增塑剂。这些增塑剂中，以邻苯二甲酸酯类增塑剂的使用最为广泛。上述增塑剂还存在一些缺点，如有的有致癌性，容易造成内分泌紊乱、对生殖毒性较大等；有的使用后树脂的低温柔软性、可延展性不佳等。
发明内容
本发明所要解决的一个技术问题是：将提供一种无毒、能降低聚氯乙烯树脂熔融温度、提高聚氯乙烯树脂柔软性的用作聚氯乙烯树脂增塑剂的组合物，本发明要解决的另一个问题是：将提供上述组合物的具体使用方法。
为解决上述第一个问题，本发明采用的技术方案是：用作聚氯乙烯树脂增塑剂的组合物中含有质量百分比为10～90％的环氧大豆油，优选20～80％，尤其优选20～60％；组合物中含有10～90％的C12-C18烷基吡咯烷酮，优选20～80％，尤其优选40～80％。
为解决上述第二个问题，本发明采用的技术方案是：上述组合物的具体使用方法是：用作聚氯乙烯树脂的增塑剂，并且该组合物在聚氯乙烯树脂中的存在量是10～100phr(相对于每百份树脂的加入量)，尤其优选20～80phr。
本发明的优点是：本发明的组合物具有无毒、能降低聚氯乙烯树脂熔融温度、提高聚氯乙烯树脂柔软性的优点。将本发明的组合物加入聚氯乙烯树脂后，会使聚氯乙烯树脂具有邵氏A硬度小于100的性能。本发明的组合物可以单独或是与一种或多种主增塑剂或辅助增塑剂配合使用于聚氯乙烯树脂中，这些聚氯乙烯树脂适合制造压延板材、增塑溶胶、薄膜、公称管或是管子件等。
具体实施方式
下面通过具体实施例对本发明作进一步地描述，但不应理解本发明仅限于这些实施例。
实施例1
根据本发明给出的典型的聚氯乙烯树脂的配方如下表1，
表1
Figure G2007101922124D00031
注：A是一种K值为70的悬浮聚氯乙烯。
采用表1中各种配比的混合物生产压延板材时，添加了环氧大豆油和烷基吡咯烷酮的压延板材比添加了邻苯二甲酸二辛酯的压延板材更加柔软和透明。添加了十四烷基吡咯烷酮的板材是可塑性最好的。
实施例2
根据本发明给出下表2的配方，
表2
Figure G2007101922124D00032
注：A是一种K值为70的悬浮聚氯乙烯。
采用表2中各种配比的混合物生产压延板材时，添加了环氧大豆油和烷基吡咯烷酮的压延板材比添加了邻苯二甲酸二辛酯的压延板材更加柔软和透明。含有10％环氧大豆油的组合物的可塑性是最好的。
实施例3
根据本发明给出下表3的配方，
表3
Figure G2007101922124D00041
注：B是一种K值为71的悬浮聚氯乙烯。
采用表3中各种配比的混合物生产压延板材时均采用了200℃的温度，故都加入了Ca/Zn稳定剂。
采用表3中各种配比的混合物生产得到的压延板材被测定了邵氏A硬度，如下表4所示，通过表4可以看出，添加40phr组合物与添加80phr邻苯二甲酸二辛酯可以得到相同的邵氏A硬度，也就是组合物比邻苯二甲酸二辛酯更容易使聚氯乙烯树脂达到所需的增塑状态。
表4
  实验批次   邵氏A硬度<sup>*</sup>
  1   75
  2   97
  3   75
  4   42
注：测试方法为GB2411-1980

Claims (5)

1.用作聚氯乙烯树脂增塑剂的组合物，其特征在于：所述组合物中含有质量百分比为10～90％的环氧大豆油，质量百分比为10～90％的C12-C18烷基吡咯烷酮。
2.根据权利要求1所述的组合物，其特征在于：所述组合物中含有质量百分比为20～80％的环氧大豆油，20～80％的C12-C18烷基吡咯烷酮。
3.根据权利要求1所述的组合物，其特征在于：所述组合物中含有质量百分比为20～60％的环氧大豆油，40～80％的C12-C18烷基吡咯烷酮。
4.根据权利要求1、2或3所述的组合物的使用方法，其特征在于：所述的组合物用作聚氯乙烯树脂的增塑剂，并且该组合物在聚氯乙烯树脂中的存在量是10～100phr，相对于每百份树脂的加入量。
5.根据权利要求4所述的组合物的使用方法，其特征在于：所述的组合物在聚氯乙烯树脂中的存在量是20～80phr，相对于每百份树脂的加入量。
CN2007101922124A 2007-12-19 2007-12-19 用作聚氯乙烯树脂增塑剂的组合物及其使用方法 Active CN101225236B (zh)