KR101852731B1 - Non-inflammably Highly Efficient Heat Insulator and Method for Preparing the Same - Google Patents

Non-inflammably Highly Efficient Heat Insulator and Method for Preparing the Same Download PDF

Info

Publication number
KR101852731B1
KR101852731B1 KR1020170124278A KR20170124278A KR101852731B1 KR 101852731 B1 KR101852731 B1 KR 101852731B1 KR 1020170124278 A KR1020170124278 A KR 1020170124278A KR 20170124278 A KR20170124278 A KR 20170124278A KR 101852731 B1 KR101852731 B1 KR 101852731B1
Authority
KR
South Korea
Prior art keywords
layer
glass fiber
rubber foam
heat
foam layer
Prior art date
Application number
KR1020170124278A
Other languages
Korean (ko)
Inventor
석보미
Original Assignee
석보미
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 석보미 filed Critical 석보미
Priority to KR1020170124278A priority Critical patent/KR101852731B1/en
Application granted granted Critical
Publication of KR101852731B1 publication Critical patent/KR101852731B1/en

Abstract

The present invention discloses a high-functional semi-inflammable heat insulation material and a method for manufacturing the same. In the present invention, a rubber foam layer which is excellent in flame retardancy and waterproofing and is resistant to corrosion due to chemical reactions and a glass fiber film layer having an air layer as a semi-inflammable material are stacked separately on an upper surface and a lower surface of a base layer made of glass fiber having excellent warm-retaining properties and elasticity restoring force. As a result, the elasticity of the thermal insulation material can be increased to enable thinning of the heat insulating material while being installed, and the thickness regarding an installation space can be adjusted to increase the space utilization. The heat insulation material of the present invention is excellent in soundproofing, waterproofing preventing dew condensation and flame retardancy, and heat insulation, and can be used semi-permanently.

Description

고기능성 준불연 단열재 및 그 제조방법 {Non-inflammably Highly Efficient Heat Insulator and Method for Preparing the Same}TECHNICAL FIELD [0001] The present invention relates to a high-performance semi-fireproof insulating material,

본 발명은 단열재에 관한 것으로, 보다 상세하게는 보온성과 탄성복원력이 우수한 유리섬유의 베이스층 상,하면에 각각 난연성 및 방수성이 우수하고 화학적 반응에 의한 부식이 방지되는 고무발포층과 준불연재로서 공기층을 가지는 글라스 화이버(glass fiber)의 피막층을 적층 구성하여, 방음 및 결로를 예방하는 방수성과 난연성, 그리고 단열성이 우수하면서도 반영구적 사용이 가능한 고기능성 준불연 단열재 및 그 제조방법에 관한 것이다.More particularly, the present invention relates to a heat insulating material, and more particularly, to a rubber foam layer which is excellent in flame retardancy and waterproofness on the base layer side and the bottom surface of glass fiber excellent in heat retention and elastic restoring force and is resistant to corrosion by chemical reaction, Which is excellent in waterproof property, flame retardancy, and heat insulating property to prevent soundproofing and dew condensation, and which can be used semi-permanently, and a method for manufacturing the same.

일반적으로, 건축물 및 일반 산업시설 등에는 외부로부터 열이 유입되는 것을 차단하거나 내부의 열이 외부로 방출되는 것을 방지하기 위하여 단열재가 사용되고 있다. 단열재의 재료로서는 통상적으로 스티로폼이 사용되고 있으며, 상기 스티로폼은 발포 수지로서 건축물의 내, 외벽 또는 천장이나 바닥면에 부착된 상태에서 방음 및 단열의 기능을 한다.Generally, heat insulating materials are used in buildings, general industrial facilities, and the like in order to prevent heat from entering from the outside or to prevent internal heat from being released to the outside. Styrofoam is generally used as a material of the heat insulating material, and the foamed resin functions as soundproofing and heat insulation in a state where it is attached to the inner, outer wall, ceiling or floor of the building.

그러나, 종래의 단열재는 다음과 같은 문제점이 있었다.However, the conventional insulator has the following problems.

첫째, 스티로폼만으로는 단열 성능에 한계가 있어 단열효과가 우수하지 못할 뿐만 아니라, 부피가 커서 시공성이 좋지 못한 문제점이 있다.First, Styrofoam alone has a problem that the insulation performance is limited and the insulation effect is not excellent, and the workability is poor due to its large volume.

둘째, 스티로폼의 단열효과를 높이기 위하여 보완재를 결합하여 사용시, 스티로폼과 보완재가 못이나 스테이플러 등과 같은 결합요소에 의해 단순히 기계적으로 결합되는 경우 겹치는 부분에 틈이 생성되고 이러한 틈으로 수분이 침투되어 방수효과가 저하되는 문제점이 있다.Second, when using a combination of fillers to enhance the adiabatic effect of the styrofoam, when the styrofoam and the filler are merely mechanically bonded by a coupling element such as a nail or a stapler, a gap is formed in the overlapping portion, Is lowered.

셋째, 시공된 후에는 스티로폼과 보완재의 결합체의 외면에 별도의 마감용 벽지 등을 더 부착하여야 하는 번거로움이 있다.Third, there is a need to attach additional finishing wallpaper to the outer surface of the combination of the styrofoam and the filler after the construction.

이에, 선행기술로서 등록특허 제 10-1100937 호(명칭; 단열재 및 이의 제조방법), 등록특허 10-620117 호(명칭; 보온단열용 복합구조체 및 그 제조방법), 공개특허공보 제 10-2010-21121(명칭; 단열재 및 그 제조방법)을 통해 상기와 같은 종래 문제점을 개선하도록 하였으며, 본 발명은 이러한 선행기술들의 단점을 보완한 것이다.Accordingly, as a prior art, Patent Document No. 10-1100937 (name: a heat insulating material and a method for manufacturing the same), a registered patent 10-620117 (a name: a composite structure for thermal insulation and a method for manufacturing the same, 21121 (name; insulation material and manufacturing method thereof), and the present invention overcomes the disadvantages of these prior arts.

즉, 상기와 같은 선행기술들은 냉기, 열기 및 습기를 차단하여 단열재의 단열효과를 높이도록 은이 증착되는 은박 폴리에틸렌(PE) 발포체를 사용하였지만, 상기 은이 증착되는 폴리에틸렌 발포체는 공해 유발 원인 물질로서 친환경적이지 않은 문제점이 있고, 특히 단열재를 구성함에 있어 그 두께가 상대적으로 두꺼워 제품을 얇게 제작하는 박형화가 어렵고, 화학적 반응에 의한 부식으로 훼손되면서 단열재의 단열성능을 저하시키게 되는 문제가 발생하였던 것이다.That is, although the above-described prior arts use a silver foil polyethylene (PE) foil to shield cold air, heat, and moisture to enhance the heat insulating effect of the heat insulator, the polyethylene foam on which the silver is deposited is eco- In particular, the thickness of the heat insulating material is relatively thick, so that it is difficult to make the product thinner and the heat insulating performance of the heat insulating material deteriorates due to the corrosion caused by the chemical reaction.

따라서, 본 발명은 상기와 같은 종래의 문제점을 개선하기 위한 것으로 본 발명의 목적은, 방음 및 결로를 예방하는 방수성과 난연성, 그리고 단열성이 우수하면서도 반영구적 사용이 가능한 고기능성 준불연 단열재를 제공하려는 것이다.DISCLOSURE Technical Problem Accordingly, the present invention has been made to solve the above-mentioned problems occurring in the prior art, and it is an object of the present invention to provide a high performance semi-inflammable insulation material which is excellent in waterproofness, flame retardancy and heat insulation to prevent soundproofing and condensation, .

본 발명의 다른 목적으로는, 단열재의 탄성을 증대시켜 단열재 설치에 따른 박형화는 물론, 설치 공간에 대한 두께 조정을 통해 공간 활용도를 높이도록 하는 고기능성 준불연 단열재 제조방법을 제공하려는 것이다.Another object of the present invention is to provide a method for manufacturing a high functionality semi-inflammable insulation material that increases the elasticity of the heat insulating material to increase the space utilization by adjusting the thickness of the installation space as well as the thickness of the heat insulating material.

상기 목적 달성을 위한 본 발명의 고기능성 준불연 단열재는, 보온성과 탄성복원력을 가지는 유리섬유로 이루어지는 경량의 베이스층; 단열효과를 높이는 보온 재료로서, 상기 베이스층의 상,하면에 각각 적층되어 구성되며, 벌집 구조의 제 1 공기실을 형성하고 있고, 화학적 반응에 의한 부식 훼손이 방지되도록 고무발포 보온재로 이루어지는 고무발포층; 및, 준불연재로서 제 2 공기실을 형성하고 있으며, 상기 베이스층과 상기 고무발포층 사이 또는 상기 고무발포층의 바깥쪽 타면에 부착되는 유리섬유(glass fiber)의 피막층; 을 포함하여 구성하는 것이다.The high functionality semi-inflammable insulation material of the present invention for achieving the above object is a lightweight base layer made of glass fiber having heat retention and elastic restoring force; And a first air chamber of a honeycomb structure is formed on each of the upper and lower surfaces of the base layer. The first air chamber is formed of rubber foams made of a rubber foaming insulating material so as to prevent corrosion by chemical reaction layer; And a film layer of glass fiber which forms a second air chamber as a quasi-nonflammable material and adheres to the other surface of the rubber foam layer or between the base layer and the rubber foam layer; As shown in FIG.

본 발명의 다른 일면에 따른 고기능성 준불연 단열재는, 상,하면에 각각 알루미늄 피막의 제 1 외피층이 일체로 부착되고, 보온성과 탄성복원력을 가지는 유리섬유로 이루어지는 경량의 베이스층; 단열효과를 높이는 보온 재료로서, 상기 베이스층의 제 1 외피층에 각각 부착되어 적층되는 상하 한 쌍의 구조물이며, 벌집 구조의 제 1 공기실이 형성되어 있으면서 화학적 반응에 의한 부식 훼손이 방지되도록 타공 난연폼으로 이루어지는 고무발포층; 및, 준불연재로서 복수의 제 2 공기실이 형성되며, 상기 고무발포층의 바깥쪽 타면에 부착되어 적층되는 상하 한 쌍의 구조물인 유리섬유(glass fiber)의 피막층; 을 포함하여 구성하고, 상기 제 1 외피층과 상기 고무발포층은 폴리에틸렌 계열의 접착필름으로 접착되면서 열융착으로 적층 고정되는 것이다.According to another aspect of the present invention, there is provided a high functionality semi-inflammable insulation material, comprising: a lightweight base layer made of glass fiber having a first outer covering layer of an aluminum coating integrally attached on upper and lower surfaces thereof and having thermal insulation and elastic restoring force; A heat insulating material for enhancing a heat insulating effect, comprising: a pair of upper and lower structures each of which is adhered to and laminated on a first outer skin layer of the base layer, wherein a first air chamber of a honeycomb structure is formed, A foamed rubber foam layer; A film layer of a glass fiber, which is a pair of upper and lower structures, which are formed by stacking a plurality of second air chambers as quasi-nonflammable materials and attached to the outer surface of the rubber foam layer; And the first outer skin layer and the rubber foam layer are laminated and fixed by thermal fusion bonding while being adhered with a polyethylene-based adhesive film.

또한, 상기 고무발포층의 안쪽 일면에는 상기 접착필름에 접착되면서 열융착되는 제 3 열반사층; 을 형성하는 것이다.A third heat reflecting layer on the inner surface of the rubber foam layer, the third heat reflecting layer being adhered to the adhesive film while being thermally fused; .

또한, 상기 베이스층과 상기 고무발포층 사이에는 상기 피막층을 대신하여, 상기 제 1 공기실을 폐쇄시키면서 외부 열을 반사시켜 차단하는 제 1 열반사층; 을 부착하여 구성하는 것이다.A first heat reflecting layer is provided between the base layer and the rubber foam layer, instead of the coating layer, to block and reflect external heat while closing the first air chamber. As shown in Fig.

또한, 상기 피막층은 준불연재인 유리섬유 교직물; 및, 상기 유리섬유 교직물의 상면 또는 하면에 부착되는 준불연재로서 외부의 열을 반사시켜 차단하는 제 2 열반사층; 을 포함하며, 상기 유리섬유 교직물은 나선형으로 연속하여 감기는 제 1 방향의 위사와 제 2 방향의 경사를 교직 구조로 직조하여 내부에 상기 제 2 공기실을 형성하는 것이다.Also, the coating layer is a quasi-nonflammable glass fiber fabric; And a second thermally reflecting layer for reflecting and shielding external heat as a semi-fire-resistant material adhered to an upper surface or a lower surface of the glass fiber fabric; Wherein the glass fiber fabric member is formed by weaving the warp yarn in the first direction and the warp yarn in the second direction, which are spirally and continuously wound, in a textured structure to form the second air chamber therein.

또한, 교직 구조로 직조되는 상기 위사와 경사 중 어느 하나는 2가닥 이상으로 합사하여 상기 제 1 방향 또는 제 2 방향으로 평행하게 권취하고, 상기 제 1,2 열반사층은 상기 제 1 방향의 위사 및 상기 제 2 방향의 경사가 서로 교직되어 형성되는 상기 유리섬유 교직물의 제 2 공기실들을 통해 서로 밀착되어 내면 결합이 이루어지도록 구성하는 것이다.In addition, any one of the weft yarns and the warp yarns woven in a weaving structure may be wound in two or more strands and wound in parallel in the first direction or the second direction, and the first and second heat reflecting layers may be wound in the first direction and / And the inclined portions in the second direction are tightly joined to each other through the second air chambers of the glass fiber fabric member formed by being woven together.

또한, 상기 유리섬유 교직물에는 강성 보강을 위한 돌가루가 첨가되도록 구성하는 것이다.In addition, stones for stiffening reinforcement are added to the glass fiber fabric.

또한, 상기 제 1,2 열반사층은 알루미늄 호일인 것이다.The first and second heat reflecting layers are aluminum foils.

또한, 상기 알루미늄 호일은 알루미늄 호일을 압연하는 워크롤의 거칠기 조정을 통하여 그 광택도가 서로 다르게 설정되도록 하여 일면은 유광면으로 하고 타면은 무광면으로 구성하는 것이다.Further, the aluminum foil is made of a glossy surface on one side and a non-glossy side on the other side so that the glossiness of the aluminum foil is adjusted through roughness adjustment of the work roll for rolling the aluminum foil.

또한, 상기 단열재에 대한 박형화를 위해, 상기 유리섬유 교직물은 0.05mm 내지 0.15mm 범위내의 두께를 가지고, 상기 제 1,2 열반사층은 0.030mm 내지 0.040mm 범위내의 두께를 가지도록 구성하는 것이다.In order to reduce the thickness of the heat insulating material, the glass fiber fabric has a thickness within a range of 0.05 mm to 0.15 mm, and the first and second thermal reflective layers have a thickness within a range of 0.030 mm to 0.040 mm.

또한, 상기 고무발포층의 최외측으로 노출되는 상기 피막층의 바깥쪽 타면에는 OPP필름 또는 PET필름으로서 단열재의 시공시 실내측에 배치되어 습기 유입을 차단시키는 방습필름층을 접착 구성하는 것이다.Further, on the other surface of the coating layer exposed to the outermost side of the rubber foam layer, an OPP film or a PET film is disposed on the inner side of the heat insulating material when the heat insulating material is applied to adhere the moistureproof film layer for blocking the inflow of moisture.

또한, 상기 고무발포층의 최외측으로 노출되는 상기 피막층의 바깥쪽 타면에는 단열재의 시공시 실내측에 배치되는 이형지를 접착 구성하는 것이다.In addition, a releasing paper disposed on the inner side of the heat insulating material when the heat insulating material is applied is adhered to the outer surface of the outer side of the coating layer exposed to the outermost side of the rubber foam layer .

다른 일면에 따라, 상기 고기능성 준불연 단열재의 제조방법으로는, (a) 준불연재인 유리섬유를 제 1 방향 위사와 제 2 방향 경사의 교직 구조로 직조하여 내면에 제 2 공기실을 갖는 유리섬유 교직물을 형성한 후 상기 유리섬유 교직물의 상,하면에 각각 알루미늄 호일로 이루어지는 제 2 열반사층을 열융착하여 피막층을 형성하는 공정; (b) 상기 (a)으로부터 형성되는 피막층 또는 외부 열을 반사시켜 차단하는 제 1 열반사층을 보온성과 탄성복원력을 가지는 유리섬유로 이루어지는 경량의 베이스층 상,하면에 각각 열융착시키는 공정; (c) 단열효과를 높이고 화학적 반응에 의한 부식 훼손이 방지되도록 고무발포 보온재로 이루어지면서 단열효과를 높이도록 벌집 구조의 제 1 공기실을 가지는 고무발포층을 형성하고, 상기 고무발포층을 상기 (b)공정으로부터 상기 베이스층의 상,하면에 각각 융착되는 상기 피막층 또는 상기 제 1 열반사층의 일면에 열융착시키는 공정; 및, (d) 상기 (c)공정으로부터 상기 피막층 또는 상기 제 1 열반사층의 일면에 융착되는 상기 고무발포층의 상기 고무발포층의 최외측으로 노출되는 바깥면에는 각각 상기 (a)공정으로부터 형성되는 상기 피막층을 열융착시키는 공정; 을 포함하여 진행하는 것이다.According to another aspect of the present invention, there is provided a method for producing a high functionality semi-inflammable insulation material, comprising the steps of: (a) preparing a glass fiber having a second air chamber on its inner surface by woven glass fibers of quasi-nonflammable materials in a first- A step of forming a coating layer by thermally fusing a second heat reflective layer made of aluminum foil on the upper and lower surfaces of the glass fiber fabric after forming the fiber fabric; (b) a step of thermally fusing a coating layer formed from (a) or a first heat reflecting layer for reflecting and shielding external heat on a lower surface of a lightweight base layer made of glass fiber having thermal insulation and elastic restoring force; (c) forming a rubber foam layer having a first air chamber having a honeycomb structure so as to enhance the adiabatic effect and to prevent corrosion damage caused by a chemical reaction, the rubber foam layer being formed of the rubber foam layer, thermally fusing one surface of the coating layer or the first heat reflecting layer, which is fused to the upper and lower surfaces of the base layer, from the step (b); And (d) an outer surface of the rubber foam layer, which is fused to one surface of the coating layer or the first heat reflecting layer, exposed from the outermost surface of the rubber foam layer from the step (c) A step of thermally fusing the above-mentioned coating layer; .

또 다른 일면에 따라, 상기 고기능성 준불연 단열재의 제조방법으로는, (a1) 준불연재인 유리섬유를 제 1 방향 위사와 제 2 방향 경사의 교직 구조로 직조하여 내면에 제 2 공기실을 갖는 유리섬유 교직물을 형성한 후 상기 유리섬유 교직물의 바깥쪽 타면에 알루미늄 호일로 이루어지는 제 2 열반사층을 열융착하여 피막층을 형성하는 공정; (b1) 보온성과 탄성복원력을 가지는 유리섬유의 상,하면에 각각 알루미늄 피막의 제 1 외피층이 일체로 부착하여 경량의 베이스층을 형성하는 공정; (c1) 단열효과를 높이고 화학적 반응에 의한 부식 훼손이 방지되도록 타공 난연폼으로 이루어지면서 단열효과를 높이도록 벌집 구조의 제 1 공기실을 가지는 고무발포층을 형성한 후 이를 접착필름을 이용하여 상기 (b1)공정으로부터 형성되는 상기 베이스층의 상,하면 제 1 외피층에 접착시킨 후 그 접착부위를 열융착하는 공정; 및, (d1) 상기 (c1)공정으로부터 상기 제 1 외피층에 열융착되는 상기 고무발포층의 최외측으로 노출되는 바깥면에는 각각 상기 (a1)공정으로부터 형성되는 상기 피막층을 열융착시키는 공정; 을 포함하여 진행하는 것이다.According to another aspect of the present invention, there is provided a method for producing a high-performance semi-inflammable insulation material, comprising the steps of (a1) weaving a glass fiber, which is semi-nonflammable material, in a weave structure in a first direction warp and a second direction, Forming a glass fiber cloth and then forming a coating layer by thermally fusing a second heat reflective layer made of aluminum foil on the outer surface of the glass fiber cloth; (b1) a step of forming a lightweight base layer by integrally adhering a first outer skin layer of an aluminum film on upper and lower surfaces of a glass fiber having a warming property and an elastic restoring force; (c1) forming a rubber foam layer having a honeycomb-structured first air chamber so as to increase the heat insulation effect and prevent corrosion damage caused by chemical reaction, (b1) bonding the upper and lower first outer layers of the base layer formed by the step (b1), and then thermally fusing the bonded portions thereof; And (d1) a step of thermally fusing the coat layer formed from the step (a1) on the outermost surface of the rubber foam layer thermally fused to the first outer skin layer from the step (c1); .

또한, 상기 (a1)공정에는, 상기 피막층의 안쪽 일면에 알루미늄 호일로 이루어지는 제 1 열반사층을 열융착시켜, 상기 제 1,2 열반사층이 상기 제 1 방향의 위사 및 상기 제 2 방향의 경사가 서로 교직되어 형성되는 상기 유리섬유 교직물의 제 2 공기실들을 통해 서로 밀착되어 내면 결합이 이루어지도록 하는 공정; 을 더 포함하는 것이다.In the step (a1), the first heat reflecting layer made of aluminum foil is thermally fused to the inner surface of the coating layer, and the first and second heat reflecting layers are formed in the weft in the first direction and the inclination in the second direction Wherein the first and second air chambers of the glass fiber fabric formed by being knitted together are brought into close contact with each other to allow inner surface bonding; .

또한, 상기 (c1)공정에는, 상기 고무발포층의 안쪽 일면에 제 3 열반사층을 일체로 형성한 후 이를 상기 접착필름에 접착시켜 열융착시키는 공정; 을 포 포함하는 것이다.In the step (c1), a third heat reflecting layer is integrally formed on the inner surface of the rubber foam layer, and the thermally fusing adhesive is adhered to the adhesive film. .

또한, 상기 (d)공정과 상기 (d1)공정에는, 상기 고무발포층의 최외측으로 노출되는 상기 피막층의 바깥쪽 타면에 OPP필름 또는 PET필름으로서 단열재의 시공시 실내측에 배치되어 습기 유입을 차단시키는 방습필름층을 접착 구성하는 공정; 을 더 포함하는 것이다.In the step (d) and the step (d1), an OPP film or a PET film is disposed on the other side of the coating layer exposed to the outermost side of the rubber foam layer , A step of bonding a moisture-proofing film layer to be blocked; .

또한, 상기 (d)공정과 상기 (d1)공정에는, 상기 고무발포층의 최외측으로 노출되는 상기 피막층의 바깥쪽 타면에 단열재의 시공시 실내측에 배치되는 이형지를 접착 구성하는 공정; 을 더 포함하는 것이다.In the step (d) and the step (d1), a releasing paper is disposed on the other surface of the coating layer exposed to the outermost side of the rubber foam layer ; .

이와 같이, 본 발명은 보온성과 탄성복원력이 우수한 유리섬유의 베이스층 상,하면에 각각 난연성 및 방수성이 우수하고 화학적 반응에 의한 부식이 방지되는 고무발포층과 준불연재로서 공기층을 가지는 글라스 화이버(glass fiber)의 피막층을 적층 구성한 것이며, 이를 통해 단열재의 탄성을 증대시켜 단열재 설치에 따른 박형화는 물론, 단열재의 설치 공간에 대한 두께 조정이 가능하도록 하여 공간 활용도를 높이고, 방음 및 결로를 예방하는 방수성과 난연성, 그리고 단열성이 우수하면서도 반영구적 사용이 가능한 효과를 기대할 수 있는 것이다.As described above, the present invention provides a rubber foam layer excellent in flame retardancy and waterproofness on the base layer and the bottom surface of the glass fiber excellent in warmth and elastic restoring force and resistant to corrosion due to chemical reaction, and a glass fiber fiber to increase the elasticity of the thermal insulation material to reduce the thickness of the thermal insulation material as well as to adjust the thickness of the thermal insulation material to improve the space utilization and to prevent soundproofing and condensation. Flame retardancy, and heat insulation, but also semi-permanent use.

본 발명의 효과들은 이상에서 언급한 효과들로 제한되지 않으며, 언급되지 않은 또 다른 효과들은 청구범위의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.The effects of the present invention are not limited to the effects mentioned above, and other effects not mentioned can be clearly understood by those skilled in the art from the description of the claims.

도 1은 본 발명의 실시예로 고기능성 준불연 단열재의 구조를 보인 사진.
도 2는 본 발명의 실시예로 고기능성 준불연 단열재의 구조를 보인 단면 개략도.
도 3은 본 발명의 실시예로 교직 구조를 가지는 유리섬유 교직물의 상하면에 각각 제 2 열반사층이 융착된 상태를 보인 구성도.
도 4는 본 발명의 실시예로 교직 구조를 가지는 유리섬유 교직물의 상하면에 각각 제 2 열반사층이 융착된 상태를 보인 단면 개략도.
도 5는 본 발명의 실시예로 고기능성 준불연 단열재에 대한 제조 공정 흐름도.
도 6은 본 발명의 다른실시예로 피막층의 바깥쪽 타면에 방습필름층이 융착된 상태를 보인 단면 개략도.
도 7은 본 발명의 또 다른실시예로 피막층의 바깥쪽 타면에 이형지가 융착된 상태를 보인 단면 개략도.
도 8은 본 발명의 또 다른실시예로 피막층의 구조를 보인 사진.
도 9는 본 발명의 또 다른실시예로 고기능성 준불연 단열재의 구조를 보인 단면 개략도.
BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a photograph showing the structure of a high-performance semi-fireproof insulator according to an embodiment of the present invention. FIG.
2 is a schematic cross-sectional view showing the structure of a high-function semi-inflammable insulation material according to an embodiment of the present invention.
FIG. 3 is a view showing a state in which a second heat reflective layer is fused on the upper and lower surfaces of a glass fiber fabric having a textured structure according to an embodiment of the present invention. FIG.
FIG. 4 is a schematic cross-sectional view showing a state in which a second heat reflective layer is fused on the upper and lower surfaces of a glass fiber cloth having a textured structure according to an embodiment of the present invention. FIG.
5 is a flow chart of a manufacturing process for a high functionality semi-inflammable insulation material according to an embodiment of the present invention.
6 is a cross-sectional schematic view showing a state in which a moisture-proof film layer is fused on the other surface of a coating layer according to another embodiment of the present invention.
7 is a cross-sectional schematic view showing a state in which a release paper is fused to the other surface of the coat layer according to another embodiment of the present invention.
8 is a photograph showing the structure of a coating layer according to still another embodiment of the present invention.
9 is a schematic cross-sectional view showing the structure of a high-performance semi-inflammable insulation material according to another embodiment of the present invention.

이하, 첨부된 도면을 참조하여 본 발명의 실시예를 설명하기로 한다.Hereinafter, embodiments of the present invention will be described with reference to the accompanying drawings.

도 1은 본 발명의 실시예로 고기능성 준불연 단열재의 구조를 보인 사진이고, 도 2는 본 발명의 실시예로 고기능성 준불연 단열재의 구조를 보인 단면 개략도이며, 도 3은 본 발명의 실시예로 교직 구조를 가지는 유리섬유 교직물의 상하면에 각각 제 2 열반사층이 융착된 상태를 보인 구성도이고, 도 4는 본 발명의 실시예로 교직 구조를 가지는 유리섬유 교직물의 상하면에 각각 제 2 열반사층이 융착된 상태를 보인 단면 개략도를 도시한 것이다.FIG. 1 is a photograph showing the structure of a high-performance semi-inflammable insulation material according to an embodiment of the present invention, FIG. 2 is a schematic cross-sectional view showing the structure of a high-performance semi-inflammable insulation material according to an embodiment of the present invention, FIG. 4 is a schematic view showing a state in which a second thermal reflective layer is fused onto the upper and lower surfaces of a glass fiber cloth having a textured structure. And shows a schematic cross-sectional view showing a state in which the reflection layer is fusion-bonded.

첨부된 도 1 내지 도 4에서와 같이, 본 발명의 실시예에 따른 고기능성 준불연 단열재는, 베이스층(10)과 피막층(20) 및 고무발포층(30)의 적층 구조를 이루고, 이에 더하여 제 1 열반사층(40)을 더 포함하여 구성할 수도 있는 것이다.1 to 4, the high functionality semi-inflammable insulation material according to the embodiment of the present invention has a laminated structure of the base layer 10, the coating layer 20 and the rubber foam layer 30, And may further comprise a first thermal reflective layer 40.

상기 베이스층(10)은 보온성과 탄성복원력을 가지는 일정두께의 유리섬유층으로 구성하여둔 것이다.The base layer 10 is made of a glass fiber layer having a certain thickness and having a warming property and an elastic restoring force.

즉, 상기 유리섬유(Glass Fiber)는 내열성 및 내식성과 내습성, 그리고 방음성 및 전기 절연성이 우수한 것으로, 이를 베이스층으로 구성하는 것은 방음 및 결로를 예방하는 한편, 탄성복원력을 통해 평면은 물론 굴곡진 면에서의 단열재 설치가 용이하게 이루어지도록 하면서, 단열재의 설치 공간에 대한 두께 조정이 가능하도록 하여 공간 활용도를 높이기 위함인 것이다.That is, the glass fiber is excellent in heat resistance, corrosion resistance, moisture resistance, sound insulation and electrical insulation, and it is preferable that the base layer is made of a base layer to prevent noise and condensation, So that it is possible to adjust the thickness of the heat insulating material with respect to the installation space, thereby improving space utilization.

상기 피막층(20)은 준불연재인 유리섬유 교직물(21)과 제 2 열반사층(22)을 포함하는 것이다.The coating layer 20 includes a glass fiber cloth 21 and a second thermal reflective layer 22, which are quasi-nonflammable materials.

상기 유리섬유 교직물(21)은 제 1 방향의 위사(21a)와 제 2 방향의 경사(21b)를 교직하는 방식으로 직조하여 구성하는 것으로, 이같은 직조에 따라 내부에 도면에는 표시하지 않았지만 제 2 공기실이 별도로 구성되는 것이며, 유리섬유는 백금로에서 용융해 작은 구멍으로 떨어뜨려 장섬유 상태로 한 것이며, 이는 내열성, 내구성, 흡음성, 전기 절연 효과를 지닌 것이다.The glass fiber cloth 21 is formed by weaving a weft yarn 21a in a first direction and a warp yarn 21b in a second direction by weaving. According to this weaving, although not shown in the figure, The glass fiber is melted in a platinum furnace and dropped into a small hole to be made into a long fiber state, which has heat resistance, durability, sound absorption and electric insulation effect.

상기 유리섬유 교직물(21)에는 단열재의 강성 보강을 위해 추가적으로 돌가루를 첨가 구성할 수 있도록 하였다.The glass fiber cloth 21 is further provided with stone powder for reinforcing the rigidity of the heat insulating material.

상기 제 2 열반사층(22)은 상기 유리섬유 교직물(21)의 상하면에 각각 열착되는 것으로, 상기 제 2 열반사층(22)은 알루미늄 호일로 구성되는 것이다.The second thermal reflective layer 22 is bonded to the upper and lower surfaces of the glass fiber fabric 21 and the second thermal reflective layer 22 is formed of aluminum foil.

여기서, 상기 알루미늄 호일은 알루미늄 호일을 압연하는 워크롤의 거칠기 조정을 통하여 그 광택도가 서로 다르게 설정되도록 하여 일면은 유광면(A1)으로 하고 타면은 무광면(A2)으로 구성할 수도 있는 것이다.Here, the aluminum foil may be made of a glossy surface A1 on one side and a matte surface A2 on the other side so that the degree of gloss of the aluminum foil is adjusted differently by adjusting the roughness of the work roll for rolling the aluminum foil.

상기 고무발포층(30)은 고무발포 보온재인 것이며, 이러한 고무발포 보온재는 신축성이 좋고 가벼우며, 독립성 기포조직으로 흡수성, 단열성, 난연성 등이 탁월하여 냉난방 보온효과를 지닌 것으로서, 분진 발생이 없으며, 대중 이용시설에 깨끗한 실내공기 IAQ(Indoor Air Quality) 유지에 적합하고, 인체에 유해한 물질을 방출하지 않는 친환경적 소재인 것이다.The rubber foam layer 30 is a rubber foam insulator. The rubber foam insulator is excellent in stretchability and light weight, and has an independent bubble structure, excellent in absorbency, heat insulation, flame retardancy, etc., It is an environmentally friendly material that is suitable for maintaining clean indoor air IAQ (Indoor Air Quality) in public facilities and does not emit harmful substances to human body.

이때, 상기 고무발포층(30)은 상기 베이스층(10)의 상,하면에 각각 적층되는 상기 피막층(10)에 적층되어 열융착되는 것으로, 상기 고무발포층(30)은 도면에는 표시하지 않았지만 단열효과를 높이는 제 1 공기실을 가지도록 구성되며, 이에따라 상기 고무발포층(30)은 상기 제 1 공기실을 형성할 수 있는 벌집 구조의 형상을 가지는 것이다.The rubber foam layer 30 is laminated and thermally fused to the coating layer 10 laminated on the upper and lower surfaces of the base layer 10. The rubber foam layer 30 is not shown in the drawing The rubber foam layer 30 is formed to have a honeycomb structure capable of forming the first air chamber.

상기 제 1 열반사층(40)은 상기 베이스층(10)과 고무발포층(30) 사이에서 상기 피막층(20)을 대신하여 열융착될 수 있는 것으로, 상기 제 1 열반사층(40)은 알루미늄 호일로 구성되는 것이다.The first thermal reflective layer 40 may be thermally fused in place of the coating layer 20 between the base layer 10 and the rubber foam layer 30. The first thermal reflective layer 40 may be an aluminum foil .

여기서, 상기 알루미늄 호일은 알루미늄 호일을 압연하는 워크롤의 거칠기 조정을 통하여 그 광택도가 서로 다르게 설정되도록 하여 일면은 유광면(A1)으로 하고 타면은 무광면(A2)으로 구성할 수도 있는 것이다.Here, the aluminum foil may be made of a glossy surface A1 on one side and a matte surface A2 on the other side so that the degree of gloss of the aluminum foil is adjusted differently by adjusting the roughness of the work roll for rolling the aluminum foil.

따라서, 상기와 같이 고기능성 준불연 단열재는 단열효과를 높이도록 유리섬유로 이루어지는 베이스층(10)을 기준으로 하여, 상기 베이스층(10)의 상,하면에 각각 유리섬유 교직물(21)과 제 2 열반사층(22)을 포함하는 피막층(20) 또는 알루미늄 호일로 이루어진 제 1 열반사층(40)의 일면을 융착 구성하는 한편, 상기 피막층(20) 또는 상기 제 1 열반사층(40)의 타면에는 제 1 공기실을 가지는 고무발포층(30)을 열융착하여 구성하고, 이에 더하여, 상기 고무발포층(30)의 일면에 다시 상기 유리섬유 교직물(21)과 제 2 열반사층(22)을 포함하는 피막층(20)을 열융착시키는 한편, 상기 유리섬유 교직물(21)은 0.05mm 내지 0.15mm 범위내의 두께를 가지도록 하고, 상기 제 2 열반사층(22)은 0.030mm 내지 0.040mm 범위내의 두께를 가지도록 하면서, 상기 베이스층(10)과 피막층(20) 또는 제 1 열반사층(40)과 고무발포층(30), 그리고 피막층(20)의 순서로 적층 구조를 이루어게 되는 단열재는 박형화가 가능하게 되는 것이다.Therefore, as described above, the high-performance semi-inflammable insulation material is provided with glass fiber cloths 21 and 21 on upper and lower surfaces of the base layer 10 with reference to the base layer 10 made of glass fiber, A first heat reflecting layer 40 made of an aluminum foil or a film layer 20 including a second heat reflecting layer 22 is fused and bonded to the other surface of the coating layer 20 or the first heat reflecting layer 40 The glass foamed woven fabric 21 and the second heat reflecting layer 22 are further included on one side of the rubber foamed layer 30 by thermally fusing the rubber foamed layer 30 having the first air chamber The glass fiber fabric 21 has a thickness within a range of 0.05 mm to 0.15 mm while the second thermal reflective layer 22 has a thickness within a range of 0.030 mm to 0.040 mm The base layer 10 and the coating layer 20 or First heat reflecting layer 40 and the insulation rubber being made to the layered structure in the order of the foam layer 30 and film layer 20 will be to enable a reduction in thickness.

여기서, 상기와 같은 열융착은 여러개의 롤러부(미도시)와 가열부(미도시)를 포함하여 이루어지는 제조장치에 의해 이루어질 수 있으며, 상기 제조장치의 구성은 특정하게 한정되는 것은 아니다.Here, the thermal fusion may be performed by a manufacturing apparatus including a plurality of roller units (not shown) and a heating unit (not shown), and the configuration of the manufacturing apparatus is not particularly limited.

이와 같이, 본 발명의 실시예에 따른 고기능성 준불연 단열재는 첨부된 도 1 내지 도 5에서와 같이, 유리섬유 교직물(21)과 제 2 열반사층(22)이 열융착됨으로써 형성되는 피막층(20) 또는 제 1 열반사층(40)이 유리섬유로 이루어진 베이스층(10)의 상,하면에 각각 열융착하고, 상기 피막층(20) 또는 제 1 열반사층(40)의 일면에 고무발포층(30)을 열융착한 이후에, 다시 상기 고무발포층(30)의 일면에 상기 피막층(20)을 열융착함에 따라 그 열융착 부분들에 틈이 형성되는 것이 최소화될 수 있고, 이를 통해 공기의 투과 및 수분이 침투되는 것이 방지될 수 있으며 더욱 우수한 접착 상태를 유지하는 한편, 보온성과 탄성복원력이 우수한 유리섬유로 이루어진 경량의 상기 베이스층(10)과 미도시된 제 1 공기실을 가지는 상기 고무발포층(30)으로 인해 단열효과를 종래보다 현저히 향상시킬 수 있는 것임은 물론, 상기 유리섬유 교직물(21)은 0.05mm 내지 0.15mm 범위내의 두께(바람직하게는 0.1mm)를 가지도록 제작하고, 상기 제 2 열반사층(22)은 0.030mm 내지 0.040mm 범위내의 두께(바람직하게는 0.035mm)를 가지도록 제작하여 박형화가 가능하였고, 특히 상기 베이스층(10)의 보온성 및 탄성복원력으로부터 공간 활용이 용이하다는 장점은 물론, 상기 고무발포층(30)이 화학적 반응에 의한 부식이 억제되므로, 단열재의 단열 성능 저하는 물론 변형을 방지할 수 있게 되면서 단열재의 반영구적 사용이 가능하게 되는 것이었다.1 to 5, a high-performance semi-inflammable insulation material according to an embodiment of the present invention includes a coating layer 20 formed by thermally fusing a glass fiber cloth 21 and a second thermal reflective layer 22, Or the first heat reflecting layer 40 is thermally fused to the upper and lower surfaces of the base layer 10 made of glass fiber and the rubber foam layer 30 It is possible to minimize the formation of gaps in the heat-sealed portions as the coating layer 20 is thermally fused to one surface of the rubber foam layer 30, And a lightweight base layer 10 made of a glass fiber having excellent heat retention and elastic restoring force, and a rubber layer (not shown) having a first air chamber Because of the layer 30, (Preferably 0.1 mm) within the range of 0.05 mm to 0.15 mm, and the second thermal reflective layer 22 is formed to have a thickness of 0.030 mm to 0.15 mm The thickness of the rubber foam layer 30 (preferably 0.035 mm) can be made thinner than the thickness of the rubber foam layer 30 (0.035 mm), and in particular, it is advantageous in terms of space utilization from the warmth and elastic restoring force of the base layer 10, ), The corrosion caused by the chemical reaction is suppressed, so that the heat insulating performance of the heat insulating material is deteriorated as well as the deformation can be prevented, so that the semi-permanent use of the heat insulating material becomes possible.

이는 또한, 상기 베이스층(10)과 상기 고무발포층(30)의 우수한 방수 및 차수효과로 인하여 방습 및 난연의 효과면에 있어서도 종래의 폴리에틸렌 발포체로부터 기대할 수 없었던 향상된 효과를 확인할 수 있었으며, 특히 상기 고무발포층(30)에 열융착되는 상기 피막층(20)의 유리섬유 교직물(21)에 의해 1차 보온 및 열교 차단효과를 기대할 수 있는 것이었다.This is also because the excellent waterproofing and water-absorbing effect of the base layer 10 and the rubber foam layer 30 can improve the moisture resistance and flame retardancy of the conventional polyethylene foam, The glass fiber fabric 21 of the coating layer 20 which is thermally fused to the rubber foam layer 30 can be expected to have a primary effect of keeping the thermal insulation and breaking the heat bridge.

한편, 첨부된 도 6은 본 발명의 다른실시예로, 이는 단열재의 최하단에 위치하는 피막층(20)의 바깥쪽 타면에 OPP필름 또는 PET필름으로서 방습필름층(50)을 접착 구성하도록 한 것이다.FIG. 6 is another embodiment of the present invention in which a moisture-proof film layer 50 is bonded as an OPP film or a PET film to the other surface of the coating layer 20 located at the lowermost end of the heat insulating material.

즉, 본 발명의 다른실시예에서는 단열재의 시공시 실내측에 배치되면서 습기 유입을 차단하도록 OPP필름 또는 PET필름으로 이루어지는 방습필름층(50)을 상기 피막층(20)의 바깥쪽 타면에 열융착시키도록 구성한 것이다.That is, in another embodiment of the present invention, a moisture-impermeable film layer 50 made of an OPP film or a PET film is thermally fused to the outside surface of the coating layer 20 so as to block the inflow of moisture while being placed on the inside of the room .

한편, 첨부된 도 7은 본 발명의 또 다른 실시예로, 이는 단열재의 최하단에 위치하는 상기 피막층(20)의 바깥쪽 타면에 이형지(60)를 접착 구성하도록 한 것이다.FIG. 7 is another embodiment of the present invention, in which the release paper 60 is adhered to the outer surface of the coating layer 20 located at the lowermost end of the heat insulating material.

즉, 본 발명의 또 다른실시예에서는 단열재의 시공시 실내측에 배치되는 이형지(60)를 상기 피막층(20)의 바깥쪽 타면에 열융착시키도록 구성한 것이다.That is, in another embodiment of the present invention, the release paper 60 disposed on the indoor side at the time of applying the heat insulating material is thermally fused to the other surface of the coating layer 20.

여기서, 상기 이형지(60)는 접착제에 의해 기존의 건축물의 내벽에 접착됨으로써, 상기 단열재가 손쉽게 부착될 수 있도록 한 것이다.Here, the release paper 60 is adhered to the inner wall of the existing building by an adhesive so that the heat insulation material can be easily attached.

한편, 첨부된 도 8 및 도 9는 본 발명의 또 다른실시예로서, 이는 경량의 베이스층(10) 상,하면에 각각 알루미늄 피막의 제 1 외피층(11)을 일체로 부착 구성하여둔 상태에서, 상기 제 1 외피층(11)에 각각 타공 난연폼으로 이루어진 고무발포층(30')을 열융착시키는 한편, 상기 고무발포층(30')에 피막층(20)을 열융착시키도록 한 것이다.8 and 9 show another embodiment of the present invention, in which a first outer skin layer 11 of an aluminum coating is integrally attached to the lower surface of a lightweight base layer 10, A rubber foam layer 30 'made of a flame retardant foam is thermally fused to the first outer skin layer 11 and a coat layer 20 is thermally fused to the rubber foam layer 30'.

이때, 상기 제 1 외피층(11)과 상기 고무발포층(20')은 폴리에틸렌 계열의 접착필름(70)으로 접착하여 열융착시키는 한편, 상기 피막층(20)에 포함되는 유리섬유 교직물(21)의 상면인 바깥쪽 타면에는 제 2 열반사층(22)이 열융착되지만, 상기 유리섬유 교직물(21)의 하면인 안쪽 일면에는 제 1 열반사층(40)이 선택적으로 열융착될 수 있으며, 상기 유리섬유 교직물(21)의 바깥쪽 타면과 안쪽 일면에 각각 제 2 열반사층(22)과 제 1 열반사층(40)이 열융착시, 상기 제 1,2 열반사층(40)(22)은 제 1 방향의 위사(21a) 및 상기 제 2 방향의 경사(21b)가 서로 교직되어 형성되는 상기 유리섬유 교직물(21)의 제 2 공기실들을 통해 서로 밀착되면서 내면 결합이 이루어지도록 구성하여둔 것이다.At this time, the first outer skin layer 11 and the rubber foam layer 20 'are adhered and thermally fused with a polyethylene-based adhesive film 70, and the glass fiber cloth material 21 included in the coating layer 20 The first thermal reflective layer 40 may be selectively thermally fused to the inner surface of the lower surface of the glass fiber fabric 21 and the second thermal reflective layer 22 may be thermally fused to the other outer surface of the glass fiber fabric 21, When the second heat reflecting layer 22 and the first heat reflecting layer 40 are thermally fused to the outer surface and the inner surface of the outer surface of the fabric 21, the first and second heat reflecting layers 40 and 22 are arranged in the first direction The weft yarn 21a of the first direction and the warp yarns 21b of the second direction are in contact with each other through the second air chambers of the glass fiber fabric 21 formed by being woven together.

그리고, 상기 고무발포층(30')의 안쪽 일면에는 알루미늄 피막인 제 3 열반사층(80)이 선택적으로 부착될 수 있도록 하였으며, 상기 제 3 열반사층(80)은 그 하부에 접착 가공될 중간부재인 상기 베이스층(10)의 제 1 외피층(11)으로 대체될 수 있도록 구성하여둔 것이다.A third thermal reflective layer 80 is formed on the inner surface of the rubber foam layer 30 'as an aluminum film. The third thermal reflective layer 80 has an intermediate member The first outer covering layer 11 of the base layer 10 can be replaced.

다시말해, 상기 고무발포층(30')의 바깥쪽 타면은 상기 피막층(20)의 안쪽 일면에 형성되는 제 1 열반사층(40)에 의해 밀폐되면서, 상기 고무발포층(30')의 안쪽 일면에서는 제 1 공기실이 개방되지만, 그 개방된 상기 제 1 공기실은 상기 베이스층(10)의 상,하면에 각각 일체로 형성되는 제 1 외피층(11)에 의해 효과적으로 폐쇄될 수 있게 되면서, 상기 제 3 열반사층(80)은 그 적용이 선택적으로 이루어질 수 있는 것이다.In other words, the outer surface of the rubber foam layer 30 'is sealed by the first heat reflective layer 40 formed on the inner surface of the coating layer 20, and the inner surface of the rubber foam layer 30' The first air chamber is opened, but the opened first air chamber can be effectively closed by the first outer shell layer 11 integrally formed on the upper and lower surfaces of the base layer 10, The three-layer reflective layer 80 can be selectively applied.

이하, 본 발명의 실시예들인 첨부된 도 1 내지 도 7에서와 동일부분에 대하여는 동일부호로 표시하여 그 중복되는 설명은 생략하였다.Hereinafter, the same parts as those of the embodiments of the present invention, which are the same as those in FIGS. 1 to 7, are denoted by the same reference numerals, and redundant explanations thereof are omitted.

이상에서 본 발명의 고기능성 준불연 단열재 및 그 제조방법에 대한 기술사상을 첨부도면과 함께 서술하였지만, 이는 본 발명의 가장 바람직한 실시예를 예시적으로 설명한 것이지 본 발명을 한정하는 것은 아니다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments.

따라서, 본 발명은 상술한 특정의 실시예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변형 실시가 가능한 것은 물론이고, 그와같은 변경은 청구범위 기재의 범위내에 있게 된다.Therefore, it is intended that the present invention not be limited to the particular embodiment described and that it will be apparent to those skilled in the art that various modifications and variations can be made therein without departing from the spirit and scope of the invention as defined in the appended claims. And such changes are, of course, within the scope of the claims.

10; 베이스층 11; 제 1 외피층
20; 피막층 21; 글라스 화이버층
21a; 위사 21b; 경사
22; 제 2 열반사층 30,30'; 고무발포층
40; 제 1 열반사층 50; 방습필름층
60; 이형지 70; 접착필름
80; 제 3 열반사층 A1; 유광면
A2; 무광면
10; A base layer 11; The first outer layer
20; Coating layer 21; Glass fiber layer
21a; Weft yarn 21b; slope
22; A second thermal reflective layer 30, 30 '; Rubber foam layer
40; A first thermal reflective layer 50; Moisture-proof film layer
60; Release paper 70; Adhesive film
80; A third thermal reflective layer A1; Bright side
A2; Matte surface

Claims (18)

보온성과 탄성복원력을 가지는 유리섬유로 이루어지는 베이스층;
단열효과를 높이는 보온 재료로서, 상기 베이스층의 상,하면에 각각 적층 구성되며, 벌집 구조의 제 1 공기실을 형성하고 있고, 화학적 반응에 의한 부식 훼손이 방지되도록 고무발포 보온재로 이루어지는 고무발포층; 및,
준불연재로서 제 2 공기실을 형성하고 있으며, 상기 베이스층과 상기 고무발포층 사이 또는 상기 고무발포층의 바깥쪽 타면에 부착되는 유리섬유(glass fiber)의 피막층; 을 포함하여 구성하는 것을 특징으로 하는 고기능성 준불연 단열재.
A base layer made of glass fiber having heat retention and elastic restoring force;
A rubber foam layer made of a rubber foam insulating material so as to prevent corrosion damage caused by a chemical reaction; ; And
A coating layer of glass fiber which forms a second air chamber as a quasi-nonflammable material and adheres to the other surface of the rubber foam layer or between the base layer and the rubber foam layer; Characterized in that the high-performance semi-fireproof insulating material comprises a high-performance semi-fireproof material.
상,하면에 각각 알루미늄 피막의 제 1 외피층이 일체로 부착되고, 보온성과 탄성복원력을 가지는 유리섬유로 이루어지는 경량의 베이스층;
단열효과를 높이는 보온 재료로서, 상기 베이스층의 제 1 외피층에 각각 부착되어 적층되는 상하 한 쌍의 구조물이며, 벌집 구조의 제 1 공기실이 형성되어 있으면서 화학적 반응에 의한 부식 훼손이 방지되도록 타공 난연폼으로 이루어지는 고무발포층; 및,
준불연재로서 복수의 제 2 공기실이 형성되며, 상기 고무발포층의 바깥쪽 타면에 부착되어 적층되는 상하 한 쌍의 구조물인 유리섬유(glass fiber)의 피막층; 을 포함하여 구성하고,
상기 제 1 외피층과 상기 고무발포층은 폴리에틸렌 계열의 접착필름으로 접착되면서 열융착으로 적층 고정하는 것을 특징으로 하는 고기능성 준불연 단열재.
A lightweight base layer formed integrally with the first outer skin layer of the aluminum film on the upper and lower surfaces thereof and made of glass fiber having heat retention and elastic restoring force;
A heat insulating material for enhancing a heat insulating effect, comprising: a pair of upper and lower structures each of which is adhered to and laminated on a first outer skin layer of the base layer, wherein a first air chamber of a honeycomb structure is formed, A foamed rubber foam layer; And
A coating layer of a glass fiber which is a pair of upper and lower pairs of structures formed by stacking a plurality of second air chambers as quasi-nonflammable materials and attached to the outer surface of the rubber foam layer; And,
Wherein the first outer skin layer and the rubber foam layer are laminated and fixed by thermal fusion bonding while being bonded with a polyethylene-based adhesive film.
제 2 항에 있어서,
상기 고무발포층의 안쪽 일면에는 상기 접착필름에 접착되면서 열융착되는 제 3 열반사층; 을 형성하는 것을 특징으로 하는 고기능성 준불연 단열재.
3. The method of claim 2,
A third heat reflecting layer on the inner surface of the rubber foam layer, the third heat reflecting layer being adhered to the adhesive film while being adhered thereto; Is formed.
제 1 항에 있어서,
상기 베이스층과 상기 고무발포층 사이에는 상기 피막층을 대신하여, 상기 제 1 공기실을 폐쇄시키면서 외부 열을 반사시켜 차단하는 제 1 열반사층; 을 부착하여 구성하는 것을 특징으로 하는 고기능성 준불연 단열재.
The method according to claim 1,
A first heat reflecting layer disposed between the base layer and the rubber foam layer for blocking external heat while blocking the first air chamber instead of the coating layer; To the high-performance semi-inflammable insulation material.
제 4 항에 있어서,
상기 피막층은 준불연재인 유리섬유 교직물; 및, 상기 유리섬유 교직물의 상면 또는 하면에 부착되는 준불연재로서 외부 열을 반사시켜 차단하는 제 2 열반사층; 을 포함하며,
상기 유리섬유 교직물은 나선형으로 연속하여 감기는 제 1 방향의 위사와 제 2 방향의 경사를 교직 구조로 직조하여 내부에 상기 제 2 공기실을 형성하는 것을 특징으로 하는 고기능성 준불연 단열재.
5. The method of claim 4,
Wherein the coating layer is a quasi-nonflammable material; And a second thermally reflecting layer for reflecting and shielding external heat as a semi-fire-resistant material adhered to an upper surface or a lower surface of the glass fiber fabric; / RTI >
Wherein the glass fiber fabric is formed by weaving a weft yarn in a first direction and an inclination in a second direction in a spiral shape so that the second air yarn is formed therein.
삭제delete 제 5 항에 있어서,
상기 유리섬유 교직물에는 강성 보강을 위한 돌가루가 첨가되도록 구성하는 것을 특징으로 하는 고기능성 준불연 단열재.
6. The method of claim 5,
Characterized in that stones for stiffening reinforcement are added to the glass fiber fabric.
제 5 항에 있어서,
상기 제 1,2 열반사층은 알루미늄 호일인 것을 특징으로 하는 고기능성 준불연 단열재.
6. The method of claim 5,
Wherein the first and second thermal reflective layers are aluminum foils.
제 8 항에 있어서,
상기 알루미늄 호일은 알루미늄 호일을 압연하는 워크롤의 거칠기 조정을 통하여 그 광택도가 서로 다르게 설정되도록 하여 일면은 유광면으로 하고 타면은 무광면으로 구성하는 것을 특징으로 하는 고기능성 준불연 단열재.
9. The method of claim 8,
Wherein the aluminum foil is made of a glossy surface on one side and a non-glossy side on the other side so that the gloss of the aluminum foil is adjusted differently by adjusting the roughness of the work roll rolling the aluminum foil.
제 5 항에 있어서,
상기 단열재에 대한 박형화를 위해, 상기 유리섬유 교직물은 0.05mm 내지 0.15mm 범위내의 두께를 가지고, 상기 제 1,2 열반사층은 0.030mm 내지 0.040mm 범위내 두께를 가지도록 구성하는 것을 특징으로 하는 고기능성 준불연 단열재.
6. The method of claim 5,
Characterized in that the glass fiber fabric has a thickness within a range of 0.05 mm to 0.15 mm and the first and second thermal reflective layers have a thickness within a range of 0.030 mm to 0.040 mm. Functional semi-inflammable insulation.
제 1 항 또는 제 2 항에 있어서,
상기 고무발포층의 바깥쪽 타면에 부착되는 상기 유리섬유(glass fiber) 피막층 외측에는 OPP필름 또는 PET필름으로서 단열재의 시공시 실내측에 배치되어 습기 유입을 차단시키는 방습필름층을 접착 구성하는 것을 특징으로 하는 고기능성 준불연 단열재.
3. The method according to claim 1 or 2,
And a moisture-proof film layer disposed on the outside of the glass fiber coating layer attached to the other surface of the rubber foam layer and disposed on the inside of the room as an OPP film or a PET film when the heat insulation material is applied, High-performance semi-fireproof insulation material.
제 1 항 또는 제 2 항에 있어서,
상기 고무발포층의 바깥쪽 타면에 부착되는 상기 유리섬유(glass fiber) 피막층 외측에는 단열재의 시공시 실내측에 배치되는 이형지를 접착 구성하는 것을 특징으로 하는 고기능성 준불연 단열재.
3. The method according to claim 1 or 2,
Characterized in that a releasing paper disposed on the side of the room at the time of application of the heat insulating material is adhered to the outside of the glass fiber coating layer adhered to the outer surface of the rubber foam layer .
(a) 준불연재인 유리섬유를 제 1 방향 위사와 제 2 방향 경사의 교직 구조로 직조하여 내면에 제 2 공기실을 갖는 유리섬유 교직물을 형성한 후 상기 유리섬유 교직물의 상,하면에 각각 알루미늄 호일로 이루어지는 제 2 열반사층을 열융착하여 피막층을 형성하는 공정;
(b) 상기 (a)으로부터 형성되는 피막층 또는 외부 열을 반사시켜 차단하는 제 1 열반사층을 보온성과 탄성복원력을 가지는 유리섬유로 이루어지는 경량의 베이스층 상,하면에 각각 열융착시키는 공정;
(c) 단열효과를 높이고 화학적 반응에 의한 부식 훼손이 방지되도록 고무발포 보온재로 이루어지면서 단열효과를 높이도록 벌집 구조의 제 1 공기실을 가지는 고무발포층을 형성하고, 상기 고무발포층을 상기 (b)공정으로부터 상기 베이스층의 상,하면에 각각 융착되는 상기 피막층 또는 상기 제 1 열반사층의 일면에 열융착시키는 공정; 및,
(d) 상기 (c)공정으로부터 상기 피막층 또는 상기 제 1 열반사층의 일면에 융착되는 상기 고무발포층의 최외측으로 노출되는 바깥면에는 각각 상기 (a)공정으로부터 형성되는 상기 피막층을 열융착시키는 공정; 을 포함하여 진행하는 것을 특징으로 하는 고기능성 준불연 단열재 제조방법.
(a) A glass fiber cloth having a second air chamber is formed by weaving the quasi-nonflammable glass fiber into a weave structure in a first direction warp and a second direction warp, and then a glass fiber cloth is formed on the upper and lower surfaces of the glass fiber cloth, A step of forming a coat layer by thermally fusing a second heat reflecting layer made of foil;
(b) a step of thermally fusing a coating layer formed from (a) or a first heat reflecting layer for reflecting and shielding external heat on a lower surface of a lightweight base layer made of glass fiber having thermal insulation and elastic restoring force;
(c) forming a rubber foam layer having a first air chamber having a honeycomb structure so as to enhance the adiabatic effect and to prevent corrosion damage caused by a chemical reaction, the rubber foam layer being formed of the rubber foam layer, thermally fusing one surface of the coating layer or the first heat reflecting layer, which is fused to the upper and lower surfaces of the base layer, from the step (b); And
(d) The coating layer formed from the step (a) is thermally fused to the outermost surface of the rubber foam layer which is fused to one surface of the coating layer or the first heat reflective layer from the step (c) fair; Wherein the step of preparing the high-performance semi-inflammable insulation material comprises:
(a1) 준불연재인 유리섬유를 제 1 방향 위사와 제 2 방향 경사의 교직 구조로 직조하여 내면에 제 2 공기실을 갖는 유리섬유 교직물을 형성한 후, 상기 유리섬유 교직물의 바깥쪽 타면에 알루미늄 호일로 이루어지는 제 2 열반사층을 열융착하여 피막층을 형성하는 공정;
(b1) 보온성과 탄성복원력을 가지는 유리섬유의 상,하면에 각각 알루미늄 피막의 제 1 외피층이 일체로 부착하여 경량의 베이스층을 형성하는 공정;
(c1) 단열효과를 높이고 화학적 반응에 의한 부식 훼손이 방지되도록 타공 난연폼으로 이루어지면서 단열효과를 높이도록 벌집 구조의 제 1 공기실을 가지는 고무발포층을 형성한 후, 이를 접착필름을 이용하여 상기 (b1)공정으로부터 형성되는 상기 베이스층의 상,하면 제 1 외피층에 접착시킨 후 그 접착부위를 열융착하는 공정; 및,
(d1) 상기 (c1)공정으로부터 상기 제 1 외피층에 열융착되는 상기 고무발포층의 최외측으로 노출되는 바깥면에는 각각 상기 (a1)공정으로부터 형성되는 상기 피막층을 열융착시키는 공정; 을 포함하여 진행하는 것을 특징으로 하는 고기능성 준불연 단열재 제조방법.
(a1) Weaving a non-flammable glass fiber woven in a weft-woven structure of a first direction warp and a second direction to form a glass fiber woven fabric having a second air chamber on the inner surface thereof, A step of forming a coat layer by thermally fusing a second heat reflecting layer made of foil;
(b1) a step of forming a lightweight base layer by integrally adhering a first outer skin layer of an aluminum film on upper and lower surfaces of a glass fiber having a warming property and an elastic restoring force;
(c1) A rubber foam layer having a first air chamber of honeycomb structure is formed so as to increase the heat insulation effect and prevent corrosion damage caused by chemical reaction, A step of adhering the upper and lower surfaces of the base layer formed from the step (b1) to the first outer skin layer, followed by thermally fusing the bonded portion; And
(d1) a step of thermally fusing the coating layer formed from the step (a1) on the outermost surface of the rubber foam layer thermally fused to the first outer skin layer from the step (c1); Wherein the step of preparing the high-performance semi-inflammable insulation material comprises:
제 14 항에 있어서,
상기 (a1)공정에는, 상기 피막층의 안쪽 일면에 알루미늄 호일로 이루어지는 제 1 열반사층을 열융착시켜, 상기 제 1,2 열반사층이 상기 제 1 방향의 위사 및 상기 제 2 방향의 경사가 서로 교직되어 형성되는 상기 유리섬유 교직물의 제 2 공기실들을 통해 서로 밀착되어 내면 결합이 이루어지도록 하는 공정; 을 더 포함하는 것을 특징으로 하는 고기능성 준불연 단열재 제조방법.
15. The method of claim 14,
The step (a1) may include a step of thermally fusing a first heat reflecting layer made of aluminum foil on one inner side of the coating layer so that the weft in the first direction and the inclination in the second direction And the second air chambers of the glass fiber fabric member are formed to be in close contact with each other so that inner surface bonding is performed; Further comprising the steps of: (a) providing a base material having a high thermal conductivity;
제 14 항에 있어서,
상기 (c1)공정에는, 상기 고무발포층의 안쪽 일면에 제 3 열반사층을 일체로 형성한 후 이를 상기 접착필름에 접착시켜 열융착시키는 공정; 을 포함하는 것을 특징으로 하는 고기능성 준불연 단열재 제조방법.
15. The method of claim 14,
In the step (c1), a step of integrally forming a third heat reflecting layer on the inner surface of the rubber foam layer and bonding the same to the adhesive film to thermally fuse the same; Wherein the method comprises the steps of:
제 13 항 또는 제 14 항에 있어서,
상기 고무발포층의 최외측으로 노출되는 상기 피막층의 바깥쪽 타면에는 OPP필름 또는 PET필름으로서 단열재의 시공시 실내측에 배치되어 습기 유입을 차단시키는 방습필름층을 접착 구성하는 공정; 을 더 포함하는 것을 특징으로 하는 고기능성 준불연 단열재 제조방법.
The method according to claim 13 or 14,
A step of bonding a moisture-proofing film layer disposed on the inner side of the heat insulation material as an OPP film or PET film on the outer surface of the outer side of the coating layer exposed to the outermost side of the rubber foam layer to block moisture inflow; Further comprising the steps of: (a) providing a base material having a high thermal conductivity;
제 13 항 또는 제 14 항에 있어서,
상기 고무발포층의 최외측으로 노출되는 상기 피막층의 바깥쪽 타면에는 단열재의 시공시 실내측에 배치되는 이형지를 접착 구성하는 공정; 을 더 포함하는 것을 특징으로 하는 고기능성 준불연 단열재 제조방법.
The method according to claim 13 or 14,
A step of adhering a releasing paper disposed on the outer side of the coating layer exposed to the outermost side of the rubber foam layer on the side of the room when the heat insulating material is applied; Further comprising the steps of: (a) providing a base material having a high thermal conductivity;
KR1020170124278A 2017-09-26 2017-09-26 Non-inflammably Highly Efficient Heat Insulator and Method for Preparing the Same KR101852731B1 (en)