US20100155251A1 - Hard anodize of cold spray aluminum layer - Google Patents

Hard anodize of cold spray aluminum layer Download PDF

Info

Publication number
US20100155251A1
US20100155251A1 US12/342,148 US34214808A US2010155251A1 US 20100155251 A1 US20100155251 A1 US 20100155251A1 US 34214808 A US34214808 A US 34214808A US 2010155251 A1 US2010155251 A1 US 2010155251A1
Authority
US
United States
Prior art keywords
component
repair material
affected area
aluminum
providing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/342,148
Other languages
English (en)
Inventor
William Bogue
Robert J. DeRosa
Gary M. Lomasney
Billie W. Bunting
Joseph J. Parkos, Jr.
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
RTX Corp
Original Assignee
United Technologies Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by United Technologies Corp filed Critical United Technologies Corp
Priority to US12/342,148 priority Critical patent/US20100155251A1/en
Assigned to UNITED TECHNOLOGIES CORPORATION reassignment UNITED TECHNOLOGIES CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BOGUE, WILLIAM, BUNTING, BILLIE W., DEROSA, ROBERT J., LOMASNEY, GARY M., PARKOS, JOSEPH J., JR.
Priority to EP09252862A priority patent/EP2204473A3/de
Publication of US20100155251A1 publication Critical patent/US20100155251A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C24/00—Coating starting from inorganic powder
    • C23C24/02—Coating starting from inorganic powder by application of pressure only
    • C23C24/04—Impact or kinetic deposition of particles
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
    • C23C28/32—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer
    • C23C28/322—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer only coatings of metal elements only
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
    • C23C28/34—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates
    • C23C28/345—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates with at least one oxide layer
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D11/00—Electrolytic coating by surface reaction, i.e. forming conversion layers
    • C25D11/02—Anodisation
    • C25D11/04—Anodisation of aluminium or alloys based thereon
    • C25D11/06—Anodisation of aluminium or alloys based thereon characterised by the electrolytes used
    • C25D11/08—Anodisation of aluminium or alloys based thereon characterised by the electrolytes used containing inorganic acids
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D11/00—Electrolytic coating by surface reaction, i.e. forming conversion layers
    • C25D11/02—Anodisation
    • C25D11/04—Anodisation of aluminium or alloys based thereon
    • C25D11/16—Pretreatment, e.g. desmutting
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D11/00—Electrolytic coating by surface reaction, i.e. forming conversion layers
    • C25D11/02—Anodisation
    • C25D11/04—Anodisation of aluminium or alloys based thereon
    • C25D11/18—After-treatment, e.g. pore-sealing
    • C25D11/24—Chemical after-treatment
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D11/00—Electrolytic coating by surface reaction, i.e. forming conversion layers
    • C25D11/02—Anodisation
    • C25D11/30—Anodisation of magnesium or alloys based thereon
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
    • F01D—NON-POSITIVE DISPLACEMENT MACHINES OR ENGINES, e.g. STEAM TURBINES
    • F01D5/00—Blades; Blade-carrying members; Heating, heat-insulating, cooling or antivibration means on the blades or the members
    • F01D5/12—Blades
    • F01D5/28—Selecting particular materials; Particular measures relating thereto; Measures against erosion or corrosion
    • F01D5/288—Protective coatings for blades
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F05—INDEXING SCHEMES RELATING TO ENGINES OR PUMPS IN VARIOUS SUBCLASSES OF CLASSES F01-F04
    • F05D—INDEXING SCHEME FOR ASPECTS RELATING TO NON-POSITIVE-DISPLACEMENT MACHINES OR ENGINES, GAS-TURBINES OR JET-PROPULSION PLANTS
    • F05D2230/00—Manufacture
    • F05D2230/30—Manufacture with deposition of material
    • F05D2230/31—Layer deposition
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F05—INDEXING SCHEMES RELATING TO ENGINES OR PUMPS IN VARIOUS SUBCLASSES OF CLASSES F01-F04
    • F05D—INDEXING SCHEME FOR ASPECTS RELATING TO NON-POSITIVE-DISPLACEMENT MACHINES OR ENGINES, GAS-TURBINES OR JET-PROPULSION PLANTS
    • F05D2230/00—Manufacture
    • F05D2230/90—Coating; Surface treatment
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F05—INDEXING SCHEMES RELATING TO ENGINES OR PUMPS IN VARIOUS SUBCLASSES OF CLASSES F01-F04
    • F05D—INDEXING SCHEME FOR ASPECTS RELATING TO NON-POSITIVE-DISPLACEMENT MACHINES OR ENGINES, GAS-TURBINES OR JET-PROPULSION PLANTS
    • F05D2300/00—Materials; Properties thereof
    • F05D2300/10—Metals, alloys or intermetallic compounds
    • F05D2300/12—Light metals
    • F05D2300/121—Aluminium

Definitions

  • the invention relates to the field of repairing gas turbine components that have experienced corrosion damage and, more particularly, relates to methods that extend component life by reducing or eliminating further corrosion damage which could cause the component to be scrapped.
  • Gas turbine engine components such as fan cases, bleed valves, bleed ducts, clamps, nacelle v-grooves, nacelle track sliders, gearboxes, and the like, are typically constructed of aluminum and magnesium alloys.
  • Aluminum alloys such as AA 6061 and AA 2024 are soft and suffer damage via general wear, fretting against steel components, impact, etc.
  • One method of mitigating wear of aluminum alloys is anodic conversion of the alloy to produce a hard oxide layer on the exposed surface per processes such as AMS 2468 or AMS 2469. There exist many means to dimensionally restore aluminum alloys; however, wear resistance is inferior to these hard anodic coatings.
  • Aluminum alloys are susceptible to general corrosion and especially salt (halide) environments and galvanic corrosion during regular service in the field. And, magnesium alloys, being typically less noble than aluminum alloys, are actually more susceptible to galvanic corrosion. For example, corrosion damage can be caused from electrical contact with a more noble alloy or by electrolytes in the presence of water or moisture. Environmental conditions such as chemical fallout, saltwater, and others can accelerate corrosion or add additional corrosion processes. Hard anodic layers provide some corrosion protection, especially when sealed with corrosion inhibiting materials, e.g., chromium conversion coatings.
  • Hard anodizing processes consume part of the components' surface.
  • the hard anodize process adds thickness to the surface, but the interface between anodize surface and parent alloy moves in to the parent material to approximately an equivalent thickness when forming a hard anodized layer 8 and repairing the component 6 (See FIG. 1 ).
  • the rework of the anodic layer requires that all prior layer be removed. This limits the number of times the hard anodized layer may be applied in the rework and repair of the component.
  • Magnesium alloys can be hard anodized, but the processes are substantially more difficult and expensive.
  • What is desired is a method of repairing gas turbine components that have suffered wear and corrosive deterioration by identifying and mitigating the corrosion attack before the component wall thickness has deteriorated below that required to provide minimum strength requirements, and restoring the original component dimensions while restoring original or offering added wear resistance and corrosion protection.
  • a process for repairing components broadly comprises the steps of providing a component having an affected area on a surface of a component to be repaired; depositing a repair material over the affected area on the surface of the component so that the repair material plastically deforms without melting and bonds to the affected area upon impact with the affected area and thereby covers the affected area; providing a sulfuric acid based anodizing solution; anodizing a deposited repair material on said surface of said component in said sulfuric acid based anodizing solution; consuming only a portion of said deposited repair material to form a hard anodized coating layer upon said deposited repair material to form a hard anodized coated component; providing a corrosion resistant sealant solution; and contacting a hard anodized coated component with the corrosion resistant sealant solution to form a corrosion resistant sealant coating on the hard anodized coated component.
  • a repaired component broadly comprises a component including a surface having a cold sprayed layer of repair material disposed thereupon, the component further includes an original thickness and the surface includes a restored thickness; and an anodized, hard coat disposed upon the cold sprayed layer, wherein the original thickness is a thickness of the component prior to applying the cold sprayed layer and the restored thickness is the original thickness combined with a thickness of the cold sprayed layer.
  • FIG. 1 is a representation of a substrate surface being consumed during a hard anodizing process of the prior art.
  • FIG. 2 is a flowchart representing an exemplary process for the hard anodize of cold spray aluminum layer on a substrate
  • FIG. 3 is a representation of a cold spraying deposition apparatus for use in the process described herein;
  • FIG. 4 are a set of four (4) microphotographs at different magnifications showing a comparison of a metallographic examination of the bond line between the cold spray layer and substrate of an anodized 6061 aluminum alloy plate cold sprayed with 6061 aluminum (unsealed);
  • FIG. 5 are a set of four (4) microphotographs at different magnifications showing a comparison of a metallographic examination of the bond line between the cold spray layer and substrate of an anodized 6061 aluminum alloy plate cold sprayed with 6061 aluminum (sealed) after undergoing salt fog testing (ASTM B-117) for approximately 336 hours;
  • FIG. 6 are a set of four (4) microphotographs at different magnifications showing a comparison of a metallographic examination of the junction area of a hard coating and the substrate of an 6061 aluminum alloy plate cold sprayed with 6061 aluminum after undergoing salt fog testing (ASTM B-117) for approximately 336 hours; and
  • FIG. 7 is a representation of an exemplary hard anodized component having a hard oxidized layer deposited upon a cold spray layer covering the surface of the component.
  • cold spray gas dynamic spraying
  • This technique is advantageous in that it provides sufficient energy to accelerate particles to high enough velocities such that, upon impact during an initial pass, the particles plastically deform and bond to the surface of the component on which they are being deposited so as to build a relatively dense coating or structural deposit. On subsequent passes, the particles bond to the previously deposited layer.
  • Cold spray does not metallurgically transform the particles from their solid state.
  • the cold spray process has been found to be most useful in effecting repairs of components formed from ductile materials.
  • the cold spray process may be used during the repair of turbine engine components, such as a fan exit inner case or a gearbox, formed from aluminum or magnesium based materials.
  • the process described herein restores the coating of an affected area on the surface of a component without consuming the surface, that is, the original thickness, of the component.
  • hard anodizing processes alone can consume parent alloy up to fifty percent (50%) of the anodic layer.
  • the inventors of the present application discovered first depositing a repair material via, for example, cold spray deposition techniques, and then anodizing the repaired component actually preserved the original thickness of the component while in turn imparting wear resistance and corrosion protection.
  • This process is effective for providing economical hard anodize protection to magnesium alloys.
  • the hard anodic conversion processes are not easily or economically applied to magnesium alloys.
  • the inventors discovered by first applying cold sprayed aluminum to magnesium alloy based components, hard anodic conversion and chromate conversion coatings may be applied and the advantages and benefits achieved as disclosed herein. Moreover, there are benefits and advantages beyond the application to aluminum and magnesium based alloys. As the cold spray is a mechanical bonded substrate, the cold spray material may be applied to more expensive alloys or alloys known to be difficult to apply hard anodized coatings upon and be subsequently hard anodized more efficiently.
  • FIG. 2 shows a flowchart illustrating an exemplary process of the present disclosure.
  • a component composed of a magnesium alloy, aluminum alloy, conductive alloys, combinations comprising at least one of the foregoing alloys, and the like, and having an exterior surface is provided.
  • Representative aluminum alloys for cold spray deposition include but are not limited to 1000 series, 5000 series and 6000 series.
  • the component may be a gas turbine engine such as fan cases, bleed valves, bleed ducts, clamps, nacelle v-grooves, nacelle track sliders, gearboxes, and the like.
  • the component may be inspected for damage at step 10 using any one of a number of techniques known to one of ordinary skill in the art.
  • the material composition of the component may also be determined at step 12 using any one of a number of techniques known to one of ordinary skill in the art.
  • corrosion pits and/or damaged areas are mechanically removed (step 14 ) through grinding, machining, or other applicable techniques known to one of ordinary skill in the art.
  • the resultant surface area may be cleaned using a chemical based cleaning technique (step 16 ) known to one of ordinary skill in the art.
  • the chemically cleaned surface area of the component may be prepared for cold spray deposition (step 18 ) using a grit blasting technique known to one of ordinary skill in the art.
  • FIG. 3 there is shown a system for carrying out a cold spray process on an affected area 44 of a component or a part.
  • a representative cold spray process is disclosed in U.S. patent application Ser. No. 11/825,384 to Bunting et al., assigned to United Technologies Corporation and incorporated herein by reference in its entirety.
  • Another representative process is disclosed in United States Patent Publication No. 2006/0134320 to DeBiccari et al., and assigned to United Technologies Corporation, the assignee of the present application, is incorporated herein by reference in its entirety.
  • the system includes a spray gun 42 having a converging/diverging nozzle 40 through which the repair material is sprayed onto an affected area of a surface 45 of the component 60 to be repaired.
  • the component 60 may be held stationary or may be articulated or translated by any suitable means (not shown) known in the art.
  • spray nozzle 40 may be held stationary or may be articulated or translated. In some situations, both the part and the nozzle may be manipulated.
  • Suitable aluminum containing materials which may be used to effect repairs in accordance with the process described herein, but are not limited to, pure aluminum, aluminum alloy 6061, aluminum alloy 2219, Al-12Si alloy, Al—Sc alloy, aluminum alloy 6061/B4C, and aluminum alloy 5056.
  • the aluminum containing material comprises a material which has a composition that includes more than 50% by weight of aluminum.
  • the repair material feedstock may be a powdered aluminum containing material 51 .
  • the powdered aluminum containing material may be a powdered aluminum containing material of ⁇ 325 mesh with particle sizes in the range of from 5 microns to 50 microns. Smaller particle sizes such as those mentioned before enable the achievement of higher particle velocities. Below 5 microns in diameter, the particles risk getting swept away from the surface 45 and/or the affected area 44 due to a bow shock layer above the surface 45 and/or the affected area 44 . This is due to insufficient mass to propel the particles through the bow shock. The narrower the particle size distribution, the more uniform the particle velocity will be. This is because if one has large and small particles (bi-modal), the small ones will hit the slower, larger ones and effectively reduce the velocity of both.
  • the fine particles of the aluminum containing repair material may be accelerated to supersonic velocities using compressed gas, such as helium, nitrogen, or other inert gases, and mixtures thereof.
  • compressed gas such as helium, nitrogen, or other inert gases, and mixtures thereof.
  • Helium and nitrogen are preferred gases because both helium and nitrogen produce the highest velocity due to their low molecular weights.
  • the bonding mechanism employed by the method of the present invention for transforming the powdered aluminum containing repair material into a deposit is strictly solid state, meaning that the particles plastically deform. Any oxide layer that is formed on the particles and/or on the component surface is broken up and fresh metal-to-metal contact is made at very high pressures.
  • the powdered aluminum containing repair material used to form the deposit may be fed to the spray gun 42 using any suitable means known in the art, such as modified thermal spray feeders.
  • a Praxair® powder feeder at a wheel speed of 1-5 rpm may be used.
  • the feeder may be pressurized with a gas 53 selected from the group consisting of helium, nitrogen, or other inert gases, and mixtures thereof.
  • a gas 53 selected from the group consisting of helium, nitrogen, or other inert gases, and mixtures thereof.
  • the feeder may be pressurized using helium at a pressure in the range from 200 psi to 400 psi, preferably from 300 to 350 psi.
  • the main gas is preferably heated so that the gas temperatures is in a range from 250° C. (482° F.) to 550° C. (1022° F.), preferably from 350° C. (662° F.) to 450° C. (842° F.).
  • the feeder may be pressurized using nitrogen gas at a pressure in a range from 400 psi to 600 psi, preferably from 500 psi to 550 psi.
  • the main gas is also preferably heated so that the gas temperature is in a range from 250° C. (482° F.) to 550° C. (1022° F.), preferably from 350° C. (662° F.) to 450° C. (842° F.).
  • the gas may be heated to keep it from rapidly cooling and freezing once it expands past the throat of nozzle 20 .
  • the net effect is a surface temperature on the part being repaired of about 46° C. (115° F.) during deposition. Any suitable means known in the art may be used to heat the gas.
  • the nozzle 40 may pass over the affected area 44 of the part 60 being repaired more than once.
  • the number of passes required is a function of the thickness of the repair material to be applied.
  • the method of the present invention is capable of forming a deposit having any desired thickness. If one wants to form a thick layer, the spray gun 42 may be held stationary to form a thick deposit over the affected area 44 .
  • the main gas that is used to deposit the particles of the repair material over the affected area 44 may be passed through the nozzle 40 via an inlet 50 at a flow rate of 0.001 SCFM to 60 SCFM, preferably in the range of 15 SCFM to 50 SCFM.
  • the foregoing flow rates are useful when either helium or nitrogen is used as the main gas.
  • the pressure of the spray gun 42 may be in the range of from 200 psi to 400 psi, preferably from 300 psi to 350 psi.
  • the powdered aluminum containing repair material is preferably fed from a hopper, which is under a pressure in the range of 10 to 50 psi higher than the specific main gas pressure, preferably 15 psi higher to the spray gun 42 via line 54 at a feed rate in the range of 10 grams/min to 100 grams/min, preferably 15 grams/min to 50 grams/min.
  • the powdered aluminum containing repair material is preferably fed to the spray gun 42 using a non-oxidizing carrier gas.
  • the carrier gas may be introduced via inlet 50 at a flow rate of 0.001 SCFM to 50 SCFM, preferably 1 SCFM to 15 SCFM.
  • the foregoing flow rates are useful when either helium or nitrogen is used as the carrier gas.
  • the spray nozzle 20 is held at a distance from the affected area 24 . This distance is known as the spray distance. Preferably, the spray distance is in the range of 10 mm to 50 mm.
  • the velocity of the powdered repair material particles leaving the spray nozzle 20 may be in a range from 825 m/s to 1400 m/s, preferably from 850 m/s to 1200 m/s.
  • the deposit thickness per pass may be in the range of 0.001 inches to 0.030 inches.
  • the aluminum containing repair material such as aluminum alloy 6061
  • the aluminum containing repair material may be cold sprayed (step 20 ) over the affected area on the component 60 to a thickness above the original wall thickness.
  • the component 60 may undergo stress relief, for example, heat treatment, at step 22 as known to one ordinary skill in the art.
  • the stress relief step may be carried out at a temperature which achieves the desired ductility for the component 60 .
  • the heat treatment may be one in which the component with the cold sprayed aluminum containing material deposit is heated in an air oven to a temperature of 260° C. (500° F.) for a time period of 1 hour to 2 hours. When some aluminum containing repair materials are used, no heat treatment may be needed. When other aluminum containing repair materials are used, the heat treatment may be at a temperature which varies from 38° C. (100° F.) to a temperature greater than 260° C. (500° F.) for a time period in the range of 1 hour to 24 hours. When the component requires undergoing stress relief, the entire component, or the local area of the repair, may be treated.
  • the cold spray layered component 60 with the deposited repair material may be mechanically smoothed in the region of the affected area 44 and structural credit may be claimed for the repaired area.
  • Structural credit as used herein refers to the fact that the cold sprayed aluminum alloy repair material has a percentage of the base material strength and repaired thickness is considered as part of the measured wall thickness.
  • the cold spray layered component 60 may be preliminarily inspected to determine whether the wear resistance is sufficient at step 24 . Any one of a number of suitable techniques for determining wear resistance known to one of ordinary skill in the art may be utilized.
  • the term effective wall thickness means that if one considers the sprayed deposit to have 75% of the strength of the base material forming the component 60 , then the repair thickness is credited 75%. Thus, if the current wall thickness of the component 60 is 0.100 inches and a deposit of 0.050 inches is applied to make total thickness of 0.150 inches, the effective wall thickness of the repair is 0.1375 inches since the repair material has 75% of the strength of the base material of the component.
  • the component 60 may undergo a final inspection at step 32 . However, if the component 60 does not demonstrate sufficient wear resistance, the cold sprayed aluminum layered component 60 then undergoes an anodizing process.
  • the cold sprayed aluminum layered component 60 may be treated to remove grease, if necessary, from the cold spray layer as known to one of ordinary skill in the art.
  • the optional grease removal step may be done, if necessary, prior to anodizing the cold sprayed aluminum layer.
  • anodized aluminum refers to aluminum and its alloys which have been subjected to the anodizing process to produce adherent aluminum oxide (Al 2 O 3 ) coatings thereon.
  • adherent aluminum oxide Al 2 O 3
  • Such aluminum oxide coatings provide hard and strong protective coatings and protect against corrosion and abrasion as well as strengthen the coated articles and provide electrical insulation thereon.
  • the process described herein subjects the deposited cold sprayed aluminum layer to an anodizing process (step 26 ) known to one of ordinary skill in the art.
  • the anodizing process comprises anodizing the metal substrate in a sulfuric acid based anodizing solution, preferably a sulfuric oxalic acid anodizing solution, at step 26 .
  • the deposited cold sprayed aluminum layer may be subjected to a sulfuric oxalic acid anodize by any manner as known to one of ordinary skill in art.
  • the anodizing process forms a hard oxide layer 70 upon a cold spray layer 68 of component 60 without consuming the parent alloy and only consuming a portion of the cold spray layer 68 (See FIG. 7 ).
  • the hard anodized component 60 may be preliminarily inspected to determine whether the corrosion resistance is sufficient at step 28 .
  • Sufficient corrosion resistance may be determined using any one of a number of techniques known to one of ordinary skill in the art. If the hard anodized component 60 demonstrates sufficient corrosion resistance, the hard coated component 60 may then undergo a final inspection at step 32 . However, if the hard anodized component 60 does not demonstrate sufficient corrosion resistance, the hard coated component 60 may then undergo a corrosion resistant sealant process at step 30 .
  • the hard coated component 60 may be contacted with an acidic trivalent chromium containing solution to form a trivalent chrome enriched coating upon the anodized component.
  • the acidic aqueous solution comprises a water soluble trivalent chromium compound, a water soluble fluoride compound and an alkaline reagent.
  • a representative acidic aqueous solution may comprise a trivalent chromium compound is present in an amount of between 0.2 g/liter to 5 g/liter (preferably between 0.5 g/liter to 2 g/liter), a fluoride compound is present in an amount of between 0.2 g/liter to 5 g/liter (preferably 0.5 g/liter to 2 g/liter), and an alkaline reagent is present in an amount to maintain the pH of the solution between 3.0 to 5.0 (preferably 3.5 to 4.0).
  • water soluble molybdenum compound may be substituted for the trivalent chromium compound as such molybdenum compounds may also be utilized as corrosion resistant sealants.
  • the solution may be applied or contacted upon the hard coated component 60 using any one of a number of processes including but not limited to immersion, spraying, painting, and the like as known to one of ordinary skill in the art.
  • each Panel 1 - 7 was removed to perform metallographic examination of the bond line between the cold spray aluminum 6061 layer and aluminum alloy 6061 substrate and the microstructural comparison between the two (See Panel 1 of FIG. 4 ).
  • Panels 1 - 7 submitted for anodized hard anodize were non-standard size for subsequent salt fog testing ASTM B-117.
  • Panels 1 - 7 were hard anodized per AMS 2469 (See FIG. 5 ).
  • Metallographic evaluation of the junction area of the anodized hard coating and substrate did not reveal any evidence of crevice corrosion after salt fog exposure (See FIG. 6 ).
  • the chemistry of the cold sprayed aluminum alloy 6061 deposited material was the same as standard aluminum alloy 6061 material of the panels. However, the metallurgical structure was different between the cold sprayed aluminum alloy layer and the parent aluminum alloy panel. The cold sprayed aluminum alloy layer responded to the hard anodize process the same as the parent aluminum alloy. Satisfactory coatings were generated using typical 6061 parameters and there was no noticeable difference in the coating in the interface where the base 6061 material and the cold sprayed 6061 met. There was no discernible loss in salt fog test performance and no difference at the interface of the base metal and coating. Hardness measurements in the hard anodized area as well as the base material and cold sprayed material were consistent with normal readings for this material. The tensile bond strength specimens all failed in the epoxy indicative of good adhesion of the coating. These tests confirmed that hard anodize of cold sprayed aluminum alloy 6061 is a viable candidate for repairing aluminum structures.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Metallurgy (AREA)
  • Electrochemistry (AREA)
  • Mechanical Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • General Engineering & Computer Science (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
  • Application Of Or Painting With Fluid Materials (AREA)
  • Chemical Treatment Of Metals (AREA)
US12/342,148 2008-12-23 2008-12-23 Hard anodize of cold spray aluminum layer Abandoned US20100155251A1 (en)

Priority Applications (2)

Application Number Priority Date Filing Date Title
US12/342,148 US20100155251A1 (en) 2008-12-23 2008-12-23 Hard anodize of cold spray aluminum layer
EP09252862A EP2204473A3 (de) 2008-12-23 2009-12-22 Hartanodisieren von Cold-Spray-Aluminiumschicht

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US12/342,148 US20100155251A1 (en) 2008-12-23 2008-12-23 Hard anodize of cold spray aluminum layer

Publications (1)

Publication Number Publication Date
US20100155251A1 true US20100155251A1 (en) 2010-06-24

Family

ID=41719001

Family Applications (1)

Application Number Title Priority Date Filing Date
US12/342,148 Abandoned US20100155251A1 (en) 2008-12-23 2008-12-23 Hard anodize of cold spray aluminum layer

Country Status (2)

Country Link
US (1) US20100155251A1 (de)
EP (1) EP2204473A3 (de)

Cited By (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100187119A1 (en) * 2009-01-29 2010-07-29 Honeywell International Inc. Cold spray and anodization repair process for restoring worn aluminum parts
US20110073602A1 (en) * 2009-09-29 2011-03-31 Calphalon Corporation Lightweight cookware and method of making same
CN104046981A (zh) * 2013-03-12 2014-09-17 朗姆研究公司 等离子体室部件上的抗腐蚀铝涂层
US20150132602A1 (en) * 2013-11-13 2015-05-14 Applied Materials, Inc. High purity metallic top coat for semiconductor manufacturing components
US20160097329A1 (en) * 2014-10-01 2016-04-07 Rolls-Royce Corporation Corrosion and abrasion resistant coating
CN105926015A (zh) * 2016-05-12 2016-09-07 安徽纯启动力机械有限公司 一种铝合金压铸件电化学表面强化处理工艺
US9599210B2 (en) 2013-11-06 2017-03-21 Sikorsky Aircraft Corporation Damage mitigation for gearbox
US9624593B2 (en) 2013-08-29 2017-04-18 Applied Materials, Inc. Anodization architecture for electro-plate adhesion
US9850591B2 (en) 2013-03-14 2017-12-26 Applied Materials, Inc. High purity aluminum top coat on substrate
US10077499B2 (en) 2013-11-06 2018-09-18 Sikorsky Aircraft Corporation Corrosion mitigation for gearbox
CN108937604A (zh) * 2017-05-22 2018-12-07 佛山市顺德区美的电热电器制造有限公司 铁锅及其制备方法和烹饪器具
CN110280968A (zh) * 2019-05-23 2019-09-27 中国人民解放军第五七一九工厂 一种发动机滑油泵组复合材料衬套修装方法
US10458035B2 (en) 2017-07-21 2019-10-29 United Technologies Corporation Anodization of bonded assembly
CN111172525A (zh) * 2020-01-08 2020-05-19 中国科学院宁波材料技术与工程研究所 一种利用冷喷涂连接异质材料的方法
CN111996524A (zh) * 2020-07-21 2020-11-27 国营芜湖机械厂 一种飞机液压系统铝合金活塞杆耐磨层损伤的修复方法
US11662300B2 (en) 2019-09-19 2023-05-30 Westinghouse Electric Company Llc Apparatus for performing in-situ adhesion test of cold spray deposits and method of employing
US11898986B2 (en) 2012-10-10 2024-02-13 Westinghouse Electric Company Llc Systems and methods for steam generator tube analysis for detection of tube degradation
US11935662B2 (en) 2019-07-02 2024-03-19 Westinghouse Electric Company Llc Elongate SiC fuel elements

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ITTO20110257A1 (it) * 2011-03-24 2012-09-25 Avio Spa Metodo per la riparazione di un componente in lega di alluminio
CN103255410B (zh) * 2013-04-24 2015-08-26 中国航空工业集团公司北京航空材料研究院 一种镁合金抗腐蚀防护涂层的制备方法
CN104562136A (zh) * 2013-10-21 2015-04-29 广东澳美铝业有限公司 一种铝型材磨砂工艺
CN104894555A (zh) * 2014-11-14 2015-09-09 天津工业大学 一种铁基镍包碳化硼激光熔覆材料的制备方法
EP3936640A1 (de) * 2020-07-10 2022-01-12 Siemens Aktiengesellschaft Farbig eloxierte stromschienen mit kaltgasbeschichtung für stromrichter

Citations (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4504325A (en) * 1982-03-19 1985-03-12 The Boeing Company Method for sealing an aluminum oxide film
US4545876A (en) * 1984-05-02 1985-10-08 United Technologies Corporation Method and apparatus for surface treating
US4775427A (en) * 1986-09-18 1988-10-04 Gerhard Collardin Gmbh Phosphate conversion coatings for composite metals
US5304257A (en) * 1993-09-27 1994-04-19 The United States Of America As Represented By The Secretary Of The Navy Trivalent chromium conversion coatings for aluminum
US6139713A (en) * 1996-08-26 2000-10-31 Nippon Telegraph And Telephone Corporation Method of manufacturing porous anodized alumina film
US6365222B1 (en) * 2000-10-27 2002-04-02 Siemens Westinghouse Power Corporation Abradable coating applied with cold spray technique
US6444259B1 (en) * 2001-01-30 2002-09-03 Siemens Westinghouse Power Corporation Thermal barrier coating applied with cold spray technique
US6491208B2 (en) * 2000-12-05 2002-12-10 Siemens Westinghouse Power Corporation Cold spray repair process
US6511532B2 (en) * 2000-10-31 2003-01-28 The United States Of America As Represented By The Secretary Of The Navy Post-treatment for anodized aluminum
US6537678B1 (en) * 2000-09-20 2003-03-25 United Technologies Corporation Non-carcinogenic corrosion inhibiting additive
US6706319B2 (en) * 2001-12-05 2004-03-16 Siemens Westinghouse Power Corporation Mixed powder deposition of components for wear, erosion and abrasion resistant applications
US6759085B2 (en) * 2002-06-17 2004-07-06 Sulzer Metco (Us) Inc. Method and apparatus for low pressure cold spraying
US6780458B2 (en) * 2001-08-01 2004-08-24 Siemens Westinghouse Power Corporation Wear and erosion resistant alloys applied by cold spray technique
US6887321B2 (en) * 2002-05-22 2005-05-03 United Technologies Corporation Corrosion resistant surface treatment for structural adhesive bonding to metal
US20060134320A1 (en) * 2004-12-21 2006-06-22 United Technologies Corporation Structural repair using cold sprayed aluminum materials
US20060169592A1 (en) * 2005-01-31 2006-08-03 Hewlett-Packard Development Company, L.P. Periodic layered structures and methods therefor
US20060240192A1 (en) * 2005-04-25 2006-10-26 Honeywell International, Inc. Magnesium repair and build up
US20070227683A1 (en) * 2005-09-19 2007-10-04 United Technologies Corporation Manufacture of casting cores
US7402277B2 (en) * 2006-02-07 2008-07-22 Exxonmobil Research And Engineering Company Method of forming metal foams by cold spray technique
US20090011123A1 (en) * 2007-07-06 2009-01-08 United Technologies Corporation Corrosion protective coating through cold spray
US20090148622A1 (en) * 2006-03-02 2009-06-11 Thorsten Stoltenhoff Process for the repair and restoration of dynamically stressed components comprising aluminium alloys for aircraft applications

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE10359046B4 (de) * 2003-12-17 2012-07-19 Newspray Gmbh Verfahren zum Erzeugen einer dekorativen Oberfläche und hergestellter Gegenstand
EP1832671A3 (de) * 2006-03-07 2010-07-28 Linde AG Verfahren zur Verschleiss-und Korrosionsschutzbeschichtung
DE102006010520A1 (de) * 2006-03-07 2007-09-13 Linde Ag Verfahren zur dekorativen anodischen Oxidation

Patent Citations (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4504325A (en) * 1982-03-19 1985-03-12 The Boeing Company Method for sealing an aluminum oxide film
US4545876A (en) * 1984-05-02 1985-10-08 United Technologies Corporation Method and apparatus for surface treating
US4775427A (en) * 1986-09-18 1988-10-04 Gerhard Collardin Gmbh Phosphate conversion coatings for composite metals
US5304257A (en) * 1993-09-27 1994-04-19 The United States Of America As Represented By The Secretary Of The Navy Trivalent chromium conversion coatings for aluminum
US6139713A (en) * 1996-08-26 2000-10-31 Nippon Telegraph And Telephone Corporation Method of manufacturing porous anodized alumina film
US6537678B1 (en) * 2000-09-20 2003-03-25 United Technologies Corporation Non-carcinogenic corrosion inhibiting additive
US6365222B1 (en) * 2000-10-27 2002-04-02 Siemens Westinghouse Power Corporation Abradable coating applied with cold spray technique
US6511532B2 (en) * 2000-10-31 2003-01-28 The United States Of America As Represented By The Secretary Of The Navy Post-treatment for anodized aluminum
US6491208B2 (en) * 2000-12-05 2002-12-10 Siemens Westinghouse Power Corporation Cold spray repair process
US6444259B1 (en) * 2001-01-30 2002-09-03 Siemens Westinghouse Power Corporation Thermal barrier coating applied with cold spray technique
US6780458B2 (en) * 2001-08-01 2004-08-24 Siemens Westinghouse Power Corporation Wear and erosion resistant alloys applied by cold spray technique
US6706319B2 (en) * 2001-12-05 2004-03-16 Siemens Westinghouse Power Corporation Mixed powder deposition of components for wear, erosion and abrasion resistant applications
US6887321B2 (en) * 2002-05-22 2005-05-03 United Technologies Corporation Corrosion resistant surface treatment for structural adhesive bonding to metal
US6759085B2 (en) * 2002-06-17 2004-07-06 Sulzer Metco (Us) Inc. Method and apparatus for low pressure cold spraying
US20060134320A1 (en) * 2004-12-21 2006-06-22 United Technologies Corporation Structural repair using cold sprayed aluminum materials
US20060169592A1 (en) * 2005-01-31 2006-08-03 Hewlett-Packard Development Company, L.P. Periodic layered structures and methods therefor
US20060240192A1 (en) * 2005-04-25 2006-10-26 Honeywell International, Inc. Magnesium repair and build up
US20070227683A1 (en) * 2005-09-19 2007-10-04 United Technologies Corporation Manufacture of casting cores
US7402277B2 (en) * 2006-02-07 2008-07-22 Exxonmobil Research And Engineering Company Method of forming metal foams by cold spray technique
US20090148622A1 (en) * 2006-03-02 2009-06-11 Thorsten Stoltenhoff Process for the repair and restoration of dynamically stressed components comprising aluminium alloys for aircraft applications
US20090011123A1 (en) * 2007-07-06 2009-01-08 United Technologies Corporation Corrosion protective coating through cold spray

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
Cotell, C.M.; Sprague, J.A.; Snidt, F.A.: ASM Handbook, Volume 5: Surface Engineering. ASM International, 1994, p. 482-493. *

Cited By (31)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8486249B2 (en) * 2009-01-29 2013-07-16 Honeywell International Inc. Cold spray and anodization repair process for restoring worn aluminum parts
US20100187119A1 (en) * 2009-01-29 2010-07-29 Honeywell International Inc. Cold spray and anodization repair process for restoring worn aluminum parts
US20110073602A1 (en) * 2009-09-29 2011-03-31 Calphalon Corporation Lightweight cookware and method of making same
US11898986B2 (en) 2012-10-10 2024-02-13 Westinghouse Electric Company Llc Systems and methods for steam generator tube analysis for detection of tube degradation
CN104046981A (zh) * 2013-03-12 2014-09-17 朗姆研究公司 等离子体室部件上的抗腐蚀铝涂层
US20140272459A1 (en) * 2013-03-12 2014-09-18 Lam Research Corporation Corrosion resistant aluminum coating on plasma chamber components
KR20140111997A (ko) * 2013-03-12 2014-09-22 램 리써치 코포레이션 플라즈마 챔버 부품 상의 내식성 알루미늄 코팅
US9337002B2 (en) * 2013-03-12 2016-05-10 Lam Research Corporation Corrosion resistant aluminum coating on plasma chamber components
KR102218717B1 (ko) 2013-03-12 2021-02-22 램 리써치 코포레이션 플라즈마 챔버 부품 상의 내식성 알루미늄 코팅
US9850591B2 (en) 2013-03-14 2017-12-26 Applied Materials, Inc. High purity aluminum top coat on substrate
US10774436B2 (en) 2013-03-14 2020-09-15 Applied Materials, Inc. High purity aluminum top coat on substrate
US9624593B2 (en) 2013-08-29 2017-04-18 Applied Materials, Inc. Anodization architecture for electro-plate adhesion
US9599210B2 (en) 2013-11-06 2017-03-21 Sikorsky Aircraft Corporation Damage mitigation for gearbox
EP3066232A4 (de) * 2013-11-06 2017-06-07 Sikorsky Aircraft Corporation Schadenverminderung für getriebe
US10077499B2 (en) 2013-11-06 2018-09-18 Sikorsky Aircraft Corporation Corrosion mitigation for gearbox
US10677340B2 (en) 2013-11-06 2020-06-09 Sikorsky Aircraft Corporation Damage mitigation for gearbox
US10883178B2 (en) 2013-11-06 2021-01-05 Sikorsky Aircraft Corporation Corrosion mitigation for gearbox
US9663870B2 (en) * 2013-11-13 2017-05-30 Applied Materials, Inc. High purity metallic top coat for semiconductor manufacturing components
US9879348B2 (en) 2013-11-13 2018-01-30 Applied Materials, Inc. High purity metallic top coat for semiconductor manufacturing components
US10260160B2 (en) 2013-11-13 2019-04-16 Applied Materials, Inc. High purity metallic top coat for semiconductor manufacturing components
US20150132602A1 (en) * 2013-11-13 2015-05-14 Applied Materials, Inc. High purity metallic top coat for semiconductor manufacturing components
US20160097329A1 (en) * 2014-10-01 2016-04-07 Rolls-Royce Corporation Corrosion and abrasion resistant coating
US10077717B2 (en) * 2014-10-01 2018-09-18 Rolls-Royce Corporation Corrosion and abrasion resistant coating
CN105926015A (zh) * 2016-05-12 2016-09-07 安徽纯启动力机械有限公司 一种铝合金压铸件电化学表面强化处理工艺
CN108937604A (zh) * 2017-05-22 2018-12-07 佛山市顺德区美的电热电器制造有限公司 铁锅及其制备方法和烹饪器具
US10458035B2 (en) 2017-07-21 2019-10-29 United Technologies Corporation Anodization of bonded assembly
CN110280968A (zh) * 2019-05-23 2019-09-27 中国人民解放军第五七一九工厂 一种发动机滑油泵组复合材料衬套修装方法
US11935662B2 (en) 2019-07-02 2024-03-19 Westinghouse Electric Company Llc Elongate SiC fuel elements
US11662300B2 (en) 2019-09-19 2023-05-30 Westinghouse Electric Company Llc Apparatus for performing in-situ adhesion test of cold spray deposits and method of employing
CN111172525A (zh) * 2020-01-08 2020-05-19 中国科学院宁波材料技术与工程研究所 一种利用冷喷涂连接异质材料的方法
CN111996524A (zh) * 2020-07-21 2020-11-27 国营芜湖机械厂 一种飞机液压系统铝合金活塞杆耐磨层损伤的修复方法

Also Published As

Publication number Publication date
EP2204473A2 (de) 2010-07-07
EP2204473A3 (de) 2010-07-14

Similar Documents

Publication Publication Date Title
US20100155251A1 (en) Hard anodize of cold spray aluminum layer
US8597724B2 (en) Corrosion protective coating through cold spray
Champagne The repair of magnesium rotorcraft components by cold spray
EP1674595B1 (de) Strukturelle Reparatur durch Kaltspritzverfahren von Aluminumwerkstoffen
EP2088225B1 (de) Erosions- und korrosionsbeständiges Beschichtungssystem und Verfahren dafür
EP1877598B1 (de) Magnesiumreparatur und -aufbau
Parco et al. Investigation of HVOF spraying on magnesium alloys
Yandouzi et al. Aircraft skin restoration and evaluation
KR930008927B1 (ko) 이중 보호 피복물을 갖는 강철제품과 그 제조방법
Moridi et al. Number of passes and thickness effect on mechanical characteristics of cold spray coating
Petráčková et al. Mechanical performance of cold-sprayed A357 aluminum alloy coatings for repair and additive manufacturing
JP2002303272A (ja) 保護コーティングを有する圧縮機及び圧縮機コーティング方法
Champagne et al. Magnesium repair by cold spray
Nourian et al. Effect of substrate surface finish and particle velocity on fatigue performance of cold spray coated A6061 aluminum alloy
Champagne et al. Cold spray applications
Champagne Repair of magnesium components by cold spray techniques
CN114318324A (zh) 一种用于镁合金车轮冷喷涂的喷涂粉末及其喷涂工艺和评价方法
JP3479753B2 (ja) 鋼材の表面処理方法および水系クロメート処理液
Huang et al. Comparison of cold sprayed and arc sprayed Zn15Al alloy coating on AZ91D magnesium substrate
JP3420568B2 (ja) 低熱膨張係数材料
CN109628875A (zh) 一种制备铁基材料锌系合金机械结合改性层的方法
Mäkinen et al. Mechanical properties and corrosion resistance of cold sprayed coatings
Percoco et al. Cold Spray Defects: An Investigation on Very Low Scanning Speeds
Yandouzi et al. Restoration of Damaged Aircraft Skin by Cold Spray Technique: The Advantages and the Challenges
Borhan Dayani Improvement of fatigue and corrosion-fatigue resistance of AZ31B cast alloy by cold spray coating and top coating

Legal Events

Date Code Title Description
AS Assignment

Owner name: UNITED TECHNOLOGIES CORPORATION,CONNECTICUT

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:BOGUE, WILLIAM;DEROSA, ROBERT J.;LOMASNEY, GARY M.;AND OTHERS;REEL/FRAME:022020/0248

Effective date: 20081218

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION