JPH0419187B2 - - Google Patents

Info

Publication number
JPH0419187B2
JPH0419187B2 JP24477983A JP24477983A JPH0419187B2 JP H0419187 B2 JPH0419187 B2 JP H0419187B2 JP 24477983 A JP24477983 A JP 24477983A JP 24477983 A JP24477983 A JP 24477983A JP H0419187 B2 JPH0419187 B2 JP H0419187B2
Authority
JP
Japan
Prior art keywords
parts
cement
weight
present
silicate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
JP24477983A
Other languages
Japanese (ja)
Other versions
JPS60141687A (en
Inventor
Masamichi Kohitsu
Takahiro Hori
Shozo Shimabukuro
Yukifumi Tokunaga
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Telegraph and Telephone Corp
Original Assignee
Nippon Telegraph and Telephone Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Telegraph and Telephone Corp filed Critical Nippon Telegraph and Telephone Corp
Priority to JP24477983A priority Critical patent/JPS60141687A/en
Publication of JPS60141687A publication Critical patent/JPS60141687A/en
Publication of JPH0419187B2 publication Critical patent/JPH0419187B2/ja
Granted legal-status Critical Current

Description

【発明の詳細な説明】[Detailed description of the invention]

本発明は、セメント、モルタル、コンクリート
等の硬化物からなるセメント系材料の表面強化仕
上げ方法に関する。 従来より、セメント、モルタル、コンクリート
等の硬化物は、セメント系材料として建築、土木
その他の分野に多用されているが、風雨に曝され
ると共に気温変化によつて、その表面から次第に
内部へと劣化が進み特に構造物壁面における劣化
は由々しき事態を引き起す原因ともなつている。
かかるセメント系材料の劣化は、外気による中性
化と共に、その表面に存する微細孔が次第にクラ
ツクへと進展することによることが知られてい
る。したがつてセメント系材料表面の強化仕上げ
方法としては、セメント系材料の表面層を化学的
に改質する方法や、仕上げ材により被覆する方法
が提案されているが、未だ充分なものは見られな
い。例えば特開昭55−78764号公報には、劣化し
たコンクリートの表面から、珪酸塩化合物の水溶
液を含浸させた後、更にその上にセメントペース
トを被覆することによる鉄筋コンクリートの補修
方法が示されているが、このセメントペーストに
よる被覆層は弾力性、耐クラツク性を有さず、か
つ耐水性、耐透水性、耐通気性が充分でないた
め、補修後長期に亘り使用すると劣化の進行を止
めることができない。一方通常、被覆材として用
いられる合成樹脂バインダーをベースとした有機
系仕上げ材は、現在、ゴム状弾性体仕上げ材や、
壁面防水材などの名称で開発され、これを用いて
形成される塗膜は一応柔軟性、弾力性、耐クラツ
ク性を具備しているが、耐水性、乾燥硬化性、長
期耐候性に劣り、かつ当然のことながら不燃性を
全く有しないなどの欠点を有するためセメント系
材料の表面強化仕上げ方法として完全なのとは言
えない。 本発明者らは、珪酸アルカリを主成分として含
有する処理液をセメント系材料の表面から含浸さ
せ、ついでこれを乾燥させた後、その表面にゴム
状高弾性を有する無機系仕上げ材または不燃性弾
性仕上げ材を塗布し硬化させることによつて得ら
れたセメント系材料は、該処理液の含浸液化によ
つて得られる改質表面層が厚く、かつ劣化表面層
の強度及びアルカリ度が復元されるため、改質表
面層の劣化が著しく防止されると共に、この改質
表面層の表面は、仕上げ材との接着強度を高める
性質を有するので、この表面に該仕上材を塗布す
ることにより形成される塗膜が風雨に曝され、気
温変化が大きくとも、クラツク、剥離などを生ず
ることがなく、また耐水性、耐透水性、耐通気性
が優れるため、または不燃性であるため、一層良
好にセメント系材料の表面強化仕上げができるこ
とを見い出して本発明を完成した。 本発明の目的はセメント系材料の表面を強化仕
上げるために、セメント系材料の表面から内部の
深い部位に亘り、強度が高く、耐水性、耐透水
性、耐候性等が改良された表面層を形成せしめた
後に、耐クラツク性、耐剥離性および耐水性、耐
透水性、耐通気性が改良されたゴム状高弾性を有
する無機系塗膜、また更に不燃性である弾性塗膜
を形成せしめることによつて、セメント系材料の
表面を強化仕上げする方法を提供することにあ
る。 本発明方法が適用されるセメント系材料は、セ
メント、モルタル、コンクリート、ALC、スレ
ート板等通常のセメントを原料成分とし、これに
必要成分を配合したものを硬化反応により硬化さ
せたものである。上記セメント系材料としては打
設直後のものから打設後使用により既に表面の劣
化が起つているもの、打設時ドライアウトしたも
のなど全てに本発明の方法が適用し得るが、本発
明により処理液を含浸させる前に、充分に乾いて
いるものが好ましい。 本発明に用いられる珪酸アルリは、Li、Na、
K、Cs、NH4等の珪酸塩であり、上記アルカリ
金属原子またはNH4をMで表すとき、SiO2
M2Oモル比で、1〜4のナトリウム水ガラス、
カリウム水ガラス、リチウム水ガラス、珪酸セシ
ウム、珪酸アンモニウムなどであつて、これらは
市販製品として容易に入手し得る。本発明におい
て上記珪酸アルカリは、水で稀釈することにより
珪酸アルカリ分1〜30重量%の水溶液として、ま
たそれらの2種以上を混合した溶液として用いら
れる。好ましい珪酸アルカリとしては、SiO2
M2Oモル比2.2〜4.0の珪酸リチウムが挙げられ
る。珪酸リチウムを用いると、本発明方法を適用
することにより得られたセメント系材料表面の耐
水性が著しく向上し、更に白華現象も起きない。
特に好ましい珪酸リチウム水溶液としては、例え
ば特公昭54−20480号公報に記載されているよう
な透明なものが用いられる。 本発明に用いられる処理液としては、本発明の
目的が達成される限り、上記珪酸アルカリの他に
更に添加剤を含有させても差支えない。また場合
によつては他の添加剤を含有させることによつて
更に好ましい処理液が得られる。 即ち、上記珪酸アルカリ水溶液100重量部と添
加剤としてナフタレンスルホン酸ソーダアルデヒ
ド縮合物塩を0.01〜5重量部含む処理液は、含浸
性が改良されることにより改質表面層の厚さを一
層増大させることができる。 また、上記珪酸アルカリ水溶液100重量部とメ
ターノール、エタノール、n−プロパノール、イ
ソプロパノール、ブタノール等直鎖または分枝鎖
を有する脂肪族1価低級アルコールを0.01〜5重
量部を含む処理液は、同様に含浸性が改良され
る。 一方、上記珪酸アルカリを1〜30重量%と固形
分として1〜30重量%となる量のポリマー水性エ
マルジヨンを含有する処理液によれば、改質表面
層の厚さは減少することなく、更にその表面の耐
水性が著しく増大し表面層からのアルカリ分の溶
出が極度に低下し、改質表面層の表面において劣
化が著るしく防止される。またこの改質表面層の
表面は上塗り塗材との接着強度を高めることがで
き、一層の改良が得られる。 上記珪酸アルカリと併用されるポリマー水性エ
マルジヨンとしては、上記珪酸アルカリ水溶液と
安定に混合できるものであればよく、特に制限を
要しないが、通常好ましい例としては、アクリル
系樹脂エマルジヨン、酢酸ビニル系樹脂エマルジ
ヨン、SBRラテツクス、NBRラテツクス、天然
ゴムラテツクス等が挙げられる。 尚これらの添加剤は、本発明の目的が達成され
る限り混合して含有させて差支えない。 本発明は、まずセメント系材料の表面から、上
記処理液を含浸処理した後、該処理後のセメント
系材料を乾燥するが、上記含浸処理の方法として
は、刷毛、スプレー等による塗布法、浸漬法、加
圧または吸引による方法など通常の方法でよい。 上記含浸後の乾燥によつて、珪酸アルカリがセ
メント系材料の表面層中で硬化反応を起し、強度
およびアルカリ度を向上させた改質表面層が形成
される。 本発明の方法は更に上記改質表面上に塗材を塗
布し硬化することを特徴とする。上記塗材には、
特微成分としてセメントと、細骨材とフイルム延
び率が1500%以上で、かつガラス転移温度が−10
℃以下のアクリル系重合体のエマルジヨンが含有
される。 本発明方法に用いる上記セメントとしては普通
ポルトランドセメント、白色ポルトランドセメン
ト、高炉セメント、シリカセメント、フライアツ
シユセメントなど、種々のセメントが使用可能で
あり、また細骨材としては砂、珪砂、塞水砂、天
然および人工軽量骨材などが使用できる。 上記塗材に用いられるアルカリ系重合体のエマ
ルジヨン中のアルカリ系重合体はJISK−6301に
準拠して求められるフイルム延び率が1500%以上
で、かつガラス転移温度が−10℃以下であること
が必要であり、この範囲をはずれたものは、所期
のゴム状高弾性が得られず、また塗膜の耐ひび割
れ性付与に乏しくなるので好ましくない。 上記アクリル系重合体としては例えば2−エチ
ルエキシルアクリレート、ブチルアクリレート、
エチルアクリレート、イソプロピルアクリレー
ト、ラウリルメタクリレート、ヘキシルメタクリ
レート、スチレン、アクリロニトリルの重合体ま
たは共重合体が挙げられ、これらは本発明に係る
塗材によつて形成される塗膜に弾性を与えるもの
であり、上記例示した重合体に限定されるもので
はない。 またアクリル系重合体エマルジヨンは市場で入
手することができ、例えばポリトロンZ−220「商
品名:旭化成工業(株)製」ヨドゾールAD−21「商
品名:カネボーNSC社製」アクロナールS−400
「商品名:バスフ社製」などがある。 本発明に用いられる塗材としては、上記セメン
ト、細骨材およびアクリル系重合体の他に必要に
より顔料、亀裂防止を助けるマイカ、防水を助け
るカルシユームステアレート、その他分散剤、不
燃性を助ける硼砂などの充填剤、添加剤、水など
を含ませてもよい。 本発明に用いられる塗材はまた、その含有成分
の比率が、セメント100重量部に対して、細骨材
50〜300重量部、アクリル系重合体のエマルジヨ
ンの固形分5〜100重量部であることも特徴とす
る。細骨材の含有率が50重量部以下では塗材の延
び率が低くなりしかも施工初期の乾燥ひび割れが
生じやすくなるため好ましくない。逆に300重量
部を越えた場合は塗膜の強度が低下し付着力が低
下するのみならず、耐水性や、表面乾燥性も悪く
なるので好ましくない。また、アクリル系重合体
エマルジヨンの固形分としての含有率が25重量部
未満の場合は得られる塗膜に初期のゴム状高弾性
が得られず、逆に100重量部を越え場合は、凝集
力が低下し、しかも塗材が粘着性を帯び耐汚染性
が低下するので好ましくない。 本発明に用いられる塗材は、その目的に応じて
上記範囲内での含有率を変えることができる。例
えば、不燃性を目的とするときは、セメン100重
量部に対し細骨材は50〜200重量部、アクリル系
重合体エマルジヨン固形分として5〜15重量部程
度が好ましい。また、高度に弾性を有する塗膜を
目的とするときは、セメント100重量部に対し細
骨材50〜300重量部、アクリル系重合体エマルジ
ヨンを固形分として25〜100重量部程度が好まし
い。本発明に用いられる塗材は、上記セメント、
細骨材およびアクリル系重合体エマルジヨンを、
或いは必要に応じ任意成分及び水を加えて充分に
混合することにより容易に調整される。 本発明の方法は、前記のセメント系材料を、そ
の表面から前記処理液で含浸処理し、乾燥させた
後、更にその表面に上記塗材を塗着させた後、含
有セメントの水硬反応とエマルジヨン乾燥硬化を
起させることによつてセメント系材料表面上に塗
膜を形成させる仕上げ方法である。塗材の塗着に
は通常の方法、例ば刷毛塗り、ロール塗布などで
よい。 本発明方法は、簡易に実施することができる
し、また、本発明方法により得られたセメント系
材料は、中性化による劣化、或いはクラツクの進
展による劣化共に著しく防止され、しかも耐水
性、耐透水性、耐候性にも著しく優れる。したが
つて、劣化前のセメント系材料の劣化防止、劣化
したセメント系材料の補修、復元に極めて有用で
ある。 以下比較例と共に実施例を挙げて更に詳述する
が、本発明の技術的範囲はこれに限定されるもの
ではない。 実施例 1 表1に示す試験用の供試体No.1〜No.5のそれぞ
れに、SiO2濃度10%モル比(SiO2/Na2O)3.0の
珪酸ナトリウム溶液を刷毛で吸い込みが止まるま
で塗布した後乾燥させた。別に表2に示す配合物
を均一に混合したもの100.2部と表3に示すアク
リル系重合体エマルジヨン配合物を充分に混合し
たもの41.03部を撹拌混合して塗材を作り、上記
珪酸ナトリウムを含浸させ乾燥後の供試体に厚さ
1mm塗布して各試験用テストピースを作成し、そ
れぞれの試験を行つた。試験結果は、表9に示
す。
The present invention relates to a surface reinforcement finishing method for cementitious materials made of hardened materials such as cement, mortar, and concrete. Traditionally, cured products such as cement, mortar, and concrete have been widely used as cement-based materials in architecture, civil engineering, and other fields. Deterioration progresses, and deterioration, especially on the walls of structures, is causing serious problems.
It is known that such deterioration of cementitious materials is due to carbonization by outside air and the gradual development of micropores existing on the surface into cracks. Therefore, as methods for strengthening and finishing the surface of cementitious materials, methods have been proposed in which the surface layer of cementitious materials is chemically modified or coated with finishing materials, but no satisfactory method has yet been found. do not have. For example, JP-A-55-78764 discloses a method for repairing reinforced concrete by impregnating the surface of deteriorated concrete with an aqueous solution of a silicate compound, and then coating the impregnated surface with cement paste. However, this coating layer made of cement paste does not have elasticity or crack resistance, and does not have sufficient water resistance, water permeability resistance, or air permeability, so if it is used for a long time after repair, it may be difficult to stop the progress of deterioration. Can not. On the other hand, organic finishing materials based on synthetic resin binders, which are usually used as coating materials, are currently available in rubber-like elastomer finishing materials,
It was developed under the name of wall waterproofing material, and the coating film formed using this material has some flexibility, elasticity, and crack resistance, but it is inferior in water resistance, dry hardening properties, and long-term weather resistance. As a matter of course, it has drawbacks such as not being nonflammable at all, so it cannot be said to be a perfect method for surface reinforcement finishing of cementitious materials. The present inventors impregnated the surface of a cement material with a treatment liquid containing alkali silicate as a main component, dried it, and applied an inorganic finishing material with rubber-like high elasticity or a nonflammable finishing material to the surface. The cementitious material obtained by applying and curing the elastic finishing material has a thick modified surface layer obtained by impregnating and liquefying the treatment liquid, and the strength and alkalinity of the deteriorated surface layer are restored. Therefore, deterioration of the modified surface layer is significantly prevented, and the surface of this modified surface layer has the property of increasing the adhesive strength with the finishing material, so by applying the finishing material to this surface, the surface of the modified surface layer can be formed. Even if the coating film is exposed to wind and rain and there are large temperature changes, it will not crack or peel, and it is even better because it has excellent water resistance, water permeability, and air permeability, and is nonflammable. The present invention was completed by discovering that the surface of cement-based materials can be strengthened. The purpose of the present invention is to provide a surface layer with high strength and improved water resistance, water permeability, weather resistance, etc., from the surface of the cement material to the deep inside, in order to strengthen and finish the surface of the cement material. After forming, an inorganic coating film having rubber-like high elasticity with improved crack resistance, peeling resistance, water resistance, water permeability resistance, and air permeability resistance, and an elastic coating film that is also nonflammable is formed. In particular, it is an object of the present invention to provide a method for enhancing the surface of cementitious materials. The cementitious material to which the method of the present invention is applied uses ordinary cement such as cement, mortar, concrete, ALC, slate board, etc. as a raw material, and the necessary components are blended with this and then hardened by a hardening reaction. The method of the present invention can be applied to all types of cement-based materials, including those that have just been poured, those that have already experienced surface deterioration due to use after placement, and those that have dried out during placement. It is preferable that the material is sufficiently dry before being impregnated with the treatment liquid. The allyl silicate used in the present invention includes Li, Na,
It is a silicate of K, Cs, NH 4 etc., and when the above alkali metal atom or NH 4 is represented by M, SiO 2 /
M2O molar ratio of 1 to 4 sodium water glass,
Potassium water glass, lithium water glass, cesium silicate, ammonium silicate, etc., are easily available as commercial products. In the present invention, the alkali silicate can be used as an aqueous solution having an alkali silicate content of 1 to 30% by weight by diluting it with water, or as a mixture of two or more thereof. Preferred alkali silicate is SiO 2 /
Lithium silicate with an M 2 O molar ratio of 2.2 to 4.0 may be mentioned. When lithium silicate is used, the water resistance of the cement material surface obtained by applying the method of the present invention is significantly improved, and furthermore, efflorescence does not occur.
As a particularly preferred aqueous lithium silicate solution, a transparent one such as that described in Japanese Patent Publication No. 54-20480 is used. The treatment liquid used in the present invention may contain additives in addition to the alkali silicate described above, as long as the object of the present invention is achieved. In some cases, a more preferable treatment liquid can be obtained by containing other additives. That is, the treatment liquid containing 100 parts by weight of the aqueous alkali silicate solution and 0.01 to 5 parts by weight of naphthalene sulfonic acid sodium aldehyde condensate salt as an additive further increases the thickness of the modified surface layer by improving the impregnating property. can be done. Similarly, a treatment solution containing 100 parts by weight of the aqueous alkali silicate solution and 0.01 to 5 parts by weight of an aliphatic monohydric lower alcohol having a linear or branched chain such as methanol, ethanol, n-propanol, isopropanol, butanol, etc. Impregnating properties are improved. On the other hand, according to the treatment liquid containing the above-mentioned alkali silicate in an amount of 1 to 30% by weight and a polymer aqueous emulsion in an amount of 1 to 30% by weight as solid content, the thickness of the modified surface layer did not decrease and The water resistance of the surface is significantly increased, the elution of alkaline components from the surface layer is extremely reduced, and deterioration of the surface of the modified surface layer is significantly prevented. Furthermore, the surface of this modified surface layer can increase the adhesive strength with the top coating material, resulting in further improvement. The aqueous polymer emulsion used in combination with the alkali silicate is not particularly limited as long as it can be stably mixed with the aqueous alkali silicate solution, but usually preferred examples include acrylic resin emulsion, vinyl acetate resin, etc. Examples include emulsion, SBR latex, NBR latex, natural rubber latex, etc. Note that these additives may be mixed and contained as long as the purpose of the present invention is achieved. In the present invention, the surface of the cement material is first impregnated with the treatment liquid, and then the cement material after the treatment is dried. Examples of the impregnation method include coating with a brush, spray, etc., and dipping. Any conventional method may be used, such as a method using pressure, pressure, or suction. By drying after the impregnation, the alkali silicate causes a hardening reaction in the surface layer of the cement material, forming a modified surface layer with improved strength and alkalinity. The method of the present invention is further characterized in that a coating material is applied onto the modified surface and cured. The above coating materials include
The special components are cement, fine aggregate, film elongation of 1500% or more, and glass transition temperature of -10.
Contains an emulsion of an acrylic polymer at a temperature of 0.degree. As the above-mentioned cement used in the method of the present invention, various cements such as ordinary Portland cement, white Portland cement, blast furnace cement, silica cement, and fly ash cement can be used, and as the fine aggregate, sand, silica sand, and impregnated sand can be used. , natural and artificial lightweight aggregates, etc. can be used. The alkaline polymer in the alkaline polymer emulsion used in the above coating material must have a film elongation of 1500% or more and a glass transition temperature of -10°C or less as determined in accordance with JISK-6301. If the amount is outside this range, the desired rubber-like high elasticity cannot be obtained and the cracking resistance of the coating film becomes poor, so it is not preferable. Examples of the acrylic polymers include 2-ethylexyl acrylate, butyl acrylate,
Examples include polymers or copolymers of ethyl acrylate, isopropyl acrylate, lauryl methacrylate, hexyl methacrylate, styrene, and acrylonitrile, which impart elasticity to the coating film formed by the coating material according to the present invention, It is not limited to the polymers exemplified above. Acrylic polymer emulsions are available on the market, such as Polytron Z-220 (trade name: manufactured by Asahi Kasei Corporation), Yodozol AD-21, and Acronal S-400 (trade name: manufactured by Kanebo NSC).
"Product name: Manufactured by Basuf Corporation" etc. In addition to the above-mentioned cement, fine aggregate, and acrylic polymer, the coating materials used in the present invention include pigments as necessary, mica to help prevent cracks, calcium stearate to help waterproof, other dispersants, and nonflammability. Fillers such as borax, additives, water, etc. may be included. The coating material used in the present invention also has a content ratio of fine aggregate to 100 parts by weight of cement.
50 to 300 parts by weight, and the solid content of the acrylic polymer emulsion is 5 to 100 parts by weight. If the content of fine aggregate is less than 50 parts by weight, it is not preferable because the elongation rate of the coating material becomes low and dry cracks are more likely to occur in the initial stage of construction. On the other hand, if it exceeds 300 parts by weight, it is not preferable because not only the strength and adhesion of the coating film decreases, but also the water resistance and surface drying properties deteriorate. In addition, if the solid content of the acrylic polymer emulsion is less than 25 parts by weight, the resulting coating film will not have high initial rubber-like elasticity, and if it exceeds 100 parts by weight, the cohesive strength It is not preferable because the coating material becomes sticky and the stain resistance decreases. The content of the coating material used in the present invention can be varied within the above range depending on the purpose. For example, when nonflammability is desired, the fine aggregate is preferably 50 to 200 parts by weight, and the solid content of the acrylic polymer emulsion is preferably about 5 to 15 parts by weight per 100 parts by weight of cement. When a highly elastic coating film is intended, it is preferable to use 50 to 300 parts by weight of fine aggregate and 25 to 100 parts by weight of acrylic polymer emulsion as a solid content per 100 parts by weight of cement. The coating material used in the present invention includes the above cement,
fine aggregate and acrylic polymer emulsion,
Alternatively, it can be easily adjusted by adding optional ingredients and water as necessary and mixing thoroughly. In the method of the present invention, the surface of the cement material is impregnated with the treatment liquid, dried, and then the coating material is applied to the surface, and then the hydraulic reaction of the cement contained therein is carried out. A finishing method that forms a coating film on the surface of a cementitious material by drying and curing an emulsion. The coating material may be applied by conventional methods such as brush application, roll application, etc. The method of the present invention can be easily carried out, and the cement-based materials obtained by the method of the present invention are significantly prevented from deterioration due to carbonation or the development of cracks, and are water resistant and resistant. It also has excellent water permeability and weather resistance. Therefore, it is extremely useful for preventing the deterioration of cementitious materials before deterioration, and for repairing and restoring deteriorated cementitious materials. The present invention will be described in more detail below by giving Examples together with Comparative Examples, but the technical scope of the present invention is not limited thereto. Example 1 A sodium silicate solution with a SiO 2 concentration of 10% and a molar ratio (SiO 2 /Na 2 O) of 3.0 was applied to each of the test specimens No. 1 to No. 5 shown in Table 1 with a brush until the suction stopped. After application, it was dried. Separately, a coating material was prepared by stirring and mixing 100.2 parts of a homogeneous mixture of the formulations shown in Table 2 and 41.03 parts of a thorough mixture of the acrylic polymer emulsion formulations shown in Table 3, and impregnated with the above sodium silicate. Test pieces for each test were prepared by coating the sample with a thickness of 1 mm after drying, and each test was conducted. The test results are shown in Table 9.

【表】 表 2 ポルトランドセメント 46部 タンカルG−100* 17〃 タンカルG−50* 30〃 硼 砂 4〃 マイカ 1〃 ステアリン酸カルシウム 0.2部酸化チタン 2部 計 100.2部 * 林化成社製:炭酸カルシウムの商品名 表 3 アクロナールS−400* 12.5部 メチルセルロース 0.2〃 グルコン酸カルシウム 1.0〃 ノニオン界面活性剤 1.0部 スラモニーB** 0.03部 ノブコNXZ*** 0.3部水 26.0部 計 41.03部 *バスフ社製:固形分57%のアクリル計重合体エ
マルジヨンの商品名、重合体のガラス転移温度
は−20℃で、延び率は2700%以上である。 **武田薬品工業社製:防腐剤の商品名 ***サンノブコ社製:消泡剤の商品名 実施例 2〜6 実施例1の珪酸ナトリウ溶液を以下に示す珪酸
アルカリ溶液に変えた他は、実施例1と全く同様
にして試験を行つた。 結果は表9に示す。 実施例 2 珪酸カリウムSiO2濃度10%SiO2/M2Oモル比
3.0 実施例 3 珪酸リチウムSiO2濃度10%SiO2/M2Oモル比3.5 実施例 4 珪酸リチウムSiO2濃度10%SiO2/M2Oモル比3.5 ナフタレンスルホン酸ソーダホルマリン縮合物
0.1% 実施例 5 珪酸リチウムSiO2濃度10%SiO2/M2Oモル比
3.5 エチルアルコールを0.5%となるよう添加 実施例 6 珪酸リチウムSiO2濃度10%SiO2/M2Oモル比
3.5 アクリル−スチレン合成樹脂エマルジヨン固形
分として5% 実施例 7 実施例3と同様に各供試体に、SiO2濃度10%
モル比3.0の珪酸リチウム水溶液を塗布、乾燥後、
表4、5の各配合物を均一に混合して得た塗材を
厚さ1mm塗布したものについて、同様にして試験
を行つた。結果は表9に示す。 表 4 白色ポルトランドセメント 46部 タンカルG−100 17部 タンカルG−50 30部 硼 砂 4部 マイカ 1部 ステアリン酸カルシウム 0.2部酸化チタン 2部 計 100.2部 表 5 アクロナールS−400 80部 メチルセルロース 0.3部 グルコン酸カルシウム 1.0部 ノニオン活性剤 1.0部 防腐剤 0.03部ノブコNXZ 0.3部 計 82.63部 比較例 1 実施例1の珪酸ナトリウ溶液の代わりに、エチ
レン酢酸ビニール系の合成樹脂エマルジヨン溶液
(固形分25%)を100〜120g/m2塗布した他は実
施例1と全く同様にして行つた。 これら比較例の結果を表9に示す。 比較例 2 表6に示す配合物を混合したものを塗材として
用いた他は実施例1と全く同様にして試験を行つ
た。 表 6 モビニールDM−60* 25部 タンカルG−100 66部 マイカ 6.5部 メチルセルロース 0.15部 プライマール850** 0.7部 エチレングリコール 1.0部 ノブコNXZ 0.4部水 1.5部 計 101.25部 *ヘキスト合成社製:固形分50%のアクリル系重
合体エマルジヨンの商品名、重合体のガラス転
移温度は10℃で、フイルム延び率は約550%で
ある。 **日本アクリル化成社製:分散剤商品名 比較例 3 下表に示す配合物を実施例1と同様に混合製造
し、別に下表8に示す重合体エマルジヨン配合物
を実施例1と同様に作つた。 表 7 ポルトランドセメント 40部 タンカルG−50 45部 マイカ 5.5部 プラスター 4.5部 酸化チタン 5.0部ステアリン酸カルシウム 0.2部 計 100.2部 表 8 スミカフレツクス400* 11.2部 メルセルロース 0.2部 グルコン酸カルシウム 1.0部 ノニオン界面活性剤 1.0部 スラモニーB 0.03部 ノブコNXZ 0.3部水 26.3部 計 40.03部 *住友化学社製:固形分50%の酢酸ビニール系エ
マルジヨンの商品名、この樹脂のガラス転移温
度は約0℃で、フイルム延び率は520%である。 上記表7の配合物100.2部に表8の配合物40.03
部を混合したものを塗材とした他は実施例1と全
く同様にして試験を行つた。 結果は表9に示す。
[Table] Table 2 Portland cement 46 parts Tancal G-100 * 17〃 Tancal G-50 * 30〃 Borax sand 4〃 Mica 1〃 Calcium stearate 0.2 parts Titanium oxide 2 parts Total 100.2 parts * Manufactured by Hayashi Kasei Co., Ltd.: Calcium carbonate Product name Table 3 Acronal S-400 * 12.5 parts Methyl cellulose 0.2〃 Calcium gluconate 1.0〃 Nonionic surfactant 1.0 parts Slamony B ** 0.03 parts Nobuco NXZ *** 0.3 parts Water 26.0 parts Total 41.03 parts * Manufactured by Basf Corporation: Solid Trade name of 57% acrylic polymer emulsion, the glass transition temperature of the polymer is -20℃, and the elongation is more than 2700%. **Manufactured by Takeda Pharmaceutical Co., Ltd.: Brand name of preservative ***Manufactured by San Nobuco Co., Ltd.: Brand name of antifoaming agent Examples 2 to 6 The sodium silicate solution in Example 1 was changed to the alkaline silicate solution shown below. The test was conducted in exactly the same manner as in Example 1. The results are shown in Table 9. Example 2 Potassium silicate SiO 2 concentration 10% SiO 2 /M 2 O molar ratio
3.0 Example 3 Lithium silicate SiO 2 concentration 10% SiO 2 /M 2 O molar ratio 3.5 Example 4 Lithium silicate SiO 2 concentration 10% SiO 2 /M 2 O molar ratio 3.5 Naphthalenesulfonic acid soda formalin condensate
0.1% Example 5 Lithium silicate SiO 2 concentration 10% SiO 2 /M 2 O molar ratio
3.5 Example of adding ethyl alcohol to 0.5% 6 Lithium silicate SiO 2 concentration 10% SiO 2 /M 2 O molar ratio
3.5 5% as solid content of acrylic-styrene synthetic resin emulsion Example 7 As in Example 3, SiO 2 concentration of 10% was added to each specimen.
After applying a lithium silicate aqueous solution with a molar ratio of 3.0 and drying,
A test was conducted in the same manner on a coating material obtained by uniformly mixing each of the formulations shown in Tables 4 and 5 and applied to a thickness of 1 mm. The results are shown in Table 9. Table 4 White Portland cement 46 parts Tancal G-100 17 parts Tancal G-50 30 parts Borax sand 4 parts Mica 1 part Calcium stearate 0.2 parts Titanium oxide 2 parts Total 100.2 parts Table 5 Acronal S-400 80 parts Methyl cellulose 0.3 parts Gluconic acid Calcium 1.0 parts Nonionic activator 1.0 parts Preservative 0.03 parts Nobuco NXZ 0.3 parts Total 82.63 parts Comparative Example 1 Instead of the sodium silicate solution of Example 1, 100% of an ethylene-vinyl acetate-based synthetic resin emulsion solution (solid content 25%) was used. The process was carried out in exactly the same manner as in Example 1, except that ~120 g/m 2 was applied. Table 9 shows the results of these comparative examples. Comparative Example 2 A test was conducted in exactly the same manner as in Example 1, except that a mixture of the formulations shown in Table 6 was used as the coating material. Table 6 Movinyl DM-60 * 25 parts Tancal G-100 66 parts Mica 6.5 parts Methyl cellulose 0.15 parts Primal 850 ** 0.7 parts Ethylene glycol 1.0 parts Nobuko NXZ 0.4 parts Water 1.5 parts Total 101.25 parts *Manufactured by Hoechst Synthetic Co., Ltd.: Solid content The product name is 50% acrylic polymer emulsion, the glass transition temperature of the polymer is 10℃, and the film elongation is about 550%. **Manufactured by Nippon Acrylic Kasei Co., Ltd.: Dispersant trade name Comparative Example 3 The formulations shown in the table below were mixed and manufactured in the same manner as in Example 1, and separately, the polymer emulsion formulations shown in Table 8 below were mixed and manufactured in the same manner as in Example 1. I made it. Table 7 Portland cement 40 parts Tancal G-50 45 parts Mica 5.5 parts Plaster 4.5 parts Titanium oxide 5.0 parts Calcium stearate 0.2 parts Total 100.2 parts Table 8 Sumikaflex 400 * 11.2 parts Mercellulose 0.2 parts Calcium gluconate 1.0 parts Nonionic surfactant 1.0 Part Ramony B 0.03 parts Nobuco NXZ 0.3 parts Water 26.3 parts Total 40.03 parts *Manufactured by Sumitomo Chemical Co., Ltd.: Trade name of vinyl acetate emulsion with solid content of 50%. The glass transition temperature of this resin is approximately 0°C, and the film elongation rate is It is 520%. 100.2 parts of the formulation in Table 7 above and 40.03 parts of the formulation in Table 8
A test was conducted in exactly the same manner as in Example 1, except that a mixture of these parts was used as a coating material. The results are shown in Table 9.

【表】 試験方法 a 試験体の中央にΔ状の鉄筋を挟み割裂する。
割裂面の埃り等を除去した後、フエノールフタ
レインを1%含むエタノール水比9:1の溶液
を吹き付けモルタル表面よりの呈色した部分ま
での深さを測定。 b JISA−6910による。 c 同上 d JISA−1321による。 e 温度30℃湿度60%、CO2濃度5%の室内に1
ケ月放置した後、割裂し、フエノールフタレイ
ン溶液を吹き付けて表面より呈色部分まで深さ
を測定。
[Table] Test method a A Δ-shaped reinforcing bar is placed in the center of the specimen and split.
After removing dust etc. from the cracked surface, spray a solution containing 1% phenolphthalein in an ethanol/water ratio of 9:1 and measure the depth from the mortar surface to the colored area. b According to JISA-6910. c Same as above d According to JISA-1321. 1 in a room with a temperature of 30°C, humidity of 60%, and a CO2 concentration of 5%.
After leaving it for several months, it was split open, sprayed with phenolphthalein solution, and the depth measured from the surface to the colored area.

Claims (1)

【特許請求の範囲】[Claims] 1 セメント系材料をその表面から、珪酸アルカ
リを1〜30重量%含有する処理液で含浸処理し、
乾燥させた後、得られた表面に更にセメント100
重量部と細骨材50〜300重量部とフイルム延び率
1500%以上で、かつガラス転移温度−10℃以下で
あるアクリル系重合体のエマルジヨンを固形分と
して5〜100重量部とを含有する塗材を塗着硬化
させることを特徴とするセメント系材料の表面強
化仕上方法。
1 Impregnating the cement material from its surface with a treatment solution containing 1 to 30% by weight of alkali silicate,
After drying, further cement 100% on the resulting surface
Weight part, fine aggregate 50-300 weight part and film elongation rate
A cement-based material characterized by applying and curing a coating material containing 5 to 100 parts by weight of an acrylic polymer emulsion with a solid content of 1500% or more and a glass transition temperature of -10°C or less. Surface reinforcement finishing method.
JP24477983A 1983-12-27 1983-12-27 Surface enhancement finishing method for cementitious material Granted JPS60141687A (en)