WO2015011994A1 - Composition de résine de polycarbonate pour composant optique mince et composant optique mince - Google Patents

Composition de résine de polycarbonate pour composant optique mince et composant optique mince Download PDF

Info

Publication number
WO2015011994A1
WO2015011994A1 PCT/JP2014/064717 JP2014064717W WO2015011994A1 WO 2015011994 A1 WO2015011994 A1 WO 2015011994A1 JP 2014064717 W JP2014064717 W JP 2014064717W WO 2015011994 A1 WO2015011994 A1 WO 2015011994A1
Authority
WO
WIPO (PCT)
Prior art keywords
polycarbonate resin
thin
resin composition
pellet
mass
Prior art date
Application number
PCT/JP2014/064717
Other languages
English (en)
Japanese (ja)
Inventor
恵介 冨田
松本　晋
Original Assignee
三菱エンジニアリングプラスチックス株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2013155539A external-priority patent/JP5699188B2/ja
Priority claimed from JP2014081958A external-priority patent/JP5699240B1/ja
Application filed by 三菱エンジニアリングプラスチックス株式会社 filed Critical 三菱エンジニアリングプラスチックス株式会社
Priority to KR1020167001809A priority Critical patent/KR102121093B1/ko
Priority to US14/894,671 priority patent/US9701835B2/en
Priority to CN201480042499.0A priority patent/CN105431488B/zh
Publication of WO2015011994A1 publication Critical patent/WO2015011994A1/fr

Abstract

L'invention concerne une composition de résine de polycarbonate pour un composant optique mince et un composant optique mince, qui présentent une transmittance élevée, une bonne teinte et une résistance à la décoloration thermique exceptionnelle. La composition de résine de polycarbonate pour composant optique mince se caractérise en ce qu'elle contient, par rapport à 100 parties en masse d'une résine de polycarbonate (A), 0,1-2 parties en masse d'un composé polyalkylène éther glycol (B) représenté par la formule (1) suivante et 0,005-0,5 partie en masse d'un stabilisant à base de phosphore.
PCT/JP2014/064717 2013-07-26 2014-06-03 Composition de résine de polycarbonate pour composant optique mince et composant optique mince WO2015011994A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
KR1020167001809A KR102121093B1 (ko) 2013-07-26 2014-06-03 박육 광학 부품용 폴리카르보네이트 수지 조성물 및 박육 광학 부품
US14/894,671 US9701835B2 (en) 2013-07-26 2014-06-03 Polycarbonate resin composition for thin optical component, and thin optical component
CN201480042499.0A CN105431488B (zh) 2013-07-26 2014-06-03 薄壁光学构件用聚碳酸酯树脂组合物及薄壁光学构件

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
JP2013-155539 2013-07-26
JP2013155539A JP5699188B2 (ja) 2013-07-26 2013-07-26 薄肉光学部品用ポリカーボネート樹脂組成物および薄肉光学部品
JP2014043838 2014-03-06
JP2014-043838 2014-03-06
JP2014-081958 2014-04-11
JP2014081958A JP5699240B1 (ja) 2014-03-06 2014-04-11 薄肉光学部品用ポリカーボネート樹脂組成物および薄肉光学部品

Publications (1)

Publication Number Publication Date
WO2015011994A1 true WO2015011994A1 (fr) 2015-01-29

Family

ID=52393047

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/064717 WO2015011994A1 (fr) 2013-07-26 2014-06-03 Composition de résine de polycarbonate pour composant optique mince et composant optique mince

Country Status (1)

Country Link
WO (1) WO2015011994A1 (fr)

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016111117A1 (fr) * 2015-01-07 2016-07-14 三菱エンジニアリングプラスチックス株式会社 Composition de résine de polycarbonate pour composants optiques minces et composant optique mince
WO2016111101A1 (fr) * 2015-01-07 2016-07-14 三菱エンジニアリングプラスチックス株式会社 Composition de résine de polycarbonate pour éléments optiques fins et élément optique fin
WO2016194749A1 (fr) 2015-05-29 2016-12-08 出光興産株式会社 Composition de résine de polycarbonate et article moulé à base de celle-ci
JP2016222860A (ja) * 2015-06-03 2016-12-28 住化スタイロンポリカーボネート株式会社 ポリカーボネート樹脂組成物およびそれからなる光学用成形品
EP3070124A4 (fr) * 2013-11-11 2017-07-12 Idemitsu Kosan Co., Ltd. Composition de résine de polycarbonate
CN107109046A (zh) * 2015-02-03 2017-08-29 三菱工程塑胶株式会社 芳香族聚碳酸酯树脂组合物及其成型品
JP2017197704A (ja) * 2016-04-20 2017-11-02 住化ポリカーボネート株式会社 ポリカーボネート樹脂組成物及び光学用成形品
CN107949604A (zh) * 2015-11-27 2018-04-20 三菱工程塑胶株式会社 芳香族聚碳酸酯树脂组合物及其成型品
JP2019035098A (ja) * 2017-02-01 2019-03-07 出光興産株式会社 ポリカーボネート樹脂組成物
US10472477B2 (en) 2015-01-07 2019-11-12 Mitsubishi Engineering-Plastics Corporation Polycarbonate resin composition for thin optical component, and thin optical component
CN110546204A (zh) * 2017-04-18 2019-12-06 三菱工程塑料株式会社 光学部件用聚碳酸酯树脂组合物和光学部件
JPWO2019026784A1 (ja) * 2017-07-31 2020-05-28 出光興産株式会社 芳香族ポリカーボネート樹脂組成物及び光学成形品
JP2020193253A (ja) * 2019-05-27 2020-12-03 三菱エンジニアリングプラスチックス株式会社 ポリカーボネート樹脂組成物

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1135692A (ja) * 1997-07-23 1999-02-09 Mitsubishi Eng Plast Kk 光ディスク基板用ポリカーボネート成形材料
JP2000234052A (ja) * 1999-02-16 2000-08-29 Mitsubishi Engineering Plastics Corp 光ディスク基板用ポリカーボネート成形材料
WO2011083635A1 (fr) * 2010-01-07 2011-07-14 出光興産株式会社 Composition de résine de polycarbonate aromatique et articles moulés à usage optique qui sont fabriqués à l'aide de celle-ci
JP2013000913A (ja) * 2011-06-13 2013-01-07 Asahi Kasei Chemicals Corp 押出機およびそれを用いた溶融混練方法
JP2013139097A (ja) * 2011-12-28 2013-07-18 Idemitsu Kosan Co Ltd ポリカーボネート樹脂組成物ペレット及びその製造方法
JP2013231899A (ja) * 2012-05-01 2013-11-14 Mitsubishi Engineering Plastics Corp 導光板用ポリカーボネート樹脂組成物および導光板

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1135692A (ja) * 1997-07-23 1999-02-09 Mitsubishi Eng Plast Kk 光ディスク基板用ポリカーボネート成形材料
JP2000234052A (ja) * 1999-02-16 2000-08-29 Mitsubishi Engineering Plastics Corp 光ディスク基板用ポリカーボネート成形材料
WO2011083635A1 (fr) * 2010-01-07 2011-07-14 出光興産株式会社 Composition de résine de polycarbonate aromatique et articles moulés à usage optique qui sont fabriqués à l'aide de celle-ci
JP2013000913A (ja) * 2011-06-13 2013-01-07 Asahi Kasei Chemicals Corp 押出機およびそれを用いた溶融混練方法
JP2013139097A (ja) * 2011-12-28 2013-07-18 Idemitsu Kosan Co Ltd ポリカーボネート樹脂組成物ペレット及びその製造方法
JP2013231899A (ja) * 2012-05-01 2013-11-14 Mitsubishi Engineering Plastics Corp 導光板用ポリカーボネート樹脂組成物および導光板

Cited By (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3070124A4 (fr) * 2013-11-11 2017-07-12 Idemitsu Kosan Co., Ltd. Composition de résine de polycarbonate
US9783674B2 (en) 2013-11-11 2017-10-10 Idemitsu Kosan Co., Ltd. Polycarbonate resin composition
US10472477B2 (en) 2015-01-07 2019-11-12 Mitsubishi Engineering-Plastics Corporation Polycarbonate resin composition for thin optical component, and thin optical component
WO2016111101A1 (fr) * 2015-01-07 2016-07-14 三菱エンジニアリングプラスチックス株式会社 Composition de résine de polycarbonate pour éléments optiques fins et élément optique fin
WO2016111117A1 (fr) * 2015-01-07 2016-07-14 三菱エンジニアリングプラスチックス株式会社 Composition de résine de polycarbonate pour composants optiques minces et composant optique mince
CN107109046A (zh) * 2015-02-03 2017-08-29 三菱工程塑胶株式会社 芳香族聚碳酸酯树脂组合物及其成型品
WO2016194749A1 (fr) 2015-05-29 2016-12-08 出光興産株式会社 Composition de résine de polycarbonate et article moulé à base de celle-ci
JP7271860B2 (ja) 2015-05-29 2023-05-12 出光興産株式会社 ポリカーボネート樹脂組成物及びその成形品
JPWO2016194749A1 (ja) * 2015-05-29 2018-03-15 出光興産株式会社 ポリカーボネート樹脂組成物及びその成形品
US11034834B2 (en) 2015-05-29 2021-06-15 Idemitsu Kosan Co., Ltd. Polycarbonate resin composition and molded article of same
JP2016222860A (ja) * 2015-06-03 2016-12-28 住化スタイロンポリカーボネート株式会社 ポリカーボネート樹脂組成物およびそれからなる光学用成形品
CN107949604B (zh) * 2015-11-27 2020-10-09 三菱工程塑胶株式会社 芳香族聚碳酸酯树脂组合物及其成型品
US10767043B2 (en) 2015-11-27 2020-09-08 Mitsubishi Enigineering-Plastics Corporation Aromatic polycarbonate resin composition and molded article of the same
CN107949604A (zh) * 2015-11-27 2018-04-20 三菱工程塑胶株式会社 芳香族聚碳酸酯树脂组合物及其成型品
JP2017197704A (ja) * 2016-04-20 2017-11-02 住化ポリカーボネート株式会社 ポリカーボネート樹脂組成物及び光学用成形品
JP2019035098A (ja) * 2017-02-01 2019-03-07 出光興産株式会社 ポリカーボネート樹脂組成物
EP3578608A4 (fr) * 2017-02-01 2020-10-14 Idemitsu Kosan Co.,Ltd. Composition de résine de polycarbonate
JP7033051B2 (ja) 2017-02-01 2022-03-09 出光興産株式会社 ポリカーボネート樹脂組成物
CN110546204A (zh) * 2017-04-18 2019-12-06 三菱工程塑料株式会社 光学部件用聚碳酸酯树脂组合物和光学部件
CN110546204B (zh) * 2017-04-18 2021-08-17 三菱工程塑料株式会社 光学部件用聚碳酸酯树脂组合物和光学部件
JPWO2019026784A1 (ja) * 2017-07-31 2020-05-28 出光興産株式会社 芳香族ポリカーボネート樹脂組成物及び光学成形品
US11525056B2 (en) 2017-07-31 2022-12-13 Idemitsu Kosan Co., Ltd. Aromatic polycarbonate resin composition and optical molded article
JP2020193253A (ja) * 2019-05-27 2020-12-03 三菱エンジニアリングプラスチックス株式会社 ポリカーボネート樹脂組成物

Similar Documents

Publication Publication Date Title
JP6101856B1 (ja) 薄肉光学部品用ポリカーボネート樹脂組成物および薄肉光学部品
KR102121093B1 (ko) 박육 광학 부품용 폴리카르보네이트 수지 조성물 및 박육 광학 부품
WO2015011994A1 (fr) Composition de résine de polycarbonate pour composant optique mince et composant optique mince
JP5699240B1 (ja) 薄肉光学部品用ポリカーボネート樹脂組成物および薄肉光学部品
JP5699188B2 (ja) 薄肉光学部品用ポリカーボネート樹脂組成物および薄肉光学部品
JP5893774B1 (ja) 薄肉光学部品用ポリカーボネート樹脂組成物および薄肉光学部品
JP2018028025A (ja) 光学部材用ポリカーボネート樹脂組成物
JP6587948B2 (ja) 光学部品用ポリカーボネート樹脂組成物および光学部品
JP6893340B2 (ja) 光学部品用ポリカーボネート樹脂組成物および光学部品
JP6416423B1 (ja) 光学部品用ポリカーボネート樹脂組成物および光学部品
JP6645886B2 (ja) ポリカーボネート樹脂組成物
JP6522818B2 (ja) 光学部品用ポリカーボネート樹脂組成物及び光学部品
JP6526871B2 (ja) 薄肉光学部品用ポリカーボネート樹脂組成物および薄肉光学部品
WO2016111117A1 (fr) Composition de résine de polycarbonate pour composants optiques minces et composant optique mince
JP6490490B2 (ja) ポリカーボネート樹脂組成物および薄肉光学部品
JP6522493B2 (ja) 光学部品用ポリカーボネート樹脂組成物および光学部品
JP6396792B2 (ja) 導光部材用ポリカーボネート樹脂組成物及び導光部材
JP6446601B1 (ja) 光学部品用ポリカーボネート樹脂組成物及び光学部品
WO2018193702A1 (fr) Composition de résine de polycarbonate pour composant optique, et composant optique
JP6422734B2 (ja) 薄肉光学部品用ポリカーボネート樹脂組成物および薄肉光学部品
JP2019214744A (ja) ポリカーボネート樹脂組成物

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201480042499.0

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14830289

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 14894671

Country of ref document: US

ENP Entry into the national phase

Ref document number: 20167001809

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14830289

Country of ref document: EP

Kind code of ref document: A1