0.8mm thickness | 200 mesh | 325 mesh | 3D Design | 3D Modeling | 3D Printer | 3D Printing Clay | 3D Slicer | 3D-Printing | Abrasion Ceramics | Acidic Oxides | Agglomeration | AI in Ceramics | Alkali | Alkaline Earths | All-in-one case mold | Amorphous | Apparent porosity | Artware | Ball milling | Bamboo Glaze | Base Glaze | Base-Coat Dipping Glaze | Basic Oxides | Batch Recipe | Bisque | Bit Image | Black Core | Bleeding of colors | Blender Mixing | Blunging | Body Bloating | Body glaze Interface | Body Warping | Bone China | Borate | Boron Blue | Boron Frit | Borosilicate | Breaking Glaze | Brick Making | Brushing Glaze | Calcination | Calculated Thermal Expansion | Candling | Carbon Burnout | Carbon trap glazes | CAS Numbers | Casting-Jiggering | Catch Glaze | Celadon Glaze | Ceramic | Ceramic Binder | Ceramic Decals | Ceramic Glaze | Ceramic Glaze Defects | Ceramic Ink | Ceramic Material | Ceramic Oxide | Ceramic Slip | Ceramic Stain | Ceramic Tile | Ceramic Transfer | Ceramics | Characterization | Chemical Analysis | Chromaticity | Clay | Clay body | Clay Body Porosity | Clay Stiffness | Clays for Ovens and Heaters | Co-efficient of Thermal Expansion | Code Numbering | Coil pottery | Colloid | Colorant | Commercial hobby brushing glazes | Cone 1 | Cone 5 | Cone 6 | Cone plaque | Copper Red | Cordierite Ceramics | Crackle glaze | Cristobalite | Cristobalite Inversion | Crucible | Crystalline glazes | Crystallization | Cuerda Seca | Cutlery Marking | Decomposition | Deflocculation | Deoxylidration | Differential thermal analysis | Digitalfire API | Digitalfire Foresight | Digitalfire Insight | Digitalfire Insight-Live | Digitalfire Reference Library | Digitalfire Taxonomy | Dimpled glaze | Dip Glazing | Dipping Glaze | Dishwasher Safe | Displacer | Dolomite Matte | Drop-and-Soak Firing | Drying Crack | Drying Performance | Drying Shrinkage | Dunting | Dust Pressing | Earthenware | Efflorescence | Encapsulated Stain | Engobe | Eutectic | Fast Fire Glazes | Fat Glaze | Feldspar Glazes | Fining Agent | Firebrick | Fireclay | Fired Strength | Firing Schedule | Firing Shrinkage | Flameware | Flashing | Flocculation | Fluid Melt Glazes | Flux | Food Safe | Foot Ring | Forming Method | Formula Ratios | Formula Weight | Frit | Fritware | Functional | GHS Safety Data Sheets | Glass vs. Crystalline | Glass-Ceramic Glazes | Glaze Blisters | Glaze Bubbles | Glaze Chemistry | Glaze Compression | Glaze Crawling | Glaze Crazing | Glaze Durability | Glaze fit | Glaze Gelling | Glaze laydown | Glaze Layering | Glaze Mixing | Glaze Recipes | Glaze shivering | Glaze Shrinkage | Glaze thickness | Globally Harmonized Data Sheets | Glossy Glaze | Green Strength | Grog | Gunmetal glaze | High Temperature Glaze | Hot Pressing | Incised decoration | Industrial clay body | Infill and Support | Ink Jet Printing | Inside-only Glazing | Iron Red Glaze | Jasper Ware | Jiggering | Kaki | Kiln Controller | Kiln Firing | Kiln fumes | Kiln venting system | Kiln Wash | Kneading clay | Kovar Metal | Laminations | Leaching | Lead in Ceramic Glazes | Leather hard | Limit Formula | Limit Recipe | Liner Glaze | Liner Glazing | Liquid Bright Colors | LOI | Low Temperature Glaze | Majolica | Marbling | Material Substitution | Matte Glaze | Maturity | Maximum Density | MDT | Mechanism | Medium Temperature Glaze | Melt Fluidity | Melting Temperature | Metal Oxides | Metallic Glazes | Micro Organisms | Microwave Safe | Mineral phase | Mineralogy | Mocha glazes | Mohs Hardness | Mold Natches | Mole% | Monocottura | Mosaic Tile | Mottled | Mullite Crystals | Native Clay | Non Oxide Ceramics | Oil-spot glaze | Once fire glazing | Opacifier | Opacity | | Overglaze | Oxidation Firing | Oxide Formula | Oxide Interaction | Oxide System | Particle orientation | Particle Size Distribution | Particle Sizes | PCE | Permeability | Phase Diagram | Phase Separation | Physical Testing | Pinholing | Plainsman Clays | Plaster Bat | Plaster table | Plasticine | Plasticity | Plucking | Porcelain | Porcelaineous Stoneware | Pour Glazing | Pour Spout | Powder Processing | Precipitation | Primary Clay | Primitive Firing | Propane | Propeller Mixer | Pugmill | Pyroceramics | Pyrometric Cone | Quartz Inversion | Raku | Reactive Glazes | Reduction Firing | Reduction Speckle | Refiring Ceramics | Refractory | Refractory Ceramic Coatings | Representative Sample | Restaurant Ware | Rheology | Rutile Blue Glazes | Salt firing | Sanitary ware | Sculpture | Secondary Clay | Shino Glazes | Side Rails | Sieve | Sieve Shaker | Silica:Alumina Ratio | Silk screen printing | Sintering | Slaking | Slip Casting | Slip Trailing | Slipware | Slurry | Slurry Processing | Slurry Up | Soaking | Soluble colors | Soluble Salts | Specific gravity | Splitting | Spray Glazing | Stain Medium | Stoneware | Stull Chart | Sulfate Scum | Sulfates | Surface Area | Surface Tension | Suspension | Tapper Clay | Tenmoku | Terra Cotta | Terra Sigilatta | Test Kiln | Theoretical Material | Thermal Conductivity | Thermal shock | Thermocouple | Thixotropy | Throwing | Tipping point | Tony Hansen | Toxicity | Trafficking | Translucency | Transparent Glazes | Triaxial Glaze Blending | Ultimate Particles | Underglaze | Unity Formula | Upwork | Variegation | Viscosity | Vitreous | Vitrification | Volatiles | Water Content | Water in Ceramics | Water Smoking | Water Solubility | Wedging | Whiteware | WooCommerce | Wood Ash Glaze | Wood Firing | WordPress | Zero3 | Zero4 | Zeta Potential

Ovenware

Ovenware clay bodies have a low expansion by virtue of materials in their recipe and/or the way they are fired. But potters bend the rules.

Key phrases linking here: ovenware - Learn more

Details

Ovenware clay bodies have a lower thermal expansion than typical bodies so they can withstand more sudden changes in temperature without cracking. Flameware bodies are not the same, they can withstand an open flame and demand much more compromise in working properties, strength, glaze fit, etc.

Ovenware manufacturers dedicate considerable resources to producing low-expansion bodies and matching glazes that are far more thermal shock-resistant than what a typical potter can make. They are also experts in shapes that have inherent strength to resist the stresses of uneven heating. Still, potters have found ways to get away with using standard bodies and glazes. For example, by making sure glazes fit well (no crazing or excessive compression as proven by testing), drying and firing evenly so as not to build in stresses, avoiding highly vitreous bodies (which propagate cracks better) and bodies with quartz sand, make ware with an even cross-section, avoiding angular contours and larger sizes with broad flat bottoms and telling customers to be careful about subjecting ware to sudden temperature change.

Glaze fit is a major problem in designing an ovenware body since common glazes will certainly craze (it is much easier to make a low-expansion clay body than a glaze). Thus it is normal to compromise the lowest possible expansion on the body in order to get a reliable glaze fit. The lowest expansion glazes can be made using MgO based boron frits in glazes having the lowest possible KNaO. Glaze chemistry is invaluable to shape a compromise between low expansion and the desired appearance. Anyone serious about producing low-expansion ware needs to understand thermal expansion and be ready to change their process and endure increased costs.

There are main two mechanisms for creating a low expansion body: By firing to form a crystalline matrix that has low expansion (e.g. Corningware, cordierite) or by employing materials having particles of low expansion (e.g. mullite, pyrophyllite, petalite and kyanite) and formulating and firing in such a way that the thermal shock properties of the materials survive the firing (without being altered). The former produces a more vitreous body and requires much more expertise and test equipment. As noted, the latter is a bit of a 'crowbar' approach and is dependent on not firing to full maturity (otherwise mineral species can be dissolved by the feldspar in the body or simply altered in crystal form and the low expansion effect is lost). This can create a bit of a 'tug-of-war' in the body since the glass that glues all the particles into a matrix will likely have a higher expansion. Obviously, ovenware bodies should have much lower free quartz content, especially the larger particle sizes, since these have very high thermal expansion. This does not just mean avoiding only ground silica, ball clays also contribute a lot of quartz.

Often, ovenware body recipes are published without any explanation about the mechanism they employ or what to do about glaze. Common recipes found in textbooks often feature a high percentage of spodumene (30%) along with some feldspar and pyrophyllite (about 10% of each) and a mix of ball clay and kaolin or stoneware clays. The object with these appears to be to create a low expansion glassy matrix in which the kaolin can convert to mullite. But if ball clays and stoneware clays are present, these contain significant amounts of quartz particles; while some may dissolve, it seems likely that much will not (a nothing in ceramics has a higher thermal expansion than quartz). Some recipes are a combination of talc and ball clay or fireclay. The intent is to create cordierite at cone 10. However, cordierite does not develop until long after cone 10 so it is no coincidence that such bodies also contain large amounts of grog (which assumes the burden of absorbing or slowing cracks). For more information on this and testing standards and labs, see the last part of the article on flameware.

A common thermal expansion-resistant non-glazed product that many potters are asked to make is pizza stones. These are fairly thin and can be diameters to 14 inches or more. Although they do not need to withstand the same shock as regular ovenwares, the flat shape makes them susceptible to cracking on the uneven heating they often are subjected to. The principles outlined above should be sufficient to create a product that will endure common, but not extreme use.

Related Information

Can terra cotta ware survive an open flame without cracking?


It can if the flame is not too big! This is a roadside stand in Mexico in 2016. Each of these "cazuelas" (casseroles) have a small flame under them to keep the food inside warm. The pedestal is unglazed. The ware is thick and heavy. The casseroles are hand decorated with under-glaze slip colors with a very thin layer of lead glaze painted over (producing a terra sigilatta type appearance, but with brush stroke texture). These have been made and used here for hundreds of years. How can they not crack over an open flame? The flame is small and it is applied in the center of the bottom so that stresses are distributed radially and symmetrically. The ware is fired at what potters in Canada or the US would consider bisque temperature. It is porous, open and able to absorb the stresses. Some of them do have small cracks, but these seem to relieve stresses and prevent more. They know these pieces are not strong, so they treat them with care in heating, handling and washing. They know the glaze will leach lead or even dissolve if they put acidic liquids in them - so they don't do that.

A flameware recipe. Are they kidding?


This is made from a recipe promoted by a popular website (equal parts of talc, ball clay and grog). Are they serious? How could the page fail to mention how coarse this is? How is it possible to throw something like this. Wouldn’t ware be porous and weak? Is this an attempt to make cordierite? But that needs special firing. Maybe the idea is that anything with this much grog can automatically be ovenware!

Links

Glossary Flameware
Flameware is ceramic that can withstand sudden temperature changes without cracking. The low thermal expansion of true flameware makes craze-free glazes very difficult.
Glossary Co-efficient of Thermal Expansion
The co-efficient of thermal expansion of ceramic bodies and glazes determines how well they fit each other and their ability to survive sudden heating and cooling without cracking.
Glossary Cordierite Ceramics
Cordierite is a man-made refractory low thermal expansion crystalline solid that forms at very high temperatures (in the right mix of kaolin and talc).
Materials Ferro Frit 3249
A magnesia borosilicate frit. Very low thermal expansion and melting point. Invaluable in pottery to increase the MgO in glazes and thereby prevent crazing.
Tests Thermal Shock Failure
A simple test any potter can do by making and firing square tiles and using a plumbing torch to see how long before they fracture.
URLs https://www.emilehenryusa.com/pages/about
Emile Henry ceramic ovenware from France.
They claim products are "direct freezer-to-oven", they have extraordinary thermal shock resistance and heat retention properties. Products are glazed. It seems impossible but they are doing it.
URLs https://xtrema.ca/pages/use-and-care
Xtrema ceramic ovenware fired at 2500F
Skillets, saucepans and bake pans with recommended precautions to avoid cracking.
By Tony Hansen
Follow me on

Got a Question?

Buy me a coffee and we can talk

 



https://digitalfire.com, All Rights Reserved
Privacy Policy