JPH08319216A - Solid non-aqueous powder cosmetic - Google Patents

Solid non-aqueous powder cosmetic

Info

Publication number
JPH08319216A
JPH08319216A JP14977395A JP14977395A JPH08319216A JP H08319216 A JPH08319216 A JP H08319216A JP 14977395 A JP14977395 A JP 14977395A JP 14977395 A JP14977395 A JP 14977395A JP H08319216 A JPH08319216 A JP H08319216A
Authority
JP
Japan
Prior art keywords
powder
silicone
cosmetic
sebum
solid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
JP14977395A
Other languages
Japanese (ja)
Inventor
Tetsuo Tsunoda
哲夫 角田
Tsuneo Suhara
常夫 須原
Fukuji Suzuki
福二 鈴木
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shiseido Co Ltd
Original Assignee
Shiseido Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shiseido Co Ltd filed Critical Shiseido Co Ltd
Priority to JP14977395A priority Critical patent/JPH08319216A/en
Publication of JPH08319216A publication Critical patent/JPH08319216A/en
Withdrawn legal-status Critical Current

Abstract

PURPOSE: To obtain the subject cosmetic prevented from developing spotted detachment and unfavorable appearance with time due to sebum secretion, having use feeling with refreshingness and dampishness, by incorporating hydrophobic powder with a silicone-based surfactant and a specific hydrocarbon. CONSTITUTION: This cosmetic is obtained by incorporating a combination of pref. 30.0-94.0wt.% of hydrophobic powder and pref. 0.1-20.0wt.% of a silicone- based surfactant with pref. 1.0-50.0wt.% of a low-boiling isoparaffin-based hydrocarbon 210-350 deg.C in boiling point whose vaporization rate due to contact with body temp. skin and air is close to sebum developing rate. The silicone-based surfactant is a polyether-modified silicone of the formula ((y+z) is 1-2000; (a) is 1-100; (b) is 0-100; R is H, an alkyl or COCH3 ). The hydrophobic powder is prepared by hydrophobicizing e.g. polyamide resin powder, polyethylene powder, silicon powder.

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【産業上の利用分野】本発明は固型状非水系粉末化粧料
に関し、更に詳細には、化粧くずれ、特に汗等の水分に
よるトレ及び皮脂による経時のトレ・テカリ等を防止し
て初期状態を持続するとともに、さっぱりかつしっとり
とした使用感を有する固型状非水系粉末化粧料に関す
る。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a solid non-aqueous powder cosmetic, and more particularly, to an initial state by preventing makeup deterioration, in particular, a tore due to moisture such as sweat and a tore and shine due to sebum. The present invention relates to a solid non-aqueous powder cosmetic having a long-lasting effect and a refreshing and moisturizing feeling.

【0002】[0002]

【従来の技術】化粧くずれは、スポーツ時あるいは夏場
の汗等の水分によるものと、高温(20〜25度)に保
たれた現代社会の環境下で、1年中起こりえる皮脂によ
るものとに2分される。汗・涙・雨等の水分によるトレ
に関しては、疎水性粉末の使用でかなり改善されたが、
固型状粉末化粧料においては未だ満足できるものではな
い。また、皮脂の分泌による経時の化粧成分のトレや顔
面のテカリについては、ほとんど対策がとられていなか
った。
2. Description of the Related Art Deterioration of makeup is caused by moisture such as sweat during sports or in the summer, and by sebum that can occur all year round under the environment of modern society kept at high temperature (20 to 25 degrees Celsius). Two minutes. Regarding the training due to moisture such as sweat, tears, rain, etc., it was considerably improved by using hydrophobic powder,
It is not yet satisfactory in solid powder cosmetics. In addition, almost no countermeasures have been taken for the training of cosmetic ingredients and the shininess of the face due to the secretion of sebum.

【0003】水分によるトレについては、固形状粉末化
粧料では配合油分量が少ないため、疎水性粉末の肌への
密着性を向上させることが重要である。一方、皮脂の分
泌による経時のトレや顔面のテカリは、化粧膜に存在す
る総油分量、すなわち、塗布した化粧料中の油分と分泌
皮脂量の総和が化粧料に含有する粉末の一定吸油量を越
えた時に起こるものと推定される。この現象は、皮脂の
分泌の多い鼻・額の部位で顕著である。従って、皮脂に
よる化粧くずれは化粧料の潜在的吸油量と油分の量に影
響を受けやすく、特にワックス、ワセリンおよびロウ等
の固形油分あるいは半固形油分が配合されている化粧料
や乳化系化粧料では顔面のテカリが起こりやすい。揮発
性油分を使用すると塗布後に油分が揮発し潜在的吸油量
が増加することでき、皮脂によるトレを防止できるもの
と考えられるが、揮発速度が速すぎると塗布後の粉っぽ
さや、つっぱり等の使用感の問題に加え、化粧料製造工
程中や製品容器への負担も大きく好ましくなかった。
With regard to trays due to moisture, it is important to improve the adhesion of the hydrophobic powder to the skin because the solid powder cosmetic has a small amount of oil content. On the other hand, secular secretion due to the secretion of sebum and facial shine are the total amount of oil present in the cosmetic film, that is, the sum of the amount of oil in the applied cosmetic and the amount of secreted sebum is the constant oil absorption of the powder contained in the cosmetic. It is presumed that this will occur when the temperature exceeds. This phenomenon is remarkable in the nose and forehead where sebum is secreted. Therefore, makeup deterioration due to sebum is easily affected by the potential oil absorption amount and the oil content of the cosmetic, and in particular, a cosmetic or an emulsified cosmetic in which solid oil or semi-solid oil such as wax, vaseline and wax is blended. Then face shininess is likely to occur. If volatile oil is used, the oil will volatilize after application and the potential oil absorption can be increased, and it is thought that it is possible to prevent training due to sebum, but if the volatilization rate is too fast, it will be powdery or taut after application. In addition to the problem of the feeling of use, the burden on the cosmetics manufacturing process and the product container was large, which was not preferable.

【0004】[0004]

【発明が解決しようとする課題】近年、上述したような
問題を改善し、皮脂によるトレや顔面のテカリを防止す
るために、油分の揮発速度と皮脂発生速度が近い、より
分子量の大きい特定の徐放性シリコ−ンを配合する技術
が開発されている(特開平4−117315号公報、特
開平4−117316号公報、特開平4−187611
号公報、特開平4−187612号公報、特開平4−3
05510号公報、特開平4−305511号公報)。
しかし、疎水性粉末を多配合する固型状非水系粉末化粧
料においては、より分子量の大きい特定の徐放性シリコ
−ンを配合することにより粉末の伸びが重くなり使用感
触が悪化してしまうという欠点があった。このため、固
型状非水系粉末化粧料を用いた場合の化粧くずれの防止
方法として満足できる技術は未だ見出されていないのが
実情であった。
In recent years, in order to improve the above-mentioned problems, and prevent the seizure due to sebum and the shininess of the face, the specific molecular weight and the sebum generation rate are close to each other Techniques for blending sustained-release silicones have been developed (JP-A-4-117315, JP-A-4-117316, and JP-A-4-187611).
JP-A-4-187612, JP-A-4-3
05510, JP-A-4-305511).
However, in solid non-aqueous powder cosmetics containing a large amount of hydrophobic powder, the addition of a specific sustained-release silicone having a larger molecular weight causes the powder to be spread more and the feeling of use to deteriorate. There was a drawback. For this reason, it has been the actual situation that no satisfactory technique has been found as a method for preventing makeup deterioration when a solid non-aqueous powder cosmetic is used.

【0005】本発明は上記実情に鑑みなされたものであ
り、その目的は化粧くずれ特に汗等水分によるトレ及び
皮脂による経時のトレ・顔面のテカリ等を防止して初期
状態を持続するとともに、さっぱりかつしっとりとした
使用感を有する固型状非水系粉末化粧料を提供すること
にある。
The present invention has been made in view of the above circumstances, and an object thereof is to maintain the initial state by preventing makeup deterioration, especially due to moisture such as sweat and aging due to sebum, and facial shine, and to maintain the initial state. Another object of the present invention is to provide a solid non-aqueous powder cosmetic having a moisturizing feel.

【0006】[0006]

【課題を解決するための手段】本発明者らは、上記従来
の問題点を解決するために鋭意研究を行った結果、疎水
性粉末にシリコーン系界面活性剤を加えることにより疎
水性粉末の肌への密着性が向上し、汗等の水分によるト
レが防止できると同時に、肌上に水分が加わるとシリコ
ーン系界面活性剤の粘度が上昇し、肌への密着性がさら
に増強されること、さらには肌の温度や空気との接触に
よる揮発速度が皮脂発生速度に近い特定の低沸点イソパ
ラフィン系炭化水素を加えることにより皮脂の分泌によ
る経時のトレ・テカリを防止し、さっぱりかつしっとり
した使用感を有することを見出し、本発明を完成するに
至った。
Means for Solving the Problems As a result of intensive studies to solve the above-mentioned conventional problems, the present inventors have found that by adding a silicone-based surfactant to the hydrophobic powder, the skin of the hydrophobic powder can be improved. The adhesion to the skin is improved, and the training due to moisture such as sweat can be prevented, and at the same time, when the water is added to the skin, the viscosity of the silicone-based surfactant is increased, and the adhesion to the skin is further enhanced. Furthermore, by adding a specific low-boiling point isoparaffinic hydrocarbon whose volatilization rate due to skin temperature and contact with air is close to the sebum generation rate, the secular secretion of sebum is prevented from over-exercising, resulting in a refreshing and moisturizing feeling. The present invention has been completed and the present invention has been completed.

【0007】すなわち本発明は、低沸点イソパラフィン
系炭化水素、シリコーン系界面活性剤および疎水性粉末
を配合してなる固型状非水系粉末化粧料である。
That is, the present invention is a solid non-aqueous powder cosmetic composition containing a low boiling point isoparaffin hydrocarbon, a silicone surfactant and a hydrophobic powder.

【0008】本発明に用いられる低沸点イソパラフィン
系炭化水素は、通常化粧品に用いられるものであるが、
皮膚残存性(揮発速度)および皮膚刺激性により沸点
(b.p.)が210〜350℃のものが望ましい。例えば、
アイソパー(登録商標)M (b.p.204 〜260 ℃)、化粧
品グレード585LCL(225〜255 ℃)(エクソン
社)、アイソゾール(登録商標)400(204〜260 ℃)
(日本石油)、パールリーム(登録商標)6(320〜335
℃)、パールリームEX(300〜315 ℃)(日本油脂)、
テトライソブタン90(210〜250 ℃)(バイエル社)、
パーメチル(登録商標)101A(210〜250 ℃)、10
2A(275℃)(プレスパース社)等である。
The low-boiling isoparaffinic hydrocarbon used in the present invention is generally used in cosmetics,
Boiling point due to skin persistence (volatilization rate) and skin irritation
It is desirable that the (bp) is 210 to 350 ° C. For example,
Isopar (registered trademark) M (bp204 to 260 ° C), cosmetic grade 585LCL (225 to 255 ° C) (Exxon), Isozole (registered trademark) 400 (204 to 260 ° C)
(Nippon Petroleum), Pearlream (registered trademark) 6 (320 to 335)
℃), Pearlream EX (300-315 ℃) (NOF Corporation),
Tetraisobutane 90 (210-250 ° C) (Bayer),
Permethyl (registered trademark) 101A (210 to 250 ° C.), 10
2A (275 ° C.) (Press Perth Co.).

【0009】低沸点イソパラフィン系炭化水素の配合量
は1.0〜50.0重量%であり、好ましくは10.0
〜30.0重量%である。50.0重量%を越える配合
量ではケーキングを生じるので好ましくなく、一方、
1.0重量%未満の配合量では揮発性油分が少ないため
吸油量が不十分であり、テカリを生じてしまう。
The amount of low-boiling isoparaffin hydrocarbon is 1.0 to 50.0% by weight, preferably 10.0.
~ 30.0% by weight. If the compounding amount exceeds 50.0% by weight, caking occurs, which is not preferable.
If the blending amount is less than 1.0% by weight, the volatile oil content is small and the oil absorption is insufficient, resulting in shininess.

【0010】本発明に用いられるシリコーン系界面活性
剤としては、次の一般式(1)で示されるポリエーテル
変性シリコーンが好ましい。
The silicone-based surfactant used in the present invention is preferably a polyether-modified silicone represented by the following general formula (1).

【0011】[0011]

【化1】 Embedded image

【0012】(式中、y+z=1〜20000、a=1
〜100、b=0〜100、Rは水素原子、炭素原子数
が1〜20のアルキル基または式−COCH3 で示され
る基を示す。)
(In the formula, y + z = 1 to 20000, a = 1
˜100, b = 0 to 100, R represents a hydrogen atom, an alkyl group having 1 to 20 carbon atoms, or a group represented by the formula —COCH 3 . )

【0013】シリコーン系界面活性剤の配合量は0.1
〜20.0重量%であり、好ましくは0.1〜10.0
重量%である。0.1重量%未満では疎水性粉末の肌へ
の密着性が悪く、トレが多くなってしまう。配合量が多
いほどトレは少なくなるが、20.0重量%を超えると
皮膚への刺激が大きくなって安全性上問題がある。
The amount of the silicone-based surfactant compounded is 0.1.
% To 20.0% by weight, preferably 0.1 to 10.0
% By weight. If it is less than 0.1% by weight, the adhesion of the hydrophobic powder to the skin will be poor, and the training will increase. If the blending amount is large, the training amount is small, but if it exceeds 20.0% by weight, irritation to the skin becomes large and there is a safety problem.

【0014】本発明に用いられる疎水性粉末は、粉末自
体が疎水性のもののみならず、親水性粉末等であっても
粉末表面を疎水化処理した疎水化処理粉末も含む。
The hydrophobic powder used in the present invention includes not only hydrophobic powder itself, but also hydrophobic powder such as hydrophilic powder whose surface is hydrophobized.

【0015】疎水性の粉末としては、具体的には、ポリ
アミド樹脂粉末(ナイロン粉末)、ポリエチレン粉末、
ポリメタクリル酸メチル粉末、ポリスチレン粉末、スチ
レンとアクリル酸の共重合体樹脂粉末、ベンゾグアナミ
ン樹脂粉末、ポリ四フッ化エチレン粉末、セルロ−ス粉
末などの有機粉末や、トリメチルシルセスキオキサン粉
末などのシリコン粉末等が例示される。
Specific examples of the hydrophobic powder include polyamide resin powder (nylon powder), polyethylene powder,
Organic powder such as polymethylmethacrylate powder, polystyrene powder, copolymer resin powder of styrene and acrylic acid, benzoguanamine resin powder, polytetrafluoroethylene powder, cellulose powder, and silicon such as trimethylsilsesquioxane powder. A powder etc. are illustrated.

【0016】疎水化処理粉末の粉末成分としては、例え
ばタルク、カオリン、雲母、絹雲母(セリサイト)、白
雲母、金雲母、合成雲母、紅雲母、黒雲母、リチア雲
母、パーミキュライト、炭酸マグネシウム、炭酸カルシ
ウム、ケイ酸アルミニウム、ケイ酸バリウム、ケイ酸カ
ルシウム、ケイ酸マグネシウム、ケイ酸ストロンチウ
ム、タングステン酸金属塩、マグネシウム、シリカ、ゼ
オライト、硫酸バリウム、焼成硫酸カルシウム(焼セッ
コウ)、リン酸カルシウム、フッ素アパタイト、ヒドロ
キシアパタイト、セラミックパウダー、金属石鹸(ミリ
スチン酸亜鉛、パルミチン酸カルシウム、ステアリン酸
アルミニウムなど)、窒化ホウ素等の無機粉末;二酸化
チタン、酸化亜鉛等の無機白色顔料;酸化鉄(ベンガ
ラ)、チタン酸鉄等の無機赤色系顔料;γ−酸化鉄等の
無機褐色系顔料;黄酸化鉄、黄土等の無機黄色系顔料;
黒酸化鉄、カーボンブラック、低次酸化チタン等の無機
黒色系顔料;マンゴバイオレット、バルトバイオレット
等の無機紫色系顔料;酸化クロム、水酸化クロム、チタ
ン酸コバルト等の無機緑色系顔料;群青、紺青等の無機
青色系顔料;酸化チタンコーテッドマイカ、酸化チタン
コーテッドオキシ塩化ビスマス、酸化チタンコーテッド
タルク、着色酸化チタンコーテッドマイカ、オキシ塩化
ビスマス、魚鱗箔等のパール顔料;アルミニウムパウダ
ー、カッパーパウダー等の金属粉末顔料等;赤色201
号、赤色202号、赤色204号、赤色205号、赤色
220号、赤色226号、赤色228号、赤色405
号、橙色203号、橙色204号、黄色205号、黄色
401号または青色404号等の有機顔料;赤色3号、
赤色104号、赤色106号、赤色227号、赤色23
0号、赤色401号、赤色505号、橙色205号、黄
色4号、黄色5号、黄色202号、黄色203号、緑色
3号または青色1号のジルコニウム、バリウムまたはア
ルミニウムレーキ等の有機顔料;クロロフィル、β−カ
ロチン等の天然色素等が挙げられる。本発明ではこれら
粉末成分を疎水化処理したものが用いられる。
Examples of the powder component of the hydrophobized powder include talc, kaolin, mica, sericite, muscovite, phlogopite, synthetic mica, phlogopite, biotite, lithia mica, permiculite, magnesium carbonate, Calcium carbonate, aluminum silicate, barium silicate, calcium silicate, magnesium silicate, strontium silicate, tungstate metal salt, magnesium, silica, zeolite, barium sulfate, calcined calcium sulfate (calculated gypsum), calcium phosphate, fluoroapatite, Hydroxyapatite, ceramic powder, metallic soap (zinc myristate, calcium palmitate, aluminum stearate, etc.), inorganic powder such as boron nitride; inorganic white pigment such as titanium dioxide, zinc oxide; iron oxide (red iron oxide), iron titanate Nothing Red pigment; .gamma. inorganic brown pigments such as iron oxide; yellow iron oxide, inorganic yellow pigments loess and the like;
Inorganic black pigments such as black iron oxide, carbon black and low-order titanium oxide; inorganic purple pigments such as mango violet and balt violet; inorganic green pigments such as chromium oxide, chromium hydroxide and cobalt titanate; ultramarine blue and navy blue. Inorganic blue pigments such as; Titanium oxide coated mica, titanium oxide coated bismuth oxychloride, titanium oxide coated talc, colored titanium oxide coated mica, bismuth oxychloride, pearl pigments such as scale foil; metal powders such as aluminum powder and copper powder Pigment, etc .; red 201
No. 202, Red No. 202, Red No. 204, Red No. 205, Red No. 220, Red No. 226, Red No. 228, Red No. 405
No. 203, Orange No. 203, Orange No. 204, Yellow No. 205, Yellow No. 401 or Blue No. 404 and other organic pigments; Red No. 3,
Red No. 104, Red No. 106, Red No. 227, Red No. 23
Organic pigments such as No. 0, Red No. 401, Red No. 505, Orange No. 205, Yellow No. 4, Yellow No. 5, Yellow No. 202, Yellow No. 203, Green No. 3 or Blue No. 1 such as zirconium, barium or aluminum lake; Examples include natural pigments such as chlorophyll and β-carotene. In the present invention, those obtained by hydrophobizing these powder components are used.

【0017】疎水化処理方法としては、撥水性を付与で
きる方法であればいかなるものでもよく、その方法は問
わないが、例えば気相法、液相法、オートクレーブ法、
メカノケミカル法等、通常の表面処理方法を用いること
ができる。
The hydrophobic treatment method may be any method as long as it can impart water repellency, and the method is not limited, and examples thereof include a gas phase method, a liquid phase method, an autoclave method,
A usual surface treatment method such as a mechanochemical method can be used.

【0018】例えば疎水化処理剤を原料粉末に添加して
処理を行う場合、適当な溶媒(ジクロルメタン、クロロ
ホルム、ヘキサン、エタノール、キシレン、揮発性シリ
コーン等)に希釈して添加してもよく、あるいは直接添
加してもよい。粉末と処理剤の混合攪拌には、ボールミ
ル、ホジャーサイトボールミル、振動ボールミル、アト
ライター、ポットミル、ロッドミル、パンミル、ホモミ
キサー、ホモディスパー、ヘンシェルミキサー、ナウタ
ーミキサー等も使用することができる。この他にも、粉
末表面の活性を利用し、気相反応により100℃以下の
低温で環状オルガノシロキサンを粉体表面上で重合させ
る方法(特公平1−54380号)や、前記方法の後に
表面のシリコーンポリマーのSi−H部分にグリセロー
ルモノアリルエーテル等のペンダント基を付加させる方
法(特公平1−54381号)等も用いることができ
る。
For example, when a hydrophobizing agent is added to the raw material powder for treatment, it may be added after diluting it with an appropriate solvent (dichloromethane, chloroform, hexane, ethanol, xylene, volatile silicone, etc.), or You may add directly. A ball mill, a hogersite ball mill, a vibrating ball mill, an attritor, a pot mill, a rod mill, a pan mill, a homomixer, a homodisper, a Henschel mixer, a Nauta mixer and the like can also be used for mixing and stirring the powder and the treating agent. In addition to this, a method of polymerizing a cyclic organosiloxane on the surface of a powder at a low temperature of 100 ° C. or lower by a gas phase reaction utilizing the activity of the surface of the powder (Japanese Patent Publication No. 1-54380), or a surface after the above method The method of adding a pendant group such as glycerol monoallyl ether to the Si-H portion of the silicone polymer (Japanese Patent Publication No. 1-54381) can be used.

【0019】疎水化処理剤としては、特に限定されるも
のではないが、脂肪酸デキストリン処理粉末、トリメチ
ルシロキシ珪酸処理粉末、フッ素変性トリメチルシロキ
シ珪酸処理粉末、メチルフェニルシロキシ珪酸処理粉
末、フッ素変性メチルフェニルシロキシ珪酸処理粉末、
ジメチルポリシロキサン、ジフェニルポリシロキサン、
メチルフェニルポリシロキサン等の低粘度〜高粘度油状
ポリシロキサン処理粉末、ガム状ポリシロキサン処理粉
末、メチルハイドロジェンポリシロキサン処理粉末、フ
ッ素変性メチルハイドロジェンポリシロキサン処理粉
末、メチルトリクロルシラン、メチルトリアルコキシシ
ラン、ヘキサメチルジシラン、ジメチルジクロルシラ
ン、ジメチルジアルコキシシラン、トリメチルクロルシ
ラン、トリメチルアルコキシシラン等の有機シリル化合
物あるいはそれらのフッ素置換体による処理粉末、エチ
ルトリクロルシラン、エチルトリアルコキシシラン、プ
ロピルトリクロルシラン、プロピルトリアルコキシシラ
ン、ヘキシルトリクロルシラン、ヘキシルトリアルコキ
シシラン、長鎖アルキルトリクロルシラン、長鎖アルキ
ルトリエトキシシラン等の有機変性シランあるいはそれ
らのフッ素置換体による処理粉末、アミノ変性ポリシロ
キサン処理粉末、フッ素変性ポリシロキサン処理粉末、
フッ化アルキルリン酸処理粉末等が挙げられる。
The hydrophobizing agent is not particularly limited, but fatty acid dextrin-treated powder, trimethylsiloxysilicic acid-treated powder, fluorine-modified trimethylsiloxysilicic acid-treated powder, methylphenylsiloxysilicic acid-treated powder, fluorine-modified methylphenylsiloxy. Silicic acid treated powder,
Dimethyl polysiloxane, diphenyl polysiloxane,
Low-viscosity to high-viscosity oily polysiloxane-treated powder such as methylphenylpolysiloxane, gum-like polysiloxane-treated powder, methylhydrogenpolysiloxane-treated powder, fluorine-modified methylhydrogenpolysiloxane-treated powder, methyltrichlorosilane, methyltrialkoxysilane , Hexamethyldisilane, dimethyldichlorosilane, dimethyldialkoxysilane, trimethylchlorosilane, trimethylalkoxysilane and other organic silyl compounds or their fluorine-substituted treatment powder, ethyltrichlorosilane, ethyltrialkoxysilane, propyltrichlorosilane, Propyltrialkoxysilane, hexyltrichlorosilane, hexyltrialkoxysilane, long-chain alkyltrichlorosilane, long-chain alkyltriethoxysilane Organic modified silane or treated powder according to their fluorine substitution products, amino-modified polysiloxane treatment powder, fluorine-modified polysiloxane treatment powder,
Fluorinated alkyl phosphoric acid treated powder and the like can be mentioned.

【0020】これら疎水性粉末は1種を用いてもよく、
あるいは2種以上を用いてもよい。また、一般の化粧品
に適用できる疎水性粉末であればよく、上記の成分に限
定されるものではない。なお、本発明において疎水性粉
末の配合量は30.0〜94.0重量%であり、好まし
くは50.0〜90.0重量%である。
One kind of these hydrophobic powders may be used,
Alternatively, two or more kinds may be used. Further, the powder is not limited to the above components as long as it is a hydrophobic powder applicable to general cosmetics. In the present invention, the blending amount of the hydrophobic powder is 30.0-94.0% by weight, preferably 50.0-90.0% by weight.

【0021】本発明の固型状粉末化粧料には前記した必
須成分の他に、油分として流動パラフィン、イソ流動パ
ラフィン、スクワラン等の炭化水素;オリーブ油、パー
ム油、ヤシ油、マカデミアナッツ油、ホホバ油等の油
脂;イソステアリルアルコール等の高級アルコール;高
級脂肪酸、ミリスチン酸イソプロピル等のエステル類;
ジメチルポリシロキサン、メチルフェニルポリシロキサ
ン、メチルハイドロジェンポリシロキサン等の鎖状ポリ
シロキサン;オクタメチルシクロテトラシロキサン、デ
カメチルシクロペンタシロキサン、ドデカメチルシクロ
ヘキサシロキサンの環状ポリシロキサン等のシリコーン
オイル;プロピレングリコール、1、3−ブチレングリ
コール、グリセリン等の多価アルコール類;グルコー
ス、ガラクトース、フラクトースリエチレングリコール
等の糖または糖アルコール類;ポリオキシエチレンメチ
ルグルコシド、ポリオキシプロピレンメチルグルコシド
等の糖誘導体;デキストリン、ヒアルロン酸、コンドロ
イチン硫酸等の多糖類;グリシン、アラニン、グルタミ
ン酸、セリン、アルギニン、PCAソーダ糖のアミノ酸
類またはその類似物質;コラーゲン等のポリペプダイド
類;クエン酸ソーダ、乳酸ソーダ、リンゴ酸ソーダ等の
有機酸塩などの保湿剤;ベンゾフェノン誘導体、パラア
ミノ安息香酸誘導体、パラメトキシ桂皮酸誘導体、サリ
チル酸誘導体等の紫外線吸収剤;酸化防止剤、防腐剤、
香料、血行促進剤、冷感剤、制汗剤、殺菌剤、皮膚賦活
剤、消炎剤、ビタミンなどを必要に応じて適宜配合する
ことができる。
In the solid powder cosmetic of the present invention, in addition to the above-mentioned essential components, hydrocarbons such as liquid paraffin, iso liquid paraffin and squalane as oil components; olive oil, palm oil, coconut oil, macadamia nut oil, jojoba oil. Fats and oils such as; higher alcohols such as isostearyl alcohol; higher fatty acids, esters such as isopropyl myristate;
Chain polysiloxanes such as dimethylpolysiloxane, methylphenylpolysiloxane, methylhydrogenpolysiloxane; silicone oils such as octamethylcyclotetrasiloxane, decamethylcyclopentasiloxane, cyclic polysiloxanes of dodecamethylcyclohexasiloxane; propylene glycol, Polyhydric alcohols such as 1,3-butylene glycol and glycerin; sugars or sugar alcohols such as glucose, galactose and fructose ethylene glycol; sugar derivatives such as polyoxyethylene methyl glucoside and polyoxypropylene methyl glucoside; dextrin, hyaluronic acid , Polysaccharides such as chondroitin sulfate; amino acids of glycine, alanine, glutamic acid, serine, arginine, PCA soda sugar or analogs thereof Polypeptides such as collagen; Moisturizers such as organic acid salts such as sodium citrate, sodium lactate, sodium malate; UV absorbers such as benzophenone derivatives, paraaminobenzoic acid derivatives, paramethoxycinnamic acid derivatives, salicylic acid derivatives; antioxidants Agents, preservatives,
A fragrance, a blood circulation promoting agent, a cooling sensation agent, an antiperspirant, a bactericidal agent, a skin activating agent, an anti-inflammatory agent, vitamins and the like can be appropriately blended as necessary.

【0022】[0022]

【実施例】次に実施例及び比較例を挙げて本発明を更に
詳細に説明する。本発明はこれにより限定されるもので
はない。配合量は重量%である。
EXAMPLES Next, the present invention will be described in more detail with reference to Examples and Comparative Examples. The present invention is not limited to this. The blending amount is% by weight.

【0023】実施例1、比較例1〜3 実施例1として次の表1の配合組成よりなる固型ファン
デーションを調製した。 (製法)イソパラフィン系炭化水素、界面活性剤、保湿
剤以外の成分を混合し、粉砕機により粉砕する。これに
イソパラフィン系炭化水素、界面活性剤および保湿剤を
室温で攪拌混合したものを加え、さらに粉砕機で均一に
混合粉砕後、粉砕機から取り出し金皿等の容器中に圧縮
成型して固形ファンデーションを得た。
Example 1, Comparative Examples 1 to 3 As Example 1, a solid foundation having the composition shown in Table 1 below was prepared. (Manufacturing method) Components other than isoparaffin hydrocarbon, a surfactant and a moisturizer are mixed and pulverized by a pulverizer. Add a mixture of isoparaffinic hydrocarbon, surfactant and humectant with stirring at room temperature, mix and grind evenly with a crusher, then remove from the crusher and compression mold into a container such as a gold plate to solid foundation. Got

【0024】比較例として不揮発性のオイルを配合した
試料(比較例1)、非シリコーン系界面活性剤を配合し
た試料(比較例2)、疎水化未処理粉末を配合した試料
(比較例3)を調製し、次の方法でトレ試験、テカリ試
験による比較を行った。結果を表1に示す。
As comparative examples, a sample containing a non-volatile oil (Comparative Example 1), a sample containing a non-silicone surfactant (Comparative Example 2), and a sample containing a hydrophobized untreated powder (Comparative Example 3). Were prepared and compared by a tray test and a shine test by the following method. The results are shown in Table 1.

【0025】(トレ評価方法)穴開きフィルム(ポリエ
チレン/エチレンビニルアルコール)の表面に試料固形
ファンデーションを20μg/7cm2 塗布し、表面に
濾紙を接触させ、裏側からイオン交換水1.6g、人工
皮脂(トリオレイン60%、オレイン酸20%、スクワ
レン20%)40mgを同時に透過させた後、裏側に
3.5g/cm2の重りを60秒乗せ、濾紙へのファン
デーションの付着の程度を下記の評価基準に基づいて肉
眼判定する。この試験は汗と皮脂によるトレを同時に評
価するものである。
(Tray evaluation method) A solid sample foundation of 20 μg / 7 cm 2 was applied to the surface of a perforated film (polyethylene / ethylene vinyl alcohol), a filter paper was brought into contact with the surface, and 1.6 g of ion-exchanged water and artificial sebum were applied from the back side. (Triolein 60%, oleic acid 20%, squalene 20%) 40 mg was simultaneously permeated and then a 3.5 g / cm 2 weight was placed on the back side for 60 seconds to evaluate the degree of foundation adhesion to the filter paper as follows. The naked eye is judged based on the standard. This test evaluates sweat and sebum training simultaneously.

【0026】(評価基準) 5;ファンデーション塗布量の100%〜90%濾紙に
付着している。 4;ファンデーション塗布量の89%〜60%濾紙に付
着している。 3;ファンデーション塗布量の59%〜30%濾紙に付
着している。 2;ファンデーション塗布量の29%〜5%濾紙に付着
している。 1;ファンデーション塗布量の5%未満が濾紙に付着し
ている。
(Evaluation Criteria) 5: 100% to 90% of the foundation coating amount adheres to the filter paper. 4; 89% to 60% of the amount of foundation applied adheres to the filter paper. 3; 59% to 30% of the foundation coating amount adheres to the filter paper. 2; 29% to 5% of the amount of foundation applied adheres to the filter paper. 1; Less than 5% of the applied amount of foundation adheres to the filter paper.

【0027】(テカリ評価方法)自己申告で脂性肌と答
えた20代女性10人に、洗顔後、試料の固形ファンデ
ーションを塗布してもらい、塗布4時間後に下記の評価
基準に基づき判定者5人にテカリ評価を行ってもらっ
た。判定者の評価点の平均を被験者各人の評点とし、被
験者10名の評点の平均をその試料のテカリ評価点とし
た。
(Evaluation method) Ten women in their twenties who answered oily skin by self-report were asked to apply the solid foundation of the sample after washing the face, and 5 hours after the application, 5 judges based on the following evaluation criteria. Asked me to do a shining evaluation. The average of the evaluation scores of the judges was used as the evaluation score of each test subject, and the average of the evaluation scores of 10 test subjects was used as the shine evaluation score of the sample.

【0028】(評価基準) 5;非常にテカっている。 4;ややテカっている。 3;塗布直後と変化なし。 2;やや粉っぽい。 1;非常に粉っぽい。(Evaluation criteria) 5: Very good. 4; Somewhat shiny. 3; Immediately after application and no change. 2; Somewhat powdery. 1; Very powdery.

【0029】[0029]

【表1】 ────────────────────────────────── 実施例 比較例 比較例 比較例 成 分 (%) 1 1 2 3 ────────────────────────────────── 低沸点イソパラフィン 8.0 − 8.0 8.0 (アイソゾール400) スクワラン − 8.0 − − ポリエーテル変性シリコーン*1 5.0 5.0 − 5.0 セスキイソステアリン酸ソルビタン − − 5.0 − 1,3−ブチレングリコール 3.0 3.0 3.0 3.0 シリコーン化合物処理酸化チタン*2 10.0 10.0 10.0 − シリコーン化合物処理白雲母*2 15.0 15.0 15.0 − シリコーン化合物処理セリサイト*2 20.0 20.0 20.0 − シリコーン化合物処理合成雲母*2 30.0 30.0 30.0 − シリコーン化合物処理酸化鉄*2 6.3 6.3 6.3 − 酸化チタン − − − 10.0 白雲母 − − − 15.0 セリサイト − − − 20.0 合成雲母 − − − 30.0 酸化鉄 − − − 6.3 ナイロンパウダー 2.2 2.2 2.2 2.2 防腐剤 0.5 0.5 0.5 0.5 ────────────────────────────────── トレ評価 1 5 3 5 テカリ評価 3.2 4.6 2.8 2.3 ────────────────────────────────── 化粧くずれ総合評価 ○ × △ × ──────────────────────────────────[Table 1] ────────────────────────────────── Examples Examples Comparative Examples Comparative Examples Comparative Examples Composition (% ) 1 1 2 3 ────────────────────────────────── Low boiling point isoparaffin 8.0-8.0 8.0 (Isozol 400) Squalane − 8.0 − − Polyether-modified silicone * 1 5.0 5.0 − 5.0 Sorbitan sesquiisostearate − − 5.0−1,3-butylene glycol 3.0 3.0 3.0 3.0 Titanium oxide treated with silicone compound * 2 10.0 10.0 10.0 − Muscovite treated with silicone compound * 2 15.0 15.0 15.0 − Silicone compound treated sericite * 2 20.0 20.0 20.0 − Silicone compound treated synthetic mica * 2 30.0 30.0 30.0 − Silicone compound treated iron oxide * 2 6.3 6.3 6.3 − Titanium oxide − − − 10.0 White mica − − − 15.0 Sericite − − − 20.0 Mica − − − 30.0 Iron oxide − − − 6.3 Nylon powder 2.2 2.2 2.2 2.2 Preservative 0.5 0.5 0.5 0.5 ─────────────────────────── ─────── Training evaluation 1 5 3 5 Shine evaluation 3.2 4.6 2.8 2.3 ──────────────────────────────── ─── Overall evaluation of makeup deterioration ○ × △ × ───────────────────────────────────

【0030】*1:一般式(1)中、y+z=52〜6
5、a=8〜10、b=0、R=水素原子 *2:メチルハイドロジェンポリシロキサン処理粉体
* 1: y + z = 52 to 6 in the general formula (1)
5, a = 8 to 10, b = 0, R = hydrogen atom * 2: Methyl hydrogen polysiloxane treated powder

【0031】以上の結果から、イソパラフィン系炭化水
素、シリコ−ン系界面活性剤と疎水性粉末を組み合わせ
た固型状非水系粉末化粧料は化粧くずれに対して良好で
あることが認められた。
From the above results, it was confirmed that the solid non-aqueous powder cosmetics in which the isoparaffin hydrocarbon, the silicone surfactant and the hydrophobic powder are combined are good for makeup breakage.

【0032】実施例2、比較例4〜5 実施例2として次の表2の配合組成よりなる固型ファン
デーションを調製した。 (製法)イソパラフィン系炭化水素、界面活性剤以外の
成分を混合し、粉砕機により粉砕する。これにイソパラ
フィン系炭化水素および界面活性剤を室温攪拌混合した
ものを加え、さらに粉砕機で均一に混合粉砕後、粉砕機
から取り出し金皿等の容器中に圧縮成型して固形ファン
デーションを得た。
Example 2 and Comparative Examples 4 to 5 As Example 2, solid foundations having the composition shown in Table 2 below were prepared. (Production method) Components other than the isoparaffin hydrocarbon and the surfactant are mixed and pulverized by a pulverizer. To this was added a mixture of isoparaffinic hydrocarbon and surfactant mixed at room temperature with stirring, and the mixture was further uniformly mixed and ground by a grinder, then taken out from the grinder and compression molded into a container such as a gold plate to obtain a solid foundation.

【0033】比較例として沸点が210℃未満のイソパ
ラフィン系炭化水素を配合した試料(比較例4)と不揮
発性イソパラフィン系炭化水素を配合した試料(比較例
5)を調製し、トレ試験、テカリ試験による比較を行っ
た。結果を表2に示す。
As comparative examples, a sample containing isoparaffinic hydrocarbons having a boiling point of less than 210 ° C. (Comparative Example 4) and a sample containing non-volatile isoparaffinic hydrocarbons (Comparative Example 5) were prepared, and a tray test and a shine test were conducted. Was compared. Table 2 shows the results.

【0034】[0034]

【表2】 ────────────────────────────── 実施例 比較例 比較例 成 分 (%) 2 4 5 ────────────────────────────── 低沸点イソパラフィン 13.0 − − (パームリーム6) 低沸点イソパラフィン − 13.0 − (アイソパーH) 不揮発性パラフィン − − 13.0 (流動パラフィン) ポリエーテル変性シリコーン*3 5.0 5.0 5.0 シリコーン化合物処理酸化チタン*4 15.0 15.0 15.0 シリコーン化合物処理セリサイト*4 25.0 25.0 25.0 シリコーン化合物処理金雲母*4 15.0 15.0 15.0 シリコーン化合物処理タルク*4 15.5 15.5 15.5 シリコーン化合物処理酸化鉄*4 6.0 6.0 6.0 二酸化ケイ素 5.0 5.0 5.0 防腐剤 0.5 0.5 0.5 ────────────────────────────── トレ評価 1 1 5 テカリ評価 3.0 2.1 4.2 ────────────────────────────── 化粧くずれ総合評価 ○ △ × ──────────────────────────────[Table 2] ────────────────────────────── Example Comparative Example Comparative Example Component (%) 2 4 5 ── ──────────────────────────── Low-boiling isoparaffin 13.0 − − (Palmream 6) Low-boiling isoparaffin − 13.0 − (Isopar H) Non-volatile Paraffin − − 13.0 (Liquid paraffin) Polyether modified silicone * 3 5.0 5.0 5.0 Silicone compound treated titanium oxide * 4 15.0 15.0 15.0 Silicone compound treated sericite * 4 25.0 25.0 25.0 Silicone compound treated phlogopite * 4 15.0 15.0 15.0 Silicone compound treated Talc * 4 15.5 15.5 15.5 Iron oxide treated with silicone compound * 4 6.0 6.0 6.0 Silicon dioxide 5.0 5.0 5.0 Preservative 0.5 0.5 0.5 ──────────────────────── ────── Training evaluation 1 1 5 Shine evaluation 3.0 2.1 4.2 ────────────────────────────── Overall evaluation of makeup loss ○ △ × ───────────── ──────────────────

【0035】*3:一般式(1)中、y+z=52〜6
5、a=8〜10、b=0、R=水素原子 *4:メチルハイドロジェンポリシロキサン処理粉体
* 3: y + z = 52 to 6 in the general formula (1)
5, a = 8-10, b = 0, R = hydrogen atom * 4: Methylhydrogenpolysiloxane treated powder

【0036】以上の結果から、沸点が210℃未満の低
沸点イソパラフィン系炭化水素では粉っぽく使用感が悪
かった。逆に不揮発性のパラフィンではトレもテカリも
することができなかった。以上より沸点が210〜35
0℃のイソパラフィン系炭化水素が最も好ましいものと
思われた。
From the above results, the low boiling point isoparaffin hydrocarbon having a boiling point of less than 210 ° C. was powdery and had a bad feeling in use. On the contrary, non-volatile paraffin could neither be trained nor shine. From the above, the boiling point is 210-35
Isoparaffinic hydrocarbons at 0 ° C appeared to be the most preferred.

【0037】[0037]

【発明の効果】以上説明したように、本発明の固型状非
水系粉末化粧料は、化粧くずれ、特に汗等の水分による
トレおよび皮脂による経時のトレ・テカリ等を防止する
とともに、さっぱりとした使用感を有すものである。
As described above, the solid non-aqueous powder cosmetics of the present invention prevent makeup deterioration, especially traits due to moisture such as sweat and tractiness and aging due to sebum, as well as freshness. It has a feeling of use.

Claims (4)

【特許請求の範囲】[Claims] 【請求項1】 低沸点イソパラフィン系炭化水素、シリ
コーン系界面活性剤および疎水性粉末を配合することを
特徴とする固型状非水系粉末化粧料。
1. A solid non-aqueous powder cosmetic, comprising a low-boiling isoparaffin hydrocarbon, a silicone surfactant and a hydrophobic powder.
【請求項2】 イソパラフィン系炭化水素の沸点が21
0〜350℃であることを特徴とする請求項1記載の固
型状非水系粉末化粧料。
2. The boiling point of the isoparaffin hydrocarbon is 21.
It is 0-350 degreeC, The solid non-aqueous powder cosmetics of Claim 1 characterized by the above-mentioned.
【請求項3】 シリコ−ン系界面活性剤がポリエ−テル
変性シリコ−ンである請求項1〜2のいずれかに記載の
固型状非水系粉末化粧料。
3. The solid non-aqueous powder cosmetic according to claim 1, wherein the silicone-based surfactant is a polyether-modified silicone.
【請求項4】 更に固体、半固体の油性原料を含まない
請求項1〜3のいずれかに記載の固型状非水系粉末化粧
料。
4. The solid non-aqueous powder cosmetic according to claim 1, further containing no solid or semi-solid oily raw material.
JP14977395A 1995-05-25 1995-05-25 Solid non-aqueous powder cosmetic Withdrawn JPH08319216A (en)